cracking testとは 意味・読み方・使い方

METHOD FOR WELD SOLIDIFICATION CRACKING TEST FOR THIN PLATE例文帳に追加

薄板の溶接凝固割れ試験方法 - 特許庁

To provide a jig for stress corrosion cracking test and capable of easily mounting a plurality of test pieces.例文帳に追加

より簡易に複数の試験片を設置できる応力腐食割れ試験用ジグを提供する。 - 特許庁

To provide a small-sized and low-profile choke coil in which core cracking in a vibration impulse test and a temperature cycle test is suppressed.例文帳に追加

振動衝撃試験、温度サイクル試験でのコア割れを抑制した、小型で低背型のチョークコイルを提供すること。 - 特許庁

To provide an apparatus and a method for manufacturing a test piece for the low-temperature cracking resistance test formed of a material of small fluidity with the uniform density.例文帳に追加

流動性の小さい材料の低温ひび割れ抵抗性試験用供試体を、均一な密度で作製する装置及び方法を提供すること。 - 特許庁

This testing device is equipped with a testing device body for applying a prescribed load repeatedly on the test piece having a notch for cracking to develop a crack on the test piece, and an imaging means for imaging the cracking surface of the test piece mounted on the testing device body and served for a fatigue crack test.例文帳に追加

亀裂発生用の切欠きを備えた試験片に所定の負荷を繰り返し加えて該試験片に亀裂を生起する試験装置本体と、この試験装置本体に装着されて疲労亀裂試験に供されている試験片の亀裂発生面を撮像する撮像手段とを備える。 - 特許庁

To provide a manufacturing method of a stress corrosion cracking sample capable of easily manufacturing a sample into which the stress corrosion cracking formed in an actual machine is introduced with good reproducibility on the basis of the elucidation result of a mechanism of stress corrosion cracking in low-carbon stainless steel, and a test piece for a non-destructive test.例文帳に追加

低炭素ステンスレス鋼での応力腐食割れのメカニズムを解明した結果に基づき、実機に発生する応力腐食割れを再現性良く導入したサンプルを容易に作製することができる応力腐食割れサンプルの作製方法および非破壊試験用試験片を提供すること。 - 特許庁

To perform an environmental acceleration cracking generation test by using a test piece exposed to the same environment as that for incore equipment which is actual machine and structure, and to evaluate environmental acceleration cracking simulating the actual machine state more properly.例文帳に追加

実機である炉内機器および構造物と同じ環境に曝された試験片を用いて環境助長割れ発生試験を行い、実機状態をよりよく模擬した環境助長割れの評価を行う。 - 特許庁

The fixed displacement is imparted forcibly to an opening part of the test piece, prescribed repeated compression loads are loaded to the test piece under a fixed displacement condition to be returned thereafter to the fixed displacement, and a stress corrosion cracking test is carried out.例文帳に追加

試験片の開口部に強制的に一定変位を付与し、一定変位状態の試験片に所定の繰り返し圧縮荷重を与え、その後に一定変位に戻し、応力腐食割れ試験を行う。 - 特許庁