    This document provides technical specifications for the steel grade 20MnCrS5 N° 1.7149. It includes information on chemical composition ranges, mechanical properties, heat treatment processes, hardness values at various stages, and expected mechanical properties under different conditions. The steel can be supplied with an addition of lead, and some property values are provided for reference only and were obtained from test samples.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Technical Card Gruppo Lucefin Revision 2014 All Rights Reserved

    Uploaded by

    Daniel Riveros
    79 views2 pages
    This document provides technical specifications for the steel grade 20MnCrS5 N° 1.7149. It includes information on chemical composition ranges, mechanical properties, heat treatment processes, hardness values at various stages, and expected mechanical properties under different conditions. The steel can be supplied with an addition of lead, and some property values are provided for reference only and were obtained from test samples.

    Original Description:

    Important material technical sheet.

    Original Title

    20mncr5en19

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides technical specifications for the steel grade 20MnCrS5 N° 1.7149. It includes information on chemical composition ranges, mechanical properties, heat treatment processes, hardness values at various stages, and expected mechanical properties under different conditions. The steel can be supplied with an addition of lead, and some property values are provided for reference only and were obtained from test samples.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    79 views2 pages

    Technical Card Gruppo Lucefin Revision 2014 All Rights Reserved

    Uploaded by

    Daniel Riveros
    This document provides technical specifications for the steel grade 20MnCrS5 N° 1.7149. It includes information on chemical composition ranges, mechanical properties, heat treatment processes, hardness values at various stages, and expected mechanical properties under different conditions. The steel can be supplied with an addition of lead, and some property values are provided for reference only and were obtained from test samples.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    TECHNICAL CARD

    According to standards
    GRUPPO LUCEFIN
    REVISION 2014
    Number
    ALL RIGHTS RESERVED



    max max max
    0,170,22 0,40 1,101,40 0,025 0,035 1,001,30 Product deviations are
    0.02 + 0.03 0.05 + 0.005 + 0.005 0.05 allowed
    20MnCrS5 N 1.7149 S% 0.0200.040 permissible deviation on the product 0.005%
    On request, this steel grade may be supplied with addition of lead (Pb) 0.150.35%



    1150850 860880 860890 750930 880980 810840 150
    air oilpolymer gas oilpolymer 200
    (HB 140201) salt bath salt bath


    650700 860 furnace 720740 furnace 870 welding must be carried out on the annealed state
    furnace cooling cooling to cooling to 670, water and before carburizing
    650, then air pause, 150350 600 furnace cooling
    cooling to 300, *core
    then air **carburizing surface
    730 830 390* 200**
    (HB max 217) (HB 170217) (HB 152201)

    9501000 quick cooling to 620650, stop according to 600620
    the thickness of the material, then air (HB 152201) (HB max 230)

    values obtained on test blanks after core hardening + stressrelieving UNI 7846: 1978. Use only as reference
    size Testing at room temperature (longitudinal)
    mm 0.2
    test blanks N/mm2 N/mm2 min. min. J min.
    11 12301570 930 7 17.5
    30 9301230 690 8 20 for information only
    63 7801080 540 9 25 for information only
    values obtained at room temperature on rounds of 10 mm after quenching at 870 C in oil
    426 426 421 421 415 409 395 381 362 336 294 261 240 224
    45.5 45.5 45 45 44.5 44 42.5 41 39 36 31 26.5 22.5
    N/mm2 1500 1500 1490 1480 1460 1430 1370 1300 1210 1100 980 875 795 740
    0.2 N/mm2 1060 1140 1190 1230 1240 1240 1220 1180 1090 960 850 750 670 600
    % 11.5 11.9 12.0 12.0 11.9 11.8 11.9 12.2 12.8 14.0 16.0 18.8 21.8 23.2
    % 48 49 50 52 53 55 56 58 60 62 64 67 70 72
    J 38 40 40 40 38 38 32 34 75 75 100 128 145 155
    carburizing 64.5 64 63 60.5 59 57
    Tempering at
    1.7149 EN 102774: 2008
    size mm Soft annealing +A +SH Soft annealing +A +C Heat treatment +FP +SH Heat treatment +FP +C
    for pearlite / ferrite for pearlite / ferrite
    +SL
    from to max max
    5 a) 10 270
    10 16 260
    16 40 217 255 152201 152250
    40 63 217 250 152201 152245
    63 100 217 250 152201 152245
    a) for thickness < 5 mm, mechanical properties should be agreed before order placement

    UNI 8550: 1984. Use only as reference


    size mm Testing at room temperature (longitudinal)
    0.2
    from to N/mm2 N/mm2 min min (L) J min (L)
    11 12251570 930 7 17.5
    11 25 9301225 685 8 20
    25 50 7851080 540 9 25
    Mechanical properties obtained on test blanks after core hardening + stressrelieving
    L = longitudinal
    EN 10084: 2008 grain size 5 min.
    mm distance from quenched end

    41 39 36 33 30 28 26 25 23 21 normal
    49 49 48 46 43 42 41 39 37 35 34 33 32
    44 42 40 37 34 33 31 30 28 26 25 24 23
    49 49 48 46 43 42 41 39 37 35 34 33 32
    41 39 36 33 30 28 26 25 23 21
    46 46 44 42 39 37 36 34 32 30 29 28 27
    106 K1 11.1 12.1 12.9 13.5 14.1
    long. GPa 210 205 195 175 155
    tang. GPa 80 78 75 67 59
    J/(KgK) 460
    W/(mK) 41
    Kg/dm3 7.85
    Ohmmm2/m 0.16
    Siemensm/mm2 6.25

    The symbol indicates temperature between 20 C and 100 C, 20 C and 200 C


    EN UNI GB DIN AFNOR B.S. GOST AISI/SAE
    20MnCr5 20MnCr5 20CrMn 20MnCr5 20MC5 20HG 5120