Location via proxy:   [ UP ]  
[Report a bug]   [Manage cookies]                
Scribd Logo
Upload

Welcome to Scribd!

  • 698 views

    Pds Accmon 80 Revised

    Uploaded by

    Swaroop Kumar
    This document summarizes the properties of ACCMON 80, a low cement castable product that is 80% alumina. It has a maximum service temperature of 1700°C. The castable has a typical chemical composition of 79.5% Al2O3, 2.05% Fe2O3, and 2.65% CaO. Its physical properties include a typical dry density of 2.85 g/cc and compressive strengths of 750 kg/cm2 after drying and 1220 kg/cm2 after heating to 1550°C. The castable has good refractory properties with a typical refractoriness of +1820°C and +1.40% linear change after heating to 15

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    Pds Accmon 80 Revised

    Uploaded by

    Swaroop Kumar
    698 views1 page
    This document summarizes the properties of ACCMON 80, a low cement castable product that is 80% alumina. It has a maximum service temperature of 1700°C. The castable has a typical chemical composition of 79.5% Al2O3, 2.05% Fe2O3, and 2.65% CaO. Its physical properties include a typical dry density of 2.85 g/cc and compressive strengths of 750 kg/cm2 after drying and 1220 kg/cm2 after heating to 1550°C. The castable has good refractory properties with a typical refractoriness of +1820°C and +1.40% linear change after heating to 15

    Original Description:

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document summarizes the properties of ACCMON 80, a low cement castable product that is 80% alumina. It has a maximum service temperature of 1700°C. The castable has a typical chemical composition of 79.5% Al2O3, 2.05% Fe2O3, and 2.65% CaO. Its physical properties include a typical dry density of 2.85 g/cc and compressive strengths of 750 kg/cm2 after drying and 1220 kg/cm2 after heating to 1550°C. The castable has good refractory properties with a typical refractoriness of +1820°C and +1.40% linear change after heating to 15

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    698 views1 page

    Pds Accmon 80 Revised

    Uploaded by

    Swaroop Kumar
    This document summarizes the properties of ACCMON 80, a low cement castable product that is 80% alumina. It has a maximum service temperature of 1700°C. The castable has a typical chemical composition of 79.5% Al2O3, 2.05% Fe2O3, and 2.65% CaO. Its physical properties include a typical dry density of 2.85 g/cc and compressive strengths of 750 kg/cm2 after drying and 1220 kg/cm2 after heating to 1550°C. The castable has good refractory properties with a typical refractoriness of +1820°C and +1.40% linear change after heating to 15

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    LOW CEMENT CASTABLE

    PRODUCT TYPE NATURE OF BOND INSTALLATION

    : : : :

    ACCMON 80 80% ALUMINA LC CASTABLE HYDRAULIC VIBRATION CASTING

    GENERAL PROPERTIES
    MAX. SERVICE TEMPERATURE: MAXIMUM GRAIN SIZE: WATER REQUIRED FOR CASTING: 1700 C 6 mm 4.5 5.2 %

    CHEMICAL ANALYSIS, %
    Al2O3 Fe2O3 CaO RANGE 78 81 1.70 2.20 2.5 2.70 TYPICAL VALUE 79.5 2.05 2.65 TEST PROCEDURE BIS 12107 Part 3 BIS 12107 Part 6 ASTM C 573

    PHYSICAL PROPERTIES
    RANGE Dry density, g / cc after drying at 110 C / 24 hrs CCS, kg/cm2 after drying at 110 C / 24 hrs after heating at 1100 C / 3 hrs after heating at 1550 C / 3 hrs % Retained on maximum size 2.80 2.95 700 850 850 1000 1100 1250 05 TYPICAL VALUE 2.85 750 990 1220 4.0 TEST PROCEDURE BIS 10570 BIS 10570 BIS 10570 BIS 10570 BIS 1528 Part 14

    THERMAL PROPERTIES
    RANGE Refractoriness, Orton / C PLC, % after heating at 1550 C / 3 hrs Packaging: 50 kg bags TYPICAL VALUE + 37 / + 1820 +1.40 TEST PROCEDURE BIS 1528 Part 1 BIS 10570

    (+ 1.8) to ( 0.5)

    Delivery State: Dry

    Storage Life: Best till 6 months from the date of production, if stored in proper condition.
    07 / 2010

    Note: (1) The data are current production averages. They can not be used as limits for specification. (2) Extended Storage Life can be achieved when the product is supplied in 2 pack.

    PD / LC / 08