Abstract
The Al-C, Si-C, and Al-Si-C systems were investigated by metallography, X-ray diffraction, electron microprobe, and thermal analysis. Internally sealed liquidus crucibles were used to determine the solubility of C in Al and Si in the range 1700° to 2150 °C and isothermal sections for the ternary system at 2000° and 2150 °C. The isopleth Al4C3-SiC, determined in the range 1900° to 2300 °C, was found to contain the ternary intermediate phases 2A14C3 · SiC and A14C3 · SiC, which decompose incongruently at 2085° and 2080 °C, respectively. The incongruent decomposition temperature of A14C3 (2156 °C) was confirmed. A phase reported by others with the stoichiometry Al4C3-2SiC was not confirmed. A partial liquidus surface was mapped from the carbon solubility and thermal analysis measurements.
Similar content being viewed by others
References
M. Dokiya and H. Yokokawa:Tetsu-to-Hagané, 1983, vol. 69^(11), pp. 1382–87.
M. J. Bruno: Final Tech. Rept. to DOE prepared under contract DEAC01-77CS40079, Feb. 1983, pp. 2, 335.
P.T. Stroup:Trans. AIME, 1964, vol. 230, pp. 356–72.
M. Hansen and K. Anderko:Constitution of Binary Alloys, McGraw- Hill, New York, NY, 1958, p. 133.
K. Motzfeldt and B. Sandberg:Light Metals, 1979, TMS-AIME, pp. 411-28.
R.I. Scace and G.A. Slack:J. Chem. Phys., 1959, vol. 30(6), pp. 1551–55.
R. T. Dolloff: WADD-TR 60-143, 1960, 22 pp.
V.J. Barczak:J. Amer. Ceram. Soc, 1961, vol. 44, p. 299.
J. Schoennahl, B. Miller, and M. Daire:Materials Science, 1979, vol. 4, pp. 338–45.
G. Schneider, L. J. Gaucklev, G. Petzow, and A. Zangvil:J. Amer. Ceram. Soc, 1979, vol. 62^(11–12), pp. 574–76.
H. Yokokawa, M. Dokiya, M. Fujishige, T. Kameyama, S. Ujiie, and K. Fukuda:Commun. Amer. Ceram. Soc, 1982, vol. 65(3), pp. C40-C41.
B.L. Kidwell, L. L. Oden, and R. A. McCune:J. Appl. Crystall., 1984, vol. 17, pp. 481–82.
Z. Inoue, Y. Inomata, H. Tanaka, and H. Kawabata:J. Mater. Sei., 1980, vol. 15, pp. 575–80.
Y. Inomata, H. Tanaka, Z. Inoue, and H. Kawabata:J. Ceram. Soc. Japan, 1980, vol. 88^(6), pp. 353–55.
H. Schmitt and H. Wittner:Z. Erzbergbau Metallhuettenwis., 1960, vol. 13(10), pp. 471–77.
W. B. Pearson:A Handbook of Lattice Spacings and Structures of Metals and Alloys, Pergamon Press, New York, NY, 1958, vol. 1, p. 956.
S. Gjerstad: Thesis, Norges Tekniske Högskole, Trondheim, 1968, 127 pp.
H. Ginsberg and V. Sparwald:Aluminum, 1965, vol. 41, pp. 181–93.
A. Prince:Alloy Phase Equilibria, Elsevier, Amsterdam, 1966, p. 207.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Oden, L.L., McCune, R.A. Phase equilibria in the Al-Si-C system. Metall Trans A 18, 2005–2014 (1987). https://doi.org/10.1007/BF02647073
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF02647073