Abstract
ZnO-nanorods/graphene heterostructure was synthesized by hydrothermal growth of ZnO nanorods on chemically reduced graphene (CRG) film. The hybrid structure was demonstrated as a biosensor, where direct electron transfer between glucose oxidase (GOD) and electrode was observed. The charge transfer was attributed to the ZnO nanorod wiring between the redox center of GOD and electrode and the ZnO/graphene heterostructure facilitated the transport of electrons on the hybride electrode. The glucose sensor based on the GOD-ZnO/CRG/Pt electrode had a high sensitivity of 17.64âμAâmMâ1, which is higher than most of the previously reported values for direct electron transfer based glucose biosensors. Moreover, this biosensor is linearly proportional to the concentration of glucose in the range of 0.2â1.6âmM. The study revealed that the band structure of electrode could affect the detection of direct electron transfer of GOD, which would be helpful for the design of the biosensor electrodes in the future.
Similar content being viewed by others
Introduction
In recent years, amperometric glucose biosensors have attracted intensive attention and have been extensively studied because of their important applications in healthcare, food industry, chemical and biological analysis1,2,3,4,5. In an amperometric glucose biosensor, electron transfer between glucose oxidase (GOD) and electrodes can be realized by redox mediators or direct electron transfer (DET)6. Because redox mediators based biosensors have many critical limitations, such as high cost, potential cytotoxicity and low selectivity7, direct electrochemistry biosensor is considered to be the choice of next generation of biosensor for its reversible nature and low interference resulted from its low redox potential8. However, it still remains a challenge to achieve direct electrochemistry of most redox enzymes on bare solid electrodes because redox centers of the enzymes are deeply buried in the proteins and the biological matrix is instable upon interaction with the electrode surface7,9. Nanostructured materials have shown great potential for direct electron transfer because some of them may wire between the redox center of enzymes and the electrodes10,11,12,13,14,15.
Graphene possesses a large specific surface area (up to 2630âm2â·âgâ1) to accommodate abundant biomolecule loadings and shows the potential to impart excellent bio-detection sensitivity. The high conductivity and small bandgap features of graphene facilitate the electron transfer between the biomolecules and graphene surface16. On the other hand, nanostructured ZnO is also an excellent candidate for biosensor materials due to its high surface area, low toxicity, good chemical stability and biological compatibility and high electron mobility17,18,19. Moreover, ZnO has a high isoelectric point (IEP) about 9.5, which makes it suitable for absorption of GOD primarily driven by electrostatic interaction20,21. Up to date, some with low IEP about 4.2 in the physiological pH, because the enzyme immobilization is primarily driven by electrostatic interaction. ZnO-nanostructure-based glucose sensors have been reported22,23,24,25,26, but only a few works have been reported on the direct electrochemistry of GOD immobilized on ZnO/graphene hybrid nanocomposites27,28,29,30. Moreover, to the best of our knowledge, there are no literature that is published to illustrate which kinds of metal oxides based composite materials favor the DET process from the consideration of band gap and work function of heterostructured electrodes.
In this paper, ZnO-nanorods/graphene heterostructure was prepared by growing ZnO nanorods on chemically reduced graphene (CRG) film. Direct electron transfer behavior was observed on the GOD immobilized ZnO-nanorods/graphene heterostructure, in sharp contrast to ZnO nanorods directly grown on Pt electrode and graphene/Pt electrode, for which no signal of direct electron transfer were presented. We find that not only the morphology31 but also the electronic band structure of functional material electrode affect the detection of direct electron transfer. Furthermore, the redox reversibility of GOD and surface controlled electrochemical process on the ZnO-nanorods/graphene heterostructure reveal its potential application for the redox-mediator-free biosensors.
Results
Figure 1 showed typical SEM and TEM images of the ZnO-nanorods/graphene heterostructure. As shown in Fig. 1a, the top-image of SEM indicated that the ZnO nanorod arrays were produced on graphene with high uniformity and packing density, consistent with the cross-sectional SEM image as shown as Fig. 1b. The thickness of the CRG film was estimated to be about 450â600ânm. TEM image further confirmed the heterostructure of ZnO-nanorods/graphene, as shown as Fig. 1c. Figure 1d shows a single ZnO nanorod obtained by crushing the sample up by sonication. The diameter of the nanorod is about 30ânm with length about 150ânm. The HRTEM image shown in Fig. 1e indicated that the nanowire was high crystalline with a lattice spacing of 0.26ânm, which corresponded to the (002) plane in the ZnO crystal lattice (PCPDF #89-1397). Note the ZnO nanorods had a rough surface (Fig. 1d,e), which may be favorable for immobilization of GOD and wiring the proteins.
The XRD patterns of the ZnO-nanorods/graphene heterostructure and CRG film were presented in Supplementary Fig. S3. One broad reflection peak centered around 2θâ=â25° was observed in the XRD pattern of CRG, which can be correlated to an interlayer spacing of 0.36ânm in the graphene. All diffraction peaks in the range 30°â<â2θâ<â60° for the ZnO/CRG heterostructure can be indexed to the hexagonal wurtzite structured ZnO with lattice constants aâ=â0.325ânm and câ=â0.521ânm, which are in good agreement with the values provided by the standard JCPDS card (JCPDS 36-1451) database. As shown as Supplementary Fig. S4, the PL spectrum shows a strong peak at 382ânm for the sample of ZnO-nanorods/graphene heterostructure, which is in consistence with the band edge emission of ZnO.
Fourier transform infrared spectroscopy of pure GOD, as-prepared ZnO nanorods and GOD-fixed ZnO nanorods confirmed the strong interaction between the ZnO nanorods and GOD molecules, as shown as Fig. 2â32. For pure GOD, there are some characteristic absorption bands of GOD, typical amide I absorption band round 1648âcmâ1 and amide II absorption near 1544âcmâ1. The ZnO nanorods exhibit obvious absorption band at 1382âcmâ1, which attributes to the symmetrical vibration of âCOOâ, suggesting acetic ions are adsorbed on the surface of ZnO nanorods which came from acetic zinc used in the preparation33. After dropping GOD and Nafion solution, the two absorption bands of amide are appear in the IR spectrum of the ZnO nanorods, which demonstrate that GOD molecules are effectively supported on the surface of ZnO nanorods.
The electrochemistry performances were all measured at 30â°C. Figure 3a shows cyclic voltammograms (CV) of GOD ZnO-nanorods/graphene heterostructure and the control samples of GOD-CRG film and GOD-ZnO nanorod/Pt electrode in N2-saturated 0.2âM PBS solution (pHâ=â5.8). A pair of well-defined redox peaks was observed in the curve of ZnO/CRG (Curve a), indicating direct electron transfer between GOD and ZnO/CRG. The formal potential calculated by averaging the cathodic and anodic peak potentials was estimated to be ~â0.39âV (vs SCE), with ~61âmV peak-to-peak separation. From scan rates of 10 to 200âmVâsâ1, the cathodic peak current (Ipc) and anodic peak current (Ipa) increase linearly with the scan rate increase (Inset of Fig. 3b). This is attributed to the reversible surface control of GOD electrochemical reaction. According to Lavironâs equation for a surface-controlled electrochemical system (ÎEpâ<â200/nâmV)23,
where m is a parameter related to the peak-to-peak separation and is calculated to be 0.60, n is the transferred electrons number which is assumed to be two, F is the Faraday constant, v is the scan rate, R is the gas constant and T is the temperature. The apparent heterogeneous electron transfer rate constant (ks) was estimated to be 0.92âSâ1, suggesting the direct electron transfer of GOD had good reversibility. The effect of scan rate on the electrochemical response of the immobilized GOD is shown in Fig. 3b. The redox peak current scaled linearly to the scan rate between 10 to 200âmVâsâ1 (Fig. 3b inset). Meanwhile the cathodic and anodic peak potentials showed a small shift and ÎEp was also gradually increased. All these characteristics suggested that the direct electron transfer between GOD and ZnO could be easily performed on the ZnO-nanorods/graphene heterostructure and it was a surface-controlled electrochemical process34. Electrochemical measurements have also been performed on the controls of CRG film and ZnO nanorods/Pt, as shown as Fig. 3a (Curve b and c, respectively). No redox peaks were found in the controls, indicating that no direct electron transport was detected on the both samples.
Discussion
The morphology of ZnO nanorods favors for the immobilization of GOD and detection of direct electronic transfer. It is well known that the active redox center of GOD is deeply embedded in a protective protein shell, which makes the direct electron transfer between GOD and electrode difficult to realize. We suggested that the nanoscale size and the accidented surface of ZnO nanorods facilitate the immobilization of GOD and wiring its redox center with the electrode. When GOD was dropped onto the surface, the protein was immobilized on ZnO by electrostatic interaction. The rough surface of the ZnO nanorods, as shown as Fig. 1d,e, should favor the absorption of GOD on ZnO nanorods and reduce the distance between the active redox center and surface of ZnO, facilitating the direct electron transfer process.
The proper energy level alignment of ZnO/graphene heterostructure was critical to the detection of the electron transport signals. Note that no direct electrochemistry was detected for the control of ZnO-nanorods/Pt electrode, as shown in Fig. 3a. The band structures of the electrode interfaces are shown in Fig. 4. ZnO has a wide band gap about 3.37âeV and the work function (W) of eigen-state ZnO, graphene and Pt are 5.3âeV35, 4.42âeV36 and 5.65âeV37, respectively. Figure 4a,b show the band structure before and after contact of ZnO-nanorods and graphene film. In the ZnO/graphene heterostructure, the energy band of ZnO was bent downward because the work function of ZnO was higher than that of CRG (WZnOâ>âWCRG) and an electron anti-blocking layer was formed. As a result, the heterostructure would be favorable for the electron transport from GOD-ZnO to the electrode. In contrast, for the electrode structure of ZnO-nanorods grown on Pt electrode directly, the band structure before and after contact of ZnO and Pt is shown in Fig. 4c,d. The energy band of ZnO/Pt was bent upward, because the work function of ZnO is smaller than that of Pt (WZnOâ<âWPt). As a result, a Schottky barrier about 0.35âeV was formed, which blocked the electron transport from the ZnO nanorods to the Pt electrode. In addition, most of the ZnO are n-doped, its actual work function will be smaller than intrinsic ZnO and the barrier should be larger than 0.35âeV, implying that electron would be more difficult to transfer from ZnO to Pt electrode. All of these indicate that the heterostructure of ZnO/CRG facilitates the electron transfer from ZnO to electrode and favors for the detection of direct electrochemical signal of enzyme.
Furthermore, we demonstrated the heterostructure of ZnO/CRG as glucose sensors. The measurement was conducted in 0.2âM PBS solution with different concentrations of glucose saturated with O2. Figure 5 shows the CV curves of GOD-ZnO/CRG/Pt electrode. When the concentration of glucose is gradually increased from 0.2 to 1.6âmM, the calibration curve corresponding to the amperometric response is almost linearly dependent on the concentration of glucose with a correlation coefficient (R) at 0.998. The sensitivity calculated from the linear portion of the calibration is 17.64âμAâmMâ1, i.e., 89.84âμAâmMâ1âcmâ2, which is higher than most of the previously reported values for direct electron transfer based glucose biosensors13 and could be used for detecting the glucose content in the body fluid, such as perspiration and tears.
The GOD-ZnO/CRG/Pt electrode also exhibits excellent selectivity for glucose detection. As shown in Fig. 6a, the addition of interferents, e.g., 0.3âmM of ascorbic acid (AA) and 0.3âmM of uric acid (UA), in 0.1âM PBS containing 0.3âmM of glucose gives rise to small current changes, while a significant current response can be found for the subsequent addition of 0.6âmM of glucose. The response time is less than 3âs. To assess its stability, the GOD-ZnO/CRG/Pt electrode was stored at 4â°C after use and used to measure the current response for 0.3âmM of glucose every two days. The GOD-ZnO/CRG/Pt electrode retains 92% of its original current response over a storage period of 2 weeks (Fig. 6b), indicating a good shelf lifetime for the modified electrode.
Conclusions
In summary, a heterostructure of ZnO and CRG has been obtained by hydrothermal growth of ZnO nanorods on CRG film and was used as GOD immobilization electrode. Direct electrochemistry of GOD was achieved on heterostructure electrode. The properly aligned band structure of the ZnO/CRG heterostructure promoted the electron transfer from GOD-ZnO to electrode and favored for the detection of the direct electrochemistry signal between GOD and ZnO-nanorods. Moreover, the heterostructure showed potential for glucose sensing. The study demonstrated for the first time that Pt can be used as electrode in ZnO based DET glucose biosensors and revealed that the band structure of electrode could influence the performance of direct electron transfer of GOD and modulating the band structure would be helpful for the future design of electrodes in biosensors.
Materials and Methods
Synthesis and characterization of ZnO-nanorod/graphene heterostructure thin film
The heterostructure was prepared by hydrothermal growth of ZnO nanorods on CRG film. CRG was synthesized according to previously reported method22. The thin film of CRG was obtained by filtering method, which was then transferred onto a SiO2 substrate. Then, zinc acetate was spray-coated onto the CRG film by using an air brush with 10âmM zinc acetate/ethanol solution, with the substrate temperature at about 80â°C. Finally, ZnO nanorods were grown on the film in a solution containing equimolar concentrations (30âmM) of zinc nitrate hexahydrate (Zn(NO3)2â·â6H2O) and hexamethylenetetramine (C6H12N4, HMTA) at 90â°C for 1âh. The ZnO-nanorods/graphene heterostructure was characterized by scanning electron microscopy (SEM, JSM-7000F), transmission electron microscopy (TEM, JEM-2100), X-ray diffraction (XRD, XRD-6000, Cu Kα radiation) and photoluminescence spectra (PL, HR800, 325ânm). Fourier transform infrared spectroscopy (FT-IR) were recorded on a NEXUS870 spectrophotometer (USA).
Biosensor device and electrochemical testing
To fabricate the glucose biosensor, the ZnO-nanorods/graphene film was transferred onto a standard Pt electrode with a diameter of 5âmm. ZnO nanorods directly grown on Pt electrode and graphene thin film on Pt electrode were taken as the controls. GOD solution was prepared by dissolving 40âmg GOD (~140âUâmgâ1) in 1âml 0.02âM phosphate buffer solution (PBS). 20âμl GOD solution was dropped onto the electrode surface for immobilization and dried under ambient condition. Then, 10âμl 5% (w/w) Nafion solution was dropped onto it and dried overnight at room temperature. All the electrochemical experiments were conducted on electrochemical workstation (CHI 660C), using conventional three-electrode electrochemical system with saturated calomel electrode (SCE) and platinum wire as the reference and counter electrodes, respectively.
Additional Information
How to cite this article: Zhao, Y. et al. ZnO-nanorods/graphene heterostructure: a direct electron transfer glucose biosensor. Sci. Rep. 6, 32327; doi: 10.1038/srep32327 (2016).
References
Rakow, N. A. & Suslick, K. S. A colorimetric sensor array for odour visualization. Nature 406, 710â713 (2000).
Ang, L. F., Por, L. Y. & Yam, M. F. Development of an Amperometric-Based Glucose Biosensor to Measure the Glucose Content of Fruit. Plos One 10, e0111859 (2015).
Lin, Y., Lu, F., Tu, Y. & Ren, Z. Glucose Biosensors Based on Carbon Nanotube Nanoelectrode Ensembles. Nano Lett. 4, 191â195 (2004).
Li, L., Shi, Y., Pan, L., Shi, Y. & Yu, G. Rational design and applications of conducting polymer hydrogels as electrochemical biosensors. J. Mater. Chem. B 3, 2920â2930 (2015).
Zhai, D. et al. Highly Sensitive Glucose Sensor Based on Pt Nanoparticle/Polyaniline Hydrogel Heterostructures. ACS Nano 3540â3546 (2013).
Ghindilis, A. L., Atanasov, P. & Wilkins, E. Enzyme-catalyzed direct electron transfer: Fundamentals and analytical applications. Electroanalysis 9, 661â674 (1997).
Holland, J. T., Lau, C., Brozik, S., Atanassov, P. & Banta, S. Engineering of glucose oxidase for direct electron transfer via site-specific gold nanoparticle conjugation. J. Am. Chem. Soc. 133, 19262â19265 (2011).
Armstrong, F. A., Hill, H. A. O. & Walton, N. J. Direct electrochemistry of redox proteins. Acc. Chem. Res. 21, 407â413 (1988).
Xiao, Y., Patolsky, F., Katz, E., Hainfeld, J. F. & Willner, I. âPlugging into enzymesâ: nanowiring of redox enzymes by a gold nanoparticle. Science 299, 1877â1881 (2003).
Zhang, L. et al. A polyaniline microtube platform for direct electron transfer of glucose oxidase and biosensing. J. Mater. Chem. B 3, 1116â1124 (2015).
Gao, R. & Zheng, J. Amine-terminated ionic liquid functionalized carbon nanotube-gold nanoparticles for investigating the direct electron transfer of glucose oxidase. Electrochem. Commun. 11, 608â611 (2009).
Wu, W., Huang, J. & Tsai, Y. Direct electron transfer and biosensing of glucose oxidase immobilized at multiwalled carbon nanotube-alumina-coated silica modified electrode. Mater. Sci. Eng. C 32, 983â987 (2012).
Mutyala, S. & Mathiyarasu, J. Direct electron transfer at a glucose oxidase â chitosan-modified vulcan carbon paste electrode for electrochemical biosensing of glucose. Appl. Biochem. Biotechnol. 172, 1517â1529 (2014).
Moumene, M., Rochefort, D. & Mohamedi, M. Electrochemical functionalization as a promising avenue for glucose oxidase immobilization at carbon nanotubes: enhanced direct electron transfer process. Int. J. Electrochem. Sci. 8, 2009â2022 (2013).
Guo, C. X. & Li, C. M. Direct electron transfer of glucose oxidase and biosensing of glucose on hollow sphere-nanostructured conducting polymer/metal oxide composite. Phys. Chem. Chem. Phys. 12, 12153â12159 (2010).
Vashist, S. K. & Luong, J. H. T. Recent advances in electrochemical biosensing schemes using graphene and graphene-based nanocomposites. Carbon 84, 519â550 (2014).
Yakimova, R. ZnO materials and surface tailoring for biosensing. Front. Biosci. E4, 254 (2012).
Ahmad, M., Pan, C., Gan, L., Nawaz, Z. & Zhu, J. Highly sensitive amperometric cholesterol biosensor based on Pt-incorporated fullerene-like ZnO nanospheres. J. Phys. Chem. C 114, 243â250 (2010).
Arya, S. K. et al. Recent advances in ZnO nanostructures and thin films for biosensor applications: Review. Anal. Chim. Acta 737, 1â21 (2012).
Zhao, Z., Lei, W., Zhang, X., Wang, B. & Jiang, H. ZnO-based amperometric enzyme biosensors. Sensors 10, 1216â1231, doi: 10.3390/s100201216 (2010).
Hu, F. et al. Enzymatic ZnO nanoparticle and multiwalled carbon nanotubes for glucose oxidase direct electron transfer and electrocatalytic activity investigation. J. Mol. Catal. B, Enzym. 72, 298â304 (2011).
Zhu, X., Yuri, I., Gan, X., Suzuki, I. & Li, G. Electrochemical study of the effect of nano-zinc oxide on microperoxidase and its application to more sensitive hydrogen peroxide biosensor preparation. Biosens. Bioelectron. 22, 1600â1604 (2007).
Wei, A. et al. Enzymatic glucose biosensor based on ZnO nanorod array grown by hydrothermal decomposition. Appl. Phys. Lett. 89, 123902 (2006).
Weber, J., Jeedigunta, S. & Kumar, A. Fabrication and characterization of ZnO nanowire arrays with an investigation into electrochemical sensing capabilities. J. Nanomater, doi: 10.1155/2008/638523 (2008).
Wang, J. X. et al. Zinc oxide nanocomb biosensor for glucose detection. Appl. Phys. Lett. 88, 233106 (2006).
You, X. et al. Zinc oxide inverse opal enzymatic biosensor Zinc oxide inverse opal enzymatic biosensor. Appl. Phys. Lett. 102, 253103 (2014).
Liu, J. et al. Electrochemistry communications carbon-decorated ZnO nanowire array: a novel platform for direct electrochemistry of enzymes and biosensing applications. Electrochem. Commun. 11, 202â205 (2009).
Dai, Z., Shao, G., Hong, J., Bao, J. & Shen . Immobilization and direct electrochemistry of glucose oxidase on a tetragonal pyramid-shaped porous ZnO nanostructure for a glucose biosensor. Biosens. Bioelectron. 24, 1286â1291 (2009).
Zhai, Y. et al. Effects of morphology of nanostructured ZnO on direct electrochemistry and biosensing properties of glucose oxidase. J. Electroanal. Chem. 656, 198â205 (2011).
Palanisamy, S., Vilian, A. T. E. & Chen, S. Direct electrochemistry of glucose oxidase at reduced graphene oxide/zinc oxide composite modified electrode for glucose sensor. Int. J. Electrochem. Sci. 7, 2153â2163 (2012).
Wei, A. et al. Enzymatic glucose biosensor based on ZnO nanorod array grown by hydrothermal decomposition. Appl. Phys. Lett. 123902, 28â31 (2016).
Vinu, A., Miyahara, M. & Ariga, K. Biomaterial Immobilization in Nanoporous Carbon Molecular Sieves: Influence of Solution pH, Pore Volume and Pore Diameter. J. Phys. Chem. B 109, 6436 (2005).
Liu, X. et al. Aligned ZnO nanorods: A useful film to fabricate amperometric glucose biosensor. Colloid Surface B 74, 154â158 (2009).
Wu, B. S., Ju, H. & Liu, Y. Conductive mesocellular silica â carbon nanocomposite foams for immobilization, direct electrochemistry and biosensing of proteins Adv. Funct. Mater. 17, 585â592 (2007).
Minami, T., Miyata, T. & Yamamoto, T. Work function of transparent conducting multicomponent oxide thin films prepared by magnetron sputtering. Surf. Coat. Technol. 109, 583â587 (1998).
Guo, C. X. et al. Layered graphene/quantum dots for photovoltaic devices. Angew. Chem. Int. Ed. 49, 3014â3017 (2010).
Michaelson, H. The work function of the elements and its periodicity. J. Appl. Phys. 48, 4729 (1977).
Acknowledgements
Y.Z., L.P. and Y.S. are grateful for funding support from the Chinese National Key Fundamental Research Project (2013CB932900, 2011CB92210), the National Natural Science Foundation of China (61229401, 61076017, 41401257, 60990314), Natural Science Foundation of Jiangsu Province of China (BK20141054) and the PAPD Programs.
Author information
Authors and Affiliations
Contributions
W.L., Y.Z., W.Y., Y.W., D.Z. and W.C. carried out the preparation and characterization experiments. Y.Z., W.L., D.Z. and L.L. performed the electrochemical measurements. Y.Z., W.L., L.P., Y.S. and J.-B.X. wrote the manuscript. X.W. contributed to analysis the experimental data. All authors discussed the results and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the articleâs Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Zhao, Y., Li, W., Pan, L. et al. ZnO-nanorods/graphene heterostructure: a direct electron transfer glucose biosensor. Sci Rep 6, 32327 (2016). https://doi.org/10.1038/srep32327
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep32327
This article is cited by
-
A direct electrochemical biosensor for rapid glucose detection based on nitrogen-doped carbon nanocages
Rare Metals (2024)
-
Simple synthesis of ZnO 3D-hierarchical nanostructures by microfluidics process
Journal of Materials Science: Materials in Electronics (2022)
-
ZnO-based electrochemical sensors for highly sensitive and selective detection of gallic acid at impact of substrate temperature
Applied Physics A (2021)
-
Photo sensitizing and electrochemical performance analysis of mixed natural dye and nanostructured ZnO based DSSC
SÄdhanÄ (2020)
-
Fabrication of amperometric sensor for glucose detection based on phosphotungstic acidâassisted PDPA/ZnO nanohybrid composite
Ionics (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.