Abstract
Vast experiments have demonstrated that the external specimen size makes a large difference in the deformation behavior of crystalline materials. However, as one important kind of internal planar defects, the role of grain boundary (GB) in small scales needs to be clarified in light of the scarce and inconsistent experimental results at present. Through compression of Cu bicrystal and its counterpart monocrystal micropillars, it is found that, in contrast to the monocrystals, the bicrystals are characterized by work hardening with discrete strain bursts. Interestingly, the stress rise between two adjacent strain bursts of the bicrystals increases with the decrease of specimen size. The results suggest that GBs play a critical role in the work hardening of materials in small scales, which may provide important implications to further understand the general work hardening behaviors of materials in the future.
Similar content being viewed by others
Introduction
Both the internal sizes of the microstructural units and the external sizes of the specimens govern the mechanical properties of materials in micro and smaller scales simultaneously1,2,3. In recent years, materials in small scales have been investigated a lot by applying micromechanical tests to the specimens fabricated by focus ion beams (FIB) milling method2. Investigations on monocrystal pillars reveal that the strength increases with the decrease of the sample size due to the geometrical constraints on the dislocation nucleation and motion4,5,6. In addition, the deformation in small scales is characterized by discrete strain burst2,7 and low hardening rate even up to large strains2,8. Generally speaking, conventional strain hardening in bulk materials is invalid in the specimen with limited volumes since the dislocation density does not grow significantly with strain9.
Grain boundary (GB) is an important kind of internal planar defects in crystalline materials. By working as sinks, sources or obstacles to lattice dislocations, the GBs always play a crucial role in the mechanical properties of polycrystalline metals10. The GBs are opaque to dislocation motion and it was proposed by Hall and Petch that decreasing grain sizes would effectively increase the yield strength of materials11,12. Moreover, the GBs could improve the initial work hardening behavior of bulk materials by providing back stress to dislocations13,14,15. On the other hand, the GB-mediated deformation in the way of grain rotation and GB sliding can become prominent when the average grain size is below some critical value16,17. Beyond bulk materials, the role of GBs in small scales has also been investigated via nanocrystal, multi-crystal or bicrystal pillars in micro or nano scale in recent years7,18,19,20,21,22. However, there is large scatter of the experimental results of pillars with GBs under compression. The strength of nanocrystal pillars may increase or decrease as a function of the extrinsic specimen size19,22. Wherein, the weakening effect is likely due to the activation of GB-mediated processes22; instead, the strength significantly rises when twin boundaries (TBs) are present to greatly impede dislocation glide19.
In the previous studies, polycrystalline aggregates were mainly employed and the existence of numerous GBs makes it difficult to distinguish the intrinsic role of individual boundary. To overcome this drawback, bicrystals with an individual GB were employed. Direct evidence has been offered to show that high-angle GBs have low resistance to fatigue cracking and serve as the preferential fatigue cracking sites23, while the TBs have variable and tunable fatigue cracking behaviors24. However, the GB effect is not remarkable in tension or compression behaviors of bulk Cu bicrystals as a result of the quite low GB fraction. In micro or smaller scales, the fraction is so high that the GBs can strongly influence the deformation behaviors of the bicrystals by interacting with lattice dislocations. Earlier studies indicated that the GB could work as a dislocation trap to induce strengthening or smoothening effects of the bicrystal micropillars18,20,21. On the contrary, the GB was reported to work as a dislocation sink to contribute to the intermittent strain bursts and decreasing the work hardening degree of Al bicrystal nanopillars7. The divergences might be derived from different GB characters25,26, inclination angles27 or specimen sizes7,21. It could be seen that GBâs role in the deformation behaviors of the bicrystal pillars in small scales has not been thoroughly understood, including the work hardening behaviors, which needs to be further clarified with more studies.
Micro-compression tests were deliberately designed in this investigation with a series of Cu bicrystal and the two counterpart monocrystal micropillars. Here we present that the bicrystals deform more homogeneously than the monocrystals and are characterized by stepwise work hardening behavior. Moreover, it is interesting to find that the stress increase between two adjacent strain bursts of the bicrystals is inversely proportional to the specimen size. The GB could provide restrict to the annihilation and operation of dislocations which gives rise to the specific deformation and work hardening behaviors of the bicrystal micropillars.
Results
The two monocrystal pillars were named as SC1 and SC2 respectively, while the bicrystal pillar was named as BC. The crystallographic orientations of SC1 and SC2 are <345> and <136>, respectively. Representative compressive stress-strain curves for monocrystal and bicrystal micropillars with the sizes of 1âμm, 5âμm and 10âμm are displayed in Fig. 1. Obviously, all these micropillars are much stronger than their bulk counterparts. Besides, the smaller the specimen size is, the larger scatter the datum shows. As to the monocrystal pillars, the flow stress increases as the specimen size decreases, indicating a strong sample size effect analogous to the former studies28,29. The yield stresses of the two monocrystal pillars are different ascribed to their different loading directions30. During the compression, monocrystal pillars exhibited a short period of elastic loading firstly and a catastrophic plastic flow event with a little stress drop subsequently. The instable plastic flow continued for a long strain regime which may be closely concerned with the avalanche-like motion of dislocations31. Moreover, there is no work hardening of monocrystal pillars similar to the former works2,4,32.
The stress-strain curves are correlated with the characteristic deformation morphologies. Surface observations of the deformed monocrystal micropillars with different diameters are displayed in Fig. 2. Wherein, Fig. 2aâc represent the SC1 monocrystals, while Fig. 2dâf represent the SC2 monocrystal pillars, respectively. In general, strongly localized slip bands (SBs) with significant shear offsets are prevalent on the sample surface since the dislocations could easily escape from the crystals to the free surface2,32. Different slip systems operated in the two monocrystal pillars attributed to their different orientations. In addition, as shown in Fig. 2e, a secondary slip system operated in the SC2 monocrystal pillars, which might be related to the fact that the its Schmid factor is close to the highest one. In addition, multiple slip systems could be activated in micro scale8,32 and simulations show that the dominance of the maximum Schmid-factor system drops as the specimen size decreases33,34. Although both the primary and secondary SBs were activated in the SC2 monocrystal pillars, they had no intersection with each other so as not to facilitate the work hardening behavior.
For the bicrystal pillars, however, they exhibited distinct features from the monocrystal pillars in both the stress-strain curves and deformation morphologies. It could be seen from Fig. 1a that the flow stress also increases in a âsmaller is strongerâ fashion for the bicrystal micropillars as observed in the nano and micro bicrystal pillars before7,18. Different from the two monocrystal pillars, the stress-strain curves of the bicrystals are composed of many regular strain bursts which are separated by elastic loading segments. Each strain burst continued at nearly the same stress level and the subsequent strain burst occurred at a higher stress level. That is, the flow stress of the bicrystals increases in a stepped mode exhibiting a distinct work hardening feature.
The representative deformation morphologies of the bicrystal micropillars are displayed in Fig. 3. Figure 3aâc demonstrate BC pillars with sizes of about 1âμm, 5âμm and 10âμm, respectively. Different SBs operated in the two component grains due to the different grain orientations and all of them ceased at the GB. Besides, there are also some secondary SBs showed up due to the strain or stress incompatibility35 and intersected with the primary SBs as shown in Fig. 3a. The secondary SBs usually arise in the vicinity of the GB in bulk materials, nevertheless, the SBs distributed through the entire grain on one side of the GB due to the size limit at present. Comparatively speaking, the deformation of the bicrystal pillars is undertaken by SBs which distributed more homogeneously and widely than those in monocrystal pillars. The height of the slip steps on the surface of bicrystal pillars is obviously lower than that of monocrystal pillars. In addition, Fig. 3d is an enlarged image of local position from Fig. 3b. It could be observed that there is a shear step formed along the GB which may arise from the deformation incompatibility between the two component grains. It has been proposed that frictional sliding along the GB plane served as the dominant deformation mechanism in Al nano-bicrystals27. There might also be little GB sliding in the present bicrystals since there should be resolved shear stress along the present GB which is not perfectly parallel to the loading direction. More studies on the investigation of the GB sliding behavior are still underway.
Discussion
Based on the above results, the two monocrystal pillars show stress-strain curves of the same characteristics without work hardening. During the compression, the stressed area of monocrystal pillar decreases with the compressive strain since the deformation is highly localized in the SBs, as illustrated by the insets in Fig. 4a. Based on the scanning electron microscope (SEM) observation, the actual stressed area was measured and the flow stress was amended. The flow stress increased a little, but not enough to appear as work hardening in the present strain range. As shown in Fig. 4b, the true stress of the bicrystal pillars can be considered as equal to the engineering stress in the present strain range, since the stressed area did not change much due to the homogeneous deformation. Compared with monocrystal pillars, there is definite work hardening behavior of bicrystal pillars.
The value of macroscopic shear strain γ is related to the density of mobile dislocations Ï and their travel distance with the Orowanâs equation36: . For monocrystal pillars, due to the low initial dislocation density9,37, high stress is required to nucleate sufficient dislocations to sustain the shear strain38,39. It is the same case in the bicrystal pillars and hence the yield strength is also higher than bulk counterparts due to the low initial dislocation density in the limited specimen size. In the following deformation process, different dislocation behaviors occur in the monocrystals and bicrystals. The deformed bicrystal and monocrystal pillars with the size of 5âμm were milled into longitudinal thin-foil sections for transmission electron microscopy (TEM) examination.
The dislocation configuration of the <136> monocrystal pillar with the nominal strain of ~8.4% is shown in Fig. 5a while the dislocation configurations in the two component grains of the bicrystal pillars with the nominal strain of ~4.7% are exhibited in Fig. 5b,c. The Burgers vector of the dislocations in Fig. 5c was determined to be which belongs to the primary slip system with the highest Schmid factors. Meanwhile, the Burgers vectors of the dislocations in Fig. 5a,b were determined to be which belongs to the secondary slip systems indicating that the Schmidâs law may break down in small scale33,34. In general, the dislocation density should be higher with higher strain. However, the dislocation density of the compressed bicrystal is a little higher than that in the monocrystal, while they are estimated to be in the same order of 1014/m2. Wherein, the dislocation density was measured by the line-intercept method8,40. Therefore, it could be deduced that the dislocations can readily zip through the monocrystal specimen and annihilate at the surface leading to the low dislocation density. It has been revealed previously that the dislocation density of the monocrystal micropillars did not increase significantly after serious deformation by in-situ and ex-situ TEM investigations5,9. Thus, in the monocrystal pillars, dislocations have low chance to interact with each other5,9,41 and thus work hardening is absent as shown by the sketch map in Fig. 4a.
On the other hand, one end of some dislocations is usually pinned by the GB as shown in Fig. 5b,c. That is, the GB can provide obstruction to dislocation annihilation which leads to the global higher dislocation density than monocrystal. Additionally, take the red line in Fig. 5b as a dividing line, the dislocations distribute more densely when approaching to the GB which implies that the dislocations could pile up at the GB. During deformation, mobile dislocations could pile up at GBs or annihilate at surface, so new dislocations should be nucleated and emitted to sustain the following plastic deformation. As reflected by the stress-strain curves in Fig. 4b, during each strain burst, the activated dislocations slip through the grain and then are blocked by the GB leading to exhaustion of mobile dislocations. Afterwards, stress rise is needed to activate new dislocations38,41,42 to produce the subsequent strain burst which provides the major contribution to the work hardening behavior of bicrystal pillars.
The amplitudes of the stress rise ÎÏ (illustrated by the inset in Fig. 6) for the bicrystal micropillars are collected and analyzed. It is found that ÎÏ is very concentrated for the bicrystal pillars with the same size. Then the amplitudes of stress rise for the bicrystal pillars with all the sizes (1âμm, 5âμm and 10âμm) are collected and listed in Fig. 6. It is clear that the stress rise amplitude ÎÏ is proportional to dâ1.29, exhibiting a strong size effect. As shown by the stress-strain curves in Fig. 1, differences exist between the yield stresses of the two monocrystal pillars with the same size, which are estimated to be 24.5â±â0.3âMPa for the 10âμm pillars, 49.8â±â5.5âMPa for the 5âμm pillars and 4.3â±â7.7âMPa for the 1âμm pillars. Obviously, yield stresses scatter largely when the pillar size is reduced to 1 μm. However, these differences in the yield strength are quite different from the corresponding ÎÏ, which are about 3.2âMPa, 8.8âMPa and 63.2âMPa for 10âμm, 5âμm and 1âμm pillars, respectively. Therefore, ÎÏ is more closely related to the existence of GB than to the orientation differences between the two monocrystal counterparts.
In bulk polycrystals, the dislocations piled up or stored at the GB will contribute to the building up of back stresses13,15. At low strain level, the strengthening effect of GB increases evidently with decreasing the grain size13,14. It is conceivable that the GB back stress Ï exerted on a source could be one reason for the dislocation immobilization. The back stress Ï could be calculated by43:
where in, ν is Poissonâs ratio, μ is shear modulus, b is the magnitude of the Burgers vector. The separation x between source and GB should be proportional to the specimen size44 and it is assumed to be about half of the pillarâs size. The back stress exerted on each dislocation in the pilling-up, i.e., the stress rise ÎÏâ² needed to release one dislocation in the pilling-up can be estimated from Eq. (1) as below:
It is obvious that both ÎÏâ² and ÎÏ increase with the decrease of the specimen size, but in different ways: ÎÏâ² is proportional to dâ1 while ÎÏ is proportional to dâ1.29. The discrepancy may arise from the rough estimation in the separation distance x and the specific number of dislocations released from the source for one strain burst, both of which are hard to determine and in need of further study. Even so, it confirms that the GB poses barrier both to the dislocation motion and source reemission which facilitates the work hardening behavior of the bicrystal pillars, which could be extended to bicrystal pillars with other kind of GBs.
In conventional bulk materials, there are numerous dislocation sources and dislocations can multiply easily which smoothes the plastic deformation. Thus stress rise is principally associated with the strong interactions between dislocations, leading to the typical work hardening behavior. In large scales, the initial work hardening behavior in polycrystals is dependent on the grain size owing to the GB back stress to the dislocation motion. However, in small scales, changes take place in nucleation and multiplication of the dislocations, which would then influence the dislocation interactions with the GB. In the bicrystal micropillars, the deformation was controlled by progressive activation and subsequent exhaustion of dislocations, both of which are associated with the GB. To be specific, the GB not only traps the mobile dislocations but also generates back stress to other dislocations. Therefore, it is understandable that the work hardening behavior of bicrystal micropillars exhibit as discrete strain bursts during compression, which is distinct from the smooth work hardening of bulk materials.
To summarize, the present study reveals different deformation behaviors of Cu monocrystal and bicrystal pillars in the micro scale. In contrary to the uninhibited plastic flow without work hardening in the monocrystal pillars, the bicrystal pillars exhibit stepwise work hardening behavior with discrete strain bursts. In particular, the stress rise amplitude is inversely proportional to the specimen size. It is suggested that the GB obstruction to dislocation annihilation stabilizes the deformation while the GB barrier effect to dislocation motion alleviates the softening of the pillars. Both the GB and the sample size influence the deformation and work hardening behaviors of the bicrystal pillars. The present results may provide important implications to further understand the general work hardening behaviors of materials in the future.
Materials and Experiments
The bulk Cu bicrystal with a high-angle GB was grown from 5N purity Cu by the Bridgman method. Micropillars of the bicrystal and two counterpart monocrystals were prepared from the bulk bicrystal by focused ion beam (FIB) milling. Wherein, the GB is parallel to the loading axis. The orientations of two monocrystals are <345> and <136> respectively and the misorientation of the GB is about 40° as determined by the electron backscatter diffraction (EBSD) method. A cuboid sample with the size of 8âmmâÃâ8âmmâÃâ2âmm was carefully mechanically ground and electro-polished firstly as a base and then micropillar specimens were fabricated from this bulk sample. The FIB milling was carried out in a Nova 200 Nanolab dual beam system at 30âkV with gallium as the ion source. For coarse milling, a 3ânA ion-beam current was used and the current was gradually stepped down to 30âpA for the final polishing analogous to the method used before9. A series of cylindrical monocrystal pillars were produced with the diameters ranging from ~1âμm to ~10âμm and the aspect ratio ranging from 5:1 to 7:1. The pillars were slightly tapered within 2° and the sample sizes were taken from the head of the pillars. Bicrystal pillars with nearly square-shaped cross section were produced with the nominal width ranging from ~1âμm to ~10âμm and the aspect ratio ranging from 3:1 to 4:1. Uniaxial compression tests were conducted using a Nanoindenter G200 (Agilent Technologies) equipped with a flat punch. The nominal strain rate ranged from 3â~â5âÃâ10â4 for all the specimens. In addition, comprehensive SEM observations of the surface morphologies before and after compression were carried out via Supra 55 SEM with the specimens at 52° tilt. Deformed bicrystal and monocrystal pillars with the size of 5âμm were milled with FIB along the loading direction into thin-foil sections for ex-situ TEM examination of the dislocation structures. These deformed pillars were first coated with a platinum protective layer in the FEI Helios 650 Dual beam FIB system and then parts of pillars containing slip traces were cut off from the base, finally they were transferred by an in-situ lift-out system (OmniProbeTM 200) to a Cu grid. The sample was first milling by Ga+ ions beam at an accelerating voltage of 30âkV and was thinned to 1â~â2âμm with a beam current of 0.77ânA. Afterwards, a beam current of 33âpA was employed to further thin the sample into electron transparency. The final size of the TEM specimen is about ~6âμmâÃâ~â6âμm with the thickness of 60â~â80ânm. All TEM observations were performed on a 200âkV FEI Tecnai F20 fitted with a field-emission electron source.
Additional Information
How to cite this article: Li, L. L. et al. Stepwise work hardening induced by individual grain boundary in Cu bicrystal micropillars. Sci. Rep. 5, 15631; doi: 10.1038/srep15631 (2015).
References
Arzt, E. Size effects in materials due to microstructural and dimensional constraints: a comparative review. Acta Mater. 46, 5611â5626 (1998).
Uchic, M. D., Dimiduk, D. M., Florando, J. N. & Nix, W. D. Sample dimensions influence strength and crystal plasticity. Science 305, 986â989 (2004).
Greer, J. R. & De Hosson, J. T. M. Plasticity in small-sized metallic systems: Intrinsic versus extrinsic size effect. Prog. Mater. Sci. 56, 654â724 (2011).
Greer, J. R., Oliver, W. C. & Nix, W. D. Size dependence of mechanical properties of gold at the micron scale in the absence of strain gradients. Acta Mater. 53, 1821â1830 (2005).
Oh, S. H., Legros, M., Kiener, D. & Dehm, G. In situ observation of dislocation nucleation and escape in a submicrometre aluminium single crystal. Nat. Mater. 8, 95â100 (2009).
Parthasarathy, T. A., Rao, S. I., Dimiduk, D. M., Uchic, M. D. & Trinkle, D. R. Contribution to size effect of yield strength from the stochastics of dislocation source lengths in finite samples. Scripta Mater. 56, 313â316 (2007).
Kunz, A., Pathak, S. & Greer, J. R. Size effects in Al nanopillars: Single crystalline vs. bicrystalline. Acta Mater. 59, 4416â4424 (2011).
Norfleet, D. M., Dimiduk, D. M., Polasik, S. J., Uchic, M. D. & Mills, M. J. Dislocation structures and their relationship to strength in deformed nickel microcrystals. Acta Mater. 56, 2988â3001 (2008).
Ng, K. S. & Ngan, A. H. W. Stochastic nature of plasticity of aluminum micro-pillars. Acta Mater. 56, 1712â1720 (2008).
Hirth J. P. The Influence of Grain Boundaries on Mechanical Properties. Metall. Trans. 3, 3047â3067 (1972).
Hall, E. The deformation and ageing of mild steel: III discussion of results. Proc. Phys. Soc. Section B 64, 747â753 (1951).
Petch, N. J. The cleavage strength of polycrystals. J. Iron Steel Institute 174, 25â28 (1953).
Sinclair, C., Poole, W. & Bréchet, Y. A model for the grain size dependent work hardening of copper. Scripta Mater. 55, 739â742 (2006).
Thompson, A. W. Effect of grain size on work hardening in nickel. Acta Metall. 25, 83â86 (1977).
Mecking, H. & Kocks, U. F. K.inetics of flow and strain-hardening. Acta Metall. 29, 1865â1875 (1981).
Shan, Z. W. et al. Grain boundary-mediated plasticity in nanocrystalline nickel. Science 305, 654â657 (2004).
Wang, L. H. et al. Grain rotation mediated by grain boundary dislocations in nanocrystalline platinum. Nat. Commun. 5, 4402 (2014).
Kheradmand, N., Vehoff, H. & Barnoush, A. An insight into the role of the grain boundary in plastic deformation by means of a bicrystalline pillar compression test and atomistic simulation. Acta Mater. 61, 7454â7465 (2013).
Rinaldi, A., Peralta, P., Friesen, C. & Sieradzki, K. Sample-size effects in the yield behavior of nanocrystalline nickel. Acta Mater. 56, 511â517 (2008).
Zhang, J. Y., Liu, G. & Sun, J. Strain rate effects on the mechanical response in multi- and single-crystalline Cu micropillars: Grain boundary effects. Int. J. Plasticity 50, 1â17 (2013).
Ng, K. S. & Ngan, A. H. W. Deformation of micron-sized aluminium bi-crystal pillars. Phil. Mag. 89, 3013â3026 (2009).
Jang, D., Cai, C. & Greer, J. R. Influence of homogeneous interfaces on the strength of 500 nm diameter Cu nanopillars. Nano Lett. 11, 1743â1746 (2011).
Zhang, Z. F. & Wang, Z. G. Grain boundary effects on cyclic deformation and fatigue damage. Prog. Mater. Sci. 53, 1025â1099 (2008).
Li, L. L., Zhang, Z. J., Zhang, P., Wang, Z. G. & Zhang, Z. F. Controllable fatigue cracking mechanisms of copper bicrystals with a coherent twin boundary. Nat. Commun. 5, 3536 (2014).
Imrich, P. J., Kirchlechner, C., Motz, C. & Dehm, G. Differences in deformation behavior of bicrystalline Cu micropillars containing a twin boundary or a large-angle grain boundary. Acta Mater. 73, 240â250 (2014).
Li, L. L. et al. Microcompression and cyclic deformation behaviors of coaxial copper bicrystals with a single twin boundary. Scripta Mater. 69, 199â202 (2013).
Aitken, Z. H., Jang, D., Weinberger, C. R. & Greer, J. R. Grain boundary sliding in aluminum nano-bi-crystals deformed at room temperature. Small 10, 100â108 (2014).
Kraft, O., Gruber, P. A., Mönig, R. & Weygand, D. Plasticity in confined dimensions. Annu. Rev. Mater. Res. 40, 293â317 (2010).
Kiener, D., Grosinger, W., Dehm, G. & Pippan, R. A further step towards an understanding of size-dependent crystal plasticity: In situ tension experiments of miniaturized single-crystal copper samples. Acta Mater. 56, 580â592 (2008).
Schneidera, A. S., Frickb, C. P., Clarkc, B. G., Gruberd, P. A. & Arzta E. Influence of orientation on the size effect in bcc pillars with different critical temperatures. Mater. Sci. Eng. A 528, 1540â1547 (2011).
Csikor, F. F., Motz, C., Weygand, D., Zaiser, M. & Zapperi, S. Dislocation avalanches, strain bursts and the problem of plastic forming at the micrometer scale. Science 318, 251â254 (2007).
Dimiduk, D. M., Uchic, M. D. & Parthasarathy, T. A. Size-affected single-slip behavior of pure nickel microcrystals. Acta Mater. 53, 4065â4077 (2005).
Marichal, C., Van Swygenhoven, H., Van Petegem, S. & Borca, C. {110} Slip with {112} slip traces in bcc Tungsten. Sci. Rep. 3, 2547 (2013).
Ng, K. S. & Ngan, A. H. W. Breakdown of Schmidâs law in micropillars. Scripta Mater. 59, 796â799 (2008).
Tiba, I., Richeton, T., Motz, C., Vehoff, H. & Berbenni, S. Incompatibility stresses at grain boundaries in Ni bicrystalline micropillars analyzed by an anisotropic model and slip activity. Acta Mater. 83, 227â238 (2015).
Meyers, M. A. & Chawla, K. K. . Mechanical behavior of materials. Upper Saddle River (NJ), Prentice Hall, 1999.
Kirchlechner, C. et al. Impact of instrumental constraints and imperfections on the dislocation structure in micron-sized Cu compression pillars Acta Mater. 59, 5618â5626 (2011).
Brinckmann, S., Kim, J. Y. & Greer, J. R. Fundamental differences in mechanical behavior between two types of crystals at the nanoscale. Phys. Rev. Lett. 100, 155502 (2008).
Greer, J. R. & Nix, W. D. Nanoscale gold pillars strengthened through dislocation starvation. Phys. Rev. B 73, 245410 (2006).
Ham, R. K. The determination of dislocation densities in thin films, Phil. Mag. 6, 1183â1184 (1961).
Tang, H., Schwarz, K. & Espinosa, H. Dislocation escape-related size effects in single-crystal micropillars under uniaxial compression. Acta Mater. 55, 1607â1616 (2007).
Jennings, A. T., Burek, M. J. & Greer, J. R. Microstructure versus size: mechanical properties of electroplated single crystalline Cu nanopillars. Phys. Rev. Lett. 104, 135503 (2010).
Hirth, J. P. & Lothe, J. Theory of dislocations. (1982).
Zhu, T., Li, J., Samanta, A., Leach, A. & Gall, K. Temperature and Strain-Rate Dependence of Surface Dislocation Nucleation. Phys. Rev. Lett. 100, 025502 (2008).
Acknowledgements
This work was financially supported by the National Natural Science Foundation of China (NSFC) under grant Nos. 51171194, 51331007, 51471170 and the IMR SYNL-T.S. Kê Research Fellowship.
Author information
Authors and Affiliations
Contributions
Z.F.Z. conceived and designed the research plan. L.L.L. prepared the Cu monocrystal and bicrystal. J.T. prepared the micropillars and the TEM samples with the FIB milling method. L.L.L., C.B.J. and R.T.Q. carried out the nanoindentation test. L.L.L. and Z.J.Z. carried out the TEM observation. L.L.L., Z.J.Z., P.Z, J.B.Y. and Z.F.Z. collected and analyzed the data. L.L.L. wrote and Z.F.Z. revised the paper. All authors contributed to data analysis and scientific discussions.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the articleâs Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, L., Zhang, Z., Tan, J. et al. Stepwise work hardening induced by individual grain boundary in Cu bicrystal micropillars. Sci Rep 5, 15631 (2015). https://doi.org/10.1038/srep15631
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep15631