The vases produced in Athens between the 6th and the 4th century BC, are among the highest artist... more The vases produced in Athens between the 6th and the 4th century BC, are among the highest artistic and technological achievements of ancient Greek handicraft. This study was the opportunity to analyze a few samples of Greek ceramic founded on the French archaeological site of Lattes (Hérault). Dated between 500 and 300 BC, they display various decorations made from black and red slips. The purpose of this study was to undertake a chemical and mineralogical characterization of the slips, and to elucidate the firing protocols used. For this purpose, the slips were investigated using optic microscopy, SEM, SEM-EDS, an electron microprobe, Raman microspectroscopy and XRD. This has allowed to make a chemical characterization of the ceramic's bodies and slips and to recover some firing processes.
La porcelaine à décor bleu et blanc, ou porcelaine qinghua, est l'une des céramiques les plus... more La porcelaine à décor bleu et blanc, ou porcelaine qinghua, est l'une des céramiques les plus célèbres au monde. Produite dès le XIIIe siècle dans les fours de Jingdezhen (province du Jiangxi), elle se caractérise par l'usage d'un décor sous glaçure à base de métaux de transition (cobalt principalement mais également fer ou manganèse). Ce type de porcelaine est constitué d'une structure en couche qui se prête particulièrement bien à une décomposition en différents systèmes (glaçure, zone pigmentaire, pâte, interface entre la pâte et la glaçure dans les zones sans décor). Notre thèse a pour objet l'étude de la microstructure des différents systèmes et sous-systèmes constituants la porcelaine afin, par une approche de type " rétro-ingénierie ", de remonter aux procédés techniques à l'origine de la fabrication de ces objets. Pour ce faire, 33 échantillons datés des dynasties Yuan (1279-1368), Ming (1368-1644) et Qing moyenne (1736-1850), fabriqués sur ...
Abstract The blue underglaze decorations of Chinese blue-and-white porcelains are due to the use ... more Abstract The blue underglaze decorations of Chinese blue-and-white porcelains are due to the use of a cobalt-based blue pigment. Nevertheless, for a same time period and production centre, wares can present wide colour variations in both hue and intensity. Fourteen Ming samples were investigated using colorimetry, Raman spectroscopy and SEM-EDS, in order to better understand the origin of these variations. The majority of the sherds dates back to the middle 15th- early 16th century. The chromogenic mechanism of the hue and intensity variations appears to be complex and multifactorial. Six main factors have been identified: the elemental composition of the pigment particles, in particular the Fe/Co ratio, the pigment spinel structure, the size as well as the distribution of the colouring particles, the environment of the pigment particles and the colour of the glaze.
Phase mapping and quantitative analysis of complex cultural heritage materials thanks to multivar... more Phase mapping and quantitative analysis of complex cultural heritage materials thanks to multivariate analysis applied to XRD-CT data.
La porcelaine a decor bleu et blanc, ou porcelaine qinghua, est l'une des ceramiques les plus... more La porcelaine a decor bleu et blanc, ou porcelaine qinghua, est l'une des ceramiques les plus celebres au monde. Produite des le XIIIe siecle dans les fours de Jingdezhen (province du Jiangxi), elle se caracterise par l'usage d'un decor sous glacure a base de metaux de transition (cobalt principalement mais egalement fer ou manganese). Ce type de porcelaine est constitue d'une structure en couche qui se prete particulierement bien a une decomposition en differents systemes (glacure, zone pigmentaire, pâte, interface entre la pâte et la glacure dans les zones sans decor). Notre these a pour objet l'etude de la microstructure des differents systemes et sous-systemes constituants la porcelaine afin, par une approche de type " retro-ingenierie ", de remonter aux procedes techniques a l'origine de la fabrication de ces objets. Pour ce faire, 33 echantillons dates des dynasties Yuan (1279-1368), Ming (1368-1644) et Qing moyenne (1736-1850), fabriques sur ...
L’imitation des porcelaines chinoises est une problématique importante en archéologie et histoire... more L’imitation des porcelaines chinoises est une problématique importante en archéologie et histoire de l’art. Les décors ou le style peuvent être aisément copiés mais les matériaux constituant l’objet sont le fruit de processus techniques qu’il peut être plus difficile à imiter lorsque les matières premières ne sont plus accessibles ou que les procédés de fabrication ont évolué. Utiliser une approche de type « science des matériaux » en se concentrant sur la composition des porcelaines permet ainsi d’identifier un certain nombre de caractéristiques qui peuvent servir de marqueurs pour l’expertise. Cet article a pour objectif de présenter les apports et limites d’une telle approche, au travers de quelques exemples sur les porcelaines à décor bleu et blanc.
The blue underglaze decorations of Chinese blue-and-white porcelains are due to the use of a coba... more The blue underglaze decorations of Chinese blue-and-white porcelains are due to the use of a cobalt-based blue pigment. Nevertheless, for a same time period and production centre, wares can present wide colour variations in both hue and intensity. Fourteen Ming samples were investigated using colorimetry, Raman spectroscopy and SEM-EDS, in order to better understand the origin of these variations. The majority of the sherds dates back to the middle 15th- early 16th century. The chromogenic mechanism of the hue and intensity variations appears to be complex and multifactorial. Six main factors have been identified: the elemental composition of the pigment particles, in particular the Fe/Co ratio, the pigment spinel structure, the size as well as the distribution of the colouring particles, the environment of the pigment particles and the colour of the glaze.
Chinese potters were highly imaginative in their use
of iron as a colouring for glazes. Playing n... more Chinese potters were highly imaginative in their use of iron as a colouring for glazes. Playing not only on its level of oxidation (Fe3+, Fe2+), but also on its chemical speciation, they succeeded in producing a rich palette of colours. In this paper we shall present the latest archeometric research findings and show that the discovery of a rare form of ferric oxide (ε-Fe2O3) in these glazes opens up interesting perspectives in both the history of techniques and materials science.
L’imitation des porcelaines chinoises est une problématique importante en archéologie et
histoire... more L’imitation des porcelaines chinoises est une problématique importante en archéologie et histoire de l’art. Les décors ou le style peuvent être aisément copiés mais les matériaux constituant l’objet sont le fruit de processus techniques qu’il peut être plus difficile à imiter lorsque les matières premières ne sont plus accessibles ou que les procédés de fabrication ont évolué. Utiliser une approche de type « science des matériaux » en se concentrant sur la composition des porcelaines permet ainsi d’identifier un certain nombre de caractéristiques qui peuvent servir de marqueurs pour l’expertise. Cet article a pour objectif de présenter les apports et limites d’une telle approche, au travers de quelques exemples sur les porcelaines à décor bleu et blanc.
We report on the analysis of dendritic crystals present in the dark spot areas of blue‐and‐white ... more We report on the analysis of dendritic crystals present in the dark spot areas of blue‐and‐white Ming porcelains. Using Raman spectroscopy and scanning electron microscopy equipped with energy dispersive spectrometer, we were able to evidence Mn‐rich spinels. Small Mn‐based spinel crystals being highly sensitive to laser‐induced heating, we identified proper working conditions, avoiding excessive heating and damage. Local temperatures during Raman measurements were deduced from Stokes/anti‐Stokes intensity ratios. By analysing the behaviour of the A1g mode of Mn‐rich spinels, we were able to identify phases ranging from jacobsite‐like to hausmannite‐like compounds. Polarized Raman scattering was shown to provide a convenient means of discriminating between these two types of phases, as they display different symmetries. Inhomogeneities within the dendritic network, as evidenced by micro‐Raman measurements, highlight its gradual formation during the cooling phase of firing, depending of Fe3+ and Mn3+ availability. The presence of Mn‐based spinels is consistent with the use of a local Chinese Mn‐rich cobalt ore during the middle Ming Dynasty.
The vases produced in Athens between the 6th and the 4th century BC, are among the highest artist... more The vases produced in Athens between the 6th and the 4th century BC, are among the highest artistic and technological achievements of ancient Greek handicraft. This study was the opportunity to analyze a few samples of Greek ceramic founded on the French archaeological site of Lattes (Hérault). Dated between 500 and 300 BC, they display various decorations made from black and red slips. The purpose of this study was to undertake a chemical and mineralogical characterization of the slips, and to elucidate the firing protocols used. For this purpose, the slips were investigated using optic microscopy, SEM, SEM-EDS, an electron microprobe, Raman microspectroscopy and XRD. This has allowed to make a chemical characterization of the ceramic's bodies and slips and to recover some firing processes.
La porcelaine à décor bleu et blanc, ou porcelaine qinghua, est l'une des céramiques les plus... more La porcelaine à décor bleu et blanc, ou porcelaine qinghua, est l'une des céramiques les plus célèbres au monde. Produite dès le XIIIe siècle dans les fours de Jingdezhen (province du Jiangxi), elle se caractérise par l'usage d'un décor sous glaçure à base de métaux de transition (cobalt principalement mais également fer ou manganèse). Ce type de porcelaine est constitué d'une structure en couche qui se prête particulièrement bien à une décomposition en différents systèmes (glaçure, zone pigmentaire, pâte, interface entre la pâte et la glaçure dans les zones sans décor). Notre thèse a pour objet l'étude de la microstructure des différents systèmes et sous-systèmes constituants la porcelaine afin, par une approche de type " rétro-ingénierie ", de remonter aux procédés techniques à l'origine de la fabrication de ces objets. Pour ce faire, 33 échantillons datés des dynasties Yuan (1279-1368), Ming (1368-1644) et Qing moyenne (1736-1850), fabriqués sur ...
Abstract The blue underglaze decorations of Chinese blue-and-white porcelains are due to the use ... more Abstract The blue underglaze decorations of Chinese blue-and-white porcelains are due to the use of a cobalt-based blue pigment. Nevertheless, for a same time period and production centre, wares can present wide colour variations in both hue and intensity. Fourteen Ming samples were investigated using colorimetry, Raman spectroscopy and SEM-EDS, in order to better understand the origin of these variations. The majority of the sherds dates back to the middle 15th- early 16th century. The chromogenic mechanism of the hue and intensity variations appears to be complex and multifactorial. Six main factors have been identified: the elemental composition of the pigment particles, in particular the Fe/Co ratio, the pigment spinel structure, the size as well as the distribution of the colouring particles, the environment of the pigment particles and the colour of the glaze.
Phase mapping and quantitative analysis of complex cultural heritage materials thanks to multivar... more Phase mapping and quantitative analysis of complex cultural heritage materials thanks to multivariate analysis applied to XRD-CT data.
La porcelaine a decor bleu et blanc, ou porcelaine qinghua, est l'une des ceramiques les plus... more La porcelaine a decor bleu et blanc, ou porcelaine qinghua, est l'une des ceramiques les plus celebres au monde. Produite des le XIIIe siecle dans les fours de Jingdezhen (province du Jiangxi), elle se caracterise par l'usage d'un decor sous glacure a base de metaux de transition (cobalt principalement mais egalement fer ou manganese). Ce type de porcelaine est constitue d'une structure en couche qui se prete particulierement bien a une decomposition en differents systemes (glacure, zone pigmentaire, pâte, interface entre la pâte et la glacure dans les zones sans decor). Notre these a pour objet l'etude de la microstructure des differents systemes et sous-systemes constituants la porcelaine afin, par une approche de type " retro-ingenierie ", de remonter aux procedes techniques a l'origine de la fabrication de ces objets. Pour ce faire, 33 echantillons dates des dynasties Yuan (1279-1368), Ming (1368-1644) et Qing moyenne (1736-1850), fabriques sur ...
L’imitation des porcelaines chinoises est une problématique importante en archéologie et histoire... more L’imitation des porcelaines chinoises est une problématique importante en archéologie et histoire de l’art. Les décors ou le style peuvent être aisément copiés mais les matériaux constituant l’objet sont le fruit de processus techniques qu’il peut être plus difficile à imiter lorsque les matières premières ne sont plus accessibles ou que les procédés de fabrication ont évolué. Utiliser une approche de type « science des matériaux » en se concentrant sur la composition des porcelaines permet ainsi d’identifier un certain nombre de caractéristiques qui peuvent servir de marqueurs pour l’expertise. Cet article a pour objectif de présenter les apports et limites d’une telle approche, au travers de quelques exemples sur les porcelaines à décor bleu et blanc.
The blue underglaze decorations of Chinese blue-and-white porcelains are due to the use of a coba... more The blue underglaze decorations of Chinese blue-and-white porcelains are due to the use of a cobalt-based blue pigment. Nevertheless, for a same time period and production centre, wares can present wide colour variations in both hue and intensity. Fourteen Ming samples were investigated using colorimetry, Raman spectroscopy and SEM-EDS, in order to better understand the origin of these variations. The majority of the sherds dates back to the middle 15th- early 16th century. The chromogenic mechanism of the hue and intensity variations appears to be complex and multifactorial. Six main factors have been identified: the elemental composition of the pigment particles, in particular the Fe/Co ratio, the pigment spinel structure, the size as well as the distribution of the colouring particles, the environment of the pigment particles and the colour of the glaze.
Chinese potters were highly imaginative in their use
of iron as a colouring for glazes. Playing n... more Chinese potters were highly imaginative in their use of iron as a colouring for glazes. Playing not only on its level of oxidation (Fe3+, Fe2+), but also on its chemical speciation, they succeeded in producing a rich palette of colours. In this paper we shall present the latest archeometric research findings and show that the discovery of a rare form of ferric oxide (ε-Fe2O3) in these glazes opens up interesting perspectives in both the history of techniques and materials science.
L’imitation des porcelaines chinoises est une problématique importante en archéologie et
histoire... more L’imitation des porcelaines chinoises est une problématique importante en archéologie et histoire de l’art. Les décors ou le style peuvent être aisément copiés mais les matériaux constituant l’objet sont le fruit de processus techniques qu’il peut être plus difficile à imiter lorsque les matières premières ne sont plus accessibles ou que les procédés de fabrication ont évolué. Utiliser une approche de type « science des matériaux » en se concentrant sur la composition des porcelaines permet ainsi d’identifier un certain nombre de caractéristiques qui peuvent servir de marqueurs pour l’expertise. Cet article a pour objectif de présenter les apports et limites d’une telle approche, au travers de quelques exemples sur les porcelaines à décor bleu et blanc.
We report on the analysis of dendritic crystals present in the dark spot areas of blue‐and‐white ... more We report on the analysis of dendritic crystals present in the dark spot areas of blue‐and‐white Ming porcelains. Using Raman spectroscopy and scanning electron microscopy equipped with energy dispersive spectrometer, we were able to evidence Mn‐rich spinels. Small Mn‐based spinel crystals being highly sensitive to laser‐induced heating, we identified proper working conditions, avoiding excessive heating and damage. Local temperatures during Raman measurements were deduced from Stokes/anti‐Stokes intensity ratios. By analysing the behaviour of the A1g mode of Mn‐rich spinels, we were able to identify phases ranging from jacobsite‐like to hausmannite‐like compounds. Polarized Raman scattering was shown to provide a convenient means of discriminating between these two types of phases, as they display different symmetries. Inhomogeneities within the dendritic network, as evidenced by micro‐Raman measurements, highlight its gradual formation during the cooling phase of firing, depending of Fe3+ and Mn3+ availability. The presence of Mn‐based spinels is consistent with the use of a local Chinese Mn‐rich cobalt ore during the middle Ming Dynasty.
Uploads
ACADEMIC WORKS by Ariane Pinto
electron microprobe, Raman microspectroscopy and XRD. This has allowed to make a chemical characterization of the ceramic's bodies and slips and to recover some firing processes.
Papers by Ariane Pinto
of iron as a colouring for glazes. Playing not only on its level
of oxidation (Fe3+, Fe2+), but also on its chemical speciation, they
succeeded in producing a rich palette of colours. In this paper we
shall present the latest archeometric research findings and show
that the discovery of a rare form of ferric oxide (ε-Fe2O3) in these
glazes opens up interesting perspectives in both the history of
techniques and materials science.
histoire de l’art. Les décors ou le style peuvent être aisément copiés mais les matériaux
constituant l’objet sont le fruit de processus techniques qu’il peut être plus difficile à imiter
lorsque les matières premières ne sont plus accessibles ou que les procédés de fabrication ont
évolué. Utiliser une approche de type « science des matériaux » en se concentrant sur la
composition des porcelaines permet ainsi d’identifier un certain nombre de caractéristiques qui
peuvent servir de marqueurs pour l’expertise. Cet article a pour objectif de présenter les apports
et limites d’une telle approche, au travers de quelques exemples sur les porcelaines à décor bleu
et blanc.
electron microprobe, Raman microspectroscopy and XRD. This has allowed to make a chemical characterization of the ceramic's bodies and slips and to recover some firing processes.
of iron as a colouring for glazes. Playing not only on its level
of oxidation (Fe3+, Fe2+), but also on its chemical speciation, they
succeeded in producing a rich palette of colours. In this paper we
shall present the latest archeometric research findings and show
that the discovery of a rare form of ferric oxide (ε-Fe2O3) in these
glazes opens up interesting perspectives in both the history of
techniques and materials science.
histoire de l’art. Les décors ou le style peuvent être aisément copiés mais les matériaux
constituant l’objet sont le fruit de processus techniques qu’il peut être plus difficile à imiter
lorsque les matières premières ne sont plus accessibles ou que les procédés de fabrication ont
évolué. Utiliser une approche de type « science des matériaux » en se concentrant sur la
composition des porcelaines permet ainsi d’identifier un certain nombre de caractéristiques qui
peuvent servir de marqueurs pour l’expertise. Cet article a pour objectif de présenter les apports
et limites d’une telle approche, au travers de quelques exemples sur les porcelaines à décor bleu
et blanc.