CHAPTER 5
Abstract
Biomass material such as rice straw, banana leaves and teak leaves (Tectona grandis) could
be densified by means of wet briquetting process. Wet briquetting is a process of
decomposing biomass material up to a desired level under controlled environment in order to
pressurize to wet briquettes at a lower pressure. Upon drying these wet briquettes could be
used as solid fuels. This study is aimed at to develop methodologies to measure quality and
handling characteristics of these briquettes and burning characteristics as well.
5.1 Introduction
India produces yearly a large amount of agro residue such as rice straw, rice husk,
coffee husk, jute stick, coir pith, bagasse, groundnut shells etc. Some part of this agro residue
is used as animal fodder. A large amount of agro residue is left on the paddy fields to be burnt
or decomposed [Ponnamperuma et al., 1983]. Both ways are means of pollution to
environment, as field burning of agro residue emits a lot of GHGs to environment and
decomposition of the agro residue too produces methane gas which is considered of the GHGs
[Campbell et al., 2002; Sokhansanj et al., 2006]. Instead of letting these agro residues to be
burnt or decomposed, these could be converted to densified forms by briquetting method
[Stanely, 2003]. This will mitigate the problems of pollution while at the same time we would
be successful to trap this energy resource for industrial purposes. Briquettes are far better to
handle rather than loose biomass.
40
Recent Advances in Bioenergy Research, Vol. III 2014
then made into briquettes by casting and pressing. The second technology is direct extrusion
type, where the biomass is dried and directly compacted with high heat and pressure (Grover
and Mishra, 1994). The last type is called wet briquetting in which decomposition is used in
order to breakdown the fibers. On pressing and drying, briquettes are ready for direct burning
or gasification. These briquettes are also known as fuel briquettes [Stanley, 2003, Chou et al.,
2010, Saikia et al., 2013].
These fuel briquettes are the newest edition of briquettes manufactured at low pressure
unlike the others. As these briquettes are produced at relatively low pressure, a series of
quality test such as durability, compressive strength, shear strength, impact test and
combustion tests are needed to be done so that they could be more competitive with existing
types.
Durability, shear strength and impact resistance of briquettes are the basic parameters to
assess the quality of briquettes in terms of handling and transportability of fuel briquettes
(Grover and Mishra, 1994). .
5.2.1 Durability
Durability of briquettes gives the mechanical handling of the solid fuel (Chou, 2009).
This is measured by standard procedure ASAE S269.4 [Kaylyan et al]. To measure durability,
100 g of sample is taken and sample is tumbled at 50 rpm for 10 minutes in a dust tight
enclosure of size 300mm300mm. Metal cloth of aperture size 4mm is used to retain
crumbled briquettes after tumbling.
!" #$ %&'() ) & " $'*) + ,
Briquettes durability index in % given by= ," +&) *" #$ %&'() ,
100
Durability test set up: Working principle: The test set up is fabricated according to
specification of ASAE S269.4 (Temmerman et al., 2006). The set up consists of a box 300
mm 300 mm 125 mm mounted on a frame. The box can be rotated by wooden handle or a
motor at 50 rpm for 10 minutes which simulates the probable conditions of briquettes under
transport by truck or conveyer belt into furnace. Figure below shows a durability measuring
test set up made according to specification.
To measure shear strength, a simple test is done. Briquette is sheared between two
planes and shear force developed is the shear strength of briquette (Saikia and Baruah, 2013).
41
Recent Advances in Bioenergy Research, Vol. III 2014
Shear strength test set up: To measure shear strength, shearing test set up has been
fabricated. The instrument consists of three wooden plates. The middle plate with a central
cylindrical hole of 45 mm diameter and 30 mm thickness slides over the bottom plate. In the
top plate, a cylindrical hole of same diameter as that of moving plate with 20 mm thickness is
being provided in such a way that it coincides with the one that is provided in the movable
plate when this plate is fully inserted between top and non moving bottom plate. The movable
plate is connected to dead weights.
2F
Shear strength, kPa =
D2
This test simulates the forces encountered during emptying of densified products from
trucks onto ground, or from chutes into bins. Drop tests can be used to determine the safe
height of briquette production during mass production (Debdoubi A. et al., 2005). ASTM
D440-86 method is used to determine impact resistance index (Kaliyan N. and Morey R.V.,
2008).. In the drop test, briquettes are dropped twice from a height 1.83 m onto a concrete
floor. An impact resistance index (IRI) is calculated.
100N
IRI = n
Where, N= Number of drops, n= Total number of pieces. The upper limit of IRI is 200 which
would result if the briquettes are not broken even after dropping twice.
42
Recent Advances in Bioenergy Research, Vol. III 2014
Proximate analysis and combustion rates of briquettes were done to assess effectiveness
of briquettes as cooking fuel.
Moisture Content: The moisture content is determined according to the method described in
the Forestry Hand Book (Wenger, 1984). 10 g of sample is taken immediately upon sampling
and then air dried. This air- dried sample is taken immediately in an aluminum moisture box
and kept in an oven heated at 105 3 C until constant weight is obtained. The difference of
the oven dry weight of the sample and the fresh weight of the sample is used to determine the
percentage of moisture content as follows:
-" % ,. + /"0
Moisture content, % = 100
-" %
Ash content: For determination of ash content, ASTM Test No. D-271-48 is followed. At
first, an empty 25 ml. silica crucible as well as the sample is heated in a moisture oven.
Sample is weighed accurately to 2 g. The sample in the crucible is kept in muffle furnace with
the lid cover. Muffle furnace temperature is set at 550 50C and kept for 6 hours. After 6
hours of burning crucible is removed from the furnace and placed in a desiccators and
weighed accurately. Percentage of ash content was calculated as follows:
Weight of ash
Ash content, % = Weight of sample 100
Volatile matter: Volatile matter of samples is determined by ASTM Test No. D- 271- 48. A
clean platinum crucible of 10 ml. capacity is taken and heated in a furnace at 950C for 2
minutes and cooled in desiccators for 15 minutes. Crucible weighed to nearest 0.1 mg.
Sample filled crucible is weighed and heated in a furnace at 950C for 2 minutes. After
volatile matter escaped, the crucible is removed from furnace and cooled in air 2 to 5 minutes
and then in desiccators for 15 minutes. The percentage of weight loss of the samples is
reported as volatile matter as follows:
Wt. loss of dry sample
VM= 100
Net wt.of dry sample
Wt. loss of wet sample 100
Gross wt. of wet sample
VM= 100 (Wet samples)
100- percent moisture
43
Recent Advances in Bioenergy Research, Vol. III 2014
Combustion rate or burning rate is the mass loss per unit time. The briquettes are dried
at 105C so that it does not affect on combustion or burning. Dried briquette is placed on a
steel wire mesh grid resting on three supports allowing free flow of air (Chaney J. O.et al. ,
2010) Now the whole system is placed on mass balance. Briquette is ignited from top and
mass loss data is taken at an interval of 30 seconds.
44
Recent Advances in Bioenergy Research, Vol. III 2014
Briquette
Steel wire mesh
Electronic mass
Stop watch
balance
5.4 Conclusion
With the help of this study we aim to standardize the practice of briquette making for
the commercial purpose. Generally, there are very few literatures on the standardization of
quality testing methodologies of briquettes and burning characteristics as well. Durability,
shear strength and impact resistance of briquettes could be determined easily as discussed in
the section II in order to assess the quality of briquettes in terms of handling and
transportability. Higher the durability, impact resistance and shear strength, higher will be the
handling characteristics. But we need to reach at an optimum value of these indexes in order
to produce quality briquettes at a cost effective way as quality always adds cost to production.
Similarly, we can also asses the burning rates of briquettes in room condition as discussed in
the section III. This generally helps to build a rough idea of performance of briquettes in
actual condition. Moreover, with the knowledge of burning rates, we can further manipulate
parameters of briquette manufacturing such a density and porosity of briquettes in order to
obtain a desired level of burning rate. Apart from that proximate analysis and calorific value
tests will so help us to give answer to some of the questions regarding the fuel such as
whether it produces too much harmful fly ash and unwanted gases which are general indoor
air pollutants many households and effectiveness of the fuel in terms of heat value. A fuel
without heat value would be useless as a lot of fuel will be needed during use for its lower
heat value.
References
45
Recent Advances in Bioenergy Research, Vol. III 2014
2. Kaliyan N. and Morey R.V. (2008). Factors affecting strength and durability of
densified of biomass products, Biomass and Bioenergy, Vol 33, pg 337-359.
3. Wenger (1984). Forestry Hand Book.
4. Chaney J. O., Clifford M. J., Wilson R. An experimental study of the combustion
characteristics of low-density biomass briquettes. Biomass magazine 2010, Vol 1.
5. Grover P.D. and Mishra S.K. (1994). Development of an appropriate biomass
briquetting technology suitable for production and use in developing countries Energy
for Sustainable Development, Vol 1.
6. Faborod M. 0 (1987).Optimizing the Compression/Briquetting of Fibrous Agricultural
materials, Journal of agricultural. Engineering Resources, Vol 38, pg 245-262.
7. Chen L. (2010). The development of agro-residue densified fuel in China based on
energetics analysis, Waste Management, Vol 30, pg 808813.
8. Suramaythangkoor T. and Gheewala S.H. (2010). Potential alternatives of heat and
power technology application using rice straw in Thailand, Applied Energy, Vol 87, pg
128133.
9. Chou CS, Lin S.H., Peng C.C. and Lu W.C. (2010).The optimum conditions for preparing
solid fuel briquette of rice straw by a piston-mold process using the Taguchi method,
Fuel Processing Technology, Vol 90, pg 10411046.
10. Mania S., Tabil L.G. and Sokhansanj S. (2006). Effects of compressive force, particle
size and moisture content on mechanical properties of biomass pellets from grasses,
Biomass and Bioenergy, Vol 30, pg 648654.
11. Chou C. S. (2009). Preparation and characterization of solid biomass fuel made from
rice straw and rice bran, Fuel Processing Technology, Vol 90, pg 980987.
12. Singh R.N. (2004). Equilibrium moisture content of biomass briquettes, Biomass and
Bioenergy, Vol 26, pg 251 253.
13. Demirba A. (1997). Evaluation of biomass residue briquetting waste paper and wheat
straw mixtures, Fuel Processing Technology Vol 55, pg 175183.
14. Parikh Jigisha, Channiwala S.A. and Ghosal G.K. (2005). A correlation for calculating
HHV from proximate analysis of solid fuels, Fuel, Vol 84 (2005), pg 487494.
15. Bamgboye I. and Bolufawi S.J. (2009). Physical Characteristics of Briquettes from
Guinea Corn (sorghum bi-color) Residue, Agricultural Engineering International: the
CIGR Ejournal.
16. Husain Z., Zainac Z. and Abdullah Z. (2002). Briquetting of palm Fiber and shell from
the processing of palm nuts to palm oil, Biomass and Bioenergy, Vol 22, pg 505 509.
46
Recent Advances in Bioenergy Research, Vol. III 2014
17. Kumar N., Patel K., Kumar R.N. and Bhoi1 R.K. (2009). An assessment of Indian fuel
wood with regards to properties and environmental impact, Asian Journal on Energy
and Environment, Vol 10(02), pg 99-107
18. Saikia M. and Baruah D. (2013). Analysis of Physical Properties of Biomass Briquettes
Prepared by Wet Briquetting Method, International Journal of Engineering Research
and Development Volume 6, Issue 5 (March 2013), PP. 12-14.
19. Bikash B. Bhowmik R. and Saikia M. (2013). Challenges of Wet Briquetting from
Locally Available Biomass with Special Reference to Assam, International Journal of
Computational Engineering Research , Vol, 03, Issue, 7.
47