Standard
Standard
Standard
STANDARD-MATERIALS
-2-
TABLE OF CONTENTS
Page
1.
1.1
1.2
1.3
CAST MATERIAL
G-X5 CrNi 13 4
GS 20 Mn 5
GS-45
3
4
5
2.
2.1
2.2
2.3
PLATE MATERIAL
StE 285
StE 355
StE 420
6
7
8
2.4
2.4.1
2.5
2.6
2.7
Rst 37-2
St 52-3
X5 CrNi 13 4
X10 CrNiNb 189
X10 Cr 13
9
10
11
12
13
3.
3.1
3.2
3.3
3.4
3.5
3.6
3.7
3.8
FORGED MATERIAL
Ck 35
StE 355
St 52-3
34 Cr 4
42 CrMo 4
50 CrMo 4
C22
X 20 Cr 13
X 5 CrNi 13 4
14
15
16
17
18
19
20
21
11
4.
4.1
TUBES
St 35
22
5.
5.1
HOT BARS
St 37.2
23
-3-
1.
CAST MATERIAL
1.1
G-X5CrNi 13 4
acc. to DIN 17.445
ASTM A-743
Grade CA-6NM
Chemical Composition
C .............................................. max. 0.060 %
Si................................................max. 1.00 %
Mn.............................................. max. 1.00 %
Cr............................................... 12.0 - 13.5 %
Ni................................................3.5 - 4.5 %
Mo.............................................. 0.40 - 0.70 %
S.................................................max. 0.025 %
P.................................................max. 0.025 %
max. 0.060 %
max. 1.00 %
max. 1.00 %
11.5 - 14.00 %
3.50 - 4.50 %
0.40 - 1.00 %
max. 0.03 %
max. 0.03 %
Mechanical Properties
Tensile strength......................... 760 - 930 N/mm2
Yield point.................................. min. 540 N/mm2
Elongation (L0 = 5d0)..................min. 15 %
...................................................
Reduction of area......................min. 35%
Impact energy............................ min. 55 J
Charpy-V notch
specimen at + 20 C
(2 inches or 50 mm)
min. 35 %
not specified
-4-
1.2
GS 20 Mn 5 V
acc. to DIN 17.182
ASTM A-148
Grade 80/50
Chemical Composition
C .............................................. 0.15 - 0.23 %
Mn.............................................. 1.00 - 1.50 %
Mo.............................................. < 0.15 %
Ni................................................< 0.40 %
not specified
not specified
not specified
not specified
P.................................................max. 0.020 %
S.................................................max. 0.015 %
max. 0.05 %
max. 0.06 %
Mechanical Properties
Tensile strength......................... 500 - 650 N/mm2
Yield point.................................. min. 360 N/mm2
Elongation (L0 = 5d0)..................min. 24 %
...................................................
Reduction of area......................not specified
Impact energy............................ min. 70 J
Charpy-V notch
specimen at + 20 C
(2 inches or 50 mm)
min. 35 %
not specified
-5-
1.3
GS-45
acc. to DIN 1681
ASTM A-27
Grade
Chemical Composition
65/35
70/40
max. 0.30 %
max. 0.80 %
max. 0.70 %
max. 0.05 %
max. 0.06 %
0,25 %
0,80 %
1,20 %
0,05 %
0,06 %
Mechanical Properties
Tensile strength......................... 450 N/mm2
min. 450 MPa
Yield point.................................. min. 230 N/mm2 min. 240 MPa
Elongation (L0 = 5d0................... min. 22 %
min. 24 %
...................................................
Reduction of area......................min. 31 %
Impact energy............................ 27 J
Charpy-V notch
specimen at + 20 C
485 MPa
275 MPa
22 %
(2 inches or 50 mm)
min. 35 %
30 %
-6-
2.
PLATE MATERIAL
2.1
StE 285
acc. to DIN 17.102
ASTM A-516
Grade 60
Chemical Composition
C .............................................. max. 0.18 %
Si................................................max. 0.40 %
Mn.............................................. 0.60 - 1.40 %
P.................................................max. 0.035 %
S.................................................max. 0.030 %
0.21 - 0.27 %
0.13 - 0.45 %
0.55 - 1.30 %
max. 0.035 %
max. 0.035 %
Mechanical Properties
Tensile strength......................... 390 - 510 N/mm2
Yield point.................................. 285 N/mm2
Elongation (L0 = 5d0)..................min. 246 %
...................................................
Impact energy............................ min. 55 J
Charpy-V notch
specimen at + 20 C
(2 inches or 50 mm)
not specified
-7-
2.2
StE 355
acc. to DIN 17.102
ASTM A-537
Class 1
Chemical Composition
C .............................................. max. 0.20 %
Si................................................0.10 - 0.50 %
Mn.............................................. 0.70 - 1.50 %
P.................................................max. 0.035 %
S.................................................max. 0.030 %
max. 0.24 %
0.13 - 0.55 %
0.64 - 1.72 %
max. 0.035 %
max. 0.04 %
Mechanical Properties
Tensile strength......................... 490 - 630 N/mm2
Yield point.................................. 355 N/mm2
Elongation (L0 = 5d0)..................min. 22 %
...................................................
Impact energy............................ min. 55 J
Charpy-V notch
specimen at + 20 C
(2 inches or 50 mm)
not specified
-8-
2.3
StE 420
acc. to DIN 17.102
ASTM A-633
Grade E
Chemical Composition
C .............................................. max. 0.20 %
Si................................................0.10 - 0.60 %
Mn.............................................. 1.00 - 1.70 %
P.................................................max. 0.035 %
S.................................................max. 0.030 %
max. 0.22 %
0.15 - 0.50 %
1.15 - 1.50 %
max. 0.035 %
max. 0.040 %
Mechanical Properties
Tensile strength......................... 530 - 680 N/mm2
Yield point.................................. 420 N/mm2
Elongation (L0 = 5d0)..................min. 19 %
...................................................
Impact energy............................ min. 55 J
Charpy-V notch
specimen at + 20 C
(2 inches or 50 mm)
min. 68 J (+25 C)
-9-
2.4
Rst 37-2
ASTM A-283
Grade C
Chemical Composition
C .............................................. max. 0.20 %
P.................................................max. 0.050 %
S.................................................max. 0.050 %
Si................................................-Mn.............................................. --
max. 0.24 %
max. 0.035 %
max. 0.040 %
max. 0.40 %
max. 0.90 %
Mechanical Properties
Tensile strength......................... 360 - 470 N/mm2
Yield point.................................. 215 - 235 N/mm2
Elongation (L0 = 5d0)..................min. 24 %
...................................................
Impact energy............................ min. 27 J
Charpy-V notch
specimen at + 20 C
(2 inches or 50 mm)
not specified
-10-
2.4.1
St 52-3
ASTM A-537
Class 1
Chemical Composition
C .............................................. max. 0.20 %
P.................................................max. 0.04 %
S.................................................max. 0.04 %
Si................................................not specified
Mn.............................................. not specified
max. 0.24 %
max. 0.035 %
max. 0.035 %
0.13 - 0.55 %
0.64 - 1.72 %
Mechanical Properties
Tensile strength......................... 510 - 630 N/mm2
Yield point.................................. 305 - 355 N/mm2
Elongation (L0 = 5d0)..................min. 20 %
...................................................
Impact energy............................ min. 27 J
Charpy-V notch
specimen at + 20 C
(long.)
(2 inches or 50 mm)
not specified
-11-
2.5/3.8
X 5 CrNi 13 4
ASTM A-182
Grade F6-NM
Chemical Composition
C .............................................. max. 0.050 %
Si................................................max. 0.50 %
Mn.............................................. max. 1.0 %
Cr............................................... 12.0 - 13.5 %
Ni................................................3.3 - 4.5 %
Mo.............................................. 0.30 - 0.50 %
S.................................................max. 0.025 %
P.................................................max. 0.030 %
max. 0.05 %
max. 0.60 %
0.050 - 1.00 %
11.5 - 14.0 %
3.5 - 5.5 %
0.5 - 1.0 %
max. 0.030 %
max. 0.030 %
Mechanical Properties
Tensile strength......................... 750 - 950 N/mm2
Yield point.................................. min. 550 N/mm2
Elongation (L0 = 5d0)..................min. 16 %
...................................................
Reduction of area......................min. 25 %
Impact energy............................ min. 45 J
Charpy-V notch
specimen at + 20 C
(long.)
(2 inches or 50 mm)
min. 45 %
not specified
-12-
2.6
X 10 CrNiNb 18 9
ASTM A-240
acc. to NORM M 3121
Chemical Composition
Type 347
Type
304L
max. 0.08 %
max. 0.75 %
max. 2.00 %
17.0 - 19.0 %
9.0 - 13.0 %
max. 0.030 %
max. 0.045 %
0,03 %
0,75 %
2,00 %
18-20 %
8 - 12 %
0,030 %
0,045 %
485 MPa
170 MPa
40 %
Mechanical Properties
...................................................
(2 inches or 50 mm)
-13-
2.7
X 10 Cr 13
acc. to DIN 17.440
ASTM A-240
Type 410
Chemical Composition
C .............................................. 0.08 - 0.12 %
P.................................................max. 0.045 %
S.................................................max. 0.030 %
Si................................................max. 1.0 %
Mn.............................................. max. 1.0 %
Cr............................................... 12.0 - 14.0 %
Ni................................................--
max. 0.15 %
max. 0.040 %
max. 0.030 %
max. 1.00 %
max. 1.0 %
11.5 - 13.5 %
max. 0.75 %
Mechanical Properties
Tensile strength......................... 600 - 800 N/mm2
Yield point.................................. min. 420 N/mm2
Elongation (L0 = 5d0)..................min. 18 %
...................................................
(2 inches or 50 mm)
-14-
3.
FORGED MATERIAL
3.1
CK 35
acc. to DIN 17.200
ASTM A-668
Class D
Chemical Composition
C .............................................. 0.32 - 0.39 %
Si................................................max. 0.40 %
Mn.............................................. 0.50 - 0.80 %
S.................................................max. 0.030 %
P.................................................max. 0.035 %
not specified
not specified
max. 1.35 %
max. 0.05 %
max. 0.05 %
Mechanical Properties
Tensile strength
= 250...................................... 490 - 640 N/mm2
min. 22 %
min. 19 %
min. 22 %
min. 19 %
min. 30 %
not specified
not specified
-15-
3.2
StE 355
acc. to DIN 17.103
SAE 1522
Chemical Composition
C .............................................. max. 0.20 %
Si................................................0.10 - 0.50 %
Mn.............................................. 0.90 - 1.65 %
P.................................................max. 0.035 %
S.................................................max. 0.030 %
0.18 - 0.24 %
not specified
1.10 - 1.40 %
max. 0.04 %
max. 0.05 %
Mechanical Properties
Tensile strength......................... 490 - 630 N/mm2
Yield point.................................. 355 N/mm2
Elongation (L0 = 5d0)..................min. 23 %
not specified
not specified
not specified
not specified
-16-
St 52-3
acc. to DIN 17.100
SAE 1524
Chemical Composition
C .............................................. max. 0.22 %
Si................................................max. 0.60 %
Mn.............................................. max. 1.70 %
P.................................................max. 0.04 %
S.................................................max. 0.04 %
0.19 - 0.25 %
not specified
1.35 - 1.65 %
max. 0.04 %
max. 0.05 %
Mechanical Properties
Tensile strength......................... 490 - 630 N/mm2
Yield point.................................. 315 - 355 N/mm2
Elongation (L0 = 5d0)..................min. 20 %
not specified
not specified
not specified
not specified
-17-
3.3
34 Cr 4
acc. to DIN
17.200
AISI 5132
(ASTM A304)
Chemical Composition
A304
0.30 - 0.35 %
0,29-0,35 %
Si................................................max. 0.40 %
Mn.............................................. 0.60 - 0.90 %
Cr............................................... 0.90 - 1.20 %
P.................................................max. 0.035 %
S.................................................max. 0.030 %
0.15 - 35 %
0.60 - 0.80 %
0.75 - 1.00 %
max. 0.035 %
max. 0.040 %
0,29-0,35 %
0,50-0,90 %
0,65-1,10 %
not specified
not specified
Mechanical Properties
Tensile strength......................... 700 - 850 N/mm2 not specified
Yield point.................................. min. 510 N/mm2 not specified
Elongation (L0 = 5d0................... min. 14 %
not specified
Reduction of area .....................min. 40 %
Impact energy............................ min. 40 J
Charpy-V notch
specimen at + 20 C
not specified
not specified
-18-
3.4
42 CrMo 4
acc. to DIN
17.200
AISI 4140 H
(ASTM A304)
Chemical Composition
A304
0.38 - 0.43 %
0,37-0,44 %
Si................................................max. 0.40 %
Mn.............................................. 0.60 - 0.90 %
Cr............................................... 0.90 - 1.20 %
Mo.............................................. 0.015 - 0.30 %
S.................................................max. 0.03 %
P.................................................max. 0.035 %
0.15 - 0.35 %
0.75 - 1.00 %
0.80 - 1.10 %
0.15 - 0.25 %
max. 0.040 %
max. 0.035 %
0,15-0,35 %
0,65-1,10 %
0,75-1,20 %
0,15-0,25 %
not specified
not specified
Mechanical Properties
Tensile strength......................... 780 - 930 N/mm2 not specified
Yield point.................................. min. 560 N/mm2 not specified
Elongation (L0 = 5d0................... min. 13 %
not specified
Reduction of area .....................min. 50 %
Impact energy............................ min. 46J
Charpy-V notch
specimen at + 20 C
not specified
not specified
-19-
3.5
50 CrMo 4
acc. to DIN
17.200
AISI 4150 H
(ASTM A304)
Chemical Composition
A304
0.48 - 0.53 %
0.15 - 0.35 %
0,42-0,49 %
0,15-0,35 %
0.75 - 1.00 %
0.80 - 1.10 %
0.15 - 0.25 %
max. 0.40 %
max. 0.35 %
0,65-1,10 %
0,75-1,20 %
0,15-1,20 %
not specified
not specified
Mechanical Properties
Tensile strength......................... 780 - 930 N/mm2 not specified
Yield point.................................. min. 635 N/mm2 not specified
Elongation (L0 = 5d0................... min. 13 %
not specified
Reduction of area .....................min. 50 %
Impact energy............................ min. 39J
Charpy-V notch
specimen at + 20 C
not specified
not specified
-20-
3.6
C22
acc. to DIN 17.200
ASTM A-105
Chemical Composition
C .............................................. 0.17 - 0.24 %
Si................................................max. 0.40 %
Mn.............................................. 0.30 - 0.60 %
P.................................................max. 0.045 %
S.................................................max. 0.045 %
max. 0.35 %
max. 0.35 %
0.60 - 1.05 %
max. 0.04 %
max. 0.05 %
Mechanical Properties
Tensile strength......................... 410 - 520 N/mm2
Yield point.................................. min. 225 N/mm2
Elongation (L0 = 5d0)..................min. 22 %
...................................................
Reduction of area......................min. 45 %
Impact energy............................ min. 50 J
Charpy-V notch
specimen at + 20 C
(2 inches or 50 mm)
min. 30 %
not specified
-21-
3.7
X20 Cr 13
acc. to DIN 17.440
ASTM A-473
Type 420
Chemical Composition
C .............................................. 0.17 - 0.25 %
P.................................................max. 0.045 %
S.................................................max. 0.030 %
Si................................................max. 1.00 %
Mn.............................................. max. 1.0 %
Cr............................................... 12.0 - 14.0 %
min. 0.15 %
max. 0.040 %
max. 0.030 %
max. 1.00 %
max. 1.0 %
12.0 - 14.0 %
Mechanical Properties
Tensile strength......................... 650 - 800 N/mm2
Yield point.................................. 450 N/mm2
Elongation (L0 = 5d0)..................min. 14 %
not specified
not specified
not specified
Reduction of area......................min. 25 %
Impact energy............................ min. 46 J
Charpy-V notch
specimen at + 20 C
not specified
not specified
-22-
4.
TUBES
4.1
St35
acc. to DIN 1629 T3
ASTM A-53
Grade A
Chemical Composition
C .............................................. max. 0.17 %
Si................................................0.10 to 0.35 %
Mn.............................................. max. 0.40 %
P.................................................max. 0.05 %
S.................................................max. 0.05 %
max. 0.25 %
not specified
max. 0.95 %
max. 0.05 %
max. 0.06 %
Mechanical Properties
Tensile strength......................... 340 - 440 N/mm2
Yield point.................................. min. 235 N/mm2
Elongation (L0 = 5d0)..................min. 25 %
...................................................
cited standard
-23-
5.
HOT BARS
5.1
St 37.2
acc. to DIN 17.100
ASTM A-283
Grade C
Chemical Composition
C .............................................. max. 0.17 %
P.................................................max. 0.050 %
S.................................................max. 0.050 %
Si................................................-Mn.............................................. --
max. 0.24 %
max. 0.035 %
max. 0.04 %
max. 0.40 %
max. 0.90 %
Mechanical Properties
Tensile strength......................... 340 - 470 N/mm2
Yield point.................................. min. 235 N/mm2
Elongation (L0 = 5d0)..................min. 26 %
...................................................
(2 inches or 50 mm)