A novel approach for Ta and Nb extraction consisting of the pre-treatment of a coltan-bearing ore... more A novel approach for Ta and Nb extraction consisting of the pre-treatment of a coltan-bearing ore with an ammonium bifluoride sub-molten salt and subsequent acid leaching has been studied. The effects from ore granulometry, ammonium bifluoride (ABF) to ore mass ratio, temperature and duration of fluorination on the degree of Ta and Nb extraction were examined. The ABF to ore ratio and process temperature were found to have the most pronounced impact on extraction efficiency. The following optimal process conditions were determined: ore granulometric fraction (−75 + 45 µm), ABF-ore (5/1), fluorination temperature (200 °C) and fluorination time (2.5 h). Maintaining these parameters enabled about 94% of Ta and 95% of Nb to be brought into solution during the sulfuric-acid-leaching stage. A comparison of the proposed method with previously reported studies suggests that due to the effects of mechanical agitation and the recirculation of the HF-containing gaseous phase back into the proc...
Epigraphe 1 Marie Curie Physicienne française (1867-1934) Un scientifique dans son laboratoire es... more Epigraphe 1 Marie Curie Physicienne française (1867-1934) Un scientifique dans son laboratoire est non seulement un technicien : il est aussi un enfant placé devant des phénomènes naturels qui l'impressionnent comme des contes de fées.
I RESUME La présente recherche porte sur l'élaboration et caractérisation d'un biofilm plastique ... more I RESUME La présente recherche porte sur l'élaboration et caractérisation d'un biofilm plastique à partir d'amidon extrait des tubercules de manioc. Il poursuit comme objectif d'élaborer un biofilm plastique avec des bonnes propriétés mécaniques de sorte qu'après usage, il se dégrade facilement de façon naturelle. Les biofilms ont été élaborés par la méthode du casting à partir d'amidon natif de manioc. Ils ont été plastifiés par le glycérol et renforcés par des charges synthétiques de zéolithe Bêta, et par l'éthylène glycol. La procédure de travail a consisté à conditionner les cossettes de manioc pour extraire l'amidon à plastifier avec le glycérol et l'éthylène glycol à différentes concentrations avec ajout progressif de charge pour améliorer les propriétés. En fin de répondre convenablement aux objectifs fixés dans cette étude, nous avons retenu un seuil du glycérol de 30 % (g/g d'amidon sec), lequel facilite la mise en forme et la manutention du biofilm plastique élaboré. La charge de renfort utilisée (zéolithe beta), a une influence certaine sur l'aspect et les propriétés mécaniques des biofilms. En effet, le seuil retenu est de 2/5 (g/g d'amidon sec), au-delà de ce seuil, la plastification n'est pas aisée au taux de glycérol retenu. L'éthylène glycol utilisé augmente davantage la plasticité du matériau amylacé, ceci nous a permis de limiter son taux à 2 ml (pour 5 g d'amidon sec) dans les formulations de nos biofilms plastiques. Divers tests de caractérisation des biofilms plastiques ont également été réalisés, entre autre ceux de solubilité, d'identification des matières plastiques, de soumission des acides et bases, et de biodégradabilité. Ces tests ont été satisfaisants pour les biofilms plastiques réalisés aux conditions retenues alors qu'il serait mieux d'approfondir la caractérisation pour bien expliquer les phénomènes intervenant pour la plastification et l'élargissement de la gamme de plastifiants. Abstract II
A novel approach for Ta and Nb extraction consisting of the pre-treatment of a coltan-bearing ore... more A novel approach for Ta and Nb extraction consisting of the pre-treatment of a coltan-bearing ore with an ammonium bifluoride sub-molten salt and subsequent acid leaching has been studied. The effects from ore granulometry, ammonium bifluoride (ABF) to ore mass ratio, temperature and duration of fluorination on the degree of Ta and Nb extraction were examined. The ABF to ore ratio and process temperature were found to have the most pronounced impact on extraction efficiency. The following optimal process conditions were determined: ore granulometric fraction (−75 + 45 µm), ABF-ore (5/1), fluorination temperature (200 °C) and fluorination time (2.5 h). Maintaining these parameters enabled about 94% of Ta and 95% of Nb to be brought into solution during the sulfuric-acid-leaching stage. A comparison of the proposed method with previously reported studies suggests that due to the effects of mechanical agitation and the recirculation of the HF-containing gaseous phase back into the proc...
Epigraphe 1 Marie Curie Physicienne française (1867-1934) Un scientifique dans son laboratoire es... more Epigraphe 1 Marie Curie Physicienne française (1867-1934) Un scientifique dans son laboratoire est non seulement un technicien : il est aussi un enfant placé devant des phénomènes naturels qui l'impressionnent comme des contes de fées.
I RESUME La présente recherche porte sur l'élaboration et caractérisation d'un biofilm plastique ... more I RESUME La présente recherche porte sur l'élaboration et caractérisation d'un biofilm plastique à partir d'amidon extrait des tubercules de manioc. Il poursuit comme objectif d'élaborer un biofilm plastique avec des bonnes propriétés mécaniques de sorte qu'après usage, il se dégrade facilement de façon naturelle. Les biofilms ont été élaborés par la méthode du casting à partir d'amidon natif de manioc. Ils ont été plastifiés par le glycérol et renforcés par des charges synthétiques de zéolithe Bêta, et par l'éthylène glycol. La procédure de travail a consisté à conditionner les cossettes de manioc pour extraire l'amidon à plastifier avec le glycérol et l'éthylène glycol à différentes concentrations avec ajout progressif de charge pour améliorer les propriétés. En fin de répondre convenablement aux objectifs fixés dans cette étude, nous avons retenu un seuil du glycérol de 30 % (g/g d'amidon sec), lequel facilite la mise en forme et la manutention du biofilm plastique élaboré. La charge de renfort utilisée (zéolithe beta), a une influence certaine sur l'aspect et les propriétés mécaniques des biofilms. En effet, le seuil retenu est de 2/5 (g/g d'amidon sec), au-delà de ce seuil, la plastification n'est pas aisée au taux de glycérol retenu. L'éthylène glycol utilisé augmente davantage la plasticité du matériau amylacé, ceci nous a permis de limiter son taux à 2 ml (pour 5 g d'amidon sec) dans les formulations de nos biofilms plastiques. Divers tests de caractérisation des biofilms plastiques ont également été réalisés, entre autre ceux de solubilité, d'identification des matières plastiques, de soumission des acides et bases, et de biodégradabilité. Ces tests ont été satisfaisants pour les biofilms plastiques réalisés aux conditions retenues alors qu'il serait mieux d'approfondir la caractérisation pour bien expliquer les phénomènes intervenant pour la plastification et l'élargissement de la gamme de plastifiants. Abstract II
Uploads