Especificacion API 5l
Especificacion API 5l
Especificacion API 5l
Stock Program
Contents
Our Stock Program
High Yield Seamless Pipes (API 5L X52/X65 PSL 2) High Yield SAW Welded Pipes (API 5L X52/X56/X65 PSL 2) High Yield Offshore Plates (API / EN / Norsok) High Yield Offshore Sections (EN 10225 S355 G11+M) 6 7 8 9
Pipes - API 5L Grade X52 PSL 2 Seamless - API 5L Grade X65 PSL 2 Seamless - API 5L Grade X65 PSL 2 SAW Welded
12 14 16 18 20 22 24 26 28 30 32 34 36
Plates - API 2W Gr 50 - API 2W Gr 60 - EN 10225 S355 G10+M - EN 10225 S420 G2+M - EN 10225 S460 G2+M - EN 10025-4 S460 ML - Norsok M-120 Y20 - Norsok M-120 Y30 - Norsok M-120 Y40 Sections - EN 10225 S355 G11+M
Appendices
Pipe Schedule 40 Useful Formulas / Conversions 42 Comparison API 5L: PSL 1 versus PSL 2 42 Material Grade Comparison Chart 43
High Yield Seamless Pipes (API 5L X52/X65 PSL 2) High Yield SAW Welded Pipes (API 5L X52/X56/X65 PSL 2) High Yield Offshore Plates (API / EN / Norsok) High Yield Offshore Sections (EN 10225 S355 G11+M)
Diameter (mm)
114.3 114.3 114.3 114.3 114.3 141.3 141.3 141.3 168.3 168.3 168.3
Length (mm)
12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 1200 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 6000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000
Weight/Piece (MT)
0.193 0.203 0.249 0.268 0.492 0.261 0.372 0.483 0.339 0.389 0.447 0.511 0.585 0.651 0.811 0.951 0.512 0.589 0.637 0.776 0.956 1.085 1.456 0.726 0.743 0.979 1.210 1.377 1.436 1.651 1.862 1.034 0.884 1.170 1.308 1.449 1.585 1.723 1.919 2.244 0.973 1.289 1.599 1.902 2.340 2.482
168.3 168.3 168.3 168.3 168.3 219.1 219.1 219.1 219.1 219.1 219.1 219.1 273.1 273.1 273.1 273.1 273.1 273.1 273.1
10
100
273.1 273.1 323.9 323.9 323.9 323.9 323.9 323.9 323.9 323.9 355.6 355.6 355.6 355.6 355.6 355.6
Size (inch)
Schedule
STD/ 30 XS/ 40 60 80
Diameter (mm)
406.4 406.4 406.4 406.4 406.4 406.4 406.4 406.4
Length (mm)
12000 12000 12000 12000 12000 12000 12000 12000
Unit/Weight (kg/mtr)
93.19 123.32 153.14 160.15 182.46 203.57 238.69 245.60
Weight/Piece (MT)
1.118 1.480 1.838 1.922 2.189 2.443 2.864 2.947
16
Supply Condition
Origin: Sumitomo Metal Industries, Ltd. (Japan) Specification: API 5L X52 PSL 2 Certificate: EN10204 3.2 Charpy Value: Min 34J at -50C Heat Treatment: Q & T Origin: Sumitomo Metal Industries, Ltd. (Japan) Specification: API 5L X65 PSL 2 Certificate: EN10204 3.2 Charpy Value: Min 34J at -50C Heat Treatment: Q & T Origin: Specification: Certificate: Charpy Value: Heat Treatment: HengYang Valin Steel Tube Co., Ltd. (China) API 5L X52 PSL 2 EN10204 3.2 Min 34J at -40C Normalized / Q & T
Diameter (mm)
457.2 457.2 457.2 457.2 457.2
Length (mm)
12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000 12000
Weight/Piece (MT)
1.671 2.077 2.477 3.246 4.004 1.862 2.316 2.764 3.628 4.482 2.245 2.796 3.340 4.395 5.442 6.449 3.913 5.156 6.395 5.538 6.873 8.163
XS/ 30 20
XS
24
28
30
762.0 762.0
Supply Condition
Origin: Steel Flower Co., Ltd. (Korea) Specification: API 5L X65, PSL 2 with Supplementary tests Certificate: EN10204 3.2 Charpy Value: Min 45J at -40C Heat Treatment: TMCP Origin: Sumitomo Metal Industries, Ltd. (Japan) Specification: API 5L X52/X56/X65, PSL 2 with Supplementary tests Certificate: EN10204 3.2 Charpy Value: Min 45J at -40C
Supply Condition
Origin: Voestalpine Grobblech GmbH (Austria) POSCO (Korea) Dillinger Htte GTS (Germany) API EN Specification: 2W Gr 50 2W Gr 60 10225 S355 G10+M/N 10225 S420 G2+M 10225 S460 G2+M 10025 S460 ML Certificate: EN10204 3.2 Charpy Value: Min 41J at -40C Heat Treatment: TMCP / Normalized
Supply Condition
Origin: Specification: Certificate: Charpy Value: ArcelorMittal Long Carbon Europe (Luxembourg) Peiner Trger GmbH (Germany) Gallardo Sections (Germany) EN 10225 S355 G11+M EN10204 3.2 Min 50J at -40C
Pipes - API 5L Grade X52 PSL 2 Seamless - API 5L Grade X65 PSL 2 Seamless - API 5L Grade X65 PSL 2 SAW Welded Plates - API 2W Gr 50 - API 2W Gr 60 - EN 10225 S355 G10+M - EN 10225 S420 G2+M - EN 10225 S460 G2+M - EN 10025-4 S460 ML - Norsok M-120 Y20 - Norsok M-120 Y30 - Norsok M-120 Y40 Sections - EN 10225 S355 G11+M
API 5L, 44th Edition Specification for line pipe - technical delivery conditions
Grade
X
The X symbol followed by a two or three digit number equal to the specified minimum yield strength in 1000 psi rounded down to the nearest integer.
X 52 Q PSL 2
Minimum Yield
At pipe body 360 MPa (52,200 psi)
Delivery condition
+ N Normalizing rolling + Q Quenched and tempered where Q refers to a heat treatment process consisting of quench hardening followed by tempering.
PSL
PSL refers to the product specification level where PSL2 provides a more extensive chemical composition complete with a mandatory minimum fracture toughness.
- The steel pipe mentioned herein is substantially modified from the API 5L, X52 standard. - Pipes are fully killed and fine grain steel material. - NACE MR0175:Satisfactory - This steel offers enhanced yield tensile ratio of 0.87 (max) and impact values verified from as low as -50C. - This grade is also known as L360Q in USC Units.
Cr+Mo+Ni+Cu Nb+V Nb+V+Ti CEV (IIW) see formula below Pcm see formula below
Bi Ca B
CEV = C +
1 2
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
All nitrogen shall be tied up as nitrides. Al (total) to N ratio shall be at least 2.2:1 CEV & Pcm may vary as wall thickness of pipe increases.
Mechanical properties
Thickness t
mm -
Tensile Rm
MPa Min. 460 Max. 760
Reh / Rm
max. 0,87
CVN
-50 C min. 36J avg. 42J transverse
El
% min. 22
Surface (a) All surfaces have been 100% visually inspected. The surface condition complies with API 5L Annex E. (b) External surface of pipe shall be coated with a layer of varnish. NDT All pipes will be ultrasonic tested on pipe body and pipe end as per API 5L Annex E, Table E.2 and para E.3.3. Coverage: (a) longitudinal: 100% of the pipe surface (b) pipe ends not scanned by automatic ultrasonic system shall be inspected by manual UT or Magnetic Particle Examination. Hydrostatic test (a) Test pressure may not exceed 2970 psi in accordance to API 5L requirements (b) Holding time: minimum 5 seconds Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Marking shall be in SI units (X52) accordance with API requirements & mill standard. Dimensional control All dimensions will be supplied according to API 5L clause 9.11; In addition, the following tolerances apply: (a) Pipe body: +/- 0,75% (b) Pipe end: +/- 0,5% (c) Wall thickness: +15%, -12,5% (d) Length: -0 / +100mm Pipe Ends Pipe Ends are bevelled. End angle shall be 30- 0/+5, root face shall be 1.6mm +/- 0.8mm and fitted with bevel protectors. Protection Pipes are varnished on the outside.
API 5L, 44th Edition Specification for line pipe - technical delivery conditions
Grade
X
The X symbol followed by a two or three digit number equal to the specified minimum yield strength in 1000 psi rounded down to the nearest integer.
X 65 Q PSL 2
Minimum Yield
At pipe body 450 MPa (65,300 psi)
Delivery condition
+ N Normalizing rolling + Q Quenched and tempered where Q refers to a heat treatment process consisting of quench hardening followed by tempering.
PSL
PSL refers to the product specification level where PSL2 provides a more extensive chemical composition complete with a mandatory minimum fracture toughness.
- The steel pipe mentioned herein is substantially modified from the API 5L, X65 standard. - Pipes are fully killed and fine grain steel material. - NACE MR0175:Satisfactory - This steel offers enhanced yield tensile ratio of 0.87 (max) and impact values verified from as low as -30C. - This grade is also known as L450Q in USC Units.
Cu N Nb1 Ti V As Sb Sn Pb
Cr+Mo+Ni+Cu Nb+V Nb+V+Ti CEV (IIW) see formula below Pcm see formula below
Bi Ca B
CEV = C +
1 2 3
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
All nitrogen shall be tied up as nitrides. Al (total) to N ratio shall be at least 2.2:1 CEV & Pcm may vary as wall thickness of pipe increases. Mo, max 0.25% for thickness (t) > 25mm. 4 Max 0.60% for thickness (t) > 25mm.
Mechanical properties
Thickness t
mm -
Tensile Rm
MPa Min. 535 Max. 760
Reh / Rm
max. 0,93
CVN
-30 C min. 36J avg. 42J transverse
El
% min. 22
Surface (a) All surfaces have been 100% visually inspected. The surface condition complies with API 5L Annex E. (b) External surface of pipe shall be coated with a layer of varnish. NDT All pipes will be ultrasonic tested on pipe body and pipe end as per API 5L Annex E, Table E.2 and para E.3.3. Coverage: (a) longitudinal: 100% of the pipe surface (b) pipe ends not scanned by automatic ultrasonic system shall be inspected by manual UT or Magnetic Particle Examination. Hydrostatic test (a) Test pressure may not exceed 2970 psi in accordance to API 5L requirements (b) Holding time: minimum 5 seconds Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Marking shall be in SI units (X65) accordance with API requirements & mill standard. Dimensional control All dimensions will be supplied according to API 5L clause 9.11; In addition, the following tolerances apply: (a) Pipe body: +/- 0,75% (b) Pipe end: +/- 0,5% (c) Wall thickness: +15%, -12,5% (d) Length: -0 / +100mm Pipe Ends Pipe Ends are bevelled. End angle shall be 30- 0/+5, root face shall be 1.6mm +/- 0.8mm and fitted with bevel protectors. Protection Pipes are varnished on the outside.
API 5L, 44th Edition Specification for line pipe - technical delivery conditions
Grade
X
The X symbol followed by a two or three digit number equal to the specified minimum yield strength in 1000 psi rounded down to the nearest integer.
X 65 M PSL 2
Minimum Yield
At pipe body 450 MPa (65,300 psi)
Delivery condition
+ M Thermo mechanical rolling + N Normalizing rolling + Q Quenched and tempered Thermo mechanical rolling is a rolling process in which the final deformation is carried out in a particular temperature range leading to a material condition equivalent with certain properties which cannot be achieved or repeated by a heat treatment alone.
PSL
PSL refers to the product specification level where PSL2 provides a more extensive chemical composition complete with a mandatory minimum fracture toughness.
- The steel pipe mentioned herein is substantially modified from the API 5L, X65 standard. - Pipes are fully killed and fine grain steel material. - This steel offers enhanced yield tensile ratio of 0.90 (max) and impact values verified from as low as -40C. - This grade is also known as L450M in USC Units.
Bi Ca B
CEV = C +
1
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
All nitrogen shall be tied up as nitrides. Al (total) to N ratio shall be at least 2.2:1
Mechanical properties
Thickness t
mm -
Tensile Rm
MPa Min. 535 Max. 760
Reh / Rm
max. 0,90
CVN
-40 C min. 31J avg. 45J transverse
El
% min. 22
Surface (a) All surfaces have been 100% visually inspected. The surface condition complies with API 5L Annex E. (b) External surface of pipe shall be coated with a layer of varnish. NDT All pipes will be ultrasonic tested on pipe body and pipe end as per API 5L Annex E, Table E.1 and para E.4. Coverage: (a) longitudinal: 100% of the pipe surface (b) pipe ends not scanned by automatic ultrasonic system shall be inspected by manual UT or Magnetic Particle Examination. (c) Area with any indication exceeding the acceptance criteria by automatic/manual UT shall be inspected by radiographic test. Hydrostatic test (a) Test pressure may not exceed 2970 psi in accordance to API 5L requirements (b) Holding time: minimum 5 seconds Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Marking shall be in SI units (X65) accordance with API requirements & mill standard. Dimensional control All dimensions will be supplied according to API 5L clause 9.11; In addition, the following tolerances apply: (a) Pipe body: +/- 0,75% (b) Pipe end: +/- 0,5% (c) Wall thickness: +15%, -12,5% (d) Length: -0 / +50mm Pipe Ends Pipe Ends are bevelled. End angle shall be 30+/- 2.5, root face shall be 1.6mm +/- 0.8mm and fitted with bevel protectors. Protection Pipes are varnished on the outside. Other Technical Properties (a) Through-Thickness tests conducted to meet class Z35 as per ASTM A370 (from wall thickness 19.1mm). (b) Low sulphur content - all pipes possess sulphur content not more than 0.006%.
API 2W, 2006 edition specifies high strength steel plates for offshore structures, produced by thermo-mechanical controlled processing.
Grade
Structural
API 2W steels are intended for fabrication primarily by cold forming and welding.
Grade 50 LS Z35
Minimum Yield (expressed in ksi)
t 25 mm 345 - 517 MPa 25 < t 40 mm 345 - 483 MPa 40 < t 63 mm 345 - 483 MPa 63 < t 80 mm 345 - 483 MPa 80 < t 100 mm 345 - 483 MPa
Z35
Through thickness testing when called for via option S4. Min Tensile 358 MPa (=80% of 448 MPa).
The primary use of these steels is in tubular joints, stiffened plate construction and other intersections where portions of the plate will be subject to tension in the thickness direction. Supplementary requirement S4 provides for through-thickness testing of plates and specifies limits for acceptance. This steel offers enhanced through thickness ductility and impact values verified at minus -40C.
Chemical composition
C Si Mn P S Cr Mo Ni Al
4
0,35 0,012
2
Cr+Mo+Ni+V Nb+V Nb+V+Ti CEV (IIW) see formula below Pcm see formula below
t 40 mm: 0,39 40 <t 90 mm: 0,41 40< t 150 mm: 0,43 t 40 mm: 0,22 40 <t 90 mm: 0,23 40< t 150 mm: 0,24
Nb Ti V As3 Sb Sn Pb
0,030 0,025 -
Bi Ca B3
0,0005
CEV = C +
1 2 3
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
Nitrogen shall not be intentional added Nitrogen may be max 0,013% if titanium is 0,010-0,020% Boron shall not be intentional added 4 Acid Solublerange or otherwise a total of 0,02-0,06%
Mechanical properties
Grade 50 Thickness t
mm t 16 16 < t 25 25 < t 40 40 < t 63 63 < t 80 80 < t 100 345-483
Yield Reh
MPa 345-517
Tensile Rm
MPa
Reh / Rm
-
CVN
-40 C
El
%
min. 448
41/34J transverse
in 2, min 23
Subject
UT Tensile test Through Thickness Testing Low Sulphur Strain ageing* PWHT* Hardness* Weldability* Drop weight testing*
Remarks
According to EN 10160 S1/E2 or ASTM A578 Additional tensile test shall be taken for head and tail corner of each parent-plate TTP testing meeting class Z35 according to ASTM A370 or EN 10164. S 0,006% Strain ageing tests are carried out for thicknesses greater than or equal to 12,5 mm. Plastic strain 5%, aged for 1h at 250C. Transverse CEV-values in strain aged condition min. 41/34J at -40C For t > 40mm tensile and impact testing in PWHT condition Hardness tested according to Vickers Pre qualification for thicknesses 40 mm up to 75 mm in accordance with API RP2Z For plates over 16 mm thickness. Thickest plate per lot. No break at minus 35C acc ASTM E208
Surface All surfaces have been 100% visually inspected. The surface condition does comply with EN 10163-2, class A, sub-class 3. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Low stress die-stamping on head and tail of each plate.
API 2W, 2006 edition specifies high strength steel plates for offshore structures, produced by thermo-mechanical controlled processing.
Grade
Structural
API 2W steels are intended for fabrication primarily by cold forming and welding.
Grade 60 LS Z35
Minimum Yield (expressed in ksi)
t 25 mm 414 - 621 MPa 25 < t 40 mm 414 - 586 MPa 40 < t 63 mm 414 - 586 MPa 63 < t 80 mm 414 - 586 MPa 80 < t 100 mm 414 - 586 MPa
Z35
Through thickness testing when called for via option S4. Min Tensile 376MPa
The primary use of these steels is in tubular joints, stiffened plate construction and other intersections where portions of the plate will be subject to tension in the thickness direction. Supplementary requirement S4 provides for through-thickness testing of plates and specifies limits for acceptance. This steel offers enhanced through thickness ductility and impact values verified at minus -40C.
Chemical composition
C Si Mn P S Cr Mo Ni Al4
0,35 0,012
2
Cr+Mo+Ni+Cu Nb+V Nb+V+Ti CEV (IIW) see formula below Pcm see formula below
t 40 mm: 0,42 40 <t 100 mm: 0,45 t 40 mm: 0,23 40 <t 100 mm: 0,25
Nb Ti V As3 Sb Sn Pb
0,030 0,02 -
Bi Ca B3
0,0005
CEV = C +
1 2
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
Nitrogen shall not be intentional added Nitrogen may be max 0,013% if titanium is 0,010-0,020% 3 Boron shall not be intentional added 4 Acid Solublerange or otherwise a total of 0,02-0,06%
Mechanical properties
Grade 60 Thickness t
mm t 16 16 < t 25 25 < t 40 40 < t 63 63 < t 80 80 < t 100 414-586
Yield Reh
MPa 414-621
Tensile Rm
MPa
Reh / Rm
-
CVN
-40 C
El
%
min. 517
48/41J transverse
in 2, min 22
Subject
UT Tensile test Through Thickness Testing Low Sulphur Strain ageing* PWHT* Hardness* Weldability* Drop weight testing*
Remarks
According to EN 10160 S1/E2 or ASTM A578 Additional tensile test shall be taken for head and tail corner of each parent-plate TTP testing meeting class Z35 according to ASTM A370 or EN 10164. S 0,006% Strain ageing tests are carried out for thicknesses greater than or equal to 12,5 mm. Plastic strain 5%, aged for 1h at 250C. Transverse CEV-values in strain aged condition min. 41/34J at -40C For t > 40mm tensile and impact testing in PWHT condition Hardness tested according to Vickers Pre qualification for thicknesses 40 mm up to 75 mm in accordance with API RP2Z For plates over 16 mm thickness. Thickest plate per lot. No break at minus 35C acc ASTM E208
Surface All surfaces have been 100% visually inspected. The surface condition does comply with EN 10163-2, class A, sub-class 3. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Low stress die-stamping on head and tail of each plate.
BS- EN 10225:2009 Weldable structural steels for fixed offshore structures - technical delivery conditions.
Grade
Structural
Symbol indicating that the following figures specify the minimum yield strength in MPa. (MPa = N/mm2)
S 355 G 10 +M
Minimum Yield
In MPa for thicknesses t 16mm. t 16 mm 355 MPa t 25 mm 355 MPa t 40 mm 345 MPa t 63 mm 335 MPa t 100 mm 325 MPa
Letter G
Followed by a maximum of two digits characterizing and indicating the steel grade within the groups 1, 2 or 3, as defined per table 4 of EN 10225.
Delivery condition
+ M Thermo mechanical rolling + N Normalizing rolling + Q Quenched and tempered Thermo mechanical rolling is a rolling process in which the final deformation is carried out in a particular temperature range leading to a material condition equivalent with certain properties which cannot be achieved or repeated by a heat treatment alone.
Within EN 10225 this steel is designated as a group 3 steel which means that this grade is substantially modified from EN 10025-4. This steel offers enhanced through thickness ductility and impact values verified at -40C. This grade is also known as 1.8813+M.
Chemical composition
C Si Mn P S Cr Mo Ni Al
3
Cr+Mo+Ni+Cu Nb+V Nb+V+Ti CEV (IIW) see formula below Pcm see formula below
0,06 0,08 T 75mm: 0,41 T > 75mm: 0,42 T 75mm: 0,21 T > 75mm: 0,22
Bi2 Ca B
2
2 2
Pb
CEV = C +
1 2 3
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
As per paragraph 8.2.3.2 of EN 10225 the Pcm-value shall apply (instead of the CEV-value, see option 9) Residual elements shall be checked once every 5.000 tons per manufacturing location and shall be reported as a ladle analysis For T > 75 mm with supply condition +M the maximum Mo content shall be 0,20% 4 For T > 40 mm the minimum Ni content shall be 0,30% 5 The total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding elements are used the minimum Al value and Al:N ratio does not apply
Mechanical properties
S355G10+M Thickness t
mm t 16 < t 25 < t 40 < t 16 25 40 63
Yield Reh
MPa (min.) 355 355 345 335 325
Tensile Rm
MPa
Reh / Rm
max. 0,93
CVN
-40 C
El
%
470-630
max. 0,90
50J transverse
22
63 < t 100
Subject
PWHT* Strain ageing* Through Thickness Testing Low Sulphur Hardness Weldability*
Remarks
Mechanical tests include SPWHT condition for thicknesses greater than 40 mm Strain ageing tests are carried out for thicknesses greater than or equal to 12,5 mm. Plastic strain 5%, aged for 1h at 250C. Transverse CEV-values in strain aged condition min. 36/26J at -40C TTP testing for thicknesses 15 mm. To meet class Z35 according to EN 10164. Through thickness strengths min 80% of specified minimum tensile strength for specified thickness S 0,005% in combination with above option 13 Hardness tested according to Vickers Pre qualification for thicknesses 40 mm up to 75 mm
Surface All surfaces have been 100% visually inspected. The surface condition does comply with EN 10163-2, class A, sub-class 3. NDT All plates have been ultrasonically tested in accordance with EN 10160. Ultrasonic testing has been carried out either prior to, or after the final heat treatment and does meet the requirements of EN 10160, class S1/E2 for steels of group 3. According EN 10225 this steel designated a group 3 steel. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Low stress die-stamping on head and tail of each plate. Dimensional control All dimensions will be supplied according to EN 10029, flatness class N, thickness class A.
BS- EN 10225:2009 Weldable structural steels for fixed offshore structures - technical delivery conditions.
Grade
Structural
Symbol indicating that the following figures specify the minimum yield strength in MPa. (MPa = N/mm2)
S 420 G 2 +M
Minimum Yield
In MPa for thicknesses t 16mm. t 16 mm 420 MPa 16 < t 40 mm 400 MPa 40 < t 63 mm 390 MPa 63 < t 100 mm 380 MPa
Letter G
Followed by a maximum of two digits characterizing and indicating the steel grade within the groups 1, 2 or 3, as defined per table 4 of EN 10225.
Delivery condition
+ M Thermo mechanical rolling + N Normalizing rolling + Q Quenched and tempered Thermo mechanical rolling is a rolling process in which the final deformation is carried out in a particular temperature range leading to a material condition equivalent with certain properties which cannot be achieved or repeated by a heat treatment alone.
Within EN 10225 this steel is designated as a group 3 steel which means that this grade is substantially modified from EN 10025-4. This steel offers enhanced through thickness ductility and impact values verified at -40C. This grade is also known as 1.8857+M.
Chemical composition
C Si Mn P S Cr Mo Ni Al3
Cr+Mo+Ni+Cu Nb+V Nb+V+Ti CEV (IIW) see formula below Pcm see formula below
Bi2 Ca2 B
2
2 2
Pb
CEV = C +
1 2
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
As per paragraph 8.2.3.2 of EN 10225 the CEV-value shall apply (instead of the Pcm-value, see option 9) Residual elements shall be checked once every 5.000 tons per manufacturing location and shall be reported as a ladle analysis 3 The total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding elements are used the minimum Al value and Al:N ratio does not apply 4 A maximum carbon value of 0.15% is permitted for thichkenss less than 15mm
Mechanical properties
S420G2+M Thickness t
mm t 16 16 < t 40 40 < t 63 63 < t 100
Yield Reh
MPa (min.) 420 400 390 380
Tensile Rm
MPa 500 - 660
Reh / Rm
max. 0,93
CVN
-40 C
El
%
480 - 640
max. 0,90
60J transverse
19
Subject
PWHT* Strain ageing* Through Thickness Testing Low Sulphur Hardness Weldability*
Remarks
Mechanical tests include SPWHT condition for thicknesses greater than 40 mm Strain ageing tests are carried out for thicknesses greater than or equal to 12,5 mm. Plastic strain 5%, aged for 1h at 250C. Transverse CEV-values in strain aged condition min. 36/26J at -40C TTP testing for thicknesses 15 mm. To meet class Z35 according to EN 10164. Through thickness strengths min 80% of specified minimum tensile strength for specified thickness S 0,005% in combination with above option 13 Hardness tested according to Vickers Pre qualification for thicknesses 40 mm up to 75 mm
Surface All surfaces have been 100% visually inspected. The surface condition does comply with EN 10163-2, class A, sub-class 3. NDT All plates have been ultrasonically tested in accordance with EN 10160. Ultrasonic testing has been carried out either prior to, or after the final heat treatment and does meet the requirements of EN 10160, class S1/E2 for steels of group 3. According EN 10225 this steel designated a group 3 steel. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Low stress die-stamping on head and tail of each plate. Dimensional control All dimensions will be supplied according to EN 10029, flatness class N, thickness class A.
BS- EN 10225:2009 Weldable structural steels for fixed offshore structures - technical delivery conditions.
Grade
Structural
Symbol indicating that the following figures specify the minimum yield strength in MPa. (MPa = N/mm2)
S 460 G 2 +M
Minimum Yield
In MPa for thicknesses t 16mm. t t t t t t 16 mm 460 MPa 25 mm 440 MPa 40 mm 420 MPa 63 mm 415 MPa 80 mm 405 MPa 100 mm 400 MPa
Letter G
Followed by a maximum of two digits characterizing and indicating the steel grade within the groups 1, 2 or 3, as defined per table 4 of EN 10225.
Delivery condition
+ M Thermo mechanical rolling + N Normalizing rolling + Q Quenched and tempered Thermo mechanical rolling is a rolling process in which the final deformation is carried out in a particular temperature range leading to a material condition equivalent with certain properties which cannot be achieved or repeated by a heat treatment alone.
Within EN 10225 this steel is designated as a group 3 steel which means that this grade is substantially modified from EN 10025-4. This steel offers enhanced through thickness ductility and impact values verified at -40C. This grade is also known as 1.8887+M.
Chemical composition
C Si Mn P S Cr Mo Ni Al
3
Cr+Mo+Ni+Cu Nb+V Nb+V+Ti CEV (IIW) see formula below Pcm see formula below
Bi2 Ca B
2
2 2
Pb
CEV = C +
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
As per paragraph 8.2.3.2 of EN 10225 the CEV-value shall apply (instead of the Pcm-value, see option 9) Residual elements shall be checked once every 5.000 tons per manufacturing location and shall be reported as a ladle analysis 3 The total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding elements are used the minimum Al value and Al:N ratio does not apply
1 2
Mechanical properties
S460G2+M Thickness t
mm t 16 16 < t 25 25 < t 40 40 < t 63 63 < t 80 80 < t 100
Yield Reh
MPa (min.) 460 440 420 415 405 400
Tensile Rm
MPa 540-700 530-690 520-680 515-675 505-665 500-660
Reh / Rm
max. 0,93
CVN
-40 C
El
%
max. 0,90
60J transverse
17
Subject
PWHT* Strain ageing* Through Thickness Testing Low Sulphur Hardness Weldability*
Remarks
Mechanical tests include SPWHT condition for thicknesses greater than 40 mm Strain ageing tests are carried out for thicknesses greater than or equal to 12,5 mm. Plastic strain 5%, aged for 1h at 250C. Transverse CEV-values in strain aged condition min. 36/26J at -40C TTP testing for thicknesses 15 mm. To meet class Z35 according to EN 10164. Through thickness strengths min 80% of specified minimum tensile strength for specified thickness S 0,005% in combination with above option 13 Hardness tested according to Vickers Pre qualification for thicknesses 40 mm up to 75 mm
Surface All surfaces have been 100% visually inspected. The surface condition does comply with EN 10163-2, class A, sub-class 3. NDT All plates have been ultrasonically tested in accordance with EN 10160. Ultrasonic testing has been carried out either prior to, or after the final heat treatment and does meet the requirements of EN 10160, class S1/E2 for steels of group 3. According EN 10225 this steel designated a group 3 steel. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Low stress die-stamping on head and tail of each plate. Dimensional control All dimensions will be supplied according to EN 10029, flatness class N, thickness class A.
BS- EN 10025-4:2004 Hot rolled products of structural steel Part 4 technical delivery conditions.
Grade
Structural
Symbol indicating that the following figures specify the minimum yield strength in MPa. (MPa = N/mm2)
S 460 M L
Minimum Yield
In MPa for thicknesses t 16mm. t t t t t t t 16 mm 460 MPa 25 mm 440 MPa 40 mm 440 MPa 63 mm 430 MPa 80 mm 410 MPa 100 mm 400 MPa 120 mm 385 MPa
Letter M
Indicating the supply condition. M: Thermo mechanical rolling and CVN values specified at -20C.
Letter L
Specified minimum charpy V-notch values at test temperature not lower than -50C.
Some publications refer to this steel type as Thermo Mechanical Controlled Processed (TMCP) steels. Thermo mechanical rolling is a rolling process in which the final deformation is carried out in a particular temperature range leading to a material condition equivalent with certain properties which cannot be achieved or repeated by heat treatment alone. S460ML is also known as steel type 1.8838.
Chemical composition
C Si Mn P S Cr Mo Ni Al2
Bi Ca B
CEV = C +
1 2
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
For lowest thickness range t 16 mm. When sufficient other nitrogen binding elements are used the minimum for Al value does not apply
Mechanical properties
S460ML Thickness t
mm t 16 16 < t 25 25 < t 40 40 < t 63 63 < t 80 80 < t 100 100 < t 120
Yield Reh
MPa 460 440 440 430 410 400 385
Tensile Rm
MPa
Reh / Rm
-
CVN
-50 C
El
%
Subject
Surface Internal soundness Mechanical prop.* Strain ageing* Hardness Through Thickness Testing
Remarks
The surface condition does comply with EN 10163-2, class A, sub-class 3. No weld repair allowed Ultrasonically test in accordance with EN 10160. Ultrasonic testing carried out either prior to, or after the final heat treatment and meets the requirements of EN 10160, class S1/E2 Mechanical tests include the PWHT condition for thicknesses greater than 40 mm Strain ageing tests are carried out for thicknesses greater than or equal to 12,5 mm Hardness tested according to Vickers TTP testing for thicknesses 15 mm. To meet class Z35 according to EN 10164. Through thickness strengths min 80% of specified minimum tensile strength for specified thickness
Surface All surfaces have been 100% visually inspected. The surface condition does comply with EN 10163-2, class A, sub-class 3. NDT Internal soundness as specified in EN 10025-1. The material shall be sound and free from such internal defects which might preclude its use for the intended purpose. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Low stress die-stamping on head and tail of each plate. Dimensional control All dimensions will be supplied according to EN 10029, flatness class N, thickness class A.
Norsok M-120 revision 5, Material Data Sheet (MDS) Y20 specifies the selected options in the referred standard and modifies requirements which supersede the corresponding requirements in that standard. The referred standard is BS-EN 10225:2009 weldable structural steel for fixed offshore structures - technical delivery conditions.
Grade
Structural
Symbol indicating that the following figures specify the minimum yield strength in MPa. (MPa = N/mm2)
S 355 G 10 +M
Minimum Yield
In MPa for thicknesses t 16mm. t 16 mm 355 MPa t 25 mm 355 MPa t 40 mm 345 MPa t 63 mm 335 MPa t 100 mm 325 MPa
Letter G
Followed by a maximum of two digits characterizing and indicating the steel grade within the groups 1, 2 or 3, as defined per table 4 of EN 10225.
Delivery condition
+ M Thermo mechanical rolling + N Normalizing rolling + Q Quenched and tempered Thermo mechanical rolling is a rolling process in which the final deformation is carried out in a particular temperature range leading to a material condition equivalent with certain properties which cannot be achieved or repeated by a heat treatment alone.
Within EN 10225 this steel is designated as a group 3 steel which means that this grade is substantially modified from EN 10025-4. This steel offers enhanced through thickness ductility and impact values verified at -40C. This grade is also known as 1.8813+M.
Chemical composition
C Si Mn P S Cr Mo Ni Al2
Bi2 Ca B
2 2
CEV = C +
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
1 As per paragraph 8.2.3.2 of EN 10225 the Pcm-value shall apply (instead of the CEV-value, see option 9) 2 Residual elements shall be checked once every 5.000 tons per manufacturing location and shall be reported as a ladle analysis 3 For T > 75 mm with supply condition +M the maximum Mo content shall be 0,20% 4 For T > 40 mm the minimum Ni content shall be 0,30% 5 The total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding elements are used the minimum Al value and Al:N ratio does not apply
Mechanical properties
S355G10+M Thickness t
mm t 16 < t 25 < t 40 < t 16 25 40 63
Yield Reh
MPa 355 355 345 335 325
Tensile Rm
MPa
Reh / Rm
0,93
CVN
-40 C
El
%
470-630
0,90
50J transverse
22
63 < t 100
Subject
PWHT Strain ageing Through Thickness Testing Low Sulphur Hardness Weldability
Remarks
Mechanical tests include SPWHT condition for thicknesses greater than 40 mm Strain ageing tests are carried out for thicknesses greater than or equal to 12,5 mm. Plastic strain 5%, aged for 1h at 250C.Transverse CEV-values in strain aged condition min. 36/26J at -40C TTP testing for thicknesses 15 mm. To meet class Z35 according to EN 10164. Through thickness strengths min 80% of specified minimum tensile strength for specified thickness %S 0,005 in combination with above option 13 Hardness tested according to Vickers Pre qualification for thicknesses 40 mm up to 75 mm
Surface All surfaces have been 100% visually inspected. The surface condition does comply with EN 10163-2, class A, sub-class 3. The Norsok M-120 MDS Y20 specifies shot blasting SA2,5 and one coat of 15 microns zinc ethyl silicate primer. However, the stock plates can also be supplied in the as rolled black condition. NDT All plates have been ultrasonically tested in accordance with EN 10160. Ultrasonic testing has been carried out either prior to, or after the final heat treatment and does meet the requirements of EN 10160, class S1/E2 for steels of group 3. According EN 10225 this steel designated a group 3 steel. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by LRS. Low stress die-stamping on head and tail of each plate. Dimensional control All dimensions will be supplied according to EN 10029.
Norsok M-120 revision 5, Material Data Sheet (MDS) Y30 specifies the selected options in the referred standard and modifies requirements which supersede the corresponding requirements in that standard. The referred standard is BS-EN 10225:2009 weldable structural steel for fixed offshore structures - technical delivery conditions.
Grade
Structural
Symbol indicating that the following figures specify the minimum yield strength in MPa. (MPa = N/mm2)
S 420 G 2 +M
Minimum Yield
In MPa for thicknesses t 16mm. t 16 mm 420 MPa 16 < t 100 mm 420 MPa
Letter G
Followed by a maximum of two digits characterizing and indicating the steel grade within the groups 1, 2 or 3, as defined per table 4 of EN 10225.
Delivery condition
+ M Thermo mechanical rolling + N Normalizing rolling + Q Quenched and tempered Thermo mechanical rolling is a rolling process in which the final deformation is carried out in a particular temperature range leading to a material condition equivalent with certain properties which cannot be achieved or repeated by a heat treatment alone.
Within EN 10225 this steel is designated as a group 3 steel which means that this grade is substantially modified from EN 10025-4. This steel offers enhanced through thickness ductility and impact values verified at -40C. This grade is also known as 1.8857+M.
Chemical composition
C Si Mn P S Cr Mo Ni Al
3
Cr+Mo+Ni+Cu Nb+V Nb+V+Ti CEV (IIW) see formula below Pcm see formula below
Bi2 Ca B
2
2 2
Pb
CEV = C +
1 2 3
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
As per Norsok requirements, the Pcm-value shall apply (instead of the CEV-value, see option 9) Residual elements shall be checked once every 5,000 tonnes per manufacturing location and shall be reported as a ladle analysis The total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding elements are used the minimum Al value and Al:N ratio does not apply
Mechanical properties
S420G2+M Thickness t
mm t 16 16 < t 100
Yield Reh
MPa 420 - 540
Tensile Rm
MPa 550 - 600
Reh / Rm
0,93 0,90
CVN
-40 C 60J transverse
El
% min. 19
Subject
PWHT Strain ageing Through Thickness Testing Low Sulphur Hardness Weldability
Remarks
Mechanical tests include SPWHT condition for thicknesses greater than 40 mm Strain ageing tests are carried out for thicknesses greater than or equal to 12,5 mm. Plastic strain 5%, aged for 1h at 250C. Transverse CEV-values in strain aged condition min. 36/26J at -40C TTP testing for thicknesses 15 mm. To meet class Z35 according to EN 10164. Through thickness strengths min 80% of specified minimum tensile strength for specified thickness %S 0,005 in combination with above option 13 Hardness tested according to Vickers Pre qualification for thicknesses 40 mm up to 75 mm
Surface All surfaces have been 100% visually inspected. The surface condition does comply with EN 10163-2, class A, sub-class 3. The Norsok M-120 MDS Y30 specifies shot blasting SA2,5 and one coat of 15 microns zinc ethyl silicate primer. However, the stock plates can also be supplied in the as rolled black condition. NDT All plates have been ultrasonically tested in accordance with EN 10160. Ultrasonic testing has been carried out either prior to, or after the final heat treatment and does meet the requirements of EN 10160, class S1/E2 for steels of group 3. According EN 10225 this steel designated a group 3 steel. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized & independent inspection agency. Low stress die-stamping on head and tail of each plate. Dimensional control All dimensions will be supplied according to EN 10029.
Norsok M-120 revision 5, Material Data Sheet (MDS) Y40 specifies the selected options in the referred standard and modifies requirements which supersede the corresponding requirements in that standard. The referred standard is: BS- EN 10225:2009 Weldable structural steels for fixed offshore structures technical delivery conditions.
Grade
Structural
Symbol indicating that the following figures specify the minimum yield strength in MPa. (MPa = N/mm2)
S 460 G 2 +M
Minimum Yield
In MPa for thicknesses t 16mm. t 16 mm 460 MPa 16 < t 100 mm 460 MPa
Letter G
Followed by a maximum of two digits characterizing and indicating the steel grade within the groups 1, 2 or 3, as defined per table 4 of EN 10225.
Delivery condition
+ M Thermo mechanical rolling + N Normalizing rolling + Q Quenched and tempered Thermo mechanical rolling is a rolling process in which the final deformation is carried out in a particular temperature range leading to a material condition equivalent with certain properties which cannot be achieved or repeated by a heat treatment alone.
Within EN 10225 this steel is designated as a group 3 steel which means that this grade is substantially modified from EN 10025-4. This steel offers enhanced through thickness ductility and impact values verified at -40C. This grade is also known as 1.8887+M.
Chemical composition
C Si Mn P S Cr Mo Ni Al
3
Cr+Mo+Ni+Cu Nb+V Nb+V+Ti CEV (IIW) see formula below Pcm see formula below
Bi2 Ca2 B
2
CEV = C +
1 2 3
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
As per Norsok requirements, the Pcm-value shall be reported (instead of the CEV-value, see option 9) Residual elements shall be checked once every 5,000 tonnes per manufacturing location and shall be reported as a ladle analysis The total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding elements are used the minimum Al value and Al:N ratio does not apply
Mechanical properties
S460G2+M Thickness t
mm t 16 16 < t 100
Yield Reh
MPa 460 - 580
Tensile Rm
MPa 550 - 600
Reh / Rm
0,93 0,90
CVN
-40 C 60J transverse
El
% min. 17
Subject
PWHT Strain ageing Hardness Through Thickness Testing
Remarks
Mechanical tests include SPWHT condition for thicknesses greater than 40 mm Strain ageing tests are carried out for thicknesses greater than or equal to 12,5 mm Hardness tested according to Vickers TTP testing for thicknesses 15 mm. To meet class Z35 according to EN 10164. Through thickness strengths min 80% of specified minimum tensile strength for specified thickness
Surface All surfaces have been 100% visually inspected. The surface condition does comply with EN 10163-2, class A, sub-class 3. The Norsok M-120 MDS Y40 specifies shot blasting SA2,5 and one coat of 15 microns zinc ethyl silicate primer. However, the stock plates can also be supplied in the as rolled black condition. NDT Ultrasonically test in accordance with EN 10160. Ultrasonic testing carried out either prior to, or after the final heat treatment and does meet the requirements of EN 10160, class S1/E2. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Low stress die-stamping on head and tail of each plate. Dimensional control All dimensions will be supplied according to EN 10029, flatness class N, thickness class A.
BS- EN 10225:2009 Weldable structural steels for fixed offshore structures - technical delivery conditions.
Grade
Structural
Symbol indicating that the following figures specify the minimum yield strength in MPa. (MPa = N/mm2)
S 355 G 11 +M
Minimum Yield
In MPa for flange thicknesses t 16mm. t 16 mm 355 MPa 16 < t 25 mm 345 MPa 25 < t 40 mm 345 MPa 40 < t 63 mm 335 MPa
Letter G
Followed by a maximum of two digits characterizing and indicating the steel grade within the groups 1, 2 or 3, as defined per table 7 of EN 10225.
Delivery condition
+ M Thermo mechanical rolling + N Normalizing rolling + Q Quenched and tempered Thermo mechanical rolling is a rolling process in which the final deformation is carried out in a particular temperature range leading to a material condition equivalent with certain properties which cannot be achieved or repeated by a heat treatment alone.
Within EN 10225 this steel is designated as a group 2 steel which means that this grade is substantially modified from EN 10025-4. This steel offers enhanced through thickness ductility and impact values verified at -40C. This grade is also known as 1.8806+M.
Chemical composition
C Si Mn P S Cr Mo Ni Al3
Bi2 Ca2 B
2
CEV = C +
1 2
Mn 6
Cr+Mo+V 5
Ni+Cu 15
Pcm = C +
Si 30
Mn+Cu+Cr 20
Ni 60
Mo 15
V 10
+ 5B
As per paragraph 8.2.3.3 of EN 10225 Residual elements shall be checked once every 5.000 tonnes per manufacturing location and shall be reported as a ladle analysis 3 The total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding Elements are used the minimum Al value and Al:N ratio does not apply
Mechanical properties
S355G11+M Thickness t
mm t 16 16 < t 25 25 < t 40 40 < t 63
Yield Reh
MPa 355 345 345 335
Tensile Rm
MPa
Reh / Rm
-
CVN
-40 C4
El
%
460-620
0,87
50J longitudinal
22
The verification of the mechanical properties shall be per cast. The test frequency shall be one test per 40 tons or part thereof.
Subject
Through thickness testing UT
Remarks
TTP testing to be carried out for flange thickness (tf ) > 25mm. Test shall be in accordance with EN 10164, quality class Z35. Sections to be tested to EN 10306, by agreement.
Surface All surfaces have been 100 % visually inspected in the as rolled condition. The surface condition does comply with EN 10163-3, class C, sub-class 2. Certification and traceability All dimensions will be supplied with a 3.2 certificate according to EN 10204, endorsed by recognized and independent inspection agency. Low stress die-stamping on one end of the section, pending section height.5 Dimensional control All dimensions will be supplied according to EN 10029.
4
5
For flange thickness (tf ) 25mm, test at -20C. Restrictions per originating mill apply with regards to die stamping and labeling. Please contact us for details.
Appendices
Pipe Schedule Useful Formulas / Conversions Comparison API 5L: PSL 1 versus PSL 2 Material Grade Comparison Chart
OD mm
10.3 13.7 17.1 21.3 26.7 33.4 42.2 48.3 60.3 73.0 88.9 101.6 114.3 141.3 168.3 219.1 273.1 323.9 355.6 406.4 457.2 508.0 558.8 609.6 660.4 711.2 762.0 812.8 863.6 914.4 965.2 1016.0 1066.8 1117.8 1168.4 1219.2
40
1.73 0.37 2.24 0.63 2.31 0.84 2.77 1.27 2.87 1.69 3.38 2.50 3.56 3.39 3.68 4.05 3.91 5.44 5.16 8.63 5.49 11.29 5.74 13.57 6.02 16.07 6.55 21.77 7.11 28.26 8.18 42.55 9.27 60.31 10.31 79.73 11.13 94.55 12.70 123.30 14.27 155.80 15.09 183.42 17.48 255.41 17.48 342.91 17.48 364.90 19.05 420.42
60
XS
2.41 0.47 3.02 0.80 3.20 1.10 3.73 1.62 3.91 2.20 4.55 3.24 4.85 4.47 5.08 5.41 5.54 7.48 7.01 11.41 7.62 15.27 8.08 18.63 8.56 22.32 9.53 30.97 10.97 42.56
80
2.41 0.47 3.02 0.80 3.20 1.10 3.73 1.62 3.91 2.20 4.55 3.24 4.85 4.47 5.08 5.41 5.54 7.48 7.01 11.41 7.62 15.27 8.08 18.63 8.56 22.32 9.53 30.97 10.97 42.56 12.70 64.64 15.09 96.01 17.48 132.08 19.05 158.10 21.44 203.53 23.88 254.55 26.19 311.17 28.58 373.83 30.96 442.08
100
120
140
160
XXS
/8 /4 /8 /2 /4
4.78 1.95 5.56 2.90 6.35 4.24 6.35 5.61 7.14 7.25 8.74 11.11 9.53 14.92 11.13 21.35 11.13 28.32 12.70 40.28 14.27 54.20 15.09 75.92 18.26 114.75 21.44 159.91 23.83 194.96 26.19 245.56 29.36 309.62 32.54 381.53 34.93 451.42 38.89 547.71 18.26 90.44 21.44 133.06 25.40 186.97 27.79 224.65 30.96 286.64 34.93 363.56 38.10 441.49 41.28 527.02 46.02 640.03 20.62 100.92 25.40 155.15 28.58 208.14 31.75 253.56 36.53 333.19 39.67 408.26 44.45 508.11 47.63 600.63 52.37 720.15 13.49 33.54 15.88 49.11 18.26 67.56 23.01 111.27 28.58 172.33 33.32 238.76 35.71 281.70 40.49 365.35 45.24 459.37 50.01 564.81 53.98 672.26 59.54 808.22
7.47 2.55 7.82 3.64 9.09 5.45 9.70 7.77 10.15 9.56 11.07 13.44 14.02 20.39 15.24 27.68 17.12 41.03 19.05 57.43 21.95 79.22 22.23 107.92 25.40 155.15 25.40 186.97
10.31 53.08 12.70 81.55 14.27 108.96 15.09 126.70 16.66 160.12 19.05 205.74 20.62 247.83 22.23 294.25 24.61 355.26
12.70 64.64 12.70 81.55 12.70 97.46 12.70 107.39 12.70 123.30 12.70 139.15 12.70 155.12 12.70 171.09 12.70 187.06 12.70 202.72 12.70 218.69 12.70 234.67 12.70 250.64 12.70 266.61 12.70 282.27 12.70 298.24 12.70 314.22 12.70 330.19 12.70 346.16 12.70 351.82 12.70 377.79
Inch Units
OD Wall thickness Weight
Nominal pipe size inches
1
OD inches
0.405 0.540 0.675 0.840 1.050 1.315 1.660 1.900 2.375 2.875 3.500 4.000 4.500 5.563 6.625 8.625 10.750 12.750 14.000 16.000 18.000 20.000 22.000 24.000 26.000 28.000 30.000 32.000 34.000 36.000 38.000 40.000 42.000 44.000 46.000 48.000
40
0.068 0.24 0.088 0.42 0.091 0.57 0.109 0.85 0.113 1.13 0.133 1.68 0.140 2.27 0.145 2.72 0.154 3.65 0.203 5.79 0.216 7.58 0.226 9.11 0.237 10.79 0.258 14.62 0.280 18.97 0.322 28.55 0.365 40.48 0.406 53.52 0.438 63.44 0.500 82.77 0.562 104.67 0.594 123.11 0.688 171.29 0.688 230.08 0.688 244.77 0.750 282.35
60
XS
0.095 0.31 0.119 0.54 0.126 0.74 0.147 1.09 0.154 1.47 0.179 2.17 0.191 3.00 0.200 3.63 0.218 5.02 0.276 7.66 0.300 10.25 0.318 12.50 0.337 14.98 0.375 20.78 0.432 28.57
80
0.095 0.31 0.119 0.54 0.126 0.74 0.147 1.09 0.154 1.47 0.179 2.17 0.191 3.00 0.200 3.63 0.218 5.02 0.276 7.66 0.300 10.25 0.318 12.50 0.337 14.98 0.375 20.78 0.432 28.57 0.500 43.39 0.594 64.43 0.688 88.63 0.750 106.13 0.844 136.61 0.938 170.92 1.031 208.87 1.125 250.81 1.219 296.58
100
120
140
160
XXS
/8
6 8 10 15 20 25 32 40 50 65 80 90 100 125 150 200 250 300 350 400 450 500 550 600 650 700 750 800 850 900 950 1000 1050 1100 1150 1200
/4 /8 /2
0.188 1.31 0.219 1.94 0.250 2.84 0.250 3.76 0.281 4.86 0.344 7.46 0.375 10.01 0.438 14.32 0.438 19.00 0.500 27.04 0.562 36.39 0.594 50.95 0.719 77.03 0.844 107.32 0.938 130.85 1.031 164.82 1.156 207.96 1.281 256.10 1.375 302.88 1.531 367.39 0.719 60.71 0.844 89.29 1.000 125.49 1.094 150.79 1.219 192.43 1.375 244.14 1.500 296.37 1.625 353.61 1.812 429.39 0.812 67.76 1.000 104.13 1.125 139.67 1.250 170.21 1.438 223.64 1.562 274.22 1.750 341.09 1.875 403.00 2.062 483.12 0.531 22.51 0.625 32.96 0.719 45.35 0.906 74.69 1.125 115.64 1.312 160.27 1.406 189.11 1.594 245.25 1.781 308.50 1.969 379.17 2.125 451.06 2.344 542.13
0.294 1.71 0.308 2.44 0.358 3.66 0.382 5.21 0.400 6.41 0.436 9.03 0.552 13.69 0.600 18.58 0.674 27.54 0.750 38.55 0.864 53.16 0.875 72.42 1.000 104.13 1.000 125.49
/4
0.406 35.64 0.500 54.74 0.562 73.15 0.594 85.05 0.656 107.50 0.750 138.17 0.812 166.40 0.875 197.41 0.969 238.35
0.500 43.39 0.500 54.74 0.500 65.42 0.500 72.09 0.500 82.77 0.500 93.45 0.500 104.13 0.500 114.81 0.500 125.49 0.500 136.17 0.500 146.85 0.500 157.53 0.500 168.21 0.500 178.89 0.500 189.57 0.500 200.25 0.500 210.93 0.500 221.61 0.500 232.29 0.500 242.97 0.500 253.65
Temperature Conversion
Celsius (C) 20 0 -10 -20 -30 -40 -50 -60 -80 Fahrenheit (F) 68 32 14 -4 -22 -40 -58 -76 -112
Parameters
Steel Grades Dimensions Pipe Ends Welding Process Heat Treatments (M,N or Q&T) Chemistry Defined Max % C in Seamless Max % C in Welded Pipes Max % P Max % S Carbon Equivalent Maximum Yield Strength Maximum Tensile Stress Charpy Impact Test Repair of Body by Welding Repair of Weld by Welding Certification
PSL 1
A25 - X70 10,3 - 2032,0 mm Plain, threaded, belled, prepared for special couplings All Not established C/Mn/P/S 0,28% for grades B 0,28% for grades B 0,030% for grades A 0,030% Not required (only on purchasers demand) Minimum specified Not established Not required (only on purchasers demand) Allowed Subject to agreement When specified per 10.1.2.1
PSL 2
B - X120 114,3 - 2032,0 mm Plain (unless otherwise agreed) All, except laser For all grades from B through X120 C/Si/Mn/P/S/V/Nb/Ti/Cev 0,24% 0,24% 0,025% 0,015% The maximum established for each grade The maximum & minimum specified The maximum established for each grade Required for all grades at a min. of 0C/32F Not allowed Not allowed Mandatory as per 10.1.3
The above table is extracted from API Specification 5L, 44th Edition. *Our stocks are all specified in (the higher) PSL 2 grade.
Note: Annexes with specific manufacturing or service requirements - Annex B: Qualified manufacturing procedures for PSL 2 - Annex H: Sour services PSL 2 pipe - Annex J: Offshore services PSL 2 pipe
CVN
ASTM
API 2W / 2H
EN 10025-3 (Normalized)
EN 10025-4 (TMCP)
ABS / BV / LR
DNV
GL
None
+ 20 C
0 C
- 20 C
- 40 C
None
+ 20 C
0 C
- 20 C
- 40 C
- 50 C
None
A572 Gr. 50
+ 20 C
0 C
- 20 C
- 40 C
API 2W / H Gr. 50
EH 36
NV E36
E36
- 50 C
Gr. 50 EE
- 60 C X60 (PSL 1)
NV F36
F36
None
A572 Gr. 60
+ 20 C X60 (PSL 2) S420 N S420 M S420G1 + Q / M S420G2 + Q / M S420 NL S420 ML FH 40 X65 (PSL 1) NV F40 F40 AH 40 DH 40 EH 40 NV A40 NV D40 NV E40 A40 D40 E40
0 C
- 20 C
- 40 C
API 2W / H Gr. 60
- 50 C
- 60 C
None
0 C
- 20 C
- 40 C
- 50 C
* The above chart is for comparison reference purposes only. User to use at own discretion.
ArcelorMittal Projects Singapore 72 Anson Road #08-00 Anson House Singapore 079911 T +65 6733 9033 E projects.asia@arcelormittal.com
ArcelorMittal Projects Europe Mannesmannweg 5, 4794 SL Heijningen, P.O. Box 52 4793 ZH Fijnaart The Netherlands T +31 88 0083 700 E projects.europe@arcelormittal.com
Dubai Steel Trading Co. LLC (ANC Compound) P.O. Box 8386 Al Quoz Industrial Area 4, Dubai, UAE T +971 470 538 00 E am.dstc@arcelormittal.com
ArcelorMittal Korea 10F Jinnex B/D, 65-1 Bangi-Dong, Songpa-Gu, Seoul, Korea 138-050 T +82 (0)2 6200 6571 E projects.asia@arcelormittal.com
Arcelormittal Distribution Solutions Qatar D Ring Road Near Birla Public School P.O. Box 12179 Doha, Qatar T +974 44650 086
ArcelorMittal Projects Australia Level 1, 46 Ord Street West Perth, WA 6005 Australia T +61 8 9278 4850 E projects.asia@arcelormittal.com
ArcelorMittal Projects Brazil Av. Nossa Sra de Copacabana, 1417 Subsolo 121 Copacabana 22070-900 Rio de Janeiro, Brazil T + 55 21 2262 4493
ArcelorMittal Distributions Solutions India 403, A Wing, Delphi Hiranandani Business Park Powai, Mumbai 400076, India T +91 22 6702 9544 E amdsindia@arcelormittal.com
ArcelorMittal Projects Malaysia Wisma Pantai B-12-7, Tower B No. 5, Jalan 4/83A Off Jalan Pantai Baru 59200, Kuala Lumpur, Malaysia T +60 3 2287 8586 E projects.asia@arcelormittal.com
ArcelorMittal Distribution Solutions Vostok LLC Bolshaya Ordynka 44, bld 4 Moscow 119017, Russia T +7 495 721 1551 E amds.vostok@arcelormittal.com
Luxembourg Steel (SiChuan) Shanghai Branch Room 2410, #357 (Tongmao), Songlin Road, Pudong, Shanghai . P. R. China 200122 T +86 21 5109 8377 E projects.china@arcelormittal.com
ArcelorMittal International Luxembourg Azerbaijan Representation AGA Center, 13th floor, Room 13/5, 55 Khojali avenue, AZ1025 Baku, Azerbaijan T +99412 464 4144
ArcelorMittal Projects Nigeria 1B Adebayo Doherty Street Off Admiralty Way Lekki Phase 1 Lagos, Nigeria T +234 1 277 0802 E projects.africa@arcelormittal.com
www.arcelormittal.com/projects
Disclaimer: The information in this brochure has been compiled with the utmost care. Nevertheless, it is for general information purposes only. The use of the information is at the readers risk. No warranty is implied or expressed by the Projects organization of ArcelorMittal with respect to the use of information this brochure contains. The information in this publication is subject to change or modification without notice. Please contact your regional office for the latest information. The images used in this brochure cannot be used for personal, non-commercial or commercial purposes.
44ArcelorMittal | Offshore Stock Program Photography: Image Library; Nexen Inc.; wide.lu.; Istockphoto