Performance Enhancement of Dye-Sensitized Solar Cells Using a Natural Sensitizer

Hindawi International Journal of Photoenergy Volume 2017, Article ID 2704864, 5 pages https://doi.org/10.1155/2017/2704864 Research Article Performance Enhancement of Dye-Sensitized Solar Cells Using a Natural Sensitizer Zainal Arifin,1,2 Sudjito Soeparman,1 Denny Widhiyanuriyawan,1 and Suyitno Suyitno2 1 Department of Mechanical Engineering, Brawijaya University, Jl. Veteran, Malang 65145, Indonesia Department of Mechanical Engineering, Sebelas Maret University, Jl. Ir. Sutami 36 A, Surakarta 57126, Indonesia 2 Correspondence should be addressed to Zainal Arifin; zainal arifin@staff.uns.ac.id Received 26 October 2016; Revised 22 December 2016; Accepted 29 December 2016; Published 24 January 2017 Academic Editor: K. R. Justin Thomas Copyright © 2017 Zainal Arifin et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. Dye-sensitized solar cells (DSSCs) based on natural sensitizers have become a topic of significant research because of their urgency and importance in the energy conversion field and the following advantages: ease of fabrication, low-cost solar cell, and usage of nontoxic materials. In this study, the chlorophyll extracted from papaya leaves was used as a natural sensitizer. Dye molecules were adsorbed by TiO2 nanoparticle surfaces when submerged in the dye solution for 24 h. The concentration of the dye solution influences both the amount of dye loading and the DSSC performance. The amount of adsorbed dye molecules by TiO2 nanoparticle was calculated using a desorption method. As the concentration of dye solution was increased, the dye loading capacity and power conversion efficiency increased. Above 90 mM dye solution concentration, however, the DSSC efficiency decreased because dye precipitated on the TiO2 nanostructure. These characteristics of DSSCs were analyzed under the irradiation of 100 mW/cm2 . The best performance of DSSCs was obtained at 90 mM dye solution, with the values of 𝑉oc , 𝐽sc , FF, and efficiency of DSSCs being 0.561 V, 0.402 mA/cm2 , 41.65%, and 0.094%, respectively. 1. Introduction Performance of dye-sensitized solar cells (DSSCs) is influenced by semiconductors, electrolytes, transparent conductive oxide (TCO) substrates, counter electrode, and dye sensitizers [1–6]. Dye plays an important role in the performance of DSSCs [7–9]. When synthetic dye such as ruthenium complex is used as a sensitizer in a wide-bandgap semiconductor, the DSSC efficiency becomes over 10% [3]. Because of high costs, presence of heavy metals, and complex synthesis processes of synthetic dyes, natural dyes obtained from leaves, fruits, and plants are a cheaper option and they are nontoxic and completely biodegradable also [10]. Performance of DSSCs based natural sensitizer can be enhanced by using chlorophyll. When ethanol is used as a solvent, the efficiency of DSSCs improves to 36.11% compared to that achieved when distilled water is used [10]. The acidity of chlorophyll solution can be controlled to pH 3.5 by adding benzoic acid, which helped increase the efficiency of DSSCs from 0.07% to 0.28% [11]. The amount of dye molecules that can be absorbed by the semiconductor is also essential in improving the performance and the electron injection of DSSCs [12]. High electron injection from photoexcited sensitizers to the conduction band of semiconductors strongly influences the current density of DSSCs [1]. The amount of dye adsorbed by semiconductors can be studied by controlling the size of the semiconductor and modifying the morphological structure of the semiconductor [12–16]. The properties of the dye solution can also affect the amount of dye molecules adsorbed by semiconductors [17]. One of the solution’s properties that can be easily controlled is the concentration of the solution. The dye solution concentration on the semiconductor is also important for study because of its influence in DSSC performance. In this work, the performance of DSSCs with natural chlorophyll as the sensitizer at various concentrations was studied. The performance of chlorophyll-based DSSCs was compared with the results obtained using N719-based DSSCs. 2 International Journal of Photoenergy 2. Material and Method 2.2. DSSC Fabrication and Testing. The DSSCs were assembled as follows: fluorine-doped tin oxide (FTO, SigmaAldrich) conductive glasses were used as the substrate. The semiconductor paste was prepared by dissolving 0.24 g TiO2 nanopowder (21 nm, Sigma-Aldrich) into 4 mL ethyl alcohol (96%, Merck). The TiO2 paste was applied to FTO-coated glass and flattened using the doctor blade method until the TiO2 film becomes a homogenous layer. The semiconductor layer was maintained at 20 𝜇m and an area of 1 × 1 cm2 . Then, the TiO2 layer coated on the FTO substrate was sintered at 450∘ C for 2.5 h to enhance the bonding between the semiconductor and the FTO glass. After that, the photoelectrodes were immersed in the respective dye solution for 24 h at 30∘ C. The counter electrode was conducted by a sputtering process. The catalytic platinum was deposited on the FTO glass in a vacuum tube at 9.5 × 10−5 Torr. The platinum material target was connected to the negative terminal at a high voltage of 404 V and 125 mA, while the FTO glass was connected to the positive terminal. The electrolyte solution was synthesized by mixing 3.3 g sodium iodide (99.95%), 523.875 mg pure iodine (99.95%), 5.481 g heteropolyacid (HPA), and 30 mL acetonitrile. HPA added in the electrolyte act as an electron acceptor to prevent recombination and photoreduction of iodide (I− ) [18]. The electrolyte solution was injected into the assembled DSSCs at 30 𝜇m intervals and sealed by glass glue. The performance of DSSCs was determined by a solar 4.5 4 3.5 Absorbance 2.1. Chlorophyll Dye Synthesis. The chlorophyll dye extracted from 100 g of papaya leaves was added to 1 L of ethyl alcohol (96%, Merck, Germany) and heated at 70∘ C for 3 h. The separation of this solution was performed using Buchner funnel with single number 42 Whatman filter paper. The extracted dyes were then isolated from the ethanolic solution by rotary evaporation and got 8.5 g of crude chlorophyll. The crude chlorophyll was added to petroleum ether until a yellow color appears in the column chromatography. The separation process was followed by replacing the eluent with a solution of 10% diethyl ether in petroleum ether to produce 0.76 g (8.9%) chlorophyll (green), 0.035 g (0.41%) 𝛽-carotene (yellow), 0.03 (0.35%) phycoerythrin (orange), and residues. A detailed description of the synthesis of chlorophyll dyes can be found elsewhere [11]. The chlorophyll was dissolved in ethyl alcohol to obtain solution of various concentrations (60, 70, 80, 90, and 100 mM). The synthetic dye used in this research was 0.03 mM N719 (Dyesol). The optical properties of the dyes were measured by UV-Vis spectroscopy (Lambda 25, Perkin Elmer). The functional groups in the dyes were characterized by Fourier transform infrared spectroscopy (FTIR, Shimadzu). Cyclic voltammetry (CV, Metrohm AG) was used to determine the reduction and oxidation potentials (𝐸red and 𝐸ox , resp.) of the dyes. The Pt wire, Pt plate, and Ag/AgCl were used as a counter, working, and reference electrodes, respectively. The potential applied in the CV process was from −2.0 V to +2.0 V with a scan rate of 100 mV/s. 5 3 2.5 2 1.5 1 0.5 0 400 450 500 550 600 650 700 750 800 Wavelength (nm) N719 60 mM 70 mM 80 mM 90 mM 100 mM Figure 1: Absorption spectra of N719 and chlorophyll dyes. simulator under irradiation of 100 mW/cm2 . The currentvoltage (𝐼-𝑉) curve was measured by a digital multimeter (Keithley 2401) to obtain 𝐽sc , 𝑉oc , FF, and efficiency of DSSCs. 3. Results and Discussion 3.1. Dye Characterization. The absorption spectra in the visible light spectrum (400–700 nm) of N719 and chlorophyll dyes are shown in Figure 1. The absorption peak of N719 can be seen at 515 nm and chlorophyll at 660 nm [11]. Variation in the chlorophyll dye solution concentration did not affect the position of the absorption peak spectra but affected the absorbance value at a wavelength of 660 nm. This corresponds with the Lambert-Beer law, according to which the absorbance of a solution is proportional to its concentration at the same path length of the light beam [19]. Figure 2 and Table 1 show the cyclic voltammetry (CV) test results of N719 and chlorophyll dyes. The electrochemical oxidation and reduction onset potentials (𝐸ox and 𝐸red , resp.) were used to calculate the energy levels of the highest occupied molecular orbital (𝐸HOMO ) and the lowest unoccupied molecular orbital (𝐸LUMO ) [11]. The onset potentials were determined from the intersection of tangents between the rising current and the baseline charging current of the CV curves. As shown in Table 1, the various concentrations have a minor effect on 𝐸HOMO and 𝐸LUMO values of chlorophyll dyes. Figure 3 shows the FTIR measurements of N719 and chlorophyll dyes. All dyes display peaks in both the 2500– 3000 and 1600–1750 cm−1 region, corresponding to the presence of the –OH and C=O groups, respectively. However, the N719 dye produced more C=O stretching and –OH groups than chlorophyll dyes. In general, the concentration variation in chlorophyll dyes did not change the C=O stretching and –OH groups. International Journal of Photoenergy 3 Table 1: Energy levels of N719 and chlorophyll dyes. Dyes N719 60 mM chlorophyll 70 mM chlorophyll 80 mM chlorophyll 90 mM chlorophyll 100 mM chlorophyll a b 𝐸ox (V) 0.68 0.71 0.77 0.77 0.75 0.72 𝐸HOMO a (eV) −5.08 −5.11 −5.17 −5.17 −5.15 −5.12 𝐸red (V) −1.22 −0.76 −0.76 −0.78 −0.76 −0.70 𝐸LUMO b (eV) −3.18 −3.64 −3.64 −3.62 −3.64 −3.70 𝐸Band Gap (eV) 1.90 1.47 1.53 1.55 1.51 1.42 𝐸HOMO = −𝑒[𝐸ox + 4.4]. 𝐸LUMO = −𝑒[𝐸red + 4.4]. Table 2: Characteristics of DSSCs based on N719 and chlorophyll dyes. Dyes N719 60 mM chlorophyll 70 mM chlorophyll 80 mM chlorophyll 90 mM chlorophyll 100 mM chlorophyll 𝐽SC (mA/cm2 ) 5.612 0.169 0.188 0.401 0.402 0.346 𝑉OC (V) 0.553 0.542 0.501 0.594 0.561 0.606 Dye loading (mol/cm2 ) 1.0 × 10−7 5.7 × 10−8 8.4 × 10−8 9.8 × 10−8 1.1 × 10−7 1.3 × 10−7 𝜂 (%) 1.293 0.040 0.045 0.074 0.094 0.049 FF (%) 41.63 44.02 48.16 39.55 41.65 42.34 80 60 Carboxylic acids C–O −0.15 Aliphatic amines C–N −0.05 Aromatics C–C Carbonyls C=O 0.05 40 20 Transmittance (%) 0.15 Alkanes C –H Phenols O–H 100 −0.35 −2.5 1000 1250 1500 1750 2000 2250 2500 2750 3000 3250 3500 −0.25 3750 0 4000 Current density (mA/cm2 ) 0.25 Wavenumber (cm−1 ) −1.5 −0.5 0.5 1.5 2.5 Potential (mV) N719 60 mM 70 mM 80 mM 90 mM 100 mM Figure 2: Cyclic voltammogram curves of N719 and chlorophyll dyes. 3.2. Performance of DSSCs. Figure 4 and Table 2 show the performance of DSSCs based on N719 and chlorophyll dyes under irradiation of 100 mW/cm2 . The energy conversion efficiency of N719 dye-based DSSCs was higher than all chlorophyll dye-based DSSCs. The N719 dye-based DSSCs achieved an efficiency of 1.293%, while the highest efficiency of chlorophyll dye-based DSSCs was 0.094% at 90 mM. The amount of dye loading on the semiconductor surface was measured by the dye desorption method [12]. This process was followed by the immersion of the TiO2 -dye electrode in an ethanol solution of 0.1 M NaOH. The dye desorption took place after 1 h, with the solution becoming pink for the N719 dye and green for the chlorophyll dye. At N719 60 mM 70 mM 80 mM 90 mM 100 mM Figure 3: FTIR spectra of N719 and chlorophyll dyes. the same time, the TiO2 electrode turned colorless because it loses the dye on its surface [12, 20]. Figure 5 shows the UV-Vis absorption spectra of the solutions measured to estimate the concentration of the adsorbed dye molecules. The concentration of the adsorbed dye was calculated by using the Lambert-Beer law: 𝐴 = 𝜀 ⋅ 𝑐 ⋅ 𝑙, (1) where 𝐴 is the intensity of the UV-Vis absorption spectra at the peak of N719 and chlorophyll dye in 515 and 660 nm, respectively, 𝜀 is the molar extinction coefficient of dye, 𝑐 is the dye molecular concentration, and 𝑙 is the path length of the light beam. The molar extinction coefficient of N719 determined to be 14,100 M−1 cm−1 at 515 nm [12, 21] and for chlorophyll is 86,300 M−1 cm−1 at 660 nm [22]. 4 International Journal of Photoenergy 0.4 of 90 mM chlorophyll dye has good interaction with the TiO2 surfaces, due to the high dye loading value without producing the significant inactive dye precipitation effect. Current density (mA/cm2 ) 0.35 0.3 4. Conclusions 0.25 0.2 0.15 0.1 0.05 0 0.00 0.10 0.20 0.30 0.40 0.50 0.60 Voltage (V) 60 mM 70 mM 80 mM 90 mM 100 mM Figure 4: 𝐼-𝑉 curves of DSSCs under irradiation intensity of 100 mW/cm2 . Chlorophyll extracted from papaya leaves can be used as a dye sensitizer in DSSCs. However, the energy conversion efficiency is still lower than that of synthetic dye-based DSSCs. The N719 dye-based DSSCs achieved an efficiency of 1.293%, while the highest efficiency of chlorophyll dyebased DSSCs was 0.094% at 90 mM. The variation in the chlorophyll dye solution concentration did not change the HOMO-LUMO energy level and –COOH functionalities. Increasing the dye solution concentrations also increased the efficiency of DSSCs because of the increase in the amount of dye adsorbed by TiO2 . However, at concentrations above 90 mM, the efficiency of DSSCs decreased because of the precipitation of dye on the TiO2 nanostructure. This raises the number of inactive dye molecules on the surface of TiO2 , preventing the electron injection processes in DSSCs. 1.8 Nomenclature 1.6 𝐴: Intensity of the UV-Vis absorption (—) 𝑐: Solution concentration (molar) 𝑙: Path length of the light beam (cm). 1.4 Absorbance 1.2 1 0.8 Greek Letters 𝜀: Molar extinction coefficient (M−1 cm−1 ) 𝜂: Efficiency (%). 0.6 0.4 0.2 Competing Interests 0 450 500 550 600 650 700 750 800 Wavelength (nm) N719 60 mM 70 mM 80 mM 90 mM 100 mM The authors declare that they have no competing interests. Acknowledgments Figure 5: UV-Vis absorption spectra of the solutions containing dyes detached from TiO2 electrode. The authors thank the Rector of Sebelas Maret University (UNS) and DP2M DIKTI for the financial support through the research Grant Nr.632/UN27.21/LT/2016. Increasing the concentration of chlorophyll dyes increased the DSSC efficiency and was seen by the increase in the current density (𝐽SC ). The rise in current density is associated with the amount of dye that can be adsorbed by the TiO2 electrodes [1]. However, at concentrations above 90 mM, the dye loading value increased, while the efficiency of DSSCs decreased. This result can be explained by the precipitation of dyes on the TiO2 electrodes. Because of this phenomenon, some dissolution of TiO2 by the acidic carboxylic groups of the dye can occur. The resulting Ti+ ions form insoluble complexes with chlorophyll dyes, causing precipitation of these complexes in the pores of the film. This gives rise to inactive dye molecules on the TiO2 surfaces [20, 23]. Based on this work, it has been found that the concentration References [1] Y. Ooyama and Y. Harima, “Photophysical and electrochemical properties, and molecular structures of organic dyes for dyesensitized solar cells,” ChemPhysChem, vol. 13, no. 18, pp. 4032– 4080, 2012. [2] Suyitno, A. Zainal, A. S. Ahmad, T. S. Argatya, and Ubaidillah, “Optimization parameters and synthesis of fluorine doped tin oxide for dye-sensitized solar cells,” Applied Mechanics and Materials, vol. 575, pp. 689–695, 2014. [3] S. Ito, T. N. Murakami, P. Comte et al., “Fabrication of thin film dye sensitized solar cells with solar to electric power conversion efficiency over 10%,” Thin Solid Films, vol. 516, no. 14, pp. 4613– 4619, 2008. International Journal of Photoenergy [4] M. Grätzel, “Dye-sensitized solar cells,” Journal of Photochemistry and Photobiology C: Photochemistry Reviews, vol. 4, no. 2, pp. 145–153, 2003. [5] J. Hu, J. Cheng, S. Tong, Y. Yang, M. Chen, and S. Hu, “Ag-doped TiO2 nanotube arrays composite film as a photoanode for enhancing the photoelectric conversion efficiency in DSSCs,” International Journal of Photoenergy, vol. 2016, Article ID 2736257, 9 pages, 2016. [6] M. Kouhnavard, N. Ahmad Ludin, B. Vazifehkhah Ghaffari, K. Sopian, N. Abdul Karim, and M. Miyake, “An efficient metal-free hydrophilic carbon as a counter electrode for dyesensitized solar cells,” International Journal of Photoenergy, vol. 2016, Article ID 5186762, 7 pages, 2016. [7] I. N. Obotowo, I. B. Obot, and U. J. Ekpe, “Organic sensitizers for dye-sensitized solar cell (DSSC): properties from computation, progress and future perspectives,” Journal of Molecular Structure, vol. 1122, pp. 80–87, 2016. [8] K. E. Jasim, S. Al-Dallal, and A. M. Hassan, “Henna (Lawsonia inermis L.) dye-sensitized nanocrystalline titania solar cell,” Journal of Nanotechnology, vol. 2012, Article ID 167128, 6 pages, 2012. [9] N. Li, N. Pan, D. Li, and S. Lin, “Natural dye-sensitized solar cells based on highly ordered TiO2 nanotube arrays,” International Journal of Photoenergy, vol. 2013, Article ID 598753, 5 pages, 2013. [10] R. Syafinar, N. Gomesh, M. Irwanto, M. Fareq, and Y. M. Irwan, “Chlorophyll pigments as nature based dye for dye-sensitized solar cell (DSSC),” Energy Procedia, vol. 79, pp. 896–902, 2015. [11] S. Suyitno, T. J. Saputra, A. Supriyanto, and Z. Arifin, “Stability and efficiency of dye-sensitized solar cells based on papaya-leaf dye,” Spectrochimica Acta—Part A: Molecular and Biomolecular Spectroscopy, vol. 148, pp. 99–104, 2015. [12] Y. Dou, F. Wu, L. Fang et al., “Enhanced performance of dyesensitized solar cell using Bi2 Te3 nanotube/ZnO nanoparticle composite photoanode by the synergistic effect of photovoltaic and thermoelectric conversion,” Journal of Power Sources, vol. 307, pp. 181–189, 2016. [13] N. Sakai, T. Miyasaka, and T. N. Murakami, “Efficiency enhancement of ZnO-based dye-sensitized solar cells by lowtemperature TiCl4 treatment and dye optimization,” Journal of Physical Chemistry C, vol. 117, no. 21, pp. 10949–10956, 2013. [14] Z.-S. Wang, H. Kawauchi, T. Kashima, and H. Arakawa, “Significant influence of TiO2 photoelectrode morphology on the energy conversion efficiency of N719 dye-sensitized solar cell,” Coordination Chemistry Reviews, vol. 248, no. 13-14, pp. 1381–1389, 2004. [15] T. P. Chou, Q. Zhang, B. Russo, G. E. Fryxell, and G. Cao, “Titania particle size effect on the overall performance of dyesensitized solar cells,” Journal of Physical Chemistry C, vol. 111, no. 17, pp. 6296–6302, 2007. [16] Z. Arifin, S. Soeparman, D. Widhiyanuriyawan, A. Purwanto, and Dharmanto, “Synthesis, characterisation, and fabrication hollow fibres of Zn-doped TiO2 for dye-sensitized solar cells,” Journal of Engineering Science & Technology, In press. [17] F. M. Rajab, “Effect of solvent, dye-loading time, and dye choice on the performance of dye-sensitized solar cells,” Journal of Nanomaterials, vol. 2016, Article ID 3703167, 8 pages, 2016. [18] M. Shaheer Akhtar, K. K. Cheralathan, J.-M. Chun, and O.B. Yang, “Composite electrolyte of heteropolyacid (HPA) and polyethylene oxide (PEO) for solid-state dye-sensitized solar cell,” Electrochimica Acta, vol. 53, no. 22, pp. 6623–6628, 2008. 5 [19] J. M. Parnis and K. B. Oldham, “Beyond the beer-lambert law: the dependence of absorbance on time in photochemistry,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 267, pp. 6–10, 2013. [20] F. A. S. Lima, I. F. Vasconcelos, and M. Lira-Cantu, “Electrochemically synthesized mesoporous thin films of ZnO for highly efficient dye sensitized solar cells,” Ceramics International, vol. 41, no. 8, Article ID 10350, pp. 9314–9320, 2015. [21] D. Zhao, T. Peng, L. Lu, P. Cai, P. Jiang, and Z. Bian, “Effect of annealing temperature on the photoelectrochemical properties of dye-sensitized solar cells made with mesoporous TiO2 nanoparticles,” Journal of Physical Chemistry C, vol. 112, no. 22, pp. 8486–8494, 2008. [22] W. P. Inskeep and P. R. Bloom, “Extinction coefficients of chlorophyll a and b in N,N-dimethylformamide and 80% acetone,” Plant Physiology, vol. 77, no. 2, pp. 483–485, 1985. [23] K. Keis, J. Lindgren, S.-E. Lindquist, and A. Hagfeldt, “Studies of the adsorption process of Ru complexes in nanoporous ZnO electrodes,” Langmuir, vol. 16, no. 10, pp. 4688–4694, 2000. International Journal of Medicinal Chemistry Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 International Journal of Photoenergy Organic Chemistry International Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Advances in International Journal of Analytical Chemistry Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Physical Chemistry Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 International Journal of Carbohydrate Chemistry Hindawi Publishing Corporation http://www.hindawi.com Journal of Quantum Chemistry Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Volume 2014 Submit your manuscripts at https://www.hindawi.com The Scientific World Journal Hindawi Publishing Corporation http://www.hindawi.com Journal of International Journal of International Journal of Inorganic Chemistry Volume 2014 Journal of Theoretical Chemistry Hindawi Publishing Corporation http://www.hindawi.com Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Spectroscopy Hindawi Publishing Corporation http://www.hindawi.com Journal of Analytical Methods in Chemistry Volume 2014 Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Chromatography Research International Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Electrochemistry Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Journal of Applied Chemistry Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Bioinorganic Chemistry and Applications Hindawi Publishing Corporation http://www.hindawi.com Journal of Journal of International Journal of Catalysts Chemistry Spectroscopy Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Volume 2014 Hindawi Publishing Corporation http://www.hindawi.com Volume 2014 Volume 2014