Cutting performances and wear characteristics of WC inserts coated with TiAlSiN and CrTiAlSiN by filtered cathodic arc in dry face milling of cast iron

  • ORIGINAL ARTICLE
  • Published:
The International Journal of Advanced Manufacturing Technology Aims and scope Submit manuscript

Abstract

The aim of this work was to study the cutting performances and wear characteristics of Co-WC inserts coated with TiAlSiN and CrTiAlSiN by a filtered cathodic arc process in dry face milling of cast iron. Face milling experiments were conducted on turbine cast iron workpieces with TiAlSiN-coated, CrTiAlSiN-coated and uncoated inserts at various cutting speeds and numbers of inserts. The results showed that Ti-based coatings offered substantially better cutting performances for Co-WC inserts and could effectively protect the inserts over longer cutting lengths than uncoated ones. Specifically, the CrTiAlSiN coating offered the best cutting performances with the lowest workpiece surface roughness, the lowest flank wear rate and the longest maximum cutting length of 10 m, which was about 2.5 times as high as that of uncoated one owing to superior hardness relative to yielding and chemical properties. In addition, the workpiece quality in term of surface roughness was found to improve with increasing cutting speed in the range of 140–300 m/min and decreasing number of inserts ranging from 1 to 3. Microstructural analyses suggested that the CrTiAlSiN-coated inserts exhibited wear due to thermal cracking and partial delamination under high temperature ploughing abrasion while the TiAlSiN-coated ones displayed mainly ploughing abrasive flank wear behaviour, which resulted in a substantially lower flank wear rate than uncoated WC inserts that suffered from the combination of direct cutting and ploughing abrasive wear.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Subscribe and save

Springer+ Basic
$34.99 /Month
  • Get 10 units per month
  • Download Article/Chapter or eBook
  • 1 Unit = 1 Article or 1 Chapter
  • Cancel anytime
Subscribe now

Buy Now

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Bobzin K (2017) High-performance coatings for cutting tools. CIRP J Manuf Sci Technol 18:1–9. https://doi.org/10.1016/j.cirpj.2016.11.004

    Article  Google Scholar 

  2. Çalışkan H, Kurbanoğlu C, Panjan P, Kramar D (2013) Investigation of the performance of carbide cutting tools with hard coatings in hard milling based on the response surface methodology. Int J Adv Manuf Technol 66:883–893. https://doi.org/10.1007/s00170-012-4374-y

    Article  Google Scholar 

  3. Paller G, Matthes B, Herr W, Broszeit E (1991) Tribological properties of r.f.-sputtered titanium-based hard coatings and their behaviour under plastics-processing conditions. Mater Sci Eng A 140:647–654. https://doi.org/10.1016/0921-5093(91)90490-E

    Article  Google Scholar 

  4. Otani Y, Hofmann S (1996) High temperature oxidation behaviour of (Ti1−xCrx)N coatings. Thin Solid Films 287:188–192. https://doi.org/10.1016/S0040-6090(96)08789-5

    Article  Google Scholar 

  5. PalDey S, Deevi SC (2003) Single layer and multilayer wear resistant coatings of (Ti,Al)N: a review. Mater Sci Eng A 342:58–79. https://doi.org/10.1016/S0921-5093(02)00259-9

    Article  Google Scholar 

  6. Munz W (1986) Titanium aluminum nitride films: a new alternative to TiN coatings. J Vacuum Sci & Technol A 4:2717. https://doi.org/10.1116/1.573713

  7. Baowan P, Saikaew C, Wisitsoraat A (2017) Influence of helix angle on tool performances of TiAlN- and DLC-coated carbide end mills for dry side milling of stainless steel. Int J Adv Manuf Technol 90:3085–3097. https://doi.org/10.1007/s00170-016-9601-5

    Article  Google Scholar 

  8. Zhang B, Njora MJ, Sato Y (2018) High-speed turning of Inconel 718 by using TiAlN- and (Al, Ti) N-coated carbide tools. Int J Adv Manuf Technol 96:2141–2147. https://doi.org/10.1007/s00170-018-1765-8

    Article  Google Scholar 

  9. dos Santos JABO, Sales WF, Santos SC, Machado AR, da Silva MB, Bonney J, Ezugwu EO (2007) Tribological evaluation of TiN and TiAlN coated PM-HSS gear cutter when machining 19MnCr5 steel. Int J Adv Manuf Technol 31:629–637. https://doi.org/10.1007/s00170-005-0242-3

    Article  Google Scholar 

  10. Jiang F, Yan L, Rong Y (2013) Orthogonal cutting of hardened AISI D2 steel with TiAlN-coated inserts—simulations and experiments. Int J Adv Manuf Technol 64:1555–1563. https://doi.org/10.1007/s00170-012-4122-3

    Article  Google Scholar 

  11. Mandal P, Paul S (2013) Effect of alloyed target vis-à-vis pure target on machining performance of TiAlN coating. Int J Adv Manuf Technol 66:721–731. https://doi.org/10.1007/s00170-012-4360-4

    Article  Google Scholar 

  12. Chen L, Paulitsch J, Du Y, Mayrhofer PH (2012) Thermal stability and oxidation resistance of Ti–Al–N coatings. Surf Coat Technol 206:2954–2960. https://doi.org/10.1016/j.surfcoat.2011.12.028

    Article  Google Scholar 

  13. Vaz F, Rebouta L, Andritschky M, da Silva MF, Soares JC (1999) The effect of the addition of Al and Si on the physical and mechanical properties of titanium nitride. J Mater Process Technol 92–93:169–176. https://doi.org/10.1016/S0924-0136(99)00159-4

    Article  Google Scholar 

  14. Usana-Ampaipong T, Prapasuk S, Feung-Im K, Tuchinda K, Wathanyu K, Surinphong S, Panich N (2014) Study of interlayer element effect on properties of AlCrTiSiN thin film. Adv Mater Res 893:543–549. https://doi.org/10.4028/www.scientific.net/AMR.893.543

    Article  Google Scholar 

  15. Zheng J, Zhang SH, Wu P, Kwon SC, Li MX, Liu SY, Chen WL (2015) Microstructures and mechanical properties of duplex-treated composite ceramic coatings with and without compound layer. Ceram Int 41:2519–2526. https://doi.org/10.1016/j.ceramint.2014.10.074

    Article  Google Scholar 

  16. Zhang S, Wu W, Chen W, Yang S (2015) Structural optimisation and synthesis of multilayers and nanocomposite AlCrTiSiN coatings for excellent machinability. Surf Coat Technol 277:23–29. https://doi.org/10.1016/j.surfcoat.2015.07.033

    Article  Google Scholar 

  17. Jinlong L, Rui W, Yongxin W, Liping W (2018) Anti-oxidant mechanism of TiAlN/SiN decorative films on borosilicate glass by magnetron sputtering. Int J Adv Manuf Technol 96:1563–1569. https://doi.org/10.1007/s00170-017-0609-2

    Article  Google Scholar 

  18. Kursuncu B, Caliskan H, Guven SY, Panjan P (2018) Improvement of cutting performance of carbide cutting tools in milling of the Inconel 718 superalloy using multilayer nanocomposite hard coating and cryogenic heat treatment. Int J Adv Manuf Technol. https://doi.org/10.1007/s00170-018-1931-z

  19. Chen W, Zheng J, Lin Y, Kwon S, Zhang S (2015) Comparison of AlCrN and AlCrTiSiN coatings deposited on the surface of plasma nitrocarburized high carbon steels. Appl Surf Sci 332:525–532. https://doi.org/10.1016/j.apsusc.2015.01.212

    Article  Google Scholar 

  20. Wu ZL, Li YG, Wu B, Lei MK (2015) Effect of microstructure on mechanical and tribological properties of TiAlSiN nanocomposite coatings deposited by modulated pulsed power magnetron sputtering. Thin Solid Films 597:197–205. https://doi.org/10.1016/j.tsf.2015.11.047

    Article  Google Scholar 

  21. Inspektor A, Salvador PA (2014) Architecture of PVD coatings for metalcutting applications: a review. Surf Coat Technol 257:138–153. https://doi.org/10.1016/j.surfcoat.2014.08.068

    Article  Google Scholar 

  22. Yu D, Wang C, Cheng X, Zhang F (2009) Microstructure and properties of TiAlSiN coatings prepared by hybrid PVD technology. Thin Solid Films 517:4950–4955. https://doi.org/10.1016/j.tsf.2009.03.091

    Article  Google Scholar 

  23. He N, Li H, Ji L, Liu X, Zhou H, Chen J (2016) High temperature tribological properties of TiAlSiN coatings produced by hybrid PVD technology. Tribol Int 98:133–143. https://doi.org/10.1016/j.triboint.2016.02.034

    Article  Google Scholar 

  24. Barshilia HC, Ghosh M, Shashidhara, Ramakrishna R, Rajam KS (2010) Deposition and characterization of TiAlSiN nanocomposite coatings prepared by reactive pulsed direct current unbalanced magnetron sputtering. Appl Surf Sci 256:6420–6426. https://doi.org/10.1016/j.apsusc.2010.04.028

    Article  Google Scholar 

  25. Khanchaiyaphum S, Saikaew C, Wisitsoraat A, Surinphong S (2017) Wear behaviours of filtered cathodic arc deposited TiN, TiAlSiN and TiCrAlSiN coatings on AISI 316 stainless steel fishing net-weaving machine components under dry soft-sliding against nylon fibres. Wear 390–391:146–154. https://doi.org/10.1016/j.wear.2017.07.018

    Article  Google Scholar 

  26. Nguyen DA, Lee YR, Raghu AV, Jeong HM, Shin CM, Kim BK (2009) Morphological and physical properties of a thermoplastic polyurethane reinforced with functionalized graphene sheet. Polym Int 58:412–417. https://doi.org/10.1002/pi.2549

    Article  Google Scholar 

  27. Kim SK, Van Vinh P, Lee JW (2008) Deposition of superhard nanolayered TiCrAlSiN thin films by cathodic arc plasma deposition. Surf Coat Technol 202:5395–5399. https://doi.org/10.1016/j.surfcoat.2008.06.020

    Article  Google Scholar 

  28. Panich N, Surinphong S, Karpov DA, Tan YK, Goh CF, Ma J (2012) Mechanical properties of AlCrTiSiN coatings developed by cathodic Arc for protection applications. Solid State Phenom 185:81–83. https://doi.org/10.4028/www.scientific.net/SSP.185.81

  29. Wongpanya P, Surinphong S, Rujisomnapa J (2014) Increasing tool life by AlCrTiSiN film. Adv Mater Res 853:217–222. https://doi.org/10.4028/www.scientific.net/AMR.853.217

    Article  Google Scholar 

  30. Elosegui I, Alonso U, Lopez de Lacalle LN (2017) PVD coatings for thread tapping of austempered ductile iron. Int J Adv Manuf Technol 91:2663–2672. https://doi.org/10.1007/s00170-016-9963-8

    Article  Google Scholar 

  31. Rujisomnapa J, Surinphong S, Wongpanya P (2013) A comparative study of wear and oxidation behaviors of end mill coated by PVD coatings. Adv Mater Res 785–786:858–863. https://doi.org/10.4028/www.scientific.net/AMR.785-786.858

    Article  Google Scholar 

  32. Zitoune R, Cadorin N, Collombet F, Šíma M (2017) Temperature and wear analysis in function of the cutting tool coating when drilling of composite structure: in situ measurement by optical fiber. Wear 376–377:1849–1858. https://doi.org/10.1016/j.wear.2016.12.015

    Article  Google Scholar 

  33. Fernández-Abia AI, Barreiro J, López de Lacalle LN, González-Madruga D (2014) Effect of mechanical pre-treatments in the behaviour of nanostructured PVD-coated tools in turning. Int J Adv Manuf Technol 73:1119–1132. https://doi.org/10.1007/s00170-014-5844-1

    Article  Google Scholar 

  34. Srinivasa Prasad B, Sarcar MM (2011) Analysis of face milling operation using acousto optic emission and 3D surface topography of machined surfaces for in-process tool condition monitoring. Jordan J Mech Ind Eng 5:509–519

    Google Scholar 

  35. Chen T, Xie Z, Gong F, Luo Z, Yang Z (2014) Correlation between microstructure evolution and high temperature properties of TiAlSiN hard coatings with different Si and Al content. Appl Surf Sci 314:735–745. https://doi.org/10.1016/j.apsusc.2014.06.057

    Article  Google Scholar 

  36. Finkin EF (1974) Examination of abrasion resistance criteria for some ductile metals. J Lubr Technol 96:210–214

    Article  Google Scholar 

  37. Shi W, Zhang S, Li J, Li G, Zhang T (2017) Analysis of tool wear in face milling of alloy cast iron under constant material removal volume condition. Int J Adv Manuf Technol. https://doi.org/10.1007/s00170-017-0452-5

  38. Rao B, Shin YC (2001) Analysis on high-speed face-milling of 7075-T6 aluminum using carbide and diamond cutters. Int J Mach Tools Manuf 41:1763–1781. https://doi.org/10.1016/S0890-6955(01)00033-5

    Article  Google Scholar 

  39. Pérez RGV (2005) Wear mechanisms of WC inserts in face milling of gamma titanium aluminides. Wear 259:1160–1167. https://doi.org/10.1016/j.wear.2005.02.062

    Article  Google Scholar 

  40. Gates JD (1998) Two-body and three-body abrasion: a critical discussion. Wear 214:139–146. https://doi.org/10.1016/S0043-1648(97)00188-9

    Article  Google Scholar 

  41. Wang CY, Xie YX, Qin Z, Lin HS, Yuan YH, Wang QM (2015) Wear and breakage of TiAlN- and TiSiN-coated carbide tools during high-speed milling of hardened steel. Wear 336–337:29–42. https://doi.org/10.1016/j.wear.2015.04.018

    Article  Google Scholar 

Download references

Funding

This research is financially supported by the Office of the Higher Education Commission of Thailand and Faculty of Engineering, Khon Kaen University.

Author information

Authors and Affiliations

  1. Department of Industrial Engineering, Faculty of Engineering, Khon Kaen University, Khon Kaen, 40002, Thailand

    Sutham Siwawut & Charnnarong Saikaew

  2. National Electronics and Computer Technology Center, Pathumthani, 12120, Thailand

    Anurat Wisitsoraat

  3. NanoShield PVD Hard Coating Co., Ltd., Samutprakarn, 10560, Thailand

    Surasak Surinphong

Authors
  1. Sutham Siwawut
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Charnnarong Saikaew
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Anurat Wisitsoraat
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Surasak Surinphong
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Charnnarong Saikaew.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Siwawut, S., Saikaew, C., Wisitsoraat, A. et al. Cutting performances and wear characteristics of WC inserts coated with TiAlSiN and CrTiAlSiN by filtered cathodic arc in dry face milling of cast iron. Int J Adv Manuf Technol 97, 3883–3892 (2018). https://doi.org/10.1007/s00170-018-2200-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00170-018-2200-x

Keywords

Search

Navigation