Aceros Posco
Aceros Posco
Aceros Posco
13 1:37 PM 1 g6
Electrical Steel
2010-11-
Made in Korea
>>>
Contents
MANUFACTURING PROCESS AND FACILITIES 4
SPECIFICATION & MAIN APPLICATION 6
GRAIN-ORIENTED ELECTRICAL STEEL 8
NON-ORIENTED ELECTRICAL STEEL 14
SURFACE INSULATION 26
STRESS RELIEF ANNEALING 27
RELATIONS AMONG WEIGHT, OUTSIDE DIAMETER AND WIDTH OF COIL 29
MAJOR INTERNATIONAL STANDARDS 30
UNIT CONVERSION TABLES, THE INTERNATIONAL SYSTEM OF UNITS(SI) 32
PACKAGING/MARKING 33
GLOBAL NETWORK 34
1. Excellent materials
produces the worlds best electrical steel with its outstanding manufacturing technology.
Customers prefer products made of
electrical steel because they feature excellent performance
and high energy efficiency.
In particular, domain refined GO made by the latest laser technology are mainly used for an extra-high
voltage transformer which is the most energy efficient in the world.
>> Manufacturing
Insulation Coating
Pickling
Cold Rolling
04
www.posco.com
Annealing
Electrical Steel
05
Main Application
Grain-Oriented
Non-Oriented
PN-Core
PHDCore
PHCore
Large rotating
machine
Rotating Machines
Medium rotating
machine
Hermetically
sealed motor
Static Machines
Large power
transformer
Distribution
transformer
Audio
transformer
Welding
transformer
Magnetic
switch core
www.posco.com
General use
AC motor
Ballast
06
PGCore
The usage presented in this section reflects the general use and shall be used as a reference.
Please be sure to consult with our associates when making orders for specific usage.
Electrical Steel
07
>> Grain-Oriented
Electrical Steel
PG-Core
The grain's easy magnetization direction is aligned to the rolling direction. Therefore, this product
features excellent magnetic properties in the rolling direction. It is widely used for large-sized power
transformers or mid/small size transformers.
Standard Size
Product
PG-Core
Grade
27PG110
27PG120
27PG130
30PG110
30PG120
30PG130
30PG140
35PG145
35PG155
Width mm (in.)
Thickness
mm (in.)
Available
Standard
Inside diameter
mm (in.)
0.27
(0.0106)
0.30
(0.0118)
850-1000
(33.46-47.24)
1000
(39.37)
1200
(47.24)
508
(20)
0.35
(0.0138)
Specification
Magnetic properties and lamination factor
Grade
27PG110
27PG120
27PG130
30PG110
30PG120
30PG130
30PG140
35PG145
35PG155
Thickness
mm (in.)
Density
(kg/dm3)
0.27
(0.0106)
0.30
(0.0118)
0.35
(0.0138)
7.65
0.50
0.54
0.59
0.50
0.54
0.59
0.64
0.66
0.70
Magnetic Flux
Density.Min
T (B8)
95.0
1.80
Note: The above test is conducted in accordance to IEC60404-2 (or JIS C 2550-2000).
W17/50 indicates the core loss at the frequency of 50 Hz, magnetic flux density of 1.7T.
Core loss and induction are measured after stress relief annealing in a longitudinal direction.
(annealing condition : 840, 1Hr, Under neutral atmosphere)
08
www.posco.com
Lamination Factor,
Min(%)
95.5
96.0
Thickness
mm (in.)
Thickness Tolerance
mm (in.)
Thickness deviation in
Width Tolerance
transverse direction
mm (in.)
mm (in.)
Camber
(Length : 2m)
mm (in.)
0.27(0.0106)
0.30(0.0118)
0.35(0.0138)
0.03
(0.0012)
+0.6(0.0236)
0
0.03(0.0012)
and under
1.0(0.0394)
and under
Note : The thickness deviation in width direction means the gap between the thickness of center and the one
of part 15mm away from the edge part.
Thickness
mm (in.)
Density
(kg/dm3)
27PG110
27PG120
27PG130
Core Loss
Magnetic
Resistivity
Flux
Density.
Watt
per
pound
Watt
per
kilogram
m
T
-8
(10 ) W15/50 W17/50 W15/60 W17/60 W15/50 W17/50 W15/60 W17/60
(B8)
1.85
0.76 1.05 1.01 1.37 0.35 0.48 0.46 0.62
0.27
(0.0106)
30PG110
30PG120
30PG130
0.30
(0.0118)
7.65
48
30PG140
35PG145
35PG155
0.35
(0.0138)
1.85
1.84
1.85
1.85
1.84
1.84
1.84
1.83
0.27(0.0106)
Tensile Strength
(N/mm2)
L
C
344
385
Yield Point
(N/mm2)
L
C
322
340
L
11
C
44
0.30(0.0118)
345
412
330
350
12
0.35(0.0138)
364
423
345
357
10
Thickness
mm (in.)
Elongation
(%)
182
Lamination
Factor
(%)
98.0
49
174
99.0
40
181
99.5
Hardness
Hv1
09
PH-Core
The directional property of grain-oriented electrical steel is more reinforced in the rolling direction than
PG-Core and therefore features low core loss and high induction. It is used for iron core of both large and
other size power transformers and desirable for high efficiency and miniaturization of machinery.
Standard Size
Product
Grade
Width mm (in.)
Thickness
mm (in.)
Available
Standard
Inside Diameter
mm (in.)
23PH085
23PH090
23PH095
0.23
(0.0091)
1000
(39.37)
23PH100
PH-Core
27PH095
27PH100
0.27
(0.0106)
850-1200
(33.46-47.24)
27PH1 10
30PH100
508
(20)
1200
(47.24)
0.30
(0.0118)
30PH105
Specification
Magnetic properties and lamination factor
Grade
Thickness
mm (in.)
Density
(kg/d)
23PH085
0.39
23PH090
0.23
0.90
0.41
23PH095
(0.0091)
0.95
0.43
1.00
0.45
0.95
0.43
1.00
0.45
1.10
0.50
23PH100
27PH095
27PH100
27PH110
0.27
(0.0106)
7.65
30PH100
0.30
1.00
0.45
30PH105
(0.0118)
1.05
0.48
Magnetic Flux
Density.Min
T (B8)
Lamination
Factor, Min(%)
94.5
1.88
Note: The above test is conducted in accordance to IEC60404-2 (or JIS C 2550-2000).
W17/50 indicates the core loss at the frequency of 50 Hz, magnetic flux density of 1.7T.
Core loss and induction are measured after stress relief annealing in a longitudinal direction.
(annealing condition : 840, 1Hr, Under neutral atmosphere)
10
www.posco.com
95.0
95.5
Thickness
Tolerance
mm (in.)
Thickness
mm (in.)
Thickness deviation in
transverse direction
mm (in.)
Width
Tolerance
mm (in.)
Camber
(Length : 2 m)
mm (in.)
0.03(0.0012)
+0.6(0.0236)
1.0(0.0394)
and under
and under
0.23(0.0091)
850 and over
(33.46)
0.27(0.0106)
0.03(0.0012)
0.30(0.0118)
Note : The thickness deviation in width direction means the gap between the thickness of center and the one of part
15mm away from the edge part.
Grade
Resistivity
Thickness Density m
mm (in.) (kg/dm3) (10-8)
23PH085
Core Loss(W/kg)
Magnetic
Flux
Watt per kilogram
Watt per pound
Density.
W15/50 W17/50 W15/60 W17/60 W15/50 W17/50 W15/60 W17/60 T (B8)
0.62
0.83
0.81
1.10
0.28
0.38
0.37
0.50
1.91
23PH090
0.23
0.64
0.88
0.85
1.15
0.29
0.40
0.39
0.52
1.91
23PH095
(0.0091)
0.65
0.90
0.86
1.17
0.30
0.41
0.39
0.53
1.91
0.70
0.95
0.92
1.26
0.32
0.43
0.42
0.57
1.90
0.70
0.93
0.92
1.23
0.32
0.42
0.42
0.55
1.91
23PH100
27PH095
27PH100
27PH110
0.27
7.65
48
(0.0106)
0.72
0.97
0.95
1.27
0.33
0.44
0.43
0.58
1.90
0.78
1.03
1.01
1.37
0.35
0.47
0.46
0.62
1.90
30PH100
0.30
0.74
0.99
0.98
1.29
0.34
0.45
0.44
0.59
1.91
30PH105
(0.0118)
0.76
1.01
1.00
1.33
0.35
0.46
0.45
0.60
1.90
Tensile Strength
(N/mm2)
L
C
Yield Point
(N/mm2)
L
C
Elongation
(%)
Hardness
Hv1
Lamination
Factor
(%)
0.23(0.0091)
381
424
356
383
18
42
178
98
0.27(0.0106)
361
415
337
367
18
42
182
98
0.30(0.0118)
345
412
330
358
20
45
184
99
11
PHD-Core
Magnetic domain refined steel is a grade that has been specially laser treated to lower the core loss
some 30% from that of CGO steel. Energy efficiency is raised and magnetostriction is lowered, resulting
in low noise. . It is used for iron core of both large and other size power transformers that have not been
heat treated.
Standard Size
Product
23PHD080
23PHD085
PHD-Core
27PHD090
27PHD095
30PHD095
Width mm (in.)
Available
Standard
Thickness
mm (in.)
Grade
Inside diameter
mm (in.)
0.23(0.0091)
0.27(0.0106)
850-1000
1000
508
(33.46-39.37)
(39.37)
(20)
0.030(0.0118)
Specification
Magnetic properties and lamination factor.
Grade
23PHD080
23PHD085
27PHD090
27PHD095
30PHD095
Thickness
mm (in.)
Density
(kg/dm3)
0.23(0.0091)
0.27(0.0106)
Magnetic Flux
Density.Min
Watt per kilogram Watt per pound
T (B8)
0.36
0.80
1.88
0.39
0.85
7.65
0.030(0.0118)
0.90
0.41
0.95
0.43
0.95
0.43
1.88
Lamination
Factor, Min(%)
94.5
95.0
95.5
Note: The above test is conducted in accordance to IEC60404-3 (or JIS C 2556), using as-sheared specimens in
longitudinal to rolling direction, without stress relief annealing.
W17/50 indicates the core loss at the frequency of 50 Hz, magnetic flux density of 1.7T.
Thickness
mm (in.)
Thickness
Tolerance
mm (in.)
Thickness deviation in
transverse direction
mm (in.)
Width
Tolerance
mm (in.)
Camber
(Length : 2 m)
mm (in.)
0.03
0.03(0.0012)
and under
+0.6(0.0236)
1.0(0.0394)
and under
0.23(0.0091)
850 and over
(33.46)
0.27(0.0106)
0.30(0.0118)
(0.0012)
Note : The thickness deviation in width direction means the gap between the thickness of center and the one of part
15mm away from the edge part.
12
www.posco.com
Grade
23PHD080
23PHD085
27PHD090
27PHD095
30PHD095
Resistivity
Thickness Density m
mm (in.) (kg/dm3) (10-8)
0.23
(0.0091)
0.27 7.65
(0.0106)
48
0.30
(0.0118)
Core Loss
Magnetic
Flux
Density.
Watt per kilogram
Watt per pound
T
W15/50 W17/50 W15/60 W17/60 W15/50 W17/50 W15/60 W17/60 (B8)
0.57
0.77
0.75
1.01
0.26
0.35
0.34
0.46
1.91
0.59
0.80
0.78
1.05
0.27
0.36
0.35
0.48
1.91
0.64
0.87
0.85
1.14
0.29
0.40
0.39
0.52
1.91
0.66
0.91
086
1.18
0.30
0.41
0.39
0.54
1.91
0.68
0.93
0.91
1.23
0.31
0.42
0.41
0.56
1.91
Tensile Strength
(N/mm2)
L
C
Yield Point
(N/mm2)
L
C
Elongation
(%)
L
Hardness
Hv1
Lamination
Factor
(%)
0.23(0.0091)
381
424
356
383
14
49
176
99.0
0.27(0.0106)
361
415
337
367
11
44
185
98.5
0.30(0.0118)
345
412
330
358
12
49
183
99.0
Electrical Steel
13
>> Non-oriented
Electrical Steel
PN-Core
The non-oriented electrical steel features even magnetic properties in the rolling direction and in other directions.
They are widely used for iron core materials of rotating machines ranging from large-size power generators to
small-size precision electric motors. They are also desirable for iron core of small-size power transformers.
Standard Size
Product
Grade
0.35
(0.0138)
0.50 950~1200
50PN250, 50PN270, 50PN290, 50PN310, 50PN350
(0.0197) (37.40-47.24) 1000
(39.37)
0.65
65PN290, 65PN310, 65PN350
(0.0256)
1100
(43.31)
0.35
35PN360, 35PN440
(0.0138)
1200
(47.24)
50PN400, 50PN470, 50PN600, 50PN700, 50PN800, 0.50 950~1250
(0.0197) (37.40-49.21)
50PN1000, 50PN1300
35PN210, 35PN230, 35PN250, 35PN270, 35PN300
PN-Core
(Coil)
508
(20)
0.65
65PN600, 65PN700, 65PN800, 65PN1000, 65PN1300 (0.0256)
Note: For non-standard sizes, please contact us
Specification
Magnetic properties and lamination factor.
Grade
Density
(kg/dm3)
Magnetic Flux
Density.Min
T
(B50)
35PN210
7.60
2.10
0.95
1.62
35PN230
7.60
2.30
1.04
1.62
7.60
2.50
1.14
1.62
7.65
2.70
1.23
1.62
7.65
3.00
1.36
1.62
35PN360
7.65
3.60
1.63
1.63
35PN440
7.70
4.40
2.00
1.65
35PN250
35PN270
35PN300
14
Thickness
mm (in.)
www.posco.com
0.35
(0.0138)
Lamination
Factor,
Min
(%)
95.0
Grade
Thickness
mm (in.)
Density
(kg/dm3)
Magnetic Flux
Density.Min
T
(B50)
50PN250
7.60
2.50
1.14
1.62
50PN270
7.60
2.70
1.23
1.62
50PN290
7.60
2.90
1.32
1.62
50PN310
7.65
3.10
1.41
1.62
50PN350
0.50
7.65
3.50
1.59
1.62
50PN400
(0.0197)
7.65
4.00
1.82
1.63
50PN470
7.70
4.70
2.13
1.64
50PN600
7.75
6.00
2.72
1.66
50PN700
7.80
7.00
3.18
1.70
50PN800
7.85
8.00
3.63
1.70
50PN1000
7.85
10.00
4.54
1.70
50PN1300
7.85
13.00
5.90
1.70
65PN290
7.60
2.90
1.32
1.62
65PN310
7.65
3.10
1.41
1.62
65PN350
7.65
3.50
1.59
1.62
65PN400
7.65
4.00
1.82
1.63
65PN470
0.65
7.70
4.70
2.13
1.64
65PN600
(0.0256)
7.75
6.00
2.72
1.66
65PN700
7.80
7.00
3.18
1.70
65PN800
7.85
8.00
3.63
1.70
65PN1000
7.85
10.00
4.54
1.70
65PN1300
7.85
13.00
5.90
1.70
Lamination
Factor,
Min
(%)
96.0
97.0
Note: The above test is conducted in accordance to IEC60404-2 (or JIS C 2550-2000).
W15/50 indicates the core loss at the frequency of 50 Hz, magnetic flux density of 1.5T.
1000(39.37)
and over
0.35(0.0138)
Thickness deviation in
Thickness
transverse direction
Tolerance
mm (in.)
mm (in.)
0.035(0.00138) 0.02(0.0008) and under
0.50(0.0197)
0.65(0.0256)
0.35(0.0138)
0.035(0.00138)
Thickness
mm (in.)
Width
Tolerance
mm (in.)
+1.5(0.0591)
0
0.040(0.00158)
0.65(0.0256)
1.0(0.0394)
and under
0.50(0.0197)
Camber
(Length : 2 m)
mm (in.)
+1.5(0.0591)
0
Note : The thickness deviation in width direction means the gap between the thickness of center and the one of part
15mm away from the edge part.
Electrical Steel
15
Core Loss
Thickn
Resistivity
ess Density
m
3
mm (kg/dm )
(10-8)
(in.)
Grade
B50
7.60
59
0.84
2.04
1.03
2.53
0.38
0.93
0.47
0.17
1.56
1.65
35PN230
7.60
59
0.89
2.10
1.07
2.60
0.40
0.95
0.49
0.18
1.57
1.66
7.60
55
0.96
2.25
1.17
2.85
0.43
1.02
0.53
0.20
1.57
1.66
35PN270
(0.0138) 7.65
52
1.02
2.40
1.28
3.00
0.46
1.09
0.58
0.21
1.58
1.67
35PN300
7.65
45
1.08
2.53
1.38
3.18
0.49
1.15
0.63
0.22
1.59
1.69
35PN360
7.65
45
1.25
2.80
1.55
3.45
0.57
1.27
0.70
0.26
1.59
1.69
35PN440
7.70
42
1.39
3.08
1.73
3.82
0.63
1.40
0.79
0.29
1.62
1.71
50PN250
7.60
59
1.00
2.37
1.31
3.08
0.45
1.08
0.59
1.40
1.57
1.67
50PN270
7.60
59
1.05
2.50
1.35
3.22
0.48
1.14
0.61
1.46
1.57
1.67
50PN290
7.60
56
1.09
2.60
1.45
3.35
0.50
1.18
0.65
1.52
1.58
1.67
50PN310
7.65
53
1.21
2.70
1.55
3.46
0.55
1.23
0.70
1.57
1.59
1.68
7.65
50
1.30
2.93
1.63
3.74
0.59
1.33
0.74
1.70
1.60
1.69
45
1.41
3.18
1.82
4.01
0.64
1.44
0.83
1.82
1.61
1.70
50PN470
(0.0197) 7.65
7.70
42
1.64
3.55
2.06
4.56
0.74
1.61
0.94
2.07
1.61
1.70
50PN600
7.75
34
1.98
4.40
2.49
5.63
0.90
2.00
1.13
2.56
1.62
1.71
50PN700
7.80
30
2.62
5.55
3.30
7.03
1.19
2.52
1.50
3.19
1.64
1.72
50PN800
7.85
17
2.93
6.26
3.63
7.94
1.33
2.84
1.65
3.60
1.66
1.74
50PN1000
7.85
17
3.20
6.80
4.10
8.62
1.45
3.09
1.86
3.91
1.67
1.75
50PN1300
7.85
17
3.75
7.56
4.75
9.54
1.70
3.43
2.16
4.33
1.67
1.75
65PN400
7.65
45
1.63
3.70
2.23
4.85
0.74
1.68
1.01
2.20
1.62
1.70
65PN470
7.70
42
1.91
4.16
2.59
5.45
0.87
1.89
1.18
2.47
1.62
1.70
7.75
34
2.27
5.14
3.09
6.68
1.03
2.33
1.40
3.03
1.63
1.72
7.80
30
3.02
6.47
4.06
8.33
1.37
2.94
1.84
3.78
1.65
1.73
7.85
17
3.38
7.28
4.56
9.39
1.53
3.30
2.07
4.26
1.67
1.75
65PN1000
7.85
17
3.64
7.86
5.00
10.14
1.65
3.57
2.27
4.60
1.68
1.75
65PN1300
7.85
17
4.32
8.79
5.83
11.29
1.96
4.00
2.65
5.13
1.68
1.75
0.35
35PN250
50PN350
50PN400
0.50
65PN600
65PN700
65PN800
0.65
(0.0256)
16
www.posco.com
Thickness
mm (in.)
Tensile Stength
(N/mm2)
L
C
Yield Point
(N/mm2)
L
C
Elongation
(%)
L
C
Hardness
Hv1
35PN210
538
547
415
427
18
19
220
35PN230
535
545
393
403
19
20
216
35PN250
0.35
522
539
370
385
19
21
214
35PN270
(0.0138)
467
485
347
361
21
23
190
35PN300
456
469
336
351
21
23
188
35PN360
450
470
350
366
23
25
170
35PN440
405
415
273
285
27
29
150
50PN250
550
570
413
426
20
22
223
50PN270
535
550
406
460
22
23
205
50PN290
510
530
370
386
23
25
195
50PN310
483
505
355
361
25
28
189
470
489
344
354
25
28
189
465
482
352
365
27
30
183
415
420
265
375
34
36
143
50PN600
395
405
260
270
37
39
130
50PN700
385
395
270
280
38
39
120
50PN800
375
385
270
280
39
40
115
50PN1000
370
380
265
275
40
41
113
50PN1300
350
360
250
260
42
43
105
65PN400
499
490
320
340
24
26
170
65PN470
480
490
300
315
28
29
160
50PN350
50PN400
50PN470
0.50
(0.0197)
65PN600
0.65
420
430
295
305
30
31
150
65PN700
(0.0256)
395
405
275
285
35
37
118
65PN800
375
385
270
280
41
43
113
65PN1000
370
380
265
275
43
45
110
65PN1300
350
360
260
270
45
110
Lamination
Factor
(%)
97.5
98.0
98.0
Electrical Steel
17
PNM-Core
The non-oriented electrical steel features even magnetic properties in the rolling direction and in other
directions. It is utilized as steel material for magnetic switches and improved in wear resistance and
residual magnetism.
Standard Size
Product
PNM-Core
(Coil)
Grade
Thickness
mm (in.)
65PNM540
0.65
(0.0256)
Width mm (in.)
0.70
(0.0276)
70PNM500
Available
Standard
950~1200
(37.40-47.24)
1000
(39.37)
1050
(41.34)
1 100
(43.31)
Inside Diameter
mm (in.)
508
(20)
Specification
Magnetic properties and lamination factors.
Grade
65PNM540
70PNM500
Thickness
mm (in.)
Density
(kg/dm3)
0.65
(0.0256)
0.70
(0.0276)
7.70
5.40
2.45
1.66
97.0
7.65
5.00
2.63
1.65
97.0
Note : The above test is conducted in accordance to IEC404-2 (or JIS C 2550-2000), using as-sheared specimens
one half longitudinal and one half transverse to the rolling direction.
Thickness
mm (in.)
Thickness
Tolerance
mm (in.)
Thickness deviation in
transverse direction
mm (in.)
Width Tolerance
mm (in.)
1000(39.37)
and under
0.65(0.0256)
0.052(0.00205)
0.70(0.0276)
0.056(0.00221)
0.04(0.0016)
and under
+1.5(0.0591)
0
1000(39.37)
and under
0.65(0.0256)
0.052(0.00205)
0.70(0.0276)
0.056(0.00221)
0.04(0.0016)
and under
+1.5(0.0591)
0
Camber
(Length : 2m)
mm (in.)
1.0(0.0394)
and under
Note : The thickness deviation in width direction means the gap between the thickness of center and the one of part
15mm away from the edge part.
18
www.posco.com
Grade
Magnetic Flux
Density.Min
(T)
Core Loss
Watt per pound
B25
B50
70PNM500
0.65
(0.0256)
0.70
(0.0276)
7.70
42
1.80
3.72
2.27
4.81
0.82
1.69
1.03
2.18
1.65
1.73
7.65
44
1.72
3.63
2.18
4.78
0.78
1.65
0.99
2.17
1.61
1.70
Thickness
mm (in.)
Tensile Stength
(N/mm2)
L
C
65PNM540
0.65
(0.0256)
437
70PNM500
0.70
(0.0276)
452
Yield Point
(N/mm2)
L
C
300
315
Elongation
(%)
L
C
32
33
Hardness
(Hv1)
Lamination
Factor
(%)
155
98.0
495
503
356
371
37
39
173
Electrical Steel
19
PNF-Core
PNF-Core features good magnetic properties in high frequency where eddy current loss extremely
increase.
Standard Size
Product
Grade
PNF-Core
(Coil)
20PNF1500
Width mm (in.)
Thickness
mm (in.)
Available
Standard
Inside Diameter
mm (in.)
0.20
950~1200
1000
508
(0.0080)
(37.40-47.24)
(39.37)
(20)
Specification
Magnetic properties and lamination factor.
Core Loss , Max (W10/400)
Grade
20PNF1500
Thickness
mm (in.)
0.20
(0.0080)
Density
(kg/dm3)
7.65
15.0
Magnetic Flux
Density.Min
T
(B50)
Lamination
Factor , Min(%)
1.62
93.0
6.80
Note: The above test is conducted in accordance to IEC60404-2 (or JIS C 2550-2000), using as-sheared specimens
one half longitudinal and one half transverse to the rolling direction.
W10/400 indicates the core loss at the frequency of 400 Hz, magnetic flux density of 1.0T.
B50 indicates magnetic flux density at 5000A/m
Thickness
mm (in.)
Thickness
Tolerance
mm (in.)
1000(39.37)
and under
0.20
(0.0080)
0.020
Thickness deviation in
transverse direction
mm (in.)
Width Tolerance
mm (in.)
0.02(0.0008)
+1.5(0.0591)
and under
Camber
(Length : 2m)
mm (in.)
1.0(0.0394)
and under
1000(39.37)
and over
0.20
(0.0080)
0.020
0.03(0.0012)
+1.5(0.0591)
and under
Note : The thickness deviation in width direction means the gap between the thickness of center and the one of part
15mm away from the edge part.
20
www.posco.com
Grade
20PN
F1500
Resist
Thickn
Density ivity
ess
(kg/ m
mm
dm3)
(
(in.)
108)
0.20
(0.0080)
7.65
50
Core Loss
Watt per kilogram
Magnetic Flux
Density.Min
(T)
W10/50 W15/50 W10/60 W15/60 W10/400 W10/50 W15/50 W10/60 W15/60 W10/400 B25
B50
1.24
1.66
2.71
5.76
1.55
Thickness
mm (in.)
Tensile Stength
(N/mm2)
L
C
20PNF1500
0.20
(0.0080)
471
Yield Point
(N/mm2)
L
C
490
363
Elongation
(%)
L
C
381
16
19
Hardness
(Hv1)
Lamination
Factor
(%)
195
97.0
20PNF1500
35PN210
80
35PN440
Core Loss
(at 1.0Tesla)
60
40
20
50 100
200
400
600
800
1000
1200
(Hz)
Motor of
Premium
Slim Spindle
motor of ODD
Electrical Steel
21
PNA-Core
PNA-Core features lower core loss, high induction after SRA and good punchability.
Standard Size
Product
Grade
Width mm (in.)
Thickness
mm (in.)
Available
Standard
1000
50PNA300
PNA-Core
(Coil)
Inside Diameter
mm (in.)
(39.37)
50PNA350
0.50
950~1200
1050
508
(0.0197)
(37.40-47.24)
(41.34)
(20)
1100
50PNA450
(43.31)
Specification
Magnetic properties and lamination factor
Grade
Thickness
mm (in.)
50PNA300
50PNA350
0.50
(0.0197)
50PNA450
Density
(kg/dm3)
Magnetic Flux
Density.Min
T(B50)
Watt per kilogram Watt per pound
Lamination
Factor , Min(%)
7.75
3.0
1.36
1.70
96.0
7.75
3.5
1.59
1.70
96.0
7.80
4.5
2.13
1.70
96.0
Note: The above test is conducted in accordance to IEC60404-2 (or JIS C 2550-2000), using as-sheared specimens
one half longitudinal and one half transverse to the rolling direction. Core loss and induction are measured after
stress relief annealing.
(Annealing condition : 750, 2Hr, under neutral atmosphere)
W15/50 indicates the core loss at the frequency of 50 Hz, magnetic flux density of 1.5T.
Thickness
mm (in.)
Thickness
Tolerance
mm (in.)
Thickness deviation in
transverse direction
mm (in.)
Width
Tolerance
mm (in.)
1000(39.37)
and under
0.5(0.0197)
0.040
(0.00158)
0.03(0.0012)
and under
+1.5(0.0591)
0
0.5(0.0197)
0.040
(0.00158)
0.04(0.0016)
and under
+1.5(0.0591)
0
1000(39.37)
and under
Camber
(Length 2m)
mm (in.)
1.0(0.0394)
and under
Note : The thickness deviation in width direction means the gap between the thickness of center and the one of part
15mm away from the edge part.
22
www.posco.com
Grade
Core Loss
Thickn
ess Density
mm (kg/dm3)
(in.)
Magnetic Flux
Density.Min
(T)
0.50
(0.0197)
0.50
(0.0197)
0.50
(0.0197)
B25
B50
37
1.29
2.70
1.72
3.71
0.59
1.35
0.78
1.68
1.66
1.73
33
1.36
3.05
1.83
3.91
0.62
1.38
0.83
1.77
1.67
1.74
25
1.73
3.89
2.22
5.11
0.79
1.77
1.01
2.32
1.63
1.72
50PNA300
50PNA350
50PNA450
Thickness
mm (in.)
0.50
(0.0197)
0.50
(0.0197)
0.50
(0.0197)
Yield Point
(N/mm2)
L
C
Tensile Stength
(N/mm2)
L
C
Elongation
(%)
L
C
Hardness
(Hv1)
402
415
260
269
37
39
141
382
401
268
278
36
38
124
380
381
269
270
39
39
117
Lamination
Factor
(%)
98.0
B50(T) 1.7
50PNA350
50PN400
50PN470
200
High Induction
Punchability
180
Hardness 160
(Hv1) 140
Better
120
2.5
3.0
3.5
W15/50(W/kg)
Through higher induction and punchability, PNA-core features higher efficiency of products and longer
life of dies.
23
PNS-Core
PNS-Core features lower core loss, high induction and good punchability with lower hardness
Standard Size
Product
PNS-Core
(Coil)
Grade
Width mm (in.)
Thickness
mm (in.)
0.35
(0.0138)
35PNS250
Available
Standard
950~1200
(37.40-47.24)
1000
(39.37)
1050
(41.34)
1100
(43.31)
Inside Diameter
mm (in.)
508
(20)
Specification
Magnetic properties and lamination factor.
Grade
35PNS250
Thickness
mm (in.)
0.35
(0.0138)
Density
(kg/dm3)
Magnetic Flux
Watt per kilogram Watt per pound Density.Min T(B50)
7.60
2.5
1.14
1.63
Lamination
Factor , Min(%)
95.0
Note: The above test is conducted in accordance to IEC60404-2 (or JIS C 2550-2000), using as-sheared specimens
one half longitudinal and one half transverse to the rolling direction.
W15/50 indicates the core loss at the frequency of 50 Hz, magnetic flux density of 1.5T.
Thickness
mm (in.)
Thickness
Tolerance
mm (in.)
Thickness deviation in
transverse direction
mm (in.)
Width
Tolerance
mm (in.)
1000(39.37)
and under
0.35
(0.0138)
0.035(0.00138)
0.02(0.0008)
and under
+1.5(0.0591)
0
1000(39.37)
and over
0.35
(0.0138)
0.035(0.00138)
0.03(0.0012)
and under
+1.5(0.0591)
0
Camber
(Length : 2m)
mm (in.)
1.0(0.0394)
and under
Note : The thickness deviation in width direction means the gap between the thickness of center and the one of part
15mm away from the edge part.
24
www.posco.com
Grade
Core Loss
Thickn
ess Density
mm (kg/dm3)
(in.)
Magnetic Flux
Density.Min
(T)
0.35
(0.0138)
56
0.98
2.25
1.22
2.83
0.45
1.02
0.55
1.29
B25
B50
1.57
1.66
Thickness
mm (in.)
Tensile Stength
(N/mm2)
L
C
35PNS250
0.35
(0.0138)
442
445
Yield Point
(N/mm2)
L
C
330
332
Elongation
(%)
L
C
23
25
Hardness
(Hv1)
Lamination
Factor
(%)
186
98.0
Electrical Steel
25
NO
General
Ecofriendly
0A
GS
General
C-6A
C-9A
GO
Applied Spec
Eco-friendly
NS
NM
Notice
NT
NO
Composition
Thickness (um)
15
15
0.5
5.0
0.5
15
15
0.1
0.5
0.1
95.0
95.0
98.0
98.0
98.0
Heat resistance
flaking after SRA
Weathering (powdering)
Brfore SRA
(Mandrel bend
tester)
Adhesion
(mm)
After
SRA(Cross cut
tester)
Change of
Resistance
surface
to
Change of
refrigerants
weight
Weldability
5.0
100
98.0
97.0
ASTM A 717
SRA
condition
:
750C2hrs. in DX rich gas
0.5 SRA Not Accepted
1.0MPa 0.05 in Pressure (JIS C 2550)
Not
Not
Not
Not
Not
Not
SRA Not
recogniozed recogniozed recogniozed recogniozed recogniozed recogniozed Accepted
15524hr in Air
Not
Not
Not
Not
Not
Not
SRA Not
recogniozed recogniozed recogniozed recogniozed recogniozed recogniozed Accepted
750
C2hrs.
in DX rich gas
Not
Not
Not
Not
Not
Not
Not
recogniozed recogniozed recogniozed recogniozed recogniozed recogniozed recogniozed
65 , 95% humidity,
72 Hr
30
30
10
5B
10
5B
10
ISO 1519
5B
ASTM D3359B
[0B (poor) ~ 5B
(excellent)] SRA:
Not
Not
Not
Not
recogniozed recogniozed recogniozed recogniozed
Not
Not
Not
Not
recogniozed recogniozed recogniozed recogniozed
excellent
excellent
5B
20
good
5B
10
good
R-134a/Freol @15C =
65g/100g
(130, 21day,0.45
filter paper)
Curreent : 100150A
Not Ar 99% flow1020L/minSpeed
allowed
0.250.50mpm
Note: 1) Please designate surface insulation according to usage. Regarding coating properties, please contact us.
2) The coating thickness value and the resistivity is typical value, not guaranteed.
26
www.posco.com
Annelaing
Stress relief annealing is a process that is carried out to acquire desired magnetic properties of electrical
steel sheets by relieving stress generated in the process of shearing and punching at a proper
temperature for a certain period of time.
Annealing Temperature
If the annealing temperature is too low, it is difficult to acquire adequate magnetic properties and if the
temperature is too high, it may erode surface insulation and degrade insulation properties. The
optimum annealing temperature for grain-oriented electrical steel is 780
C to 840
C and 750
C to 800
C for non-oriented electrical steel for improved magnetism.
Annealing Time
Annealing time means the in-furnace time of materials at the highest temperature during the annealing
process. During this time, the materials in the furnace should be evenly heated. The annealing time
varies depending upon amount of materials or type of furnace. Generally, the annealing time is
between 1.5 to 2.5 hours.
Furnace Atmosphere
Furnace atmosphere should be controlled to minimize carburization or oxidization which can diminish
magnetic properties. Therefore a pure nitrogen atmosphere is ideal and the dew point of gas should
be maintained as low as possible, below 0
C is adequate. The oil used in shearing and punching
should be removed completely. Otherwise both sides of piled-up core will be damaged during the
annealing process, deteriorating the work capacity.
Electrical Steel
27
45 Temp()
20
0
50
100
150
200
250
300
350
10
15
450
Humidity(%)
25
30
35
40
Dew
Point
90%
80%
70%
60%
50%
40%
30%
20%
10%
Water is condensed on the steel surface in certain temperature and humidity in store place and steel is likely to get
rusty.
Ex) In a place of 25, humidity 80%, water is condensed when temp decrease to 22.
28
www.posco.com
Electrical Steel
29
>>
Major International
Standards
The product standards are subject to change. Please be sure to confirm the recent standards when
making orders or to consult our associates.
JIS C 2553
ASTM
EN10107
(2006)
W/kg
17/50
(2000)
W/kg
17/50
(1999)
W/kg
17/60
(1995)
W/kg
17/50
23PHD085 0.85
23R085 0.85
23Q054 1.19
0.23
23PH090 0.90
23P090 0.90
(0.0091)
23PH095 0.95
23P095 0.95
23PH100 1.00
23P100 1.00
27PHD090 0.90
27R090 0.90
Thickness
mm
(inch)
23P060 1.32
M100-23P 1.00
27PH095 0.95
0.27
27PH100 1.00
27P100 1.00
(0.0106)
27PH110 1.10
27P110 1.10
27PG120 1.20
27G120 1.20
27PG130 1.30
27G130 1.30
M103-27P 1.03
27P066 1.46
27H074 1.63
30PH100 1.00
30PH105 1.05
M105-30P 1.05
30P105 1.05
0.30
30P110 1.10
M111-30P 1.11
(0.0118)
30P120 1.20
M117-30P 1.17
30PG130 1.30
30G130 1.30
30PG140 1.40
30G140 1.40
0.35
35PG145 1.45
35G145 1.45
(0.0138)
35PG155 1.55
35G155 1.55
30H083 1.83
M140-30S 1.40
35H094 2.07
M150-35S 1.50
Note : The core loss of POSCO products is the maximum guarantee value at 1.7T and 50Hz
30
M130-27S 1.30
www.posco.com
0.35
POSCO
JIS C 2552
ASTM
EN10106
(2006)
W/kg
15/50
(2000)
W/kg
15/50
(1999)
W/kg
15/60
(1995)
W/kg
15/50
35PN210 2.10
35A210 2.10
35PN230 2.30
35A230 2.30
36F145 3.20
M235-35A 2.35
35PN250 2.50
35A250 2.50
36F155 3.42
M250-35A 2.50
35PN270 2.70
35A270 2.70
36F175 3.86
M270-35A 2.70
35PN300 3.00
35A300 3.00
36F205 4.52
M300-35A 3.00
35PN360 3.60
35A360 3.60
35PN440 4.40
35A440 4.40
(0.0138)
50A230 2.30
50PN250 2.50
50A250 2.50
50PN270 2.70
50A270 2.70
M250-50A 2.50
M270-50A 2.70
47F165 3.64
50PN290 2.90
50A290 2.90
M290-50A 2.90
47F180 3.97
50PN310 3.10
50A310 3.10
M310-50A 3.10
47F200 4.41
50PN350 3.50
50A350 3.50
M350-50A 3.50
47F210 4.63
0.50
50PN400 4.00
50A400 4.00
M400-50A 4.00
47F240 5.29
(0.0197)
50PN470 4.70
50A470 4.70
50PN600 6.00
50A600 6.00
M470-50A 4.70
M600-50A 6.00
47F400 8.82
50PN700 7.00
50A700 7.00
M700-50A 7.00
47F450 9.92
50PN800 8.00
50A800 8.00
M800-50A 8.30
50PN1000 10.00
50A1000 10.00
M1000-50A 10.00
50PN1300 13.00
50A1300 13.00
Note : The core loss of POSCO products is the maximum guarantee value at 1.5T and 50Hz.
Electrical Steel
31
A/m
A/in
7.96 x 10
2.02
1.256 x 10-2
2.54 x 10-2
4.95 x 10-1
3.94 x 10
1 Oersted
1 Ampere per Meter
(A/m)
1 Ampere per Inch
(A/in)
Magnetic Induction
Gauss
Tesla
WB/m2
line/in2
1 Gauss(G)
10-4
10-4
6.45
1 Tesla(T)
104
6.45 x 104
104
6.45 x 104
1.55 x 10-1
1.55 x 10-5
1.55 x 10-5
Core Loss
32
W/kg
W/lb
1 Watt Per
Kilogram(W/kg)
4.54x10-1
1 Watt Per
Pound(W/lb)
2.204
www.posco.com
>> Packaging/Marking
PACKAGING / MARKING
Standard packing for domestic sales
MARKING
Domestic
Export
Electrical Steel
33
>>>
Contents
MANUFACTURING PROCESS AND FACILITIES 4
SPECIFICATION & MAIN APPLICATION 6
GRAIN-ORIENTED ELECTRICAL STEEL 8
NON-ORIENTED ELECTRICAL STEEL 14
SURFACE INSULATION 26
STRESS RELIEF ANNEALING 27
RELATIONS AMONG WEIGHT, OUTSIDE DIAMETER AND WIDTH OF COIL 29
MAJOR INTERNATIONAL STANDARDS 30
UNIT CONVERSION TABLES, THE INTERNATIONAL SYSTEM OF UNITS(SI) 32
PACKAGING/MARKING 33
GLOBAL NETWORK 34