Optimum heat treatment to enhance the weak-linkresponse of Y123 nanowires prepared by SolutionBlow Spinning
Authors:
Ana M. Caffer,
Davi A. D. Chaves,
Alexsander L. Pessoa,
Claudio L. Carvalho,
Wilson A. Ortiz,
Rafael Zadorosny,
Maycon Motta
Abstract:
Although the production of YBa$_{2}$Cu$_{3}$O$_{7-δ}$ (Y123) has been extensively reported, there is still a lack of information on the ideal heat treatment to produce this material in the form of one dimension nanostructures. Thus, by means of the Solution Blow Spinning technique, metals embedded in polymer fibers were prepared. These polymer composite fibers were fired and then investigated by t…
▽ More
Although the production of YBa$_{2}$Cu$_{3}$O$_{7-δ}$ (Y123) has been extensively reported, there is still a lack of information on the ideal heat treatment to produce this material in the form of one dimension nanostructures. Thus, by means of the Solution Blow Spinning technique, metals embedded in polymer fibers were prepared. These polymer composite fibers were fired and then investigated by thermogravimetric analysis. The maximum sintering temperatures of heat treatment were chosen in the interval \SI{850}{\celsius}-\SI{925}{\celsius} for one hour under oxygen flux. SEM images allowed us to determine the wire diameter as approximately 350~nm for all samples, as well as to map the evolution of the entangled wire morphology with the sintering temperature. XRD analysis indicated the presence of Y123 and secondary phases in all samples. Ac magnetic susceptibility and dc magnetization measurements demonstrated that the sample sintered at \SI{925}{\celsius}/1h is the one with the highest weak-link critical temperature and the largest diamagnetic response.
△ Less
Submitted 6 October, 2020;
originally announced October 2020.
-
Successful production of Solution Blow Spun YBCO+Ag complex ceramics
Authors:
A. L. Pessoa,
M. J. Raine,
D. P. Hampshire,
D. K. Namburi,
J. H. Durrell,
R. Zadorosny
Abstract:
YBCO fabrics composed of nanowires, produced by solution blow spinning (SBS) are so brittle that the Lorentz force produced by induced currents can be strong enough to damage them. On the other hand, it is known that silver addition improves the mechanical and flux pinning properties of ceramic superconductors. Thus, in this work, we show how we successfully obtained a polymeric precursor solution…
▽ More
YBCO fabrics composed of nanowires, produced by solution blow spinning (SBS) are so brittle that the Lorentz force produced by induced currents can be strong enough to damage them. On the other hand, it is known that silver addition improves the mechanical and flux pinning properties of ceramic superconductors. Thus, in this work, we show how we successfully obtained a polymeric precursor solution containing YBCO$+$Ag salts, which can be spun by the SBS route to produce ceramic samples. Yttrium, barium, copper, and silver metal acetates, and polyvinylpyrrolidone (PVP) (in a ratio of 5:1wt [PVP:acetates]) were dissolved in a solution with 61.5 wt\% of methanol, 12 wt\% of propionic acid, and 26.5 wt\% of ammonium hydroxide, together with 6 wt\% of PVP in solution. Three different amounts of silver (10 wt\%, 20 wt\%, and 30 wt\%) were used in YBa$_2$Cu$_3$O$_{7-x}$. The TGA characterizations revealed a lowering of crystallization and partial melting temperatures by about \SI{30}{\celsius}. SEM images show that after burning out the polymer, a fabric composed of nanowires of diameters up to \SI{380}{\nano \metre} is produced. However, after the sintering process at \SI{925}{\celsius} for \SI{1}{\hour}, the nanowires shrink into a porous-like sample.
△ Less
Submitted 17 August, 2020; v1 submitted 6 April, 2020;
originally announced April 2020.
-
One-pot synthesis: a simple and fast method to obtain ceramic superconducting materials
Authors:
Maycon Rotta,
Maycon Motta,
Alexsander L Pessoa,
Claudio L Carvalho,
Cesar V Deimling,
Paulo N Lisboa-Filho,
Wilson A Ortiz,
Rafael Zadorosny
Abstract:
The one-pot method focuses on the reduction of the number of steps or chemical reactions in the synthesis of materials, and it is very appealing in terms of sustainability. In addition to this point of view, superconductors are desired materials due to their unusual properties, such as the zero resistivity and the perfect diamagnetism. One-pot, Thus, in this work, we described the one-pot synthesi…
▽ More
The one-pot method focuses on the reduction of the number of steps or chemical reactions in the synthesis of materials, and it is very appealing in terms of sustainability. In addition to this point of view, superconductors are desired materials due to their unusual properties, such as the zero resistivity and the perfect diamagnetism. One-pot, Thus, in this work, we described the one-pot synthesis of YBa2Cu3O7-δ superconducting ceramic. In just two steps and a few hours, a polymer composite solution was prepared, which originates a powder after burning the polymer out with pure phase and with superconducting properties better than those produced by other techniques.
△ Less
Submitted 26 August, 2019;
originally announced August 2019.