PropertiesofsomeMetalsandAlloys 297
PropertiesofsomeMetalsandAlloys 297
PropertiesofsomeMetalsandAlloys 297
of
Some Metals
and Alloys
COPPER AND COPPER ALLOYS
WHITE METALS AND ALLOYS
ALUMINUM AND ALLOYS
MAGNESIUM ALLOYS TITANIUM
ALLOYS RESISTANCE HEATING
ALLOYS MAGNETIC ALLOYS CONTROLLED EXPANSION AND CONSTANT MODULUS ALLOYS NICKEL
AND ALLOYS MONEL* NICKELCOPPER ALLOYS INCOLOY* NICKELIRON-CHROMIUM ALLOYS INCONEL*
NICKEL-CHROMIUM-IRON ALLOYS
NIMONIC* NICKEL-CHROMIUM
ALLOYS HASTELLOY* ALLOYS
CHLORIMET* ALLOYS ILLIUM*
ALLOYS HIGH TEMPERATURE-HIGH
STRENGTH ALLOYS IRON AND STEEL
ALLOYS CAST IRON ALLOYS
WROUGHT STAINLESS STEEL CAST
CORROSION AND HEAT RESISTANT
ALLOYS* REFRACTORY METALS AND
ALLOYS PRECIOUS METALS
Properties
of
Some Metals
and Alloys
INTRODUCTION
The information assembled in this publication has
been obtained from various sources. The chemical
compositions and the mechanical and physical properties are typical for the metals and alloys listed. The
sources that have been most helpful are the metal and
alloy producers, ALLOY DIGEST, WOLDMANS ENGINEERING ALLOYS, International Nickels publications
and UNIFIED NUMBERING SYSTEM for METALS and
ALLOYS.
These data are presented to facilitate general comparison and are not intended for specification or design
purposes. Variations from these typical values can be
expected and will be dependent upon mill practice and
material form and size. Strength is generally higher,
and ductility correspondingly lower, in the smaller sizes
of rods and bars and in cold-drawn wire; the converse
is true for the larger sizes. In the case of carbon, alloy
and hardenable stainless steels, mechanical properties and hardnesses vary widely with the particular
heat treatment used.
REFERENCES
Many of the alloys listed in this publication are
marketed under well-known trademarks of their producers, and an effort has been made to associate such
trademarks with the applicable materials listed herein.
Such trademarks, together with their proprietors, are
listed on page 84.
Specifications, mainly those published by the American Society for Testing and Materials, are shown for
many of the materials. Other specifications may also
be available. Where specifications appear, their latest
date of issue should apply. Sources of additional
information on properties and specifications are shown
on page 85.
This listing and the data were compiled from sources
believed reliable; however, possible errors and/or
omissions may exist. We would welcome corrections or
suggestions for use in periodically revising the publication. Thus your interest and help will contribute in
making it as accurate as possible with up-to-date
information.
INDEX
Page
2% Nickel Steel, Cast ..............................................................50
3% Nickel Steel ........................................................................48
3% Nickel Steel, Cast ..............................................................50
9% Nickel Steel ............................................................................50
15-5 PH* Stainless Steel ............................................................64
17-4 PH* Stainless Steel ............................................................64
17-7 PH* Stainless Steel ............................................................64
17-14 Cu Mo Stainless Steel ......................................................66
18-9 LW* Stainless Steel ............................................................62
18K White Gold ...........................................................................80
19-9 DL Alloy ................................................................................66
29-4 Stainless Steel ....................................................................68
29-4-2 Stainless Steel .................................................................68
35-20 Ni Cr bal Fe Alloy...............................................................20
38-7 Ni Cr + Fe Alloy ...................................................................24
42% Ni Fe Alloy............................................................................24
49% Ni Fe Controlled Expansion Alloy .....................................24
49% Ni Fe Magnetic Alloy ...........................................................22
60-15 Ni Cr bal Fe Alloy ..............................................................20
79-4 Ni Mo bal Fe Alloy ..............................................................22
80-20 Ni Cr Alloy ..........................................................................20
200 ALLOY*..................................................................................20
300M Alloy Steel .........................................................................48
611 Alloy, Cast .............................................................................30
625 Alloy, Cast ............................................................................32
713C Alloy.....................................................................................40
713LC Alloy ..................................................................................40
901 Alloy .......................................................................................40
904 L Stainless Steel ..................................................................60
9310 Alloy Steel............................................................................48
A-286 Alloy....................................................................................40
AISI 4340 Alloy Steel ..................................................................48
AISI 4620 Alloy Steel ..................................................................48
AISI 4820 Alloy Steel ..................................................................48
AISI 8620 Alloy Steel ..................................................................48
AL6X* Stainless Steel .................................................................60
ALCHROME*................................................................................20
ALOYCO* 20 Stainless Steel, Cast ...........................................74
Alnico Alloys (Permanent Magnet Alloys)
II ............................................................................................ 20
III, IV, V, VI, VII & VIII ...........................................................22
Aluminum Alloys, Cast
413.0 ......................................................................................12
B443.0, A380.0, 295.0, 514.0, 520.0, 336.0 & 242.0 .........14
Aluminum Alloys, Wrought
1100, 2017, Alclad 2024, 3003, 5052, 6061 & 7075.........12
AM 350* Stainless Steel ..............................................................64
AM 355* Stainless Steel ..............................................................64
Antimony .......................................................................................10
B-1900 Alloy ................................................................................46
Bismuth-Lead Alloy .....................................................................10
Bi-Pb-Sn-Cd Alloy .......................................................................10
Bi-Pb-In-Cd-Sn Alloy ...................................................................10
Bismuth-Tin Alloy ........................................................................10
Brass, Cast
Leaded Red Brass (C83600) ...............................................8
Brass, Wrought
Admiralty (C44300, C44400 & C44500) ...............................4
Cartridge (C26000) ..................................................................4
Naval (C46400) ........................................................................4
Red(C23000)............................................................................4
Yellow (C27000).......................................................................4
Bronze, Cast
G(C90500) ............................................................................. 8
M(C90300) ............................................................................. 8
Leaded Tin (C93200) ............................................................8
Nickel-Aluminum (C95800) ..................................................8
Nickel-Tin, Type A (C94700) .................................................8
Nickel-Tin, Type B (C94800) .................................................8
*See page 84 for list of trademarks.
Page
Bronze, Wrought
Aluminum (C61400) .............................................................. 4
High Silicon (C65500) ........................................................... 6
Nickel-Aluminum (C63200) .................................................. 6
Phosphor(C51000) ................................................................ 4
Phosphor (C52400)................................................................ 4
Carbon Steel ...............................................................................46
CARPENTER* No.10 .................................................................60
CARPENTER 20Cb-3* ...............................................................60
Cast Iron Alloys (see Iron, Cast)
CHLORIMET* 2 ...........................................................................38
CHLORIMET* 3 ...........................................................................38
Coinage Alloy ................................................................................ 6
Columbium ...................................................................................78
Columbium-Tantalum-Tungsten Alloy .......................................78
Columbium-Vanadium Alloy .......................................................78
Columbium-Zirconium Alloy .......................................................78
Constantan .................................................................................... 6
Controlled Expansion Alloys ......................................................24
Copper Alloys, Cast
C83600 (Leaded Red Brass) ............................................... 8
C90300 (M Bronze) ............................................................... 8
C90500 (G Bronze) ............................................................... 8
C93200 (Leaded Tin Bronze) ............................................... 8
C94700 (Nickel-Tin Bronze, Type A) ................................... 8
C94800 (Nickel-Tin Bronze, Type B) ................................... 8
C95800 (Nickel-Alumimum Bronze) .................................... 8
C96200(Copper-Nickel) ....................................................... 8
C96400(Copper-Nickel) ......................................................10
C97300 (Nickel Silver) ........................................................10
C97600 (Nickel Silver) ........................................................10
C97800 (Nickel Silver) ........................................................10
Copper Alloys, Wrought
C11000(Copper) .................................................................... 4
C17000 (Copper Beryllium) .................................................. 4
C17200 (Copper Beryllium) .................................................. 4
C17500 (Copper Beryllium) .................................................. 4
C17600 (Copper Beryllium 50) ............................................ 4
C23000 (Red Brass) ............................................................. 4
C26000 (Cartridge Brass) ..................................................... 4
C27000 (Yellow Brass) ......................................................... 4
C28000 (Muntz Metal) .......................................................... 4
C44300 (Admiralty Brass) .................................................... 4
C44400 (Admiralty Brass) .................................................... 4
C44500 (Admiralty Brass) .................................................... 4
C46400 (Naval Brass) ........................................................... 4
C51000 (Phosphor Bronze) ................................................. 4
C52400 (Phosphor Bronze) ................................................. 4
C61400 (Aluminum Bronze) ................................................. 4
C63200 (Nickel-Aluminum Bronze) ..................................... 6
C65500 (High Silicon Bronze) .............................................. 6
C70600 (Copper Nickel, 90-10 + Fe) .................................. 6
C71000 (Copper Nickel, 79-21) ........................................... 6
C71300 (Copper Nickel) ....................................................... 6
C71500 (Copper Nickel, 70-30 + Fe) .................................. 6
C71640 (Copper Nickel) ....................................................... 6
C72200 (Copper Nickel) ....................................................... 6
C72500 (Copper-Nickel-Tin) ................................................ 6
C72600 (Copper-Nickel-Tin) ................................................ 6
C72700 (Copper-Nickel-Tin) ................................................ 6
C72800 (Copper-Nickel-Tin) ................................................ 6
C72900 (Copper-Nickel-Tin) ................................................ 6
C73500 (Nickel Silver) .......................................................... 8
C75200 (Nickel Silver) .......................................................... 8
C76600 (Nickel Silver) .......................................................... 8
C77000 (Nickel Silver) .......................................................... 8
Copper Beryllium Alloys
C17000,C17200,C17500 & C17600 ................................... 4
Copper-Nickel Alloys
C70600, C71000, C71300, C71500, C71640 &
C72200.................................................................................... 6
(55-45) .................................................................................... 6
Castings .............................................................................8,10
Copper-Nickel-Tin Alloys
C72500, C72600, C72700, C72800 & C72900 .................. 6
Cunico ...........................................................................................22
Cunife............................................................................................22
CUSTOM 455* Stainless Steel ..................................................64
Page
D-979 Alloy ............................................................................46
DISCALOY* ...........................................................................46
DURANICKEL* Alloy 301......................................................26
Ductile Irons...........................................................................52
DURIRON* ............................................................................54
DURICHLOR*........................................................................54
DURIMET* 20 Stainless Steel, Cast.....................................74
E-BRITE* ...............................................................................68
ELINVAR*..............................................................................24
EVANOHM* ...........................................................................20
FERRALIUM* Alloy 255 ........................................................60
GMR 235D Alloy....................................................................38
Gold
Pure ................................................................................80
18K White.......................................................................80
WE. No. 1 .......................................................................80
Greek Ascoloy Stainless Steel..............................................66
HASTELLOY* alloys
B-2, C-276 & C-4............................................................34
G, G-3, N, S & W............................................................36
X .....................................................................................38
M-532 .............................................................................60
HAYNES* alloy
25 & 188 .........................................................................42
556..................................................................................40
Heat Resistant Alloys, Cast
HA, HC & HD..................................................................74
HE, HF, HH, HI, HK, HL, HN, HP HP50-WZ, HT &
HU............................................................................76
HW & HX ........................................................................78
IN-657.............................................................................76
IN-519.............................................................................78
High-Temperature High-Strength Alloys
GMR 2350 ......................................................................38
713C, 713LC, 901, HAYNES* 556, A-286, IN-100
&IN-102....................................................................40
IN-738, IN-792, IN-939, L-605, HAYNES* 188 &
MAR-M* 246 ............................................................42
M-252, RENE 41*, RA 333*, S-816, TO Nickel,
UDIMET* 500, UDIMET* 700 & WI-52 ...................44
Waspaloy, B-1900, D-979, X-40, N-155 &
DISCALOY* ............................................................ 46
High-Yield-Strength Alloy Steels...........................................50
ILLIUM* alloys
B, G & 98 ........................................................................38
P .....................................................................................74
IN-100 Alloy ...........................................................................40
IN-102 Alloy .......................................................................... 4C
IN-519 Alloy ...........................................................................78
IN-657 Alloy ...........................................................................76
IN-738 Alloy ...........................................................................42
IN-787 Alloy Steel..................................................................50
IN-792 Alloy ...........................................................................42
IN-849 Stainless Steel...........................................................74
IN-862 Stainless Steel...........................................................74
IN-939 Alloy ...........................................................................42
INCOLOY* alloys
800,801,802 & 825.........................................................30
903..................................................................................24
INCONEL* alloys
600, 601, 611 & 617.......................................................30
625, 690, 718, X-750 & 751...........................................32
Ingot Iron................................................................................ 46
INVAR* ..................................................................................24
Iridium ....................................................................................80
Iron, Cast
Gray ................................................................................52
Ductile.............................................................................52
Malleable ........................................................................52
Ni-Hard, Types 1, 2 & 4 .................................................54
Ni-Resist, Types 1, 2, 5 & D2 ........................................52
Types D5 & D-5S ...........................................................54
Iron-Silicon Alloy (DURIRON*) ......................................54
Iron-Silicon-Molybdenum Alloy (DURICHLOR*) ...........54
Page
Iron, Wrought.........................................................................46
Iron-Chromium-Aluminum Alloy ............................................20
Iron-Nickel Temperature Compensating Alloys ....................24
ISO-ELASTIC*.......................................................................24
JESSOP JS700*....................................................................60
JESSOP JS777*....................................................................60
JESSOP* Type 317L Plus.....................................................58
KANTHAL*.............................................................................20
KARMA*.................................................................................20
KOVAR*.................................................................................24
L-605 Alloy.............................................................................42
Lead
Pure ................................................................................10
Antimonial.......................................................................10
Tellurium .........................................................................10
Lead-Tin Solders
50-50 & 40-60.................................................................10
M-252 Alloy............................................................................44
Magnesium Alloys
AZ 318, AZ 80A, AZ 918, AZ 91C & AZ 92A.................14
EZ 33A & HK 31A...........................................................14
HZ 32A & ZK 60A...........................................................16
Magnetic Alloys ................................................................20,22
Malleable Iron ........................................................................52
Manganese Alloy 772............................................................12
Maraging Steels
18-200,18-250,18-300....................................................50
MAR-M* 246 Alloy .................................................................42
Moly Permalloy 4/79..............................................................22
Molybdenum ..........................................................................78
Molybdenum0.5% Titanium Alloy ......................................78
MONEL* Alloys
400, 401, 404, R-405 & K-500 .......................................28
410 (Cast), 411 (Cast) & 505 (Cast) ..............................28
Mu Metal ................................................................................20
Muntz Metal (C28000).............................................................4
N-155 Alloy ............................................................................46
Nickel Alloys, Cast
Nickel 210.......................................................................26
Nickel Beryllium M2206..................................................26
Nickel Beryllium CR-1 ....................................................26
Nickel Alloys, Wrought
200, 201, 205, 211 & 270...............................................26
Nickel Beryllium 440.......................................................26
DURANICKEL* Alloy 301...............................................26
PERMANICKEL* Alloy 300 ............................................26
TD Nickel ........................................................................44
Nickel-Chromium Alloys
80-20...............................................................................20
60-15 + Fe ......................................................................20
35-20 + Fe ......................................................................20
Nickel-Chromium-Aluminum Alloy ........................................20
Nickel-Chromium-Iron Alloys (see INCONEL*)
Nickel-Copper Alloys (see MONEL*)
Nickel-Iron Alloys
Controlled expansion alloy .............................................24
Magnetic alloy.................................................................22
Nickel-Iron-Chromium Alloys (see INCOLOY*)
Nickel-Iron-Cobalt Alloy.........................................................24
Nickel-Molybdenum Alloy (80-4) ...........................................22
Nickel Silver Alloys, Cast
C97300, C97600 & C97800...........................................10
Nickel Silver Alloys, Wrought
C73500, C75200, C76600 & C77000..............................8
Nickel-Titanium Alloy (Nitinol) ...............................................28
Ni-Hard Cast Irons
Types 1, 2 & 4 ................................................................54
NIKROTHAL*.........................................................................20
NIMONIC* Alloys
75, 80A, 90 & 115...........................................................34
Ni-Resist Cast Irons
Types 1, 2, 5 & D-2 ........................................................52
Types D5 & D-5S ...........................................................54
NI-SPAN C* ...........................................................................24
Nitinol Memory Alloy..............................................................28
*See page 84 for list of trademarks.
Page
NITRALLOY* N Alloy Steel ...................................................48
NITRONIC* Stainless Steels
20, 32, 33, 40, 50 & 60...................................................62
Non-Galling Alloys
WAUKESHA METAL* No. 23.........................................26
WAUKESHA METAL* No.88..........................................28
Palladium ...............................................................................80
Palladium Alloy No. 934 ........................................................82
Palladium-Ruthenium Alloy ...................................................82
Palladium-Silver Alloy............................................................82
Permalloy 49..........................................................................22
PERMANICKEL* Alloy 300 ...................................................26
PH 13-8 Mo* Stainless Steel.................................................64
PH 14-8 Mo* Stainless Steel.................................................64
PH 15-7 Mo* Stainless Steel.................................................64
Platinum .................................................................................80
Platinum-Iridium Alloy............................................................80
Platinum-Rhodium Alloy ........................................................82
Platinum-Ruthenium Alloy .....................................................82
Precious Metals & Alloys.................................................80, 82
RA 333* Alloy.........................................................................44
Refractory Metals & Alloys ..............................................78, 80
REN 41* Alloy......................................................................44
Resistance Heating Alloys.....................................................20
Rhodium.................................................................................80
RODAR*.................................................................................24
Ruthenium..............................................................................82
S-816 Alloy ............................................................................44
SAE 1020 Steel .....................................................................46
SANDUSKY* Alloy 75............................................................74
SEA-CURE* Stainless Steel..................................................68
Silver
Coin.................................................................................80
Fine .................................................................................80
Sterling............................................................................80
Silver Brazing Alloys
EASY-FLOW* .................................................................80
R-T Alloy .........................................................................80
Solders
50-50(Sn-Pb) ..................................................................10
60-40(Sn-Pb) ..................................................................10
Stainless Steels, Cast
CA-15, CA-40, CA-6NM & CB-7 Cu-1 ...........................68
CB-7 Cu-2, CB-30, CC-50 & CE-30...............................68
CF-3, CF-8, CF-3M & CF-8M.........................................68
CF-8C, CF-16F & CF-20 ................................................68
CG-8M, CH-20, CK-20, & CN-7M ..................................72
CD-4MCu, CW-12M-1 & CW-12M-2..............................72
N-12M-1 & N-12M-2 .......................................................72
ALOYCO* 20 ..................................................................74
DURIMET* 20.................................................................74
ILLIUM* P .......................................................................74
IN-849 .............................................................................74
IN-862 .............................................................................74
SANDUSKY* Alloy 75 ....................................................74
Stainless Steels, Wrought .....................................................54
Types 201, 202 & 301 ....................................................56
Types 302, 303, 303 Se & 304 ......................................56
Types 304L, 304 +,Boron & 305 ....................................56
Types 309, 310 &, 314 ...................................................56
Types 316, 316L, 317 & 317LM* ...................................56
Types 321, 329, 330 & 347 ............................................58
Types 405, 409, 410 & 414 ............................................66
Types 402, 430 & 431 ....................................................66
Types 440C & 446..........................................................68
15-5PH*,17-4PH* & 17-7PH*.........................................64
17-14 Cu Mc ...................................................................66
18-9LW*..........................................................................62
19-9 DL ...........................................................................66
29-4.................................................................................68
29-4-2..............................................................................68
904L ................................................................................60
AL-6X* ............................................................................60
AM 350* & AM 355* .......................................................64
CARPENTER* No. 10 ....................................................60
CARPENTER 20Cb-3* ...................................................60
CUSTOM 455*................................................................64
E-BRITE* 26-1................................................................68
INDEX
Page
FERRALIUM* 255 ..........................................................60
Greek Ascoloy ................................................................66
HASTELLOY* M-352 .....................................................60
JESSOP* JS700 & JS777..............................................60
NITRONIC* 20, 32, 33, 40, 50 & 60 ..............................62
PH 13-8 Mo*, PH 14-8 Mo* & PH 15-7 Mo* ..................64
SEA-CURE* ...................................................................68
STAINLESS W* ...........................................................64
Steel, Alloy
3% Nickel ....................................................................48
9% Nickel........................................................................50
300M...............................................................................48
9310................................................................................48
AISI 4340, 4620, 4820 & 8620.......................................48
High-Yield-Strength........................................................50
IN-787.............................................................................50
Maraging 18-200,18-250 & 18-300................................50
NITRALLOY* N ..............................................................48
Steel, Carbon.........................................................................46
Steel, Cast
2% Nickel ....................................................................50
3% Nickel ....................................................................50
Super-Invar............................................................................ 24
Tantalum................................................................................ 78
TD Nickel ...............................................................................44
THERLO*...............................................................................24
Tin..........................................................................................10
TINEL* Alloy A.......................................................................28
Titanium Alloys
Ti-35A, Ti-50A & Ti-75A.................................................16
Ti-0.2 Pd .........................................................................16
Ti-5 AI-2.5 Sn .................................................................16
Ti-8 AI-1 Mo-1 V .............................................................16
Ti-6 AI-2 Sn-4 Zr-2 Mo ...................................................18
Ti-6 AI-6 V-2 Sn..............................................................18
Ti-6 AI-4 V ......................................................................18
Ti-6 AI-2 Sn-4 Zr-6 Mo ...................................................18
Ti-13 V-11 Cr-3 AI ..........................................................18
Ti-10 V-2 Fe-3 Al............................................................20
Ti Code 12......................................................................18
TINEL* Alloy A................................................................28
Tungsten................................................................................ 78
Tungsten Alloys
Tungsten - 2.5 (Ni + Cu) ................................................78
Tungsten - 7.5 Ni-2.5 Cu................................................78
Tungsten - Rhenium.......................................................78
UDIMET* Alloy 500 ...............................................................44
UDIMET* Alloy 700 ...............................................................44
Uranium .................................................................................80
Waspaloy ............................................................................... 46
WAUKESHA METAL*
No. 23 .............................................................................26
No. 88 .............................................................................28
White Gold, 18K ....................................................................80
WI-52 Alloy ............................................................................44
Wrought Iron..........................................................................46
X-40 Alloy ..............................................................................46
YORCORON* ..........................................................................6
ZILLOY* 15............................................................................12
Zinc ........................................................................................12
Zinc Alloys
Zinc - 4 AI .......................................................................12
Zinc - 4 Al-1 Cu ..............................................................12
Zirconium ............................................................................... 80
Zirconium-Hafnium Alloy .......................................................80
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Strip Annealed
10a
32
45
RF40
Spring Temper
50a
55
RB60
145
165
RC35
170
190
RC40
150
175
RC38
180
200
RC42
Cu bal
Be 1.7
Co 0.25
Cu bal
Be 1.9
Co 0.25
Cu bal
Be 0.6
Co 2.5
90
110
11
RB96
110
120
RB99
Cu bal
Be 0.38
Co 1.55
Ag 1
90
110
17
RB96
110
120
14
RB99
Strip Annealed
15a
40
50
50
Hard Temper
60a
75
135
Strip Annealed
11a
44
66
RF54
Spring Temper
65
94
RB91
Strip Annealed
14a
46
65
RF58
Spring Temper
62
91
30
RB90
Annealed
21a
54
45
RF80
Hard
50a
70
10
RB75
Annealed
22a
53
65
RF75
Annealed
25a
58
49
RB56
58
70
17
RB75
19
47
64
RF73
Spring Temper
80
100
RB95
Annealed
28a
66
68
RB55
Spring Temper
122
RB101
Soft
45a
82
40
RB84
Hard
60a
89
32
RB87
Cu 85
Zn 15
Cu 70
Zn 30
Cu 65
Zn bal
Cu 61
Zn bal
Cu 71
Zn bal
Sn 1
As, Sb or P0.06
Cu 60.5
Zn bal
Sn 0.75
Cu bal
Sn 5
P 0.2
Cu bal
Sn 10
P 0.2
Cu bal
AI 7
Fe 2.5
Cu 99.90 min
Hard
Annealed
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
9.41
2512 3
10.3
17
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.91
1980
0.092
9.82
0.298
8.26
1600 to 1800
9.3
7503 to 900
39
750 to 900
39
19
7.3
17
6.5
14503 to 1800
20
1500 to 1700
19
0.298
8.26
1600 to 1800
0.10
0.316
8.75
1885 to 1955
9.3
9.84
6.4
Copper C11000
Copper Beryllium
C17000
Copper Beryllium
C17200
Copper Beryllium
C17500
0.316
8.75
1850 to 1900
9.8
0.316
8.75
1880
10.42
11043
28
17
0.308
8.53
1750
8403
37
16
0.306
8.47
1710
0.09
11.32
8043
38.4
15
5.6
Yellow Brass
C27000
0.303
8.39
1660
0.09
11.62
8523
37
15
5.6
Muntz Metal
C28000
0.308
8.53
1720
0.09
11.22
7683
41.5
16
6.0
0.304
8.41
1650
0.09
11.82
804
39.9
15
5.6
0.320
8.86
1920
0.09
9.92
4803
69.1
16
0.317
8.78
1830
3483
94.3
16
0.285
7.89
1915
4683
74.1
17
1 = 68 to 212F
0.09
0.09
0.09
0.09
2 = 68 to 572F
11.12
10.22
9.022
3 = at 68F
6.4
Copper Beryllium
50 C17600
Red Brass
C23000
6.0
Cartridge Brass
C26000
6.4
Admiralty Brass
C44300
C44400
C44500
Naval Brass
C46400
Phosphor Bronze
C51000
Phosphor Bronze
C52400
Aluminum Bronze
C61400
4 = 68 to 392F
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Cu 82
AI 9
Ni 5
Fe 4
Rod Annealed
52a
103
24
RB94
Cu bal
Si 3.3
Annealed
Spring Temper
21a
62a
56
110
63
4
RB76
RB97
Copper-Nickel C70600
TubeASTM B 111 & B 552
PlateASTM B 171 & B 402
RodASTM B 151
Cu bal
Ni 10
Fe 1.25
Mn 0.3
Tube Annealed
Light Drawn
16a
57a
44
60
42
10
RB65
RB72
Copper-Nickel C71000
Sheet, Strip, Plate & BarASTM B 122
Pipe & TubeASTM B 466
WireASTM B 206
Cu 79
Ni 21
Strip Annealed
Spring Temper
14
79
52
82
35
3
RB27
RB84
Copper-Nickel C71300
(Coinage Alloy)
Cu bal
Ni 25
Zn 1 max
Mn 1 max
Annealed
Spring Temper
18
82
52
86
42
6
RF79
RB89
Copper-Nickel C71500
SheetASTM B 122
PlateASTM B 171
TubeASTM B 111
Cu bal
Ni 30
Fe 0.55
Mn 0.5
Tube Annealed
25a
60
45
RB45
Copper-Nickel C71640
(YORCORON*)
Cu bal
Ni 30
Fe 2
Mn 2
Plate Annealed
Plate Hard
29
98
67
104
45
6
107
194
Copper-Nickel C72200
Plate, Sheet, Strip & BarASTM B 122 & B 402
TubeASTM B 111
Cu bal
Ni 16
Fe 0.8
Cr 0.5
Mn 0.5
Annealed
18
46
46
RB30
Copper-Nickel 55-45
(Constantan, etc.)
Cu 55
Ni 45
Annealed
21a
60
32
80
Cold Worked
135
250
Soft
22
55
35
RB42
Hard
81
83
RB85
Cu 92
Ni 4
Sn 4
95
101
649
Cu 85
Ni 9
Sn 6
143 50
163
Cu 81.8
Ni 9
Sn 8
Cb 0.2
155
170
RC36
Cu 77
Ni 15
Sn 8
162 50
178
Nominal Composition
%
Material
Copper-Nickel-Tin C72500
Plate, Sheet, Strip & BarASTM B 122
Cu-Ni-Sn Spinodal Alloy C72600
Cu bal
Ni 9.5
Sn 2.3
49 = in 1 in.
50 = 0.05 % offset
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
7.64
1905-1940
0.1053
0.308
8.53
1880
0.09
0.323
0.323
0.323
8.94
8.94
8.94
2100
0.09
2100-2190
0.09
148
17
6.4
10.02
252 3
148
15
5.6
312 3
115
18
6.8
252 3
160
20
7.5
9.52
9.12
193
9.02
204 3
225
22
8.3
8.33
173 3
301
22
8.82
139 3
159 5
20
8.2
8.28
155
300
24
372 3
94.3
20
8.94
2260
0.323
8.86
240 3
2225
0.323
9.02
0.09
0.0943
0.323
8.94
2052-2148
0.321
8.89
2355
2065
0.321
8.89
9.22
7.5
Nickel-Aluminum
Bronze
C63200
High Silicon
Bronze
C65500
Copper-Nickel
C70600
Copper-Nickel
C71000
Copper-Nickel
C71300
(Coinage
Alloy)
Copper-Nickel
C71500
Copper-Nickel
C71640
(YORCORON*)
Copper-Nickel
C72200
Copper-Nickel
55-45
(Constantan,
etc.)
Copper-Nickel-Tin
C72500
0.321
8.89
1950
69
16
Cu-Ni-Sn
Spinodal Alloy
C72600
0.321
8.89
2012
94
17
Cu-Ni-Sn
Spinodal Alloy
C72700
0.321
8.89
2012
104
17
Cu-Ni-Sn
Spinodal Alloy
C72800
0.321
8.89
2039
147
18
Cu-Ni-Sn
Spinodal Alloy
C72900
2 = 68 to 572F
3 = at 68F
5 = at 77F
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Soft
22a
55
40
RB35
65
78
RB85
25
58
40
RB40
74
85
RB87
Soft
24
60
40
RB45
Hard
65a
97
RB88
Annealed
27
60
40
RB55
Hard
85a
100
RH91
As Cast
17a
35
25
60
Hardness,
Brinell or
Rockwell
Cu 65
Zn bal
Ni 18
Cu 56.5
Zn bal
Ni 12
Hard
Annealed
Hard
Cu 55
Zn bal
Ni 18
Cu
Zn
Pb
Sn
6 Bronze C90500
(88-10-0-2)
CastingsASTM B 22, B 271, B 505 & B 584
Cu bal
Sn 10
Zn 2
As Cast
21a
45
31
80
M Bronze C90300
(88-8-0-4)
CastingASTM B 271, B 505 & B 584
Cu bal
Sn 8.5
Zn 4
As Cast
22a
52
48
70
Cu
Sn
Pb
Zn
83
7
7
3
As Cast
19a
34
18
60
Cu
Ni
Sn
Zn
bal
5
5
2
As Cast
23a
50
35
85
60a
85
10
180
Cu
Ni
Sn
Pb
Zn
bal
5
5
1
2
As Cast
23a
50
35
80
Aged (575F)
30a
60
120
Cu
AI
Ni
Fe
Mn
81
9
5
4
I
As Cast
38a
95
25
159
Copper-Nickel C96200
CastingsASTM B 369
Cu
Ni
Mn
Fe
Si
Cb
bal
10
0.9
1.4
0.2
0.5
As Cast
25
45
30
90
Cu 72
Zn bal
Ni 18
85
5
5
5
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.82
0.316
8.73
0.310
8.58
0.314
8.70
0.317
2100
2030
0.09
9.02
228 3
173
18
6.8
189
1832
264
204 3
189
18
6.8
1930
0.09
9.32
Nickel Silver
C73500
Nickel Silver
C75200
Nickel Silver
C76600
Nickel Silver
C77000
8.75
1840
10.2
500
63
13
0.315
8.72
1800
15
G Bronze
C90500
(88-10-0-1)0
0.318
8.80
1832
102
14
M Bronze
C90300
(88-8-0-4)
0.322
8.93
1800
10
14.5
0.320
8.86
1880
0.093
114
374 3
15
0.320
8.86
0.093
112
268 3
15
14
0.276
7.64
250 3
16
1880
19101940
0.1053
9.02
Nickel-Tin Bronze
Type A
C94700
Nickel-Tin Bronze
Type B
C94800
Nickel-Aluminum
Bronze
C95800
Copper Nickel
C96200
0.323
2 = 68 to 572F
8.94
2100
3 = at 68F
9.5
17
4 = 68 to 392F
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
As Cast
40b
Cu bal
Zn 20
Ni 12
Pb 9
Sn 2
As Cast
Cu bal
Zn 8
Ni 20
Pb 4
Sn 4
Cu bal
Zn 2
Ni 25
Pb 2
Sn 5
Nominal Composition
%
Material
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
75b
25b
120b
18
35
15
55
As Cast
26
47
22
85
As Cast
25a
50
18
58
Cast (Ingot)
1.56
42
Cu bal
Ni 30
Mn 0.8
Fe 0.8
Si 0.4
Cb 0.7
Sb 99.8 min.
Bismuth-lead Alloy
Bi 55.5
Pb 44.5
Cast
6.4
65
10
Bismuth-Tin Alloy
Bi 58
Sn 42
Cast
8.0
200
22
Bismuth-Lead-Tin-Cadmium Alloy
Bi
Pb
Sn
Cd
50
26.7
13.3
10
Cast
5.99
200
Bi
Pb
In
Cd
Sn
44.7
22.6
19.1
5.3
8.3
Cast
5.4
Lead
Pig FormASTM B 29
Pb 99.9 min
Rolled
1.9
2.5
50
Pb 90
Sb 10
Cast
6.8
24
13
Rolled
4.1
47
Rolled
2.2
45
Bismuth-Lead-Indium-Cadmium-Tin Alloy
Tellurium Lead
Pb 99.85
Te 0.04
Cu 0.06
1.5
12
Sn 50
Pb 50
Cast
6.8
50
14
Sn 60
Pb 40
Cast
7.1
45
15
Sn 99.8 min
Chill Cast
2.1
70
10
3.9
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.94
2260
9.42
18
Nickel Silver
C97300
0.320
8.86
1830
0.12
10.0
120
204
19
Nickel Silver
C97600
0.321
8.89
2090
150
19
0.320
8.86
1910
19
Nickel Silver
C97800
6.62
10.5
1166
0.092
5.5
131
234
11.3
2.8
255
0.03C
11.6
Bismuth-Lead
Alloy
Bismuth-Tin
Alloy
0.315
8.72
281
0.045C
8.3C
0.339
9.38
158
0.040C
12.2C
0.320
8.85
117
0.035
0.410
11.35
621
0.030
0.393
10.88
545
0.032
13.8
Antimony
Bismuth-LeadTin-Cadmium
Alloy
Bismuth-LeadIndiumCadmiumTin Alloy
16.4
240
124
Lead
15.1
200
152
Antimonial Lead
Tellurium Lead
0.410
11.35
621
0.030
16.4
240
124
0.321
8.89
421
0.051
13.1
310
93
50-50 Tin-Lead
Solder
0.306
8.50
374
0.055
12.2
330
90
60-40 Tin-Lead
Solder
0.263
7.29
449
0.053
12.8
428
66
2 = 68 to 572F
2.4
Tin
c = Estimated
11
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
19.5
65
38
Cold Rolled
21
50
35
25
130
Cold Rolled
42
20
150
10
82
91
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Zn bal
Pb 0.08
Zn bal
Mg 0.01
Cu 1
Zn bal
AI 4
Mg 0.04
Die Cast
41
Zn bal
AI 3.9
Mg 0.05
Cu 1
Die Cast
47.6
Mn 72
Cu 18
Ni 10
Rolled
95
115
Sheet Annealed
13
35
23
Cold Rolled
22
24
44
Bar Annealed
10
26
22
45
Heat Treated
40
62
22
105
Sheet Annealed
11
26
20
Heat Treated
42
64
19
Sheet Annealed
16
30
28
Cold Rolled
27
29
55
Sheet Annealed
13
28
25
47
Cold Rolled
37
42
77
Sheet Annealed
18
25
30
Heat Treated
40
45
12
95
Bar Annealed
15
33
16
60
Heat Treated
73
83
11
150
21
43
6.5
220
AI 99.0 min
AI bal
Cu 4
Mn 0.5
Mg 0.5
Core: 2024
AI bal
Cu 4.5
Mn 0.6
Mg 1.5
Cladding:
AI 99.3 min
AI bal
Mn 1.2
AI bal
Mg 2.5
Cr 0.25
AI bal
Si 0.6
Cu 0.25
Mg 1
Cr 0.25
AI bal
Zn 5.6
Cu 1.6
Mg 2.5
Cr 0.25
AI bal
Si 12
Die Casting
As Cast
12
2.5
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.259
7.14
7.18
786
0.094
792
0.096
18
746
35.5
19.3
726
38
11
Zinc
ZILLOY*
15
0.24
6.6
728
0.10
15.2
784
38.2
Zinc-Aluminum
Alloy
0.240
6.70
727
0.10
15.2
755
39.2
Zinc-AluminumCopper Alloy
0.26
7.21
0.12
15.31
58
18
0.23
1050
C.D.C. Manganese
Alloy
772
0.101
0.100
0.099
0.097
0.098
0.101
0.096
1 = 68 to 212F
2.71
2.79
2.77
2.73
2.68
2.70
2.80
2.65
1215
1185
0.23
1180
0.23
1210
0.23
1200
0.23
1205
0.23
1175
0.23
1080
0.23
1540
17
10.0
3.75
1510
18
10.0
3.75
12.71
1190 5
23
10.5
4.0
840 5
35
10.5
4.0
13.1
12.61
1340 5
21
10.6
3.75
35
10.6
4.0
1340 5
21
10.0
3.75
26
10.0
3.75
13.21
960 5
30
10.2
3.75
960 5
30
10.2
3.75
13.01
1190 5
23
10.0
3.75
1070 5
26
10.0
3.75
10.4
3.9
840 5
35
10.4
3.9
11.51
870 5
34
10.3
3.85
12.91
12.91
840
1070
Aluminum
1100
Aluminum Alloy
2017
Aluminum Alloy
Alclad
1024
Aluminum Alloy
3003
Aluminum Alloy
5052
Aluminum Alloy
6061
Aluminum Alloy
7075
Cast Aluminum
Alloy
413.0
5 = at 77F
13
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
23
10
45
24
48
24
36
12
25
50
26
48
16
75
43
47
0.5
125
0.5
85
Hardness,
Brinell or
Rockwell
AI bal
Si 5
AI bal
Cu 3.5
Si 8.5
Die Casting
AI bal
Cu 4.5
Si 1.1
Sand Casting
AI bal
Mg 4
Sand Casting
As Cast
Heat Treated
As Cast
Cast Aluminum Alloy 510.0 (UNS A05200)
CastingsASTM B 26
AI bal
Mg 10
Sand Casting
Solution Heat Treated
AI bal
Si 12
Mg 1
Ni 2.5
Cu 1
AI bal
Mg 1.5
Ni 2
Cu 4
Sand Casting
Heat Treated Plus 650F
30
32
MAGNESIUM ALLOYS
Magnesium Alloy AZ 31B (UNS M11311)
Plate & SheetASTM B 90
ForgingsASTM B 91
Bar, Tube & WireASTM B 107
Mg bal
AI 3
Zn 1
Mn 0.2 min
Sheet Annealed
22
37
21
56
Hard Sheet
32
42
15
73
Mg bal
AI 8.5
Zn 0.5
Mn 0.12 min
As Forged
33
48
11
69
36
50
72
Mg bal
All 9
Zn 0.7
Mn 0.15 min
Die Cast
22
33
63
Mg bal
AI 8.7
Zn 0.7
Mn 0.13 min
As Cast
14
24
2.5
60
19
40
70
Mg bal
AI 9
Zn 2
Mn 0.10 min
As Cast
14
25
65
Solution Treated
14
40
10
63
22
40
81
Aged Castings
16
23
50
29
37
68
CastingsHeat Treated
15
32
RB66
Mg bal
Zn 2.6
Zr 0.7
Rare earth metal3
Mg bal
Th 3.25
Zr 0.7
14
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
2.69
1170
0.23
12.31
9905
28
10.3
3.85
Cast Aluminum
Alloy
B443.0
0.098
2.72
1100
0.23
11.61
6705
45
10.3
3.85
Cast Aluminum
Alloy
A380.0
0.102
2.81
1190
0.23
12.71
9605
30
10.0
3.75
Cast Aluminum
Alloy
295.0
0.096
2.65
1185
0.23
13.41
9645
30
10.3
3.85
Cast Aluminum
Alloy
514.0
0.093
2.57
1120
0.23
13.71
6105
50
9.5
3.55
Cast Aluminum
Alloy
520.0
0.098
2.72
1050
0.23
11.01
8105
36
10.6
4.35
0.102
2.81
1175
0.23
12.61
9305
31
10.3
3.85
55
5222
87
Cast Aluminum
Alloy
336.0
Cast Aluminum
Alloy
242.0
MAGNESIUM ALLOYS
0.064
0.065
1.77
1.80
1170
1130
0.245
0.25
14.5
657
14.51
6.5
6.5
2.4
2.4
1.80
1105
0.25
14.51
4932
102
6.5
2.4
0.065
1.81
1105
0.25
14.51
4932
90
6.5
2.4
91
4932
84
0.066
1.82
1100
0.25
14.01
6.5
Magnesium Alloy
AZ 80A
0.065
Magnesium Alloy
AZ 31B
2.4
99
84
Magnesium Alloy
AZ 91B
Cast Magnesium
Alloy
AZ 91C
Magnesium Alloy
AZ 92A
0.066
1.83
1189
0.25
14.51
6966
42
6.5
2.4
Magnesium Alloy
EZ 33A
0.065
1.79
1204
0.24
7846
37
6.5
2.4
Magnesium Alloy
HK 31A
6396
46
6.5
2.4
1 = 68 to 212F
2 = 68 to 572F
5 =at 77F
15
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
13
27
55
As Extruded
38
49
14
75
Aged
44
53
11
82
Hardness,
Brinell or
Rockwell
Mg bal
Th 3.25
Zn 2.1
Zr 0.7
Mg bal
Zn 5.5
Zr 0.45 min.
TITANIUM ALLOYS
Titanium Ti-35A (UNS R50250)
ForgingsASTM B 381
Sheet, Strip & PlateASTM B 265
PipeASTM B 337
TubesASTM B 338
BarsASTM B 348
CastingsASTM B 367
Ti
C
Fe
N
H
O
bal
0.08 max.
0.12 max
0.03 max
0.015 max
0.18
Sheet Annealed
30
40
30
135
Ti
C
Fe
N
H
O
bal
0.08 max.
0.20 max
0.03 max
0.015 max
0.25 max
Sheet Annealed
45
55
25
215
Ti
C
Fe
N
H
O
bal
0.08 max
0.30 max
0.05 max
0.015 max
0.40 max
Sheet Annealed
75
85
18
265
Ti bal
Pd 0.15
C 0.08
Fe 0.20 max
N 0.03 max
H 0.015 max
O 0.25 max
Sheet Annealed
45
55
25
215
Ti bal
AI 5
Sn 2.5
C 0.08 max
Fe 0.50 max
N 0.05 max
H 0.0175 max
O 0.20 max
Annealed
125
135
13
RC39
Ti bal
AI 8
Mo 1
V 1
C 0.08 max
Fe 0.30 max
N 0.05 max
H 0.015 max
O 0.12 max
Sheet Annealed
130
140
13
RC39
16
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
1.83
1198
0.23
14.84
7556
39
6.5
2.4
0.066
1.83
1175
0.24
14.51
8156
36
6.5
2.4
845
Magnesium Alloy
ZK 60A
TITANIUM ALLOYS
Titanium
Ti-35A
0.163
4.50
3063
0.124
4.8
1083
4.8
114
118
336
14.9
6.5
Titanium
Ti-50A
0.163
4.50
3100
0.125
336
14.9
6.5
Titanium
Ti-75A
0.164
4.53
3038
0.129
4.8
360
15.1
6.5
Ti-0.2 Pd Alloy
0.163
4.50
3100
0.125
4.8
1143
340
14.9
6.5
Ti-5 AI-2.5 So
Alloy
0.162
4.47
3002
0.125
5.2
543
1092
16
7.0
Ti-8 AI-1 Mo
1V
Alloy
0.158
1 = 68 to 212F
4.36
3 = at 68F
4.7
4 = 68 to 392F
1192
17.5
17
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Bar Annealed
130
140
15
RC39
Sheet Annealed
155
165
12
RC41
Sheet Annealed
130
140
13
RC39
Heat Treated
165
175
12
Sheet Annealed
150
160
12
RC42
Sheet Annealed
130
135
13
RC37
Heat Treated
170
180
Annealed
62
82
20
240
Ti bal
AI 6
Sn 2
Zr 4
Mo 2
C 0.04 max
Fe 0.15 max
N 0.04 max
H 0.015 max
O 0.12 max
Ti bal
AI 5.5
V 5.5
Sn 2
Cu 0.7
Fe 0.7
C 0.05 max
N 0.04 max
H 0.015 max
O 0.20 max
Ti
AI
V
C
Fe
N
H
O
Ti bal
AI 6
Sn 2
Zr 4
Mo 6
C 0.04 max
Fe 0.15 max
N 0.02 max
H 0.015 max
O 0.12 max
Ti Code 12
Sheet, Strip & PlateASTM B 265
Pipe & TubeASTM B 337 & B 338
BarsASTM B 348
ForgingsASTM B 381
FittingsASTM B 363
18
Ti
V
Cr
AI
C
Fe
N
H
O
bal
6.3
4
0.08 max
0.25 max
0.05 max
0.015 max
0.20 max
bal
13.5
11
3
0.05 max
0.35 max
0.05 max
0.025 max
0.17 max
Ti bal
Ni 0.8
Mo 0.3
C 0.08 max
Fe 0.30 max
N 0.03 max
H 0.015 max
O 0.25 max
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
4.53
3000
16.5
Ti-6 AI-6 V2 Sn
Alloy
0.164
4.53
3100
0.155
5.0
503
942
16.5
Ti-6 AI-4 V
Alloy
0.160
4.42
3000
0.135
4.9
503
1026
16.5
6.1
0.175
4.64
4.83
3050
0.120
5.2
5.44
493
16.5
483
918
15
62
Ti Code 12
0.163
3 = at 68F
4.51
0.13
4 = 68 to 392F
5.328
132
28 = 32 to 600F
31236
15
6.2
35 = at 75F
19
Material
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
166
176
12
135
145
20
Annealed
60
100
30
RB88
Form and
Condition
Hardness,
Brinell or
Rockwell
Ti
V
Fe
AI
C
N
H
O
bal
10
2
3
0.05 max
0.05 max
0.015 max
0.13 max
Forgings Solution
Treated and
(1) Aged
(2) Overaged
Ni 80
Cr 20
Ni 60
Cr 15
Fe bal
Annealed
50
105
30
200
Fe bal
Ni 35
Cr 20
Annealed
55
102
30
RB83
Ni-Cr AlloyA
Ni
Cr
AI
Fe
Annealed
65
140
35
Annealed
80
100
25
215
Magnetic Annealed
22
79
64
RB62
38
90
35
Hydrogen Annealed
18
64
27
RB60
40
80
33
Hydrogen Annealed
Cast Annealed
RC45
Sintered
65
RC43
bal
20
3
3
Fe bal
Cr 23
AI 5
Co May be present
MAGNETIC ALLOYS
80 Ni-4 Mo Alloy
(Magnetically Soft)
ASTM A 753, Alloy 4
Ni 80
Mo 4
Fe bal
Mu Metal
(Magnetically Soft)
ASTM A 753, Alloy 3
Ni 77
Cu 5
Cr 2.5
Fe bal
48 Ni-bal Fe Alloy
(Magnetically Soft)
ASTM A 753, Alloy 2
Ni 48
Fe bal
Alnico II
(Permanent Magnet Alloy)
Fe bal
AI 10
Ni 18
Co 13
Cu 6
20
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.168
4.65
5.443
16
8.41
2550
0.104
7.3
9.615
10410
650
31
0.298
8.25
2460
0.112
7.6
9.416
9310
675
29
0.287
7.95
2515
0.098
8.816
14810
610
27
0.293
8.11
2550
0.104
7.4
88
800
0.262
7.25
2750
9.316
812
80 Ni-20 Cr
Alloy
Ni-Cr AlloyA
Fe-Cr-AI
AlloyB
MAGNETIC ALLOYS
80 Ni-4 Mo Alloy
0.315
0.307
0.296
8.7
8.5
8.2
2600
0.12
6.41
6.9
4.71
6.9
6.9
232
350
33.3
6.6
30
337
25
270
390
408
Mu Metal
48 Ni-bal Fe
Alloy
Alnico II
0.256
0.243
1 = 68 to 212F
7.09
6.73
2 = 68 to 572F
3 = at 77F
10 = at 212F
15 = 68 to 1832F
16 = 68 to 937F
43 = 32 to 800F
21
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Cast Annealed
Cast Annealed
Sintered
Sintered
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
RC45
RC45
RC42
RC50
50
RC44
23
RC50
Sintered
RC44
RC60
RC57
Fe bal
AI 12
Ni 26
Cu 3
Alnico IV
(Permanent Magnet Alloy)
Fe bal
AI 12
Ni 28
Cc 5
Alnico V**
(Permanent Magnet Alloy)
Alnico VI**
(Permanent Magnet Alloy)
Alnico VII**
(Permanent Magnet Alloy)
Alnico Vill**
(Permanent Magnet Alloy)
Fe bal
AI 8
Ni 15
Co 24
Cu 3
Fe bal
AI 8
Ni 16
Co 24
Cu 3
Ti 1.25
Fe bal
Al 8.5
Ni 18
Co 24
Cu 3.25
Ti 5
Fe bal
AI 7
Ni 15
Co 35
Cu 4
Ti 5
12
9.1
60
5.4
Cunico
(Permanent Magnet Alloy)
Cu 50
Ni 21
Co 29
100
RB95
Cunife
(Permanent Magnet Alloy)
Cu 60
Ni 20
Fe 20
100
RB73
Permalloy 49
Fe bal
Ni 48.5
Ni 80
Mo 4
Fe bal
22
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
6.89
7.22
3605
0.253
7.00
7.32
4505
408
0.232
6.42
7.3
0.265
7.34
6.32
2825
0.241
6.67
6.32
3005
0.268
7.42
6.32
3005
0.241
6.67
6.32
3185
Alnico IV
Alnico V**
Alnico VI**
Alnico VII**
0.259
7.17
6.12
3485
300
Alnico VIII**
0.265
7.34
0.300
8.30
7.82
1445
0.311
8.61
7.82
1085
Cunico
Cunife
2895
Permalloy
49
3495
Moly Permalloy
4/79
2 = 68 to 572F
5 = at 77F
23
Nominal Composition
%
Material
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Annealed
40
71
43
132
44
70
38
RB77
Form and
Condition
Ni 36
Fe bal
Super-Invar
Ni 31
Fe bal
Co 5.2
Mo 0.5 max
Si 0.15 max
C 0.05 max
Ni 42
Fe bal
35
68
45
138
Ni 50
Fe bal
Annealed
33
77
45
144
Iron-Nickel Temperature
Compensating Alloys
Ni
Fe
Ni
Fe
Ni
Fe
Annealed
65
125
Annealed
35
85
40
Annealed
45
80
30
150
Annealed
29
73
44
RB67
Annealed
35
90
40
125
Aged
110
175
25
305
126
131
265
176
192
365
Annealed
35
85
30
135
Cold Worked
135
155
10
305
Aged
160
190
14
Ni-Fe-Co AlloyC
Fe bal
Ni 29
Co 17
ELINVAR*
Fe bal
Ni 33
Cr 5
W 2
Mn 0.6
Si 0.5
C 0.5
38 Ni-7 Cr Alloy
Ni 38
Fe bal
Cr 7
Mn 0.45 max
Si 0.30 max
C 0.12
Ni 42.2
Mn 0.4
Fe 48.5
Cr 5.3
Ti 2.6
AI 0.6
ISO-ELASTIC*
Ni 36.85
Fe 54.25
Mn 0.55
Cr 7.10
Mo 0.45
24
29.5
bal___
31
bal___
32.5
bal
Ni 38
Co 15
AI 0.7
Ti 1.4
Cb 3
Fe bal
C
Also available, with minor chemical variations, under the following trademarks:
THERLO* RODAR* KOVAR*
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.11
2600
0.12
0.8
72.6
494
21
8.1
INVAR*
Super-Invar
0.294
8.14
0.294
8.14
0.297
8.22
0.295 to
0.292
8.17 to 8.08
Near zero
22
2600
0.12
2.9
106
405
22
8.5
42 Ni-Iron Alloy
2600
0.12
4.9
124
270
24
9.3
50 Ni-Iron Alloy
0.12
6.0 to 3.0
80
480
22
0.123
3.3
98
294
Iron-Nickel
Temperature
Compensating
Alloys
Ni-Fe-Co AlloyC
0.303
8.39
2650
ELINVAR*
0.295
8.17
0.12
3 Plus
22
38 Ni-7 Cr
Alloy
0.292
8.08
0.293
8.11
2700
3.317
570
0.12
4.519
95
611
24-29
9-10
528
25
9.2
44
44
NI-SPAN-C* Alloy
902
ISO-ELASTIC*
0.292
8.08
4 Plus
INCOLOY* Alloy
903
0.294
8.14
17 = 70 to 200F
2539
0.105
19 = at 500F
4.0
117
379
21.3
44
8.6
44
44 = at 100F
25
Material
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Annealed
35
75
40
140
As Cast
25a
57
22
110
21.5
67
47
100
18
55
55
90
21
67
47
100
Strip Annealed
16
50
50
RB80
Rod Annealed
45
121
41
160
140
176
16
325
132
185
28
330
Strip Annealed
45
105
40
RB70
Nominal Composition
%
Ni 95
Mn 4.9
C 0.1
Nickel 210
CastingsASTM A 494
Ni 95.6
Cu 0.5
Fe 0.5
Mn 0.8
Si 1.5
C 0.8
Ni 99.5
Mn 0.2
Fe 0.2
C 0.08
Ni 99.5
Mn 0.2
Fe 0.2
C 0.01
Ni 99.5
Mn 0.2
Fe 0.1
Ti 0.03
Mg 0.01
C 0.08
Ni 99.98
Ni 98.5
Mn 0.2
Ti 0.4
Mg 0.4
C 0.2
Ni 94
AI 4.4
Si 0.5
Ti 0.6
Mn 0.2
Fe 0.3
C 0.2
Ni bal
Be 1.95
Ti 0.5
Ni bal
Be 2.15
C 0.4 max
Ni
Be
Cr
C
26
bal
2.7
0.7
0.1
Annealed
150
215
15
RC47
Casting Annealed
60
110
10
RC28
180
190
RC51
As Cast
70
125
285
180
195
328
As Cast
55
75
10
160
Ni 78
Pb 3.5
Sn 8
Zn 7.5
Mn 2
a = 0.5 % extension under load
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.73
2600
7.417
0.11
3063
102
30
12
Nickel 210
(Cast)
0.301
8.34
2550
0.13
8.85
410
125
21.5
0.321
8.89
2635
0.11
7.417
5203
57
30
12
0.321
8.89
2635
0.11
7.4
5503
46
30
11
Nickel 200
Nickel 201
Nickel 205
0.321
8.89
2635
0.11
7.417
5203
57
30
12
0.321
8.89
2650
0.11
7.417
595
45
30
Nickel 270
0.316
8.75
2620
0.106
6.817
4003
100
30
11
PERMANICKEL*
Alloy
300
95
DURANICKEL*
Alloy
301
0.298
8.25
2620
0.318
8.84
0.29
0.287
0.32
3 =at 68F
8.10
7.95
8.86
2310
0.104
7.2
1653
255
30
11
8.018
2203
143
28.5
27
7.7
215
2310
4 = 68 to 392F
7.48
17 = 70 to 200F
31
192
345 to 172
32
18 = at 500F
25 to 28
22
31 = 32 to 500F
Nickel Beryllium
440
Nickel Beryllium
M 220C
Nickel Beryllium
CR-1
WAUKESHA
METAL*
No. 23
32 = 70 to 1100F
27
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
As Cast
38
45
150
Proprietary
62
125
20
RA60
30
79
48
125
25
63
48
100
31
69
45
RB67
Strip Annealed
22
64
43
RB54
Hot Rolled
45
85
35
145
Cold Drawn
75
100
25
200
49
97
44
155
111
160
23.5
300
As Cast
35
75
40
150
As Cast
35
75
40
150
Casting Annealed
225
340
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
TINEL* Alloy A
(Nitinol Memory Alloy)
Ni bal
Fe 5
Cr 12.5
Mo 3
Bi 4
Sn 4
Mn 0.8
Ni 50
Ti 50
Ni 66
Cu 31.5
Fe 1.1
Mn 1
Si 0.2
C 0.2
Ni 42.5
Cu 55
Mn 1.6
Fe 0.4
28
Ni 54.5
Cu 45
Mn 0.05
Fe 0.2
C 0.08
Ni 66
Cu 31
Fe 1.2
Mn 1
Si 0.2
C 0.2
S 0.04
Ni 65.5
Cu 29.5
AI 2.7
Ti 0.6
Fe 1
Mn 0.8
C 0.1
Si 0.2
Ni 66
Cu 30.5
Fe 1
Mn 0.8
Si 1.6
C 0.15
Ni 66
Cu 32.5
Fe 1.5
Mn 0.8
Si 1.6
Cb + Ta2.0
Ni 64
Cu 29
Fe 2
Mn 0.8
Si 4
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.58
0.23
6.5
8.031
200"
67531
27
2370
6.11
1253
600
11
TINEL* Alloy A
(Nitinal
Memory Alloy)
MONEL* NICKEL-COPPER-ALLOYS
0.319
8.84
2460
0.321
8.88
0.321
8.88
0.319
0.306
0.312
8.84
8.46
8.63
2460
2460
2450
0.102
0.099
7.7
17
7.6
17
294
7.417
300
25
151 3
307
26
0.102
7.717
0.100
7.6
17
26
9.232
186 1
32
320
136 1
380
2450
0.13
9.2
0.302
8.36
2350
0.13
8.932
14 = Dynamic Modulus
32 = 70 to 1100F
186
26
370
0.13
8.63
3 = at 68F
121
307
136 20
0.312
1 = 68 to 212F
151
320
17 = 70 to 200F
10
9.4
MONEL*
Alloy
400
MONEL*
Alloy
401
MONEL*
Alloy
404
9.5
MONEL*
Alloy
R-405
9.5
MONEL*
Alloy
K-500
Nickel-Copper
Alloy 140
(Cast)
23
Nickel-Copper
Alloy 411
(Cast)
24
23
20 = at 200F
Nickel-Copper
Alloy 505
(Cast)
(S MONEL*)
31 = 32 to 500F
33 = 68 to 1500F
29
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Ni
Cr
Fe
C
Ti
AI
32.5
21
45.5
0.05
0.4
0.4
Ni
Cr
Fe
C
Ti
32
20.5
44.5
0.05
1.1
Ni
Cr
Fe
C
32.5
21
46
0.4
Ni 42
Cr 21.5
Fe 30
Cu 2.2
Mo 3
Ti 0.9
AI 0.1
C 0.03
42
87
44
150
Strip Annealed
34
92
44
RB76
56
114
30
RB93
46
102
44
160
Rod Annealed
44
100
43
150
41
96
45
150
66
112
41
RB79
As Cast
41a
78
15
175
52
112
56
172
30
Ni 76
Cr 15
Fe 8
Mn 0.5
Si 0.2
C 0.08
Cu 0.2
Ni 60.5
Cr 23
Fe 14
AI 1.4
Mn 0.5
Si 0.2
C 0.05
Cu 0.5
Ni bal
Cr 15.5
Fe 9
Cb 2
Si 1.6
Mn 0.9
Cu 0.5
C 0.2
Ni 52
Cr 22
Co 12.5
Mo 9
AI 1.2
Fe 1.5
Mn 0.5
Si 0.5
Ti 0.3
C 0.07
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
17
0.287
7.94
2525
0.11
7.9
0.287
7.94
2525
0.1085
7.817
0.283
7.83
2500
7.817
0.11
595
28
11
865
6095
30
11
825
6695
29.7
80
INCOLOY*
Alloy
800
INCOLOY*
Alloy
801
INCOLOY*
Alloy
802
INCOLOY*
Alloy
825
0.294
8.14
2550
7.817
773
678
28
8.43
2575
0.106
7.417
1033
620
30
11
INCONEL*
Alloy
601
0.293
8.11
2494
0.1073
7.617
783
47
710
30
11.8
Cast Alloy
611
0.300
8.30
2950
0.11
41
8.9
104
700
23
INCONEL*
Alloy
617
0.302
1 = 68 to 212F
8.36
2510
3 = at 68F
0.100
6.43
5 = at 77F
94
17 = 70 to 1500F
736
36.6
46 = 80 to 750F
11.8
47 = 70 to 1400F
31
Material
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
70
140
50
180
Casting Annealed
40
70
20
Form and
Condition
Ni 61
Cr 21.5
Fe 4
Cb 3.6
Mo 9
Mn 0.2
Si 0.2
C 0.05
Ni bal
Cr 21.5
Mo 9
Cb 4
Fe 3
Mn 0.5
Si 0.6
C 0.06 max
Ni 61
Cr 29
Fe 9
Mn 0.2
Si 0.2
C 0.02
Cu 0.2
Ni 52.5
Cr 19
Fe 18.5
AI 0.5
Ti 0.9
Cb 5.1
Mo 3.0
Mn 0.2
Si 0.2
C 0.04
Ni 73
Cr 15.5
Fe 7
AI 0.7
Ti 2.5
Cb 1
Mn 0.5
Si 0.2
C 0.04
32
Ni 72.5
Cr 15.5
Fe 7
AI 1.2
Ti 2.3
Cb 1
Mn 0.5
Si 0.2
C 0.05
51
104
47
RB90
180
208
20
RC45
126
184
25
RC36
122
177
27
RC36
Annealed
75
125
50
176
142
175
20
337
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.305
8.44
2460
0.098
7.117
683
776
30.1
11.8
INCONEL*
Alloy
625
Cast Alloy
625
INCONEL*
Alloy
690
0.296
8.19
2510
0.1073
7.817
9320
691
30.6
INCONEL*
Alloy
718
0.296
0.298
0.298
3 = at 68F
8.19
8.25
8.25
2437
2600
0.104
0.103
7.217
7.017
793
725
29
11.2
833
731
31
11
2600
743
31
11
17 = 70 to 200F
INCONEL*
Alloy
X-750
INCONEL*
Alloy
751
20 = at 200F
33
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Ni
Cr
AI
Ti
Fe
C
77.4
20.5
0.15
0.35
0.5
0.10
Ni
Cr
AI
Ti
Fe
C
74.5
20.5
1.25
2.4
0.5
0.05
Ni 57
Cr 20.5
Co 17
AI 1.6
Ti 2.6
Fe 0.5
C 0.05
Ni bal
Cr 15
Co 15
Mo 3.5
Ti 4
AI 5
51
116
44
RB87
90
154
39
RC34
116
179
33
RC38
125
180
27
RC37
76
138
53
RC22
52
115
61
RB90
60
111
52
RB90
HASTELLOY*ALLOYS
HASTELLOY* Alloy B-2 (UNS N10665)
Sheet, Plate & StripASTM B 333
RodASTM B 335
Pipe & TubeASTM B 619, B 622 & B 626
FittingsASTM B 366
Ni bal
Mo 28
Fe 2 max
Co 1 max
Cr 1 max
Mn 1 max
Si 0.10 max
C 0.02 max
Ni bal
Mo 16
Cr 15.5
Fe 5
W 4
Co 2.5 max
Mn 1 max
V 0.35 max
Si 0.08 max
C 0.02 max
Ni bal
Cr 16
Mo 15.5
Fe 3 max
Co 2 max
Mn 1 max
Ti 0.70 max
Si 0.08 max
C 0.015 max
34
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.302
0.297
8.37
8.22
2515
2500
0.11
0.103
6.1
6.2
79 10
70 10
655 10
732 10
32.0
32.114
NIMONIC*
Alloy
75
NIMONIC*
Alloy
80A
NIMONIC*
Alloy
90
0.296
0.284
8.19
7.85
2500
2400
0.11
0.11
6.4
6.2
75 10
708 10
803 10
32.814
31.314
NIMONIC*
Alloy
115
HASTELLOY*ALLOYS
HASTELLOY*
Alloy
B-2
0.333
9.22
0.093 10
6.245
85 10
829 10
31.414
HASTELLOY*
Alloy
C-276
0.321
8.89
2500
0.102
6.217
78 10
779
29.814
HASTELLOY*
Alloy
C-4
0.312
10 = at 212F
8.64
0.102 10
14 = Dynamic Modulus
6.017
79 10
17 = 70 to 200F
748
30.814
45 = 68 to 600F
35
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
46
102
62
RB84
47
100
50
RB79
45
115
51
RB96
72
129
51
RB93
53
123
55
Ni bal
Cr 22
Fe 19.5
Mo 6.5
Cb + Ta2
Cu 2
Co 2.5 max
Mn 1.5
Si 1 max
W 1 max
C 0.05 max
Ni bal
Cr 22
Fe 19.5
Mo 7
Co 5 max
Cu 1.9
W 1.5 max
Mn 0.8
Si 0.4
Cb + Ta0.3
C 0.015 max
Ni bal
Cr 7
Mo 16.5
Fe 5 max
Mn 0.8 max
Si 1 max
AI + Ti 0.5 max
W 0.5 max
Cu 0.35 max
Co 0.2 max
B 0.01 max
C 0.06
HASTELLOY* Alloy S
Bars & ForgingsAMS 5711
Sheet, Plate & StripAMS 5873
WireAMS 5838
Ni bal
Cr 16
Mo 15
Mn 0.5
Si 0.4
AI 0.2
La 0.02
B 0.015 max
C 0.02 max
Fe 3 max
Co 2 max
W 1 max
Ni bal
Cr 5
Mo 24
Fe 6
Co 2.5 max
Mn 1 max
Si 1 max
V 0.6 max
C 0.12 max
36
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.31
0.10910
2450
7.517
705
27.814
HASTELLOY*
Alloy
G-3
0.300
8.31
HASTELLOY*
Alloy
N
0.320
8.93
0.10010
2550
7.045
79 10
725
31.714
HASTELLOY*
Alloy
S
0.316
8.75
0.10210
2516
6.417
97 42
770 5
30.814
HASTELLOY*
Alloy
W
0.325
1 = 68 to 212F
9.03
5 = at 77F
2400
10 = at 212F
7.038
14 = Dynamic Modulus
17 = 70 to 200F
38 = 70 to 600F
42 = at 392F
45 = 68 to 600F
37
Material
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
52
114
43
RB90
46
76
20
230
46
72
25
220
Castings
2100F, Air Cooled
58
60
221-420
Castings
2125F, Water Quenched
35
60
159
Castings
2125F, Water Quenched
41
54
18
143
Casting As Cast
103
112
Form and
Condition
Ni bal
Cr 22
Fe 18.5
Mo 9
Co 1.5
Mn 1 max
Si 1 max
W 0.6
C 0.10
CHLORIMET* ALLOYS
CHLORIMET* 2
Gen. ApplicationsASTM A 744
CastingsASTM A 494
Ni bal
Mo 31.5
Fe 3 max
Cr 1 max
Mn 1 max
Si 1 max
C 0.07 max
CHLORIMET* 3
Gen. ApplicationsASTM A 744
CastingsASTM A 494
Ni bal
Cr 18.5
Mo 18.5
Fe 3 max
Mn 1 max
Si 1 max
C 0.07 max
ILLIUM* G
ILLIUM* 98
Ni bal
Cr 28
Mo 8.5
Cu 5.5
Si 3.5
C 0.05
Ni bal
Cr 22.5
Mo 6.4
Cu 6.5
Fe 6.5
Mn 1.25 max
Si 0.2
C 0.2
Ni ball
Cr 28
Mo 8.5
Cu 5.5
Fe 1
Mn 1.25 max
Si 0.2
C 0.05
38
Ni bal
Cr 15.5
Mo 5
Fe 4.5
Ti 2.5
AI 3.5
B 0.05
3.5
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.22
2470
0.116
7.7017
63 37
712
28.514
CHLORIMET* ALLOYS
CHLORIMET* 2
0.33
9.2
2400
6.4
38
7.1
38
27
CHLORIMET* 3
0.32
9.0
2400
24
ILLIUM* ALLOYS
ILLIUM* B
0.310
8.57
ILLIUM* G
0.300
8.31
0.105
7.171
84 37
741
24.3
ILLIUM* 98
0.302
8.36
1 = 68 to 212F
8.05
3 = at 68F
14 = Dynamic Modulus
17 = 70 to 200F
28.7`
37 = at 70F
38 = 70 to 600F
39
Material
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Casting As Cast
107
123
Casting As Cast
109
130
15
RC39
130
175
14
107
166
23
Sheet Solution
Heat Treated
58
118
58
RB90
Form and
Condition
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Alloy 713LC
Ni bal
Cr 12.5
Mo 4.2
Cb 2
Ti 0.8
AI 6.1
B 0.012
Zr 0.1
C 0.12
Ni bal
Cr 12
Mo 4.5
Cb 2
Ti 0.6
AI 5.9
B 0.01
Zr 0.1
C 0.05
Ni 42.5
Cr 12.5
Mo 5.7
Fe bal
Ti 2.8
AI 0.2
B 0.015
Fe bal
Cr 22
Ni 20
Co 20
Mo 3
W 2.5
Mn 1
Cb + Ta 1
La 0.02
C 0.1
N 0.2
Si 0.4
AI 0.2
Zr 0.02
7.9
RC34
Ni 26
Cr 15
Mo 1.3
Fe bal
Ti 2
AI 0.2
B 0.015
105
146
25
RC28
Ni bal
Cr 10
Co 15
Mo 3
Ti 4.7
AI 5.5
B 0.014
V 1
Zr 0.06
Cast
123
147
Ni bal
Cr 15
Mo 3
W 3
Cb 3
Fe 7
Ti 0.6
AI 0.4
B 0.005
Zr 0.03
73
139
47
215
40
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
7.91
2350
5.9217
146 20
29.9114
Alloy
713LC
0.289
8.00
5.9217
146 20
17
20
2410
28.614
29.9
14
Alloy
901
0.297
8.22
7.75
97
HAYNES*
Alloy
556
0.297
8.23
29.514
Alloy
A-286
0.286
7.91
2550
0.10
9.1717
100 20
546
29.114
10.4
IN-100
Alloy
0.280
7.75
2435
7.2017
31.214
IN-102
Alloy
0.309
8.55
14 = Dynamic Modulus
2530
17 = 70 to 200F
7.3217
86 20
29.114
20 = at 200F
41
Material
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
138
159
5.5
154
170
101
147
7.1
Sheet Solution
Heat Treated
67
146
59
RC24
70
139
56
RB96
Cast
125
140
RC39
Form and
Condition
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
IN-792 Alloy
Ni-939 Alloy
Ni bal
Cr 16
Co 8.5
AI 3.4
Ti 3.4
W 2.6
Mo 1.7
Ta 1.7
Cb 0.9
C 0.17
Zr 0.1
B 0.01
Ni bal
Cr 12.4
Co 9
AI 3.1
Ti 4.5
W 3.8
Mo 1.9
Ta 3.9
C 0.12
Zr 0.1
B 0.02
Ni bal
Cr 22.5
Co 19
Ti 3.7
AI 1.9
W 2.0
Ta 1.4
Cb 1.0
C 0.15
Zr 0.1
B 0.01
Co bal
Ni 10
Cr 20
W 15
Fe 3 max
Mn 1.5
Si 1 max
C 0.10
Co bal
Cr 22
Ni 22
W 14
Fe 3 max
Mn 1.25 max
Si 0.35
La 0.04
C 0.10
42
Ni bal
Cr 9
Co 10
Mo 2.5
W 10
Ti 1.5
AI 5.5
B 0.015
Ta 1.5
Zr 0.05
C 0.15
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.11
2250-2400
0.1051
6.4517
88 18
29.214
11.314
IN-792
Alloy
0.298
8.25
IN-939
Alloy
0.295
0.330
8.16
9.13
2255-2444
2570
0.101
0.092
6.6
6.8
17
83
75
20
736
28.9
32.6
L-605 Alloy,
HAYNES* Alloy
25
14
HAYNES*
Alloy
188
0.324
8.97
2425
0.10110
6.617
84 20
554
33.614
MAR-M*
246 Alloy
0.307
1 = 68 to 212F
8.5
2475
10 = at 212F
14 = Dynamic Modulus
17 = 70 to 200F
33
18 = at 500F
20 = at 200F
43
Material
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
122
180
16
RC39
154
206
14
Bar Annealed
55
105
55
RB90
67
140
35
90
100
25
110
176
16
140
204
17
85
125
380
Form and
Condition
Ni bal
Cr 20
Co 10
Mo 10
Ti 2.6
AI 1
B 0.005
Ni bal
Cr 19
Co 11
Mo 10
Fe 2
Ti 3.1
AI 1.5
B 0.005
Ni bal
Cr 25.5
Fe 14.5
Mo 3.8
W 3.8
Co 3.8
Si 1.1
Mn 2 max
C 0.08 max
Ni 20
Cr 20
Co bal
Mo 4
W 4
Cb 4
Fe 4
TD Nickel
Ni bal
ThO22.2
Ni bal
Cr 18
Co 18.5
Mo 4
Ti 2.9
Al 2.9
Zr 0.05
B 0.006
Ni bal
Cr 15
Co 18.5
Mo 5.2
Ti 3.5
AI 4.3
B 0.03
WI-52 Alloy
44
Co bal
Cr 21
W 11
Cb 2
Fe 2
C 0.45
Cast
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.25
2500
5.917
90 20
29.814
REN 41*
Alloy
0.298
8.25
2500
0.11
6.6317
62 20
31.914
RA 333*
Alloy
0.298
8.25
8.6733
31
S-816
Alloy
0.313
8.65
2450
0.322
8.90
2650
0.106
7.3817
86 20
34.914
13.6
6.017
572 20
45
22.014
TD Nickel
UDIMET*
Alloy
500
0.290
8.02
2540
6.7517
77 20
32.114
UDIMET*
Alloy
700
0.286
7.91
2550
7.7421
136 20
32.414
WI-52
Alloy
0.321
8.87
14 = Dynamic Modulus
2450
0.11
17 = 70 to 200F
8.0
21
172
20
20 = at 200F
21 = 70 to 1000F
33 = 68 to 1500F
45
Material
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
115
185
25
Casting As Cast
120
141
146
204
15
Casting As Cast
76
108
58
118
49
RB92
106
145
19
300
Hot Rolled
29
45
26
90
Annealed
19
38
45
67
Form and
Condition
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Ni bal
Cr 19.5
Co 13.5
Mo 4.3
Ti 3
AI 1.3
B 0.006
Zr 0.04
B-1900 Alloy
Ni bal
Cr 8
Co 10
Mo 6
Ti 1
AI 6
Ta 4
B 0.015
Zr 0.10
Ni bal
Cr 15
Mo 4
W 4
Fe 27
Ti 3
AI 1
B 0.01
Co bal
Ni 10.5
Cr 25.5
W 7.5
Fe bal
Ni 20
Cr 21
Co 20
Mo 3
W 2.5
Cb + Ta 1
Mn 1.5
Si 1 max
C 0.10
N 0.15
Fe bal
Ni 26
Cr 13.5
Mo 2.7
Ti 1.7
AI 0.1
B 0.005
Fe bal
Slag 2.5
Hot Rolled
30
48
30
100
Fe bal
C 0.20
Mn 0.45
Si 0.25
Annealed
38
65
30
130
62
90
25
179
46
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.296
8.19
2475
6.817
74 20
30.914
B-1900
Alloy
0.297
8.22
2375
6.5017
71 20
31.014
D-919
Alloy
0.296
8.19
2550
7.6017
92 20
30.014
11.6
0.311
8.60
8.3921
82 20
32.814
X-40
Alloy
N-155 Alloy,
MULTIMET*
Alloy
0.296
8.20
2470
7.91
101 42
559
29.314
DISCALOY*
0.288
7.97
2665
0.113
8.5017
97 20
28.414
7.86
2795
0.108
6.8
490
57
30.1
11.8
0.278
7.70
2750
0.11
6.35
418
70
29
0.284
7.86
2760
0.107
6.7
360
60
30
1 = 68 to 212F
14 = Dynamic Modulus
17 = 70 to 200F
20 = at 200F
21 = 70 to 1000F
Ingot Iron
Wrought Iron
Carbon Steel
SAE 1020
42 = at 392F
47
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe bal
C 0.40
Mn 0.70
Si 0.28
Ni 1.85
Cr 0.80
Mo 0.25
Fe bal
C 0.20
Mn 0.55
Si 0.28
Ni 1.80
Mo 0.25
48
Fe bal
C 0.20
Mn 0.60
Si 0.28
Ni 3.50
Mo 0.25
Fe bal
C 0.20
Mn 0.80
Si 0.28
Ni 0.55
Cr 0.50
Mo 0.20
Fe bal
C 0.10
Mn 0.55
Si 0.28
Ni 3.25
Cr 1.20
Mo 0.12
Fe bal
C 0.24
Mn 0.55
Si 0.30
Ni 3.50
Cr 1.15
Mo 0.25
AI 1.25
Fe bal
C 0.20
Mn 0.50
Si 0.25
Ni 3.50
Yield Point
240
290
10
550
Annealed
Oil Quenched &
Tempered at 1100F
80
120
18
250
130
140
13
290
Annealed
O.Q. & Tempered 300F
Oil Quenched & Tempered
at 1100F
56
105
80
135
30
17
160
287
80
95
218
Annealed
O.Q. & Tempered 300F
Oil Quenched & Tempered
at 1100F
66
126
100
170
25
15
200
82
102
26
205
Annealed
51
76
32
157
142
17
284
100
25
200
123
159
16
321
Before Nitriding
Core after Nitriding
at 975F
115
132
22
275
170
180
16
370
Plate Normalized
45
78
23
160
Annealed
Oil Quenched & Tempered
at 300F
112
80
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.283
0.283
0.284
0.283
0.283
7.84
7.84
2740
2740
0.107
0.117
6.7
6.3
360
17
7.83
0.11
6.317
7.86
0.115
6.4
7.85
7.83
6.21
0.11
0.115
6.5
60
30
11.6
264
148
29
290 3
149
29
255 3
158
29
12
260 26
180
29
12
238
168
29
AISI 4340
Alloy
Steel
AISI 4620
Alloy
Steel
AISI 4820
Alloy
Steel
AISI 8620
Alloy
Steel
9310
Alloy
Steel
NITRALLOY* N
Alloy
Steel
0.283
7.83
0.115
6.5
240
166
29
3 1/2% Nickel
Steel
0.284
1 = 68 to 212F
7.85
3 = at 68F
0.15
21
6.15
48
17 = 70 to 200F
253
26 = at 120F
30
48 = 0 to 200F
49
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
93
88
110
110
25
26
RC23
RC23
95
73
90
108
89
104
36
28
25
195
150
185
110
125
19
255
42
75
25
156
42
75
26
157
Annealed
117
145
17
RC27
Aged at 900F
200
215
12
RC46
Annealed
116
146
19
RC29
Aged at 900F
250
260
10
RC49
Annealed
115
147
17
RC32
Aged at 900F
280
290
RC53
9% Nickel Steel
PlateASTM A 353 & A 553
Pipe & TubeASTM A 333 & A 334
Forgings ASTM A 522
Fe bal
C 0.13 max
Mn 0.60
Si 0.25
Ni 9
Fe bal
C 0.05
Mn 0.55
Si 0.25
Ni 0.85
Cr 0.75
Mo 0.2
Cu 1.15
Cb 0.04
Fe bal
C 0.16
Mn 0.85
Si 0.35
Ni 1.50 max
Cr 2.00 max
Mo 0.35
V 0.08 max
Ti 0.10 max
Zr 0.15 max
Cu 0.50 max
B 0.003
Fe bal
C 0.21
Mn 0.75
Si 0.25
Ni 2.3
Castings Normalized
and Tempered
(Heavy Sections are
Liquid Quenched)
Fe bal
C 0.13
Mn 0.75
Si 0.25
Ni 3.5
Castings Normalized
and Tempered
(Heavy Sections are
Liquid Quenched)
50
Fe bal
Ni 18
Mo 4.2
Ti 0.2
AI 0.1
C 0.03 max
Co 7.8
Fe bal
Ni 18
Mo 4.8
Ti 0.4
AI 0.1
C 0.03 max
Co 7.8
Fe bal
Ni 18.5
Mo 4.8
Ti 0.65
AI 0.1
C 0.03 max
Co 8.8
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
7.86
2730
0.08822
4.922
9123
203
3023
IN-787 Alloy
Steel
0.283
7.84
0.12
6.417
29
12
High-Yield-Strength
Alloy Steels
0.283
7.83
0.11
6.6
264
148
29
12
2 1/2% Nickel
Cast Steel
0.283
7.83
0.11
6.4
2783
6.3
132
29
12
3 1/2% Nickel
Cast Steel
0.284
0.289
7.84
8.00
2650
0.11
0.107
254
2033
5.6
24
136
144
300 to 420
30
12
273
26.2
27.0
27.5
3 = at 68F
17 = 70 to 200F
22 = 320 to 70F
23 = at 32F
Maraging
Steel
18-200
Maraging
Steel
18-250
Maraging
Steel
18-300
24 = 70 to 900F
51
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
C 3.4
Si 1.8
Mn 0.8
Fe bal
C 2.5
Si 1
Mn 0.55 max
Fe bal
As Cast
32
190
Annealed
33
52
12
130
Fe bal
C 3.6
Si 2.3
Mn 0.5
Ni 0.75
Annealed
47
65
24
160
Fe bal
C 3.6
Si 2.3
Mn 0.5
Ni 0.75
Annealed or As Cast
52
72
13
174
Fe bal
C 3.6
Si 2.3
Mn 0.5
Ni 0.75
As Cast
65
90
228
Fe bal
C 3.6
Si 2.3
Mn 0.5
Ni 0.75
80
110
260
Fe bal
C 3.6
Si 2.3
Mn 0.5
Ni 0.75
120
140
325
Fe bal
Ni 15.5
Si 2
Mn 1.25
Cu 6.5
Cr 2
C 3 max
As Cast
27
150
As Cast
27
145
Fe bal
Ni 35
Si 1.5
Mn 0.6
C 2.4 max
As Cast
22
110
Fe
Ni
Si
Cr
C
As Cast
32
59
14
170
52
Fe bal
Ni 20
Si 2
Mn 1.25
Cr 2
C 3 max
bal
20
2.25
2.25
3 max
Density,
Melting Point,
Ib/cu in. Specific Gravity
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
7.20
2150
0.264
7.32
2250
6.7
310
400
14
6.6
180
25
Malleable Iron
0.122
Ductile Iron
0.250
7.1
2150
6.21
276 10
399 11
6.2
276
10
399
11
5.9
218
10
408
11
24.5
9.3
Ductile Iron
0.250
7.1
2150
24.5
9.3
Ductile Iron
0.252
7.2
2150
24.5
9.3
Ductile Iron
0.252
7.2
2150
5.91
218 10
408 11
10
11
24.5
9.3
Ductile Iron
0.252
7.2
2150
5.9
218
408
24.5
9.3
Ni-Resist
Type 1
0.264
7.3
2250
0.116
10.44
276
1020
15.6
4.5
Ni-Resist
Type 2
0.264
7.3
2250
0.116
10.44
276
1020
15.6
4.5
Ni-Resist
Type 5
0.268
7.41
2250
2.84
273
10.5
4.5
Ductile NI-Resist
Type D-2
0.268
1 = 68 to 212F
7.41
2250
4 = 68 to 392F
10.44
93
612
17.5
10 = at 212F
11 = at 72F
53
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
As Cast
32
58
30
155
As Cast
36
63
20
160
Sand Cast
60
600
Chill Cast
90
650
Sand Cast
60
575
Chill Cast
100
625
Sand Cast
80
600
Chill Cast
110
650
As Cast
16
520
As Cast
16
520
Strip Annealed
55
115
60
RB90
Strip Annealed
55
105
55
RB90
Strip Annealed
40
up to
165
110
up to
200
60
RB85
up to
RC41
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe
Ni
Si
C
Fe bal
Ni 36
Si 5.3
Mn 0.5
Cr 2.0
C 2.0
bal
35
2
2.4 max
Fe bal
Ni 4.5
Cr 2.1
C 3.3
Si 0.5
Mn 0.6
Fe bal
Ni 4.5
Cr 2.1
C 2.8
Si 0.5
Mn 0.6
Fe bal
Ni 6
Cr 8.5
C 3
Si 1.5
Mn 0.6
DURIRON*
(Cast)
Iron-Silicon Alloy
Fe bal
Si 14.5
C 0.85
DURICHLOR*
(Cast)
Iron-Silicon-Molybdenum Alloy
Fe bal
Si 14.5
Ma 3
C 0.85
Fe bal
Cr 17
Ni 4.5
Mn 6.5
N 0.25 max
C 0.15 max
Fe bal
Cr 18
Ni 5
Mn 9
N 0.25 max
C 0.15
Fe
Cr
Ni
C
54
bal
17
7
0.15 max
Cold Rolled
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
7.68
2250
18
Ductile Ni-Resist
Type D-5
Ductile Ni-Resist
Type D-5S
0.266
7.37
0.278
7.70
0.278
0.278
7.70
7.70
2160-2232
17
5.4
4.725
4.725
6.425
16
99 26
480 5
25
99 26
480 5
25
99 26
540 5
25
Ni-Hard
Type 1
Ni-Hard
Type 2
Ni-Hard
Type 4
DURIRON*
0.255
7.0
2300
0.13
7.421
23
0.255
7.0
2300
0.13
7.2
23
DURICHLOR*
0.283
7.86
0.282
7.83
0.29
7.9
5 = at 77F
10 = at 212F
2590
0.12
17 = 70 to 200F
8.7
27
423
28.6
Type 201
Stainless
Steel
Type 202
Stainless
Steel
10.228
427
9.4
113 10
432
28
12.5
21 = 70 to 1000F
25 = 50 to 200F
26 = at 120F
27 = 32 to 700F
Type 301
Stainless
Steel
28 = 32 to 600F
55
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe
Cr
Ni
C
bal
18
9,
0.15 max
Fe
Cr
Ni
S
Se
C
bal
18
9
0.15 min or
0.15 min
0.15 max
Fe
Cr
Ni
C
bal
18.5
9.5
0.08 max
Fe
Cr
Ni
C
bal
18.5
10
0.03 max
Fe
Cr
Ni
B
bal
18
10
2
Fe
Cr
Ni
C
bal
18
12
0.12 max
Fe
Cr
Ni
C
bal
23
13.5
0.20 max
Fe
Cr
Ni
C
bal
25
20
0.25 max
Fe
Cr
Ni
Si
C
bal
25
20
2.5
0.25 max
56
Sheet Annealed
40
up to
165
90
up to
190
50
5
RB85
up to
RC40
35
90
50
160
35
up to
160
85
up to
185
50
4
RB80
up to
RC40
Sheet Annealed
28
75
50
RB70
Sheet Annealed
53
96
12
RB95
Sheet Annealed
38
85
50
RB80
Sheet Annealed
45
90
45
RB85
Sheet Annealed
45
95
45
RB85
Bar Annealed
50
100
45
180
Cold Rolled
Bar Annealed
Sheet Annealed
Cold Rolled
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
7.9
2590
0.12
9.6
113 10
432
28
12.5
0.29
7.9
2590
0.12
9.6
113 10
432
28
0.29
7.9
2650
0.12
9.6
113 10
432
28
12.5
0.29
7.9
2650
0.12
9.6
113 10
432
28
12.5
0.29
7.9
0.12
10.529
445
0.29
0.29
0.29
0.279
10 = at 212F
7.9
7.9
7.9
7.72
2650
2650
2650
0.12
0.12
0.12
0.12
113 10
9.6
96 10
8.3
96 10
8.0
8.4
28
28 = 32 to 600F
121
10
432
468
468
462
28
29
30
29
Type 302
Stainless
Steel
Type 304
Stainless
Steel
Type 304 L
Stainless
Steel
Type 304
plus Boron
Stainless
Steel
12.5
Type 305
Stainless
Steel
Type 309
Stainless
Steel
Type 310
Stainless
Steel
Type 314
Stainless
Steel
29 = 32 to 1200F
57
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe bal
Cr 17
Ni 12
Mo 2.25
C 0.08 max
Sheet Annealed
40
90
50
RB85
Fe bal
Cr 17
Ni 13
Mo 2.25
C 0.03 max
Sheet Annealed
32
75
50
RB72
Fe bal
Cr 19
Ni 13
Mo 3.5
C 0.08 max
Sheet Annealed
Fe Bal
Cr 19
Ni 14
Mo 4.25
Si 1.0 max
C 0.03 max
Annealed
44
91
42
RB85
Annealed
45
90
40
RB84
Sheet Annealed
35
90
50
RB80
Annealed 1775F,
water quenched
Aged 1400F, 8 hr
Aged 1400F, 40 hr
80
105
25
RC22
RC45
RC50
Hot Rolled
55
100
35
200
Annealed
39
85
50
150
Sheet Annealed
40
95
45
RB85
Fe bal
Cr 19
Ni 14
Mo 4.3
Si 0.7
C 0.02
Fe
Cr
Ni
Ti
C
bal
18
11
5C min
0.08 max
Fe bal
Cr 27.5
Ni 4.75
Mo 1.5
C 0.15
Fe
Cr
Ni
Si
C
Fe bal
Cr 18
Ni 11
Cb + Ta10C min
C 0.08 max
58
bal
19
35
1.25
0.08 max
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.29
0.29
0.29
0.29
0.29
0.29
0.28
0.289
0.29
10 = at 212F
7.9
7.9
7.9
7.9
7.9
7.9
7.75
8.0
8.03
2550
2550
2550
2500-2550
2500-2550
2600
0.12
0.12
0.12
0.12
0.12
0.12
0.11
2550
0.11
2600
8.9
8.9
7.9
8.0
8.1
0.12
33
9.3
17 = 70 to 200F
113
10
112
10
112 10
8.317
113
10
105
9.3
8.0
113
10
444
444
444
444
440
432
28
28
28
28
28
28
Type 316
Stainless
Steel
Type 316L
Stainless
Steel
Type 317
Stainless
Steel
Type 317LM*
Stainless
Steel
450
86
610
28.5
112 10
438
28
JESSOP*
Type 317L
Plus Stainless
Steel
Type 321
Stainless
Steel
Type 329
Stainless
Steel
Type 330
Stainless
Steel
Type 347
Stainless
Steel
33 = 68 to 1500F
59
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe
Cr
Ni
C
Fe bal
Ni 34
Cr 20
Mo 2.5
Cu 3.5
Cb + Ta8xC min
C 0.06 max
bal
16
18
0.08 max
Fe bal
Cr 20
Ni 24
Mo 6.3
Mn 1.5
Si 0.5
C 0.025
Fe bal
Cr 21
Ni 25
Mo 4.5
Cb 0.4
Cu 0.4
C 0.04 max
Fe bal
Cr 21
Ni 25
Mo 4.5
Cb 0.3
Cu 2.0
C 0.04 max
Fe bal
Cr 20
Ni 25
Mo 4.5
Cu 1.5
Mn 1.7
Si 0.4
C 0.02 max
Fe bal
Cr 22
Ni 26
Mn 2.5 max
Mo 5
Si 1.0 max
Ti 4xC min
C 0.05 max
Fe bal
Cr 26
Ni 5.5
Mo 3
Mn 0.8
Si 0.45
Cu 1.7
N 0.17
C 0.04 max
60
Annealed
35
75
55
126
Bar Annealed
43
90
39
183
Strip Annealed
40
90
45
115
127
14
151
162
4.5
Annealed
35 min
80 min
30 min
212 max
Annealed
35 min
80 min
30 min
212 max
Annealed
2012F, Water Quenched
36
85
50
140
44
84
42
RB83
94
124
25
RC21
Hardened at 950F
102
131
24
Density,
Melting Point,
Ib/cu in. Specific Gravity
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.03
0.291
8.05
0.293
8.1
0.12
0.12
2500
9.5
8.31
8.51
84.6
476
26
625
28
11
95 1
570
29
0.29
0.29
8.0
8.0
9.15
9.15
102
102
CARPENTER*
No.10
Stainless
Steel
CARPENTER
20Cb-3*
Stainless
Steel
AL 6X*
Stainless
Steel
JESSOP
J5700*
Stainless
Steel
JESSOP
J5717*
Stainless
Steel
904 L
Stainless
Steel
0.285
7.90
0.123
5.81
126
480
28
HASTELLOY*
Alloy
M-532
0.297
8.22
FERRALIUM*
Alloy
255
0.282
1 = 68 to 212F
7.81
3 = at 68F
6.745
105 3
473
14 = Dynamic Modulus
30.514
26 = at 120F
45 = 68 to 600F
61
Nominal Composition
%
Material
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
75
138
46
RC24
84
142
29
RC36
Annealed
60
115
55
RB96
135
172
28
RC28
204
238
10
RC40
Sheet Annealed
68
115
50
RB95
140
160
18
RC37
191
210
RC44
Sheet Annealed
65
108
43
RB92
132
148
18
RC31
175
192
RC39
65
125
45
RC23
174
194
15
216
234
Bar Annealed
60
103
64
RB95
112
140
35
RC31
174
217
15
RC41
Annealed
30
78
65
150
Fe bal
Cr 23
Ni 8
Mn 2.5
Si 0.8
N 0.35
C 0.33
Fe bal
Cr 18
Ni 1.6
Mn 12
Si 0.5
N 0.3
C 0.10
Fe bal
Cr 18
Ni 3
Mn 13
Si 1.0 max
N 0.3
C 0.08 max
Fe bal
Cr 20
Mn 9
Ni 6.5
Si 1 max
N 0.3
C 0.08 max
C is also available at 0.04 max in UNS S21904
Fe bal
Cr 22
Ni 12.5
Mn 5
Mo 2.25
Si 1.0 max
N 0.3
Cb 0.2
V 0.2
C 0.06 max
Fe bal
Cr 17
Ni 8.5
Mn 8
Si 4
N 0.13
C 0.10 max
62
Fe bal
Cr 18
Ni 9
Cu 3.5
Density,
Melting Point,
Ib/cu in. Specific Gravity
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.279
0.281
7.73
7.78
421
29
11
9.01
110 10
444 5
0.280
7.76
8.917
96 20
438
28
0.283
7.83
9.341
0.285
7.88
9.0
17
108
34
492
28
10
589
26
0.275
7.62
8.81
1 = 68 to 212F
5 = at 77F
10 = at 212F
17 = 70 to 200F
20 = at 200F
34 = at 300F
NITRONIC* 20
Stainless
Steel
NITRONIC* 32
Stainless
Steel
NITRONIC* 33
Stainless
Steel
NITRONIC* 40
Stainless
Steel
NITRONIC* 50
Stainless
Steel
NITRONIC* 60
Stainless
Steel
18-9 LW*
Stainless
Steel
41 = at 300F
63
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
40
130
35
RB85
Hardened
220
235
RC48
110
150
12
RC32
Hardened
185
200
14
RC44
110
150
12
RC32
Hardened
185
200
14
RC44
Solution Treated
55
130
35
RB88
Hardened
225
240
RC48
55
125
25
RB88
Hardened
220
235
RC49
100
160
15
RC30
Hardened
200
225
13
RC48
Annealed
98
135
15
RC26
Hardened at 1000F
190
200
11
RC44
Annealed
60
145
40
290
Hardened
173
206
13.5
410
Annealed
57
160
26
310
Hardened
174
210
14
415
Annealed
115
140
12
280
Hardened
220
230
10
500
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe
Cr
Ni
AI
bal
17
7
1.1
Fe bal
Cr 16.5
Ni 4
Cu 4
Cb + Ta0.3
Fe bal
Cr 15
Ni 5
Cu 4
Fe bal
Cr 15
Ni 7
Mo 2.5
AI 1.1
Fe bal
Cr 14
Ni 8
Mo 2.5
AI 1.1
Fe bal
Cr 13
Ni 8
Mo 2.2
AI 1
Fe
Cr
Ni
Ti
Al
C
Fe bal
Cr 17
Ni 4
Mo 3
C 0.08
Fe bal
Cr 15.5
Ni 4.5
Mo 3
Fe bal
Cr 11.75
Ni 9
Cu 2.25
Ti 1.2
Cb 0.3
C 0.03 max
64
bal
17
7
0.7
0.2
0.07
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
7.81
8.5
0.276
7.65
0.280
7.74
0.282
7.80
0.280
7.74
17
480
5.717
128 18
498
29
11
0.11
6.017
588
0.10
6.017
135 18
462
28.5
12.7
0.11
6.017
588
28.5
11.2
0.10
17
135
462
18
0.282
7.80
0.282
7.80
8.017
480
0.277
7.68
5.017
112 20
498
29
11.4
0.283
7.83
0.278
7.71
6.0
5.317
130 10
600
28
17-7 PH*
Stainless
Steel
17-4 PH*
Stainless
Steel
15-5 PH*
Stainless
Steel
PH 15-7 Mo*
Stainless
Steel
PH 14-8 Mo*
Stainless
Steel
PH 13-8 Mo*
Stainless
Steel
Stainless W*
0.28
7.7
0.28
7.7
145 10
510
28
11.3
0.286
7.92
2550
0.282
7.81
100
475
29.4
11.3
0.286
7.92
2550
0.282
7.81
6.4
105
455
29.3
11.4
0.280
7.74
5.9
29
11
10 = at 212F
17 = 70 to 200F
5.5
6.3
18 = at 500F
AM 350*
Stainless
Steel
AM 355*
Stainless
Steel
CUSTOM 455*
Stainless
Steel
20 = at 200F
65
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
42
86
45
170
93
114
20
255
Hot Rolled
and Stress Relieved
41
74
30
216
Cold Worked
and Stress Relieved
88
98
13
321
Bar Hardened
150
170
13
340
Sheet Annealed
40
65
25
RB75
38
68
25
RB75
Fe bal
Cr 17
Ni 14
Cu 3
Mo 2.5
Ti 0.25
Cb 0.5
Fe bal
Cr 19
Ni 9
Mo 1
W 1.25
Cb + Ta0.4
Ti 0.25
C 0.30
Fe
Cr
W
Ni
bal
12
3
2
Fe
Cr
C
Al
bal
12.5
0.08 max
0.2
Fe bal
Cr 11
Mn 1.0 max
Annealed
Si 1.0 max
Ti 0.75 max (6C min)
C 0.08
Fe bal
Cr 12
C 0.15 max
Sheet Annealed
45
70
25
RB80
Heat Treated
140
180
15
RC39
Fe
Cr
Ni
C
Sheet Annealed
105
120
15
RB98
150
200
15
RC43
Fe bal
Cr 13
C over 0.15
Bar Annealed
50
95
25
RB92
Heat Treated
195
230
500
Fe bal
Cr 17
C 0.12 max
Sheet Annealed
45
up to
95
75
up to
110
25
10
RB80
up to
225
Bar Annealed
95
125
25
260
Hardened
150
195
15
400
66
Fe
Cr
Ni
C
bal
12.5
2
0.15 max
bal
16
1.75
0.20 max
Cold Rolled
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.287
0.287
0.284
0.28
7.94
7.94
7.86
7.7
2615
2670
2790
0.278
7.68
2600-2750
0.28
7.7
2790
0.28
.28
0.280
0.280
7.7
7.7
7.75
7.75
2750
2700
0.10
0.11
0.11
0.11
0.11
0.11
0.11
0.11
8.23
8.5
5.3
6.0
6.5
6.1
5.8
5.7
5.8
6.5
98
28
9.4
29.5
29
360
29
17-14 Cu Me
Stainless
Steel
19-9
DL
Alloy
Greek
Ascoloy
Stainless
Steel
Type 405
Stainless
Steel
Type 409
Stainless
Steel
173 10
342
29
173 10
420
173 10
330
29
181 10
360
29
140 10
432
29
Type 410
Stainless
Steel
Type 414
Stainless
Steel
Type 420
Stainless
Steel
Type 430
Stainless
Steel
Type 431
Stainless
Steel
10 = at 212F
67
Material
Form and
Condition
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe bal
Cr 17
C 1.10
Fe
Cr
N
C
Fe bal
Cr 26
Mo 1
Mn 0.05
Si 0.2
N 0.01
C 0.002
Fe bal
Cr 29
Mo 4
Mn 0.3 max
Si 0.2 max
N 0.02 max
C 0.01 max
Fe bal
Cr 29
Mo 4
Ni 2
Mn 0.3 max
Si 0.2 max
N 0.02 max
C 0.01 max
Fe bal
Cr 26
Mo 3
Ni 2.5
C 0.025 max
bal
25
0.25 max
0.20 max
Bar Annealed
65
110
14
230
275
285
RC57
Sheet Annealed
50
80
20
RB83
Annealed
50
70
30
RB82
Annealed
75
90
25
RB95
Annealed
85
95
22
RB97
Annealed
75
90
32
RB95
Fe bal
Cr 12
C 0.15 max
Fe bal
Cr 12
C 0.30
Fe bal
Cr 12
Ni 4
Mo 0.7
C 0.06 max
Fe bal
Cr 17
Ni 4
Cu 3
Cb 0.3 (Optional)
C 0.07 max
68
150
200
390
Tempered at 1400F
75
100
20
200
165
220
470
Tempered at 1400F
67
110
18
212
100
120
24
269
161
187
10
412
Aged at 1100F
132
145
15
315
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.270
0.277
7.75
7.45
7.66
2700
2750
0.11
5.6
168
0.012
0.100
5.8
5.936
10
360
29
145 10
402
29
136 10
332
Type 440C
Stainless
Steel
Type 446
Stainless
Steel
E-BRITE* 26-1
Stainless
Steel
29-4
Stainless
Steel
0.278
7.69
2750
5.2'
29
0.276
7.64
2735
5.2'
29-4-2
Stainless
Steel
SEA-CURE*
Stainless
Steel
0.275
7.61
7.61
2750
2725
0.11
0.11
5.51
6.421
174 10
468
29
5.51
6.421
174 10
456
29
CA-15 Cast
Stainless
Steel
CA-40 Cast
Stainless
Steel
CA-6NM Cast
Stainless
Steel
0.278
0.280
1 = 68 to 212F
7.70
7.76
2750
2750
10 = at 212F
0.11
0.11
37
6.01
7.021
174 10
469
17
119
10
37
6.617
6.0
17 = 70 to 200F
464
21 = 70 to 1000F
29
28.5
36 = 91 to 223F
CB-7Cu-1
(17-4 PH)
Cast
Stainless
Steel
37 = at 70F
69
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe bal
Cr 15
Ni 5
Cu 3
Cb 0.3 (Optional)
C 0.07 max
Fe
Cr
Ni
C
bal
20
2 max
0.30 max
Fe
Cr
Ni
C
bal
28
4 max
0.50 max
Fe bal
Cr 28
Ni 9
161
187
10
412
Aged at 1100F
132
145
15
315
Annealed
60
95
15
195
As Cast
60
95
15
193
65
97
18
210
As Cast
60
95
15
170
63
97
18
170
32
72
55
133
32
77
55
140
Fe
Cr
Ni
C
bal
19
10
0.03 max
Fe
Cr
Ni
C
bal
19
9
0.08 max
Fe bal
Cr 19
Ni 11
Mo 2.5
C 0.03 max
40
83
50
Fe bal
Cr 19
Ni 10
Mo 2.5
C 0.08 max
42
80
50
163
Fe bal
Cr 19
Ni 10
C 0.08 max
2000F, Water Quenched
Cb 8xC min
or
Cb + Ta10C min
38
77
39
149
Fe bal
Cr 19
Ni 10
S 0.3
Mo 0.6
C 0.16 max
40
77
52
150
36
77
50
163
70
Fe
Cr
Ni
C
bal
19
9
0.20 max
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.280
7.76
2750
0.1137
6.017
6.6
17
119 10
464 37
464
37
28.5
0.272
1.53
2725
0.11
5.71
6.521
154 10
456
29
0.272
7.53
2725
0.12
5.91
6.421
151 10
462
29
510
25
0.277
7.67
2650
0.14
9.6
21
CB-7Cu-2
(15-5 PH)
Cast
Stainless
Steel
CB-30 Cast
Stainless
Steel
CC-50 Cast
Stainless
Steel
CE-30 Cast
Stainless
Steel
0.280
7.75
2600
0.12
9.01
10.021
110 10
457
CF-3 Cast
Stainless
Steel
0.280
7.75
2600
0.12
9.01
10.021
110 10
457
28
CF-8 Cast
Stainless
Steel
0.280
7.75
2550
0.12
8.91
9.721
113 10
492
CF-3M Cast
Stainless
Steel
0.280
7.75
2550
0.12
8.91
9.721
113 10
492
28
CF-8M Cast
Stainless
Steel
CF-8C Cast
Stainless
Steel
0.280
7.75
2600
0.12
9.31
10.321
112 10
28
468
28
2550
0.12
9.0
9.921
113
0.280
7.75
2575
0.12
9.61
10.421
110 10
17 = 70 to 200F
432
7.75
10 = at 212F
28
10
0.280
1 = 68 to 212F
426
21 = 70 to 1000F
CF-16F Cast
Stainless
Steel
CF-20 Cast
Stainless
Steel
37 = at 70F
71
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe bal
Cr 19
Ni 11
Mo 3.5
C 0.08 max
Fe
Cr
Ni
C
bal
24
13
0.20 max
Fe
Cr
Ni
C
bal
25
20
0.20 max
Fe bal
Cr 20
Ni 29
Mo 2
Cu 3 min
C 0.07 max
Fe bal
Cr 26
Ni 5.5
Mo 2.5
Cu 3.0
Ni bal
Cr 16.5
Mo 17
Fe 6
V 0.3
Mn 1.0 max
Si 1.0 max
C 0.12 max
Ni bal
Cr 18.5
Mo 18.5
Fe 3 max
V 0.3
Mn 1.0 max
Si 1.0 max
C 0.07 max
Ni bal
Cr 1.0 max
Mo 28
Fe 5
V 0.3
Mn 1.0 max
Si 1.0 max
C 0.12 max
Ni bal
Cr 1.0 max
Mo 31.5
Fe 3 max
Mn 1.0 max
Si 1.0 max
C 0.07 max
72
40
83
50
50
88
38
190
38
76
37
144
31.5
69
48
130
80
110
20
240
46
min
72
min
4
min
46
min
72
min
25
min
As Agreed
46
min
76
min
6
min
As Agreed
46
min
76
min
20
min
2150F min,
Water Quenched
2150F min,
Water Quenched
Density,
Melting Point,
Ib/cu in. Specific Gravity
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
10
492
CG-8M Cast
Stainless
Steel
0.280
7.75
2550
0.12
8.9
9.721
0.279
7.72
2600
0.12
8.31
9.621
98 10
504
28
CH-20 Cast
Stainless
Steel
0.280
7.75
2600
0.12
8.01
9.221
98 10
540
29
CK-20 Cast
Stainless
Steel
0.289
8.00
2650
8.61
9.721
0.11
6.51
7.121
113
145 10
538
24
CN-7M Cast
Stainless
Steel
CD-4MCu Cast
Stainless
Steel
CW-12M-1 Cast
Stainless
Steel
0.336
9.30
(Calculated)
CW-12M-2 Cast
Stainless
Steel
0.334
9.24
(Calculated)
1 = 68 to 212F
10 = at 212F
N-12M-1
Cast Stainless
Steel
N-12M-2
Cast Stainless
Steel
21 = 70 to 1000F
73
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe bal
Cr 20.5
Ni 28.8
Mo 2.5
Cu 3.5
Mn 1.5 max
Si 1.5 max
C 0.07 max
Fe bal
Cr 20.5
Ni 29
Cu 3.5
Mo 2.5
Mn 1.5 max
Si 1.5 max
C 0.07 max
Fe bal
Cr 28
Ni 8
Cu 3
Mo 2
Mn 0.75
Si 0.75
C 0.20
SANDUSKY* Alloy 75
74
Castings Annealed
(2150F, Water Quenched)
32
69
48
130
2050F, Water
Quenched
25
min
62
min
35
min
130
Castings
1975F, Water Quenched
72
100
18
235
Fe bal
Cr 26
Ni 6.8
Mn 0.7
Si 1.0
C 0.03
Castings, 2050F,
Water Quenched
67
84
26
228
Fe bal
Cr 26
Ni 6.8
Mn 0.8
Si 0.7
C 0.03
Casting, Proprietary
Heat Treatment
62
113
20
235
25
60
20
Annealed 1825F
and
Aged at 1400F
65
95
23
180
81
107
21
220
As Cast
65
70
190
Aged at 1400F
80
115
18
230
As Cast
48
85
16
190
Fe bal
Cr 21
Ni 24
Mo 5
Mn 0.5
Si 0.8
C 0.07 max
Fe bal
Cr 9
Mo 1
C 0.20 max
Fe
Cr
Ni
C
bal
28
4 max
0.50 max
Fe
Cr
Ni
C
bal
28
5.5
0.50 max
Density,
Melting Point,
Ib/cu in. Specific Gravity
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
8.02
2650
0.11
8.61
145 3
538
24
DURIMET* 20
Cast Stainless
Steel
0.289
8.02
2650
0.113
8.61
145 10
538
24
ILLIUM* P
Cast Stainless
Steel
0.275
7.61
IN-849 Cast
Stainless
Steel
0.274
7.58
2680
7.01
29
SANDUSKY*
Alloy 75
0.274
7.58
2680
7.01
29
IN-862 Cast
Stainless
Steel
0.279
0.272
0.274
1 = 68 to 212F
7.72
7.53
7.58
2750
2725
2700
0.11
0.12
0.12
3 = at 68F
6.11
7.121
182 10
420
29
6.321
151
462
29
151 10
486
27
7.721
10 = at 212F
HA Cast Heat
Resistant
Alloy
HC Cast Heat
Resistant
Alloy
HD Cast Heat
Resistant
Alloy
21 = 70 to 1000F
75
Material
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
As Cast
45
95
20
200
Aged at 1400F
55
90
10
270
As Cast
45
85
35
165
Aged at 1400F
50
100
25
190
As Cast
50
80
25
185
Aged at 1400F
55
86
11
200
As Cast
45
80
12
180
Aged at 1400F
65
90
200
As Cast
50
75
17
170
Aged at 1400F
50
85
10
190
As Cast
52
82
19
192
As Cast
38
68
17
160
As Cast
40
71
11.5
As Cast
40
71
11.5
As Cast
40
70
10
180
Aged at 1400F
45
75
200
As Cast
40
70
170
Aged at 1800F
43
73
190
As Cast
54
87
28
Form and
Condition
Fe
Cr
Ni
C
bal
28
9
0.35
Fe
Cr
Ni
C
bal
21
9
0.30
Fe
Cr
Ni
C
bal
26
12
0.35
Fe
Cr
Ni
C
bal
28
16
0.35
Fe
Cr
Ni
C
bal
26
20
0.40
Fe
Cr
Ni
C
bal
30
20
0.40
Fe
Cr
Ni
C
bal
21
25
0.35
Fe
Cr
Ni
C
bal
26
35
0.53
Fe
Cr
Ni
W
Zr
C
bal
26
35
5
0.6
0.50
Fe
Cr
Ni
C
bal
17
35
0.55
Fe
Cr
Ni
C
bal
18
39
0.55
76
Ni bal
Cr 50
Cb 1.5
Fe 0.5
Mn 0.2
Si 0.3
Ni 0.08
C 0.10 max
Density,
Melting Point,
Ib/cu in. Specific Gravity
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.280
0.279
0.279
0.280
7.67
7.75
7.72
7.72
7.75
2650
2550
2500
2550
2550
0.284
7.86
2450
0.11
0.290
0.287
1 = 68 to 212F
8.03
7.96
2450
2397
10 = at 212F
9.221
0.11
0.12
2500
2450
9.921
7.83
7.96
0.12
0.283
21
9.421
0.12
0.286
9.9
0.12
2600
2450
8.91
7.72
7.87
0.12
0.279
0.284
9.621
0.14
9.221
9.221
0.1137
0.11
108 10
480
28
98 10
480
27
98 10
27
98 10
540
29
98 10
564
29
HL Cast Heat
Resistant
Alloy
27
HN Cast Heat
Resistant
Alloy
90 10
614
27
HP Cast Heat
Resistant
Alloy
HE Cast Heat
Resistant
Alloy
HF Cast Heat
Resistant
Alloy
HH Cast Heat
Resistant
Alloy
HI Cast Heat
Resistant
Alloy
HK Cast Heat
Resistant
Alloy
HP50-WZ
Cast Heat
Resistant
Alloy
612 37
27
8.521
91 10
601
27
107 10
631
27
HU Cast Heat
Resistant
Alloy
IN-657
Cast Heat
Resistant
Alloy
0.1101
25
90 10
8.821
0.11
510
9.221
120 30
5.91
21 = 70 to 1000F
88 35
31 = at 1500F
589 35
30
35 = at 75F
HT Cast Heat
Resistant
Alloy
37 = at 70F
77
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
Fe
Cr
Ni
C
bal
12
60
0.55
Fe
Cr
Ni
C
bal
17
66
0.55
Fe bal
Cr 24
Ni 24
Cb 1.6
Mn 1.0 max
Si 1.0 max
C 0.30
As Cast
36
68
185
Aged at 1800F
52
84
205
As Cast
36
65
176
Aged at 1800F
44
73
185
As Cast
35
75
25
Sheet Annealed
37
53
26
80
84
160
90
105
14
225
Recrystallized at 2000F
56
78
32
RB82
Annealed
22
38
25
As Rolled
60
62
As Rolled
75
100
30
250
Recrystallized
50
70
45
190
As Rolled
90
120
30
290
Recrystallized
60
80
40
200
80
100
85
120
17
285
Sheet Annealed
50
40
45
Cold Rolled
100
110
123
360
400
270
Wire Wrought
310
Recrystallized
190
15
450d
Cb 99.6 min
Columbium-Tantalum-Tungsten Alloy
Cb bal
Ta 28
W 11
Zr 0.85
Columbium-Vanadium Alloy
Cb bal
V 5
Cb 98.5 min
Zr 1
Mo 99.9 plus
Mo bal
Ti 0.5
W 97.5
Ni + Cu2.4
W bal
Ni 7.5
Cu 2.5
Ta 99.8 plus
W 99.95 min
W 75
Re 25
78
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.294
0.286
8.14
2350
8.14
2350
7.92
2490
0.11
0.11
0.1083
7.821
7.821
7.21
91 10
673
25
25
HX Cast Heat
Resistant
Alloy
IN-519
Cast Heat
Resistant
Alloy
98 10
582'5
23
HW Cast Heat
Resistant
Alloy
8.57
0.390
10.8
4475
4695
0.306
8.47
4310
0.065
0.311
8.6
4350
0.065
0.369
0.369
10.20
4730
10.22
4730
0.061
0.061
4.38
21
105
15
20
377 3
131
15.8
ColumbiumVanadium Alloy
364 3
12
ColumbiumZirconium
Alloy
900 3
31.1
46
17.4
Molybdenum
816 3
31.3
46
17.4
4.1530
2.71
3.061
306
5.4
Columbium
ColumbiumTantalumTungsten
Alloy
0.5% TitaniumMolybdenum
Alloy
0.67
18.5
52
TungstenNickel-Copper
Alloy
0.61
17.0
3.77
500 8
45
TungstenNickel-Copper
Alloy
0.600
16.65
3.61
377 3
74.6
27
10
Tantalum
33.2
50
19.6
Tungsten
57
TungstenRhenium
Alloy
5425
0.034
0.697
19.30
6100
0.033
2.4
0.71
19.65
5612
1 = 68 to 212F
3 = at 68F
7 = 100 to 1200F
8 = at 32F
168
10 = at 212F
21 = 70 to 1000F
30 = 30 at 1500F
35 = at 75F
79
Material
Form and
Condition
Nominal Composition
%
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
W 50
Re 50
Uranium
CastingsASTM B 419
Melting StockASTM B 420
U 99.8 plus
Zr 99.8 plus
210
240
600d
Recrystallized
123
150
18
350d
Cast
28
56
Annealed
16
36
31
77
Annealed
50
64
23
RB89
30
32
58
Zr bal
Hf 3
Cr-Fe 0.2 max
Au 99.995 min
Annealed
Nil
19
45
25
Au 75
Ni 18.5
Zn 5.25
Cu 1.25
Annealed
93
115
25
211
Hard
178
323
Au 69
Ag 25
Pt 6
Annealed
16.3
39
33
74
Hard
70
132
18.2
54
27
Annealed
7.9
Ag 99.90 min
Hard
38
43
90
26
65
Sterling Silver
Ag 92.5
Cu bal
Annealed
20
41
Hard
50
64
125
Coin Silver
Ag 90
Cu bal
Annealed
23
42
26
70
Hard
53
65
125
Ag 50
Cd 18
Zn 16.5
Cu 15.5
Annealed
67
29
120
Cold Rolled
89
11
160
Ag 60
Cu 25
Zn 15
Annealed
45
58
38
110
Cold Drawn
75
89
160
Platinum
Pt (Commercial)
Annealed
18
38
39
Palladium
Pd (Commercial)
Annealed
25
27
38
Iridium
Ir 100
Annealed
34
155
220
Rhodium
Rh 100
Annealed
100
120
Platinum-Iridium
Pt 90
Ir 10
Annealed
55
130
Hard
90
185
80
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
13.76
4622
257
2070
116
52.3
24
TungstenRhenium
Alloy
Uranium
0.689
19.07
7.7
Zirconium
0.245
6.5
0.237
6.55
3380
0.118
2.9
246
11
3.2
145
Zirconium
Hafnium
Alloy
0.53
19.32
14.61
1945
0.031
7.9
2060
14.1
10.8
1886
210.3
16.6
0.58
16.0
95
13.0
0.379
10.49
1761
0.056
9.44
10.5
10.5
1175
0.342
0.344
0.775
9.49
9.52
21.45
12
2900
9.6
3.9
12.08
12.13
42
1325
50
13
R-T Silver
Brazing
Alloy
0.031
2826
0.058
22.65
4429
0.031
0.059
2510
2490
12.02
4.9
6.5
3.78 1
Coin Silver
EASY FLO*
Silver
Brazing
Alloy
64
24.8
Platinum
65
16.8
Palladium
406 1
32
75
Iridium
27
46
Rhodium
PlatinumIridium
494
610
13
3560
0.778
21.53
3240
150
8 = at 32F
Sterling Silver
12.41
4.6
485
0.447
1 = 68 to 212F
Fine Silver
0.813
W.E. No. 1
0.434
3256
10.5
Gold
9 = at 64F
12 = 32 to 1652F
13 = at 63F
81
Material
Nominal Composition
%
Form and
Condition
Yield
Strength
(0.2% offset),
1000 psi
Tensile
Strength,
1000 psi
Elongation
in 2 in.,
%
Hardness,
Brinell or
Rockwell
35
90
Pt 90
Rh 10
Platinum-Ruthenium
Pt 90
Ru 10
Palladium-Ruthenium
Pd 95.5
Ru 4.5
Palladium-Silver
Ruthenium
82
Pd 60
Ag 40
Pd 35
Pt 10
Au 10
Ag 30
Cu 15
Ru 100
Annealed
45
90
165
Annealed
83
31
190
Hard
150
280
Annealed
51
152
Hard
286
Annealed
55
180
Hard
100
260
Annealed
61
96
24
180
Heat Treated
125
146
10
280
Annealed
78
250 to 450
Density,
Ib/cu in. Specific Gravity
Melting Point,
F
Specific Heat
(32 to 212F),
Btu / Ib / F
Thermal
Conductivity
(32 to 212F),
Btu / sq ft
/hr / F / in.
Electrical
Resistivity,
(68F) ohms
/cir mil ft
Tensile
Modulus
of Elasticity,
in 106 psi
Torsional
Modulus
of Elasticity,
106 psi
Material
0.720
0.436
19.97
115
3000
258
2900
145
20.0
19.94
12.07
2440
252
0.430
11.9
1985
215
4190
41 8
60
0.450
12.45
PlatinumRhodium
PlatinumRuthenium
PalladiumRuthenium
Palladium
Silver
Palladium
Alloy
No. 934
Ruthenium
8 = at 32F
83
TRADEMARKED PRODUCTS
Trademarks
Product of
ALCHROME ............................................................................................................. AMAX Inc.
ALOYCO .................................................................................................................Aloyco,Inc.
AL-6X ................................................................................. Allegheny Ludlum Industries, Inc.
AM 350 .............................................................................. Allegheny Ludlum Industries, Inc.
AM 355 .............................................................................. Allegheny Ludlum Industries, Inc.
CARPENTER 20Cb-3.........................................................Carpenter Technology Corporation
CHLORIMET .................................................................................. The Duriron Company, Inc.
CUSTOM 455 ....................................................................Carpenter Technology Corporation
DISCALOY.........................................................................Westinghouse Electric Corporation
DURANICKEL ....................................................................................Inco family of companies
DURICHLOR .................................................................................. The Duriron Company, Inc.
DURIMET ...................................................................................... The Duriron Company, Inc.
DURIRON ...................................................................................... The Duriron Company, Inc.
EASY-FLOW .............................................................................................. Handy and Harman
E-BRITE .............................................................................. Allegheny Ludlum Industries, Inc.
ELINVAR ......................................................................................................... Metalimphy,Inc.
EVANOHM ............................................................................................................... AMAX Inc.
FERRALIUM .................................................................................... Bonar Langley Alloys Ltd.
HASTELLOY ................................................................................................Cabot Corporation
HAYNES .....................................................................................................Cabot Corporation
ILLIUM ......................................................................... Stainless Foundry & Engineering, Inc.
INCOLOY ..........................................................................................Inco family of companies
INCONEL ..........................................................................................Inco family of companies
INVAR............................................................................................................. Metalimphy,Inc.
ISO-ELASTIC ................................................................................. John Chatillon & Sons, Inc.
JESSOP .............................................................................................. Jessop Steel Company
KANTHAL.......................................................................................... The Kanthal Corporation
KARMA ............................................................................................... Driver-Harris Company
KOVAR .............................................................................Carpenter Technology Corporation
MAR-M......................................................................................... Martin Marietta Corporation
MONEL .............................................................................................Inco family of companies
MULTIMET...................................................................................................Cabot Corporation
NIKROTHAL ...................................................................................... The Kanthal Corporation
NIMONIC ...........................................................................................Inco family of companies
NITRONIC................................................................................................................ Armco Inc.
NI-SPAN-C.........................................................................................Inco family of companies
NITRALLOY ............................................................................. Joseph T. Ryerson & Son, Inc.
PERMANICKEL ..................................................................................Inco family of companies
RA 333 .......................................................................................................Rolled Alloys, Inc.
REN 41.........................................................................................................Teledyne Allvac
RODAR ................................................................................................................... AMAX Inc.
SANDUSKY ..............................................................Sandusky Foundry & Machine Company
SEA-CURE ........................................................................................................ Colt Industries
STAINLESS W ......................................................................United States Steel Corporation
THERLO.............................................................................................. Driver-Harris Company
TINEL ................................................................................................... Raychem Corporation
UDIMET ........................................................................................ Special Metals Corporation
WAUKESHA METAL ....................................................................Waukesha Foundry Company
YORCORON ..............................................................................IMI Yorkshire Imperial Limited
ZILLOY .................................................................................. The New Jersey Zinc Company
15-5 PH ................................................................................................................. Armco Inc.
17-4 PH ................................................................................................................. Armco Inc.
17-7 PH ................................................................................................................. Armco Inc.
18-9 LW ................................................................................................................. Armco Inc.
PH 15-7 Mo ........................................................................................................... Armco Inc.
PH 14-8 Mo ........................................................................................................... Armco Inc.
PH 13-8 Mo ........................................................................................................... Armco Inc.
200 Alloy.......................................................................................... Driver-Harris Company
317LM ...............................................................................Eastern Stainless Steel Company
84
85