JIS G 3106 - New

JAPANESE
INDUSTRIAL
STANDARD
Nur zur Information ! Kein nderungsdienst

For Information only ! Without amendment service !
TAKRAF GmbH
Translated and Published by

Japanese Standards Association
(6
JIS G 3106
2004
(JISF)
Rolled steels for welded structure
les 77.140.01
Reference number : JIS G 3106 : 2004 (E)
PROTECTED BY COPYRIGHT
20S
G 3106: 2004
Foreword
This translation has been made based on the original Japanese Industrial
Standard revised by the Minister of Economy, Trade and Industry through
deliberations at the Japanese Industrial Standards Committee, as the
result of proposal for revision of Japanese Industrial Standard submitted
by The Japan Iron and Steel Federation (JISF) with the draft being attached, based on the provision of Article 12 Clause 1 of the Industrial
Standardization Law applicable to the case of revision by the provision
of Article 14. Consequently JIS G 3106 : 1999 is replaced with this Standard.
Attention is drawn to the possibility that some parts of this Standard
may conflict with a patent right, application for a patent after opening
to the public, utility model right or application for registration of utility
model after opening to the public which have technical properties. The
relevant Minister and the Japanese Industrial Standards Committee
are not responsible for identifying the patent right, application for a
patent after opening to the public, utility model right or application for
registration of utility model after opening to the public which have the
said technical properties.
Date of Establishment: 1952-11-25
Date of Revision: 20040320
Date of Public Notice in Official Gazette: 200403 22
Investigated by: Japanese Industrial Standards Committee
Standards Board
Technical Committee on Iron and Steel
JIS G 3106 : 2004, First English edition published in 2004-06
Transla ted and published by: Japa nese Standards Association

4-1-24, Akasaka, Minato-ku, Tokyo, 107-8440 JAPAN
In the event of any doubts arising as to the contents,
the original JIS is to be the final authority.
@ J5A 2004
All r igh ts reserved. Unless otherwise specified, no part of this publication may be reproduced or
utilized in any form or by any means, electronic or mechanical, incl uding photocopying and
microfilm, without permission in writing from the publisher.
Printed in Japa n
G 3106: 2004
Contents
Page
Introduction ......... _................................................. ......................................................
Scope ....................................................................................................................
Normative references ........................................................................................
Grade and designation .....................................................................................
Chemical composition .......................................................................................
Carbon equivalent or chemical composition on sensitivity of welding

crack.....................................................................................................................

crack for SM570 ...............................................................................................

crack for thermomechanically controlled steel plate ................................
Mechanical property .........................................................................................
6.1
Yield point or proof stress, tensile strength and elongation ...................
6.2
Charpy absorption energy ..............................................................................
Shape, dimension, mass and the tolerance thereon....................................
Appearance .........................................................................................................
Heat treatment and symbol.............................................................................
9.1
Heat treatment ........................................ ........................................................
9.2
Symbol of heat treatment ..............................................................................
10
Tests.....................................................................................................................
10.1
Chemical analysis............................................................................................
10.2
Mechanical test ................................................................................................
5.1
5.2
6
11
Inspection............................................................................................................ 10
11.1
Inspection ........... ............................................................................................... 10
11.2
Reinspection......................................................................................................
10
12
Marking ........................... ..... .... .... .......................................................................
10
13
Report .................................................................................................................. 11
(i)
G 3106: 2004
Annex 1 (normative)
Sampling position of the test piece ................................
13
Annex 2 (normative)
Structural steels-Plates, wide flats , bars, section

and profiles .........................................................................
15
Annex A (normative) Position and orientation of test pieces .......................... 25

Annex B (normative) Energy values for impact test pieces of reduced
size ........................................................................................
Annex C (informative)
26
List of International Standards on tolerances for

steel products ...................................................................
27
Annex D (informative)
Notes on weldability .......................................................
28
Annex 3 (informative)
Comparison table between JIS and corresponding

International Standard ..................................................
29
(ii)
JAPANESE INDUSTRIAL STANDARD
<6 JIS G 3106: 2004
Rolled steels for welded structure
Introduction This Standard is the Japanese Industrial Standard specified by making

revisions on the text of the original Japanese Industrial Standard revised in 1999
such as the expansion of the scope of flats, and by specifying ISO 630 Structural
steels-Plates, wide flats, bars, sections and profiles published in 1995 as annex 2
without modifying the technical contents.
1 Scope This Standard specifies the hot rolled steels (hereafter referred to as "steel
products") to be used for bridges, ships, rolling stocks, petroleum storage tanks, containers and other constructions that have superior weldability.
Remarks:
In using this Standard, either its text or annex 2 shall be applied.
The International Standard corresponding to this Standard is as

follows.
In addition, symbols which denote the degree of correspondence in
the contents between the relevant International Standard and JIS
are IDT (identical), MOD (modified), and NEQ (not equivalent) according to ISOIlEC Guide 2l.
ISO 630 : 1995 Structural steels-Plates, wide {lats, bars, sections and
profiles (MOD)
2 Normative references The standards listed in attached table 1 contain provisions which, through reference in this Standard, constitute provisions of this Standard. The most recent editions of the standards (including amendments) indicated
below shall be applied.
3 Grade and designation The steel products shall be classified into 11 grades,
and their designation shall be as given in table 1.
G 3106: 2004
Table 1
Designation of grade
Applicable thickness
mm
Steel plate, steel strip in coil, section and flat
200 or under
SM400C
Steel plate, steel strip in coil and section

Flat
100 or under
50 or under
SM490A
200 or under
SM490C

Flat
100 or under
50 or under
SM490YA
100 or under
SM520B
100 or under
SM520C
Steel plate. steel strip in coil and section

Flat
100 or under
40 or under
100 or under
40 or under
SM400A
SM400B
SM490B
SM490YB
SM570
Flat
Remarks 1 The steel plate which is until 150 mm in thickness of SM520B,

SM520C and SM570 may be produced in accordance with agreement between the purchaser and supplier.
2 Flats up to 75 mm thick for SM400C and SM490C and up to
50 mm thick for SM520C may be produced in accordance with the
agreement between the purchaser and supplier.
4 Chemical composition The steel products shall be tested in accordance with

10.1 and the ladle analysis value shall be in accordance with table 2.
3
G 3106: 2004
Table 2
Chemical composition
Unit: %
Symbol of
grade
SM400A
SM400B
S;
50 mm or under in thickness
0.23 max.
Over 50 mm up to and incl. 200 mm in thickness
0.25 max.
0.20 max.
Over 50 mm up to and incl. 200
mID
in thickness
Mn
2.5 xC 0.035 0.035

min.(I) max. max.
0.35
max.
0.60 to
1.40
0.035
max.
0.035
max.
0.22 max.
SM400C
0.18 max.
0.35
max.
1.40
max.
0.035
max.
0.035
max.
SM490A
0.20 max.
0.55
max.
1.60
max.
0.035
max.
0.035
max.
0.55
max.
1.60
max.
0.035
max.
0.035
max.
Over 50 mm up to and incl. 200 rom in thickness
0.22 max.
50 rom or under in thickness
0.18 max.
Over 50 mm up to and incl. 200 mm in thickness
0.20 max.
SM490C
0.18 max.
0.55
max.
1.60
max.
0.035
max.
0.035
max.
SM490YA
0.20 max.
0.55
max.
1.60
max.
0.035
max.
0.035
max.
0.20 max.
0.55
1.60
0.035 0.035
max.
max.
max.
0.55
1.60
0.035 0.035
max.
max.
max.
SM490B
SM490YB
SM520B
SM520C
SM570
0.18 max.
max.
max.
Note (1) The value of carbon shall be applied the values of the actual ladle analysis.
Remarks 1 Alloying elements other than those given in table 2 may be added as necessary.
2 The chemical composition of the steel plate of which thickness is over 100 mm up
to and including 150 mm in thickness of SM520B, SM520C and SM570 shall be
in accordance with the agreement between the purchaser and the supplier.
5 Carbon equivalent or chemical composition on sensitivity of welding crack

5.1 Carbon equivalent or chemical composition on sensitivity of welding
crack for SM570 The carbon equivalent or chemical composition on sensitivity of
welding crack for SM570 shall be as follows:
Further, the carbon equivalent shall apply to quench-hardened and tempered steel
products.
a)
The carbon equivalent shall be calculated from the following formula by using
the ladle analysis values of 10.1 and shall be in accordance with table 3.
Carbon equivalent (%) =
C+ Mn + Si + Ni + Cr + Mo +~ ............................... (1)
6
24 40
5
4
14
4
G 3106: 2004
Table 3
Carbon equivalent
Thickness of steel product mm
50 max.
Over 50 up to and incl. 100
Over 100
Carbon equivalent %
0.44 max.
0.47 max.
As agreed upon between

the purchaser and supplier.
b)
Chemical composition on sensitivity of welding crack may be applied instead of

carbon equivalent subject to the agreement between the purchaser and supplier.
In this case, the chemical composition on sensitivity of welding crack shall be
calculated from the following formula by using the ladle analysis value of 10.1
and shall be in accordance with table 4.
Chemical composition on sensitivity of welding crack (%) =
Si
Mn Cu Ni Cr Mo
V
C+-+--+--+-+-+--+-+5B
............... (2)
30
20
20
60
20
15
10
Table 4
Chemical composition on sensitivity of welding crack
Thickness of steel product mm
50 max.
Over 100
Chemical composition on sensitivity of welding %
0.28 max.
0.30 max.
As agreed upon between

the purchaser and supplier.
5.2 Carbon equivalent or chemical composition on sensitivity of welding

crack for thermomechanically controlled steel plate The carbon equivalent
of the steel plate which is thermomechanically controlled processed under the agreement
between the purchaser and supplier and the chemical composition on sensitivity of
welding crack applied as substitute for the carbon equivalent under the agreement
between the purchaser and supplier shall be as follows:
a)
The carbon equivalent The carbon equivalent shall be calculated from the
formula (1) of 5.1 by using the ladle analysis value of 10.1 and shall be in accordance with table 5.
Table 5
The carbon equivalent

Unit %
Applicable
thickness
Remarks:
b)
SM490A
SM490B
SM490C
SM490YA
SM490YB
SM520B
SM520C
50 mm or under
0.38 max.
0040 max.
Over 50 mm up to and incl. lOOmm
0040 max.
0.42 max.
The carbon equivalent of the steel plate over 100 mm in applied thickness
shall be in accordance with the agreement between the purchaser and the
supplier.
Weld cracking susceptibility of material Weld cracking susceptibility of

material shall be calculated from the formula (2) of 5.1 by using the ladle analysis
value of 10.1 and shall be in accordance with table 6.
5
G 3106: 2004
Table 6 The weld cracking susceptibility of material

Unit %
Applicable
thickness
SM490A
SM490B
SM490C
SM490YA
SM490YB
SM520B
SM520C
50 mm or under
0.24 max.
0.26 max.
Over 50 mm up to and inel. lOOmm
0.26 max.
0.27 max.
Remarks: The weld cracking susceptibility of material of the steel plate over 100 mm
in applied thickness shall be in accordance with the agreement between the
purchaser and the supplier.
6 Mechanical property
6.1 Yield point or proof stress, tensile strength and elongation The steel
products shall be tested in accordance with 10.2 and the yield point or proof stress,
tensile strength and elongation shall be in accordance with table 7.
Table 7 Yield point or proof stress tensile strength and elongation
Q'"
CO
Yield point or proof str ess

N/mm 2
Tensile strength
Thickness of steel product(2) mm
Thickness of steel
product e) mm
Designation
of grade
16 or
under
~"
Over 16
up to and
inel. 40
Over 40
up to and
incl. 75
Over 75
up to and
incl. 100
Over 100
up to and
inel. 160
Over 160
up to and
100 or
under
Over 100
up to and
inel. 200
incl. 200
245
235
215
215
205
195
400 to
400 to
SM400B
min.
min.
min.
min.
min.
min.
610
510
SM490A
325
315
295
295
285
275
490 to
490 to
t;j
SM490B
min.
min.
min.
min.
min.
min.
610
610
"
SM490C
"
SM490YA
SM490YB
365
355
335
325
490 to
min.
min.
min.
min.
SM520B
SM520C
365
355
335
325
min.
min.
min.
min.
460
450
min.
430
420
min.
min.
SM570
min.
Note (2) For sections, the term
~t hickness
of steel
product~
520 to
570 to
720
mm
5 or under
Over 40
No.5
No.lA
No.lA
NO.4
23 min.
18
22
24
No.lA
No.IA
No.4
22
17
21
23
5 or under
Over 40
No.5
No.IA
No.IA
NO.4
19
15
19
21
5 or under
Over 40
No.5
No.lA
No.lA
No.4
19
15
19
21
16 or under
Over 16
Over 20
No.5
No.5
No.4
19
26
20
640
Test piece
NO.5
610
Thickness of steel
product(2)
5 or under
Over 40
a\
N/mm 2
SM400A
SM400C
Elongation
means the thickness at the position where the test piece is taken as shown in annex 1 figure 1.
Remarks 1 For the elongation of No.4 test piece of the steel products over 100 mm in thickness, 1 % is subtracted from the value of elongation given in
table 7 per each increase of 25 mm in thickness or its fraction. However, the limit to be subtracted shall be 3 %.
2 The yield point or proof stress, tensile strength and elongation oCthe steel plate of over 100 mm up to and including 150 mm in thickness of
SM520B, SM520C and SM570 shall be in accordance with the agreement between the purchaser and the supplier.
...g
G3106: 2004
6.2 Charpy absorption energy The steel products over 12 mm in thickness shall
be tested in accordance with 10.2 and the Charpy absorption energy shall be as given
in table 8. The Charpy absorption energy in this case shall be expressed by the average
of measured values of three test pieces and shall be judged by 9.6 of JIS G 0404.
Table 8
Cbarpy absorption energy
Test temperature
'C
Charpy absorption energy

J
Test piece
SM400B
27 min.
V-notch test piece

in rolling direction
SM400C
47 min.
SM490B
27 min.
SM490C
47 min.
SM490YB
27 min.
SM520B
27 min.
SM520C
47 min.
SM57Q
-5
47 min.
7 Shape, dimension, mass and the tolerance thereon The shape, dimension,
and mass of the steel products and the tolerance shall be in accordance with the
following standards;
JIS G 3192, JIS G 3193, JIS G 3194

In this case, the width tolerances for the steel plate and cut-edged coil as well as
the length tolerances for the steel plate shall be in accordance with the tolerance A
in JIS G 3193 unless particularly specified.
8 Appearance The appearance of the steel products shall be in accordance with
clause 9 in JIS G 3192, clause 6 in JIS G 3193 or clause 8 in JIS G 3194.
Further, the repair by welding of the steel plate of SM570 shall be previously
agreed between the purchaser and the supplier.
9 Heat treatment and symbol
9.1 Heat treatment The steel products may be subjected to normalizing, quenchhardening and tempering, or tempering, as necessary. For all designations of grade,
heat treatment such as thermomechanical control process may be applied under the
agreement between the purchaser and the supplier.
9.2 Symbol of heat treatment When the steel products have been subjected to
heat treatment, the symbol of heat treatment shall be as follows:
Further, in appending the symbol of heat treatment according to the following
manner, the symbol shall additionally be written to the end of the symbol of grade
given in table 1.
8
G 3106: 2004
a)
In the case where normalizing is applied for the steel products by agreement
between the purchaser and manufacturer: N
b)
In the case where tempering is applied for the steel products by agreement between the purchaser and manufacturer: T
c)
In the case where quench-hardening and tempering is applied for the steel
products; Q
d)
In the case where thermomechanical control is applied for the steel products: TMC
e)
In the case where appropriate heat treatment is applied for the steel products: By
agreement
Example of symbols: SM 490 CN, SM 570 TMC
10 Tests
10.1
Chemical analysis
Chemical analysis shall be as follows.
10.1.1 Generals requirements for chemical tests The chemical composition of

the steel products shall be determined by ladle analysis, and general requirements
for chemical analysis and the sampling method of specimen for analysis shall be as
specified in clause 8 in JIS G 0404.
10.1.2 Analytical method The method for chemical analysis shall be in accordance with anyone of the following standards:
JIS G 1211, JIS G 1212, JIS G 1213, JIS G 1214, JIS G 1215, JIS G 1216,
JIS G 1217, JIS G 1218, JIS G 1219, JIS G 1221, JIS G 1227, JIS G 1238,
JIS G 1253, JIS G 1256, JIS G 1257, JIS G 1258
10.2 Mechanical test
10.2.1 Test in general General requirements for mechanical testing shall be as
specified in clause 9 of JIS G 0404. In this respect, the sampling method of specimen shall conform to class A, and number of test pieces and sampling positions shall
be as follows:
a)
Number of tensile test pieces

follows:
The number of tensile test pieces shall be as
1)
Steel plate and flat A test lot shall consist of the steel products, from
one heat where the maximum thickness is within twice the minimum thickness, and one tensile test piece shall be taken therefrom. When the mass
of one test lot, however, exceeds 50 t, two tensile test pieces shall be taken.
With this respect, if a single steel plate exceeds 50 t, one test piece shall
be taken from the said plate.
2)
Steel strip in coil and cut-to-Iengths A test lot shall consist of the steel
products, from one heat, rolled to the same thickness, and one tensile test
piece shall be taken therefrom. When the mass of one test lot, however ,
exceeds 50 t , two tensile test pieces shall be taken.
9
G 3106: 2004
b)
3)
Steel section A test lot shall consist of the steel products, from one heat,
rolled to the same sectional profile group where the maximum thickness is
within twice the minimum thickness, and one tensile test piece shall be
taken therefrom. When the mass of ODe test lot, however , exceeds 50 t,
two tensile test pieces shall be taken.
4)
Number of test pieces for heat treated steel products The number
of test pieces for the heat treated steel products, from the same heat, rolled
to the same sectional profile group, subjected to heat treatment under the
same treatment conditions, shall be determined in accordance with 1), 2)
or 3) in this item.
Number of impact test pieces For the steel products that have not been heat
treated, one specimen shall be taken from the maximum thickness product of a
test lot, from one heat, rolled to the same sectional profile group. For the heat
treated steel products, one specimen shall be taken from the maximum thickness
product of a test lot, from one heat, rolled to the same sectional profile group,
subjected to heat treatment under the same treatment conditions. Three test pieces
shall be taken from each specimen parallel to the rolling direction.
c)
Sampling position of the tensile test piece Sampling position of the tensile test piece shall be in accordance with JIS G 0416. However, annex 1 may
be applied. Test pieces of steel strip in coil shall be sampled from the position
adjacent to the material section to be evaluated.
d)
Sampling position of the impact test piece Sampling position of the impact test piece shall be in accordance with JIS G 0416. For the thickness of
40 mm or less, annex A figure A.11 a) of JIS G 0416 shall apply. and for the
thickness of over 40 mm , annex A figure A.11 b ) of JIS G 0416 shall apply.
Annex 1 may be applied.
Test pieces of steel strip in coil shall be sampled from the position adjacent
to the material section to be evaluated.
10.2.2 Test piece The tensile test piece and impact test piece shall be as follows:
a)
No. lA, No.4 or No.5 test piece specified in JIS Z 2201
b)
The V-notch test piece specified in JIS Z 2202. In this case, the longitudinal
direction of the notch of the test piece shall be perpendicular to the rolled surface.
10.2.3 Test method The methods for tensile test and impact test shall be as follows:
a)
JIS Z 2241
b)
JIS Z 2242
10.2.4 Tensile test in the case where tensile test piece having specified dimensions can not be taken In the case where it is infeasible to secure the test
piece having specified dimensions, matters on execution of tensile testing, test result values or the like shall be agreed upon between the purchaser and supplier.
10
G 3106: 2004
10.2.5 Omission of tensile test and impact test of steel coil The tensile test
and impact test of the steel coil may be omitted when approved by the purchaser.
11 Inspection
11.1 Inspection
The inspection shall be carried out as follows:
a)
General requirements for inspection shall be as specified in JIS G 0404.
b)
The chemical composition shall conform to the requirements specified in clause 4.
c)
The carbon equivalent or chemical composition on sensitivity of welding crack

shall conform to the requirements specified in clause 5.
d)
The mechanical properties shall conform to the requirements specified in clause 6.
e)
The shape, dimensions and mass shall conform to the requirements specified in
clause 7.
The appearance shall conform to the requirements specified in clause 8.
g)
The purchaser may specify the ultrasonic testing specified in JIS G 0801 or
JIS G 0901 or the like in addition to the inspection items given in a) to O. In
this case, the test method, acceptance criteria, etc. shall be agreed previously
between the purchaser and manufacturer.
11.2 Reinspection
The reinspection shall be as follows:
a)
The steel products which have not passed the tensile test may be retested in
accordance with 9.8 in JIS G 0404 and then whether it is accepted or not may
be determined.
b)
The steel products which have failed in the impact test specified in 9.6 of JIS
G 0404 may be retested in accordance with 9.8 of JIS G 004 and determined to
be acceptable or not.
c)
The steel products which have not passed the mechanical test, .may be again
subjected to the mechanical test after heat treatment or reheat treatment. Then,
whether it is accepted or not may be determined.
12 Marking The steel products which have passed the inspection shall be marked
on each piece or each bundle with the following items by a suitable method. However, a part of the items may be omitted subject to the agreement between the purchaser and supplier.
a)
Symbol of grade (including the symbol which stands for symbol of heat treatment specified in 9.2)
b)
Heat number or inspection number
c)
Dimensions
d)
Quantity or mass of each bundle (for steel plate and coil)
e)
Manufacturer's name or identifying brand
11
G 3106: 2004
13 Report The test report shall be in accordance with clause 13 in JIS G 0404.
In case required, the manufacturer shall submit the symbol 2.3 or 3.1.B specified in
table 1 of JIS G 0415 to the purchaser.
Where the provision of remarks 1 of table 2 is applied, the content of alloying
elements added shall be noted in the test report.
12
G 3106: 2004
Attached Table 1
Normative references
JIB G 0404 Steel and steel products-General technical delivery requirements

JIS G 0415 Steel and steel products-Inspection documents
JIS G 0416 Steel and steel products-Location and preparation of samples and
test pieces for mechanical testing
JIS G 0801 Ultrasonic examination of steel plates for pressure vessels
JIS G 0901 Classification of structural rolled steel plate and wide flat for build
ing by ultrasonic test
JIS G 1211 Iron and steel-Methods for determination of carbon content

JIS G 1212 Iron and steel-Methods for determination of silicon content
JIS G 1213 Iron and steel-Methods for determination of manganese content
JIS G 1214 Iron and steel-Methods for determination of phosphorus content

JIS G 1215 Iron and steel-Methods for determination of sulfur content
JIB G 1216 Iron and steel-Methods for determination of nickel content
JIB G 1217 Methods for determination of chromium in iron and steel
JIB G 1218 Iron and steel-Methods for determination of molybdenum con-
tent
JIB G 1219 Iron and steel-Methods for determination of copper content
JIS G 1221 Iron and steel-Methods for determination of vanadium content
JIB G 1227 Iron and steel-Methods for determination of boron content
JIB G 1238 Steel and iron-Determination of chromium content-Potentiometric
or visual titration method

JIB G 1253 Iron and steel-Method for spark discharge atomic emission spec-
trometric analysis
JIB G 1256 Iron and steel-Method for X-ray fluorescence spectrometric analysis
JIB G 1257 Iron and steel-Methods for atomic absorption spectrometric analyszs
JIB G 1258 Iron and steel-Methods for inductively coupled plasma atomic
emission spectrometry
JIS G 3192 Dimensions, mass and permissible variations of hot rolled steel
sections
JIg G 3193 Dimensions, mass and permissible variations of hot rolled steel
plates, sheets and strip

JIg G 3194 Dimensions, mass and permissible variations of hot rolled flat steel
JIg Z 2201
Test pieces for tensile test for metallic materials
JIg Z 2202
Test pieces for impact test for metallic materials
JIg Z 2241
Method of tensile test for metallic materials
JIg Z 2242
Method of impact test for metallic materials
13
G 3106: 2004
Annex 1 (normative)
Sampling position of the test piece
1 Scope This annex specifies the sampling position of the test piece for tensile
tests and impact tests.
2 Applicable date
This annex applies until Dec. 31, 2008.
3 Sampling position of the test piece for tensile tests

the test piece for tensile tests shall be as follows:
Sampling position of
a)
Steel plate, steel strip in coil and flat The centre of the test piece shall be
at a quarter-width position from a side edge, and further in the case of No.4
test piece, it shall be at a quarter-thickness position from a surface as well as
a quarter-width position from a side edge. When it is infeasible to allow the
centre of the test piece to be at a quarter-width position from a side edge or at
a quarterthickness position from a surface, however, the sampling should be
performed as close to the aforementioned position as possible.
b)
Steel section The sampling position shall be as shown in annex 1 figure 1.

When it is infeasible to take a specimen as shown in annex 1 figure 1, the sam
pIing position should be as close to the aforementioned position as possible. In
the case of the steel H section from which a specimen is unable to take in the
same manner as shown in annex 1 figure 1, the sampling position for the I section
should be applied mutatis mutandis. For other steel sections, it should be agreed
between the purchaser and the supplier.
4 Sampling position of the test piece for impact tests

the test piece for impact tests shall as follows:
a)
Steel plate, steel strip in coil and flat The centre of the test piece shall be
at a quarterthickness position from a surface, and it shall be at a quarterwidth
position from a side edge as well as a quarter thickness position from a sur
face. When it is infeasible to allow the centre of the test piece to be at a quar
ter-thickness position from a surface and at a quarter-width position from a side
edge, however, the sampling should be performed as close to the aforementioned
position as possible.
b)
Steel section The centre of the test piece shall be at a quarter-thickness position from a surface (see annex 1 figure 1). When it is infeasible to allow the
centre of the test piece to be at a quarter-thickness position from a surface,
however, the sampling should be performed as close to the aforementioned position as possible. In the case of the steel H section from which a specimen is
unable to take in the same manner as shown in annex 1 figure 1, the sampling
position for the I section should be applied mutatis mutandis. For other steel
sections, it should be agreed between the purchaser and the supplier.
14
G 3106: 2004
I
ta l
B
Equal angle
Unequal angle
Angle with unequal leg

and unequal thickness
Channel
Bulb flat
I-section
Hsection
Annex 1 Figure 1 Sampling position of the test piece for

tensile tests and bend tests for steel section
15
G 3106: 2004
Annex 2 (normative)
Structural steels-Plates, wide flats, bars, section and profiles
Introduction This annex is the Japanese Industrial Standard prepared based on

ISO 630 Structural steels-Plates, wide flats, bars, sections and profiles published
in 1995 as the second edition without modifying its technical content.
In this annex, the portions underlined with dot line are the matters added in the
original International Standard.
Furthermore, the following annexes are contained in this annexes.
Annex A (normative)
Position and Orientation of test pieces
Annex B (normative)
Energy Values for impact test pieces of reduced size
List of International Standards on tolerances for steel

products
Notes on weldability
1 Scope This annex specifies qualities for the general purpose structural steels listed
in table 1 of the body. This annex applies to steel plates with thicknesses of 3 mm or
over, wide strip in coils with widths 600 mm or over, and more than 6 mm in thickness, wide flats, bars and hot-refold sections generally used in the as-delivered condition and normally intended for bolted, riveted or welded structures(l).
It does not include the following steels, certain of which are covered by other International Standards:
steels for boilers and pressure vessels (ISO 9328-2);
plates of drawing quality (ISO 3573 and ISO 3574);
heat-treated (quenched and tempered) structural steels;
bars for the reinforcement of concrete;
strip of width 600 mm or over and thickness not exceeding 6 mm (ISO 4955).
Note <I) For precautions to be taken when welding, the guide for the welding and
weldability of C-Mn and C-Mn micro-anoy steels published by Sub-commission IX-G of the International Welding Institute (document ISS/I IWI
843-87), together with the notes given in annex D should be referred to.
In particular, for the grade E 355, it should be noted that ISO 4950-2
specifies an equivalent grade with better welding characteristics.
2 Normative references The following standards contain provisions which, through
reference in this text, constitute provisions of this Standard. At the time of publication, the editions indicated were valid. All standards are subject to revision, and
parties to agreements based on this Standard are encouraged to investigate the
possibility of applying the most recent editions of the standards indicated below.
Members of lEe and ISO maintain registers of currently valid International Standards.
16
G 3106: 2004
ISO 148 : 1983
Steel- Charpy impact test (V-notch)
ISO 377-1 : 1989
Selection and preparation of sampLes and test pieces of wrought

steels- Part 1 : Samples and test pieces for mechanical test
This Standard has been revised as ISO 377 : 1997.

~~f~~~.~~.~~!l.. :.... ~~.9 . ~.~~~ .~~l!L~!!-.t!..~.~~~!.p.!.~4.rf.c:.~~=!:.c!.~l!:~~~~_. ~.'!:4. .P.r:!!:p.~!.f!:.~~.C?'!:
C!f.~_c!:~p?!!:~_.c!:1!:4..!~.~.~ .p.~!!:~~~. If!!...'!':!!:~~.l!:~~~l!:!..t!!:~~~~Q.. ~.f:'.. !~~.~~~~~.~ .~~.~:l?:
the said standard.
ISO 377-2 : 1989
Selection and preparation of samples and test pieces of wrought

steels-Part 2: Samples for the determination of the chemical
composition
This Standard has been revised as ISO 14284: 1996.

Information:
JIS G 0417 Steel and iron-Sampling and preparation of samples
. f~E.f~i..~~~.~~.~~.~~.~9.~.~{~.~~;;j.~~~l.~.~~P..9.~t.~Ti!.~)~.-.~~.~~.~~.~.~~..~H~
the said standard.
ISO 404 : 1992
Steel and steel products-General technical deli very requirements
ISO 25661 : 1984 Steel-Conversion of elongation values-Part 1 : Carbon and low

alloy steels
ISO 3573 : 1986
Hotrolled carbon steel sheet of commercial and drawing qualities
ISO 3574 : 1986
Cold-reduced carbon steel sheet of commercial and drawing
ISO 4948-1 : 1982 Steels-Classification-Part 1 : Classification of steels into unalloyed and alloy steels based on chemical composition
ISO 4950-2 : 1995 High yield strength flat steel products- Part 2 : Products supplied in the normalized or controlled rolled condition
ISO 4955 : 1994
Heat-resisting steels and alloys
ISO 4995 : 1993
Hot-rolled steel sheet of structural quality
ISO 6892 : 1984
Metallic materials- Tensile testing
ISO 6929 : 1987
Steel products-Definitions and classification
ISO 7788 : 1985
Steel-Surface finish of hot-rolled plates and wide flats-Delivery requirements
ISO 9328-2 : 1991 Steel plates and strips for pressure purposes- Technical delivery
conditions-Part 2 : Unalloyed and low-alloyed steels with speci-
fied room temperature and elevated temperature properties

ISO 10474: 1991
Steel and steel products-Inspection documents
~~K~~~?:~~~:r?: .: .... ~~~ ..g ..9~~.. ~~~!..r:!.T}:~.!!!.~~.?p!.~.c!:~.c:.~~=!~.~R.~~~.~'?~ .4.~~~.'!!:~!!:~.~.. ~.~
identical with the said standard.
3 Definitions Definitions of the terms "plate", "wide strip", "narrow strip" and
"wide flat" are given in ISO 6929.
17
G 3106: 2004
4 General requirements
4.1 Steelmaking process Unless otherwise agreed at the time of enquiry and
order, the steel marking process is left to the discretion of the manufacturer: except
for quality 0, the purchaser shall be informed of the process at the time of delivery.
4.2
Delivery condition
4.2.1 The products are generally delivered in the as-rolled condition. Other delivery conditions may form the subject of agreement when ordering.
4.2.2 Flat products of quality D may be ordered in two categories.
Quality Dl: It shall be delivered in the normalized or equivalent condition. The

mechanical properties given in annex 2 table 3 are applicable in both the delivered condition and after normalizing by separate heat treatment after delivery.
Quality D2: The mechanical properties given in annex 2 table 3 are only applicable in the delivery condition. The delivery condition is left to the discretion of
the manufacturer.
4.3
Surface appearance-Defects
4.3.1 Surface appearance The products shall have a smooth surface corresponding
to the rolling method used ; they shall have to defects that are prejudicial to their
subsequent processing or appropriate use.
4.3.2 Flat products The requirements of ISO 7788 shall apply.
4.3.3 Long products
a)
Minor defects may be removed by the manufacturer with grinding, provided that
the thickness stays within the lower tolerance limits specified in the appropriate International Standards (refer to list in annex C) or, in the absence of International Standards, is not reduced locally by more than 6 % in relation to its
nominal value.
b)
Unless otherwise specified in the order, imperfections that are greater in depth
than the limit specified in a) may be removed and deposited by welding subject
to the following conditions.
The reduction of thicknes s of the material, resulting from removal of imperfections prior to welding, shall not exceed 2 % of the nominal thickness at
the location of the imperfection.
All welding shall be performed by competent welders, using welding electrodes appropriate for the grade being repaired and following welding procedures approved by the purchaser.
5 Characteristics of grades and qualities

5.1 Chemical composition The steels specified are carbon steels in accordance
with ISO 4948-1.
18
G 3106: 2004
5.1.1 Ladle analysis The maximum values of the composition limits for ladle analy
sis are given in annex 2 table 1.
5.1.2 Product analysis Annex 2 table 2 gives the permitted deviations on analysis relative to the values for ladle analysis which are given in annex 2 table 1.
5.2 Mechanical properties The steels, in the delivery condition defined in 4.2:
shall comply with the mechanical properties specified in annex 2 table 3 when these
are determined on test pieces prepared in accordance with 6.4.
For products over 200 mm in thickness, the mechanical properties shall be the
subject of an agreement between the purchaser and the supplier.
6 Inspection and testing

6.1 General Rolled products covered by this annex may be the subject of an inspection and testing in accordance with the conditions specified in 8.3 of ISO 404 :
1992, relating to the mechanical properties and chemical analysis of the product.
However, grade E 185 is only supplied with non-specific inspection and testing. Verification of chemical composition on the product and of the impact energy values at
ambient temperature is only carried out by agreement at the time of enquiry and
order. If an inspection and testing has been specified in the order, it shall be carried out in accordance with 6 .2 to 6.5, unless otherwise agreed when ordering.
6.2
Test unit
Batching shall be by cast.
6.2.1 The test unit shall be 50 t or its fraction taken from one cast.
6.2.2 For each test unit and thickness range, as defined in annex 2 table 3, the series of the following tests shall be carried out.
one tensile test [or additional test, in accordance with 6.2.4 a) for products of
thickness 16 mm or under};
one set of three impact tests at 0 C for quality C and one set of three test at
-20 C for quality D:
If specified on the order,
one product analysis;
one set of three impact tests at +20 C for quality B.
6.2.3 The purchaser or his representative may witness the selection of the product
sample from which the samples shall be taken for the verification of properties (refer to ISO 404).
6.2.4 Unless otherwise agreed by the purchaser, the procedure shall be as follows.
a)
Tensile test One test sample shall be taken for each thickness range given in
annex 2 table 3, with a supplementary requirement that, for the thickness 16 rom
or under, the thickness of products shall be such that the maximum thickness
is not greater than twice the minimum thickness.
19
G 3106: 2004
Annex 2 Table 1
Grade
Quality
Chemical composition (ladle analysis)
Thickness
Method of
deoxidation (l)
mm
E 185
(Fe 310)
E 235
(Fe 360)
A
B
16 or under

40 or under
Over 40
C
D
E 275
(Fe 430)
(2)
Si
max.
max.
max.
max.
0.050
0.050
0.045
0.22
0.17
0.20
0.17
0.20
0.17
0.17
0.40
1.40
0.045
0.40
0.40
1.40
1.40
0.045
0.045
0.40
1.40
0.045
0.045
0.045
0.045
DAD
1.40
0.40
lAO
0.040
0.035
0.040
0.035
NE
0.24
0.21
Over 40
NE
NE
GF
0.22
0.40
0.20
0.20
0.40
0.20
NE
NE
GF
GF
Mn
max.
40 or under
30 or under
Over 30
30 or under
Over 30
Note
NE
NE
NE
GF
A
B
C
D
E 355
(Fe 510)
0.22
0.20
0.22
0.050
0.050
0.045
0.045
0.040
0.035
0.045
0.045
0.40
1.50
1.50
1.50
1.50
0.55
0.55
0.55
0.55
1.60
1.60
l.60
1.60
0.040
0.040
0.035
0.035
0.040
0.040
0.035
0.035
0.40
0.040
0.035
NE = Nonrimming
GF = These steels shall have a sufficiently high content of elements to produce a
grained structure (for example total AI 0.02 % or over).
Information: The letters shown in ( ) are the former designation of the steel products.
Annex 2 Table 2
Element
Permissible deviation for the product

analysis relative to the specified ladle
analysis [refer to 6.4.3 a)]
Specified limits %
Permissible deviation %
0.24 or under
+0.03
Si
0.55 or under
+0.05
Mn
p
1.60 or under
+0.10
0.050 or under
+0.010
0.050 or under
+0.010
fine~
Annex 2 Table 3 Mechanical properties

Grade
Yield point R.u min. N/mm 2
Quality
strength
N/mm 2
(.)
(.)
(.)
(.)
Energy
min.(~)
175
300 to 540
18
E 235
225
225
225
225
225
215
215
195
185
340 to 470
26
25
24
22
21
B (6)
235
235
235
235
235
215
(Fe 360)
340 to 470
26
215
215
215
215
215
215
215
2<5
195
195
195
185
185
185
340 to 470
26
22
27
24
22
340 to 470
26
24
22
21
21
21
+2.
26
25
25
25
24
340 to 470
-2.
21
21
21
21
2.
2.
2.
2.
18
18
18
18
17
17
+2.
21
21
2.
2.
18
18
17
BNE
C
0
~
tl
215
27
27
(')
E 275
(Fe 430)
()
Over 40 Over 63 Over 100 Over 150 Test ternunder up to Hnd up to and up to and up to and perature
incl. 63
incl. 100 incl. 150 incl. 200
'C
16 or
(85
. .....
(Fe 310)
Over 16
E ta5(e)
Thickness mm
Rm(3)
Over 40 Over 63 Over 80 Over 100 Over 150

under up to and up to and up to and up to and up to and up to and
incl. 80
incl . 100 incl. 150 incl. 200
incl. 40
inel. 63
16 or
Impact test
(V-notch), KV
Elongation A min. (Lo = 5.65.[So) %
Tensile
Thickness mm
Q'"
",0
C
0
275
275
275
275
255
255
255
255
255
255
255
255
245
245
245
245
235
235
235
235
225
225
225
225
215
2<5
215
215
41000540
22
41000540
22
410 to 540
22
22
410 to 540
17
17
27
27
-2.
27
27
(')
E 355
(Fe 510)
C
0
355
355
345
345
335
335
325
325
315
315
295
295
285
285
490 to 640
22
490 to 640
22
17
- 2.
(')
Remarks:
R ell = upper yield stress

Rm = tensile strength
A = percentage elongation after fracture %
Lo = gauge length on test piece

So = original cross-sectional area of gauge length
1 N/mm 2 = MPa
Notes (3) For the tensile strength of wide strip only the minimum value of the range is applicable.
(') For transverse test pieces (plates and wide flats of width 600 mm or over), these values are reduced by two points.
(5) Average of three tests; no individual result shall be less than 70 % of the specified minimum average value.
(6) This quality B is only delivered in thickness less than 25 mm .
(1) For over 100 mm in thi ckness, the lower limit of the range may be reduced 20 N/mm z.
27
....
'"
...g
21
G 3106: 2004
b)
Impact test One test sample shall be taken for each thickness range specified in annex 2 table 3. For flat products of quality D, if agreed at the time of
enquiry and order, a test sample shall be taken from each rolled product (parent plate or coil).
6.3
Position and orientation of test sample (refer to
..
~~g ~T?
and
~~.Q .. ~.~.~~)
6.3.1 Plates, wide steel strip in coil and wide flats of width 600 mm or over
The test samples shall be taken a quarter-width from a side edge.
a)
The longitudinal axes of tensile test piece shall be perpendicular to the direction of rolling.
b)
The longitudinal axes of impact test piece shall always be parallel to the direction of rolling.
6.3.2 Sections, girders and wide flats of width less than 600 mm The longi
tudinal axes of the test pieces shall be parallel to the direction of rolling. However,
if agreed, transverse test piece may be used for widths between 450 mm and 600 mm.
For sections, the test samples shall be taken such that the axis of the test piece
is 113 from the outer edge of the half flange (refer to Hand U sections, ISO 6929) or
of the flange (for other sections) or, for the small sections, as near as possible to this
position (refer to annex A figure A.l). For the tapered-flange, sections, the test samples
may be taken at the outer 1/4 position of the web.
6.3.3 Rounds, squares, flat bars, hexagons and other similar products The
longitudinal axes of test pieces shall be parallel to the direction of rolling.
For small sizes, the product itself shall be taken as a test piece.
In other cases, the test piece shall be taken the axis of the test piece so as to be
the following position.
for squares and flat bars, at 1/6 of the width (from the outer face) or of the diagonal.
for rounds and hexagons , at 1/6 from the outside of the diagonal or the diameter
(refer to annex A figure A.I).
6.4
Test methods-Types of test pieces
6.4.1 Tensile test (refer to ISO 6892) Normally, the test piece used shall be plate
type or rod type of proportional shape and have an original gauge length Lo given by
the formula,
Lo
= 5.65,fS;
where S o is the crosssectional area of the gauge length of the test

piece
The test piece of plate type with rectangular crosssection shall have a maximum
width on the gauge length portion of 40 mm, and its thickness shall be that of the
product: however, if the product thickness exceeds 30 mm, it may be reduced to 30 mm
by planing or milling on one face only.
22
G 3106: 2004
A test piece of rod type may be used for products more than 40 mm thick; it shall
be 10 mm to 30 mm in diameter and its original gauge length shall be determined
by the above formula; the axis of the test piece shall be positioned at 1/4 of the thickness
of the product.
A non-proportional test piece with a fixed initial gauge length may be used.
In this case, reference shall be made to a conversion table (refer to ISO 2566-1),
However, in case of dispute, only the results obtained on a proportional test piece
shall be taken into consideration.
The yield stress specified in annex 2 table 3 of this Standard is the upper yield
stress Re H, if the yield phenomenon is not visible, either the 0.2 % proof stress (RpO.2)
or the 0.5 % proof stress (total elongation) (Rto.5) may be used. The specification of
the material is complied with in this respect if one or other of these values satisfies
the specified yield stress value.
6.4.2 Impact test
a)
The impact test shall normally be carried out on products having a thickness more
than 12 mm or diameter more than 16 mm. The test piece shall be machined so
that the face nearest to the rolled surface is not more than 1 mm from it.
For products of thickness greater than 40 mm, the test piece shall be taken in
such a way that its axis is positioned at 114 of the thickness from the surface.
The notch shall be perpendicular to the rolled surface. If agreed at the time
of ordering, impact tests may be carried out on products having a thickness less
than 12 mm: the dimensions of the test pieces shall be in accordance with the
requirements of ISO 148, i.e. 10 mm x 7.5 mm and 10 mm x 5 mm, or shall correspond to 10 x e (e: being the product thickness). The specified energy values
are given in annex B.
b)
The test shall be carried out using a V-notch test piece supported at both ends
(refer to ISO 148), the value to be taken into account being the average of the
results obtained from three test pieces cut adjacent to each other from the same
product, unless there are reasons for a retest (refer to 6.4.5).
6.4.3 Chemical analysis

a)
If a products analysis is specified on the order, the number of samples to be
taken shall be in accordance with agreement between the purchaser and the
supplier.
The samples may be taken from the test pieces used to check the mechanical
properties or from the full thickness of the product at the same place as the
test pieces. In case of dispute , only the analysis of material from the full thickness of the product shall be taken into consideration.
For the selection and preparation of samples for chemical analysis, the requirements of ~~.Q ..~~.~~.~ shall be applied.
b)
In case of dispute, the method used for chemical analysis shall be in accordance
with the requirements specified in the corresponding International Standard.
If an International Standard does not exist, the method to be used shan be agreed
between the parties concerned.
23
G 3106: 2004
6.4.4 Faulty test and defective test pieces When a test does not give the re
quired results because of an error in carrying out the test, it shall be cancelled. Error
in carrying out the test means incorrect machining, incorrect mounting in the testing machine, malfunction of this machine or any other anomaly independent of the
metal itself.
If a defective test piece gives satisfactory results, the batch shall be accepted but
the corresponding item (from which the test sample was taken) may be subjected to
an individual examination for soundness.
6.4.5 Retests If during inspection, a test does not give the required results, additional tests, unless otherwise agreed, may be carried out as follows:
a)
Tensile test Procedures defined in 8.3.4.3.2 "Non-sequential tests" of ISO 404 :

1992 shall apply.
b)
Impact test The assessment of impact test results shall be made following a
sequential method as described in 8.4.3.2 of ISO 404 : 1992 and if retests are
necessary, they shall be carried out according to 8.3.4.3.3 of ISO 404.
6.5 Inspection documents The type of inspection documents required shall be

chosen among those defined in ISO 10474 and specified in the order.
In any case, this inspection document shall state the manufacturer's results for
the ladle analysis of all chemical elements specified for the steel grade concerned.
7 Sorting and reprocessing The requirements of clause 9 of ISO 404 : 1992 shall
apply.
8 Non-destructive tests If the purchaser requires non-destructive tests to check
the soundness of the products by means of ultrasonic, magnetic or liquid penetrant
examination methods, these tests shall be agreed upon at the time of enquiry and
order. This agreement shall include details of the test methods and interpretation
of results .
9 Marking Unless otherwise agreed at the time of ordering, products other than
those of E 185 shall be legibly marked with the followings.
a)
the identification symbols for the grade and quality of the steel;
b)
brand of the manufacturer;
c)
if necessary, symbols, letters or numbers which allow the inspection document,

test samples and products to be identified.
In the case of products of small unit mass which are consigned in bundles,
the above information may be marked on a tag securely attached to each bundle
(or it may be marked on the upper plate ).
10 Order The order shall specify.

if a particular steel making process is required (4.1 )
if the purchaser wishes to be informed of the steel making process (the choice of
process being left to the manufacturer) (4.1)
24
G 3106: 2004
if a particular delivery condition is required (4.2)
the type of quality D required (4.2.2)
if repair by welding is not permitted [4.3.3 b)]
if product analysis is required (5.1.2) and the number of samples required [6.4.3 a)]
if impact tests for quality B are required (6.1)
if impact tests for each rolled product are required for quality D [6.2.4 b)]
if impact tests for products less than 12 mm thick are required [6.4.2 a)l
if retests are not permitted (6.4.5)
the type of inspection document required (6.5)
if non-destructive tests are required (8)

if other types of marking are required (9)
Points that are not specified shall not be taken into account by the manufacture
25
G 3106: 2004
Annex A (normative)
Position and orientation of test pieces

,
!
1/3
I
2/3
113
2J3 I
1j 2J3
I
-l-
1/3
213
1/3
113
1/3
i
213
213
I
i
~ Position of test piece
Remarks: Refer to 6.4.2 [for the impact test, see also 6.4.2 a )].
Annex A Figure A.l
Position and orientation of test pieces
26
G 3106: 2004
Annex B (normative)
Energy values for impact test pieces of reduced size
Introduction This annex is the Japanese In dustrial Standard prepared based on

annex B (nor mative) to ISO 630 Structural steels-Plates, wide flats, bars, sections
and profiles published in 1995 as the second edition without modifying its technical
content.
27
26
25
24
19
18
17
16
15
14
13
10
Width of test piece, mm
Annex B Figure B.1
Minimum impact energy values for test pieces

with a width between 5 mm and 10 mm
27
G 3106: 2004
List of International Standards on tolerances for steel products

This annex shall not a parts of this Standard, provided only a supplement for the
items related to the provision of the body of this Standard.
ISO 657-5: 1976
Hot-rolled steel sections-Part 5: Equal-leg angles and unequal

leg angles-Tolerances for metric and inch series
ISO 657-13: 1981
Hot-rolled steel sections-Part 13: Tolerances on sloping flange

beam, column and channel sections
Information: ISO 657-13 : 1981 was withdrawn in 2002.

ISO 657-18: 1980 Hot-rolled steel sections- Part 18: L sections for shipbuilding
{metric series)-Dimensions, sectional properties and tolerances

ISO 657-19: 1980 Hot-rolled steel sections-Part 19: Bulb fats (metric series)-
Dimensions, sectional properties and tolerances

ISO 1035-4 : 1982 Hot-rolled steel bars-Part 4 : Tolerances
ISO 7452: 1984
Hot-rolled structural steel plates- Tolerances on dimensions

and shape
28
G 3106: 2004
Notes on weld ability

annex D to ISO 630 Structural steels-Plates, wide fiats, bars, sections and profiles
published in 1995 as the second edition without modifying its technical content.
This annex shall not a parts of this Standard. provided only a supplement for the
items related to the provision of the body of this Standard.
The steels specified in this annex do not have unlimited suitability for the vari
welding processes, since the behaviour of a steel during and after welding depends not only on the material but also on the dimensions and shape, as well as on
the manufacture and service conditions of the components.
QUS
There is no information concerning the weldability of the grade E 185 and quality A
available, as no requirements are specified concerning the chemical composition or
in a satisfactory way in terms of weldability.
Steels of qualities B, C and D are generally suitable for all welding processes.
The weldability increases from quality B to D. For grade E 235 B, killed steels
(NE or GF) are preferable to steels without specified deoxidation, particularly if segregation zones could be encountered during welding.
With increasing product thickness and increasing strength level, the main risk is
the occurrence of cold cracking in the welded zone.
Cold cracking is caused by a combination of the following factors :
the amount of diffusible hydrogen in the weld metal;
a brittle structure of the heat-affected zone;
a significant concentration of tensile stress in the welded joint.
Annex 3 (informative)
Comparison table between JIS and corresponding International Standard
ISO 6S0 : 1995 StructuraL steels-Plates, wide /lats. bars.
1rections and profiles
JIS G 3106: 2004 RolLed steels for welckd structure

(I) Requirements in JIS
;::
~
~
'~"
Clause
International
Standard
number
(11)
Content
(III) Requirements in International

Standard
(lV) Classifi cation and details of

technical deviation between JIS
and the International Standard
by clause
Location of deviation: a nnex
Indication method: dotted
underlines
Clause
Classification by
Scope
ISO 630
Steel plate, steel st.rip in coil ,

section a nd flat
Detail of technical
devia tion
clause
()
Content
Justification for
the technical deviation
a nd rut-ure measures
(V )
JIS G 0404 , JIS G 0415 ,
JIS G 0416 and others
Grade and designation
SM400A, B, C
SM490A, B, C
SM490YA, VB
SM520C
SM570
Scope
Steel plates, wide slrip in
coils, wide fl oLa, bars, section s nd profiles
MODI
deletion
ISO 148-1 , ISO 377 and
others
MODI
Characteristics of grades
and qualities
E185
E235
E275
E355
NEQ
alteration
JIS does not include

bars.
Bars are specified in

other JIS which can
be applied ss needed.
Some JIS have no

corresponding International Standards.
International Standards will be cited

after the ha rmonization of cited. standards.
is determined based
on the tensile strength
in JIS a nd on the
yield point in ISO.
'"o
~
'"
'"~~
(I)
Requirements in JIS
(II) International
Standard

Standard
number
Content
Classification by
clause
Detail of technical
deviation
Chemical composition
Five elements (e, Si, Mo, P, S)
are specified. Alloying clemeots may be added as necessary.
Characteristics of grades
and qualities
Five elements (C, Si, Mo, P,
S) arc specified. Grades are
also provided to which elements which produce a
fine-grained structure are
added.
NEQ
ISO's specification is
less strict especially in
P and S.
We will propose the
Not specified in ISO.
We will propose to
specify them.
NEQ
Carbon equivalent or chemica l

composition on sensitivity of
welding crack
Mechanical property
Inspection and testing
6.1
Yield point or proof stress,

tensile strength and elongation
6.2.4
Tensile test
Yield stress, tensile strength
and elongation are specified.
NEQ
JIS and ISO differ in

the balance of yield
point and tensile
strength (difference of
design concept).
6.2
Charpy absorption
B grade: 0 c, 27 J
C grade: 0 c, 47 J
SM570: - S oC, 47 J
6.4.2
Impact test
Test temperature:
- 20,0,+20
27 J min.
MODI
alteration

the specified values of
temperature and
energy.
7 Shape, dimension, mass and

the tolerance thereof
JIS G 3192, J I S G 3193 and
J I S G 3194 are cited.
NEQ
No items in ISO.
----
-_
..
_ - --
energy
min.
min.
min.
__ .
- --_ . . _--
....
a;
'"o
Clause
~c
~~
:i:
Content
t;i
Justification for
and future measures
(V)
Clause
'"-<
(IV) Classification and details of

by clause
Location of deviation: annex
underlines
value of JIS.
We will propose the

grade of J I S to ISO.
(1) Requirements in
~
~
?!
8
~
i5
:!i
JIS
International
Standard
number
(II)

Standard

by clause
underlines
Justification for
and future measures
(V)
Clause
Content.
Clause
Content
Classification by
clause
Detail of technical
deviation
Appearance
Appearances in JIS G 3192,
JIS G 3193 and JIS G 3194
are cited.
4.3
Surface appearanceDefects
ISO 7788 is cited.
NEQ

the cited standards.
Heat treatment and symbol

Normalizing, quench-hardening
and tempering, tempering and
thermomechanical control are
spedfied .
4.2
Delivery condition
As-rolled condition.
Other conditions shall Ix!
agreed upon.
Symbols arc not specified.
NEQ
[SO has no specification of symbols.
10
Tcsts
10. 1
Chemical analysis
Clause 8 of JIB G 0404 is cited.
For analytical methods,
methods of each JIB are cited.
6.4.3
Chemical analysis
In case the corresponding
International Standard
does not exist, the method
w be used sha ll be agreed
between the purchaser and
t he supplier.
MODI
JIB cites JIB for the

analytical method.
We will harmonize the

analytical methods of
JIB to ISO.
Analytical method
Clause 9 of JIB G 0404 is cited.
In case of over 50 t, 2 pieces.
For the sampling position of
test pieces, JIB G 0416 is cited.
6 .2
Test unit
50 t or part thereof
We will propose JIB .
Annex
Sampling position of test

pieces
JIB and ISO differ in

the test number when
the test lot exceeds
100 t.
test pieces has been
harmonized.
10.2
alteration
NEQ
We will harmonize the

cited standards.
"
to'"
'"
...8~
~
(I)
Requirements in J I S
(II)
Inter-
national
Standard
number
(II1l Requirements in International

Standard

technical deviation between JI8
a nd the International Standard
by clause
Indication method: dolted
Justification for
snd future measures
(V)
underlines
Clause
11
~
~
12
Clause
6.4.5
Retests
ISO 404 is cited.
Marking
Marking
a) Grade snd quality of the
steel
b) Brand of the manufacturer
c) Identification number as
needed
b) Heat number of inspection

number
c) Dimension
d) Quantity or mass of each
bundle
e) Manufacturer's name or
identifying brand
()
i5
Report
J IS G 0404 and JIS G 0415
are cited.
6.5
Annex
1
(normative) Sampling position

of the test piece
Annex
Annex
2
(normative) Structural steelsPlates, wide flats, bars, section

and profiles
",,'
13
Content
Inspection
For general matters and
reinspection, J IS G 0404 is
cited.
s) Symbol of grade
2l
Content
Classification by
clause
Detail of technical
deviation
IDT
MODI
addition
Inspection documents
ISO 10474 is cited.
MODI
Position snd orientation of

test pieces
NEQ
(normative) Structural
Bteels-Plates, wide flats.
bars, section and profiles
IDT
alteration
JIS has more specified items than [SO.
We will propose J IS.
J IS has more detailed

contents than ISO.
We will propose JIS.
JIS is specified with

the applicable date
and will be harmonized to ISO in future.
Q'"
",'"
~
'"
'"
~
(I)
Requirements in JIS
International

Standard
Standard

number
by clause
(II)
(V)
Justification for
the tech nical deviation

and future measures

Indication method: doLled
underlines
Clause
Content
Clause
Content
Clsssification by
clause
Annex
(normative) Position and

orientation of test pieces
Annex
(normative) Position and

orientation of test pieces
lOT
(normative) Energy vulues for

impact test pieces of reduced
size
Annex
(normative) Energy valucs

for impact test pieces of
reduced size
lOT
(informative) List of Internstional Standards on tolerances

for steel products
Annex
(informative) List. of Internationa l Standards on 1olerances for steel products
lOT
(informat.ive) Notes on weldabilit.y
Annex
(informative) Notes on
weldability
lOT
Detail of technical
deviation
."
'~"
~
Annex
tl
Annex
2i
Annex
D
I Designated degree of correspondence between JIS and International Standard: MOD
----
----
._----
----
_I
Remarks 1 Symbols in s ub-columns of classification by clause in the above table indicate as follows:
IDT: Identical in technical contents.
MOD/deletion: Deletes specification item(s) or content(s) of International Standard.
MOD/addition: Adds specification item(s) or content(s) not included in International Standard.
MOD/alteration: Alters t he specification content(s) included in International Standard.
NEQ: Not equiva lent.
2 Symbol in column of designated degree of corresponden ce between JIS and In terna tion al Sta ndard in the
above table indicates as follows:
-
MOD:
Modifies In ternational Standard.
<;)
'"g
~
'"
~~
ns (English edition) are printed in Standardization Journal, publisbed monthly

by the Japanese Standards Association, and also provided to subscribers of TIS (English
edition) in Monthly Information.
Errala for
Errata will be provided upon request. please contact:

StaDciardization Promotion Department, Japanese Standards Association
4-124, Akasaka.., Minato--ku. Tokyo, 1078440 JAPAN
TEL. 0335838002
FAX. 0335830462

JIS G 3106 - New

Uploaded by

Copyright:

Available Formats

JIS G 3106 - New

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

JIS G 3106 - New

Uploaded by

Copyright:

Available Formats

JAPANESE

Nur zur Information ! Kein nderungsdienst

Translated and Published by

Rolled steels for welded structure

Reference number : JIS G 3106 : 2004 (E)

JIS G 3106 : 2004, First English edition published in 2004-06

Transla ted and published by: Japa nese Standards Association

Normative references ........................................................................................

Grade and designation .....................................................................................

Chemical composition .......................................................................................

Carbon equivalent or chemical composition on sensitivity of welding

Carbon equivalent or chemical composition on sensitivity of welding

Carbon equivalent or chemical composition on sensitivity of welding

Mechanical property .........................................................................................

Yield point or proof stress, tensile strength and elongation ...................

Charpy absorption energy ..............................................................................

Shape, dimension, mass and the tolerance thereon....................................

Heat treatment and symbol.............................................................................

Heat treatment ........................................ ........................................................

Symbol of heat treatment ..............................................................................

Mechanical test ................................................................................................

Inspection ........... ............................................................................................... 10

Marking ........................... ..... .... .... .......................................................................

Sampling position of the test piece ................................

Structural steels-Plates, wide flats , bars, section

Annex A (normative) Position and orientation of test pieces .......................... 25

List of International Standards on tolerances for

Notes on weldability .......................................................

Comparison table between JIS and corresponding

JAPANESE INDUSTRIAL STANDARD

<6 JIS G 3106: 2004

Rolled steels for welded structure

Introduction This Standard is the Japanese Industrial Standard specified by making

In using this Standard, either its text or annex 2 shall be applied.

The International Standard corresponding to this Standard is as

Steel plate, steel strip in coil, section and flat

Steel plate, steel strip in coil and section

Steel plate, steel strip in coil, section and flat

Steel plate, steel strip in coil and section

Steel plate, steel strip in coil, section and flat

Steel plate, steel strip in coil, section and flat

Steel plate. steel strip in coil and section

Steel plate, steel strip in coil and section

Remarks 1 The steel plate which is until 150 mm in thickness of SM520B,

4 Chemical composition The steel products shall be tested in accordance with

Over 50 mm up to and incl. 200 mm in thickness

Over 50 mm up to and incl. 200

2.5 xC 0.035 0.035

100 mm or under in thickness

Over 50 mm up to and incl. 200 rom in thickness

50 rom or under in thickness

Over 50 mm up to and incl. 200 mm in thickness

100 mm or under in thickness

100 mm or under in thickness

100 mm or under in thickness

100 mm or under in thickness

5 Carbon equivalent or chemical composition on sensitivity of welding crack

Thickness of steel product mm

Over 50 up to and incl. 100