Evaluation of Autogenous Healing in Flexural Mortar Members by Chloride Ion Penetration Resistance

In this study, we investigated the effects of mineral admixtures on the autogenous healing of flexural mortar members through a chloride ion penetration test. The mineral admixtures used were ground granulated blast-furnace slag (GGBS), fly ash, silica fume (SF), clinker binder, and clinker sand. Through a four-point bending test, a crack of approximately 100 μm was induced at the bottom of the flexural mortar member, and the chloride ion penetration depth through the crack was measured to evaluate the self-healing performance. Additionally, we analyzed the correlation between the self-healing performances, which was measured through water flow and water absorption tests. The experimental results showed that the chloride ion penetration depth decreased due to crack healing, and the self-healing performance of the GGBS and SF was the highest. It was found that the subtle change in the self-healing performance was more accurately evaluated by the chloride ion penetration test.