    5000 HR Test

    Uploaded by

    mrhom
    The document reports on test results for polymer-housed surge arresters. It describes two accelerated aging tests conducted to verify the arresters' ability to withstand salt fog and weather conditions according to IEEE standards. No physical damage or failures occurred and measurements remained within specification limits.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    5000 HR Test

    Uploaded by

    mrhom
    30 views1 page
    The document reports on test results for polymer-housed surge arresters. It describes two accelerated aging tests conducted to verify the arresters' ability to withstand salt fog and weather conditions according to IEEE standards. No physical damage or failures occurred and measurements remained within specification limits.

    Original Description:

    weather test

    Original Title

    5000 hr test

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    The document reports on test results for polymer-housed surge arresters. It describes two accelerated aging tests conducted to verify the arresters' ability to withstand salt fog and weather conditions according to IEEE standards. No physical damage or failures occurred and measurements remained within specification limits.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    30 views1 page

    5000 HR Test

    Uploaded by

    mrhom
    The document reports on test results for polymer-housed surge arresters. It describes two accelerated aging tests conducted to verify the arresters' ability to withstand salt fog and weather conditions according to IEEE standards. No physical damage or failures occurred and measurements remained within specification limits.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    Certified Test Report UltraSIL Polymer-Housed VariSTAR Normal-Duty, Heavy-Duty and Riser Pole Distribution-Class Arresters

    TEST O 1000 HOURS ACCELERATED AGING TEST WITH EXPOSURE TO SALT FOG OBJECT
    To verify the ability of the arrester to withstand continuous salt fog conditions and endure surface arcing and heating in accordance with IEEE Std C62.11-2005 standard, Para. 8.7.

    TEST P 5000 HOURS WEATHER AGING TEST OBJECT


    To verify the ability of the arrester to endure surface arcing and heating while subject to humidification, thermal cycling, rain, simulated solar radiation (UV) and salt fog. Testing was performed in accordance with IEEE Std C62.11-2005 standard, Annex C.

    PROCEDURE x One sample of the longest electrical section


    with the highest rated voltage was subjected to pre-tests consisting of Reference Voltage and Partial Discharge measurements. The Reference Voltage was measured at a peak resistive current of 3mA for normal-duty and 4mA for heavy-duty. Partial Discharge was measured at a test voltage of 1.05 x Uc. Sample was placed in the vertical position inside a test chamber equipped for heating, humidity, UV-radiation, artificial rain and salt fog. The sample was subject to a multi-stress cycle as defined by IEEE Std C62.11-2005 standard, Annex C, and Figure C.1 for duration of 5,000 hours. Post-tests were conducted for Reference Voltage and Partial Discharge to verify measured values did not exceed specified levels by the standard. Sample was inspected to assure that no physical damage had occurred.

    PROCEDURE x
    One sample of the longest electrical section with the highest rated voltage was subjected to pre-tests consisting of Reference Voltage and Partial Discharge measurements. The Reference Voltage was measured at a peak resistive current of 3mA for normal-duty and 4mA for heavy-duty. Partial Discharge was measured at a test voltage of 1.05 x Uc. Sample was placed in the vertical position inside an enclosure with salt fog mist of 10kg/m salinity level and energized at Uc for duration of 1000 hours. Post-tests were conducted for Reference Voltage and Partial Discharge to verify measured values did not exceed levels specified by the standard. Sample was inspected to assure that no physical damage had occurred.

    RESULTS
    The sample tested successfully met the test requirements of IEEE Std C62.11-2005 standard, Para. 8.7. There were no housing punctures or erosion of the housing, no internal breakdowns; no surface tracking was evidenced by physical examination. The arrester reference voltage did not decrease by more than 5% and the partial discharge level did not exceed 10pC.

    RESULTS
    The sample fulfilled the requirements of IEEE Std C62.11-2005 standard, Annex C. No over current trip-out occurred during the testing procedure. There was no tracking, cracking or treeing of the external housing. There were no housing punctures or internal breakdowns. The arrester reference voltage did not decrease by more than 5% and the partial discharge level did not exceed 10pC.