STP 1425
ASTM International
100 Barr Harbor Drive
PO Box C700
West Conshohocken, PA 19428-2959
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Library of Congress Cataloging-in-Publication Data
ISBN:
TA460.F72 2003
620.1'66--dc21
2003041827
Copyright 9 2003 AMERICAN SOCIETY FOR TESTING AND MATERIALS INTERNATIONAL, West
Conshohocken, PA. All rights reserved. This material may not be reproduced or copied, in whole or
in part, in any printed, mechanical, electronic, film, or other distribution and storage media, without
the written consent of the publisher.
Photocopy Rights
Each paper published in this volume was evaluated by two peer reviewers and at least one edi-
tor. The authors addressed all of the reviewers' comments to the satisfaction of both the technical
editor(s) and the ASTM International Committee on Publications.
To make technical information available as quickly as possible, the peer-reviewed papers in this
publication were prepared "camera-ready" as submitted by the authors.
The quality of the papers in this publication reflects not only the obvious efforts of the authors
and the technical editor(s), but also the work of the peer reviewers. In keeping with long-standing
publication practices, ASTM International maintains the anonymity of the peer reviewers. The ASTM
International Committee on Publications acknowledges with appreciation their dedication and con-
tribution of time and effort on behalf of ASTM International.
Printed in Bridgeport, NJ
March 2003
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Foreword
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Contents
Overview ix
INVITED PAPER
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LIFE PREDICTION
TITANIUM A L L O Y S
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Evaluation of Ti-48AI-2Cr-2Nb Under Fretting Conditions--K. MIYOSHI,
B. A. LERCH, S. L. DRAPER, AND S. V. RAJ 323
SURFACE TREATMENT
The Analysis of Fretting Fatigue Failure in Backup Role and Its Prevention--
M. KUBOTA, H. O D A N A K A , C. SAKAE, Y. OKOMORI, AND Y. K O N D O 434
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Overview
The Third International Symposium on Fretting Fatigue was held in Nagaoka, Japan on
May 15-18, 2001. This symposium is a follow-up to the First International Symposium on
Fretting Fatigue held at the University of Sheffield in April 1993 (see Fretting Fatigue, ESIS
Publication 18, edited by Waterhouse and Lindley, 1994) and the Second International Sym-
posium on Fretting Fatigue held at the University of Utah on August 31, 1998 (see Fretting
Fatigue: Current Technology and Practices, ASTM STP 1367, edited by Hoeppner, Chan-
drasekaran and Elliott, 2000). Fretting is well known to degrade fatigue strength significantly.
Fretting fatigue failure has been increasingly disclosed in service components because those
components have suffered more severe loading conditions than before due to the demands
of save-energy and environment-preservation. One of major magic behaviors in fretting fa-
tigue problems will be that a micro-slip between two combined components occurs under
service loading, while such a slip is never expected at the designing stage. Great efforts have
been devoted for understanding the fretting fatigue phenomenon and for developing the
fretting fatigue design. This symposium was organized to focus on the progress in basic
understanding and application and to continue the extensive interchange of ideas that has
recently occurred.
Fifty-seven delegates from seven countries attended the symposium to present papers and
participate in lively discussions on the subject of fretting fatigue. Dr. Waterhouse, who did
pioneering research since the 1960s and is well known as a father of fretting research, was
invited to this symposium. Technical leaders in the area of fretting fatigue were in attendance
from most of the leading countries that are currently involved in fretting fatigue research,
development, and engineering design related matters, as well as failure analysis and main-
tenance engineering issues. ASTM International Committee E8 provided the ASTM Inter-
national organizational support for the symposium. The collection of papers contained in
this volume will provide as an update to a great deal of information on fretting fatigue. This
volume surely serves engineers that have a need to develop an understanding of fretting
fatigue and also serves the fretting fatigue community including both newcomers and those
that have been involved for some time.
The Symposium was sponsored by the following organizations as well as ASTM Inter-
national: 1) Materials and Processing Division of JSME, 2) MTS Systems Corporation, 3)
SHIMADZU Corporation, 4) HITACHI Ltd., and 5) JEOL Ltd.
All of the above organizations provided valuable technical assistance as well as financial
support. The Symposium was held at Nagaoka Grand Hotel in the center of Nagaoka city,
which is famous for fireworks and excellent rice and related products, such as Japanese sake
and snacks. Many of the delegates would enjoy them.
The organizing committee members were: Dr. Yoshiharu Mutoh, Chair (Japan), Dr. David
Hoeppner (USA), Dr. Leo Vincent (France), Dr. Toshio Hattori (Japan), Dr. Trevor Lindley
(UK), and Dr. Helmi Attia (Canada). At the conclusion of the symposium, the organizing
committee announced that the next symposium would be held a few years after this sym-
posium in France with Dr. Vincent as coordinator and chair.
Editing and review coordination of the symposium was done with the outstanding coor-
dination of Ms. Maria Langiewicz of ASTM International. The editors are very grateful to
her for her extensive effort in assisting in concluding the paper reviews and issuing this
volume in a timely manner.
ix
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
X FRETTINGFATIGUE: ADVANCES
The symposium opened with remarks by the symposium chair. Subsequently, Dr. Robert
Waterhouse gave the distinguished invited lecture on Fretting in Steel Ropes and cables. Six
keynote lectures were given in the following sessions, which were "Fretting wear and crack
initiation", "Fretting fatigue crack and damage", "Life prediction", Fretting fatigue param-
eter effects", Loading condition and environment", Titanium alloys", "Surface treatment",
and "Case studies and applications". Forty-three papers were presented and this volume
contains twenty-nine of those papers.
The new knowledge about the process of fretting crack nucleation under fretting wear was
provided through both detailed in-situ observations and mechanical models, which included
not only fracture mechanics but also interface mechanics. Fretting fatigue crack propagation
under mixed mode was discussed based on fracture mechanics approach. However, small
crack problems, especially those related to threshold and under mixed mode, are still re-
mained for future efforts. Fretting fatigue life estimations were attempted based on various
approaches including fracture mechanics, notch fatigue analysis and multiaxial fatigue par-
ameters. A number of factors are well known to influence on fretting fatigue,behavior and
strength. Effects of those parameters, which included contact pressure, friction coefficient,
contact pad geometry, mating material and so on, were discussed. Effect of loading condi-
tions including block loading, high frequency and service loading was also presented. The
knowledge about loading wave effect has been limited until now. Improvements of fretting
fatigue strength by using coating techniques were presented. Titanium alloys have been
typically used for structural components suffering fretting fatigue, such as turbine compo-
nents and bio-joints, due to their lightweight as well as excellent corrosion resistance. A lot
of works on this material including a review paper were presented to understand fretting
fatigue behavior in various conditions. Case studies on electrical cables, dovetail joints, pin
joints and rollers were introduced. Methods for bridging between specimen-based research
works and case studies are required, when a fretting fatigue test method would be standard-
ized. These topics will be also important future work.
This publication is only one aspect of the symposium. The sessions and discussions con-
tribute greatly to the mission of the symposium. The effort of the co-chairmen of the sessions
is acknowledged and appreciated. The editors are thankful to the attendees of the symposium
for interesting points and useful comments they made during the discussions that followed
the paper presentations. Their enthusiasm to follow up this symposium with the next sym-
posium in France is appreciated and well taken. The editors hope that those concerned with
the subject of fretting fatigue will find this publication useful and stimulating.
Y. Mutoh
Nagaoka University of Technology
Nagaoka, Japan
Symposium co-chairman and editor
D. W. Hoeppner
University of Utah
Salt Lake City, UT
Symposium co-chairman and editor
S. E. Kinyon
MTS Systems Co.
Eden Prairie, MN
Editor
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
INVITED PAPER
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Robert B.Waterhouse i
REFERENCE: Waterhouse, R. B., "Fretting in Steel Ropes and Cables--A Review," Fretting
Fatigue: Advances in Basic Understanding and Applications, STP 1425, Y. Mutoh, S. E. Kinyon,
D. W. Hoeppner, and, Eds., ASTM International, West Conshohoeken, PA, 2003.
Abstract: The numerous inter-wire contacts in ropes and cables are potential sites for
nucleation of fatigue cracks by fretting. At larger amplitudes of movement excessive
wear can occur leading to decreased cross-section of a wire and increased stress, or if
debris accumulates, forcing apart of the wires. In locked coil ropes this can cause local
stiffness and ingress of eorrodants. The wires themselves have.an asymmetric residual
stress distribution circumferentially resulting from the drawing process. The position of
an inter-wire contact relative to this greatly influences the fretting fatigue strength. Hot
dip galvanising reduces these stresses as well as giving cathodic protection. Local
friction is reduced by incorporating a lubricant in locked coil ropes. Conventional
grease-based lubricants with high shear strength are most effective in reducing friction
but recent experiments with a lower viscosity oil containing graphite show promise
Introduction
The great virtue of ropes and cables fabricated from steel or other metal wires, is their
flexibility which allows them to be wound on drums or passed over pulleys and sheaves,
combined with their great strength, which under tension, often approaches that of the
individual wires. They are therefore widely used in the construction industry as the
support in suspension and cable-stayed bridges and also in the roofs of some buildings.
The lifting ropes of cranes and elevators are a further application. In marine engineering
they are used as hawsers, rigging and as anchor and mooring ropes. The involvement of
the author with the latter has been with the mooring of the off-shore oil rigs, which are
tethered with four ropes the size of tree thinks at each comer. In mountainous countries
ski-lifts and cable cars which cater for the recreational and tourist trades are entirely
dependent on steel cables. In some instances they provide the compressive stress in post-
tensioned concrete beams [1]. A further use, which has developed in more recent years,
is as strengthening in the bead, belt and carcass areas &pneumatic automobile radial
tyres. These are very different from the traditional steel rope in that they consist of two
or three wires of diameter 0.t 5 to 0.38mm of strength 2300 to 3000MPa which are brass
plated to bond with the rubber [2]. The optimum design for a two-filament cord with
superior fatigue resistance is for one to be maintained straight and the other to be wound
around it [3].
3
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
4 FRETTINGFATIGUE: ADVANCES
In all these applications there are obviously an astronomically high number of inter-
wire contacts and therefore the possibility of fretting under operating conditions is
absolutely certain. The question is to what extent does fretting prejudice the function of
a particular rope? Some evidence is available from the examination of ropes taken from
a motorway bridge over the Norderelbe, which had been in service for 25 years. They
were tested in static and dynamic loading and showed remarkable remaining fatigue life
and carrying capacity [4]. However it was stated that fretting had a dominating influence
on damage extension. As failure is initiated by the fracture of an individual wire, the
total failure of a rope is usually apparent before it actually occurs particularly if there is
some system in force to detect individual wire failures. For this reason catastrophic
failures are relatively rare.
(a) (b)
20 m m i 9
Figure 1 - Types of locked coil ropes: (a) half lock 189 (b)full lock 2x
Design of ropes
Ropes are divided into two categories, single strand and stranded. The simplest rope
is where six wires of circular diameter are wound around a central (king) wire. In a
stranded rope such strands are further wound together in combinations of increasing
complexity. The author's experience has been entirely with single strand ropes
consisting of a much larger number of wires. In the case of the mooring ropes for the
off-shore oil rigs the wires were 5mm dia. wound in close packed layers with succeeding
layers being obliquely inclined to each other. This results in the inter-wire contact in the
same layer being a line contact whereas the contact between wires in adjacent layers
being a so-called "trellis" contact. The rope consisted of several hundred wires and was
filled with bitumen and encased in a thick polymer coating so that its overall diameter
was some 24cm, like a tree-trunk. Since they were operating in seawater with the
possibility of outward damage and penetration of seawater, the wires were hot-dipped
galvanised. In other ropes particularly lift ropes and those for cable cars, they were of
the locked coil type where the wires in the external layers were shaped to fit together to
form almost solid sheets. Figure 1 shows some examples. With such ropes a lubricant
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
WATERHOUSE ON FRETTING IN STEEL ROPES/CABLES 5
can be incorporated within the rope and this is an important factor in the prevention of
fretting. Power cables consist of a central steel strand surrounded by three layers of
aluminium wires (Figure 2). In some cases the central strand may also be of aluminium.
Another design of rope which is favoured in Japan, is the parallel wire strand rope which
consists of a bundle of parallel wires which is given a certain amount of twist. This has
the advantage of avoiding trellis inter-wire contacts (Figure 3).
~
~ LAYE~3
LAyI~2
Although fretting on line contacts will have an effect on the fatigue behaviour of a
rope, the effect of trellis contacts is much greater because they are localised and the
contact stresses are consequently much higher than on line contacts. Hobbs and Raoof
[5] and Raoof [6] separately have conducted detailed analyses into the conditions at such
contacts when the rope is subjected to tensile, torsional and bending stresses. Applying
this to a single strand mooring rope, the theory indicates that internal wire fractures occur
prior to external fractures and that they are located at trellis point contacts between an
outermost wire and the layer immediately below. This has been found to be the case in
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
6 FRETTINGFATIGUE: ADVANCES
locked coil ropes [7,8]. Figure 4 shows fretting marks on a wire from a single strand
rope and Fig 5 shows fatigue cracks generated at such marks in a laboratory test. Since
the amplitude of the fretting movement is extremely small the situation is that of partial
slip with the cracks developing at or towards the edge of the contact spot as in his
example, If however the movement becomes larger, fretting wear may occur and failure
may result from increased stresses at the reduced cross-section, Fig 7. Fatigue tests on
ropes confirm that fractures occur at trellis points [9].
Figure 4 - Wire from rope with fretting marks from a trellis contact
One of the problems in fatigue testing ropes and individual wires is gripping the ends
of the specimen in such a way as to prevent fretting failure in the anchorage or grips.
Related to this factis the observation that failures in power cables are usually located in
the vicinity of clamps near pylons [10]. Anchorages are obviously important in the
construction of suspension bridges and the topic has been dear with in detail by Chaplin
[11]. The development of zero-loss anchorages in which either the relative
Displacements or atmospheric oxygen is eliminated such that fretting corrosion is
reduced to an insignificant level results in the fatigue strength not being diminished [12].
The design of a rope also influences the fatigue behavior in service. In locked coil ropes
the 2x arrangement attains 80% higher service life than the 1 1/2x (Fig 1). This is
attributed to the larger contact areas in the former [7].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
WATERHOUSE ON FRETTING IN STEEL ROPES/CABLES 7
The Wires
In the construction of a rope or cable the wires themselves are the vital component.
In steel ropes the wires are high strength eutectoid or hypereutectoid steel which is
drawn down through twelve or thirteen dies. Solid lubricants are applied during the
drawing process. The original steel rod is passed through a zinc phosphate bath which
deposits an iron-zinc conversion coating and then through a 20% sodium tetraborate bath
to neutralize the acid from the phosphate bath and also acts as a sealant and finally
powdered sodium stearate is applied as a solid lubricant. Remnants of this treatment on
the surface of the wire have some effect in the eventual fretting contacts. The wire is
drawn at an angle to the final die so that the wire forms a coil, It is the residual stress
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
8 FRETTING FATIGUE: ADVANCES
thus introduced that has a major influence on the properties of the wire. The level of the
residual stress is also governed by the degree of reduction in the final die. A further
metallurgical complication which may occur is decarburization often traceable back to
the original billet.
MPa
-500
tlJ
B
-4oo B
/%,
! k'.
C ..-'"OIA 2oo~ / X~..c~
Y I O0 /,"
~-/ , .... , - -
500 i
i % REDUCTION
135
no4oo 012
i \ Z& 26.5
3o~
t~
7, q
~= 2oc
t~
Figure 8 shows the residual stress pattern round the circumference of a 5 mm alia
wire. The residual stress has a maximum tensile value at the ends of a diameter
perpendicular to the plane of the coil of the wire (B position). On the convex surface the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
WATERHOUSE ON FRETTING IN STEEL ROPES/CABLES 9
stress is compressive (A position) and a lower tensile stress on the concave surface. On
straightening the wire the latter two stresses both increase as indicated in Figure 8. The
level of these stresses also depends on the degree of reduction in the final die, which is
shown in Figure 9 for the B position. Hot dip galvanizing greatly reduces the stresses
and this is included in Figure 9 where the wire has been given a heat treatment
comparable with the galvanizing process.
The fretting fatigue behavior of individual wires depends on the location of interwire
contact points in relation to the residual stress pattern, which is shown in Figure 10. The
higher tensile stress at position B is where a crack will initiate leading to a lower fatigue
strength. The level of stress also has its expected effect Figure 11. The beneficial effect
of the galvanizing heat treatment should be noted.
400
n~ 350 POSITION
0 B
U3 A A A-C
30o
rY
~ 25c
Z
t--
z~ 20C
n.-
"t
< 150
I00 I
0-,.
! I
10s 106 107
CYCLES TO FAILURE
Environment
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
10 FRETTINGFATIGUE: ADVANCES
400
0_2
~176176
'Ok *1, REDUCTION
n~ 350 k [] 5
~ O 12
\ 26.5
<150
100
I I
lo 6 lo7
CYCLES TO FAILURE
One of the dangers of fretting in ropes besides that of initiating fatigue cracks, is that
fretting wear may occur producing oxide debris which is of greater volume than the
metal consumed in its creation. This can cause the wires to be forced apart so that
ingress of the environment is more likely and the increase in coefficient of friction
between the wires leads to local stiffness in the rope which becomes apparent if it is
passing over a pulley or sheave. Lubricants are incorporated to ensure inter-wire friction
remains low. Those in use are proprietary products whose composition is not divulged.
However, a study by the author of five of these materials allowed them to be ranked in
their ability to improve resistance to fretting fatigue failure. The increase in the fretting
fatigue strength of the wires by their application ranged from 7.5 to 32%. The properties
of the best lubricant were a high drop point, low unworked penetration and a high shear
strength and resistance to shear i.e. a low increase in penetration on working, and a high
value of shear strength in an extrusion test. Zhou et al have investigated the effect of a
proprietary reversible protective grease on the fretting behaviour of an electrical
conductor in cyclic bending and found a decrease in contact wear and particle oxidation
together with shorter fretting cracks and a higher service life [15].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
WATERHOUSE ON FRETTING IN STEEL ROPES/CABLES 11
300
\
"•200
7
F-
Z
ioo
0 AIR
9 SEAWATER
V SEAWATER +C.P.
I I
10~ 10s 106 10?
CYCLES TO FAILURE
Since the main purpose of lubrication is to reduce the coefficient of friction, it was
decided to measure friction in fretting wear tests rather than fatigue testing. Tests on the
as received 2.8 mm dia wire, so-called "bright wire" with the remnants of the drawing
lubricant on the surface showed that the latter resulted in low friction of 0.15 for the
initial 3000 to 5000 cycles after which it rose to 0.65. When the wire was abraded the
friction was 0.65 from the start. After 100 000 cycles the friction rose steadily to 0.9,
Figure 14. Contact resistance measurements indicated that this was due to the
accumulation of debris, A suspension of graphite in a low viscosity paraffinic oil
smeared on to the wire surfaces maintained a friction of 0.15 for the duration of the test,
300 000 cycles, Figure 15 [16]. Further experiments with chopped carbon fibre and
Kevlar in a paraffinic oil were less successful. The Kevlar actually produced surface
damage by indenting the hard steel surface.
Surface Treatment
The standard and most effective method of dealing with fretting problems is to apply
some form of surface treatment such as shot-peening, ion implantation or coatings. To
employ such methods in the case of wire ropes is difficult practically and not viable
economically. However the problem has been tackled by a group in Australia with a
proposal to apply coatings using contact resistance heating between a roller and the wire
and feeding in a powder of the coating material [18]. Tests have shown that a promising
coating is molybdenum which when applied by PVD provided useful wear resistance
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
12 FRETTINGFATIGUE: ADVANCES
[ | i i i i i ]
O:.'g
o I*
t_J
-7 /
Y C a : 260 MPa
R :0.3
g S Hz
o AIR
9 SEAWATER
9 C.R(~850 mV,SCE)
0.8
0
0 o ~ + ~ +.
~ 0.6
+~
O
Number of cycles
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
WATERHOUSE ON FRETTING IN STEEL ROPES/CABLES 13
although the friction remained high at 0.7. Whether this would have any beneficial
effect on fatigue has yet to be demonstrated.
1 X Graphite powder
0,9 4cSt + graphite
.o 0.8 O 20cSt + graphite ~x•
y, 0,7
X
0.6 o
0.5
X X xxX
r 0.4 x Oco(P o ) ~
0.3 o ~ 1 7 6 1 7 6 o1 7 6 oo
,~ o
o 0.2 o ,~
Number of Cycles
.... iO0~o 9 ' 1-~x)o
Conclusion
In a survey of the future development of cables and ropes particularly for bridges
Gourmelon has suggested that materials which are insensitive to fretting should be
explored [18]. Aramid fibre cables have the required tensile strength comparable with
steel i.e. 2000 MPa, with the advantage of low density and resistance to corrosion but
nevertheless steel still~has the competitive advantage. One of the disturbing features of
steel wire is the residual tensile stress which exists in 75% of the circumference of the
wire which is not ideal from the fatigue point of view. The way forward would seem to
be exploring new coatings, including improvements in galvanising and the search for
more efficient lubricants.
References
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
14 FRETTINGFATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FRETTING WEAR AND CRACK INITIATION
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Siegfried Fouvry,1Philippe Kapsa, 1and Lro Vincent 2
REFERENCE: Fouvry, S., Kapsa, Ph., and Vincent, L., " A Global Methodology to
Quantify Fretting Damages," Fretting Fatzgue: Advances in Basic Understanding and
Applications, ASTMSTP 1425, Y. Mutoh, S. E. Kinyon, and D. W. Hoeppner Eds.,
ASTM International, West Conshohocken, PA, 2003.
ABSTRACT: Fretting wear and fretting fatigue are commonly associated with damage
of quasistatic loaded assemblies and with decrease in lifetime. Depending on the sliding
condition, wear induced by fretting or cracking induced by fretting can be observed. To
quantify such competitive damage phenomena, a fretting map approach has been
extensively applied describing the sliding conditions and the damage evolution as a
function of the normal force and the displacement amplitude. This approach, considered
as a useful methodology to analyze tribo-systems, nevertheless presents the limitation of
not allowing a direct comparison between tribo-systems. To rationalize this experimental
approach and facilitate the comparison between tribo-systems, normalized sliding
condition and crack nucleation fretting maps are introduced. Based on contact mechanics,
the sliding transition is quantified using a fretting sliding criterion, and a specific
formulatiofl is provided to identify the local friction coefficient under partial slip
condition. Cracking, which is mainly observed under stabilized partial slip condition, is
analyzed by applying multiaxial criteria and taking into account the size effect. Wear,
which is favored under gross slip condition, is quantified through an energy approach.
Finally a global methodology is developed by which the sliding condition, the crack
nucleation under partial slip condition and the wear kinetics under gross slip regime may
be quantified.
KEYWORDS: Fretting, Fretting map, sliding condition, crack nucleation, size effect,
wear, dissipated energy.
Introduction
l UMR CNRS 5513, Ecole Centrale de Lyon, BP 163, 69131, Ecully, France.
z UMR CNRS 562t, Ecole Centrale de Lyon, BP 163, 69131, Ecully, France
17
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by
by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
18 FRETTINGFATIGUE: ADVANCES
to vibration and thus concerns many industrial branches (helicopters, aircraft, trains,
ships, trucks, electrical connectors) [1-3] (Figure la). Fretting is a very complex problem
involving numerous aspects such as tribology, contact mechanics, fatigue mechanics and
material science, but also corrosion science. To reproduce such phenomena different
fretting tests have been developed which permit the control of the normal loading and
displacement amplitudes [4-5]. The relative displacement induces tangential loading,
which can be described by the fretting loop: Q(t)=f(~(t)) (Figure lb).
Two fretting conditions are identified : partial slip, which is characterized by a closed
elliptical fretting loop, associated with a composite contact of the sliding and sticking
zone. The gross slip condition which is identified by a quadratic dissipative fretting loop,
is related to full sliding occurring over the entire interface.
The friction coefficient changes during loading and this can lead to a change of sliding
condition. It is then possible to define various fretting regimes : Partial slip Regime
(P.S.R) : when the partial slip condition is maintained during the test; Mixed Fretting
Regime (MFR) : when there is a transition from one condition to another; Gross Slip
Fretting Regime (GSR): when the gross slip condition is maintained. Waterhouse et al [1]
first indicated a correlation between the sliding regime and damage evolution (Figure 2).
Cracking is mainly encountered in partial slip regimes and mixed fretting regimes
stabilized under partial slip condition, whereas wear is observed for larger amplitudes in
gross slip regimes. The experimental mapping of the material response (MRFM :
Material response fretting mapping) was originally introduced by P. Blanchard et al [6].
A major defect of such a mapping approach is the use of mechanical variables like
normal force and displacement amplitude which, depending on the geometry and
mechanical properties studied, cannot permit a direct correlation between fretting
situations. This paper will develop a quantitative approach defining pertinent variables,
which allow the damage evolution to be quantified (Figure 3).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FOUVRY ET AL. ON GLOBAL METHODOLOGY 19
Figure 3 - Illustration of the methodology for thefretting damage analysis (after [6]).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
20 FRETTINGFATIGUE: ADVANCES
As mentioned before, the sliding transition is classically defined from the fretting loop
shape. One major difficulty of such an analysis is the subjectivity of the observation,
particularly close to the transition between partial and gross slip.
To overcome this difficulty, several sliding criteria have been introduced to quantify the
sliding analysis (Figure 4) [10, 12]. An energy sliding criterion has been introduced
which corresponds to the ratio between the dissipated energy (i.e. area of the hysteresis
loop) and an equivalent total energy which could be defined as the total energy dissipated
by the contact system if it presents infinite tangential compliance.
A - Ed - Ed
E t 4. Q . - ~ , (2)
It has been demonstrated for the elastic sphere/plane configuration that this variable
presents a constant value (A = 0.2) at the sliding transition (Figure 5) [6].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FOUVRY ET AL. ON GLOBAL METHODOLOGY 21
This value is independent of the contact dimension and the elastic properties of the
tribosystems. Therefore, the experimental sliding analysis can be quantified and the
sliding regime formalized. Finally, the running condition fretting map is more easily
established. Figure 6a clearly illustrates that the sliding transition (St) is mainly
controlled by the friction coefficient. The Mindlin analysis confirms this proportional
relation.
8t - KI'~t'P , with K 1 = + (3)
a G2
with
vl, v 2 : Poisson coefficients of the plane (1) and the sphere (2),
G t, G2: Shear elastic moduli of the plane (1) and the sphere (2),
a : Hertzian contact radius.
Regarding the Mindlin formulation, the transition amplitude can also be expressed as a
function of the maximum Hertzian pressure (P0) (or shear stress q0) and the contact
Hertzian radius "a" (Figure 6b) [8].
rc Ix.P0 _ q0 _ St
(4)
8 G* (8. G*/rt) a
Figure 5 - Variation o f the sliding criteria "A" versus the displacement amplitude
SC652/100C6 (R=12. 7mm) : Cs=0.0075 ~am/N; 9 : P = 250 N []: P = 450 N .
A similar analysis has been introduced by Chateauminois et al. [9] where the transition
amplitude is normalized by the friction value and the contact radius and plotted versus the
mean pressure. The advantage of the present representation is that each part of the
equation is non dimensional, which permits a normalized fretting chart to be defined
(Figure 6b) with a constant slope equal to one.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
22 FRETTINGFATIGUE: ADVANCES
~'~theoretical co 0.01
lO0
.~__-/.
w transition g
o o
2 4 6 8 10 12 14 0.01 0.02 0 03 0 04 0.05
(a) displacement amplitude : 5, (lam) (b) normalized transition amplitude :~t/a
The results obtained from different contact dimensions and various pairs of materials are
directly compared.
A comparison of the different tfibosystems and loading situations confirms the good
prediction obtained by the Mindlin formalism as long as the loading remains elastic. For
softer materials and higher loading situations, a shift of the transition towards larger
amplitudes can be observed. The threshold loading marking the transition toward a plastic
accommodation through the contact is currently being studied, with both yield stress and
the cyclic hardening behavior of the materials being considered.
Figure 7 - Evolution of the mixed regime deduced from the analysis of the ".4" and "["
variables. (SC652/52100, R=12. 7mm, Cs=O.006 tzm/N; P = 300 N; 8* = 4.2 I~m).
As well as analyzing the sliding condition, it is fundamental to correctly identify the local
friction coefficient operating through the sliding domain. This latter variable is essential
to estimate properly the stress. While determination of the local friction coefficient under
gross slip is obvious, it is more complex under partial slip. Indeed, the friction coefficient
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FOUVRY ET AL. ON GLOBAL METHODOLOGY 23
is not equal to the ratio between the tangential force amplitude and the normal force,
depending on whether part of the tangential loading is related to the elastic
accommodation through the sticking domain.
Nevertheless, considering elastic condition and applying the Mindlin formalism, the local
friction coefficient can be estimated by combining the two measured variables which are
the energy ratio A and the force ratio f (Figure 7) [10].
The stress loading path can correctly be evaluated and the crack nucleation predicted
by transposing a multiaxial fatigue analysis [11-15], provided there is a precise
description of the sliding condition and a precise definition of the friction coefficient
operating through the sliding domain. Note that the crack nucleation analysis developed
here is related to the first observed very small cracks (usually inferior to 30 ~tm length). It
corresponds to the incipient crack nucleation condition and at this stage it can not be
extrapolated if it will propagate or not.
In opposition to classical fatigue analysis, where the maximum stress field concerns a
rather large volume of matter, contact loading is characterized by a very sharp stress
gradient on and below the surface. Indeed, the maximum stress field concerns volume
dimensions which can be inferior to the grain size. To estimate the contact failure from a
macroscopic fatigue approach, a size effect must be taken into account [11, 15].
Figure 8 - Influence of size effect on the cracking risk (30NiMo, c/a=0.5, ~=0.8 ).
The local fatigue approach based on a point stress analysis (point M) must be replaced by
a non local fatigue description which considers a mean loading state ~(M, t)averaged on
a micro-volume V(M) surrounding the point on which the fatigue analysis is performed
(Figure 8). Such a micro volume is obviously highly dependent on the microstructure. A
tempered low alloyed steel (30NCD16) was studied under a fretting wear situation.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
24 FRETTINGFATIGUE: ADVANCES
When a Dang Van fatigue description was considered, good prediction of the crack
nucleation through the contact was found if the contact stress loading path was averaged
through a 5-6 rtm cubic edge representative micro-volume [11].
This dimension appears sm~ller than the original austenitic grain size. Therefore, the
intrinsic length scale (~) required to conduct an optimized fatigue analysis is very small,
grain and even subgrain dimensions need to be considered. This leads to the practical
consequence that to predict fretting crack nucleation using FEM modeling, very fine
meshing of the fretted surface must be defined. The grain size appears to be a relevant
dimension.This multiaxial fatigue description leads us to conclude that the cracking risk
under fretting wear can be described through five fundamental variables which are :
- the Hertzian pressure P0 (normalized by the Hertzian yield pressure under pure
indentation P0y = 1.6 CYy0.2),
- the fretting sliding condition here expressed by the ratio between the tangential force
amplitude and the amplitude at the transition (Qt = IX-P ),
the friction coefficient operating through the sliding domain under partial slip
condition,
the conventional fatigue properties associated to the shear and bending fatigue limits,
the intrinsic length scale parameter (~) associated to the studied material.
c r a c k nucleation b o u n d a r y el ~ a(e=S~m)=S
( l o s cycles) , / I
1500" 47~ partiat / . ~,/ g ,.o
,~ stip reoime/ ~e~/ ~,
\\'x rc, c,,t
~1250
z
- - -
o.8
no crack ~3 crack X+~/~/ 7
O- 1000"
nucleatl~ ~ ! u c l ~ 7 ~. 0.6 7 ~
8 -
,~ 750" Cl.
0.4
"~ 500" ~V/ grossslip i
250"
S regime 0.2
[no crack nucleation]
0
0 ~I 1 I I I I l I 0.0 i I i I I I i I I
0 4 8 12 16 0.0 0.2 0.4 0.6 0.8 1.0
(a) displacement amplitude (+/- pm) (b) normalized sliding condition : Q-/Qi
Figure 9 -Crack nucleation response of the 30NCD16/I OOC6 (R=50 mm) under partial
slip condition. (a) Material Response Fretting Map (MRFM) ; (b) Corresponding
Normalized Crack nucleation Fretting Map OVCFM); - - : Dang Van crack nucleation
limits of the 30NCD16 alloy (d(E=5lxm)=l) as a function of the friction coefficient :
P0Y = 1.6'~ Q*/Qt =Q*/(I-tL "P) (tzL(1)=0"66' Itz(2)=0"6'/tL(3)=0"56' txL(4)=0"53)
loading situations reducing crack nucleation. This approach has been extended to
different fretting fatigue and fretting on pre-stressed specimen conditions. The
comparison between similar tempered low alloyed steels confirms the stability of this
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FOUVRY ET AL ON GLOBAL METHODOLOGY 25
approach indicating that for such material the critical length scale parameter (0 defining
the present size effect approach is constant e= 5- 6 gm. Then, considering the Dang Van
diagram, a normalized representation can be introduced by dividing the critical stress
couple ('~, 13) respectively by (~d and "cA - "cd od/3 ).
o~ "cd - (Yd/2
With : oa (MPa) :Altemating bending fatigue limit ( 1 0 6 cycles).
xd (MPa) : Alternating shear fatigue l i m i t (10 6 cycles).
Thanks to this normalized representation (Figure 10), all the experiments could be
compared. The classical result, that crack nucleation is a function of the shear stress
amplitude and the mean tensile state, can also be inferred from it.
This size effect approach appears to be a powerful means for the designer to optimize
contact geometry and surface treatments, but also to define relevant FEM meshing to
compute loading paths and establish cracking risks. This approach has been extended to
different materials like aluminium and titanium alloys. The analysis of 2618A aluminium
concludes that a significantly longer scale parameter (t>40gm) should be used,
confirming the influence of the microstructure on the crack nucleation mechanisms.
Current physical EBSD analyses, allowing the local identification of grain orientations,
tend to confirm that this length scale parameter is related to the crack arrest phenomenon
(i.e. the incipient crack are stopped at the interface of the grain boundary). The calculated
length (~ =5 ~tm for the low alloy studied), defined through an average stress approach,
can be associated with the maximum size that an incipient crack nucleating through the
grain can reach before being stopped by the strongest barrier : the grain boundary.
It verifies the K.J. Miller assumption that "the fatigue limit can be seen to be a function of
the maximum non-propagating crack length associated with a particular stress level" [16].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
26 FRETTINGFATIGUE: ADVANCES
Archard approach
The most common wear model proposed in tribology is the Archard model which
relates the wear volume to the product of the sliding distance with the normal force. A
wear coefficient (K) is usually extrapolated from the following relationships [17]:
V
K= (6)
P.S
with :
K : Archard wear coefficient,
V : Volume of the fretting scar defined by surface profiles,
P : normal force,
S : sliding distance.
Confirming previous studies, the wear response under gross slip condition shows that for
the same material, the K factor strongly depends on the wear mode, the displacement
amplitude, the contact geometry and the friction coefficient (Figure 11).
To interpret the various wear behaviors it is fundamental to consider the elasto-plastic
response of a metallic material. An elastic-plastic structure such as a fretted contact can
respond to cyclic loading in three identifiable ways [18, 19]. Under sufficiently small
loads, such that no element of the structure reaches the yield points, the response is
perfectly elastic and reversible. For higher loading conditions plastic flow can take place
during the first few cycles, but plastic deformation, residual stresses and strain hardening
may enable the structure to reach a perfectly cyclic elastic response commonly called
"elastic shakedown". The maximum loading for which this evolution is possible is known
as the elastic shakedown limit. Above this limit, plastic deformation takes place with each
loading cycle.
Figure 11 - Tribological and wear behavior of a sintered steel DC1 displaying a surface
porosity containing lubricant (20000 cycles): a - Evolution o f the friction coefficient
(first and last fretting cycles); b - Wear coefficients versus mean friction values.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FOUVRY ET AL. ON GLOBAL METHODOLOGY 27
Figure 12 - Wear map taking into account the shakedown behavior (repeated
sphere~plane sliding contact): - - elastic limit (Von Mises), m elastic shakedown limit
(kinematical hardening, A.D. Hearle et al.), DC1 wear kinetics (Figure 11) reported as a
function of the loading parameters 9 : high wear regime 16000<K(l~m3/N.m) <38000, [] :
low wear regime, K(llm3/N.m) <3000.
The relation between a high wear regime and a plastic shakedown or a ratchetting
condition demonstrates that plastic dissipation is probably one of the most relevant
parameters to quantify the wear kinetics of metals. An exact determination of the plastic
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
28 FRETTING FATIGUE: ADVANCES
work requires long and fastidious finite element computation which must be generalized
for any test situation. An alternative solution consists in assuming a relationship between
the plastic dissipation and the total dissipated energy introduced through the contact. The
dissipated energy which is measured from the Q*-~* fretting loop activates numerous
damage mechanisms such oxidation, debris formation and ejection, as well as material
transformation. If the controlling parameter of wear is assumed to be the material's
plastic transformation, then a linear relationship between the accumulated dissipated
energy and the wear volume could be considered [6,23]. This correlation has been
previously observed on high speed and low carbon steels but also for ceramics [23]. For
ceramic materials, the low energy wear factors which are identified can be related to the
activation of abrasion and oxidation mechanics.
Accordingly, Figure 13 displays the wear volume versus the corresponding accumulated
dissipated energy. A linear evolution is observed and an energy wear coefficient ~ v
(56500 ~tm3/J) can be extrapolated. This expresses the wear volume created by each joule
dissipated. The linear approximation is justified by a high regression coefficient (R2>0.9).
Comparison with the Archard's analysis (Figure 13) confirms that such a shear work
approach is much more relevant to identify the intrinsic wear resistance of a
microstrncture. The energy approach, which is more stable, can be considered as an
extension of the Archard description, which better integrates the influence of the friction
coefficient.
80 80
DC1/alumina s~ c DCl/alumina
E E ! O:v 565oo0m3/,
= =/
:~- 6O
A
r,,
K ~ 60 Edth = 5 7 J
/ .C-
> A / >
40
/y~
A A//~ []
J E
0 S ~
/ >
20 20 ,
IA
It also permits a more physical description of the damage processes. It can be noted that
the linear approximation does not cross the origin but presents a smooth shift along the
energy axis (Figure 13b). This was previously observed mainly for steel or metal alloys
rather than for ceramics. This energy, called the threshold energy of wear activation
(Edtla) can be associated with the incipient plastic work first required to transform the
material's surface. A layer formed of TTS (tribologically transformed structure) is
generated. Hard and fragile, it is continually fractured by the contact loading leading to
debris formation [24].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FOUVRY ET AL. ON GLOBAL METHODOLOGY 29
This transient period can also be interpreted with regard to the rachetting phenomenon
induced by the contact loading. Indeed, as mentioned by Kapoor, before reaching a
stabilized wear evolution, the first layer of the material has to endure a given plastic
strain deformation or plastic dissipation [25]. Therefore an initial dissipated energy has to
be introduced (Edth) through the contact to transform the material before wear initiates
(Figure 14). Therefore the wear extent can be formulated through the following relation :
Though it is more stable, and allows more in depth investigations of wear phenomenon,
the application of the energy approach nevertheless has to be considered carefully. The
wear evolution depends on the third body flowing through the interface. It is a function of
the sliding amplitude or the sliding condition (i.e. repeated sliding - like pin on disk - or
alternating sliding like fretting).
Figure 15 - Wear energy analysis of hard coating; (a) P VD TiN~hard coating behavior
(P=50-200N, ~, = +/- 25 - 2001tm, R=12. 7mm); (b) Comparison for similar loading
conditions between metal and hard coatings [23].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
30 FRETTINGFATIGUE: ADVANCES
The methodology developed here to attempt to quantify fretting damage brings out the
following aspects:
- A simple mechanical analysis of the contact loading as a function of the sliding
amplitudes shows that cracking will be favored under stabilized partial slip conditions
(partial and mixed fretting regimes) whereas wear by debris formation is predominant
under gross slip regime. Nevertheless the classical Normal force - Displacement fretting
map approach displays the limitation that it is restricted to a given contact geometry ;
therefore to extend and formalize this approach, normalized representations have been
introduced (Figure 16).
- To quantify the sliding condition, an energy sliding ratio was introduced. As an online
indicator it allows the fretting regime evolution to be controlled. Using a simple
formulation it can also be used to identify the local friction coefficient operating under
partial slip conditions. A normalized sliding fretting map was introduced to consider
plastic accommodation under severe loading conditions.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FOUVRY ET AL. ON GLOBAL METHODOLOGY 31
- Cracking was investigated using a multiaxial approach. It was shown that to correctly
predict the crack nucleation risk, fatigue analysis has to consider the size effect related to
the very.sharp stress gradient imposed by the contact loading [26]. A critical length scale
parameter was considered that seems to be related to the microstructure. Recent
investigations tend to associate such a "crack nucleation length variable" to a crack arrest
condition. By contrast, the propagation analyses [27,28] assume that the crack extension
is more affected by the contact size and the stress field distribution below the contact.
-Wear quantification is less advanced and formalized. It was nevertheless shown that to
identify correctly the wear kinetics under fretting it is essential to consider the
elastoplastic response of the material. The shakedown limit is highly dependent on the
friction coefficient, and the Archard law, which doesn't integrate this variable, cannot
properly quantify the wear kinetics under large friction fluctuations.
An energy approach is introduced allowing better wear quantification and permitting an
easier comparison between surface treatments.
Acknowledgments
This work was supported in part under contracts BRE2-CT92-0224 and BE96-3188
BriteEuram projects. The authors are grateful to Prof. Ky Dang Van, Prof. F. Sidoroffand
Prof. Wronski for his helpful comments and suggestions.
References
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
32 FRETTINGFATIGUE: ADVANCES
[9] Chateauminois, A., Kharmt, M., Krichen, A., "Analysis of fretting damage in
Polymers by Means of Fretting Maps", ASTM STP 1367, 2000, p. 352-366.
[ 10] Fouvry, S., Kapsa, Ph., Vincent, L., "Developments of fretting sliding criteria to
quantify the local friction coefficient evolution under partial slip condition",
Eds. D. Dowson et al, Tribology serie, 34,1997, p. 161-172.
[11] Fouvry, S., Kapsa, Ph., Sidoroff, F.,Vincent, L., "Identification of the characteristic
length scale for fatigue cracking in fretting contacts", J. Phys. IV France 8
(1998), Pr8-159.
[12] Fan'is, T.N., Szolwinski, M.P., Harish, G., "Fretting in Aerospace Structures and
Materials", ASTM STP 1367, 2000, p.523-537.
[13] Neu, R.W., Pape, J.A., Swalla, D.R., "Methodologies for linking Nucleation and
Propagation Approaches for Predicting Life Under Fretting", ASTM STP 1367,
2000, p.369-388.
[14] Lykins, C.D., Mall, S., Jain, V., "An evaluation of parameters for predicting fretting
fatigue crack initiation" International Journal of Fatigue (2000), p.703-716.
[15] Fouvry, S., Kapsa, Ph., Vincent, L., "Fretting-Wear and Fretting-Fatigue : Relation
through Mapping Concept ", ASTM STP 1367, 2000, p. 49-64.
[16] Miller, K.J., "Material science perspective of metal fatigue resistance", Materials
Science and Technology, June 1993, Vol. 9, pp. 453.
[17] Archard, J.F., "Contact and rubbing of flat surfaces", J. Appl. Phys., 24 (1953), p.
981-988.
[18] Johnson, K.L, Wear 190, "Contact mechanics and the wear of metals", (1995),
162-170.
[19] Wong, S.K., Kapoor, A., Williams, J.A., "Shakedown limits on coated and
engineered surfaces", Wear 203-204, (1997), 162-170.
[20] Hills, D.A., Ashelby, D.W., "The influence of residual stresses on the contact -
load-bearing capacity", Wear, 75 (1982), p. 221-240.
[21] Maouche, N., Maitournam, M.H., Dang Van, K., "On a new method of evaluation
of the inelastic state due to moving contacts", Wear 203-204, (1997), 139-147.
[22] Fouvry, S., Kapsa, Ph., Vincent, L., "An elastic plastic shakedown analysis of
fretting wear", Wear 247, 2001, p. 41-54.
[23] Fouvry, S., Kapsa, Ph., "An Energy Description of Hard Coatings Wear
Mechanisms", Surface & Coating Technology, 138 (2001) p. 141-148.
[24] Sauger, E., Fouvry, S., Ponsonnet, L., Martin, J.M, Kapsa, Ph, Vincent, L.,
"Tribologically Transformed Structure In Fretting" Wear 245, 2000, p.39-52.
[25] Kapoor, A., "Wear by plastic ratchetting", Wear 212 (1997), p. 119-130.
[26] Nowell, D, Hills, D.A, and Moobola, R., "Lengh Scale Considerations in Fretting
Fatigue" ASTM STP 1367, 2000, p. 141-166.
[27] Dubourg, M.C., Lamacq, V.," Stage II Crack Propagation Direction Determination
Under Fretting Fatigue Loading ", ASTM STP 1367, 2000, p. 436-450.
[28] Kondoh, K., Mutoh, Y., "Crack Behavior in the early stage of fretting fatigue
fracture", STP 1367, 2000, p. 282-292.
[29] Ambrico, J.M., Begley, M.R.," The role of macroscopic plastic deformation in
fretting fatigue life predictions", Int. Journal of Fatigue, 23 (2001), p. 121-128.
[30] Ciavarella, M., Demelio, G.,"A review of analytical aspects of fretting fatigue, with
extension to damage parameters, and application to dovetail joints", Int. Journal
of Solid and Structures 38 (2001) 1791- 1811.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Tomohlsa Nlshida,1 Kazunon Kondoh,2 Jin-Quan Xu, 3 and Yoshiham Mutoh 3
Reference: Nishida, T, Kondoh, K., Xu, J. Q., and Mutoh, Y., "Observations and Analysis of
Relative Slip in Fretting Fatigue," Fretting Fatigue Advances of Bastc Understanding and
Applicatzons, ASTM STP 1425, Y. Mutoh, S. E. Kanyon and D. W. Hoeppner, Eds., American
Society for Testing and Matermls International, West Conshohocken, PA, 2003.
Abstract: L-1-sltu observatmn of the relative slip along the contact surface was conducted on a
servo-hydrauhc fatigue machine with scanning electron rmcroscope. It was found that the relative
slip observed by this method was much smaller than that obtained by a conventional small
extensometer. It was also found that the relative shp depended on the rigidity of the contact pad. The
higher the rigidity of the pad was, the larger the relative shp became. Numerical analysis with the
use of the fimte element method (FEM) program ABAQUS was also camed out. The relative slip
estimated by the FEM agreed well with the observed one. Therefore, it was proved that the in-sltu
observation method introduced m this study was effective enough for measunng relative slip at the
contact edge.
Keywords: fretting fatigue, relatwe slip, m-situ observation, FEM analysis
Introduction
Fretting fatigue is well known to occur at contact of combmed components, such as joints
and bearings. The relative shp along the contact interface between the two components as one of the
most Important factors to significantly influence the fretting fatigue behavior [1-4]. Fretting fatigue
strength is generally degraded with increasing relative slip amplitude. In experiments, the relatwe
slap amplitude has been measured by using specially developed small extensometers [4-7] and a laser
extensometer [8]. However, most of the measurements gave only the apparent and macroscopic
values. It is also known that pamal slip is typical in fretting, which Implies that the relative shp
amplitude is not uniform along the contact interface. The local relative slip amplitude
33
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by
by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
34 FRETTINGFATIGUE: ADVANCES
especially at contact edge should be important to determine the stick and the micro-sliding regions in
the contact area during the fretting fatigue loading.
In the present study, the relative slip amplitude along the contact interface was measured by
the in-situ observation using a servo--hydraulic fatigue machine with a scanning electron microscope
(SEM). FEM analysis was also carried out to evaluate the relative slip amplitude along the contact
interface. From combining the results by experiments and FEM analysis, effect of rigidity of contact
pad on relative slip amplitude was discussed in detail. The crack initiation behavior was also
discussed based on the stress range distribution along the contact interface.
Experimental procedures
The material used for the fretting fatigue specimens was an aluminum alloy JIS 6063-T6,
while both the aluminum alloy JIS 6063-T6 and a Cr-Mo steel JIS SCM420 were used for the
contact pads. Chemical composition and mechanical properties of the materials used are shown in
Table 1 and 2, respectively. The shape and dimensions of the specimen and the contact pad are
shown in Fig. 1. The four different contact pads with pad foot heights L of 0.15, 0.5~1.0 and 2.0 mm
with the aligned contact surface were prepared. Fretting was induced by pressing a pair of contact
pads onto the specimen gage part using a proving ring. The fretting fatigue tests were performed
under a load-controlled tension-compression condition with a stress ratio of R=--l, sinusoidal
wave-form and frequencies of 10 to 20 Hz. The tests were carried out at a stress amplitude of 120
MPa with a constant contact pressure of 60 MPa. ln-situ observation and measurement of relative
slip were conducted using a servo-hydraulic fatigue machine with a scanning electron microscope.
The proving ring was tilted against the loading axis, as shown in Fig. 2, so that whole contact region
between the specimen and the contact pad can be observed. When measuring the relative slip,
loading frequency was reduced to 0.05Hz. The relative slip amplitude was defined as half of the
measured relative slip range. After the measurement, the test was stopped, and the fretting scars were
observed. It is found that the fretting damages corresponding to four fools are almost the same.
Finite element (FEM) analysis was carried out to estimate the stress distribution near the
contact region and the relative slip between the specimen and the contact pad. FEM analysis
program ABAQUS [9] was used. As shown in Fig. 3, FEM model with quadrilateral elements was a
quarter of the specimen with the contact pad. Boundary conditions were applied along two
symmetrical axes, and loading conditions were given as the same as the l?etting fatigue tests
conducted in the present study. Analysis was carried out assuming a linear elastic body under the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON ANALYSIS OF RELATIVE SLIP 35
.$44 Fe Cu Mn Mg Cr Zn Ti
6063-T5 0.20 0.03 0.02 0.53 0.01 0.01 0.02
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
36 FRETTING FATIGUE: ADVANCES
plane strain condition. Based on the FEM analysis results, it is found that only a very small region
near the contact edge would be yielded, i.e., it could be considered to be under the small scale
yielding condition. Therefore, the linear elastic analysis result is useful for characterizing the fretting
fatigue behavior under the present condition. The contact elements located at the sliding interface
must fulfd the Coulomb s friction law. Sliding occurs in the contact element when shear stress( r ) on
the interface becomes equal to the critical shear stress (T = ~ q ), where a , is the normal stress and
/z is the coefficient of friction. Based on the experimental result for the gross sliding case, the
coefficient of friction of 0.7 was used in the present analysis.
Figure 4 shows an example of measurement of relative slip at the contact edge for the
aluminum specimen with SCM420 steel contact pad, where the height of pad foot is 0.15 mm.
Figure 4(a) and (b) indicate micrographs at the maximum stress and at the minimum stress,
respectively. The measurement procedure was as follows: (1) looking for some clear feature marks
on both the specimen surface and the contact pad surface, (2) making a base line for measuring
relative slip, as shown in Fig. 4(a), and (3) measuring the relative slip as the distance between two
base lines on the specimen surface and the contact pad surface, as shown in Fig. 4(b). The relative
slip amplitude was given as half of the measured relative slip range.
Three typical points along the contact interface were selected for measuring the relative slip
amplitude: at the internal edge, center and external edge. Relationship between relative slip
amplitude and number of cycles for the SCM 420 steel contact pad with pad foot height of 0.5 mm is
shown in Fig. 5. It has been commonly observed [10, 11] that the relative slip behaves unstable at the
initial stage of fretting fatigue. Figure 5 shows that the relative slip amplitude becomes stable after
1• cycles. The average value after lxl02 cycles was therefore defined as the relative slip
amplitude for the cases.
The relative slip amplitude measured for the aluminum alloy specimen with the SCM 420
steel contact pad (foot height of 0.5 mm) is shown in Fig. 6. In the horizontal axis, the origin is at the
center of contact region and the external edge is in the positive side. In the figure, the relative slip
amplitudes estimated by FEM analysis, where the relative slip is determined as the difference of the
relative displacements in the horizontal direction of contact points between the pad and the specimen,
are shown together with those estimated by assuming the elastic specimen and the rigid contact pad,
which is given as [3]
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON ANALYSIS OF RELATIVE SLIP 37
5 u u a
6
9 hter~d ~
v4 9 CaztCl" -~Elastic c a l . / ]
9 F~(~(~T~ ( ~
3 ~4
g i ill IN n mu
1 .~ 2
0
-1 I I I
I
10 z zo 2 zo~ zo 4 10 5 o, ,
-1 0 1
Number of cycles Distance from contact ovnter (ram)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
38 FRETTING FATIGUE: ADVANCES
cx,~l
s= (1)
2E
where s is the relative slip amplitude, aa is the amplitude of the cyclic load, l is the span
length of contact pad and E is Young s modulus. As can be seen from the figure, the relative slip
amplitude at the external edge is the largest, while that at internal edge is the smallest and almost
zero. It is obvious that the relative slip amplitude estimated by Eq. (1) with assumption of rigid
contact pad is significantly high compared to the measured one. It is also evident that the relative slip
amplitude estimated by the FEM analysis agrees with that measured by in--situ SEM obs6rvation.
The relative slip amplitudes measured by in-situ observation and by FEM analysis for the aluminum
alloy specimen with the aluminum alloy contact pad (foot height of 0.5 ram) are shown in Fig.7. The
similar behavior to the case of the aluminum alloy specimen with the steel contact pad was observed.
To discuss the difference of relative slip amplitude between the measurements by in-situ
SEM observation and the calculation by assuming the rigid contact pad, deformation of the contact
pad was estimated by the FEM analysis. The results are shown in Fig. 8. As can be seen from the
figure, both the aluminum alloy and the steel contact pads are elastically deformed. It can be easily
understood that the difference of the displacements on the top corner and the contact edge of the pad,
which is in the order of relative slip amplitude, is not considered in Eq. (1). Because that the relative
slip amplitude estimated by assuming the rigid contact pad includes this difference of the
displacements, Eq. (1) almost gave the slip amplitude two times of that measured by in-situ SEM
observation, which is in reasonable agreement with the result of FEM analysis; The relative slip
amplitude has been often measured by using a small extensometer [3,4]. [t is obvious that the
measured value depends on the position of the measure point at the end surface of the contact pad,
the lower the measure point is, the smaller the measured slip value becomes, because the difference
of the displacements between the measure point and the contact edge becomes smaller. This also
means that the relative slip amplitude measured using a small extensometer will be in between those
estimated by assuming the rigid contact pad and measured by the in-situ SEM observation.
Therefore, improvement or development of a new method for measuring relative slip amplitude at
contact edge in fretting fatigue test is requested.
The slip amplitude distributions for the aluminum alloy specimen with the steel contact pad
with various foot heights are shown in Fig. 9. As can be seen from the figure, the relative slip
amplitude at internal edge increases with increasing pad foot height. Relationship between the
maximum relative slip amplitude at external edge and pad foot height is shown in Fig. 10. It is found
that the maximum relative slip amplitude decreases with increasing pad foot height for both the steel
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON ANALYSIS OF RELATIVE SLIP 39
and the aluminum alloy contact pads. It is also obvious that the maximum relative slip amplitude for
the aluminum alloy contact pad is smaller than that for the steel contact pad. Therefore, it is
concluded that the more rigid contact pad results in the larger relative slip amplitude. The estimated
relative slip amplitudes by FEM are also shown in Figs.9 and 10, which indicate that the estimation
agrees the experimental results.
The deformation of end surface of the steel contact pad with various pad foot heights is
shown in Fig. 11. The contact pad with large foot height is significantly deformed compared to that
with small foot height. This behavior is in accord with that the contact pad with larger foot height
indicates smaller relative slip amplitude. Therefore, it should be noted that the rigidity of contact pad
is an important factor in fretting fatigue.
~.)
FEM
r 2
~::k 1
o
Y
Distanoc flora
0
!
contact
i
center (nun)
9 SCM
z~ A Al-o.lloy
0
9
9
A
A
I End Surface,~ '\
E
@ A
0
A 4.5 Pad Y \
0 \
I)
-I
!
0
,', N
1 - 2 --
Speci men X
Displacement ( #m )
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
40 FRETTING FATIGUE: ADVANCES
From the in-situ SEM observations, fretting fatigue cracks were found to initiate near the
external edge of contact region in the very early stage (less than three percent) of fatigue life [12,13].
A fretting fatigue crack observed during a fretting fatigue test of the aluminum alloy specimen with
the steel contact pad is shown in Fig. 12. Cracks (with different lengths) were observed for all four
external edges. From careful observations, a crack initiated at a very shallow angle to the contact
surface and then turned to a higher angle: the former is supposed as the crack initiation stage and the
latter is known as the mixed-mode crack propagation stage under the influence of fretting [14].
4 i - i i
4.~,
v
9 Me.~t 9 Mean
r
N 2f~_
~ Meas~
-! 0 -1 Q ~o .
-! 0
Distance from center(nm~) Distance from center (mm) Distance fi'omcenter (ram)
SCM Al-alloy _
"• 4 s~ 99 L=O.
9
Smm L,--O. ! 5 m m
v
"I31
Experiment
FEM
9 &
4s L--2.0mm
~3 ~3 tm
I,
End [Surface"~
ttl jr,
o~ ~. 9
%
*
1
!
2
1 I
~ ~ ' ; "
}:','
"
~
,
-3
Height contact pad legs (ram) Displacement (/lm )
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON ANALYSIS OF RELATIVE SLIP 41
The FEM analysis mentioned above also can give the stress distribution near the contact
interface. Fatigue crack initiation and propagation behavior is known to be controlled by not a
maximum stress but a stress range. Figure 13 shows the stress range distributions along the contact
interface of the aluminum alloy specimen with the steel contact pad. As can be seen from the figure,
the maximum stress range is found at the external edge of contact region for any kind of stresses,
where the relative slip amplitude is also the largest.
From the foregoing results, it is concluded that a fretting fatigue crack initiates at the contact
edge, where the relative slip amplitude and the stress range are the largest. About the fretting fatigue
crack initiation and propagation, we will report in another paper [15].
~Oq
9 f !
-500
-1 0 1
Distance from contact center (ram)
Figure 13-Stress range dist~qbutions along the contact interface of
the aluminum alloy specimen with the steel contact pad,
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
42 FRETTING FATIGUE: ADVANCES
Conclusions
[n--situ measurements and FEM analysis with contact-frictional elements of relative slip
amplitude between the specimen and the contact pad were carried out. Effect of rigidity of contact
pad was discussed in detail. The main results obtained are summarized as follows:
(1) Relative slip amplitude measured by using an SEM in-situ observation technique was
significantly smaller than that measured by using a conventional extensometer.
(2) Relative slip amplitude measured by using an SEM in-situ observation technique agreed well
with that estimated by the FEM analysis.
(3) Relative slip at the contact edge increased with increasing rigidity of contact pad.
(4) From the FEM analysis, the relative slip and stress ranges were the largest at the external
contact edge, at which fretting fatigue cracks are supposed to initiate. This is in good
agreement with the observations of crack initiation in fretting fatigue test.
References
[1] Spink, G. M., Fretting fatigue of a 2.5% NiCrMoV low pressure turbine shaft steel-lhe effect of
different contact pad materials of variable slip amplitude, Wear, 136, pp.281-297, t990.
[2] Duquette, D. J., The role of cyclic wear (fretting) in fatigue crack nucleation in steels, Strength
Metals Alloys, Vol. 1, pp.213-218, 1979.
[3] Mutoh, Y., Nishida, T., and Sakamoto, [., Effect of relative slip amplitude and contact pressure on
fretting fatigue strength, Zairyo, 37(417), pp.649-655, 1988.
[4] Fermer, J., and Field, J. E., La fatigue dans les conditions de frottement, J. E., rev. Met, 55, p.475,
1958.
[5] Satoh, T., Mutoh, Y., Yada, T., Takano, A., and Tsunoda, E., Effect of contact pressure on high
temperature fretting fatigue, Zairyo, 42(472), pp.78-84, 1993.
[6] Ochi, Y., Hayashi, H., Tateno, B., Ishii, A., and Urashima, C., Fretting fatigue properties in rail
steel and fish plate materials, JSME, A63(607), pp.453-458, 1997
[7] Lee, S., Nakazawa, K., Sumita, M., and Maruyama, N., Effect of contact load and contact
curvature radius of cylinder pad on fretting fatigue in high strength steel, ASTM STP1367,
pp.199-212, 1999.
[8] Kondoh, Y., and Bodai, M., Study on fretting fatigue crack initiation mechanism based on local
stress at contact edge, JSME, A 63(608), pp.669-676, 1997.
[9] ABAQUS/Standard User s Manual, Vol.2, 1999.
[10]Nakazawa, k., Sumita, M., and Maruyama, N., Effect of contact pressure on fretting fatigue of
high strength steel and Titanium alIoy,ASTM STP 1159, pp.115--125, 1992.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON ANALYSTS OF RELATIVE SLIP 43
[ll]Lutynski, C., Simansky, G., and McEvily, A. J., Fretting fatigue of Ti-6A1-4V alloy, ASTM STP
780, pp.150--164, 1982.
[12]Zhou, Z.R., Sauger, E., and Vincent, L., Nucleation and early growth of tribologically
transformed structure induced by fretting, Wear, 212, pp.50-67, 1997.
[13]Hattori, T., Fretting fatigue analysis using fracture mechanics, JSME Int., 31(1988), pp.100-107.
[14]Nix, K.J., and Lindley, T.C., The initiation of fracture and propagation of smal] defects in
fretting fatigue, Fatigue fracture engineering of material and structure 8(1985), pp.143-160.
[15]Mutoh, Y., Xu, J.Q., and Kondoh, K., Observations and analysis of ffetIing fatigue crack
initiation and propagation, submitted to ASTM STP1425.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Paul N. Clark 1 and David W. Hoeppner I
Reference: Clark, P. N. and Hoeppner, D. W., "Fretting Fatigue Initial Damage State
to Cracking State: Observations and Analysis," Fretting Fatigue: Advances in Basic
Understanding and Applications, STP 1425, Y. Mutoh, S. E. Kinyon, and, D. W.
Hoeppner, Eds., ASTM International, West Conshohocken, PA, 2003.
44
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CLARK AND HOEPPNER ON DAMAGE/CRACKING STATES 45
Introduction:
Fretting is an insidious type of damage that is the result of the interactions between
wear and corrosion [1]. This phenomenon is most commonly witnessed between
contacting surfaces that experience small amplitude oscillatory loads. These loads can be
induced via vibrations or nearly any variety of mechanical force(s). The strain associated
with cyclic fatigue forces creates ideal circumstances in which fretting can occur.
Fretting fatigue is a particularly vexing issue as the damage caused by fretting is often
responsible for the early nucleation of fatigue cracks. This damage is often created
through the process of adhesive contact of the asperities on opposing contact surfaces.
The contact surfaces then experience the production of debris or the removal/disturbance
of oxide layers. This accelerates and compounds the effects of wear and corrosion.
Fretting damage varies with particular circumstance. The rate and measure of damage
can vary with material, strain or slip amplitude, environment, state of stress, surface
finish of contact materials, manufacturing processes and maintenance practices [1-8].
Eden, Rose and Cunningham, who noted a production of oxide between grips and
specimens with an accompanied reduction in the fatigue life of their grips, first
documented fretting in 1911 [2]. In 1939, Tomlinson published a paper documenting
some the first scheduled and controlled experiments on fretting. He noted the small
amplitudes of motion could cause surface damage and that corrosion was a
compounding effect of fretting [3]. Warlow-Davies was one of the first to suggest that
fretting has a deleterious effect on fatigue life. He performed some of the earliest work
(circa 1941) examining the effects of fretting on fatigue [4]. Since, then many have
contributed to the technical communities knowledge base. The contributors include,
among others, Fenner, Wright and Mann, Waterhouse, Nishioka and Hirakawa,
Hoeppner and Goss [5-8].
The technical community still lacks the ability to predict the fretting fatigue life of
components. A large reason for this is the lack of understanding and characterization of
fretting damage. This tack of understanding has made the development of mathematical
and mechanical models challenging. A key to understanding fretting fatigue and its
implications with regard to reliability and structural integrity is to adequately
characterize the fretting damage. This understanding will lead to a more robust
understanding of the mechanical phenomenon of fretting, fretting fatigue and damage
related to fretting. Fretting can produce, but is not limited to, the following types of
damage [9]:
9 Pitting corrosion
9 Oxides and debris (third body)
9 Disturbance of protective oxide layers
9 Scratches
9 Fretting and/or wear tracks
9 Material transfer
9 Surface plasticity
9 Subsurface cracking and/or voids
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
46 FRETTINGFATIGUE: ADVANCES
9 Fretting craters
9 Cracks at various angles to the surface(s)
Frequently, this fretting damage will lead to early formation of fatigue cracking and
will result in an often times dramatic reduction of fatigue life.
Experimental Details
Fretting fatigue tests were performed using a closed loop electro-hydraulic servo-
controlled testing system. MTS controllers were used to control specimen mechanical
forces. Figure 1 depicts the fretting fatigue experimental apparatus. The actuator visible
onthe top of the apparatus applied the normal force. Axial forces were applied parallel
with the tabletop.
The dog-bone and fretting pad specimens were made from 2024-T3 aluminum
0.063" sheet and 0.250" plate respectively. The dog-bone specimens were manufactured
lengthwise in the longitudinal direction. The fretting pad specimens were designed with
a flat contact surface. Dog-bone specimens were lap polished to a 0.3gin finish and
fretting pads were polished to a 600-grit finish. Specimens were cleaned in acetone for
15 minutes after polishing.
Axial forces were applied in the longitudinal direction while normal load was
applied via the fretting pad perpendicular to the dog-bone fatigue specimen. The normal
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CLARK AND HOEPPNER ON DAMAGE/CRACKING STATES 47
force was applied at a net stress of 3.0ksi. Constant amplitude cyclic forces were
controlled at a maximum net stress of 30.0ksi, R=0.1 and f=10Hz. The net stress was
calculated based upon the applicable loading divided by the minimum cross sectional
area of the dog-bone specimen or maximum contact area between the fretting pad and
the faying surface of the dog-bone. Experiments were conducted in laboratory air with
no lubrication in the contact area.
Specimens had fretting damage induced at 100%, 80%, 60%, 40%, 20% and 10% of
the maximum fretting fatigue cycles to fracture. 100% was defined as the total cycles to
fracture for specimen A. The remaining specimens were subsequently subjected to the
applicabIe number of fretting fatigue cycles that corresponded to the appropriate
percentage of approximately 187,020 cycles (e.g: 80% of 187,020 - 150,000). The
specimens were then microscopically analyzed. This analysis sought damage on the dog-
bone specimens in the form of cracking, depth of scarring or pitting, and other
significant indicators. The fretting fatigue damaged dog-bone specimens were then
loaded to either fracture or run-out under cyclic mechanical forces without fretting (no
normal force). Failed specimens were subjected to fractography to identify fatigue
cracking and crack origins. This process aided in understanding and characterizing the
amount of fretting damage that is sufficient to demonstrate a marked reduction of fatigue
life.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
48 FRETTINGFATIGUE: ADVANCES
Experimental Results
The results for this set of experiments are presented in Table 1. Fretting fatigue
cycles and fatigue cycles (post-fretting) were tracked and reported. A graph of the cycles
versus percent fretting fatigue life is presented in Figure 2. It is important to note that 4
of the 6 specimens did not fracture. Specimens C, D, E and F were cycled from
1,000,000 to 3,000,000 cycles and did not fracture. This indicates a fretting fatigue
damage threshold for these conditions.
Figures 3 and 4 show fretting damage on specimen A (100%FF). Note the detail in
the depth record from the confocal microscope. Figure 5 shows the fracture surface and
crack origin for specimen A. The left image depicts specimen A at an angle such that
the fretting damage on the faying surface and the crack propagation evidence on the
fracture surface can be seen concurrently. Th'e fight image is a close-up micrograph of
the crack origin. The crack origin corresponds with the most severe fretting damage. The
damage progression on the fracture surface of specimen A can be seen in Figure 5. The
fatigue crack propagated through the specimen. Evidence on the fracture surface
indicates the crack originated at the heaviest portion of the fretting damage and
propagated to the edge of the specimen. Once the crack grew to the edge of the
specimen, it appeared to propagate through the remained of the specimen as a comer
crack until a critical crack length was reached and final fracture was eminent.
Figures 6-8 show fretting damage and cracks originating from that damage on
specimen B-80%FF. This specimen was analyzed for fretting fatigue damage after
150,000 cycles. There were three fatigue cracks growing from the fretting damage
shown in Figure 6. The largest of the three cracks is visible in Figure 6. The largest crack
can be seen near the fight end of the fretting damage propagating perpendicularly to the
applied loading. This crack, measured at approximately 650pm, was the most substantial
damage noted during damage analysis and ultimately led to the fracture of specimen B.
The other two cracks were measured at 142~tm and 34~tm from the edge of the fretting
damage. The maximum fretting damage on the laying surface was approximately 10/,tin
deep. However, the damage area from which the fatigue cracks originated experienced a
maximum damage depth of approximately 4.5~tm. Note that the fatigue cracking area
was near the edge of the fretting pad contact area, whereas the fretted area that
experienced the heavier damage (~10grn) was offset from the contact edge. This is
significant due to the complex stresses induced by the fretting contact and the normal
force. Cracks will typically nucleate near the contact edge, although this does not occur
exclusively.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CLARK AND HOEPPNER ON DAMAGE/CRACKING STATES 49
Percent of
Fretting Comments from
Induced Fatigue Cycles to
Specimen Fatigue Post Fretting
Fretting Cycles Fracture
Cycles Analysis
Fatigue
Heavy fretting
damage.
A 100% 187,020 n.a. 187,020
Deepest damage
~35gm.
Moderate fretting
damage.
80% 150,000 74,249 224,249
Deepest damage
~ 10gm.
Moderate fretting.
Did not
60% 112,500 1,000,000 Deepest damage
fracture
~Sgm.
Some deep
fretting damage
Did not near center of pad
D 40% 75,000 1,200,000 contact area.
fracture
Deepest damage
-20gm.
Light fretting
damage. Most
damage
Did not concentrated at
20% 37,500 3,000,000
fracture contact edge.
Deepest damage
~4gm.
Moderate fretting
damage. Most
Did not severe damage on
10% 18,750 3,000,000 edge of specimen.
fracture
Deepest damage
~9gm.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
50 FRETTING FATIGUE: ADVANCES
120
,~Baseline: 100%FrettingFatigue [
100
~t ~
r~
8 0 84
60
9~Specimens9did~Anot
fractuIre.
.~ 4o
20.
Cycles
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CLARK AND HOEPPNER ON DAMAGE/CRACKING STATES 51
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
52 FRETTINGFATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CLARK AND HOEPPNER ON DAMAGE/CRACKING STATES 53
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
54 FRETTING FATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CLARK AND HOEPPNER ON DAMAGE/CRACKING STATES 55
Discussion
There exists a fretting fatigue damage threshold for these experimental conditions.
This fretting fatigue damage threshold is dependent upon the arrest of further fretting
damage. Upon the arrest of further fretting damage, specimens exhibited dramatically
increased fatigue life. The baseline test (specimen A-100%FF) and specimen B-80%FF
tests were very similar when comparing total cycles to fracture. Characterizing the
fretting damage of specimens A and B was dramatically different, however, the location
of the fracture origins were similar. The fatigue cracking responsible for fracture
originated near the edge of the fretting pad contact area. This is a relatively common
phenomenon. Specimens C-F that experienced 60% or less fretting fatigue cycles
displayed increased fatigue life upon the arrest of fretting damage. None of the four
specimens fractured after at least an additional 1,000,000 cycles. Specimens E and F
were cycled for 3,000,000 cycles and did not fracture.
Specimen B, shown in Figures 6-8, was the only specimen where cracking damage
was discovered prior to fracture. Note the depth of the fretting damage near the surface
cracking was approximately 4.5lam versus the nearly 35~tm fretting damage depth on
specimen A. This may indicate a few different findings. One, it may be unlikely to be
able to correlate the depth of fretting damage with the state of fatigue life of a specimen.
Two, the fretting damage on specimen A may be largely due to the increase in
displacement (slip amplitude) late in the fatigue life of the specimen due to crack
opening displacement. The normal force was applied under load control conditions not
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
56 FRETTINGFATIGUE: ADVANCES
displacement control. Therefore, there was no load relief as the fretting pad scarred
deeper into the faying surface of the dog-bone specimen.
It is interesting to note that the level of damage for specimen D was relatively
extensive. However, the damage was remote from the contact edges and did not
nucleate observable fatigue cracking. Although the specimen was cyclically loaded,
without fretting, for 1,200,000 cycles, it still showed no evidence of cracking. This is
likely due to the lower maximum stress level away from the contact edges. It is believed
that some debris became trapped between the fretting pad and faying surface of the dog-
bone coupon. Prior to experimentation there was no suggestion of scarring or damage to
explain the greater fretting damage experience by specimen D. Although specimen D
did experience more pronounced fretting damage than specimens C, E or F, no cracking
was discovered within or near the fretting damage region. This result bolsters the
suggestion of a fretting fatigue damage threshold.
Specimens C, E and F revealed fretting damage levels from 4-10gm deep and
specimen D a maximum fretting damage depth of approximately 20gm, yet none of the
specimens revealed fatigue cracking on the surface. Further all four of these specimens
were cyclically loaded for more than 1,000,000 cycles, some as many as 3,000,000
cycles, and none fractured. These results indicate that the damage induced by fretting
fatigue has a threshold. They suggest the possibility that fretting and fretting fatigue can
be managed through prediction, inspection and maintenance techniques. Through
understanding the need to arrest fretting and fretting fatigue damage prior to exceeding
the damage threshold, components can be maintained and remain in service for
prolonged periods versus those where fretting and fretting fatigue damage is disregarded.
This is a significant discovery within the scope of these experimental conditions.
However, a thorough statistically based experimental program would be necessary to
verify these results and develop a model to aid in the prediction and management of
fretting, fretting fatigue and related concerns.
It is important to document the threshold that has been demonstrated in this study
through adequately designed experiments. This contributes to the technical communities
overall understanding of fretting fatigue and the intricate variability of this complex
phenomenon.
Conclusions
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CLARK AND HOEPPNER ON DAMAGE/CRACKING STATES 57
Summary
The knowledge that can be gained through interrupted fretting fatigue experiments
using confocal and scanning electron microscopy can provide insight into the
understanding of this phenomenon. Through interrupted experiments a snap shot in time
of damage progression can be achieved. This progression of damage and analysis of that
damage can lend significant discovery to aid in the understanding of complex issues.
Confocal microscopy and scanning electron microscopy can be utilized to characterize
other insidious forms of damage. Studies on pit growth rate, characterizing pitting depth
and topography and the transition of pitting to fatigue cracking have been performed at
the University of Utah [9,12-14]. These studies have provided knowledge of how
corrosion induced damage has affected the fatigue life, including time or cycles to first
detectable surface crack and crack growth rates for a variety of aluminum alloys.
Interrupted experimentation can lead to an increased knowledge of the transition
materials experience from a pristine condition through failure.
Acknowledgement:
The authors would like to thank the University of Utah for the use of their facilities and
continued support of intellectual pursuits.
References:
[1] D. W. Hoeppner and G. L. Goss, "The Effect of Fretting Damage on the Fatigue
Behavior of Metals", Lockheed Aircraft Corporation, Office of Naval Research
Contract #N00014-71-C-0299, 1972.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
58 FRETTINGFATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FRETTING FATIGUE CRACK AND DAMAGE
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Yoshiharu Mutoh, 1 Jin-Quan Xu, 2 and Kazunori Kondoh 3
Reference: Mutoh, Y., Xu, J. Q., and Kondoh, K., "Observations and Analysis of
Fretting Fatigue Crack Initiation and Propagation," Fretting Fatigue: Advances m
Basic understanding and Applications, STP 1425, Y. Mutoh, S. E. Kinyon, and D. W.
Hoeppner, Eds., ASTM intemational, West Conshohocken, PA, 2003.
Abstract: Many factors, such as the amplitude of the cyclic load, the relative rigidity
of components and the frictional condition, play important roles in the fretting fatigue
process. This study has focused on the local singular stress field at the fatigue crack
tip or at the contact edge where the initial crack occurs, based on the numerical
analysis results with the use of finite element method (FEM) program ABAQUS. It is
proposed that all the effect of test conditions can be contained by the local stress field,
which would dominate the fatigue crack initiation and propagation. By comparing
with the experimental results, it was found that the initial fatigue crack should occur
at the point of maximum shear stress range near the contact edge, and would
propagate in the direction of maximum tangential stress range. An analytical
simulation of fretting fatigue crack propagation has been carried out. It was found that
a fatigue crack was always under the mixed mode conditions, the fracture path could
be estimated by the maximum tangential stress theory (AtTomax), and the propagation
curve could be characterized by the stress intensity factor range in this direction
( Z~r~o-Omax ).
Keywords: fretting fahgue, crack imtiation, propagation, simulation, fatigue life
Introduction
61
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
62 FRETTINGFATIGUE: ADVANCES
slip at the contact edge, which partially contains the combined effects of all the
phenomenological factors, have also been proposed to characterize the fretting fatigue
process. On the other hand, fracture mechanics is expected to assist strongly in the
evaluation of fretting fatigue crack initiation and propagation.
The most popular consideration [8-12] for applying fracture mechanics is to
introduce a vertical crack to the contact interface, though such a crack can not
represent the fretting fatigue fracture path. Giannakopoulos et al [13] considered the
kinking of an interface crack on the contact interface, to take the curve path of fretting
fatigue into account. Some three dimensional investigations [14,15] on surface
cracking due to fretting fatigue are also available. Skeikh et al [16] had analyzed the
stress intensity factors of an inclined crack from the contact edge by the finite element
method based on the pre-determined surface traction. This study focused on the effect
of the local stress field at the contact edge and the fretting fatigue crack tip.
Considering that fretting fatigue crack initiation and propagation are dominated by the
local stress field, and the interaction effects of the phenomenological factors can be
considered as being included in such a local stress field, observations, analyses and
evaluations of the fretting fatigue crack have been carried out from the viewpoint of
the local stress field. From experimental observations and analysis results, it is found
that the direction of the crack initiation agrees well with the maximum shear stress
range direction at the contact edge, where the stress range results in singular behavior,
and the direction of the crack propagation correlates well with the effective maximum
tangential stress range direction. It is also found that the fracture path can be
simulated well by the A t r 0 ~ theory, and the fretting fatigue life can be estimated by
the effective stress intensity factor range A K e ~ at the fatigue crack tip.
The stress range at the contact edge is singular due to the singular stress
distribution corresponding to the maximum and minimum loads during one cycle. The
singular stress range depends on the deformation type of the contact edge. The
deformation of the contact edge (point A) when the specimen subjected to a tension or
compression force can be distinguished as following three types, a) gapping, b)
sticking and c) slipping, as shown in Fig. 1. Therefore, during one cycle of loading,
nine types of deformation exist as shown in Table 1. It is obvious that if the contact
edge is under gapping deformation, no singular stress will appear. We denote such a
\
A A A
a) Gapping b) Sticking c) Slipping
Figure 1 - Deformation types of the contact edge
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUTOH ET AL. ON OBSERVATIONS AND ANALYSIS 63
non-singular stress field by a,jo(P), here e is the corresponding load. If the contact
edge is under sticking deformation, the singular stress field for a V-notch or bonded
edge will appear [17-20], as in the form o f avb(rl-'tb,P), where 1-;tb denotes the
corresponding singular order. If it is under slipping deformation, the slipping singular
stress field cr,,(r 1-z',P) shall appear, where 1-,t, denotes the singular order. The
details of the singular stress field will be given next. It can be easily understood that
there are six independent basic types of stress range field as shown in the table.
Therefore, it is necessary to evaluate the fretting fatigue behavior according to these
basic types. Because there is no stress singularity when the contact edge is under the
gapping deformation, we only need to consider the singular stress field for the cases
of sticking and slipping. For the purpose of generalization, we consider the fretting
contact model with an arbitrary contact pad as shown in Fig. 2. The material "1" is the
contact pad, its shear modulus and Poisson's ratio are denoted by GI and v~. The
material "2" is the fretting fatigue specimen whose elastic constants are denoted by
G2 and v2.
The theoretical solution of the stress field can be found in literature [17,18] for
this case. The general form of the stress field can be expressed as
Here, K, presents the stress intensity coefficient corresponding to the singular order
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
64 FRETTING FATIGUE: ADVANCES
7 r - 0 o + 0 , rpo 7 r - 0 o (1-21)sin(1-21)(oo
rp = 2 = -----~, Pl sin(1 + 21)fPo
(4)
(1 + 22) sin(1 - 42)(00
P2 =
sin(1 + 42 )tj00
The C a s e o f Slipping
O'02
= Kr~_l ~9 (3' -+ 1)(F- + 3' - cos 23'7r).cos(2-1)0+ F(3' + cos 23'~r) + 3.2 - 1 cos(.~ + 1)0
L (F + 3' - 1) sin 222 (F + 2 - 1) sm 23'~r
- F 3'+1
+ 3' -------~s l n ( 3 ' - l ) 0 - F + F - 1 sin(). + 1)0 }
"gr02
= KrX_l ~_ (3" - 1)(F + 3' - cos 23'1r) sin(3' - 1)O -I F(3' + cos 23'~r) + 3'z _ 1 sin(3' + 1)0
L ( F + 2 - 1)sin 23'1r (F + 3' - 1) sin 23'rc
(5)
3' 1 1
F
cos(3' - 1)0 + eos(~, + 1)0 l
+F+3'-I F+3'-I
T h e e i g e n - e q u a t i o n d e t e r m i n i n g the singular o r d e r is
p , u ( 2 / - 1) - ( / a ( 2 + 1) + ( 2 - 1 + F ) ( 2 sin20o + sin 2 2 0 o )
(6)
+ ~',(2 cos20o + cos220o)- p~(2 + 1)(2 oos20o - cos220o): 0
wh6re
2 sin 227r 1 + Aa + (1 - 2)fl + F(ct - fl)
F = -2-1
/.t (cos 22~r - 1) - sin 22,~r ' p - 1- a '
( F[1-2a +(2-1)fll-(~,-1)[(Z+l)a-(,~-1)fl] (7)
1-a
H e r e /~ is the coefficient o f friction at the interface. The D u n d e r s ' p a r a m e t e r s [22] a
and fl are d e f i n e d as follows:
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUTOH ET AL. ON OBSERVATIONS AND ANALYSIS 65
It can be found that the singular order is dependent on the coefficient of friction. The
solution of Eq.(9) is shown in Fig.3. It shall be pointed out that when the contact edge
is under slipping deformation, the stress singularity can be stronger than t / f T , which
corresponds to the energy dissipation due to the friction. Figure 4 shows the
dependence of stress singularity on the pad shape for the case that the material of the
pad and the specimen are the same. From Figs.3 and 4, it can be found that the higher
the frictional coefficient is, the stronger the edge singularity becomes. Therefore,
decreasing the coefficient of friction can be expected as an efficient method to
improve the fretting fatigue life. It is very interesting that when the frictional
coefficient is higher, for example, for the case that /1 = 1.0, the pad angle Oo = z / 2
presents the strongest stress singularity, which means that O0 = Jr/2 is the severest
shape leading to fretting fatigue, even worse than the case of larger angle.
1.0
0.9 % ~ o ,u = 0.2
0.8
o ,,=04
,~0.8
~ 0.7
~0.6
~0.~
0.51
0.4
0.~. I I ~ [ t I ~ I I t I I 1
0.0 0.2 0.4 0.6 0.8 0.3~
1.0 40 ~ 60 ~ 80 ~ 100 ~176176 ~
Frictional Coefficmnt u Shape Angle of the Pad
Figure 3 - Stress singularity for Figure 4 - Dependence of stress
various frictional coefficients singularity on the pad angle
Numerical Analysis
The analysis model and the element division for its one-fourth region are shown
in Fig.5. The FEM code ABAQUS was adopted. Frictional contact elements were
introduced along the interface. The materials of the pad and the specimen are the
same. The material constants were E = 210GPa and v = 0.3. The force P was
applied to attain the average contact pressure of 6 0 M P a on the pad foot. The
frictional coefficient is assumed as ,u = 0.8. The cyclic load was ao = 180sin cotMPa.
Figure 6 shows the deformation of the pad and the specimen under maximum tension
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
66 FRETTINGFATIGUE: ADVANCES
and compression. It can be found that the contact edge of the outside deformed as
gapping under tension, and as slipping under compression. Therefore, this analysis
example corresponds to the type 1 in Table 1. The maximum relative slip range
occurring at the edge was about 2.11/am. Figure 7 shows the stress distribution
along the interface. It can be found that there are three regions under the tension load,
i.e., the sticking region at the inside, the slip region at the middle part, and the gap
region at the outside of the interface. On the contrary, there are only two regions
under compression. It shall be pointed out that the size and existence of such regions
are dependent on the shapes of the specimen and the pad, the loading condition and the
frictional coefficient. It can be found that in the sticking region, the friction shear
stress is much smaller than that calculated by the Newton-Columb's friction law. This
fact means that the frictional coefficient cannot be calculated directly from the
~P
20 mm
12rnm i
+ !
! 8mn~
I
9 40 mm /I
a) Analysis model
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUTOH ET AL. O N O B S E R V A T I O N S A N D A N A L Y S I S 67
I_
a) Deformation under tension b) deformation under compression
Figure 6 - Deformation of the pad and the specimen
~. 2O0
~ti~_ Slipping I Oapl,~g
~ f a ' y ~ "
-t00
- 200
-300
100
200
1 S,!pp
TwO
6
-iO0
- 200 (Ty
f l i t / I l l
-4Q( ,, ..... i ...... ,,,l,,,,,,,,,i, ......
~1.0 -0.5 0.0 0.5 x/b 1.0
b) Stress on the interface under compression
Figure 7 - Stress distribution along the contact interface
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
68 FRETTINGFATIGUE: ADVANCES
3.0
o
2.0
o cry i _ A~m~= 1 . 6 5 / 3 = 0 55
0 r~r I - 3~,,,,-/= 1 - 0 . 4 5 3 = 0 . 5 4 7
observed shear force in the experiment. Figure 8 shows the logarithmic stress
distribution near the edge under the compression. It is found that the singular order
obtained numerically agrees with the theoretical result very well.
Fretting fatigue test was carried out for the observation of fretting fatigue crack
initiation and propagation. Both the specimen and the contact pad are cut out from a
SM430A plate, their geometry sizes are shown in Fig.9. The schematic diagram of the
fatigue test is shown in Fig.10. The fatigue test was carried out by an electro-
hydraulic servo-controlled fatigue test machine with a capacity of 98 kN under the
stress ratio, R, o f - 1 at frequency of 20 Hz. The average contact pressure is 60 MPa,
The coefficient of friction is measured as /z = 0.8 by a completely moving wear test.
To observe the fatigue crack initiation and propagation, the fatigue test was stopped at
160
~~ Specimen
< ,< 90 >i 1
, r_ 45 _, i ~510 I r - ~ Extensionmeter
~ Co~tact Pad
F,~ 3 , F . o . , o ~ . , , , o o ~po0,m~o. /~
I "Strain gage
II II ~ ~3._)
4:
Figure 9 - Geometry of specimen Figure 10 - Schematic diagram o f
and pad fretting fatigue test
certain cycles under the cyclic loading of 180MPa. The cross section was observed by
SEM. One ,example of the cross section is shown in Fig.ll. It can be seen that the
initial crack occurs in a very small angle from the contact interface at the outside
contact edge, and then kinks into the direction about 60 degree from the interface at
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUTOH ET AL. ON OBSERVATIONS AND ANALYSIS 69
its primary stage, and gradually propagates into the vertical direction to the contact
interface. The fracture path was measured by the SEM from multiple specimens
which are stopped at different loading cycles, as shown in Fig.12. The crack growth
rate was calculated from the well-fitted curve of the fracture path, i.e., the crack
growth rate in the tangential direction along the fracture path, not in the vertical
direction, is considered in this study. It is noted here that Figs. 11 and 12 were drawn
under the coordinate system shown in Fig.2.
In fatigue problems, the important factor is the stress variation range. Due to the
edge singularity, the stress variation during one cycle is very complicated. Figure 13
shows the stress range along the interface, obtained by the FEM analysis. It is found
that all the range of stress components becomes the maximum at the outside edge.
Therefore, it can be estimated that fatigue fracture will occur at the outside edge,
which coincides with the experimental observations. Considering that at the outside
edge the stress range is singular, the stress range in the polar coordinate is drawn as
Fig.14 (note the difference of the coordinate systems in Figs. 2 and 14). It is found
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
70 FRETTINGFATIGUE: ADVANCES
that the maximum shear stress direction located in a very small angle near the
interface, and the maximum tangential stress occurs at the direction about 0 =-120",
i.e., about 60" from the interface. Comparing with thd observed results shown in
Fig.11, it is possible to propose that the initial fretting fatigue crack may occur at the
direction where the shear stress range is maximum, and it will kink into the direction
where the tangential stress range is maximum (Acr0m~xtheory) immediately after
initiation. This fact means that the fretting fatigue crack initiation can be evaluated by
the singular stress range field. However, because the initial crack occurs in the
direction very near to the contact interface, due to the severe wearing and plastic
deformation of the contact interface, it is difficult to affirm when it occurs
and how long it is. It shall be pointed out that the life before crack initiation in
~" 6O0
b
4oo
<3
g zoc
r O.C
+~ - 200
o~ - 4 0 0
.0 -0.5 0.0 0.5 xlb 1.0
,~,1000
A,0 ~176
oO~
/I-'1
~176l
~
""
9 500
r~
0
%
r = 46.875//m ~A~X.~t
-50C
-45 -90 -135 -180
Angle (deg)
Figure 14 - Stress range in the polar coordinate
fretting fatigue only occupies several percent of the total fatigue life. Therefore, it is
reasonable to neglect it in the fatigue life evaluation of fretting fatigue. Because the
initial crack orientation has a strong effect on the subsequent crack propagation
behavior (such as kinking angle, growth rate, etc.), determining the crack orientation
has impact on evaluation of fretting fatigue.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUTOH ET AL. ON OBSERVATIONS AND ANALYSIS 71
By neglecting the life before the crack initiation, we can introduce an initial
crack to evaluate the fretting fatigue life as mainly dominated by the crack
propagation, in the direction where the shear stress range around the contact edge is
the maximum. The initial crack length is considered as the critical smallest crack
length [23] for which the linear fracture mechanics can be applied, i.e.,
a0 = (AK,h/Acr~
)2/zc (10)
Here, AKth is the threshold stress intensity factor range, and Acra is the fatigue
limit of the material under plain fatigue condition. For SM430A, it can be calculated
as a o ~ 80pro. It is easily understood that this initial crack is generally under mixed
mode condition, therefore, it should kink continuously until the crack tip loading is
mode I dominated. In plain mixed mode fatigue problems, it is well known that the
crack shall kink into the maximum tangential stress range direction (Ao'emax theory
[23], or in other words, into the direction where AKII = 0), and the fatigue properties
can be characterized by the stress intensity factor range ( A K o ~ ) in this direction.
Based on the Acrom= theory, the numerical simulation analysis by using FEM
program ABAQUS is carried out.
The crack is assumed as propagating 85pro for every step. The stress range
around the crack tip is calculated as the effective stress range, i.e., no overlapping of
the crack face is permitted. When the specimen is under compression load, the crack
face near the crack tip is dealt with using contact elements. The true contact regions
are determined by numerical procedures, assuming the coefficient of friction between
two crack faces as zero. Figure 15 shows the simulated crack propagation path. It is
obvious that this path coincides well with the fracture path by comparing with Fig.12.
Figure 16 shows the fatigue crack growth curve by using the parameter AKomax.
The plain fatigue test results under mode I are also shown in the figure. It is
noted here that AKom~x= AKI for single mode I test. It can be found that the fretting
fatigue curve agrees well with the plain fatigue curve except for the first step. This
means that the fretting fatigue crack propagation can be evaluated as the same as the
mixed mode crack propagation (i.e., using AKomax instead of AKr) in plain fatigue
except for the first step. The first step results correspond to crack initiation and its
first kinking step. Many reasons could be considered for its difference from plain
fatigue, such as the effects of small crack and the constant term in the stress range
field, the error of measured crack length and growth rate, etc. It can be considered that
this first step crack propagation has only a minimal effect on ~ e total fatigue life,
therefore, we can neglect it in the total fretting fatigue life evaluation.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
72 FRETTINGFATIGUE: ADVANCES
10 m
600
i0-12 ]
1 5 10 50
800 - - K~0)~ax (MPa m ~a)
Figure 15 - Simulated fretting fatigue Figure 16 - Fretting fatigue propagation
fracture path curve
Neglecting the first step of the crack propagation, the crack growth curve in
Fig.16 (i.e., the plain fatigue curve) can be expressed as
d a = 1.26 • 10-`2 (/~Omax)3 65 (l l)
dN
,-,, 350 t I I I I
~300
o mqjqp 9 ~
250 o
9
200
~ 150
100
Fretting faituge
50 t Plain fatigue
Estimate point
0 ] I I I I
103 104 105 106 107 10 s 109
Number of cycles to failure Nr
Figure 17 - S-N curve of the fretting fatigue and the predicted life
If we assume that the unstable crack propagation starts at the crack length of
a f = B/4 (B is the width of the specimen. Strictly, a: shall be determined by K1c,
here we use this relatively large value just for the convenience), then the fatigue life
can be predicted simply as
N = ~: da
1.26 x l0 -12 (A,K0max )365 - 1.17 x 10 6 cycles (12)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUTOH ET AL. ON OBSERVATIONSAND ANALYSIS 73
Figure 17 shows the comparison of the experimental results and the predicted result.
It can be found that the fretting fatigue life can be well predicted by the ACrOrnax
theory.
Conclusions
The fretting fatigue crack initiation and propagation are analyzed and observed.
The main results can be concluded as follows:
1) There are six basic types of stress variation range with different singularities for
different deformations at the contact edge of nine types.
2) The stress variation range becomes the maximum at the outside edge, where a
fretting fatigue crack should initiate.
3) A fretting fatigue crack initiates at the direction where the shear stress range is the
maximum.
4) Immediately after crack initiation, the crack kinks into the direction where the
tangential stress range is the maximum.
5) The fatigue crack is under a mixed mode condition, and should propagate in the
direction where the tangential stress range is maximum.
6) The fretting fatigue properties can be well described by using the parameter
M~o~, and the fatigue life can be evaluated by substituting AK~with AKo~ in
the crack growth rule of the plain mode I fatigue.
References
[2] Hoeppner, D. W., Chandrasekaran, V. and Elliott III, C. B., Fretting Fatigue,
ASTM STP1367, 2000.
[3] Adibnazari, S. and Hoeppner, D. W., "A Fretting Fatigue Normal Pressure
Threshold Concept," Wear, 160, 1998, pp.33-35.
[4] Vodopivec, F., Vizintin, J. and Sustarsic, B., "Effect of Fretting Amplitude on
Microstructure of 1C-1.5Cr Steel", Material Science and Technology, 12,
1996, pp.355-360.
[5] Waterhouse, R. B., Fretting Wear ASM Handbook, Vol. 18, ASM International,
t992, pp.242-256.
[6] Mutoh, Y., Tanaka, K., and Itoh, S., "Fretting Fatigue Properties of High Strength
Stainless Steel," Journal of the Society of Materials Science, Japan, (in
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
74 FRETTINGFATIGUE: ADVANCES
[7] Berthier, Y., Vincent, L., and Godet, M., "Fretting fatigue and Fretting Wear,"
Tribology International, 22, 1989, pp.235-242.
[8] Nix, K. J., and Lindley, T. C., "The Initiation of Fracture and Propagation of Small
Defects in Fretting Fatigue," Fatigue Fracture Engineering of Material and
Structure, 8, 1985, pp.143-160.
[9] Tanaka, K., Mutoh, Y., Sakoda, S., and Leadbeater, G., Fretting Fatigue in 0.55C
Spring Steel and 0.45C Carbon Steel, Fatigue Fracture Engineering of
Material and Structure, 8(1985), P. 129-142
[10] Hattori, T., Nakamura, M., and Watanabe, T., "Fretting Fatigue Analysis by
Using Fracture Mechanics," ASME Paper No. 84- WA/DE-IO, 1984.
[11] Li, Y., and Hills, D. A., "Stress Intensity Factor Solutions for Kinked Surface
Cracks," Journal of Strain Analysis, 25, 1989, pp.21-27.
[13] Giannakopoulos, A. E., Lindley, T. C., and Suresh, S., "Aspects of Equivalence
Between Contact Mechanics and Fracture Mechanics: Theoretical
Connections and A Life-Prediction Methodology for Fretting Fatigue," Acta.
Material 46-9, 1998, pp.2955-2968.
[14] Dai, D. N., Hills, D. A., and Nowell, D., "Stress Intensity Factors for Three
Dimensional Fretting Fatigue Cracks," Fretting Fatigue, Ed., Waterhouse R.
B., and Lindley T. C., 1994, pp.59-71.
[15] Hirakawa, K., and Toyama, K., "Influence of Residual Stress on the Fatigue
Crack Initiation of Press-Fitted Axle Assemblies," Fretting Fatigue, Ed.,
Waterhouse R.B., and Lindley T.C., 1994, pp.461-473.
[16] Sheikh, M. A., Fernando, U. S., Brown, M. W., and Miller, K. J., "Elastic Stress
Intensity Factors for Fretting Cracks Using the Finite Element Method,"
Fretting Fatigue, Ed., Waterhouse R. B., and Lindley T. C., 1994, pp.83-101.
[ 18] Atkinson, C., et.al., "Stress Analysis in Sharp Angular Notches using Auxiliary
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUTOH ET AL. ON OBSERVATIONSAND ANALYSIS 75
[19] Bogy, D. B., "Two Edge Bonded Elastic Wedges of Different Materials and
Wedge Angles under Surface Tractions," Journal of Applied Mechanics, 38,
1971, pp.377-386.
[20] Dempsey, J. P., and Sinclair, G. B., "On the Singular Behavior at the Vertex of a
Bimaterial Wedge, Journal of Elasticity, 11, 1981, pp317-327.
[21] Xu, J. Q., and Mutoh, Y., "Stress Field near the Contact Edge in Fretting Fatigue
Tests," Proc. of APCFS&ATEM'01, 2001, Sendai, pp.958-963.
[22] Dunders, J., "Effect of Elastic Constants on Stress in a Composite under Plane
Deformation," Journal of Composite Materials, 1, 1967, pp.310-322.
[23] Kitagawa, H., Yuuki, R., and Tohgo, K., "Fatigue Crack Propagation Behavior
under Mixed Mode Condition," Transaction of JSME, (in Japanese), A47,
1981, pp.1283-1292.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Tom Kimura 1 and Kenkichi Satoz
Reference: Kimura, T. and Sato, K., "Stress Intensity Factors KI and Kn of Oblique
Through Thickness Cracks in a Semi-Infinite Body Under Fretting Fatigue
Conditions," Fretting Fatigue: Advances in Basic Understanding and Applications, STP
1425, Y. Mutoh, S. E. Kinyon, and D. W. Hoeppner,, Eds. ASTM International, West
Conshohocken, PA, 2003.
Abstract: In this paper the formulas for calculating KI and K~Iof an oblique crack under
fretting fatigue loading conditions have been derived. The scheme of the formulation is
based on a method using Green's functions and the principle of superposition, i.e. the
Green's functions have been obtained through boundary element analysis for normal and
tangential localized forces on oblique crack faces and superimposed their results to
calculate two components of mode I and H. The formulas for K1 and KHwere expressed
as functions of crack angle, crack length and applied loading conditions, such as bulk
fatigue stress, contact pressure distribution and friction stress distribution. A user-
friendly program based on these formulas, then, has been developed to compute the
values of stress intensity factors K1 and KII under arbitrary fretting fatigue conditions. The
values of stress intensity factors for both normal and oblique cracks have been illustrated
as examples to understand the effects of crack angle and pad load distribution.
Keywords: fretting fatigue, stress intensity factor, boundary element method, Green's
function, principle of superposition
Introduction
It has been well known that fatigue strength of machines and structures is markedly
decreased due to fretting fatigue. Fretting fatigue is a form of fatigue where micro-slip
wear takes place at the contact interface of structural components subjected to contact
pressure, friction stress and cyclic fatigue stress. The fretting fatigue crack in the early
stage propagates in the direction oblique to the contact surface due to the effects of the
above pressure and stresses combined.
In order to estimate fretting fatigue lives, the stress intensity factors of cracks have
to be known. Evaluations of the stress intensity factors of fretting fatigue cracks KI and
1Graduate Student, Graduate School of Science and Technology, Chiba University, 1-33,
Yayoi-cho, Inage-ku, Chiba, 263-8522 Japan.
2Associate Professor, Department of Urban Environment Systems, Chiba University,
1-33, Yayoi-cho, Inage-ku, Chiba, 263-8522 Japan.
76
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KIMURA AND SATO ON STRESS INTENSITY FACTORS 77
K~, however, are rather difficult because of the combined stress fields and crack features.
Since it is a conventional but complicated way to determine the stress intensity factors
using finite element method or boundary element method, the formulas proposed by
Rooke and Jones [1] have been used assuming that fretting fatigue crack is normal to the
contact surface. However, because of simplification and complexity of determining mode
II stress intensity factor KIt the mode I stress intensity factor KI has been only adopted in
the conventional analysis for fretting fatigue problems. In order to evaluate the oblique
cracks in fretting fatigue, it is important to consider the effect of mode II stress intensity
factor as well.
In this paper, therefore, the authors have expanded the method of Rooke and Jones
to determine stress intensity factors KI and KII for oblique fretting fatigue cracks. The
Green's functions for oblique cracks [2] to adopt the principle of superposition were
obtained through boundary element analysis. The general equations for K~ and Kn have
been expressed as multi-term equations including parameters of crack angle, crack length,
plate width, contact pressure, friction stress and fatigue stress.
Friction stress [
ct pressure
4~
Fatigue stress
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
78 FRETTINGFATIGUE: ADVANCES
J +
q8
(a) (b) (c)
The magnitude of the normal force per unit thickness, p, which acts on the crack
surface, on the stress intensity factor was analyzed by the boundary element model shown
in Figure 3. The magnitude of the tangential force per unit thickness, q, was also analyzed
by the model. In the model, w and h are width and height of the plate respectively, b is the
loading point on the crack surface, a and 0 are length and angle of the edge crack
respectively. To evaluate the effect of unit force, the values o f p and q were taken to be
1 N per unit thickness. In this paper the stress intensity factors due to unit forcesp and q
are called the differential stress intensity factors dki and dku, for modes I and II
respectively. They were analyzed for various ratios of a/w and b/a under several values of
crack angle 0.
W W
\
Figure 3 - Boundary element analysis for the oblique crack model subjected to
localized forces p and q acting on the crack surface.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KIMURA AND SATO ON STRESS INTENSITY FACTORS 79
The values of the differential stress intensity factor obtained from the boundary
element analysis were summarized as Equations (1) and (2) by interpolation:
dkl - a__P
~a F~o(a,b,o)+----~'Fsq~/~ra (a'b'0) (1)
P Fs/p(a,b-,0)+----~-'Fslqx/zra ( ~ , b , 0 )
dkss- %/~ , (2)
where F~,, Fsq, F1~ and Fsiq are functions formulated as multi-terms.
Stress intensity factors due to Iocalized forces on the edge of the plate
Equations (1) and (2) can be used as Green's functions to obtain the stress intensity
factors ks and kss due to normal and tangential stresses distributions, a(b) and r(b)
respectively, acting along the oblique crack surface. Since the differential normal and
tangential forces per unit thickness, acting on the differential region db at the location b
are expressed as a(b)db and r(b)db respectively, the stress intensity factors due to the
whole distribution of a(b) and r(b) are given by integration of Equations (1) and (2) with
respect to b:
Yo ~y
b
crye,a
. ~ ' ~ Crxp,Q
~ o
0
(a) 0 (b)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
80 FRETTINGFATIGUE: ADVANCES
The values of a(b) and r(b) are calculated according to Timoshenko and Goodier [4] in
the following manner. The internal normal stresses c~xe,dyp and tangential stress rxye due
to external normal force per unit thickness, P, in Figure 4(a), are calculated by Equations
(5) to (7) given below, where the origin of the coordinate is set at the applied point of the
force P:
2P Xo3
(5)
dxe- ~ (x0 2+yo2) 2
2
2P xoY o (6)
dYe = 7L" (x02 +yo2) 2
2P x02y0
rxYe = rC (X02 + y02) 2 (7)
The internal normal stress de and tangential stress re are on the assumed crack line,
inclined at the angle 0 to the normal to the boundary. The coordinate b is set along the
assumed crack line from the origin O', as shown in Figure 4(b). By substituting the
following relations,
x0 = b cos 0 (8)
yo=bsin0-y , (9)
into Equations (5) to (7), and using Equations (10) and (11),
- 2 P b y 2 cos 3 0
ere = P " f e o ( b'O' Y) = zc(b2 + y2 _ 2by sin 0) 2 (12)
In a similar way, the internal stresses due to external tangential force per unit thickness, Q,
are given by
2Q Xo2y0 (14)
dxQ = ~ (X02 + y 0 2 ) 2
3
2Q Yo (15)
ay O = ~ (x02+y02) 2
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KIMURA AND SATO ON STRESS INTENSITY FACTORS 81
2
TxyQ = 2Q xoY o (16)
a" (Xo 2 + y02) 2
Stresses u(b) and fib) in Equations (3) and (4) are replaced by ap and rp of Equations (12)
and (13), then the differential stress intensity facDrs due to normal localized force P
acting on the boundary of the plate, dKIP and dKiIP are given by
P
dRIP = ~ o 0 (fFv "FIp+ fPr "Flq)db (19)
P
dKiIP = ~a~a foo(f,, ~ "Ft,p + f p~ "Fiiq)db (20)
The differential stress intensity factors due to tangential localized force Q acting on the
edge of the plate, dKtQ and dKnQ are also given using stresses aQ and rQ of Equations (17)
and (18) as stresses a(b) and fib) in Equations (3) and (4) respectively,
Stress intensity factors due to contact pressure and fi'iction stress on the boundary of the
plate
Therefore, the stress intensity factors due to distributed contact pressure and
friction stress in the contact surface can be obtained using Equations (19) through (22).
By integrating Equations (19) to (22) with respect to y assuming that contact pressure
between yl and Y2 is represented as a(y) in Figure 5, the stress intensity factors subjected
to contact pressure, KI~ and Kn~, are obtained:
g]a=fdgip - ~yl"~OCX(y)~
1 2
'Fip+ fPr "Flq)dbdy (23)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
82 FRETTINGFATIGUE: ADVANCES
dy .~ ~ _ ( Y )
Y1 ~Crack
Figure 5 - Stress distribution in the contact region.
Similarly, by adopting friction stress z'(y) in Figure 5, stress intensity factors due to
friction stress, KI~ and Kin, are given by the following expressions:
1 2
Kit = f dK]Q = -~a~a~ fOo r(y)'(fQo "Fip + for "FTq)dbdy (25)
1
K.r= f dKnQ = ~aza
~'~or(y)'(fQ. "Flip+ for "Fllq)dbdy (26)
The stress intensity factors, Ku and Krg, due to fatigue stress applied at the end of
the plate, are obtained from boundary element analysis separately, and they are
formulated as the following relations:
The total stress intensity factors, K~ and Kix, are obtained by the sum of three
components for each mode. They are given by
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KIMURA AND SATO ON STRESS INTENSITY FACTORS 83
Detailed expressions
The boundary element analysis was carried out to obtain Equations (1) and (2) for
the following conditions: at the constant of h = 4w, the ratio a/w of 0.005, 0.010, 0.016,
0.025, 0.040, 0.0625, 0.10, 0.16 and 0.25, crack angle 0 of 0, 15, 30 and 45 degrees, and
the twenty sets of b/a ranging from 0.025 to 0.975 were assumed. For determining the
exact values of stress intensity factors by boundary element method, the proportional
stress method proposed by Yuki et al. [5] was adopted. Figure 6 shows an example of the
relations between the functions F~p, F~q, Fnp and Fnq in Equations (1) and (2) and loading
point on crack surface, b/a, changing with 0 at the constant a/w = 0.005.
The differential stress intensity factors, dk~ and dk~, obtained from the boundary
element analysis were summarized by interpolation using a numerical software
Mathematica. The multi-terms interpolation with a/w, b/a and 0 for four factors of Fxp,
F~q, F~q, and Fup in Equations (1) and (2) was determined by the least-squares method.
The expressions are given by the following power series functions:
12 0
10 IO* "0.5 oO o o~ * * * - A ~
A
"1
8 .30:1 ~-a.s
A A
~ -2 A
4 -2.5 A
A " g
m0
A
A
2 "3 ~ac
0 "3.5 IA4E
0.2 0.4 0.6 0.8 0 0.2 0.4 0.6 0.8
b/a b/a
6
"-o6 ~
A ~X A ~ A A A A A A t ~ A 4
"0.8 2
"1 0
0 02 0.4 0.6 0.8 1 0.2 0.4 06 0.8
b/a b/a
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
84 FRETTING FATIGUE: ADVANCES
t
Fip, ilq(a,b,o)= 1 ~Clp,llq~jk(w) (b)Jo k (31)
where the indices i,j and k are integer values of 0 to 3, 0 to 8, and 0 to 3, respectively,
and c~,~k, ct~qk, C~qqkand c~qk are constants.
Finally, the Green's functions to obtain stress intensity factors subjected to contact
pressure and friction stress are given by the following expressions with the term of
y/(y+a):
L k
D 3
-05 25
-I: 1.3oi
- 15
0
-253- '
IO"
9',15 ~
(15
-35
030' 0
-4
-45 -05
02 04 06 08 02 04 06 08
y y
y+a y+a
4
35 0
3 o30 ~
'5
2
I
05
0
-05
02 04 06 08 02 04 06 08
y Y
y+a y+a
Figure 7 - Stress intensity factors due to localized forces.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KIMURA AND SATO ON STRESSINTENSITYFACTOBS 85
The functions Fu and FHf for the fatigue stress in Equations (27) and (28) are given as
z,J
(a/'
F.r, .,f (7a , 0) = y d, , .,, 7 0 j , (35)
where i andj are integers assuming values 0 to 4, and dl,j and dit,j are constants.
In the present paper, the distribution of contact pressure was assumed by the
following fourth order polynomial:
where po, pl, p2, p3 and p4 are constants. The friction stress is simply expressed using
coefficient of friction ,u, that is,
By introducing Equations (36) and (37) into Equations (23) to (26), adopting Equations
(33) and (34) as dKlp, dKw~, dKIQ and dKiio, and then executing the integration between
yl and y2, fretting pad area, and adding the components of fatigue stress, given by
Equation (35), the total values of stress intensity factors, Kl and KII, by Equations (29)
and (30) can be obtained.
Back ' ~
Front~Crack /
Plate/ [-.._____J
Line loadsalong Triangular1 (T1) Parabolic1 (P1)
front (LLF)or back(LLB)
of pad foot
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
86 FRETTING FATIGUE: ADVANCES
In order to compute the stress intensity factors from the above general expressions
a computer program has been developed by using Visual Fortran (vet. 6.5). The stress
intensity factors/s and KIt obtained from this program have been compared with the
results in reference [3]. Figure 8 shows the assumed pad load distributions in reference
[3], and Figure 9 shows the relations between mode I stress intensity factors, KI~ and KiT,
and crack length a under assumed distributions of normal and frictional pad load
respectively. The values of these stress intensity factors were obtained using the
parameters of plate width of 25 mm, pad width of 1.27 mm and thickness of 8ram,
assuming in each case a load of 1 N, and the results agreed with those of reference [3].
Figures 10 and 11 show the cases of oblique crack under the same loading condition.
Figure 10 shows the mode I stress intensity factors for crack angle of 30 degrees, and a
comparison with Figure 9 shows that the absolute values of stress intensity factors for 30
degrees crack are higher than those for normal crack. Figure 11 is the case of mode II,
and the different curves for each distribution are represented.
Figures 12 (a) and (b) show the total stress intensity factor of mode I for crack
angles of 0 degrees and 30 degrees under normal pad load of 1250 N, frictional pad load
of 700 N, and bulk fatigue stress of 35 MN/m 2. Each of the curves represents the stress
~ -0 002 ~ OOC
\LLB
T2/ I~LF 1 2
I
3
0 003 Crack length a (mm)
Normal pad load Frictional pad load
Figure 9 - Mode I stress intensity factors of normal crack for different distributions.
E Z 0 006
z 0004 v 0004
~ , ~ 0 002
-0 006
0
LLB
1 2 3
-000B Crack length a (ram)
Normal pad load Frictional pad load
Figure 10 - Mode I stress intensity factors of oblique crack for different distributions.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KIMURA AND SATO ON STRESS INTENSITY FACTORS 87
_o,o01
OOl 0.001
~ " 0008 ~ 0 . . . . . .
~ 1 2 3 4
0006
LLF
E 0 004
0002
~, 0002
" LLB '3 , - ~ -0.003
- 0 002 -0.004
Crack length a (ram) Crack length a (mm)
Normal pad load Frictional pad load
Figure 11 - Mode H stress intensity factors of oblique crack for different distributions.
5 5,
E
z
v
No Pad 1 2 ---i 1 2
\LLF
-3
Crack length a (mm) Crack length a (mm)
T2 LLF
LLZ
. LLB
I ~ ' \T1 ' \No Pad
1 2 1 2
Crack length a (mm) Crack length a (mm)
(a) Normal crack (0 deg.) (b) Oblique crack (30 deg.)
intensity factor for assumed pad load distributions and also for plain fatigue without
fretting. It was found that the stress intensity factor K1 in fretting fatigue, except for
assumed line load at the front of the pad foot (LLF), has greater value in the short crack
region than that without fretting, but in the long crack region their relation is reversed,
and the reversing points vary with crack inclination angle. In Figure 12 (b), the values of
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
88 FRETTINGFATIGUE: ADVANCES
Kj initially increase then decrease markedly with increasing crack length, due to the
greater negative values of stress intensity factor KI~ in normal pad load in Figure 10. This
may change the crack propagation direction or form the non-propagating crack. Figures
13 (a) and (b) show the total stress intensity factor of mode II, Ka. As can be seen, the
value of KII changes markedly depending on the assumed pad load distributions and crack
angles. As the results, the combination of K~ and KH affects the crack initiation and
propagation morphologies in fretting fatigue.
The above calculations show that the values of stress intensity factors are
significantly affected by crack angle and also pad load distribution. That is, in Figures 12
and 13, the two extreme pad load distributions, LLF and LLB, at 30 degrees give the
maximum and the minimum values of stress intensity factors of mode I and mode II, and
other pad load distributions give the values in the range. It is noted that the studies on
fretting fatigue crack growth must be carried out by using the actual pad load
distributions. The program developed in this paper can very easily obtain the values of
stress intensity factors for normal and oblique cracks by inputting the pad load
distribution as a function of a fourth order polynomial. Unfortunately, a finite or
boundary element stress analysis for determining pad load distribution is required before
using this program separately. Therefore, the authors are now trying to develop the
advanced program which can determine the actual pad load distributions automatically in
a program execution.
Conclusions
In order to obtain stress intensity factors, KI and Kn, in fretting fatigue conditions
easily, the authors have derived the general expressions formulated through determining
Green's functions and boundary element analysis, and executing their integrals. By using
the general expressions, stress intensity factors can be calculated by inputting the values
of crack length, crack angle, magnitude and distribution of contact pressure and friction
stress, coefficient of friction, fatigue stress and plate size. The general expressions are
applicable to the study of fretting fatigue crack propagation mechanism.
References
[1] Rooke, D. E and Jones, D. A., "Stress Intensity Factors in Fretting Fatigue,"
Journal of Strain Analysis, Vol. 14, No. 1, 1979, pp. 1-6.
[2] Kimura, T. and Sato, K., "Stress intensity factors for oblique cracks in fretting
fatigue," Computational Methods in Contact Mechanics/V, L. Gaul and C. A.
Brebbia, Ed., WIT Press, Southampton, 1999, pp. 303-312.
[3] Edwards, E R., "The Application of Fracture Mechanics to Predicting Fretting
Fatigue," Fretting Fatigue, R. B. Waterhouse, Ed., Applied Science Publishers,
London, 1981, pp. 67-97.
[4] Timoshenko, S. E and Goodier, J. N., Theory of Elasticity third edition,
McGraw-Hill, 1970, pp. 97-100.
[5] Kisu, H., Yuki, R. and Kitagawa, H., "Boundary element analysis for stress
intensity factors of surface crack," Transactions, Japan Society of Mechanical
Engineers (A), Vol. 51, 1985, pp. 660-669.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
D. R. Swalla 1 and R.W. Neu 1
KEYWORDS: fretting fatigue, crack nucleation, finite element anaIysis, critical plane
approaches
Introduction
Many different methods have been employed to predict damage and initial fretting
fatigue crack location and/or orientation. Empirical approaches based on continuum field
variables correlate the combination of relevant macroscopic variables such as stress,
strain, and slip range with observed crack nucleation sites. An example is the fretting
fatigue damage parameter (FFDP) developed by Ruiz et al. [1] in the mid 1980s in which
the site of crack nucleation was determined based on a combination of the tangential
stress component, CYT,the shear stress, ~, and the relative slip anaplitude, 8, in the form
FFDP = ~ 8 . The FFDP reliably predicts the location of the crack nucleus along the
fretting interface; however, no relevance is given to the orientation of the nucleated
crack.
Cracks have been found to form very early in the life of a component due to fretting
fatigue loading. These cracks tend to nucleate and grow along particular planes
dependent upon the cyclic state of stress and the material's microstructure [2,3]. A
89
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
90 FRETTINGFATIGUE: ADVANCES
A fretting fatigue crack tends to change direction as it grows further into the specimen
[3,5], as observed in Figure 2 [8]. In general, the fretting fatigue process can be divided
into three regimes. The nucleation regime is located within a depth of approximately 50
~tm from the surface. Once the crack has grown to a depth of about 50 ~m, the crack
angle changes from about 65 ~ +_5 ~ (see Figure l) to about 55 ~ + 5 ~ The next regime is
an intermediate region, which is still strongly influenced by the frictional force. It is
located between 50 l~m and 200 Ixm from the surface and the crack angle is near 25 ~ + 5 ~
The third regime is a crack growth region located greater than 200 ~ from the surface,
with diminishing frictional force influence. The crack gradually reduces to 0 ~ which is
the direction normal to the fatigue loading. Once the crack is beyond about 50 pxn in this
high strength steel, the growth rate can be characterized by fracture mechanics [6].
Additional experimental tests (not shown here) show that the observed changes in crack
angle with increasing depth are nearly identical for different stress ratios when the normal
pad force and contact geometry are the same [7,8]. These observations point to the
existence of a critical volume of material near the contact that is highly influenced by the
fretting loads, as evidenced by the change in crack angle as it grows further into a fretting
fatigue specimen. This critical volume is referred to as the Fretting Fatigue Process
Volume (FFPV).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SWALLA AND NEU ON FATIGUE PROCESS VOLUME 91
Critical plane approaches for describing multiaxial fatigue have been used to predict
fretting fatigue damage, initial crack location and orientation [8,9,10]. A wide variety of
multiaxial fatigue models exist in the literature, differing mainly in the selection of stress
and/or strain component combinations based on whether the fatigued material falls in a
shear or tensile manner [11,12,13,14]. Usually some fitting factor is applied in order to
correlate these stresses and/or strains with the number of cycles necessary to nucleate a
fatigue crack based on stress-strain life curves from either cyclic uniaxial or torsional
experimental tests. It can be quite difficult to choose an appropriate prediction model
because of the range of required assumptions related to issues that most directly affect the
integrity of fretting fatigue analyses. Some of these issues involve (a) the properties of
the interface between the two components (i.e., the coefficient of friction), (b) the
material model (i.e., elastic or elastic-plastic and homogeneous vs. heterogeneous), and
(c) the appropriate scale of the fretting fatigue process volume and crack length.
In recognition of these problems, the analyses presented in this paper emphasize
comparison of individual stress/strain components to more easily elucidate how the
combination of these components making up some common multiaxlal fatigue models
differ with changing FFPV depth. Two multiaxial fatigue models studied in this research
are the Fatemi-Socie-Kurath (FSK) [11,12] and Smith-Watson-Topper (SWT) [15]
models. The FSK model is often used for materials that tend to fall predominantly by
shear-cracking. In this model, fatigue life is dependent on the maximum eyelie shear
strain amplitude (AT/2) on a particular plane modified by the maximum normal stress
(t~n,,~x)to this plane.
_~_( I+kCr"'r~]= z:": f (2N,)b~+y/ f
(2N,) Co (I)
The loading parameters defined on the plane experiencing the largest range of cyclic
shear strain are represented on the left-hand side of the equation. The trn,,,~ is normalized
by cry,the cyclic yield strength, to preserve the dimensionless features of strain, and k is a
material dependent parameter. The ratio try/kis often replaced by the fatigue strength
coefficient (trf), which has been found to be nearly equal. The strain-life curve generated
from fully-reversed torsional fatigue tests is represented by the right-hand side, where ry'
is the shear fatigue strength coefficient, yy'is the shear fatigue ductility coefficient, bo is
the shear fatigue strength exponent, co is the fatigue ductility exponent, G is the shear
modulus, and 2N~is the number of reversals to the formation of a surface crack of a
certain length.
Alternatively, the SWT model is used for materials that fall predominantly by tensile
cracking and is defined as follows:
A6
--~-tr..mx= tr':2(2N,) 2b +tr': (2N,) b+c (2)
E ~
where Ae./2isthe maximum principalstrainamplitude on a plane and c~n,maxthe
maximum normal stressduring the cycleon thisplane. The fight-handside of the
equation is similarin form to the Fatemi-Socie-Kurathmodel (Eq. I),but is correlated
with strain-lifedata generated from uniaxialtesting.
Both models were developed for fatiguepredictionof cracks about I m m in length.
In thiscase,one could argue thatan arbitrarylengthscalehas alreadybeen applied(e.g.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
92 FRETTINGFATIGUE: ADVANCES
crack length equal to 1 mm). However, fretting fatigue crack nucleation occurs at a much
smaller scale approaching the grain size for a given material. Microstructural approaches
that are currently being investigated hold much promise to predict damage at this scale,
but are not sufficiently well-developed at this time [16].
In the past, most fretting fatigue damage prediction methods relied on calculation of
stress and strain results obtained at a point along the fretting fatigue contact surface.
However, the mechanisms that drive crack nucleation under fretting fatigue conditions
are well understood to be dependent upon a volume of material near the contact, not just
the stresses and strains at a point [17,18,19,20]. An engineering level analysis using
macroscopic material properties is still just an approximation of fretting fatigue
mechanisms occurring at a microstructural scale. For that reason, a number of averaging
methods, such as "line" averaging, critical distance, surface averaging, and volume
averaging, have been developed in an attempt to "smear" the effect of high stress/strain
gradients over some finite damage area/volume [21,22]. These methods allow for the
introduction of a length scale to engineering level analysis, albeit in a simplistic way.
The use of"line" averaging of stresses and strains in a 2-D analysis or plane averaging in
3-D analyses seems to be more relevant when evaluating multiaxial fatigue parameters to
predict maximum fretting fatigue damage, initial crack location, and crack orientation
along a particular critical plane.
Emphasis is placed on prediction of the fretting fatigue crack orientation because it is
desirable to be able to predict the fretting fatigue crack orientation from both a model
validation standpoint as well as from an actual physical standpoint. First, when
conducting analysis of any kind it is necessary to correlate as many results as possible
with experimental test observations in order to validate the model. The ability to predict
both the location of crack nucleation and orientation gives one faith that the model
captures the "right" mechanisms. Second, depending on the geometry in actual
components, the direction of crack growth may mean the difference between cracking
that results in catastrophic failure or alternatively, a crack that may eventually stop
propagating.
In this paper, the stress and strain results of an elastic finite element analysis (FEA)
are averaged along a potential critical plane for a range of depths into the specimen,
representing a FFPV. This volume averaging approach is used to determine the relative
influence of individual stress/strain components on crack angle prediction at various
depths and will be discussed in detail. Specifically, critical values of maximum average
shear strain amplitude ( h y c/2 ), maximum average normal strain amplitude (Arn/2 ),
and average maximum normal stress (~N.m~), as well as the FSK and SWT multiaxiai
fatigue parameters are calculated. These results are then compared to interrupted fretting
fatigue experimental results to show how the individual stress/strain components that
make up each parameter affect the crack angle and subsequent life prediction values
within a certain volume. Finally, the stress amplitude, stress ratio, and material model
(elastic vs. elastic/plastic) are varied in the FEA to determine their influence on life and
crack angle prediction within a FFPV using a volume averaging approach. It will be
shown that the initial crack angle prediction is dependent upon the size of the FFPV
under consideration and the dominant stress or strain component calculated within this
volume.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SWALLA AND NEU ON FATIGUE PROCESS VOLUME 93
Finite element modeling was used to simulate a fatigue specimen clamped between
two bridge-type fretting pads and loaded using a calibrated proving ring. The finite
element model shown in Figure 3(a) represents a symmetric section of this fretting
fatigue assembly. Experimental test details and specimen dimensions are listed elsewhere
[7,23]. The fretting pad is cylindrical with a radius of curvature equal to 15 mm. A
mapped mesh with element width of 10 ~trnwas used near the area of contact in a region
1 mm (length) x 0.5 mm (depth), and a free mesh was used elsewhere. A close-up of the
mesh near the contact is shown in Figure 3(b) along with the angle convention used in the
analyses. The positive angle direction is counter-clockwise. The 0~ referenge is
perpendicular to the bulk fatigue loading (or) direction.
The ABAQUS users manual states that a body initially in contact at one point, which
is the ease for a cylindrical contact, must be grounded with soft springs or dashpots to
eliminate rigid body motion in the early steps of the analysis [24]. A springy layer of
reduced stiffness elements has been added above the pad to perform this function, as well
as to model the compliance of the proving ring assembly in the experimental
configuration [25]. The elements along the top of the springy layer are fixed in the x- and
y-directions. The pad and specimen are fixed in the x- and y-directions along lines of
symmetry. ABAQUS CPE8R elements, which are 8-noded biquadratic quadrilateral 2-D
solid plane strain reduced integration elements, were used. Conditions of plane strain
were considered appropriate because the area of contact is much smaller than the width of
the specimen. Contact pair elements with small sliding assumption are used for the
contact elements between the fretting pad and the specimen. The specimen is defined as
the master surface and the fretting pad is defined as the slave surface. A Lagrange
multiplier formulation is used to enforce the sticking constraints along the interface
between the two contacting surfaces.
Figure 3 - Finite element model showing (a) overall geometry and boundary conditions,
and (b) mesh near contact area.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
94 FRETTINGFATIGUE: ADVANCES
The material properties of the pad and specimen are representative of PH 13-8 Mo
stainless steel. All material constants (fatigue, kinematic hardening, and elastic constants)
were obtained through experimental tests on the same heat of material used in the fretting
fatigue experimental tests [23]. The elastic constants are E = 192 GPa and v = 0.3. The
modulus of the springy layer was set to 0.001 * E, which was determined by trial-and-
error to match the ideal elastic Hertzian contact solution before addition of the bulk
fatigue loading. The theoretical Hertzian contact width (2a) is equal to 0.26 mm for these
loading conditions (2a/R = 0.017). There are approximately 30 eight-noded elements
encompassing the theoretical Hertzian contact width. A mesh density of this order has
been proven to capture the qualitative behavior of plastic strain evolution [26].
The elastic solution before addition of the bulk fatigue loading was verified via
Hertzian contact theory [27,28]. The error in the stresses along the interface was less
than 1.0%. For our exact experimental configuration and boundary conditions, there are
no analytical solutions that are presently available to perform further direct validation.
The classic Mindlin solution used by others performing similar analyses [25,29,30] does
not exactly apply because of the presence of the bulk fatigue loading, which cannot be
uncoupled from the sheafing (or frictional) force in our model. Furthermore, when the
bulk stress is included in the analytical analysis, it is assumed to be uniform in the fatigue
specimen [30]. In bridge-type apparatus the bulk stress varies along the length of the
contact. We chose to more closely represent our experimental conditions in order to
make closer links to experimental and model response; therefore, the mesh refinement
method was used to assure convergence for the elastic and elastic-plastic solution after
addition of the bulk loading.
The plastic behavior for selected analyses is described using a nonlinear kinematic
hardening model available in ABAQUS [24] with the evolution equation having the
form:
= c (* - - (3)
The constants are obtained using the cyclic stress-strain curve. For PH13-8 Mo stainless
steel, C = 157.3 GPa, y = 381.8 MPa, and 6 ~ = 909 MPa. The 0.2% offset monotonic
yield strength is 1286 MPa [23].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SWALLA AND NEU ON FATIGUE PROCESS VOLUME 95
results. For example, doubling the number of points beyond the minimum resolution
resulted in a percent difference of no more than 0.6% for line lengths up to 400 tan and
up to 100 points.
TY •
x~
I I/P&.II II I "
IA I I"b~ I I I
f i ' x l l I[~k, I I
1
I I 1"%111"391
11111",J IAI
Illlll~ll
The stress/strain values at the points are then transformed at a particular angle and
averaged along the "plane" for every increment in the cycle. This sequence is repeated
for angles corresponding to -90~ to 90~ in increments of 2 ~ to encompass a FFPV of
depth equal to radial length L. Finally, the predicted critical plane orientation is the
angle at which the average stress/strain, or combination thereof (depending on the chosen
multiaxial fatigue parameter), is a maximum along a plane of length L. Results shown in
subsequent sections are presented in terms of the FFPV radial length L, which
corresponds directly with the FFPV depth into the specimen. By varying the radial
length in the analyses, the influence of individual stress/strain components on the
accuracy of different multiaxial fatigue parameters used in fretting fatigue damage
prediction for a given crack length scale can be evaluated.
Both the FSK and SWT models were used to determine the critical plane using the
line averaging method just presented. In this case, the stress and strain components in
either model are replaced by their respective averaged values.
For the results in this section, the stress/strain response was obtained using an FEA
with an elastic material model and prescribed loading conditions matching the
experimental fretting fatigue conditions described earlier (see Figs. 1 and 2). The normal
force (P) equal to 343.4 N, was first imposed and then three full cycles were modeled by
incrementing ten load steps during the analysis. Three complete load cycles are
considered sufficient to capture steady-state response [26,31]. The remote fatigue stress
amplitude was 217 MPa with stress ratio, R = 0.1, which corresponds to maximum and
minimum fatigue loads of 34.9 kN and 3.49 kN, respectively. The prescribed coefficient
of friction is 1.5; previous analyses have shown that this value gives results that correlate
well with the observed experimental deformation field [32].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
96 FRETTINGFATIGUE: ADVANCES
= E ! q
g o.ol 6 =~
-~ 0 . 0 0 8 4 3
g
m
0.006 2
" 0.004 LJ-&.~.~.~--e~L~ b ~ , ' ~ i_~L_~• 0
-100 -50 0 50 100
Angle (Degrees)
Figure 4 - Values of AF/2,~, FSK, and SWT parameters on different planes at the point of
maximum damage on the interface (x/a = -0. 72 _+0.10).
The full-field Al'/2m~ calculated at the eentroid of th~ FEM elements is ~hown in
Figure 5. Near the fretting interface, the gradient in strain amplitude is quite large. The
calculation of stress/strain at a point on the surface does not capture the physical
significance of the effect that this steep gradient has on fretting fatigue damage within a
critical volume near the contact. The results shown in Figures 4 and 5 illustrate why
using cyclic stresses and strains at a point do not lead to accurate initial angle predictions
and also brings into question whether using stress/strain response at a point can be
successfully used for life prediction as well. The remainder of this section is devoted to
showing how critical values of maximum average shear strain amplitude ( A y c / 2 ) ,
maximum average normal strain amplitude (z~N/2 ), average maximum normal stress
(o'u.~,=), as well as the FSK and SWT multiaxial fatigue parameters influence initial
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SWALLA AND NEU ON FATIGUE PROCESS VOLUME 97
crack angle and life prediction using the volume averaging approach outlined in the
previous section.
2a = 0.26 mm
The Aye/2 and AeN/2 , calculated for a FFPV radii equal to L = 20, 40, 100, and
400 ~m, are shown in Figure 6, along with the critical angle predictions. Note that the
lines describing the AYe/2 and AgN/2 magnitudes have similar slope and drop
significantly with depth into the specimen. At any length, the magnitude of Aye/2 is
nearly double that of A6 N/2 . Furthermore, the values of either "A7'c/2 or A6N/2 at L
= 20 jam are double their respective values when L = 400 ~tm. The critical angle is the
angle at which the peak damage is predicted (similar to Figure 4). The number of points
averaged on a given plane are 5, 10, 15, and 50 points, respectively, for each of these line
lengths. The starting point on the interface is located at x/a = -0.72, which was earlier
calculated as the point of maximum damage. The angle prediction at L < 40 tan is 70 ~
using Ayc/2 , which corresponds well to experimental observations of fretting cracks of
this length (see Figs. 1 and 2). Recall that two critical planes are predicted, as shown
earlier in Figure 4, when Ay/2m~xis calculated at a point. However, when using
hyc/2 at any given depth, only one critical value is predicted.
As the radius is increased beyond 100 ~m, the predicted critical angle approaches 90 ~
for Ayc/2 , which indicates that the severity of the shear strain gradient into the
specimen has diminished significantly. For AeN/2 , the predicted critical angle stays
relatively constant (between 20 ~ and 30 ~ for any L < 400 txm and correctly predicts the
crack angle once it has grown to L > 100 ~tm. It is not predictive when L < 100 ~tm.
The cr N.,~x along with the critical angle prediction for FFPV radii ranging in length
from 20 ~tm < L < 400 lain is shown in Figure 7. The value of cru.m~xat L = 20 ~tm is
nearly double the value at L = 400 i.tm, which is similar to the trend in shear and normal
strains (see Figure 6). However, much of the reduction (about 60%) in tru,,~x occurs
within L < 100 kurt, unlike the strains, which exhibit a more gradual change in slope.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
98 FRETTING FATIGUE: ADVANCES
90 ~ . . . . ~, , ~ , ! .... ~ 0.012
,~, 60 ~ .............................. 0.01 x
30 ~ ; o - . ~ . . . . . i. . . . . . . . . i. . . . . . . ~ .... ~ 0 . 0 0 8 ,"
"
-=,
v
o L-
,-
. . . '. . " ," ..... .i "........ i'..... q 0.006 (t~
Figure 6 - The influence of the size of the process volume on the values of zXT,/2 and
As~ /2 and the associated angle of the critical plane.
o Angle 1
aNmax
90 ,L-~~T~-~-7~-~-~ 11oo ~:
60~- .... :.............................. 1000 .~.
~-30 . . . . . . . . . . . . . . . . . . . . . . . . . 700
<-60 600 z =
-90 500
0 100 200 300 400 500
Radial length (am)
Figure 7 - The influence of the size of the process volume on the value of ~r~,m~ and the
angle of the critical plane.
The predicted critical plane angle is equal to 10 ~ for L ___40 pan, changing to 5 ~ when
L = 100 ~aa, and finally to 0 ~ at L = 400 Jam. The critical angle calculated using ~ , . = is
not predictive for crack lengths less than 400 ~trn, but does correspond to the 0 ~ angle
observed in experiments once the crack has grown to a length that is well outside the
FFPV.
The critical plane angle predictions obtained using the FSK and SWT models are shown
in Figure 8 (a) and (b) for L = 20 I~m to L = 400 pal. For comparison, the critical plane
predictions using A y J 2 , ~-~'6~/2 , and ~ . m ~ are also shown. The schematics Figure
8 (b)) illustrate how the predicted critical angle changes with radius length. Note that the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SWALLA AND NEU ON FATIGUE PROCESS VOLUME 99
predicted critical angle is negative for L _<40 pm using the FSK parameter, but switches
to 65 ~ at 50 pm. When L=100 pan and greater, the FSK and Agc/2 critical angle
predictions tend to converge. Although the FSK parameter is primarily a shear-strain
based parameter, it is also influenced by the t r ~ , ~ .
The critical angle predicted using the SWT parameter is 15~ when L _<40 larn,jumps
up to 25 ~ when L = 50 Hm, then back down to 10~ or 15~ for 100 ~tm _<L < 400 lain.
From this plot, it is not clear whether the Ar or ~N,mx has a stronger influence on
the SWT parameter critical angle prediction. The crack angle prediction using either
parameter corresponds with the experimentally observed crack angle when 100 ~m < L <
400 tam.
+ u
-<><~
60 . . . . . . . 7, . . . . . . . . . . . . . . . . . . . i
; ...... 4
30 ~_~-- +i . . . . . . . :. . . . . . . . i. . . . . . . ~ .....
|= -~ ~ : : ~
| ~oo : ; :
-30 - ...... :. . . . . . . . 'r. . . . . . . :. . . . . . . . :. . . . .
(i,,i, ,=i
L (lan~A~ ~o 80 4o 2o
"90 1 t ~ ] I 1 t ~ I I [ $ i i i ; i I ~ i
(a) (b)
Figure 8 - (a) Predicted critical planes using different critical plane parameters (1o)
Schematic illustrating the angle of the critical plane with radius length.
The trend in predicted life for different parameters is shown in Figure 9. The fatigue
constants were obtained from uniaxial fatigue tests on smooth specimens conducted on
the same heat of material at Georgia Institute of Technology (constants given in Table 1).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
100 FRETTINGFATIGUE: ADVANCES
~( 1997MPa
e( 0.525
b -0.074
c -0.737
To approximate the shear-based fatigue constants from the uniaxial constants given in
Table 1, the von Mises assumption is used. The relationships between the shear and
normal components are:
trf i
43 (3)
yi'= xf38y' (4)
where trf' is the fatigue strength coefficient, ~y' is the fatigue ductility coefficient, bo =
b, and co= c.
The damage and crack lengths studied here are much smaller than the crack scale in
standard low cycle fatigue (LCF) testing. For that reason, it is more relevant to discuss
the relative differences between the various models rather than focus exclusively on the
life values on individual data points. As an example, interrupted fretting fatigue
experiments indicate that cracks nucleate and grow to a length of about 30 ixm in as few
as 200 cycles. Cracks considered long enough to indicate crack "initiation" in LCF tests
are often on the order of 1 mm in length.
There is a strong correlation between the Aye//2 and the FSK parameter and the
predicted life using As~r or SWT parameters are nearly identical when 20 Ixm -< L <
400 I~m. The latter suggests that A6N//2 is the predominate component influencing life
prediction when using the SWT parameter.
Both A?"c//2 and FSK are shear stress/strain dominated parameters, and both
A6~//2 and SWT are normal stress/strain dominated parameters. When L < 40 ~m and
at L = 400 ~m, all of the parameters predict similar lives. However, there is a certain
volume (around 100 Ixm in depth) in which the shear stress/strain and normal stress/strain
parameters diverge.
Given these results, it is clear that the most physically realistic damage parameter is
dependent on the size of the FFPV considered. First, it is clear that the A y J 2 is the
primary component influencing the initial crack angle prediction and therefore it seems
likely that it would be a logical parameter for correlating cycles to nucleation for this
material when L< 40 Ixm. When L = 40 to 100 Ixm, a transitional region exists in which
the normal stresses/strains, such as ~N.m~ and Ao~N//2 , become increasingly dominant,
as evidenced by the crack angle predictions. This is also the region in which the trend in
life prediction using a shear stress/strain or normal stress/strain parameter diverges
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SWALLA AND NEU ON FATIGUE PROCESS VOLUME 101
significantly. At this scale, use of a multiaxial fatigue model that incorporates both the
shear stress/strain and normal stress/strain, such as the FSK parameter, seems desirable.
When L > 100 ~tm, the normal stresses resulting from the bulk fatigue load are clearly
dominant. In this region, a tensile cracking multiaxial fatigue model similar to the SWT
model seems to be more appropriate. At this length a much greater proportion of the
crack length is oriented in a normal direction. Therefore, the optimal multiaxial fatigue
model depends on the length scale of the initial fretting fatigue crack in question, or in
other words, the size of the FFPV.
o FSK l
- - r~ - - SWT
0 ATe/2
)( A~ N/2
106~
z 105 ~-....
-i
lO 4
)
lO 3 i : ~
o 1O0 200 300 400 5OO
Radial length (~tm)
Parametric Study
The influence of stress amplitude, stress ratio, and material model (elastic vs.
elastic/plastic) on life and crack angle prediction within a FFPV using a volume
averaging approach is now considered. Unless explicitly stated otherwise, all
stress/strain results were obtained using elastic material properties.
Using a constant stress amplitude ((ra) of 100 MPa, the influence of stress ratio (-1.0 <
R -< 0.5) was considered with results shown in Figure 10. Both the critical angle
prediction and magnitude are rather insensitive (+ 5 ~ to the stress ratio. On the other
hand, when the stress amplitude is varied for a constant R= 0.1 (Figure 11), the
difference in magnitude of Ayc/2 is quite noticeable, with increasing stress amplitude
leading to larger values of Ayc/2 . However, the difference in critical angle prediction is
not significant when L > 20 lain. Even when L = 20 lam, the difference between the angle
prediction when 100 MPa < oa< 250 MPa is only about 10 ~
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
102 FRETTING FATIGUE: ADVANCES
-30 0.002
< -60 ~ ........ :. . . . . . ~........ ~. . . . . . ~ - ~ 0.001 t~
b~
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SWALLA AND NEU ON FATIGUE PROCESS VOLUME 103
the influence of the material model on ~-6"~-6~/2and the corresponding predicted angle is
shown in Figure 13. The AcN/2 is less sensitive than A7c/2 to the choice of material
modelThe FSK parameter follows similar trends as Aye/2 and the SWT follows the
~-~r trends, suggesting that FSK parameter is more sensitive to an elastic-plastic
material model. As shown here and in earlier figures, the use of an elastic material model
may result in non-conservative life prediction. However, even though the difference in
strain magnitude is somewhat significant in this case, the angle prediction is relatively
insensitive to the choice of material model using any parameter.
9o~,,~, ,,~ . . . . ~0.012
:o d : ', i ~
60 ~ ~ -i-I o Ang(ep) . . . . -~ 0.01 X~
| 0 - 0.006
O
-30 0.004
r., r
< -60 _ ~,7c/2 (ep) . . . . __ -j_f 0 . 0 0 2
1---~2(")I i
0 100 200 300 400 500
Radial length (am)
(a)
Figure 12 - Influence of material model (elastic vs. elastic-plastic) using AYc/2 on (a)
critical plane angle and (b) life prediction.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
104 FRETTING FATIGUE: ADVANCES
90 ~-I [ I I I [ I I ,~ I I I [ I ! I I I I I I I I 0.012
(D
-30
t,.-
<
-60 0.002 z
t~
Figure 13 - Influence of material model (elastic vs. elastic-plastic) on critical plane angle
using As s/2 .
Conclusions
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SWALLA AND NEU ON FATIGUE PROCESS VOLUME 105
Acknowledgements
References
[1] Ruiz, C., Boddington, P.H.B., and Chen, K.C., "An Investigation of Fatigue and
Fretting in a Dovetail Joint", Experimental Mechanics, Vol. 24, No. 3, 1984, pp.
208-217.
[3] Endo, K., and Goto, H. "Initiation and Propagation of Fretting Fatigue Cracks,"
Wear, Vol. 38, 1976, pp. 311-324.
[4] Pape, J.A., and Neu, R.W., "Fretting fatigue damage accumulation in PH13-8
Mo stainless steel", Submitted to International Journal of Fatigue, October
2000.
[5] Adibnazari, S. and Hoeppner, D.W. "Study of fretting fatigue crack nucleation
in 7075-T6 aluminum alloy", Wear, Vol. 159, 1992, pp. 257-264.
[6] Hills D.A. and Nowell, D., Mechanics of Fretting Fatigue. Dordrecht, The
Netherlands: Kluwer Academic Publishers, 1994.
[81 Neu, R.W., Pape, J.A., and Swalla, D.R., "Methodologies for Linking Nucleation
and Propagation Approaches for Predicting Life under Fretting Fatigue,"
Fretting Fatigue: Current Technology and Practices, ASTM STP 1367. D.W.
Hoeppner, V. Chandrasekaran, and C.B. Elliott, Eds., American Society for
Testing and Materials, 2000.
[9] Glinka G, Shen G, Plumtree A, A multiaxial fatigue strain energy density parameter
related to the critical fracture plane, Fatigue Fract. Engng. Mater. Struct.,
Vol.18, No. 1, pp. 37-46, 1995.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
106 FRETTINGFATIGUE: ADVANCES
[10] Szolwinski, M, Farris, T., "Mechanics of fretting fatigue crack formation", Wear,
Vol. 198, 1996, pp. 193-107.
[12] Fatemi, A. and Socie, D., "A Critical Plane Approach to Multiaxial Fatigue
Damage Including Out-of-Phase Loading "Fatigue and Fracture of
Engineering Materials and Structures, Vol. 11, No. 3, 1988, pp. 145-165.
[13] Socie, D., "Multiaxial Fatigue Damage Models," J.ofEng. Mat. and Tech.
ASME, Vol. 109, 1987, pp. 293-298.
[15] Smith, R.N., Watson, P., and Topper, T.H., "A Stress Strain Function for the
Fatigue of Metals," J. of Materials JMLSA, Vol. 5, No. 4, 1970, pp. 767-778.
[16] Goh, C,-H., Wallace, J.M., Neu, R.W., and MeDowell, D.L., "Polyerystal
Plasticity Simulations of Fretting Fatigue," International Conference on Fatigue
Damage of Structural Materials III, September 18-22, 2000, Hyannis, MA;
papers to be published in International Journal of Fatigue, submitted for review,
September 2000.
[18] Fouvry, S., Kapsa, P., and Vincent, L., "A multiaxial fatigue analysis of fretting
contact taking into account the size effect", Fretting Fatigue: Current
Technology and Practices, ASTM STP 1367, D.W. Hoeppner, V.
Chandrasekaran, and C.B. Elliott, Eds., American Society for Testing and
Materials, 1999.
[19] Lamacq,V., Dubourg, M., Vincent, L., "A theoretical model for the prediction
of initial growth angles and sites of fretting fatigue cracks", Tribology
International, Vol. 30, No. 6, 1997, pp. 391-400.
[20] Mura, T., and Nakasone, Y., "A theory of fatigue crack initiation in solids", J.
Appl. Mech., 1990, Vol. 57, pp. 1-6.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SWALLA AND NEU ON FATIGUE PROCESS VOLUME 107
[21] Slavik, D.C., Dunyak, T., Crdffiths,J., Kurath, P., "Crack Initiation Modeling in
Ti-6AI-4V for Smooth and Notched Geometries", proe. 5th National Turbine
Engine High Cycle Fatigue Conference (HCF '00), Chandler, Arizona, 7-9
March 2000.
[22] Krgo, A., Kallmeyer, A.R., Kurath, P., "Evaluation ofHCF Multiaxial Fatigue
Life Prediction Methodologies for Ti-6A1-4V. proc. 5th National Turbine
Engine High Cycle Fatigue Conference (HCF '00), Chandler, Arizona, 7-9
March 2000.
[23] Pape, J.A., and Neu, R.W., "Influence of contact configuration in fretting fatigue
testing", Wear, (225-229), 1999, pp. 1205-1214. 9
[24] Hibbitt, Karlsson & Sorensen Inc. ABAQUS User's Manual, Version 5.8, 1998,
West Lafayette, IN.
[25] MeVeigh,P.A. and Farfis, T.N., "Finite Element Analysis of Fretting Stresses",
J.Tribology, Vol. 119, 1997, pp. 797-801.
[26] Ambrico, J.M., Begley, M.R., "Plasticity in fretting contact", J. Mech. Phys.
Solids, Vol. 48, 2000, pp.2391-2417.
[29] Nowell, D. and Dai, D.N., "Analysis of Surface Tractions in Complex Fretting
Fatigue Cycles Using Quadratic Programming", J. Tribology, Vol. 120, 1998,
pp. 744-49.
[30] Nowell, D. and Hills, D.A., "Mechanics of Fretting Fatigue Tests", lnt. J. Mech.
Sci., Vol. 29, No. 5, 1987, pp. 355-65.
[31] Petiot, C., Vincent, L., Dang Van, K., Maouehe, N., Foulquier, J., Journet, B.,
"An analysis of fretting fatigue failure combined with numerical calculations to
predict crack nucleation", Wear, Vol. 181,1995, pp. 101-11.
[32] Swalla, D.R. and Neu, R.W., "Influence of Coefficient of Friction on Fretting
Fatigue Crack Nucleation Prediction", submittedto TribologyInternational,Sept.
2000.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Michele Ciavarella, 1 Daniele Dini, z Giuseppe P. Demelio 3
REFERENCE: Clavarella, M., Dini, D., and Demeho, G. P., "A Critical Assessment of
Damage Parameters for Fretting Fatigue," Fretting Fatigue.Advances in Basic
Understandmg and Apphcations, ASTM STP 1425, Y. Mutoh, S. E. Kinyon, and D. W.
Hoeppner, Eds., ASTM International, West Conshohocken, PA, 2003.
ABSTRACT. Fretting Fatigue (FF) has been considered as fatigue in a region of stress
concentration due to the contact accelerated by mechanical erosion (possibly enhanced by metal
transfolmatlons and/or chemical reactions in an aggressive envtronment). Whether the effect of
erosion is significant or not is not clear. However, recently a more precise quantification of the
effect of stress concentration has been attempted (some authors have used the terminology
"crack analogue" and "notch analogue"). Most.practical cases are concerned with finite stress
concentration, so that a "notch analogue" criterion seems more appropriate, like for example in
the Hertzlan FF set of experiments hke those on Alumlnium alloy (A1/4%Cu, HE15-TF) by
Nowell in the late '80s, and (A12024) by Farris in late 90s. Application of the "notch analogue"
with a simple stress concentration criterion is usually overconservative for a notch (and indeed it
is for the experiments considered, although it may not in general because of mechanical erosion
effect in the FF case), so that "averaging" methodologies have been proposed where
unfortunately the best-fitting averaging constant turns to be not just a material constant. In fact,
in the present paper the "best fitting distance" is shown to be much smaller than what expected
from existing Kf criteria.
KEYWORDS: Fretting fatigue, fatigue, gas turbine engines, HCF, LCF, surface damage, stress
concentration, SCF
Introduction
As generally defined, Fretting Fatigue (FF) is a phenomenon caused by the synergy
between mechanical erosive surface damage and initiation o f cracks due to the stress field
(although this synergetic effect has never been precisely quantified). Attention has been
for long time focused on minute surface tangential motion arising between components
pressed together by normal forces and subjected to oscillatory loads or vibratory motion
(one o f the sites o f greatest concern with FF is in the compressor stages o f gas turbine
engines, and particularly blade-disk dovetail joints).
FF is responsible to many in service "mishaps" in gas turbine engines, for which H C F
(High Cycle Fatigue) is itself the largest single cause o f failure. Despite the remarkable
progress, FF is still one o f the most "inexact" areas o f fatigue, where effort is now being
108
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CIAVARELLA ET AL. ON ASSESSMENT/DAMAGE PARAMETERS 109
focused. Inparticular, it is not clear, to date, ifFF is (i) a surface damage phenomenon, or
(ii) it is simply fatigue from a stress raiser feature. Even though surface damage
parameters can be computed analytically or quasi-analytically in a wide range of contact
FF conditions [1-6], attempts to use method (i) have so far remained very empirical and,
as it will be shown in the present paper, only a vague qualitative correlation with fatigue
life is obtained; moreover, a precise and quantitative correlation is hardly possible in the
future as connection to the standard fatigue law understanding is not foreseeable.
Attempts to use method (ii) have surprisingly been very limited until recently (crack and
notch "analogues" have been proposed by the MIT group in [7,8]), but the use of notch
analogues seems to be the most promising. We discuss aspects of both approaches in the
following paragraphs.
. .
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
110 FRETTINGFATIGUE: ADVANCES
F2-Nfailure
*Series 1 nSeries2
,, Series 3
O
I!
,l* i
I,A
m A
ql,
,t
In the present paper, we computed these parameters for the Hertzian experiments in
(Farris & Szolwinski, 1998, [14]) and (Nowell & Hills, 1988, [1514). The original stress
analysis in [14, 15] has also been improved to consider finite thickness of the specimen, 5
with a minor correction for [14], but quite large for [15] in terms of increase of the
surface tensile stresses. Also, in [15] there was no surface damage parameter calculation.
Results are synthetically shown in Fig. 1 for the Ruiz' parameter, F2, showing a power-
law correlation similar to fatigue S-N curves (the scales are different and [14] have much
lower fatigue life and concentrated in the range 200-900 x 103 cycles, whereas [15] span
a wider range with run-out in several cases (smaller contact areas) >107 cycles.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CIAVARELLA ET AL. ON ASSESSMENT/DAMAGE PARAMETERS 111
400 [] Sigma_maxNowell
SWT power-law
300
~ 2o0
100
0 t ~
Despite a quite large scatter, the data seem to fit the simple model proposed in [14].
However, this is surprising if we consider that a Kt criterion is usually largely over-
conservative when the gradient of the stress field is high as in the contact region. Using
this simple stress criterion for the full set of the Nowell and Hills' data [15] would be
reasonable for the large contact area sizes, but extremely conservative for the set of
smaller contact areas where much higher fatigue life is found. A simple SWT approach is
then inadequate to predict the size effect fretting fatigue life. This is clearly pointed out in
Fig. 2 where, by comparing the maximum tensile stress with the SWT~tr=, (see Eq. (3)
written below), the difference between the real maximum stresses and SWTx,~e= is larger
for the "run-out" experiments (small contact areas) than for the finite life ones (large
contact area) failing at small number of cycles. This effect can be qualitatively explained
with the stress gradient increment of the internal tensile stress associated with the
decrement of the contact area shown in Fig. 3.
One possibility to consider a less over-conservative prediction and take size effect
into account is based on an empirical averaging of the stress field [19,20]. However,
Refs. [19,20] havefound that there is no unique "material constant" distance over which
the results fit the data in Nowell and Hills [ 15] reasonably well.
Various criteria exist for the fatigue knock down factor Kf, which is by definition
l<Ke<Kt, where Kt is the stress concentration factor. An alternative to Kf is often defined
via a notch sensitivity, 0<q<l:
(K s - 1)
q= (K,-1) (1)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
112 FRETTING FATIGUE: ADVANCES
Ot
i ;
! i " -250.
i - -200-
8
9 _ _~50
! - -I-00.
0
-:. . . . . 50,
1
i .... i . . . . 51) '
4 ~n
, " ~3UU
r
'i~ -: 250 -
D.
; ,: 2ee -
,, . . . . . . . . . . : -15o-
t~
J
=.
ol -108-
c
_o
{o ~ ' _
a} 1
e~
0
0.
oE 4] 15
u)
~J, ~/ 0!~ 0.
~9
4.*
ill ......... :......... ~~
Ii 4r i i
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CIAVARELLA ET AL. ON ASSESSMENT/DAMAGE PARAMETERS 113
Recent work by Taylor [21,22] has shown that Neuber and Peterson's notch
sensitivity factors belong to the averaging techniques. In particular, in order to make
them consistent with fracture mechanics, the averaging distance needs to be connected to
the intrinsic material defect constant (also knows as "Topper" constant), depending on
fatigue limit A~I and threshold AKt~, as:
1 (~v,h) 2
(2)
a0 = ~- ~,~7-Gx)
Specifically, the simplest method is to use the stress at distance ao/2 from the trailing
edge of the contact, which is sometimes called the "hot spot" stress (ahot-,pot).Either ways,
the stress has to be compared with the predicted SWTst..... [14]:
= (2N)2b ,, 1
+~ E
VL ' / ]l-v2
(3)
where NUis the failure life and E, v, or/', er a, and b are material constants that could
be extracted from a uniaxial fatigue experiment and indeed are known for A12024-T351
and HE15-TF to present values shown in Tablel. The results are plotted in Fig. 4.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
114 FRETTING FATIGUE: ADVANCES
Predictions-Nowell's data
500
450 I . Maximum tensile stress (with finite thickness correction)
t -- SWT based on 'power-law' prediction
400 J
" A Hot Spot (best fit)
350 -4
f o Hot Spot (Topper constant)
250 9
o 00t .....
t
!~ 100J i,i i
|
5o ~
0 , t i ,
O.E+O0 2.E+06 4.E+06 6,E+06 8.E+06 1 .E+07
N f a i l u r e [n* c y c l e s ]
Predictions-Szolwinski's data
400
150. o
41, 9 9 o0 9 ~ 9
100 9 9, ~ AI**A , == A%
9 ,,. .
!50.
4=0
i .~00,
9%| ,~*
.| =
%*
. g*
*=
.| ~ =
AA,e,
|
A &
0
| @ Q
150.
* Maximum tensile stress (with finite thickness correction)
100 - .... SWT based on power-law prediction
" Hot Spot (best fit)
50.
e Hot Spot (Topper constant)
0
2.E+05 3.E+05 4.E+05 5.E+05 6.E+05 7.E+05 8.E+05 9.E+05
N f a i l u r e [n ~ c y c l e s ]
b)
FIG.4 - - A comparison between different fatigue approaches." a) Nowell's
experimental data; b) Szolwinski ' experimental data ("Best fit" corresponds to ao/2= 15
~m).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CIAVARELLA ET AL. ON ASSESSMENT/DAMAGE PARAMETERS 1 15
The hot spot results obtained using the "Topper" constant (we used ao = 91 l~m for
Nowell's material, see [20] and ao = 129 Itm for Szolwinski's data, see [22]) are still very
under-conservative, as the best fit would only occur for much smaller hot spot constants
(around 15/zm).
This result does not necessarily imply that a prediction based purely on fatigue is
incorrect: it is possible, for example, that this averaging constant is not just a material
constant, but depends on geometrical features. Therefore, there is not enough evidence to
suggest that the difference is due to fretting per se, returning to the well-known concept
that FF is a combination of both surface damage and fatigue.
Similar conclusion is drawn from Fig. 5 where only the best-fit hot spot constants (15
lzm) is used to fit correctly the size effect experimental results.
.=. 5.E+06
\
.=
:3 4.E+06 .\
z 3.E+06
2.E+06
1.E+06
0.E+00 i i i ........ i .... i
Conclusions
Surface damage parameters have been found to be qualitatively correlated to FF life
for both sets of experiments [14,15], particularly F1 and F2. Obviously, these parameters
are of empirical nature and suffer from the drawback of being uarelated to any other
fatigue parameter. Further, they would depend on surface conditions, particularly friction
coefficient of the pair of contacting materials, as typical in tribology. On the other hand,
"pure fatigue" lifing methodology also requires some caution. In [15] it was apparently
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
116 FRETTINGFATIGUE: ADVANCES
found that a simple Kt approach would make conservative results. However, we have
shown that this may be just a coincidence of fretting effect nearly cancelling the notch
sensitivity effect, which we expect because of high stress gradient. Therefore, there is no
reason to believe that the "additional" fretting effect on fatigue life would be always so
simply taken into account. In other words, a Kt approach neglecting the additional
fretting damage contribution may result in underconservative prediction under
appropriate circumstances: in particular, when the notch sensitivity of the material is not
so high and the fretting damage is large.
A specific FF-related notch sensitivity, or alternative additional parameters,
depending again on surface conditions, friction and materials in contact, may be required.
Fatigue criteria are more likely to be successful in the future, but if a methodology is
to be expected to be conservative, fundamentally solid and amenable to standardisation, a
lot better understanding of the "notch sensitivity" effect is needed. Use of stress
concentration alone, as suggested in some existing "notch analogues" criteria (Farris,
[15], Giannakopoulos et al., 2000 [8]), is not necessarily a conservative approach, and
could be made arbitrarily over-conservative when the Kt factor becomes large.
Introducing a Kt factor design limit would probably render inadequate the majority or
existing designs! On the other hand, using existing "best-fitting" averaging
methodologies (Nowell & Arafijo, 2000 [19], Arafijo, 2000 [20]) has proved to be
questionable and empirical. In fact, the "best-fitting" distance turns out to be very much
dependent not just on material constants but also on loading conditions, and it is to be
expected that other dependencies (particularly on geometry), not emerged in existing
experimental validation, could be also found.
References
[1 ] Ciavarella, M. and Demelio, G., "A review of analytical aspects of fretting fatigue,
with extension to damage parameters, and application to dovetail joints,"
International Journal of Solids and Structures, 2001, Vol. 38 (10-13), pp. 1791-
1811.
[2] Ciavarella, M., "The Generalized Cattaneo Partial Slip Plane Contact Problem. I-
Theory", International Journal of Solids and Structures, 1998, Vol. 35/18, pp.
2349-2362. II-Examples, pp. 2363-2378.
[3] Ciavarella, M., Demelio, G., and Hills, D. A., "The use of almost complete Contacts
for Fretting Fatigue Tests", Fatigue and Fracture Mechanics: twenty-ninth Volume,
ASTM STP 1332, T.L.Panontin and S.D.Sheppard, Eds., ASTM International, West
Conshohocken, PA, 1999a, pp. 696-709.
[4] Ciavarella, M. and Hills, D. A., "Brief note: some observation on oscillating
tangential forces and wear in general plane contacts," European Journal of
Mechanics, Part A: Solids, 1999, 18, pp. 491--497.
[5] Ciavarella, M., Demelio, G., and Hills, D.A, "An Analysis of Rotating Bending
Fretting Fatigue Tests using "Bridge" Specimens." Fretting Fatigue: Current
Technologies and Practices, ASTM STP 1367, D.W. Hoeppner, V. Chandrasekaran
and C. B. Elliot, Eds., ASTM International, West Conshohocken, PA, 1999b.
[6] Ciavarella, M., Hills, D. A., and Monno, G, "The influence of rounded edges on
indentation by a flat punch." IMechE part C - Journal of Mechanical Engineering
Science, 1998, Vol. 212, No. 4, pp. 319-328.
[7] Giannakopoulos, A. E., Lindley, T. C., and Suresh, S., "Aspect of equivalence
between contact mechanics and fracture mechanics: theoretical connections and a
life-prediction methodology for fretting-fatigue," Acta Metallurgica Inc., Elsevier
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CIAVARELLA ET AL. ON ASSESSMENT/DAMAGE PARAMETERS 117
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LIFE PREDICTION
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Carlos Navarro, l Mercedes Garcla, / and Jaime Dominguez 2
Reference: Navarro, C., Garcia, M., and Dominguez, J., "An Estimation of Life in
Fretting Fatigue Using an Initiation-Propagation Model," Fretting Fatigue: Advances
m Basic Understanding and Applications, STP 1425, Y. Mutoh, S. E. Kinyon, and D. W.
Hoeppner, Eds., ASTM International, West Conshohocken, PA, 2003.
Abstract: This paper proposes a method for estimating the total fatigue life in fretting
fatigue. It compares the fatigue life of some specimens obtained in various series of
fretting fatigue tests wath the estimates of total fatigue life using a model that separately
takes into account the initiation and propagation of the crack, The experimental tests used
a spherical contact and were conducted on an aluminum alloy (A1 7075-T6). The
initiation of the crack is considered using the multiaxial fatigue criterion of McDiarmid
together with the theoretical distribution of stresses for the given loads applied in each
test. The propagation of the crack is considered using two different laws of propagation,
Paris law and a curve given by Lankford that would represent the upper limit for the crack
propagation velocity (lower limit for fatigue life) when the crack is short. These two
estimates are an upper and lower bound respectively of the fatigue life of the specimen;
the actual life lies in between.
Introduction
121
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
122 FRETTINGFATIGUE: ADVANCES
the prediction of the endurance under the design loads and many efforts and resources are
dedicated to it. This is a difficult problem and there are different approaches that are
aimed at solving it [2,3].
There is a general agreement that the fretting fatigue process has two different phases:
the fatigue crack initiation and crack propagation, which are due to different mechanisms.
Some methods to estimate the fretting fatigue life are based on the initiation mechanism,
and use the data obtained in tests with smooth specimens under completely reversed
loading, combined with various multiaxial fatigue criteria. These methods are more
frequently used when the initiation phase dominates over propagation. Another approach
consists in the use of linear elastic fracture mechanics. In this case the initiation life is
assumed to be small compared to propagation [4]. Another method is to combine
initiation with propagation using a fixed crack initiation length [3]. This length tries to
determine the separation of the process of initiation and propagation. The total life would
be the sum of the number of cycles required to initiate a crack and the number of cycles to
propagate a crack of this length until final fracture [5]. A step forward in this study is, as
in the latter case, to combine initiation and propagation, but instead of previously
choosing a fixed initiation length, it will come out as a result of the calculations. There
are different ways to make these calculations developed by several authors [6, 7,8] for
notched specimens, although they have not been applied to fretting fatigue.
This paper presents a similar method to the one proposed by Socie [8], which
combines initiation and propagation defining a non-arbitrary crack initiation length, to
estimate the life obtained in a series of fretting fatigue tests with spherical contact.
Initiation-Propagation Model
The method used in this paper is a modification of Socie, Morrow and Chen [8] for
fatigue life analysis of notched members. This modification takes into account the
multiaxial stress field developed in fretting fatigue with spherical contact. The authors
calculated two curves as a function of crack depth, i.e., along the hypothetical crack path:
(a) a crack growth rate caused by crack initiation mechanisms from low cycle fatigue
concepts and (b) the damage rate during the crack propagation phase from linear elastic
fracture mechanics (LEFM) concepts. The first one is obtained estimating, for every point
along that path, the number of cycles needed to initiate a crack and then calculating the
derivative. Hence, something that could be considered as a crack propagation rate due to
initiation is obtained. This function decreases with depth, and for points close to the
surface it is higher than the classical crack propagation rate due to fracture mechanics,
which increases with depth. Therefore, a hypothetical crack close to the surface would
grow faster by initiation than by propagation. At a certain depth, the two curves cross, and
from then on the crack grows faster by propagation. According to their proposal, this
point sets what they call the crack initiation length. The crack initiation life, Ni, would be
the one corresponding to this point and the crack propagation life, Np, would be the
number of cycles needed to propagate a crack from that point until final fracture.
Instead of calculating the growth rates as explained, a similar but numerically
equivalent method is used [9]. Along the hypothetical crack path, the fatigue life at each
point based on low cycle fatigue is calculated, Ni. This would be the number of cycles
needed to initiate a crack at that point. Also, for each point, the number of cycles needed
to grow a crack from that point to the final crack length, Np, are calculated using LEFM.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAVARRO ET AL. ON INITIATION-PROPAGATION MODEL 123
The sum of N, and Np gives the total life associated to each point, considered as the point
where the growth law changes from initiation to crack propagation. Therefore, the life of
the specimen would be the minimum of that curve, (Figure 1). The point at which the
minimum is produced also defines the crack initiation length, which coincides exactly
with the one calculated using the procedure explained in the former paragraph [8].
4.0x106
3.5x106 ,t N total
9 N propagation
3 0xl0 B"
9 N initiation
2.5x106"
minimuml .
2.0x106.
~ A 9 i
1,5x10a-
1.0x106-
5.0x105-
0.0 I I I I
0.00 0.02 0.04 0.06 0.08
Depth (mm)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
124 FRETTINGFATIGUE: ADVANCES
perpendicular to the surface and from points close to the edge of the contact zone give
initiation curves that are similar but give higher values of the initiation life when
compared to the crack located exactly on the edge. This implies that, supposing the crack
grows perpendicular to the surface, the most critical crack seems to initiate at the edge of
the contact zone, therefore this location will be chosen for all the calculations.
In order to calculate the initiation curve, McDiarmid multiaxial fatigue criterion will
be applied [12]
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAVARRO ET AL. ON INITIATION-PROPAGATIONMODEL 125
A rmo~ t
+ o'.o~ -- o-q (1)
2 2O'rs
where Arm~ is the maximum increment of tangential stresses, tYmo~is the maximum
normal stress in the direction perpendicular to the plane where Ar is maximum (Armax), t
is the fatigue limit in torsion and errs is the ultimate stress. This criterion is used together
with the strain-life relationship
where Ae is the normal strain obtained in tests with smooth specimens under completely
reversed loading, E is the Young modulus, N, is the number o f cycles to the initiation of a
crack and the remaining parameters are constants that depend on the material and are
determined experimentally. The values for the constants are taken from [9] for the
material A1 7075-T6, cQ= 1917 MPa, b = -0.176, e ) = 0.8, c = -0.839. In order to
combine both equations, (1) and (2), McDiarmid criterion is applied to a fatigue test of a
smooth specimen under completely reversed loading, • a. The plane where the maximum
shear stress can be found is at 45 ~ from the loading direction. In this plane, the amplitude
of shear stresses is a/2 and the maximum normal stress in the direction perpendicular to
such plane is a/2. The value of the equivalent stress is
o- t o-
O'eq = - - + -- = cr . f (3)
2 2~rrs 2
where
f= 1+ (4)
Writing (2) in terms of stress instead of deformation and multiplying both terms by (4)
yields
The latter equation gives the number of cycles to initiation given the equivalent stress
calculated with eqn. (1).
As it was said earlier, the crack initiates at a small angle and rapidly rotates to an angle
of 700-80 ~ In order to calculate the stress intensity factor (SIF), the crack is presumed to
be perpendicular to the surface below that point. The fact that the first part of the kinked
crack, a (Figure 4), is very different from 90~ will not affect the calculation of the SIF in
the second part, b (Figure 4), even for high values o f a / b (10 ~ a/b) [13].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
126 FRETTINGFATIGUE: ADVANCES
There is mixed mode loading at the crack tip, but only K~ is going to be used because
the crack is nearly perpendicular to the surface, and in this case mode II stress intensity
factors are small compared to mode I. Therefore the crack growth will not be significantly
changed [4]. In order to calculate the SIF in mode I for a crack perpendicular to the
surface, the following weight function calculated for an edge through crack in a two-
dimensional problem proposed by Bueckner [14] has been used.
where a, t and W are shown in Figure 5 and ml and m2 are functions which depend on the
ratio a/W. Using this weight function, the stress intensity factor can be obtained from the
expression
Kt = ~2 fow(t).crx(t) dt (7)
where ~ is the normal stress in the direction perpendicular to the crack plane. This stress
intensity factor calculated has to be corrected to take into account the shape of the crack
and that it is a three-dimensional problem. The aspect ratio of the crack is approximately
0.5 and this gives a correction factor of 0.78, [15].
W t
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAVARRO ET AL. ON INITIATION-PROPAGATIONMODEL 127
At this point different propagation laws can be used. The data for crack growth in
NASA/FLAGRO program [16] for A1 7075-T6 was chosen. This data coincides with
other sources for long cracks [i 7,18] but not for short cracks where there is crack growth
below the long crack threshold. The function used in the NASA/FLAGRO program, eqn.
(8), includes the effect of the stress ratio, R, the critical stress intensity factor, Kc, and the
threshold stress intensity factor range for long cracks, AKth.
This threshold can be corrected to include the small crack effect multiplying by a
factor which depends on the crack length eqns. (9) and (10), [19].
r a
A K 'h = A K 'h~ "~[ + (9)
where a is the crack length, AKa,~ is the threshold stress intensity factor range for long
cracks and a stress ratio of R = 0 and A ~ is the fatigue limit. But this correction can be
still insufficient as will be seen in the results. Figure 6 shows the propagation rate versus
the stress intensity factor range for four different models. The first one is directly the eqn.
8 with the data from the program NASA/FLAGRO (long crack), and the second is the
same one but modified for short cracks using eqns. (9) and (10), (modified long crack).
The third is simply the Paris law for this material for R = -1 and the data from [16],
The fourth is taken from Lankford [20] where different curves for A1 7075-T6 from
different sources for short cracks are presented. From these curves, different points lying
in the limit for short cracks with high stress levels were chosen. The curve shown in
Figure 6 is the result of doing a best fit of the points extracted from [20]. The
mathematical expression of this curve is
da 3.2706.10 -9 - 1.8416-10 -7
- - -- 1.8416.10 -7 + (12)
dj~f &K-I 5 267
1 q- e 203103
With lower stresses this curve would present a local minimum in the short crack region
and the depth of it will depend, among other factors, on the stress level. Therefore, using
this data to calculate the crack growth would give shorter lives. The four curves coincide
for AK> 8 MPa m ~/z, that is long cracks, but below that value they are very different.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
128 FRETTING FATIGUE: ADVANCES
. . . . ' I
1E-9 1E-9
Z
-a 1E-10 IE-10
1E-11 IE-11
[ I I I I I [
2 3 4 5 6 7 8 910
AK (MPa m 1~)
Experimental Data
The experimental data were obtained from Wittkowsky et al [21]. The material used in
the tests was A1 7075-T6 and its principal mechanical properties are listed below, (Table
1). The spherical surfaces and plane specimens were machined from extruded bars with a
diameter o f 25.4 and 12.7 ram, respectively. Specimens were flat-sided plates with a
rectangular gage section and the radius of the spherical pads was 25.4 ram. The grain size
perpendicular to the surface was approximately 35 gin, measured according to ASTM
Standard Test Methods for Determining Average Grain Size (E 112-88).
AKth (R= 0)
UTS (MPa) ayO.~(MPa) E (GPa)
MPa m "1/2
572 503 72 2.2
The loads applied in each test are listed in Table 2 and a schematic of the test setup is
shown in Figure 7, where the load Q and P, which gives rise to the bulk stress or, are
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAVARRO ET AL. ON INITIATION-PROPAGATIONMODEL 129
cyclic loads that vary in phase, while N is a constant load. This test setup for fretting
fatigue is further explained in [22].
B
Q
P
IN
Figure 7 - Fretting test loads
Results
The lives of these tests have been calculated using the Paris law, eqn. (11), and the
curve obtained from Lankford, eqn. (12). The other two laws give an infinite life and the
reason is that these laws are useful for long cracks, eqn. (8), and physically small cracks,
eqn. (8) modified with eqns. (9) and (10), but they do not describe the behavior of
microstructurally short cracks. The results obtained with the Paris law and with the curve
obtained from Lankford are summarized in Table 3. This table shows the crack initiation
length, a, the initiation life, N,, the propagation life, Np, and the total estimated life using
the Paris law, Nrp. The next column shows the experimental life, Nfand last one shows
the total life using the law obtained [r0m Lankford, NrL. Just one value of life is given
because in this case the initiation life iszero.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
130 FRETTINGFATIGUE:ADVANCES
107
.9. . .Paris
.... ' ........ . ~ 1 . . /
. . . . . .
I " Lankford~ ~ ~
106
0~
E
.m
09
(3
>.,
"6 10~
10" , , , , , . . . . , , , , , , , , , , , , ,,
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAVARRO ET AL. ON INITIATION-PROPAGATIONMODEL 131
McDiarmid multiaxial fatigue criterion was used in this paper, but any other could be
used. As can be seen in Table 3, the life spent in initiation is considerably smaller than in
propagation, so at this stage of the model and with these stress levels, other multiaxial
fatigue criteria would have given similar results in the total estimated life. This means that
for those stress levels more attention has to be paid to the propagation process. The crack
initiation length calculated, 25-38 gm long, is longer than the depth at which the crack
turns (about 20 p.m), this means that stage I of the crack, where it grows at small angles, is
included in the initiation process. When the curve obtained from Lankford (Figure 5) is
used to estimate the fatigue lives of the specimens the results show that the initiation
length is null and everything is propagation. This law underestimates the fatigue life of
the specimens. The total estimated lives using these two laws are shown in Figure 8. Real
lives lie in the middle and this is because the crack growth rates shown in Figure 5 do not
represent the behavior for short cracks correctly. The Paris law does not show the
behavior of short cracks and give too low crack growth rates, on the other side, the curve
obtained from Lankford [20] shows what seems to be the limit for short cracks and give
too high rates. The latter would be closer to reality for higher stresses (shorter lives), as
can be seen in Figure 8.
Conclusions
An estimated life for a specimen subjected to fretting fatigue with spherical contact
has been obtained considering the crack initiation and propagation, together with a non-
arbitrary crack initiation length. It has been shown that for the cases analyzed the
initiation of the crack takes place very soon compared to the total life and that it includes
the early stage of the crack where it grows at small angles.
The comparison of these estimates with the results of a series of tests shows that life is
overestimated by a factor around 4 in the range of stresses studied when Paris crack
growth law is considered. This law gives better results for long lives. The law obtained
from the results of Lankford is an upper bound for crack growth rate (lower bound for life
estimate), therefore the lives obtained are underestimated and it gives better results for
shorter lives (higher stresses).
More attention has to be paid to the growth of short cracks in order to obtain better
results for the fatigue life. In future analysis the model will be expanded including mixed
mode crack growth and the inclination of the crack in stage II and the exact point of
initiation.
Acknowledgments
The authors wish to thank the Ministerio de Educaci6n y Cultura for their financial
support through the investigation project with reference PB97-0696-C02-01.
References
[1] Waterhouse, R. B. and Lindley, T. C., Eds., Fretting Fatigue, ESIS 18, Mech. Eng.
Publ., 1994.
[2] Harish G. and Farris T.N., "Shell Modeling of Fretting in Riveted Lap Joints," AIAA
Journal, Vol. 36, 1998, pp. 1087-1093.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
132 FRETTINGFATIGUE: ADVANCES
[3] Rulz C., Boddington P.H.B. and Chen K.C., "An investigation of the fatigue and
fretting in a Dovetail Joint," Experimental Mechanics, Vol. 24, 1984, pp. 208-217.
[4] Faanes, S. and Femando, U.S., "Life Prediction in Fretting Fatigue using Fracture
Mechanics," Fretting Fatigue, ESIS 18, Mech. Eng. Publ.,1994, pp. 149-159.
[5] Szolwinski, M.P. and Farris, T.N., "Observation, analysis and prediction of fretting
fatigue in 2024-T351 aluminum alloy," Wear, Vol. 221, 1998, pp. 24-36.
[6] Dowling N.E., "Notched member fatigue life predictions combining crack initiation
and propagation," Fatigue of Engineering Materials and Structures, Vol. 2, 1979,
pp. 129-138.
[7] Smith, R.A. and Miller, K.J., "Prediction of fatigue regimes in notched
components," International Journal of Mechanical Sciences, Vol. 20, 1978, pp.
201-206.
[8] Socie, D.F., Morrow, J. and Chen, W.C., "A procedure for estimating the total
fatigue life of notched and cracked members," Journal of Engineering Fracture
Mechanics, Vol. 11, 1979, pp. 851-859.
[9] Chen, W.C., PhD Thesis, University of Illinois at Urbana-Champaign, U.S.A., 1979.
[10] Hamilton, G.M., "Explicit equations for the stresses beneath a sliding spherical
contact," Proceedings of the Institution of Mechanical Engineering, 197C, 1983, pp.
53-59.
[ 11] Navarro, C. and Dominguez, J., "Contact conditions and stresses induced during
fretting fatigue," Computational Methods in Contact Mechanics IV, WIT Press,
1999, pp. 453-462.
[ 12] McDiarmid, D.L., "A shear stress based critical-plane criterion of multiaxial fatigue
failure for design and life prediction," Fatigue and Fracture of Engineering
Materials and Structures, Vol. 17, 1994, pp. 1475-1484.
[ 13] Hills D.A., Kelly, P.A., Dai D.N. and Korstmsky A.M., Solution of Crack Problems:
The Distributed Dislocation Technique, Kluwer Academic Publishers, 1996.
[14] Bueckner, H.J., "Weight functions and stress-intensity factors," Methods of analysis
and solutions of crack problems (Chapter 5, Appendix II), Sih, G.C., Ed., Noordhoff
International Publishing, 1973, pp. 306 313.
[15] Suresh, S., Fatigue of Materials, Cambridge University Press, 1998.
[ 16] Fatigue Crack Growth Computer Program, NASA/FLAGRO, L.B. Jonhson Space
Center, JSC-22267, 1986.
[17] Fatigue and Fracture, ASM Handbook, Vol. 19, 1996.
[ 18] Taylor D. and Jianchun L., Sourcebook on Fatigue Crack Propagation: thresholds
and crack closure, EMAS, 1993.
[I9] E1 Haddad, M. H., Topper, T. H. and Smith, K. N., "Prediction of non propagating
cracks," Engineering Fracture Mechanics, Vol. 11, 1979, pp. 573-584.
[20] Lankford, J., "The growth of small fatigue cracks in 7075-T6 aluminum," Fatigue of
Engineering Materials and Structures, Vol. 5, 1982, pp. 233-248.
[21] Wittkowsky, B.U., Birch, P.R., Dominguez, J. and Suresh, S., "An Experimental
Investigation of Fretting Fatigue with Spherical Contact in 7075-T6 Aluminum
Alloy," Fretting Fattgue: Current Technology and Practices, ASTM STP 1367,
2000, pp. 213-227.
[22] Wittkowsky, B.U., Birch, P.R., Dominguez, J. and Suresh, S., "An apparatus for
quantitative fretting-fatigue testing," Fatigue and Fracture of Engineering
Materials and Structures, Vol. 22, 1999, pp. 307-320.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
David Nowell 1 and J. Alex Arafijo )
Abstract: Many practical fretting contacts give rise to high stress concentrations or
singularities that cause high stress gradients. Straightforward application of initiation-
based life prediction methods can result in conservative life predictions as the high stress
levels are not sustained over a critical volume. This paper uses experimental results that
show a size effect with the Hertzian contact geometry to investigate the application of
Smith, Watson, Topper, and Fatemi-Socie multiaxial initiation parameters to fretting
fatigue. It is concluded that, for cases where a high stress gradient exists, an averaging
procedure is required in order to produce an acceptable prediction of initiation life. This
approach is compared to an alternative procedure based on short crack arrest and the
similarities and differences are discussed.
Introduction
133
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
134 FRETTINGFATIGUE: ADVANCES
gone into the analysis of the long crack problem using fracture mechanics based
techniques e.g. [3, 4]. It is clear that this aspect of the problem may be solved with the
available tools, viz. Fracture mechanics and the Paris Law [5], although it should be
recognized that the loading is mixed-mode, non-proportional and there may be a
significant amount of crack closure.
Unfortunately, solution of the long crack problem does not seem to have brought us
much closer to a practical life prediction method for the majority of fretting situations
and component'failures are still a practical concern [6]. The reason for this is, of course,
that in many cases most of the life is consumed in crack initiation and propagation.
Attempts have been made to extend a propagation-based analysis into this regime [7] by
using an "effective initial flaw size" methodology. Such methods are in common use for
critical parts (e.g. gas turbine disks) under plain fatigue, but have met with limited
success in the fretting situation. The reason for this is not entirely clear, but is likely to
be associated with the treatment of initiation as Paris Law propagation from an effective
initial flaw. In the case of high stress gradients this assumption will give different
weight to the initiation phase than in the case of more modest gradients. In recent years,
attention has therefore turned to the initiation and short crack phases of crack
development. Several attempts [8, 9] have been made to predict fretting fatigue
thresholds using short crack methods based on the Kitagawa-Takahashi diagram [10].
These show some promise, but can be lengthy and time-consuming to implement. Others
[11, 12, 13] have concentrated on the initiation approach and have attempted to apply
widely accepted initiation parameters to the fretting problem. This approach seems to
work reasonably well for large contacts of Hertzian-type geometry, where stress
gradients are not excessively high. However, these are not necessarily typical of actual
component geometries, where complete or nearly-complete contacts are frequently used
and stress gradients can be very high in the neighbourhood of stress concentrations or
singularities.
Even with the Hertzian geometry (where there is no stress singularity), the high stress
gradients present in small contacts can lead to anomalous results. Fouvry et al [13]
found that, applying the Dang Van criterion [14] to Hertzian contact of a sphere on a fiat
produced an under-estimate of specimen life unless the Dang Van parameter was
averaged over a characteristic volume. The need for this averaging process was ascribed
to the high stress gradients present. The difficulty is illustrated particularly well
experimentally in experiments first carried out by Bramhall [15], and repeated by
Nowell [16, 17]. Here a Hertzian geometry of a cylinder on flat was used and the
contact geometry and loading were varied in such a way as to produce a constant
maximum stress across a range of contacts, but to vary the size of contact and therefore
the size of subsurface region affected. It was found that large contacts produced low
lives, whereas for small contacts the life appeared very long (greater than 10 7 cycles).
The experiments in [15-17] were carried out with an aluminium alloy, but similar results
have been obtained with other materials.
In practical design situations, the designer is often interested in the fatigue threshold
under fretting. He or she must design the contact so that fretting fatigue is unlikely to be
a life-limiting phenomenon for the components. We believe that experiments of the type
described above provide an important input for this type of safe-life design. Transition
to the long-life regime in the Hertzian experiments might enable us to determine the
critical volume which must be subjected to high stresses in order to initiate cracks in the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NOWELL AND ARAOJO ON HIGH STRESS GRADIENTS 135
Experiments
The main features of the experiment have been described elsewhere (e.g. [15-17]),
but a brief overview will be given here for readers unfamiliar with the configuration. A
schematic diagram of the experimental geometry is shown in Figure 1. Cylindrical
fretting pads are brought into contact with a plane specimen under the influence of a
constant normal force, P, and a cyclic tensile stress, cr0sin(c0t), is then applied to the
specimen. This causes extension of the specimen, so that the contact point moves. The
pads are restrained by springs and these cause the development of a tangential fretting
force, Q, as the contact displaces. Hertzian contact takes place between the pads and the
specimen and it can be shown [19] that the peak contact pressure, p0, is proportional to P
and to the pad radius, R, as follows
Po o~~f~ (1)
Similarly, the semi-width of contact, a, also varies with P and R, but in a different
combination:
Hence by varying P and IL so that their ratio remains constant it is possible to carry
out a series of experiments where the peak contact pressure remains constant, but the
size of the contact varies. This was done for a number of different values of the salient
parameters (Po, o0 and Q/P). In each case small contacts produced a life greater than 107
cycles, 2 whereas larger contacts produced lives in the region of 105 to 106 cycles.
Typical results are shown in Figure 2 for HE15-TF, and AI-4%Cu alloy. The transition
between long and short life regimes may readily be seen. It should be noted that all tests
were carried out in partial slip at a constant frequency of 20Hz.
Analysis
In developing an analysis method, the first decision to be made is which initiation
parameter or parameters are to be used. A wide variety of empiricaUy based parameters
have been used in practice. Some [20] have been specifically developed for fretting
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
136 FRETTINGFATIGUE: ADVANCES
situations, but more recent approaches have attempted to use parameters which have
been more widely adopted in other fatigue situations. A full discussion of suitable
r,b
The value of this parameter may be related empirically to the fatigue life, Nf, by a
relationship of the form
l~sgrf = -~-(2Nf)
O".12- 2b + o - j i ( 2 N c ) b+" (4)
where E is Young's Modulus and of, of, b and c are material constants, which may be
derived from the S-N curve in plain fatigue. The above parameter is not, however,
appropriate for materials which exhibit shear mode initiation and a similar parameter,
suggested by Fatemi and Socie [22] is an appropriate alternative in this case. The
Fatemi-Socie parameter Frs is related to the range of shear strain, A?, as well as AOm~x
and is given by
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NOWELL AND ARAUJO ON HIGH STRESS GRADIENTS 137
h - ~ O'max
(5)
where Oy is the tensile yield stress of the material and ~ a constant which approaches
unity for long lives. Again the parameter may be related empirically to fatigue life using
the empirical equation
where G is the shear modulus and xf, yf, d, and e are material parameters, again derived
from the plain fatigue curve. This parameter has been used by Neu et al. [12] to predict
fretting fatigue life.
1.1E+07
1.0E+07 [] Calculated total life - SWT
9.0E+06 o Actual total life - FS
8.0E+06 9 Calculated total life
7.0E+06
6.0E+06
5.0E+06
.m
4.0E+06
m
3.0E+06
O
I- 2.0E+06
1.0E+06 o
o o o o
rm
0.0E+00 [] []
l
[] []
i
~
i
W
i
[]
J i
In a given fretting situation one does not necessarily know a priori whether initiation
will take place in tensile or shear mode, so an appropriate design philosophy might be to
predict the initiation lives by both methods and take the lowest prediction. In order to
analyse our experimental configuration it is necessary to determine the stresses and
strains in the neighbourhood of the contact. The contact pressure is essentially Hertzian
and in partial slip the shear tractions are similar to those described by Mindlin [23], with
a modification (essentially a shift of the stick zone) for the presence of tension in the
specimen [24]. By treating the experiment as a half plane, it is possible to use
Muskhelishvili potentials to determine the stress components [25]. Some caution is
needed in the use of half-plane methods and a modification to the stress component
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
138 FRETTING FATIGUE: ADVANCES
parallel with the surface is required in some cases [26, 27]. Once the stresses have been
obtained, values of the initiation parameters may be determined by evaluating the stress
history for a complete cycle at a grid of points underneath the contact. It should be
noted that a full range of candidate critical planes needs to be examined at each point so
that the number of calculations required is quite large. Figure 3 shows contours of the
two initiation parameters beneath the contact for Series 1 experiments (p0 = 157 MPa, ~0
= 93 MPa, Q/P = 0.45). It will be seen that in both cases there is a concentration of the
parameter towards the trailing edge of contact where experimental failures are observed.
(a)
Y/a
-1.5
-0.05
-0.1
-0.15
-1 -0.5
XJa
oj
0.5 1
TM
1.5
-0.2
I
-0.25
X/a
(b)
-1.5 -1 -0.5 0 0.5 1 1.5
1
-0.05
/ / \ o.12
-0.1
Y/a
-0.15
-0.2 0.3
-0.25 I f ,/
Figure 3 - Contours of (a) l"sgprE/po2 and (b) FFsG/pofor AI 4%Cu Series 1 experiments
(po = 157 MPa, Cro = 93 MPa, Q/P = 0.45)
The experiments were run to 107 cycles or to failure (whichever was earlier) so that
information is obtained on total life. In order to compare the experimental total life with
predicted values, materials data for equations (4) and (6) was obtained from plain fatigue
tests reported in the literature. 3 This gave initiation life to a crack size of lmm. In order
to obtain total life, the propagation life from a lmm crack to failure was estimated using
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NOWELL AND ARAOJO ON HIGH STRESS GRADIENTS 139
the Pads Law [5] and added to the predicted initiation life. 4 In general it was found that
the predicted initiation life was much less than the propagation life. Figure 2 shows the
predictions of total life according to the SWT and FS parameters together with the
experimental results. It can be seen that the predicted lives are similar for both
parameters, and that both approaches give rise to reasonable predictions of life for large
contacts. The transition to long lives at small contacts is, however, not predicted by
either approach. The reason for this is clear; the magnitude of the stresses has remained
unchanged between the different experiments, whereas the extent of the stress field has
changed. Since the parameters and the predictions of life are based only on the most
severe stress state, there will be no difference in predicted life. It is clear that, in order to
predict the size effect properly, it will be necessary to develop a method which
introduces a length scale into the problem.
Averaging procedures
From a physical basis it might be argued that a high value of an initiation parameter
at a single point is insufficient to cause crack initiation. Cracks will not propagate by
LEFM until they have reached a sufficient size for the stress intensity factor range to
equal the long crack threshold. Thus, one might argue that for a crack to initiate and
propagate to this 'onset size', high values of stresses must be sustained over a sufficient
distance for the crack to become established. In terms of the multiaxial initiation
parameters discussed here, we may propose that the average value of the parameter over
a critical length or volume is a better measure of the likelihood of crack initiation.
Accordingly two averaging methods were investigated:
Method 1: averaging along the critical plane - Here we first found the most highly
stressed point (i.e. the maximum of the parameter) and established the critical plane. It
was argued that the crack would initiate on this plane and values of the parameter were
therefore averaged over a distance dc along the direction of the critical plane. Several
values ofdc were chosen in order to see which would provide the best fit to the
experimental results.
Method2: averaging over a volume - In this case we chose to define a critical
volume (Vo = do3 ).5 Averaging of the stress components was carried out over the
volume before calculation of the initiation parameters. Different volumes were chosen
around the most heavily loaded point in order to establish the one which gave the largest
value of averaged parameter. This was used to predict the initiation life. Once again
different values of do were used.
Figures 4 and 5 show the results obtained for each method for different values of do
using the SWT parameter. Once again total life was calculated as the sum of initiation
life (to lmm) and propagation life. Results were also calculated for the F-S parameter,
but were rather similar. A full presentation of the results, including those for different
series of experiments and for another material (Ti-6/4) is given in [28]. It can be seen
4 Stress intensity factors were calculated for a two-dimensional geometry (i.e. assuming
a through-thickness crack) under contact loading using the dislocation density method
(see [16, 28]).
5 In practice the stress analysis used here is two-dimensional, so the actual averaging
was carried out over an area in this case.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
140 FRETTING FATIGUE: ADVANCES
from the figure that there is little difference between the results from the two averaging
procedures. Choice of do in the region of 50 txm seems to give a reasonable fit to the
experimental results over the full range of contact sizes The value must, of course, be
chosen by reference to a series of tests like these before it can be used in a design
situation and it remains to be seen whether it may be regarded as a material constant.
However it is worth noting that the value of the parameter is of the same order as the
grain size of the material (about 100 txm in the alloy used, which has a highly elongated
grain structure in the extrusion direction (along the specimen axis)). A similar effect
was noted with later experiments using Ti6/4 [29], where the best fit value for do was
about 10 Ixm, compared with a grain size of 5 gm.
2.0E+06 ,,
0.0E+00 , , 7 - - , ,
0 0.2 0.4 0.6 0.8 1 1.2
Contact half width, a (mm)
The work carried out here has shown that simple application of multiaxial initiation
parameters can lead to under-prediction of fatigue life in cases where there are high
stress gradients. Averaging the parameters over a volume gives a much better estimate
of the fatigue life and can be used to explain the size effect noted in the Hertzian contact
geometry. A number of different techniques for averaging are available, but the results
do not seem to be very sensitive to the method used. The size of the averaging volume
appears to be of the same order as the grain size for the two materials which have been
investigated so far, but more work needs to be done to establish whether this is the case
for other materials. Other workers have, however, found similar effects; Fouvry et al
[13] have carried out fretting fatigue tests on a low alloy stainless steel using the Dang
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NOWELL AND ARAOJO ON HIGH STRESS GRADIENTS 141
Van initiation parameter [14]. The found that averaging of the parameter over a cube of
side 5gm was necessary in order to predict the fatigue life correctly. This dimension
was of the same order as the grain size, As part &the current program of work [28] we
have also employed the Dang Van parameter, but as noted by Fouvry, the results are
rather similar to the Fatemi-Socie predictions, but the computations are more lengthy.
We have not, therefore, carried out the averaging procedure for the Dang Van parameter
Totallife(cycles)
1.20E+07
A~ ~; + \ O Expenmental data
1.00E+07 <~ ~, ~. ~, \ "" O ' " SWT - do = 50 microns
: ~t --x-- SWT - do = 80 microns
b
2 00E+06
- ~" . . . . . -I~ . . . . . 2~2. 2."_'.'_~ : :_": :_-.-~
0 00E+00 I I I I I I
0 0.2 04 0.6 08 1 12
Half width contact, a (ram)
There are a number of implications for life prediction of fretted components. First,
some form of averaging procedure is likely to be necessary in cases of high stress
gradients. In particular, applications such as dovetail blade roots and spline joints in gas
turbine engines give rise to very localised stress concentrations and life prediction on the
basis of peak stress values will almost certainly produce underestimates of fatigue lives.
At present it is not clear how to choose the averaging dimension, but Hertzian tests in
which the normal load and contact radius are varied so that the P/R ratio remains
constant provide a potentially useful means of establishing the appropriate value.
Secondly, although multiaxial parameters were used in the current study, it should be
noted that failures actually took place on the surface close to the edge of contact, where
the shear component of loading is small. Direct stress amplitude in a direction parallel
to the surface may therefore provide a simpler procedure yielding satisfactory results. In
order for the proposed method to gain widespread acceptance it will be necessary to
validate the procedure using more practical contact geometries. We are currently
undertaking an experimental program of work on the dovetail and spline geometries in
order to provide the necessary information on fatigue life.
It should be noted that averaged initiation parameters are not the only means of
accounting for the size effect discussed here. Our earlier work has proposed that short
crack arrest methods based on the Kitagawa-Takahashi diagram could be used to similar
effect [8]. In a general sense there is not much fundamental difference between the two
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
142 FRETTINGFATIGUE: ADVANCES
approaches in that they both require a high level of stress to be sustained over a
sufficient distance so that crack initiation and early growth can take place. The method
described here approaches the problem from an initiation standpoint, whereas the short
crack work uses a growth threshold. Neither approach is likely to be completely correct,
since initiation and short crack growth are both required in order for failure to take place.
Further, the mechanics of these processes are not well understood and the use of
empirical initiation parameters, stress range, or AK to characterise the 'crack driving
force' is questionable. More fundamental research into the mechanics of initiation and
short crack work is clearly required. Nevertheless, designers still require improved
methods of life prediction in fretting fatigue, and the method described above provides a
possible solution, at least in the short to medium term.
Acknowledgments
Alex Arafijo would like to acknowledge the support of the Brazilian government
(CAPES).
References
[2] Nowell, D., Hills, D. A., and Moobola, R. "Length scale considerations in fretting
fatigue," Fretting Fatigue: Current Technology and Practices, ASTM STP 1367,
D. W. Hoeppner, V. Chandrasekaran, and C. B. Elliott, Eds., American Society
for Testing and Materials, West Conshohocken, PA, 2000, pp. 141-153.
[3] Edwards, P. R., Ryman, R. J., and Cook, R., "Fracture Mechanics Prediction of
Fretting Fatigue under Constant Amplitude Loading," RAE TechnicalReport
77056, 1977.
[4] Hattori, T., Nakamura, M., Sakata, H. and Watanabe, T. "Fretting Fatigue Analysis
using Fracture Mechanics," JSME International Journal, Series 1, 31, 1, 1988,
pp. 100-107.
[5] Paris, P. C., Gomez, M. P., and Anderson, W. P. "A Rational Analytic Theory of
Fatigue," The Trend in Engineering, 13, 1961, pp. 9-14.
[6] Xi, N. S., Zhong, P. D., Huang, H. Q., Yan, H., and Tao, C. H. "Failure
Investigation of Blade and Disk in First Stage Compressor," Engineering Failure
Analysis, 7, 200, pp. 385-392.
[7] Fellows, L. J., Nowell, D., and Hills, D. A., "Analysis of Crack Initiation and
Propagation in Fretting Fatigue: the Effective Initial Flaw Size Methodology,"
Fatigue & Fracture of Engineering Materials & Structures, 20, 1, 1997, pp. 61-
70.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NOWELL AND ARAOJO ON HIGH STRESS GRADIENTS 143
[8] Nowell, D., and Arafijo, J. A., "Analysis of Pad Size Effects in Fretting Fatigue
using Short Crack Arrest Methodologies," International Journal of Fatigue, 21,
1999, pp. 947-956.
[9] Chan, K. S., Li, Y., Davidson, D. L., and Hudak, S. J. Jr, "A Fracture Mechanics
Approach to High Cycle Fretting Fatigue based on the Worst Case Fret Concept:
Part 1 - Model Development," International Journal of Fracture, 112, 2001, pp.
299-330.
[10] Kitagawa, H., & Takahashi, S., "Applicability of Fracture Mechanics to Very Small
Cracks or the Cracks in the Early Stage," Proceedings of the 2ndlnternational
Conference on Mechanical Behaviour ofMaterials, American Society for Metals,
1976, pp. 627-631.
[11] Szolwinski, M. P., Harish, G., McVeiglL P. A., and Farris, T. N., "Experimental
Study of Fretting Crack Nucleation in Aerospace Alloys with Emphasis on Life
Prediction," Fretting Fatigue: Current Technology and Practices, ASTM STP
1367, D. W. Hoeppner, V. Chandrasekaran, and C. B. Elliott, Eds., American
Society for Testing and Materials, West Conshohocken, PA, 2000, pp. 267-281.
[12] Neu, R. W., Pape, J. A., and Swalla-Michaud, D. R., "Methodologies for Linking
Nucleation and Propagation Approaches for Predicting Life under Fretting
Fatigue," Fretting Fatigue: Current Technology and Practices, ASTM STP 1367,
D. W. Hoeppner, V. Chandrasekaran, and C. B. Elliott, Eds., American Society
for Testing and Materials, West Conshohocken, PA, 2000, pp. 369-388.
[13] Fouvry, S., Kapsa, P., and Vincent, L., "A Multiaxial Analysis of Fretting Contact
taking into account the Size Effect" Fretting Fatigue: Current Technology and
Practices, ASTM STP 1367, D. W. Hoeppner, V. Chandrasekaran, and C. B.
Elliott, Eds., American Society for Testing and Materials, West Conshohocken,
PA, 2000, pp. 167-182.
[14] Dang Van, K., Griveau, B., and Message, 0., "On a New Multiaxial Fatigue Limit
Criterion: Theory and Application," Biaxial and Multiaxial Fatigue, M. W.
Brown and K. J. Miller, Eds., MEP, London, 1989, pp. 479-496.
[16] Nowell, D., "An Analysis of Fretting Fatigue," D,Phil. Thesis, University of
Oxford, 1988.
[17] Nowell, D., and Hills, D. A. "Crack Initiation Criteria in Fretting Fatigue", Wear,
136, 1990, pp. 329-343
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
144 FRETTINGFATIGUE: ADVANCES
[18] Arat]jo, J. A., and Nowell, D., "The Effect of Rapidly Varying Contact Stress
Fields on Fretting Fatigue," International Journal of Fatigue, 24, 2002, pp. 763-
775.
[20] Ruiz, C., and Chen, K.C., "Life Assessment of Dovetail Joints between Blades and
Discs in Aero-Engines", Proceedings of the International Conference on
Fatigue, Sheffield, 1986, I.Mech.E., London, 1986.
[21] Smith, K. N., Watson, P., and Topper, T. H., "A Stress-Strain Function for the
Fatigue of Metals," Journal of Materials, 5, 4, 1970, pp. 767-778.
[22] Fatemi, A., and Socie, D. F., "A Critical Plane Approach to Multiaxial Fatigue
Damage Including Out of Phase Loading," Fatigue and Fracture of Engineering
Materials and Structures', 11, 1988, pp. 149-165.
[24] Nowell, D., and Hills, D. A., "Mechanics of Fretting Fatigue Tests," International
Journal of Mechanical Sciences, 29, 5, 1987, pp. 355-365.
[25] Hills, D. A., and Nowell, D., "Mechanics of Fretting Fatigue", Kluwer, Dordrecht,
1994.
[26] Fellows, L. J., Nowell, D., and Hills, D. A., "Contact Stresses in a Moderately Thin
Strip (with Particular Reference to Fretting Fatigue Experiments)", Wear, 185,
1995, pp. 235-238.
[27] Hills, D. A., and Noweil, D., "A Discussion of: "Peak Contact Pressure, Cyclic
Stress Amplitudes, Contact Semi-Width and Slip Amplitude: Relative Effects on
Fatigue Life" by K. Iyer," International Journal of Fatigue, 23, 2001, pp. 747-
748.
[28] Arafijo, J. A., "On the Initiation and Arrest of Fretting Fatigue Cracks," D.Phil.
Thesis, University of Oxford, 2000.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Andrew Mugadu, ~David A. Hills,2 and Ludwig Limmer3
A Theoretical and Experimental Procedure for Predicting the Fretting Fatigue
Strength of Complete Contacts
REFERENCE: Mugadu, A., Hills, D. A., and Llmmer, L., "A Theoretical and
Experimental Procedure for Predicting the Fretting Fatigue Strength of Complete
Contacts," Fretting Fatigue: Advances in Basic Understanding and Applications, STP
1425, Y. Mutoh, S. E. Kinyon, and D. W. Hoeppner, Eds., ASTM International, West
Conshohocken, PA, 2003.
Introduction
Much of the experimental work in fretting fatigue earned out recently at Oxford
has been aimed at understanding the basic mechan]cs of the fretting fatigue problem,
using a two-actuator test apparatus, and employing Hertzian contacts [1] and [2]. This
approach has been taken because it is possible to separate out the contact problem
from the crack initiation and propagation problems easily. Furthermore, the contact
problem itself is amenable to a solution in closed form, both for the contact pressure
distribution and the effects of complex shearing tractions with attendant stink and slip
zone regimes. It has therefore proved possible to elucidate a great deal about the nature
of the partial slip contact problem and the crack propagation problem, in a compelling
way, but, at the same time, there are still some unanswered questions. The principal
1DPhil. student, sponsored by the Rhodes Trust, Department of
Engineering Science, Oxford University, Parks Road, OXI 3PJ,
U.K.
2Professor of Engineering Science, Department of Engineering Science, Oxford
University, Parks Road, OX1 3PJ, U.K.
3Department of Engineering Science, Oxford University, Parks Road,
OX1 3PJ, U.K.
145
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
146 FRETTING FATIGUE: ADVANCES
Complete contacts
. Internal spline " ~ - ~ ' ~
Figure 1 - Schematic diagram of the cross-section of a spline tooth pair, looking in the
axial direction
one concerning the results of Hertzian tests is the "size effect," whereby we find that,
for two identical tests sustaining the same stress state, the one involving a small contact
will exhibit an infinite life, while the one involving a large contact will show a finite
life. This has never been fully resolved, although various tentative explanations have
been presented. For example, it has been suggested that a critical volume of material at
the initiation point needs to experience a critical plane parameter before nucleation can
proceed. A second problem concerns the development of a life-prediction approach
when the contact pressure is singular. Practical examples of this abound: the conformal
contact between involute spline teeth (Figure 1), various types of bolted and clamped
joints, and certain designs of dovetail fixings at fan-blade roots. In all these cases,
because the pressure at the edge of the contact as implied by an elasticity solution is
singular, any method involving the simulation of the stress state using a Hertzian type
specimen would obviously be inappropriate.
An alternative approach to this problem is to use ideas borrowed from fracture
mechanics (and sharp notch mechanics), VlZ. to attempt to simulate the process zone
in which the crack initiates, at the contact edge. The strategy to be developed is as
follows: first, the state of stress near the edge of a slipping contact has been studied
in the literature. It is known that there is a power order singularity (usually less than
square root in strength), related to both the local contact angle and coefficient of
friction. In the experimental apparatus, a tensile test specimen with contacting pads
pressed onto the surface is utilized [1,3]. However, in contrast to the Hertzian contacts
employed in previous experiments, the pads have fiat faces with edges inclined at
the same contact angles as those present in the prototypical problem. Thus, with the
coefficient of friction matched in both problems, the spatial distribution of stresses is
the same and hence, providing small scale yielding conditions exist, so is the nature
of the strain history of material present in the process zone. There is a strong analogy
between this problem and that of two cracks, each suffering say, mode I loading. In
the case of the crack, to make the stress fields equal in magnitude as well as spatial
variation, it would be necessary to match the stress intensity factors. The same is true
of the two fretting problems; we define generalized stress intensity factors to scale the
asymptotic fields in the two problems and arrange for these to be matched so that the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUGADU ET AL. ON STRENGTH OF COMPLETE CONTACTS 147
stress states are, identical in every respect. To ensure that the test truly represents the
prototypical conditions further matching is needed, in the form of ensuring that the
two components have the same surface finish characteristics, and also, that the same
slip displacement is employed. It is then proposed that the nucleation/no nucleation
conditions, and the number of cycles to nucleate a crack in the former case, will be the
same for the two problems.
AsymptoticAnalysis
The fundamental asymptotic solution required is that of the stress state adjacent
to the comer of a component sliding on a half-plane (Figure 2). Although a fall
understanding of the macroscopm contact of (Figure 1) would require formulation in a
different domain, in an asymptotic solution we focus m on a very small process zone
at the contact comer. In these circumstances the remote shape of the contact domain is
unimportant. This problem has been studied in detail before [4] and [5], and here, only
the salient points will be presented. The stress state in the neighborhood of the wedge
comer is of the form
where (r, 0) are polar coordinates centered on the contact comer, A and gi~ (0; f, r are,
respectively, the eigenvalue and eigenfunctions of the solution, f, the coefficient of
friction, r the contact angle, and K*, the generalized stress intensity factor defined
as
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
148 FRETTING FATIGUE: ADVANCES
sxgn. A positive slgu indmates that the frictional force is directed away from the wedge
comer, and gives rise to the weaker singularity, for a given wedge angle, and vice versa.
This figure displays the strongest singularity which can he found and, in contrast to the
monolithic wedge problem (Figure 4), which is conveniently split into a symmetric and
antisymmetric solution, the corresponding eigenfunctions here, 9~3(0; f, r contains
neither inherent symmetry nor anti-symmetry. The order of singularity associated with
these solutions (symmetric and antisymmetrxc loading) is also included in (Figure 3)
where r = 2c~ - 7r. The majority of the region depicts a singularity which is weaker
than square root singular, although, there is a range of parameters for which the
order of the singularity is greater than - 1 / 2 . This rather surprising result is, in fact,
physically correct, and represents conditions when the coefficient of friction in the
wedge problem is greater than the "naturally occurring" traction ratio, Tro/aoo, in a
monolithic wedge of the same geometry i.e. r = 2a - 7r.
Calibration
The multiplicative factor scaling the magnitude of the solutions, K*, has, in
general, to be found by a purely numerical procedure, such as the finite element
method. This is not without difficulty, as the asymptotic form of the stress field ought
to be imposed on the general behavior of the stress state around the contact corner,
in order to accelerate convergence of the solution, and this is not easy to achieve.
However, it wall be noted from Figure 3 that for a contact angle of r = 90~ if the
coefficient of friction is equal to 2/3, a square root singularity exists (for the shearing
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUGADU ET AL. ON STRENGTH OF COMPLETE CONTACTS 149
-a a x
force directed towards the wedge comer, negative f), This permits standard crack-tip
elements to be used adjacent to the contact comer [6].
A problem that admits an analytical solution is that of a rigid, square-ended pad,
of half width a, subject to a normal load, P, and sliding against an elastically dissimilar
half-plane (Figure 5). For this case the normal traction distribution, p(x), is given by
[z]
Dundurs' parameter, fl, varies such that 0 < fl < 0.5 which, from equation (4) above,
corresponds to 0.5 > v > 0. Here we define the generalized stress intensity factor, K~,
as
K; = ! p(rlr (5)
where r is a polar coordinate measured from the pad comer. Making the substitution
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
150 FRETTINGFATIGUE:ADVANCES
D-shapedbronzeholders
Figure 6 - Schematic of the carriage showing the D-shaped bronze holders journalled
between two rails
r = z + a in equation (3), we take the limit x ~ -a, i.e. for the left hand comer of the
pad, (Figure 5). This leads to a solution for the normalized generalized stress intensity
factor
a 1-~ K{ sin A17r
p 7r21-x-, " (6)
Experimental
A modified form of the fretting apparatus used in the past to conduct Hertzian
type tests has been developed to enable the new type of test pad geometry to be
employed. Clearly, the essential difference between a flat-ended pad and a Hertzian
cylindrically faced pad is that the alignment of the pad front face against the test
specimen face is absolutely critical. Any imperfection here will materially change the
form of the stress state at the pad comer, and so, a self-aligning arrangement is highly
desirable. At the same time, the shearing force must be applied strictly along the plane
of the contact, rather than above it, so that no rocking moment is developed. These
stringent and, to some extent, opposing requirements have been achieved by means of
the pad holding assembly shown schematically in Figure 6. The essential feature of the
fixture is the use of D-shaped bronze holders for the specimens, having an included
angle of about 190 ~ and arranged so that the front faces of the pads lie exactly along
the diameter of the D. The holders are permitted to rotate freely, and so the pads,
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUGADU ET AL. ON STRENGTH OF COMPLETE CONTACTS 151
loaded by a centrally applied contact force, are free to take up a natural orientation
such that the pad face is pressed uniformly along the test piece face. At the same time,
the sheafing force is guaranteed to be transmitted along the correct line of action.
It is clear that, if the arrangement is geometrically correct and the generalized
stress intensity factors for the two problems are matched, the state of stress in the
neighborhood of the initiation zones will be identical. For complete fidelity between
the prototype and the experiment the surface finish and slip displacement must also be
matched.
Over 150 tests on super CMV shaft steel have been conducted on this apparatus
for Rolls Royce plc. The results obtained are internally consistent and support the
methodology described in this paper, but we cannot report the data for reasons of
commercial confidentiality.
Nucleation Conditions
It is argued that, if the process zone where crack initiation occurs is sufficiently
small for the local strains to be completely dominated by a surrounding zone in
which the asymptotic singular field applies, the nucleation conditions are properly
represented in the experiment. This is completely analogous to the concept of "small
scale yielding" in fracture mechanics terms. For the particular problem of a rigid,
square-ended block sliding along an elastic half-plane described above, it is possible
to deduce the complete contact stress field, as well as to determine the eigenfunctions
corresponding to the singular (dominant) term. Explicitly, for this problem, the singular
field associated with f = 2/3 in the half plane, (-Tr < 0 < 0), is given by
a~
O'00 K * r ~-1 -1.743sin(0.440 + 0.794) -1.050sin(1.560 + 0.589)
7-~o -0.492 sin(0.440 0.777)
- -1.050 sin(1.560 0.982)
-
(7)
where K* is defined in equation (2). The complete stress field is found from the
Muskhelishvili potential for this problem, which is given by
P 1
(z) = (z + f) 2azr (z - 1) 1-~' (z + 1) ~1 (8)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
152 FRETTINGFATIGUE: ADVANCES
y/a
0 . . . . . . . . . . . . . . . . . ~
-0 05 o
-0.15
-02
-0 25
-1.2 -1.1 -1 0 -0.9 -0.8
Figure 7(a) - Plot showing the percentage difference between the full and asymptotic
fields,(V~zy~u - x/~z~sv~p)/V/-~z:~u%)fo r f = 2/3
y/a [ , Q
0
x/a
-0.05
-0.1
-0.15
-0.2
-0,25
-1.2 -1.1 -1.0 -0.9 -0.8
Figure 7(b) - Plot showing the percentage difference between the full and asymptotic
fields, ( v~2 /~u - v~J2asymp)/ X/-~2futt %, f Or f = - 2 / 3
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUGADU ET AL. ON STRENGTH OF COMPLETE CONTACTS 153
y/a
Q
Ii
, , , _ _ )
0
x/a
-0.05
-0 1
-0.15
-0.2
-0.25
-1.2 -11 -10 -09 -08
mechanics Figures 8(a and b) show the extent of the implied plasticity zone for a
given normal load, P Here a is the half-width of the pad, and k is the yield stress in
pure shear Just as in fracture mechanics, judging the size of the acceptable plasticity
zone so that it might reasonably be assumed to exist under conditions of small scale
yielding is not something which has an exact outcome If, for example, a maximum of
3% difference between the full-field and singular solution is deemed acceptable, the
largest load which may be tolerated, and still come within the scope of small scale
yielding is about 08 for f = 2/3 (Figure 8(a)), and 06 for f = - 2 / 3 (Figure 8(b)).
A further aspect of the initiation process which warrants attention is the effect of
reversing the direction of the shearing force which, by definition, is a feature present
in all fretting problems It should be noted that this does not imply that the slip
displacement need be the same in each direction, although, if this were not so, creep
would result: and it should also be noted that, in a shpping region, the shear tractions
can only be of magnitude :kfp(x), and not lower We have already shown that, for
some values of the contact angle, ~b, the state of stress will be singular, regardless
of whether the shearing tractions are directed towards or away from the pad comer
These problems present a particular challenge, as both the exponent in the asymptotic
solution, and the multiplicative factor, the generalized stress intensity factor, will vary
from one half cycle to the other It is therefore not immediately clear whether it is the
half cycle which generates the larger stress intensity factor, or the one which generates
the stronger singularity, if different, or a combination of the two, which controls crack
nucleation conditions These cases will require further analysis, and the behavior will,
to some extent, be controlled by the extent of the process (plasticity) zone However,
there is a significant range of geometries and coefficients of friction where the stress
state is bounded when the shearing tractions act away from the comer, and is singular
when the shearing tractions act towards it. In these cases, providing small scale
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
154 FRETTINGFATIGUE: ADVANCES
y/a
Q
m
rda
00,/ o jO./i __
-0.1
I...............i I 1.4
. . . . .
--
-0.25
rl.2 -1.1 -1.0 -0.9 -0.8
Figure 8(b) - Plot of the normalizedpunch load, Pa/ k, for f = - 2 / 3
Conclusion
References
[1] Hills, D. A. and Nowell, D., Mechanics of Fretting Fatigue, Kluwer Academic
Publishers, Dordrecht, The Netherlands, 1994.
[2] Fellows, L. J., Nowell, D., and Hills, D. A., "Analysis of Crack Initiation and
Propagation in Fretting Fatigue: The effective initial flaw size metho-'dology,"
Fatigue and Fracture of Engineering Materials and Structures, Vol. 20, No. 1,
1997, pp. 61-70.
[3] Hills, D. A. and Nowell, D., "The Development of a Fretting Fatigue Experiment
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MUGADU ET AL. ON STRENGTH OF COMPLETE CONTACTS 155
[4] Gdoutos, E. E. and Theoearis, E S., "Stress Concentration at the Apex of a Plane
Indenter Acting on an Elastic Half Plane," Journal of Applied Mechanics, Vol. 42,
1975, pp. 688-692.
[5] Comninou, M., "Stress Singularity at a Sharp Edge in Contact Problems with
Friction," Journal of Applied Mathematws andPhysics (ZAMP), Vol. 27, 1976, pp.
493-499.
[6] Mugadu, A., Hills, D. A., and Limmer, L., "An Asymptotic Approach to Crack
Initiation m Complete Contacts," Journal of Mechanics and Physics of Solids, Vol.
50, No. 3, 2002, pp. 531-547.
[7] Hills, D. A., Nowell, D., and Sackfield, A., Mechanics of Elastic Contacts. Pub.
Butterworth Heinemann, Oxford, 1993.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
FRETTING FATIGUE PARAMETER EFFECTS
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Toshio Hattori,l Masayuki Nakamura, 2 and Takashi Watanabe3
ABSTRACT A new estimation method for fatigue crack initiation criteria using plain
fatigue limit, threshold stress intensity factor range, and specific depth is proposed.
Using this, new design method for improving fretting fatigue strength have been
developed by using stress-release slits on the pads near the contact edges. This design
has analyzed on the basis of stress singularity parameters at the contact edges, and the
analysis results were used to optimize the slit shapes, such as slit depth and slit position.
This optimization takes into account the fretting fatigue crack initiation strength at the
contact edge and the fatigue strength at the slit root. We confirmed that the fretting
fatigue crack initiation strength of the optimized design is about twice that of a
conventional (i.e., slitless) design.
KEYWORDS: crack initiation, stress singularity parameters, stress-release slit, knuding,
Introduction
Fretting can occur when a pair of structural elements are in contact under a normal load,
while cyclic stress and micro-slippage are forced along the contact surface. This
condition can be seen in bolted or riveted joints [1,2], in shrink-fitted shafts [3,4], and in
the blade dovetail region of turbo machinery [5,6], among others. When fretting occurs
the fatigue strength decreases to less than one-third of that without fretting [7,8]. The
strength is reduced because of the concentration of contact stresses such as contact
1Chief Researcher, Mechanical Engineering Research Laboratory, Hitachi
Ltd., Tsuchiura, Ibarald, Japan.
2Researcher, Mechanical Engineering Research Laboratory, Hitachi Ltd.,
Tsuchiura, Ibaraki, Japan.
3Chief Engineer, Hitachi Works, Hitachi Ltd., Hitachi, Ibaraki, Japan.
159
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by
by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
160 FRETTING FATIGUE: ADVANCES
pressure and tangential stress at the contact edge, where cracks from fretting fatigue form
and propagate.
Previously, the authors presented new fretting fatigue strength estimation methods
using fracture mechanics for the fretting fatigue limit [7,9] and stress singularity
parameters for the fretting fatigue crack initiation strength [10]. Using these methods,
many fretting fatigue improvement designs such as grooving or knurling the contact
surface [11], placing a low stiffness spacer on a contact interface, and reducing the wedge
angle [10] were introduced. In this paper the authors introduce another fretting fatigue
strength improvement method using stress-release slits on the pads near the contact edges.
This design was analyzed on the basis of stress singularity parameters at the contact edges,
and the analysis results were used to optimize the slit shapes, such as slit depth and slit
position. This optimization takes into account the fretting fatigue crack initiation strength
at the contact edge and fatigue strength at the slit root. It was confirmed that the fretting
fatigue crack initiation strength of the optimized design is about twice that of a
conventional (i.e., slitless) design.
The authors have already presented many fretting fatigue strength improvement
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HATTORI ET AL. ON USING STRESS-RELEASESLITS 161
design methods. Firstly, design methods involving grooving or knurling a contact surface
were introduced as shown in Fig. 1.By using stress analysis, fracture mechanics analysis,
and fretting fatigue tests, the improvement of fretting fatigue limit about 70-80% have
been confirmed as shown in Fig. 2. Then designs having a low stiffness spacer on a
contact interface and a reduction of the wedge angle were introduced, and by using the
stress and stress singularity parameter analyses, the improvement of fretting fatigue crack
initiation strength was estimated as shown in Figs. 3 and 4. But these designs created
many problems, such as complicating the manufacturing process and reducing safety. In
this paper therefore another fretting fatigue strength improvement design using stress-
release slits on the pads near the contact edges was presented.
300
~ 2OO
.. (R=Smm, d=lmm) ~.
". Grooved tvoe
""'-,.Plain fretting
100
f t ,
Figure 2-Fretting fatigue test results for grooving or knurling type specimens.
-$
.~...w,~ge
~,~, 70
60
in
- - . ~ak~,2,~2
L
"~ 50
?2
e
-g 40
30
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
162 FRETTINGFATIGUE: ADVANCES
(.-
.r
o 100 AL Pad
(~
.m
.---9
O
50
D
bD Steel Pad
,D
9 I
1 2
Young's modulus ratio C C = E / Esteel
Figure 4-Estimation results offretting fatigue crack initiation limits for each pad
stiffness.[ lO]
The stress-release slit type contact model is shown in Fig. 5. In this model, the
uniform contact pressure P0 is applied to the outermost edge of the pad and uniform
nominal stress cr 0 is applied to the specimen. The stress-release slits are formed on the
pads near the contact edges. By using these slits, the concentration of contact pressures
and tangential stresses at the contact edges are decreased and fretting fatigue crack
initiation strength can be increased. The validity of this fretting fatigue crack initiation
strength improvement method is confirmed by the stress and stress singularity parameters
analyses that follow.
Pad
Specimen
d
.4OI 9 Unit; mm
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HATTORI ET AL. ON USING STRESS-RELEASESLITS 163
yJ
Po
Stressreleaseslit
/~'~Contact surface
wao ~--~ Contact edge
I - - Sr p =
e c =i ----m= e~~- = : == : = : : O',
= . . . . . . . . . . . . . i _..~X
To analyze the stress and stress singularity parameters of the stress-release slit
contact model as shown in Fig. 5, the boundary element method for contact problems was
used. The boundary element mesh for analyzing the stress and stress singularity
parameters is shown in Fig. 6. This is a quarter section of the analytical model shown in
Fig. 5. The frictional coefficient /1 on the contact surface was set at 0.7 by assessing the
damage to the contact surface by repeated micro slippage [3].
To evaluate the fretting fatigue crack initiation strength of this model we used the
stress singularity parameters as follows. The stress fields near the contact edges show
singularity behavior as shown in Fig. 7. These stress distributions near the contact edges
can be expressed using the two stress singularity parameters, H and ,~, as follows,
(~(r)=H/r x (1)
where a is the stress (MPa), r is the distance from the singularity point (mm), H is the
intensity of the stress singularity, and 2 is the order of the stress singularity.
Parameters" ~ and H are calculated as follows. The order of the stress singularity ( ~ )
for the contact edge can be calculated analytically [12] using wedge angles 0 1 and 0
2 , Young's moduli E1 and E2, Poisson's ratios v 1 and v 2 the frictional coefficient /~
(Fig. 8). However, in this paper ~ is calculated by finding the best fit of Eq.(1) to the
stress distribution near the contact edge. The stress distribution can be calculated by
numerical stress analysis methods, such as the finite element or boundary element
methods. The intensity of the stress singularity (H) is calculated by the best fit of Eq.(1)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
164 FRETTINGFATIGUE:ADVANCES
Contact edge
Fig. 7-Stress distributions near a contact edge and stress singularity parameters,.
~? tional coefficient #
In this paper three points (A: contact edge, B: inner - contact interface, and C:
root of stress-release slit) were selected as the targets for the fatigue strength evaluation of
this stress-release slit model (Fig. 9). The fatigue strength of these points was evaluated by
using the stress at a certain depth from the surface or singular point. For instance, in the
case of stress singular points, the fretting fatigue crack initiation criterion Hc was derived
from the plain fatigue limit (~o) and the threshold stress intensity factor range (A Kth) of
the specimen material Ni-Mo-V steel. On both critical conditions the stress distributions
cross at a point 0.012 mm in depth from the singular point as shown in Fig. 10. We expect
that for the critical conditions for each stress concentration case, the stress distributions
cross at this specific depth point rc = 0.012 mm. From this assumption we can estimate
the critical intensity value of stress singularity Hc for each order of stress singularity A
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HATTORI ET AL. ON USING STRESS-RELEASE SLITS 165
~~LP~196 MPa
R=0-5~ ! I t
1'1.sl |t
-- - .... ~ -+Go
-Specimen A Unit; mm
350
250
200
k initiation
=
oriteria
~
]
-go 150
100
50
0
0 0.1 0.2 0.3 0.4 0.5
Order" of stress sinipJlar/ty PL
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
166 FRETTINGFATIGUE:ADVANCES
as shown in Fig. 11. First, the fretting fatigue crack initiation limits at contact edge A and
contact interface B can be estimated as follows. The stress distributions near points A and
B with slit depth d -- 3.8 mm, slit root radius R = 0.5 ram, and slit position t -- 3 ram, and
on the loading conditions o f nominal contact pressure P0 = 196 MPa and nominal axial
repeated stress a a = -+98 MPa are shown in Fig. 12. From these calculated results the
order o f stress singularity can be calculated as 2 = 0.281 and intensity o f stress
singularity Ha = AH/2 = 100 M P a . m m a f o r contact edge A, and ,~ = 0.0 and Ha = 230
M P a ' m m ~ for contact interface B. By comparing these calculated results o f stress
singularity parameters Ha with the critical intensity value o f stress singularity Hc, the
fretting fatigue crack initiation limits at contact edge A and contact interface B can be
estimated, Then the fatigue crack initiation limit at slit root C can be estimated by the
assumption that the fatigue cracks initiate when the stress at'the specific depth point rc =
0.012 m m reaches the plain fatigue limit o f ~ w0 = 360 MPa as shown in Fig. 13. Using
these comparisons o f analyzed stress at specific depth rc = 0.012 m m near each point with
the plain fatigue limit a w0 = 360 MPa the fatigue crack initiation limit for each point can
15e estimated as Fig. 14. From these estimated results we can see that the fretting fatigue
crack initiation limit at contact edge A increases in accordance with the increase o f slit
depth, but on the contrary the fatigue crack initiation limit at slit root C and on contact
interface B decrease in accordance with the increase of slit depth. And finally the relation
between slit position and fatigue crack initiation strength for each optimized slit shape can
be obtained as Fig. 15. From these results we can see that the fatigue crack initiation limit
with stress-release slits o f the optimum design can be increased to about 100 MPa, which
is more than twice that of a conventional (i.e., slitless) design.
1000
~,Po-"196MPa
=0.281} Pad ~ .~
I. I
b ~R~0'5 B~~t= 3
I00
Specimen ~r O'. =•
10 I I ,, L
0.01 0.1 I0
Distance from contact edge r [mm~
~'g. 12-Stress distributions n e a r contact edge a n d contact interface.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HATTORI ET AL. ON USING STRESS-RELEASE SLITS 167
500
" ~Po:Ig6MPa
!
\ / R=0 s ' c ~ = s
!
I ~
250 ~C- [~ | Specimen A
o',:+98MPa
~ =
I 0.05
f0.1
, 0.15
Distance.from point C F ~mm~
] '~176
I ~__.~,--~.
=00 ~ -el i,-~..
-O*r
A
t=2
j
t~3
~--4..~
~.J_
t--4
ir'~
r
=uefmce ( a )
t~O.$ _ ]
?.-/ho .......
(A)
,. II
I
I I I . I I I
1 2 8 4 5 6
SIR depth d (mm)
Fig. 14-Relation between crack initiation stress amplitude and silt shapes.
/ Sp.c,m.. A "~-,~"
I00-- ~ A,C
Simple pad ( 5 4 M P a )
0 1
I 2 3
I
4
I I 5
S l i t po_sition t ~mm~
Fig. 15 Re]ation between crack initiation stress amplitude and slit position.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
168 FRETTINGFATIGUE: ADVANCES
Conclusions
1. A new estimation method for fatigue crack initiation criteria using plain fatigue limit,
threshold stress intensity factor range, and specific depth is proposed.
2. Using these fatigue crack initiation criteria, the stress-release slit design is optimized.
3. By optimizing the slit depth and slit position, the fretting fatigue crack initiation
strength can be increased to about 100 MPa, which is about twice that of a conventional
(i.e., slitless) design.
References
[1] Gassner, E., "The value of surface-protective media against fretting corrosion on the
basis of fatigue strength tests," Laboratoriumfur Betriebsfestigkeit TM19/67, 1967.
[2] Buch, A., "Fatigue and fretting of pin-lug joints with and without interference fit,"
Wear, 1977, 43, p. 9.
[3] Hattori, T., Kawai, S., Okamoto, N. and Sonobe, T., "Torsional fatigue strength of a
shrink- fitted shaft," Bulletin of the JSME, 24, 197, 1981, p. 1893.
[4] Cornelius, E. A. and Contag, D., "Die Festigkeits-minderung yon Wellen unter dem
Einflu/? von Wellen-Naben- Verbindungen durch Lotung, Nut und Pa/s
Kerbverzahnungen und Keilprofile bei wechselnder Drehung," Konstruktion, 14, 9,
1962, p. 337.
[5] Hattori, T., Sakata, S. and Ohnishi, H., "Slipping behavior and fretting fatigue in the
disk/blade dovetail region," Proceedings, 1983 Tokyo Int. Gas Turbine Cong., 1984,
p. 945.
[6] Johnson, R. L. and Bill, R. C., "Fretting in aircraft turbine engines," NASA TM X-
71606, 1974.
[7] Hattori, T., Nakamura, M. and Watanabe, T., "Fretting fatigue analysis by using
fracture mechanics," ASME Paper No.84-WA/DE-lO, 1984.
[8] King, R. N.and Lindley, T. C., "Fretting fatigue in a 3 l/z Ni-Cr-Mo-V rotor steel,"
Proc. 1CF5, 1980, p. 631.
[9] Sakata, H., Hattori, T. and Hatsuda, T., "An application of fracture mechanics to
fretting fatigue analysis," Role of Fracture Mechanics in Modern Technology, Elsvier
Science Publications B. V., 1987, p. 303.
[10] Hattori, T. and Nakamura, M., "Fretting fatigue evaluation using stress singularity
parameters at contact edges," Fretting Fatigue, ESIS Publication 18, 1994, pp. 453.
[11] Hattori, T., Nakamura, M., and Watanabe, T., "Fretting fatigue analysis of strength
improvement models with grooving or knurling on a contact surface," ASTM STP
1159, 1992, pp. 101.
[121 Dempsey, J. P. and Sinclair, G. B., "On the singular behavior at the vertices of a bi-
material wedge," J. Elasticity, 11, 1981, E 317.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Kozo Nakazawa, t Norio Maruyama, 1 and Takao Hanawa l
Reference: Nakazawa, K., Maruyama, N., and Hanawa, 1,., "Effect of Contact Pressure
on Fretting Fatigue in Type 316L Stainless Steel," Fretting Fatigue: Advances in Basic"
Understanding and Applications, ASIM STP 1425, Y. Mutoh, S. E. Kinyon, and D. W.
Hoeppner, Eds., ASTM International, West Conshohocken, PA, 2003.
Keywords: fretting fatigue, contact pressure, concavity, notch effect, austenitic stainless
steel
Introduction
In fretting fatigue, contact pressure is one of the most important factors. The effect
of contact pressure has been studied by many researchers. Most of the researchers found
that fretting fatigue life or strength decreased with an increase in contact pressure [1-9].
A few researchers found that the fretting fatigue life showed a minimum at a certain
contact pressure [10-14]. The present authors found a singular phenomenon in high
strength steel that under a certain test conditions, the fretting fatigue life exhibited a
minimum and a maximum with an increase in contact pressure [15, 16]. Waterhouse
~Leader, Senior Researcher, and Team Leader, respectively, Biomatenals Research Team, National
Institute for Materials Science, 1-2-1 Sengen, Tsukuba, 305-0047 Japan.
169
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
170 FRETTINGFATIGUE: ADVANCES
reported the effect of normal load on fretting fatigue life under the test of cylinder pad on
flat specimen and a fixed breadth of contact using alpha brass and aluminum alloy [10].
A minimum in life was observed at a certain normal load in aluminum alloy, but not in
alpha brass. The contact pressure dependence of life depended on materials used even if
the test conditions were the same. It is necessary to obtain a fundamental and consistent
understanding of the phenomenon as to the effect of contact pressure on fretting fatigue.
In the present study, the contact pressure dependence of life in type 316L austenitic
stainless steel was studied. It was found that contact pressure dependence 9f life was
different from that observed so far and that at high contact pressures, deep concavity was
formed at the fretted surface without accompanying heavy wear. This concavity was
suggested to significantly affect fretting fatigue judging from fracture behavior and
contact pressure dependence of life. This paper aims to make clear the effects of contact
pressure and the concavity on fretting fatigue life in type 316L steel.
Experimental Procedures
The material used was a type 316L austenitic stainless steel bar 25 mm in diameter.
Table 1 shows the chemical composition of the steel. The steel was solution-treated at
1323K for 10 min then water quenched. Its austenitic grain size was about 15 ~tm.
Mechanical properties of the steel are shown in Table 2. The yield strength and the
ultimate tensile strength of the steel are about 330 and 600 MPa, respectively.
Dimensions of the fatigue specimen and the fretting pad are shown in Fig. 1. Bridge-type
fretting pads of the same material as the fatigue specimen were used. The gage parts of
the fatigue specimens and the fretting pads were polished with 0-grade (#600) emery
paper and then degreased with acetone.
The fretting fatigue tests were performed on a 100 kN capacity dosed loop
electro-hydraulic fatigue testing machine. A constant normal pad load was applied by a
small hydraulic actuator. The contact pressure, calculated by dividing a normal load by
the apparent contact area for one foot of the fretting pad (2x6=12 ram2), was maintained
C Si Mn P S Ni Cr Mo
0.019 0.48 1.18 0.038 0.013 12.10 16.72 2.05
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAKAZAWA ET AL ON CONTACT PRESSURE/316L STAINLESS 171
, /o ,/
Fretting Pad
2 2
Figure 1 - Shape and dimensions (mm) of the fretting fatigue specimen and the pad.
~L/Fat
- igue
Specimen
FrettinPad
g
~~i[ ~ Normal Load
~CyclLoad
ic
Figure 2 - Exaggerated representation of fretting damage.
at a given contact pressure of 15 to 120 MPa. The tests were carried out using a
sinusoidal wave form at a frequency of 20 H_z, under load control at a stress ratio of 0.1
in laboratory air of 40 to 70% relative humidity at room temperature. The contact
pressure dependence of fretting fatigue life was studied at an axial stress amplitude of
180 MPa. This stress amplitude is equivalent to a maximum stress of 400 MPa.
Tangential friction force between the fatigue specimen and the pad was measured using
strain gauges bonded to the side of the central part of the pad. Frictional stress amplitude
was calculated by dividing a tangential friction force amplitude by apparent contact area
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
172 FRETTING FATIGUE: ADVANCES
Results
Fretting fatigue
Normal Load
DI
Specimen
Cyclic Load
D = (D1 + D2) / 2
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAKAZAWA ET AL. ON CONTACT PRESSURE/316L STAINLESS 173
300
i
3161. 20Hz
i600
13_
v
200
o•"•--.•Fatigue
"O 400
E Fretting Fatigue E
100 E
r
200
Contact Pressure
co o 30 MPa
zx 60 MPa
, , 11,1,,I , , , ,,,111 , , ,,,,,,r
04 10 5 10 6 10 7
Number of Cycles to Failure
Figure 4 - S-N curves of fatigue and fretting fatigue for contact pressures of 30 and
60 MPa.
60 I I I I
E
< 30
CO
CO
co 20
KI
t.-
.o 10
."6
u
LL
I I I I
0 50 100 15O 20O 250
Stress Amplitude (MPa)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
174 FRETTINGFATIGUE:ADVANCES
The S-N curves of fatigue and fretting fatigue at contact pressures of 30 and 60
MPa are shown in Fig. 4. Plain fatigue strength at 107 cycles is approximately 200 MPa.
At stress amplitudes of more than 150 MPa, fretting fatigue life at a contact pressure of
60 MPa is less than one third of that at a contact pressure of 30MPa. However, fretting
fatigue strength at 107 cycles at a contact pressure of 60 MPa is almost equal to that at a
contact pressure of 30 MPa. Relations between axial stress amplitude and frictional stress
amplitude for contact pressures of 30 and 60 MPa are shown in Fig. 5. The frictional
stress amplitude at a contact pressure of 60 MPa is larger than that at a contact pressure
of 30 MPa.
The effect of contact pressure on fretting fatigue lives of FF and F&FF tests are
shown in Fig. 6. The number of cycles to failure at a contact pressure of 0 means plain
fatigue life and is beyond l x l 0 7 'cycles. In the specimens of FF test, the fretting fatigue
life decreases sharply to 2x105 cycles at a contact pressure of 15 MPa. With an increase
in contact pressure, the life remains (2-3)x10 a cycles until at a contact pressure of 45
MPa, then decreases drastically at contact P4.ressures of more than 60 MPa. At contact
pressures of 90 to 120 MPa, the life is 5x10 cycles. In the specimens of F&FF test, the
fretting fatigue life decreases sharply at a contact pressure of 15 MPa just like in the
specimens of FF test. The life remains ~2-3)x105 cycles at contact pressures of 15 to 90
MPa and then decreases to about l x l 0 ~ cycles at a contact pressure of 120 MPa. At a
contact pressure of 15 to 45 MPa, the fretting fatigue lives in the specimens of both FF
and F&FF tests are almost the same, but the former is shorter than the latter at contact
pressures of more than 60 MPa. Relations between contact pressure and frictional stress
10 7 StressAmplitude 180MPa
o
D \ ; ;ra:~g::~atigue
12.
O3
106i ~ ~ Fretting Fatigue
105
E
z
10 4 I , I i I , I t I , I , I
0 20 40 60 80 100 120
ContactPressure (MPa)
Figurc 6 - The effect of contact pressure on fretting fatigue lives of FF and F&FF
tests.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAKAZAWA ET AL. ON CONTACT PRESSURE/316L STAINLESS 175
0 I I I I f
60
"0
E
< 40
O3
,=
-I--,
O9
t' -
20
._o
I.k
i I i I J I ~ I ~ I , I
00 20 40 60 80 100 120
Contact P r e s s u r e (MPa)
Figure 7 - Relations between contact pressure and frictional stress amplitude around
104 cycles for FF and F&FF tests.
amplitude for FF and F&FF tests are shown in Fig. 7. Frictional stress amplitudes of both
tests increase smoothly with an increase in contact pressure. There is almost no
difference between the frictional stress amplitudes for both tests.
Fretting damage
The initiation sites of the main cracks responsible for failure depend on the contact
pressure. Figure 8 shows fretted surfaces near the initiation sites of the main cracks in the
fractured specimens of both FF and F&FF tests for contact pressures of 30 and 120 MPa.
At a contact pressure of 30 MPa, the main cracks are initiated at a middle portion of the
fretted area for both specimens of FF and F&FF tests. At a contact pressure range of 15
to 45 MPa, the main cracks occurred similarly. At a contact pressure of 120 MPa,
however, the main cracks are initiated at the outer edge of the fretted area for the
specimens of both tests. At contact pressures beyond 60 MPa, the main cracks occurred
almost at the outer edge of fretted area for both tests. Especially in the specimens of FF
test, deep concavity is formed at the fretted area and the main crack occurs just at the
outer edge comer of the concavity as shown in Fig. 8(b).
Relations between depth of fretted area, D and stress amplitude at contact pressures
of 30 and 60 MPa in the specimens of FF test shown in Fig. 4 are shown in Fig. 9. The
depth of fretted area increases with an increase in stress amplitude, but the rate of
increase in the depth at a contact pressure of 60 MPa is higher than that at a contact
pressure of 30 MPa. Relations between depth of fretted area ~nd contact pressure at a
stress amplitude of 180 MPa in the specimens of both FF and F&FF tests shown in Fig. 6
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
176 FRETTING FATIGUE: ADVANCES
Figure 8 - Fretted surfaces near the initiation sites of the main cracks in the fractured
specimens of FF and F&_FF tests for contact pressures of 30 and 120 MPa. Arrows
indicate fretting scar produced in the early stage of test.
are shown in Fig. 10. The depth of fretted area increases almost lineady with an increase
in contact pressure. The rate of the increase in the depth for the specimens of FF test is
about five times higher than that for the specimens of F&FF test.
Discussion
With an increase in contact pressure, the fretting fatigue lives decrease sharply at a
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAKAZAWA ET AL. ON CONTACT PRESSURE/316L STAINLESS 177
2o
r"
121
[ _ _ I
Figure 9 - Relations between depth of fretted area and stress amplitude for contact
pressures of 30 and 60 MPa in the specimens of FF test.
100|- , j , , , ,
E~ Stress Amplitude 180 MPa
a o Fretting Fatigue
[] Fatigue &
'-- Fretting Fatigue
< 5O
IJ _
*6
~_ ...• . . . . . . . . . []
_-lJ .......
0 ---
0 20 40 60 80 100 120
Contact Pressure (MPa)
Figure 10 - Relations between depth of fretted area and contact pressure in the
specimens of FF and F&I~F tests.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
178 FRETTINGFATIGUE: ADVANCES
contact pressure of 15 MPa in both specimens of FF and F&FF tests as shown in Fig. 6.
At contact pressures of 15 to 45 MPa, the fretting fatigue lives in the former specimens
are almost equal to those in the latter specimens. This means that the application of plain
fatigue cycles of 104 prior to fretting fatigue test has almost no effect on subsequent
fretting fatigue life. With an increase in contact pressure from 15 to 45 MPa, both of the
lives remain almost unchanged, although the frictional stress amplitudes in both
specimens increase from 20 to about 40 MPa as shown in Fig. 7. It is well known that the
frictional stress amplitude is closely related to fretting fatigue life. In general, the fretting
fatigue life becomes shorter as the frictional stress amplitude increases [1]. There exists
no relationship between the change in fretting fatigue life and that in frictional stress
amplitude at contact pressures of 15 to 45 MPa.
The contact pressure and the frictional stress amplitude defined in the present
paper are nominal values, that is, normal load and tangential friction load ~er one foot of
the bridge-type pad were divided by apparent contact area (2x6 = 12 mm ). Hence, it is
assumed that their distribution at the fretted area is uniform. It is impossible to explain a
sharp decrease in life at a contact pressure of 15 MPa, directly by apparent contact
pressure and frictional stress amplitude. The decrease in life at low contact pressures was
probably caused by the local stress concentration at the fretted area proposed by
Nakazawa et al [15]. Under a certain testing condition, there exists a stick region in the
middle portion of a fretted area and slip regions on either side of it. This situation
depends on the contact pressure, relative slip amplitude and number of cycles [17, 18].
The higher the contact pressure, the wider the stick region. When the contact pressure is
low and the stick region is narrow, net values of contact pressure and frictional stress
amplitude acting in the stick region must be higher, while those in slip region must be
lower than nominal values due to the existence of wear debris and its removal from the
fretted area. The decrease in life at a contact pressure of 15 MPa was probably caused by
the concentration of contact pressure and frictional stress amplitude at narrow stick
region. Their net values must have been considerably larger than the apparent ones. At
low contact pressures, the main cracks responsible for failure occurred at the middle
portion of fretted area as shown in Fig. 8. This result also supports an existence of both
narrow stick region and stress concentration there, since the crack is sometimes initiated
at slip region near the boundary between the stick region and the slip region [15, 18].
In the specimens of F&FF test, the fretting fatigue life at contact pressures of 60 to
90 MPa, is almost the same as that at low contact pressures. It decreases slightly at a
contact pressure of 120 MPa. In the specimens of FF test, however, the fretting fatigue
life decreases down to about one third of the life in F&FF test at contact pressures of
more than 60 MPa. The shorter fretting fatigue lives in FF test at contact pressures of
more than 60 MPa compared with that in F&FF test cannot be explained by the frictional
stress amplitude shown in Fig. 7, since the frictional stress amplitudes in both tests are
almost the same. When the contact pressure is high, the depth of concavity at the fretted
area is large in FF test, but small in F&FF test as shown in Fig. 10. Furthermore, the
main crack initiation in the specimens of FF test occurred just at the outer edge comer as
shown in Fig. 8(b). These results suggest that the outer edge of fretted area acts as a
source of stress concentration. The shorter fretting fatigue lives were probably related to
stress concentration arising from profile of the outer edge rather than from so-called
fretting damage. The fretting fatigue lives of both tests at contact pressures of 15 to 45
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAKAZAWA ET AL. ON CONTACT PRESSURE/316L STAINLESS 179
MPa are probably not affected by the concavity, since its depth is small.
At stress amplitudes of more than 150 MPa, fretting fatigue lives at a contact
pressure of 60 MPa are extremely shorter than that at a contact pressure of 30 MPa as
shown in Fig. 4. It is suggested that the fretting fatigue life at a contact pressure of 60
MPa is probably affected rather by the stress concentration due to the concavity than by
the frictional stress amplitude shown in Fig. 5, since the life in F&FF test at a contact
pressure of 60 MPa is almost the same as that at a contact pressure of 30 MPa as shown
in Fig. 6. The fretting fatigue strength at 107 cycles for a contact pressure of 30 MPa is
140 MPa and is equal to that for a contact pressure of 60 MPa. At a stress ratio of 0.1
used in the present study, the stress amplitude of 140 MPa corresponds to the maximum
stress of about 310 MPa. This maximum stress value is smaller than the yield strength of
316L steel used (Table 2). Hence, the depth of concavity is small as described later and
there is no effect of concavity on the fretting fatigue strength.
Formation of concavity
In fatigue or fretting fatigue test under load control, parallel gauge section of the
specimen is deformed plastically and elongated during loading when the maximum stress
is exceeded beyond yield stress. In 316L steel used in the present study, work hardening
occurs with an increase in strain. After unloading, parallel gauge section remains as being
uniformly elongated to the loading axis due to the plastic deformation. Figure 11 shows a
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
180 FRETTINGFATIGUE: ADVANCES
load-elongation response of the fretting fatigue specimen subjected to plain fatigue of 104
cycles without fretting pads under load control at a stress amplitude of 180 MPa at a
frequency of 1 Hz. The elongation was measured using an extensometer attached to the
parallel gauge section of the specimen. With an increase in number of cycles, the
elongation increases, and the maximum load increases and the minimum load decreases.
The load change in the early stage of fatigue experiment probably resulted from transient
loading state to stable load response under load control in closed loop electro-hydraulic
fatigue testing machine. At 50 cycles, the load approaches to a certain value, and
permanent elongation is about 3.5%. At 104 cycles, the elongation is almost saturated,
and the permanent elongation is about 4.2%.
The fretting pad is deformed elastically due to frictional force that develops
between two pad feet, although fretting fatigue specimen is deformed plastically and
elongated permanently with number of cycles in the early stage of test. Thus, the span
length between the two fretting scars of pad feet on the specimen surface along cyclic
stress axis is expanded outwards with an increase in number of cycles, but the position of
contact area is almost fixed after 104 cycles, in Fig. 8 (a) and (b), fretting scar produced
in the early stage of test is seen to be adjacent to the main scar as shown by arrows.
In the specimens of FF test, the depth of concavity at the fretted area increases with
an increase in contact pressure as shown in Fig. 10, This result was probably caused by
the fact that the degree of constraint of specimen deformation along its thickness
direction by fretting pad is large when the contact pressure is high. The depth of
concavity also increases with an increase in stress amplitude under a given contact
pressure as shown in Fig. 9. Furthermore, the maximum stress values at the depth Of
concavity zero of the extrapolated relationship between stress amplitude and depth of
concavity for contact pressures of 30 and 60 MPa are about 250 and 300 MPa,
respectively. These stress values are smaller than the yield strength. However, they are
roughly equal to the yield strength, and this suggests that the formation of concavity is
closely related to plastic deformation. The deep concavity observed in the present study
is probably associated with low yield strength of 316L steel used.
On the other hand, in the specimens of F&FF test, cyclic strain hardening occurs
due to plain fatigue of 104 cycles prior to fretting fatigue test. By this plain fatigue,
Vickers hardness number of the specimens is increased from 160 to 200. Consequently,
the depth of concavity is small even though fretting fatigue test is started successively
after the plain fatigue, since the plastic deformation of the specimen during fretting
fatigue test is slight. The situation of concavity formation in a cold worked 316L steel
may be different from that in a solution-treated one used in the present study.
Conclusions
The effect of contact pressure on fretting fatigue in type 316L stainless steel has
been studied at a stress amplitude of 180 MPa. The conclusions obtained are as
followings.
(1) With an increase in contact pressure, fretting fatigue life is almost unchanged at
contact pressures of 15 to 45 MPa, but it decreases drastically at contact pressures
beyond 60 MPa. It is impossible to explain the contact pressure dependence of life by the
change in frictional stress amplitude since the frictional stress amplitude increases
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NAKAZAWA ET AL. ON CONTACT PRESSURE/316L STAINLESS 181
References
[1] Nishioka IC and Hirakawa K., "Fundamental Investigation of Fretting Fatigue (Part 6,
Effects of Contact Pressure and Hardness of Materials)," Bulletin of the JSME, Vol.
15, 1972, pp. 135-144.
[2] Endo K. and Goto H., "Initiation and Propagation of Fretting Fatigue Cracks," Wear,
Vol. 38, 1976, pp. 311-324.
[3] Gaul D. J. and Duquette D. J., "The Effect of Fretting and Environment on Fatigue
Crack Initiation and Early Propagation in a Quenched and Tempered 4130 Steel,"
Metallurgical Transactions, Vol. llA, 1980, pp. 1555-1561.
[4] Sato K. and Fujii H., "Fretting-Fatigue Strength and Fracture Morphology of Carbon
Steel $45C," Journal of Japan Society of Strength and Fracture of Materials, Vol.
18, 1984, pp. 98-113 (in Japanese).
[5] Nagata K., Matsuda T., and Kashiwaya H., "Effect of Contact Pressure on Fretting
Fatigue Strength," Transactions of the Japan Society of Mechanical Engineers, Vol.
53, 1987, pp. 196-199 (in Japanese).
[6] Mutoh Y., Nishida T., and Sakamoto I., "Effect of Relative Slip Amplitude and
Contact Pressure," Journal of the Society of Materials Science, Japan, Vol. 37,
1988, pp. 649-655 (in Japanese).
[7] Satoh T., Mutoh Y., Yada T., Takano A., and Tsunoda E., "Effect of Contact Pressure
on High Temperature Fretting Fatigue," Journal of the Society of Materials Science,
Japan, Vol. 42, 1993, pp. 78-84 (in Japanese).
[8] Adibnazari S. and Hoeppner D. W., "A Fretting Fatigue Normal Pressure Threshold
Concept," Wear, Vol. 160, 1993, pp. 33-35.
[9] Satoh T., Mutoh Y., Nishida T., and Nagata K., "Effect of Contact Pad Geometry on
Fretting Fatigue Behavior," Transactions of the Japan Society of Mechanical
Engineers, Vol. 61, 1995, pp. 1492-1499 (in Japanese).
[10] Waterhouse R. B., "The Effect of Clamping Stress Distribution on the Fretting
Fatigue of Alpha Brass and Al-Mg-Zn Alloy," Transactions of American Society for
Lubrication Engineers, Vol. 11, 1968, pp. 1-5.
[11] Switek W., "Fretting Fatigue Strength of Mechanical Joints," Theoretical Applied
Fracture Mechanics, Vol. 4, 1985, pp. 59-63.
[12] Fernando U. S., Farrahi G. H., and Brown M. W., "Fretting Fatigue Crack Growth
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
182 FRETTINGFATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Chung-Hyun Goh, 1Richard W. Neu, l and David L. McDowell I
Introduction
Fretting is a damage process that is associated with local adhesion and oscillatory
displacements between contact surfaces, subjected to a cyclic, relative motion of
extremely small amplitude. Since fretting fatigue damage accumulation occurs over
relatively small volumes, the subsurface-stress state is expected to be rather non-
uniformly distributed in polycrystalline materials. The scale of the cyclic plasticity and
the damage process zone is often on the order of microstructural dimensions and the
resolution of the local stick/slip behavior along the interface may play a key role in
fretting fatigue damage process. Thus, the role of the microstructure as well as the
coefficient of friction (COF) within the fretting boundary layer is quite significant in
fretting fatigue analysis. The latter influence is found to play a first order role in the
distribution of contact stresses and plastic strain fields, yet cannot be directly controlled
in the experiment and evolves during testing.
The heterogeneity of discrete grains and their crystallographic orientation is accounted
for using continuum crystallographic cyclic plasticity models coded in an ABAQUS User
MATerial (UMAT) subroutine [1]. To provide credence for the non-homogeneous
crystal plasticity modeling approach, simulations of fretting fatigue were compared with
the results developed by an initially isotmpic J2 plasticity model as well as experiments
when Ti-rA1-4V is fretted against itself. This study explores the nature of subsurface
cyclic plasticity and contact stress/strain fields considering different pad loads and different
1GraduateResearch Assistant, AssociateProfessor, and Professor, The George W.
WoodruffSchool of MechanicalEngineering,Georgia Instituteof Technology,
Atlanta, GA 30332-0405.
183
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTMlntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
184 FRETTINGFATIGUE: ADVANCES
values of COF. In this work, we primarily address the latter issue by conducting the
finite element (FE) simulations based on crystal plasticity theory, comparing to Jz
plasticity theory with nonlinear kinematic hardening flow rule as well as experimental
results and observations.
where ~ is the effective stress, s" is the reduced deviatoric stress tensor, or0 is the initial
yield strength, and R is the radius of the yield surface. The reduced deviatoric stress
tensor is given by
{'=(s-x) (2)
where s and x are the deviatoric Cauchy stress and the deviatoric backstress tensors,
respectively: s = q - l t r ( q ) / with q the Cauchy stress tensor and / the second order
identity tensor.
For an associated flow rule, the unit normal vector can be represented as
af / ~ q _ s" (3)
n-II f/a- ll VII
The associated plastic flow rule is given by
/ \1/2
where H is the plastic modulus, q = C : ( D - D P ) , p = ~ P : ~ P ) , and the Macauley
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 185
af .e+of (5)
-5-7- ax:-
~
The plastic modulus with N decoupled backstress components is given by the normality (or
associated) flow rule based on a kinematic hardening Mises yield surface, i.e., for j~ = 0 :
H = ~ , ( ha-h~ x ~: n ) (6)
where N represents the number of backstress components and h and hD are direct
hardening and dynamic recovery coefficients, respectively. In this study, two
components of the backstress are used and the constants for duplex Ti-6AI-4V, based on
correlation to the cyclic stress-strain response, are: Go = 765 MPa, h 1= 7484 MPa,
h z ---725 MPa, h~ = 486, and hZo= 37. The reader is referred to the thesis of Matin [2]
and related paper (Matin and McDowell [3]) for more details.
= 6"6 p (7)
where F e is the elastic deformation gradient representing elastic stretch (or compress) and
rotation of the lattice, as well as the rigid body rotation, while F p is the plastic
deformation gradient describing the collective effect of dislocation motion along the active
slip planes relative to a fixed lattice in the reference configuration. The kinematics of
elastic-plastic deformation of crystals is shown in Fig. 1. In the figure, the grids represent
the crystal lattice; s o and n o denote the initial unit vectors in the slip direction and the slip
plane normal direction, respectively, for the d h slip system in the undeformed
configuration, s ~ and n ~ are not generally unit vectors, but they remain orthogonal to the
slip direction since s o -no=s . n ~ = 0 . As the material plastically deforms, the lattice
undergoes elastic deformation and rigid rotations.
The resolved shear stress (or the Schmid stress) on the a ~ slip system is given by
r ~= q : ( : | (8)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
186 FRETTINGFATIGUE: ADVANCES
where s~| ~ denotes the tensor product of two vectors s g and n ~ . The power-law
relation on the d h slip system is described by
~'g--X g m
7"~=~'o--~ sgn(z'~-x=) (9)
where G represents the isotropic drag strength, m is the flow exponent (or inverse strain-
rate sensitivity exponent), x '~ is the backstress on the a th slip system, and Y0 is the
reference shearing rate. Here, a~ = 1, 2, 3 for the planar triple slip systems. The
backstress evolves according to a pure nonlinear kinematic hardening rule of the
Armstrong-Frederick type, i.e.,
The crystal plasticity algorithm is coded into an ABAQUS UMAT subroutine [4-5].
The microstructure of the Ti-6A1-4V alloy consists of two phases, 60% primary cz and
40% lamellar colonies of ct+[3 phase, with a Young's modulus of 118 GPa and a
Poisson's ratio of 0.349 [7]. In the Ti-6A1-4V alloy with duplex microstructure, slip in
the HCP ct phase typically dominates and prismatic slip is the most active deformation
mode at room temperature [8].
As shown in Fig. 2, the crystal plasticity model with the planar triple slip idealization
has been shown to accurately represent the macroscopic cyclic stress-strain behavior of
the Ti-6A1-4V, which exhibits a nearly elastic-perfectly plastic response, while the planar
double slip idealization, commonly used for FCC materials, doesn't exhibit this
relationship with any combination of constants. This is due to the fact that with only two
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 187
slip systems in the 2D idealization, any arbitrary 2D plastic deformation must involve
both slip systems activated to the same order of shearing rate. Accordingly, the
hardening within each grain occurs at a higher rate during plastic straining. Adding a
third slip system gives a redundant system (more systems than required to accommodate
arbitrary 2-D deformation), and leads to less work hardening. Therefore, the third slip
system in the planar triple slip model is essential for describing the nearly elastic-
perfectly plastic cyclic behavior of this material. Furthermore, it is quite sensible in view
of the room temperature dominance of the prismatic slip mode for c~, which has three
systems. We believe that this is a general characteristic of two-phase systems with strong
heterogeneity and relatively weak matrix strain hardening. These systems tend to
promote shear localization. The constants for the planar triple slip model describing
duplex Ti-6A1-4V are: F0 = 0.001 s1, G = 404 MPa, m= 63, h = 500 MPa, ho = 100.
The method of determining the constants is described in Ref [9].
~176
3rd Slip system ~'~r
S3 ~ I
w ~ ~ . xX
(b) 1200
3, 1000
....... - 1 1 1 1
/
i I
aoo #1 iii
600
400 o TripleSlipIdealization
- - - DoubleSlipIdealization
200
CyclicStress-Strain
0
0 0.0O5 0.01 0.015 0.02 0.025 0.03
Effective Strain
Figure 2. (a) Planar triple slip system idealization and (b) comparison of planar double
and triple slip idealization for Ti-6Al-4V (G=404 MPa, m=63, h=500 MPa, ho=lO0,
Y0= 0-001s -z, E=118 GPa, and 1/=-0.349).
The frictional behavior is usually expressed in terms of the interfacial stresses of the
contact. Coulomb friction is the standard friction mode/implemented in ABAQUS [1].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
188 FRETTINGFATIGUE: ADVANCES
The Coulomb friction model assumes that sticking (no relative motion) occurs if the
maximum shear stress (rm,x) is less than a critical stress (rcr,,) and the contacting bodies
will slide when rm~x= T~r,,9 The critical stress (r~r,,) is given by
where/~ and p are the COF and the normal (or direct) contact pressure, respectively.
Two methods exist in ABAQUS to implement Coulomb friction: a Lagrange multiplier
method and a penalty method (see Fig. 3). The advantage of a Lagrange multiplier
method is the exact nature it captures the sticking conditions, where the relative motion is
zero. However, the Lagrange multiplier implementation tends to slow or sometimes
prevent convergence of the solution due to the presence of rigid constraints. In the
penalty method, the sticking condition is approximated with penalty stiffness (G) to
facilitate convergence. Instead of G = co, G is adapted continuously by the ratio of
critical shear stress and elastic slip, i.e. G = "Ccr'/~
v in the penalty method. Even with
/ Yen,
the convergence difficulties, the Lagrange multiplier formulation is attractive in fretting
fatigue analysis since the resolution of stick/slip behavior along the interface is
considerably important in fretting.
(a) (b)
Figure 3. Diagram of the Coulomb friction model [1]: (a) Lagrange multiplier method
and (b) penalty method, where ~:r~x and for,, are the maximum and critical shear
stresses, respectively. Also, Ycr, and Ay are the critical elastic slip and the slip (or
relative motion) increment, respectively, and G is penalty stiffness.
FiniteElementImplementation
A finite element analysis is conducted by modeling a symmetric section of the
experimental configuration consisting of the fretting pad and fatigue specimen as shown
in Fig. 4(a). The fretting pad is cylindrical with a radius of curvature (R) of 50 mm and
the fatigue specimen has dimensions of 5.0 mm (z-direction) by 12.7 mm (y-direction).
In this configuration, the trailing edge is on the left side of the contact zone for a tensile
loading. The pad and specimen are fixed in the x- and y-directions along planes of
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 189
symmetry. The elements of the spongy layer are constrained in both the x- and y-directions
along the very top of the layer. The normal load, W, is first imposed and then three fatigue
loading cycles are prescribed to the specimen in the x-direction to account for cumulative
history effects (Fig. 4(b)). The fatigue load (F,p) applied to the specimen is given by
F,p=a(w,• (12)
where o" is the bulk applied stress to the specimen, and w~ and t~ are the width and
thickness of the specimen, respectively. The maximum and minimum values of Fsp are
determined by stress ratio (R~ = o ' ~ n / c r ~ ) and the fatigue specimen bulk stress
amplitude (cr, = (Crn~x-~r~,.)/2 ) for a given dimension. For all the cases considered in
this paper, R~ = 0.1 and era = 150 MPa. Therefore, the applied stress to the specimen (~r)
is linearly varied from the minimum of 33.33 MPa to the maximum of 333.33 MPa with
time during the loading cycle.
: ~ i i i i i
0 1 2 3 4 5 6 7
Time (sec)
Figure 4. (a) Finite element mesh of experimental configuration and (b) the load history
for R~ = 0.1, where Wand Fsp denote the normal load and the fatigue load applied to the
specimen, respectively, and Points A, B, C, D denote time steps to represent interface
stress evolutions in the later section.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
190 FRETTINGFATIGUE: ADVANCES
For the elements under the contact zone, a mapped mesh is used with the element size
of 10 gm. To improve efficiency, only the elements in the region of contact, 4 mm
(length) x 0.5 mm (depth), employ the crystal plasticity constitutive model, while the
remaining elements are either specified as J2 plastic or purely elastic depending on the
location relative to the contact region. The pad is elastic and the spongy layer is assigned
a modulus of 104E.
Eight-noded biquadratic quadrilateral 2-D solid plane strain elements with reduced
integration (ABAQUS CPESR) are used and plane strain conditions are assumed in the
analysis. Contact pair elements are used with the small sliding "option within ABAQUS
[1] to represent fretting contact between the fretting pad and the specimen. A Lagrange
multiplier implementation is used to enforce the sticking constraints along the interface
between two contacting surfaces since the resolution of the stick/slip behavior is very
important for simulating fretting contact between two bodies.
Assignment of discrete grains (size and geometry) is achieved by grouping elements
with the same prescribed crystallographic orientation prior to running the simulation.
The angle of orientation (0) of the bisector axis of each grain relative to the global x-
direction is randomly assigned in the ABAQUS UMAT subroutine. To facilitate
comparison among the different loading cases, the same grain orientation assignment is
used for each case. The grain is assumed as a square of 50 lxm by 50 Ixm (i.e., 5 elements
by 5 elements); no distinction is made between tx grains and ~-13 lamellar grains in the
duplex microstructure.
Results
Since fretting fatigue is a surface-related damage process, the role of the coefficient of
friction (COF) along the interface is quite significant in fretting fatigue analysis. To
study the influence of the COF, FE simulations have been conducted for the following
conditions: stress ratio (R~) of 0.1, a bulk fatigue stress amplitude (tr,) of 150 MPa, two
normal fretting pad loads, W =1350 N (=0.3p,) and W =4050 N ( = 0 . 9 p , ) , and three
different values of COF, B = 0.75, /~ = 1.0, and kt = 1.5 ; py is the critical peak load for
initial subsurface yield [10]. Simulations using completely elastic material as well as J2
plasticity with a nonlinear kinematic hardening rule are also used to "benchmark" the
results of the simulations using crystal plasticity.
The contact stress fields along the interface may be first investigated in order to
understand the effects caused by the local surface stresses during the fretting fatigue
process. The fretting damage processes are not only associated with the microslip at the
contact surface but also the cyclic fretting contact stresses [11]. The stress distributions
along the interface at the end of 3ra loading cycle, developed from various material
models, are compared in Fig. 5. The width of the stick region found experimentally for
this loading condition is more closely represented by the /.t = 1.5 case [12]. For all
material models, the stress distributions are almost the same except near the trailing edge
in the tr= distributions (see Fig. 5 (a) and (b)). At the trailing edge, particularly for the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 191
r162
= 1.5 case, both the J 2 and crystal plasticity simulations predict a lower stress than the
elastic simulations due to stress redistribution resulting from plastic deformation. The
stress distributions of the crystal plasticity and J2 plasticity simulations are essentially the
same except for small fluctuations at the trailing edge due to crystallographic grains when
crystal plasticity is used.
o. f F
;ol
o~ x__. - - i to, I
-~.~ -, -o.~ o o.~ ~ ~.~ -1.~ -~ -o.~ o o.~ , ~.~
Normalized Position (x/a) Normalized Position (x/a)
0.2 0.2
u~ 0 I I l l J l l i l t l l J ~ l l b l l 0 9 I ~ I b I I I / I I I I I I I I I i r t
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
192 FRETTINGFATIGUE: ADVANCES
[13]. When/2=0.75 is used (not shown), the extent of the cumulative effective plastic
strains is very small in the crystal plasticity simulation and no plastic strain accumulation
is found in J2 plasticity simulation. Even with crystal plasticity, elastic shakedown is
reached by the third cycle, clearly missing the extent of deformation experimentally
observed in the subsurface layers for the same fretting fatigue condition.
Also, the/2=0.75 case predicts a gross slip condition but partial slip conditions clearly
prevail in this loading case from experimental observations [12]. Our FE simulations
using crystal plasticity and/2 = 1.5 offer the closest description of the experimentally
observed cracking behavior for specimens with the same loading conditions.
When two materials in contact experience relative sliding motion under cyclic
loading, plastic strain accumulation increases with the cycles and this plastic deformation
induces crack nucleation. Although the maximum plastic deformation occurs at the
surface, the depth of nucleation process volume may contribute significantly to whether
crack of a critical length is able to nucleate. Note that there are no significant differences
in the stress distributions between the various plasticity models as shown in Fig. 5, yet
the cumulative plastic strain fields are significantly different. Therefore, the localization
of plastic deformation cannot be represented well by the contact stress distribution or
subsurface stress field. Subsurface distributions of the cumulative effective plastic strain
as well as the plastic strain-based multiaxial fatigue criteria based on the crystal plasticity
model exhibit more realistic representation of the localization of plastic deformation,
comparable to experimental observations, than when J2 plasticity theory is used [13]. Of
course, purely elastic calculation renders little information relevant to microstructure-
scale plastic deformation and damage processes.
Figure 6. Cumulative effective plastic strain distribution in the subsurface region at the
trailing edge at the end of 3ra loading cycle for the case: R~=0.1, cr,=15O MPa,
W = 1350 N, and /2 = 1.0, showing influence of material model (a) .I2 plasticity and (b)
crystal plasticity.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 193
Figure 7. Cumulative effective plastic strain distribution in the subsurface region at the
trailing edge at the end of 3 r~ loading cycle for the case." R~=0.1, cr,=15O MPa,
W = 1350 N, and At = 1.5, showing influence of material model (a) J2 plasticity and (b)
crystal plasticity.
In fretting, the contact area generally consists of two regions, stick and slip (or micro-
slip) zones. A modification of surface topography may contribute locally to increasing
the COF and give way to stick in some micro-slip regions. In sticking zone, adhesion can
occur but little surface modification is anticipated in the sense that no relative motion will
occur within this area. On the other hand, plastic deformation and some surface
modification are inevitable in the relative slip zone [14].
The relative slip range along the interface is shown in Fig. 8. The peak value of the
relative slip range at the edge of contact on the trailing edge side is around 2.2/tin for both
COF cases. Interestingly, near the boundary between the stick and slip regions crystal
plasticity predicts a region where alternating stick and nanoslip occurs, whereas both
elasticity and J2 plasticity predict that the transition between stick and slip occurs at a single
point (see Figs. 8(b) and (d)). The mixed stick/slip region of the lower COF case (Fig.
8(b)) extends wider and has smaller magnitude than the higher COF case (Fig. 8(d)).
The mixed stick/slip ~region can be also seen by plotting the ratio of local shear
traction, q(x), to normal traction, p(x) as shown in Fig. 9. Fig. 9 shows the variation of
q(x)/p(x) over the contact area at the end of 3 ra loading cycle for the cases of p = 1.0
and kt = 1.5. The successive stick/slip regions lead to multiple stress concentration sites
along the interface. As a consequence, the plastic deformation from the crystal plasticity
theory naturally leads to a surface roughness from an initially smooth surface without the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
194 FRETTING FATIGUE: A D V A N C E S
need to employ any ad hoc asperity size and spacing algorithms. Thus, the surface may
locally experience the sticking conditions in the slip region. In the Figures 8 and 9, the
dashed boxes represent a stick zone in the mixed stick/slip regions; the locations
correspond to each other between the two figures.
~ 3.0 0.008
o J2 ...... J2
0.006
~ 2.0 Crystal
0.004
.~ 1.0
0.002
~ 0.0 0.000
\ ....................." L. . . . . J
-1.0 -0.002 . . . . . . . . . . . . . . . i [ r [ i i i i [ i i i i
0.06
t
2.0 Crystal Crystal
~~~176176
0.04
1.0
0.02
rD3
0.0 0
I. . . . . . J
"...............--"
-0.02
-1.0 i i r i I r i t i I I n a I
The ratio of the frictional force to normal contact load, Q/P, is computed from the FE
simulations throughout three cycles using
Q _ ~q(x) dA (13)
P Sp(x)dA
The ratio of Q/P starts from 0.01 in the beginning of the 1st loading cycle and at the end
of the loading cycle reaches a value of 0.88 (/.t =1.0) and 0.9 (/z =1.5). On the other
hand, the ratio of the local q(x)/p(x) varies from 0.65 to 1.0 f o r / z = 1.0 and from 0.55
to 1.5 for /z = 1.5 along the interface during the 3rd loading cycle with the peak values
being in the slip region (see Fig. 9). An estimate of the COF in the steady-state slip
region based on the size of the stick and slip zones found experimentally gave average
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 195
values of COF in the slip region ranging from 0.71 to 1.06 [12]9 The analysis suggests
that very local stress contractions near the stick/slip regions lead to high local effective
COF values.
1.02
I.,2I
1.25
;.- . . . . . . . ..]
I I
9 w - \| ~r 1
1
0.98
0.75 ..... J2 I
0.96
Crystal
-0.75 -0.25 0.25 0.75 1.25 -0.60 -0.50 -0,40 -0.30 "0.20
~ 1.496
1
1 492
0.5
1.488
~ i
0 i I i I i i i , I J i i , I i , i .... : .... : .... : .... , .... ,, . . . .
1.484
-0.75 -0.25 0.25 0.75 1.25 -0.68 -0.63 -0.58 -0.53 -0.48 -0.43 -0.38
Normalized Position (x/a) N o r m a l i z e d Position (x/a)
(c) At = 1.5 (d) /~ = 1.5
Figure 9. The ratio of local shear traction ( q(x) ) to normal traction (p(x)) predicted by
the FE simulation along the interface of the fatigue specimen at the end of 3'd loading
cycle and a magnification of the circled region showing the mixed stick~slip region for
conditions: R~ = 0.1, era = 150 MPa, and W = 1350 N ( a = 514 pm).
To better understand the evolution of the surface stresses and stick/slip conditions
during the fretting fatigue process, four points in the loading portion of the 3 ra cycle,
noted as A, B, C, and D in Fig. 4(b), are examined. The interface shear stress
distributions are shown in Fig. 10. In the figure, Q denotes frictional force (F) per unit
length (L), i.e. Q = F/L, and trrepresents the applied stress to the specimen during cyclic
loading. The shear stress ( t r ~ ) is normalized by the cyclic yield stress (try = 765 MPa)
and the applied stress (o') is normalized by the product of COF (/t) and the maximum
normal pressure (p0 = 349 MPa). The frictional forces (F) are computed from FE
analysis by summing the reaction forces in the pad along the y-axis plane of symmetry.
In this component model, these reaction forces are not prescribed, but are coupled with
the fatigue load (F,p) applied to the specimen. The frictional force per unit length
( Q = F / L ) is then normalized by COF (g) and the normal load per unit length
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
196 FRETTING FATIGUE: ADVANCES
( P = W / L ) of 1350 N I mm. The nature of the stick and slip regions along the interface
at these four points in the loading portion of the 3rd cycle for the cases of At = 1.0 and
li = 1.5 are illustrated in Fig. 11.
(a) 0.6
(b) 0.8
For #=1.5, at the minimum load just after the load reversal (Point A), there exists only
a stick region with no slip. At Point B, slip occurs at the trailing edge while a mixed
stick/slip region is present at the leading edge. The negative shear stress exists at the
trailing edge until the load reaches the value of Q/IIP = 0.49 and ~r/lIp o = 0.52 (Point
C) (see Fig. 10). As the load increases, the slip zone size increases while the stick zone
size decreases. Interestingly, the mixed stick/ slip zone is observed at the boundary
between the slip and stick zones at the trailing edge near the peak of the loading. Also,
the contact zone is shifted to the right by 0.2a mm at the final state of the 3 rd loading
cycle (Point D: Q / l I P = 0.6 and o / l i p o = 0.64). During the unloading of the 3 ~ cycle,
the order of phenomena is reversed. The lower COF case, li=l.0, shows similar tendency
as the li=l.5 case though the mixed stick/slip region near the leading edge is observed at
a later time step (Point C); it is present from Point B for li=l.5 case (see Fig. 11).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 197
(a)
D
C m
E
B
}
A
l l l l , r b i I' ' r i i I i t , i I J i i r,, I J, ,' I,, r
(b)
D
A
r , , i ~ i , i r i, i i J i I r , i i I J i i
I
, Slip Region Stick Region X Mixed Stick/Slip Region I
Figure 11. Stick and slip regions along the interface based on crystal plasticity model at
four points in the 3 rd loading cycle, as noted in Fig. 4(b), (a) lZ = 1.0 and (b) p = 1.5 for
the case: R,~ = 0.1 and o-, = 150 MPa ( W = 1350 N and a = 514 ktm ).
The total and plastic strain distributions predicted using the different material models
and COF are compared in Figs. 12 and 13, respectively. In the figures, the strain
components are normalized by the yield strain (ey = 0.0065). The strain distributions
show similar tendency for all material models but there exist significant differences
among the material models at the trailing edge where significant plasticity occurs,
particularly in shear strain distribution with the higher COF (Fig. 12(d)). In the plastic
strain distributions, crystal plasticity theory predicts nonhomogeneous distributions,
which likely results from the shear localization due to the heterogeneity of the
microstructure whereas the J2 plasticity model predicts smooth distributions as shown in
Fig. 13. Crystal plasticity simulations exhibit fluctuations in stress and strain distributions
along the contact surface due to alternating hard and soft orientations of surface grains
leading to a natural length scale for roughness, i.e. in these simulations, the grain scale.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
198 F R E T T I N G FATIGUE: A D V A N C E S
1.5 2.0-
...... Elasticity ...... Elasticity
"~ 1.0 o J2 1.5- o J2
Crystal
t 0.0 0.0-
-0,5 -0.5 . . . . : . . . . : . . . . ; . . . . : ' '--'V'
-1.5 -1 -0.5 o 0.5 1 1.5 -1.5 -1 -0.5 0 0.5 1 1.5
Normalized Position (x/a) N o r m a l i z e d Position (x/a)
( a ) / ~ = 1.0 (b) /z = 1.5
1.5. 3.0
A [ ..... Elasticity
2.5
.= 1,2 II I, ~ J2
1.5
,~ 1.0
r~ 0.3. r~
0.5
0.0. 0.0 lllll Jl i r r l l l t l l l l l
-1.5 -1 -0.5 0 0.5 1 1.5 -1.5 -1 -0.5 0 0.5 1 15
Normalized Position (x/a) N o r m a l i z e d Position (x/a)
(c)/~ = 1.0 (d)/z = 1.5
Figure 12. The total strain distributions along the interface at the end of 3m loading
cycle, comparing material models and COF: tangential strain ( ex,) and shear strain
(e~y) distributions for the case: R a = 0 . 1 , tra=15OMPa, and W = 1 3 5 0 N
(ey = 0.0065 and a = 514 r
The subsurface distributions of the cumulative effective plastic strain based on the J2
and crystal plasticity simulations for an increase in contact load, W=4050 N, w i t h / t = 1.5
are shown in Fig. 14. These results should be compared to the lower normal load case
( W = 1 3 5 0 N ) shown in Fig. 7. Comparing the two cases, the heterogeneity of the
cumulative plastic strain field for crystal plasticity appears to be magnified in the lower
normal load case, when the extent of plastically deforming material at the surface is of
the same magnitude as the grain size or smaller. To better understand the influence of
contact load on the subsurface cumulative plastic strain fields, the distributions of stress
and strain along the interface at the end of 3 rd loading cycle are shown in Figs. 15 and 16.
For clarity, only the stress and strain distributions from J2 plasticity model are shown; the
crystal plasticity distributions are similar though with some fluctuation near the trailing
edge similar to what is shown in Figs. 5 and 12. With increasing COF, the maximum
shear stress increases particularly at the trailing edge in both normal loading cases (Fig.
15). The distributions in both tangential (cr=) and shear (Cr,y) stresses significantly vary
with increasing COF over the entire contact region in case of the lower normal load,
W =1350 N while there are no significant differences due to variation of COF except
near the trailing edge (left side of the curve) in the higher normal load case, W=4050 N.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUSMATERIAL 199
~ 0,30 ~ 0.8
~ 0.25
...... J2 ...... J2
Crystal
o.s Crystal
.= 0.20
~ 0.15 0.4
"~ 0,10 !
0.2
0.05
" 0.16 t 1 _
1"01 ....... ''" .... J2
- _ _
Crystal
0.12
0.04- 0 2
r~
000 .... ; I~i:, , ; :,,,; , ,: ' r~ 0.0
-1.5 -1 -0.5 0 0.5 1 1.5 -1.5 -1 -0.5 0 0.5 1 1.5
Normalized Position (x/a) N o r m a l i z e d Position (x/a)
(c) /2 = 1.0 (d) /2 = 1.5
Figure 13. Theplastic strain distributions along the interface at the end of 3rd loading cycle,
comparing plasticity models and COF: tangential strain and shear strain distributions for
the case: R~ = 0.1, o'~ = 150 MPa, W = 1350 N , ey = 0 . 0 0 6 5 , and a = 5 1 4 / t m .
Figure 14. Cumulative effective plastic strain distribution in the subsurface region at the
trailing edge at the end of 3re loading cycle for the case: R ~ = 0 . 1 , ~ra=15OMPa,
W = 4 0 5 0 N, and ~z = 1.5, showing influence of material model (a) ~ plasticity and (b)
crystal plasticity.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
200 FRETTING FATIGUE: ADVANCES
1.5 1.5
r~ ~ 0.5
p~0.75
"~o.5 "•/•=0.75
~u
= -0.5
,u=l.5 ~ v
r
[.. -0.5
kt==l.0
-1 .... 1''~'i~'''; '~ , '1 ' ' j ~ ' -1 '''', .... ', . . . . ; .... ~''~',~:
-1.5 -1 -0.5 0 0.5 1 1.5 -1 5 -1 -0.5 0 0.5 1 1.5
Normalized Position (x/a) Normalized (x/a) Position
.= ~,, o.4
"" 0.3 o.3
~ "---" 0.2 a~ " " 0.2
0.1 0.1
0 0
-1.5 -1 -0.5 0 0.5 1 1.5 -1.5 -1 -0.5 0 0.5 1 1.5
Normalized Position (x/a) Normalized Position (x/a)
(c) W = 1350N (d) W = 4050N
Figure 15. Comparison of the distributions of tangential stress (or=) and shear stress
( cr~y) along the interface at the end of 3 rd loading cycle when various COFs are used
with conditions: R~=0.1 and cr.=150MPa (~y=765MPa, a = 5 1 4 f l m for
W = 1350 N , and a = 889 ~m for W = 4050 N ).
The influence of COF is even more significant when considering the distributions of
the strain components as shown in Fig. 16. It is observed that the shear strain (e~y) is
largest for the higher COF (r = 1.5), which is about twice as large than when /~ =1.0 is
used, and the general tendency follows in the same manner as the distributions of stress
components with increasing COF in both loading conditions, W = 1 3 5 0 N and
W ---4050 N (Fig. 15). The decrease in the apparent heterogeneity of the cumulative
plastic strain field for the higher load case may be partially attributed to the narrower
peak in the shear strain along the interface (see Fig. 16 (d)). When the peak is more
distributed as in the lower contact load case (Fig. 16 (c)), the crystal plasticity model
samples a greater number of microstruetural variations leading to multiple stress
concentrations and resulting in greater heterogeneity of the plastic strain field.
The influence of COF in the hysteresis of frictional force versus the applied fatigue
stress (which is proportional to the nominal relative displacement [12]) is shown in Fig. 17.
The hysteresis curves represent near stick, partial slip, or gross slip condition, depending on
the COF. A lower COF manifests gross sliding conditions, whereas a higher COF
promotes partial slip conditions with very little hysteresis. As the COF increases, the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 201
hysteresis curve shifts up and shows some discrepancy with the curve obtained from the
experiments, which does not exhibit this shift. A higher COF yields no gross slip
condltions even in the first cycle and thus it always leads to a positive mean stress (see Fig.
17). However, there are gross sliding conditions during the first few cycles in real contacts,
as shown in the experimental results (Fig. 18(a)). This implies that the COF should evolve
in the simulations to capture this transient effect. When the COF is incremented after each
cycle from 0 to 1.5, the steady-state mean frictional force is better predicted (Fig. 18(b)).
However, there is still some difference between the magnitude of the predicted frictional
force range (AQ) and the experimental results.
~ 2.0 2- ~
~ 15
1.5
C U
'~ 1.0
r~
~
~
~
0.5
0.0
-0.5
•1.0••/.t=/.t=
......... , . . . . . . . . ,
0.75
o5 ~ " -
0
/z:l.O
[,-~ ~--/t=0.75
~2o
: 1.5
,..~,u=I.5 4.0
~ f/z=1.5
1.o .=- 20 /I / 1o
0.5 m 1.0
Figure 16. Comparison of the distributions of tangential strain ( e~) and shear strain
( e~ ) along the interface at the end of 3 ra loading cycle when various COFs are used with
conditions: R ~ = 0 . t and cro=15OMPa (ey=0.0065, a = 5 1 4 k t m for W - 1 3 5 0 N ,
and a = 889 t,tm for W = 4050 N).
Discussion
The prescribed COF plays a key role in the distribution of contact stress and plastic
strain fields, with increasing COF leading to intensification of subsurface plasticity. The
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
202 FRETTINGFATIGUE: ADVANCES
COFs of 1.0 and 1.5 at first glance may seem unreasonably high. However, it is likely
that the local value of COF, defined as q(x) I p(x), may be considerably higher than what
is measured macroscopically, Q/P, which is simply the integral of all the local
interactions, as noted in Eq. (13). The COF is not a given material property since it also
depends on several factors such as the surface interactions and environment. As the local
normal load decreases, q(x)/p(x) may go to the infinite at the edge of contact (or at edge
of asperities when considering rough interfaces) in the ideal case when no plasticity
occurs. Therefore, surface interactions at the microscopic scale play a significant role in
determining the COF under partial slip conditions.
From fretting wear tests on three titanium alloys such as Ti-6A1-4V, Fayeulle et al.
[15] observed that the experimentally measured COF, in the steady state after 10 3 cycles,
was always very high, greater than unity, and the tangential load contributes to plastic
deformation of the substrates and formation of friction ridges. Also, recent work by
Swalla et al. [16] suggests that when prescribing the macroscopic fretting fatigue
conditions under high cycle fretting fatigue conditions, a higher COF has the effect of
accounting for the locally elevated shear stress due to asperity-asperity contacts, albeit in
an average sense. Here, the experimental deformation fields and widths of the stick/slip
regions are better predicted when a higher COF is used. The deformation field is
developed due to the local behavior and not the smeared average behavior collectively
accounting for several asperity-asperity interactions.
Since the nature of the surface interaction between two surfaces is determined by the
real area of contact, shear forces as well as normal forces acting on junctions may play a
significant role in determining the value of COF. The COF is also related to the surface
topography. These mechanisms may result in local stress and plastic strain
concentrations and thus produce a much higher value of COF than that measured in an
average sense. Surface irregularities, such as roughness and waviness, also induce
surface displacement in normal direction resulting in a dynamic normal force that can
further result in fluctuation of local COF, q(x)/p(x) [17].
The interfacial stick-slip process is caused by the fact that the frictional force varies as
a function of displacements, time, or velocity, rather than a constant [18]. Initially, the
COF rapidly increases until reaching a steady-state value in less than 20 cycles in
experiments and partial slip conditions prevail [12]. Based on the overall tangential
traction of the contact, Q, the ratio of Q/P is considerably less than the value of/.t pre~c,bea
with the COF being statically indeterminate within the stick zones. Hence, our method
for estimating the value of COFfor the partial slip case involves comparing
computational crystal plasticity and experimental results. Purely experimental methods
such as progressively increasing the slip amplitude until partial slip gives way to gross
slip over the entire contact are likely no less subject to idealization and perhaps even
moreso since the COF is dependent upon the history of sliding. Therefore, gross slip
measures cannot reflect very well the behavior within the relatively small slip zones
where fretting wear and damage are concentrated in the partial slip case and locally the
pressure at which slip occurs is comparably lower [16]. The frictional force may undergo
significant changes during the early stages of sliding before reaching the steady-state
conditions. Thus, a variable history-dependent COF in the slip and mixed slip-stick
zones may be more appropriate.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 203
1500
~ IOOO p,>l.0 ~ 1
-1000 ,
/
0 100 200 300 400
Applied Stress (MPa)
Figure 17. Comparison of the hysteresis curves of frictional force versus the applied
fatigue stress to the specimen for a constant COF throughout the 3 rd cycle
( R~ = 0.1, or. = 150 MPa, and W = 1350 N ).
(a)
1
400
-400 s
-800
0 50 100 150 200 250 300 350
Applied Stress (MPa)
(b) 1000
~ 500
V a r i a b ~
,-~ 0
Figure 18. Comparison of frictional force versus the applied fatigue stress to the
specimen: (a) the experimental results obtained from first 20 cycles [121 and (b) the
hysteresis curves obtained from FE analysis using a variable COF with cycles
( R~, = 0.1, o-, = 150 MPa, and W = 1350 N ).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
204 FRETTINGFATIGUE: ADVANCES
Concluding Remarks
Acknowledgments
This work is supported under AFOSR Grant No. F49620-01-1-0034, Length Scale
Considerations in the Formation of Attachment Fatigue Cracks. The grant is jointly
funded by the Metallic Materials program (Dr. Craig Hartley, program manager) and the
Structural Mechanics program (Dr. Dan Segalman, program manager).
References
[1] ABAQUS, version 5.8, tlibbitt, Karlsson and Sorensen, Inc., Pawtucket, RI, 1998.
[2] Matin, E.B., "A Critical Study of Finite Strain Porous Inelasticity," Ph.D Thesis,
Georgia Institute of Technology, Atlanta, GA, 1994.
[3] Marin, E.B. and McDowell, D.L., "A Semi-Implicit Integration Scheme for Rate-
Dependent and Rate-Independent Plasticity," Computers and Structures, Vol. 63,
No. 3, 1997, pp. 579-600.
[4] Bennett, V., "A Study of Microscale Phenomena in Small Crack Propagation under
Multiaxial Fatigue," Ph.D. Thesis, Georgia Institute of Technology, Atlanta, GA,
1999.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
GOH ET AL. ON NONHOMOGENEOUS MATERIAL 205
[5] McGinty, R.D. and McDowell, D.L., "Multiscale Polycrystal Plasticity," Journal of
Engineering Materials and Technology, 1999, Vol. 121, pp. 203-209.
[6] Cuitifio, A.M. and Ortiz, M., "Computational Modeling of Single Crystals," Modeling
and Simulation in Materials Science and Engineering, 1992, Vol. 1, pp. 225-263.
[7] Eylon, D, "Summary of the Available Information on the Processing of the Ti-6A1-4V
HCF/LCF Program Plates," University of Dayton, Dayton, OH, 1998.
[8] Russo, R.A. and Seagle, S.R., "Deformation and Recrystallization of Titaniumand Its
Alloys," ASM International, Course 27, Lesson, Test 5, 1994.
[9] Goh, C.-H., Wallace, J.M., Neu, R.W., and McDowell, D.L., "Computational Crystal
Plasticity Applied to Attachment Fatigue Problems, , 'proc. 5th National Turbine
Engine High Cycle Fatigue Conference (HCF '00), Chandler, Arizona, 7-9 March
2000.
[10] Goh, C.-H., Neu, R.W., and McDowell, D.L., "Shakedown, Ratchetting, and
Reversed Cyclic Plasticity in Fretting Fatigue of Ti-6A1-4V based on Polycrystal
Plasticity Simulations,"proc. 6th National Turbine Engine High Cycle Fatigue
Conference (HCF '01), Jacksonville, Florida, 5-8 March 2001.
[11] Nakazawa, K., Sumita, M., and Maruyama, N., "Effect of Contact Pressure on
Fretting Fatigue of High Strength Steel and Titanium Alloy," ASTM STP 1159,
M. Helmi Attia and R.B. Waterhouse, Eds., 1992, pp. 115-125.
[12] Wallace, J.M. and Neu, R.W., "Fretting Fatigue Crack Nucleation m Ti-6A1-4V,"
Fatigue and Fracture of Engineering Materials and Structures, submitted for
review, 2001.
[13] Gob, C.-H., Wallace, J.M., Neu, R.W., and McDowell, D.L., "Polycrystal Plasticity
Simulations of Fretting Fatigue," International Journal of Fatigue, in press.
[14] Hills, D.A. and Nowell, D., Mechanics of Fretting Fatigue, Kluwer Academic
Publishers, Dordrecht, 1994.
[15] Fayeulle S., Blanchard P., and Vincent L., "Fretting Behavior of Titanium Alloys,"
Tribology, Transactions, 1993, Vol. 36, No. 2, pp 267-275.
[16] Swalla, D.R. and Neu, R.W., "Influence of Coefficient of Friction on Fretting
Fatigue Crack Nucleation Prediction," Tribology International, in press.
[17] Yoon, E.-S., Kong, H.S., Kwon, O.-K., and Oh, J.-E., "Evaluation of Frictional
Characteristics for a Pin-On-Disk Apparatus with Different Dynamic
Parameters," Wear, Vol. 203-204, 1997, pp 341-349.
[18] Williams, J.A., Engineering Tribology, Oxford University Press, Oxford, 1994.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Marie-Christine Dubourg t
Nomenclature
a Contact half-width
c Radius of the stick zone
f , f~, J~ Coefficient of friction, static (partial slip condition) and dynamic (gross slip
condition) values of the coefficient of friction
P, Q Normal and tangential loads
R Radius of the sphere
x Abscissa at the contact surface, x = 0 corresponds to contact center
z sample depth
a Angle of the initiation plane with respect to the surface contact, i.e, Stage I
propagation plane
tResearch scientist, Laboratoire de Mrcanique des Contacts UMR CNRS 5514, INSA de
Lyon, Bgt. J. D'Alembert, 20 Av. A. Einstein, 69621 ViUeurbanne Crdex, France.
206
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
DUBOURG ON LOCAL FRETTING REGIME INFLUENCES 207
Introduction
Figure 1- A Running Condition Fretting Map (RCFM) and its associated Material
Response Fretting Map (MRFM). Here PSR= Partial Slip Regime characterized
by quasi-closed Q-fi loops, MFR= Mixed Fretting Regime characterized by quasi-
closed, parallelepipedie and elliptic Q-6 loops and GSR= Gross Slip Regime
characterized by parallelepipedie Q-r loops [3].
The mapping concept proposed by Vincent et al [3] is based on two sets of fretting maps.
These maps describe on the one hand the local fretting regime i.e Running Condition
Fretting Maps (RCFM), with corresponding contact kinematics (adhesion, partial slip,
gross slip) while on the other hand is the main initial fretting damage i.e. Material
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
208 FRETTINGFATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
DUBOURG ON LOCAL FRETTING REGIME INFLUENCES 209
Tests Results
These results have been presented elsewhere [ 5] and are only briefly recalled here.
Multiple cracks initiate in the annulus microsliding zone of the contact area (See Figure
2) and these are symmetrical about the centerline x = 0. Two main cracks develop from
this network while most of the other cracks self arrest. At the contacting surface, cracks
propagate along a semi-elliptical trajectory further below the surface, while their growth
occurs along two distinct macroscopic directions during, respectively, Stage I and Stage
II. The transition between these two propagation Stages is revealed by crack branching
along the Stage II propagation direction. Two types of crack are observed during Stage
I.
Figure 2 - Sphere -plane configuration, Top view at z=O and section in the meridian
plane y = O .
9 Type I cracks grow initially at a shallow angle to the specimen surface with a
propagation direction ranging from 15 ~ to 35 ~ to the surface. These cracks mainly
occur in the middle of the annulus sliding zone.
9 Type II cracks grow along a direction approximately perpendicular to the surface with
a direction ranging from 75 ~ to 90 ~ to the surface. They appear near the edge of the
contact area in the annulus sliding zone, inside and/or outside the contact patch.
Finally, it was observed that, for both crack types, the nearer to the contact center they
initiate, the shallower to the surface is their initial growth direction. Then, during Stage II,
both types of crack propagate along a direction of approximately 65 ~ to the surface. The
branching depth corresponds roughly to a maximum crack length of 160 p.m.
The contact problem between the contacting surfaces is solved, using Coulomb's Law,
as a unilateral contact problem with friction. An incremental description of the loading is
used to account for hysteresis phenomena. The subsurface stress field is calculated within
a zone close to the contact surface. This stress field is multiaxial, non-proportional, and
exhibits very sharp gradients [ 8]. Fatigue crack initiation during Stage I and early
propagation up to the Stage I- Stage II transition have been analyzed as a continuum
mechanics problem. The range of shear and tensile stresses have been computed for all
material locations within the sliding zone during the cyclic fretting loading for all possible
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
210 FRETTINGFATIGUE: ADVANCES
plane directions. Average stresses are used [ 6], calculated along planes of length
L=20gm. The existence of macroscopic cracks [ 9] and their influence on the stress and
strain fields is accounted for in the analysis of the fatigue crack process during Stage II
growth.
Some observations on Stage I:
9 A type I crack is a shear mode fatigue crack. Two specific parameters have been
proposed to predict both the initiation site and a single growth direction. The growth
occurs macroscopically in the direction given by an angle c~along which the value of the
shear driving force, i.e the amplitude of the average shear stress, ~m is maximum ~,~m=
AZm,maxand such that the average value g, of the average tensile stress perpendicular to
that direction, ~m (~a=0.5*(Cm,m~ + ~. . . . . )) is minimum (an absolute value of 40 MPa is
considered here for this minimum). The corresponding crack initiation domain is the
zone where both conditions are fulfilled, being assumed that the risk is the highest
where ~a is zero.
9 A type II crack is a tensile mode fatigue crack. The propagation driving force is assumed
to be the maximum amplitude of crack opening. The crack extension angle ~x is
therefore defined by the direction along which the effective amplitude of the average
stress normal to crack trajectory Aorta* is maximum, Affm*=A~m*,max.Furthermore the
amplitude of the average shear stress tends to a minimum value along that direction. A
Type II crack location is therefore near the edge of the contact area, inside or just
outside, where a high level of tensile stress occurs. The angle ct thus ranges from 90 ~
(outside the contact patch) to 70 ~ (inside the contact zone).
The conditions governing crack branching from Stage I to Stage II are identified. Both
initial crack types (I and II) branch as a consequence of:
9 the decrease of the Stage I propagation driving force, gradually leading to a mixed I+II
mode, (Note that, crack locking effects gradually hinder type I crack propagation)
9 at the same time, the effective amplitude of the tensile stress increases perpendicular to
the plane that is 65 ~ to the contact surface, where the shear mode driving force is at a
minimum.
Hence, branching and initial propagation during Stage II are governed by the maximum
amplitude of the crack opening and not by its maximum value.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
DUBOURG ON LOCAL FRETTING REGIME INFLUENCES 211
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
212 FRETTING FATIGUE: ADVANCES
9 for type I cracks, the greater the slip zone within the contact area, the larger the
potential zone for crack initiation. This leads to an increase in the number of cracks
that may initiate and a greater variety of crack inclinations. The risks of cracking are
linked to the shear stress amplitude which in turn is dependent on the friction
coefficient,
9 for type II cracks, the initiation process is controlled either by a tensile-compressive or
a tensile fatigue mechanism. Since the normal load and the bulk stress are kept
constant, then the variations of the propagation driving force .are only induced by the
variations of the tangential tractions. The fatigue limit is equal to 230 MPa for R =
O'mm/(Ymax = 0.1. It is clear that each material point within the sliding zone is subjected
to a different maximum tensile stress amplitude and a different mean tensile stress.
There are no fretting fatigue data available for these pairs. Only qualitative or rough
estimations of the risks of cracking can be predicted. Nevertheless the stresses are the
highest in the zone close to the contact boundary.
9 The growth direction is nearly unchanged, except that, for a high friction coefficient,
cracks are more inclined towards the specimen surface,
9 For a given risk of initiation, as quantified by the maximum shear and the effective
tensile stress amplitude, the damage occurring at the contacting surfaces depends on
the "contact dynamics" and their effect in trapping the wear particles generated from
crack coalescence. This efficiency is, among other things, linked to the amplitude of
the relative displacement A8 between the contacting bodies. From a certain relative
displacement amplitudeAS, here around 35 pm, a ridge is observed at the contact edge
and favors particle entrapment inside the contact. Furthermore, the initiation sites and
initial growth directions may be different to those predicted without accounted for the
presence of this ridge.
The ridge that forms at the contact boundary is subjected during the contact life to a
continuous development in its mechanical properties and its geometry. We are interested
in its influence on contact parameters i.e., contact pressure, tangential tractions and
contact patch dimensions, which govern, in turn, the internal stresses and finally the crack
initiation process.
A ridge is considered as an asperity and its mechanical properties are assumed to be
the same as those of the specimens. Its dimensions are indicated in Fig. 4, and correspond
to experimental observations. In the analysis PSR(2) conditions are simulated with and
without this ridge.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
DUBOURG ON LOCAL FRETTING REGIME INFLUENCES 213
The normal and tangential tractions are indicated in Fig. 5. The variations of the specific
parameters for the (smooth = no ridge) and (with a ridge) cases for type I and II cracks are
presented respectively in Figs 6 and 8.
In the smooth case, Po, the maximum hertzian pressure and 2a, the contact width are
respectively 150 MPa and 3.57 mm. The presence of the ridge (i) induces a sharp peak of
pressure reaching 236 MPa, (ii) shifts the left contact edge from x=-1.785 mm to x=-
1.665 mm and (iii) reduces slightly the contact area to 3.5 mm.
The stress state at the near surface is strongly influenced by the ridge which induces
localized stress concentrations. This has the following consequences for:
9 type I shear cracks:
a considerable increase in A'Cm,max is obtained at x=-1.78 mm, i.e from 296 to 573 MPa,
see Figs 6(a) and 6(b), while a decrease is observed for points situated inside the contact
area; for instance at x=-1.60 mm, from 324 to 278 MPa. Looking at the crack nucleation
sites, it appears that the condition (~a close to zero is satisfied at two different locations,
x = -1.78 mm and x = -1.60 ram, while in the smooth case only the latter point was
obtained. Furthermore, AZm,max has increased by a factor of nearly 2. This large increase
may accelerate the crack initiation process and increases the risks. Isovalues of "rma~are
shown in Fig. 7 for one load step, at Q = 420 N/ram. A confined plastic zone appears
behind the ridge which will enhance fretting crack nucleation. It can be seen that in front
of and immediately beneath this zone xm~ decreases very rapidly. At x = -1.78ram, the
initial crack propagation direction is equal to 35 ~ while in the smooth case it is about 3 I-
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
214 FRETTINGFATIGUE: ADVANCES
32 ~ The ridge thus influences the crack direction during Stage I, leading to shallower
cracks.
Figure 6 - Variations in or, Arm,max, era over part of the relative sliding zone for a Shear
crack.
Figure 7 - Isovalues o f Arm at Q = 420 N/mm near the contact edge showing the influence
o f the ridge.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
DUBOURG ON LOCAL FRETTING REGIME INFLUENCES 215
90~ *a | DR
li| tZom,min * a
85! ~ ' - 500 --0.1 7 9o
600
i OoO0
-0.2 400
-0.3
200
0
-0.4 -200
80
70
; . . . . . . . . . . . . . . . . . . . - - (YD
-400
65 200 -0.5 60
-1.8 -1.6 -1.4 -1.2 -1.0 -0.8 -[8 -1.6 -1A -12 -1.0
x (mm) x (mm)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
216 FRETTINGFATIGUE: ADVANCES
z (pm)
0
100
200
4OO
Figure 9 shows Um,mm, Urn,max and A'~m variations versus depth at x = -1.78 ram, along
c~=35~ which is the initial growth direction for the tensile crack. Values of A'cm and Urn,max
decrease very rapidly through a zone of depth 50 ~tm, close to the contact surface, the
former being divided by nearly a factor 2 and the latter by more than a factor 2. Then
from a depth of 100 ~tm, they decrease very slowly and u . . . . does not become negative.
It is thus not possible to define a Zm,xvalue as previously. However it is clear that the
relative sliding along the crack faces are rapidly limited due to the strong reduction in
both A'Cmand the tensile stress.
x = -1.78 mm
..................................- ~ -'~-............
Ranges of tensile and shear stresses are computed at the crack tip situated at varying
depths from z = 21 ~tm to z = 99 ~tm along the initial crack growth direction c~=35~ (see
Fig. 10) for all possible branching directions 13. Figure 1 l(a) shows the values of u . . . . .
and Ur~,m~xversus 13. The value of Aura *,max is obtained for 13 ranging from 75 ~ to 80 ~
Figure 11 (b) presents Ax. . . . variations along the direction defined by [3. It should be
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
DUBOURG ON LOCAL FRETTING REGIME INFLUENCES 217
noted that the Stage I/Stage II transition zone is likely to be bounded between 50 and 70
/.tm.
MPa 4- z=21 gm
9 z = 51/am 20-
400 - <> z = 6 9 ~tm
[] z = 9 9 um
- - (~rll,max
200 9 - . . O'lil~mli1
6~
, A~" 80-
(a) Variations of cr. . . . . and (~. . . . . versus [3 (b) Variations of Ax. . . . . versus
for different depths depth along 13
Figure 11 - Stress state variations at x=-t.78 ram for a shear crack inetined initially at
a = 35~ the PSR(2) condition and showing the effect of a ridge at the
contact edge
Conclusions
A theoretical model for fretting contact fatigue has been developed. Stage I crack
initiation and Stage I/Stage II transition processes were analyzed through an approach
based on continuum mechanics. The computational predictions were first validated for
the Partial Slip Regime (PSR) with a small displacement amplitude between the
contacting surfaces.
This paper highlights the influence of the local fretting regime on the crack initiation and
early growth processes. The effects of the displacement amplitudes between the
contacting surfaces and of a ridge are analyzed. On the basis of the results presented, the
following conclusions can be made:
* The displacement amplitude A6 between the contacting surfaces, is a key parameter,
9 the greater the value of Ar, the larger the fretting crack initiation zone giving an
increase in the density of secondary cracks which favors crack coalescence and
particle detachment,
9 particle expulsion or trapping is dependant on A6 and the contact geometry,
9 the crack direction is nearly independent on AS,
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
218 FRETTINGFATIGUE: ADVANCES
9 For values of A6 greater than about 35 gm, a ridge is formed at the contact edge. In
comparison to a smooth surface tested under similar conditions, localized stress
concentrations are obtained that modify the Stage I crack initiation and Stage I/Stage
II processes. The transition zone is closer to the contact surface and the Stage II
direction of growth is changed;
Short crack growth behavior is thus clearly linked to the contact conditions and the
local fretting regime. The predicted results correlate well with the experimental ones if
the surface evolution is taken into account in the analysis of the fretting fatigue
mechanism. Above a certain displacement amplitude, cracking is no more the dominant
fatigue mechanism and competes with wear processes, which may be a consequence of a
great density of small cracks that coalesce leading to particle detachment and expulsion
from the contact. Pits and scales appear at the contacting surfaces and induce localized
stress concentrations which may accelerate or decelerate the growth of secondary cracks,
which in turn may modify the growth of the predominant cracks situated at the contact
edges.
Acknowledgements
References
[ 3] Vincent L., Berthier Y., Godet M.," Testing Methods in Fretting Fatigue : A Critical
Appraisal", ASTM STP 1159 on "Standardization of Fretting Fatigue Test
Methods and Equipment', American Society for Testing and Materials, West
Conshohocken, PA, 1992, pp. 33-48.
[ 4] Forsyth P.J.E., " A Two-Stage process of fatigue crack growth ", in Symposium. on
Crack propagation, Cranfield, HMSO London, 1971, pp. 76-94.
[ 5] Lamacq V., Dubourg M.-C., Vincent L., " A theoretical model for the prediction of
initial growth angle and sites of fretting fatigue cracks", Tribology International,
Vol. 30, N~ 1997, pp. 391-400.
[ 6] Lamacq V., Dubourg M.-C., " Modeling of initial fatigue crack growth and crack
branching under fretting conditions", Fatigue Engineering Material Structure,
Vol. 22, 1999, pp. 535-542.
[ 7] Dubourg M.-C., Lamacq V., " Stage II crack propagation direction determination
under fretting fatigue loading. A new approach in accordance with experimental
observations", ASTM STP 1367 on "Fretting Fatigue: Current Technology and
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
DUBOURG ON LOCAL FRETTING REGIME INFLUENCES 219
[ 8] Brown M.W., Miller K.J., Femando U .S. Yates J.R., Suker D.K., " Aspects of
Multiaxial fatigue crack propagation", in 'Multiaxial and Fatigue Design" ESIS
Publication 21, Edited by Pineau A., Cailletaud G., and Lindley T.C., Mechanical
Engineering Publications, London, 1996, pp. 317-334.
[ 9] Dubourg M.-C., Godet M., Villechaise B., " Analysis of multiple cracks - Part II :
Results", American Society of Mechanical Engineers, Journal of Tribology, Vol.
114, 1992, pp. 462-468.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Yasuo OchiJ Yohide Kido, 2 Taisuke Akiyama, 2 and Takashi Matsumura I
Reference: Ochi, Y., Kido, Y., Akiyama, T., and Matsumura, T., "Effect of Contact Pad
Geometry on Fretting Fatigue Behavior of High Strength Steel," Fretting Fatigue:
Advances in Basic Understanding and Applications, ASTM STP 1425, Y. Mutoh, S.
Kinyon, and D.W. Hoeppner, Eds., ASTM International, West Conshohocken, PA,
2003.
Abstract: The effect of contact pad geometry on fretting fatigue behavior of high
strength steel was examined by using the clamping double bridge pads system. In order
to investigate the effects of bridge pad shapes, the fretting fatigue tests were carried out
by using four types of bridge pad with different leg height h*. The fretting fatigue
strength decreased with decreasing in the h*. Also, the stick area increased as increasing
of the h*. The contact pressure distribution was measured by strain gauge and calculated
by using a finite element method in order to investigate the effect of the pads leg height
h*. The contact pressure concentrated in the inside on the contact surface where the main
crack initiated. Two-stage tests were carried out in order to investigate the fretting fatigue
damage. The two-stage test was performed to a certain cycles under fretting condition
and then plain tests without fretting as removing the pads were continued.
Keywords: fretting fatigue, contact pad geometry, contact pressure distribution, strain
gauge measurement, FEM analysis, relative slip amplitude, two-stage test, high strength
steel
Introduction
It has been known that the fretting fatigue strength is affected by the shapes of
specimen and contact pad. However, there have been a few studies, which have
investigated the effect systematically. Also, the experimental method and the shapes of
specimen and contact pad have been selected differently by each study. As a result, it is
difficult to compare the data published [1]. Therefore, it is important that the effecting
factors on the fretting fatigue property should be clarified by systematic fretting fatigue
tests with varying testing parameter.
220
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OCHI ET AL. ON CONTACT PAD GEOMETRY 221
In order to elucidate the effect that the fretting fatigue property is affected by the
shapes of specimen and contact pad, it is necessary to consider the contact condition in
detail. A lot of research by using the analytical method was conducted by now. For
example, it is reported that, in case of the plane-to-sphere contact and the
sphere-to-sphere contact, it is widely carried out the analysis using the equation of Hertz
and Mindlin et al. in search of the contact pressure distribution, and that it shows the
good coincidence with the experimental results [2-4]. But, in case of the plane-to-plane
contact, it has been shown that the contact pressure has a partial concentration at the
stress singular point in the outer edge [5-7], or in the outer and the inner edges [8] of the
contact surface. Therefore, it is difficult that the analytical results agree with the
experimental results, and it still needs to examine carefully.
In this paper, in order to investigate the effect of shapes of contact pad that
influenced fretting fatigue behavior, fretting fatigue tests and two-stage test by using the
bridge pad with different leg height were carried out with a high strength steel SNCM439
(Japanese Industrial Standard). And, in order to examine the contact pressure distribution,
the contact stress in the vicinity of eontact surface was measured by using subminiature
5-element strain gauge. Furthermore, a finite element method (FEM) analysis was
conducted to compare with the experimental results.
Material
Nickel chrome molybdenum steel SNCM439 was used as the materials for
specimen and bridge pad in the present study. The steel was quenched and tempered in
the following sequence: heated to 1123K for 6• 103 seconds then oil cooled and heated to
893K for 7.2• seconds then water cooled. Tables 1 and 2 show the chemical
compositions and mechanical properties of the materials, respectively. The shape and
dimensions of specimen and bridge pad are shown in Figs. 1 and 2, respectively. The
contact surfaces of specimen and bridge pad were finished by grinding with a #50
grindstone.
Experimental Procedure
Fretting fatigue tests were carried out by using a servo hydraulic testing machine.
The equipment for generation of fretting is shown in Fig. 3 (a). Fretting was produced by
clamping bridge pads from both sides of specimen under an axial stress amplitude. The
tests were carried out at a frequency of 10 Hz under tension-tension mode with a stress
ratio of 0.05 at room temperature. The contact pressure P was 200 MPa, where the
contact area of two bridge pad legs was 2• mm2 and the normal force was 7,200 N.
During a fretting fatigue test, a relative slip amplitude S was measured by using a clip
gauge. Figure 3(b) shows the measuring device of relative slip amplitude. L shape arm
was clamped to specimen, and a stand was attached in bridge pad, next, a clip gauge was
attached in L shape arm and stand. A frictional force F was measured by using a strain
gauge attached to the underside of the bridge pad, also. Four types of bridge pad (leg
height h*: 0.5, 1.0, 3.0 and 5.0 mm) were used as shown in Fig. 2. In order to investigate
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
222 FRETTINGFATIGUE:ADVANCES
the effect of the fretting fatigue damage due to the difference of h*, a two-stage test was
conducted. The contact stress in the vicinity of contact surface between the bridge pad
and the specimen was measured under the condition for the contact pressure P of 200
MPa. Figure 4 shows the measuring device of contact stress using a subminiature
5-element strain gauge (KFR-120-D19-11-N10C made by KYOWA Electronic
Instnaments Co.). The gauge pitch was 0.5 mm and the distance from the center of gauge
to the contact surface was about 0.5 ram. A specimen with a cross section of rectangle
(6x8 mm z) was used for the measurement for the stress distribution near the contact
surface.
--i" ~ 1 (h*=0.5,1.0,3.0and5.0)
.12
Figure 2-Bridge pad (mm).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OCHI ET AL. ON CONTACT PAD GEOMETRY 223
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
224 FRETTINGFATIGUE: ADVANCES
Analytical Method
In order to calculate the contact stress distribution and the relative slip amplitude, a
finite element method (FEM) was carried out using the program MARC Version K7. The
condition of FEM was elastic analysis. The boundary conditions and the load table are
shown in Fig. 5. The mesh divisions of the FEM model constituted by plain strain
elements are shown in Fig. 6. This mesh division for the leg height h*=l.0 mm was
composed of 3898 elements and 4095 nodes. The Poisson's ratio of SMCM439 steel was
0.28 which was extracted by the reference [9]. The frictional coefficient of 0.5 was
obtained from the experimental results and the preliminary analyses.
S-Ncurves
Figure 7 shows the S-N curves for plain fatigue and fretting fatigue with different
leg heights h*. In the present study, the plain fatigue strength and the fretting fatigue
0 2 4 6 8 113 12 14 16 18
Number of steps
4 Number of steps
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OCHI ET AL. ON CONTACT PAD GEOMETRY 225
strength are defined as the strength at 5x 106 cycles. The fretting fatigue strengths were as
following sequence; h*=0.5 and 1.0 mm for about 110 MPa, h*=3.0 mm for 125 MPa,
h*=5.0 mm for 150 MPa, respectively. The fretting fatigue strength remarkably
decreased in comparing with the plain fatigue strength that was about 400 MPa. That is,
the fretting fatigue strength was only 27 to 37 % of the plain fatigue strength. Difference
in the fretting fatigue strength between the conditions of the h* of 0.5 and 1.0 mm was a
little. While in the range of the h* of 1.0 to 5.0 ram, the fretting fatigue strength
decreased when h* decreased.
Frictional Force
Figure 8 shows the relationship between the frictional force F and the stress
amplitude ~a. The F was in proportion to the ~ra in all leg height h*. Difference in the F
between the conditions of the h* of 0.5 and 1.0 mm was little, while in the range of the
h* of 1.0 to 5.0 ram, the F increased as decreasing of the h*. It is known that the
frictional force F, with decreasing of the fretting fatigue strength due to the acceleration
of crack propagation rate, is the most important factor of the fretting fatigue [10]. Hence,
we consider that the h* affects the fretting fatigue strength. It is thought that F decreased
as increasing of the h* for the variable form of the bridge pad leg considering the effect
of stiffness of bridge pad leg.
Figure 9 shows the relationship between the relative slip amplitude S and the stress
amplitude era. The S increased almost linearly as ~ increased. But the difference in the S
by the variation of the h* was not observed at the identical stress amplitude level, and
each S was varied within the range of several ~tm. From observations of fretted damage
surface, the roughness of wear scars was severe and the slip area on either side of the
fretted area spread with decreasing of the h*. Some studies have shown that the same
500 . . . . . . . . i . . . . . . . . i . . . . . . .
400
P =200 MPa
[] ~ h* =0.5 mm
300 9 h* =1,0 mm
h* =3.0 mm
s [] h* =5.0 mm
200 A OC[3 v Plato fatigue
~](~ ~0 0 ~:~
100!
004 . . . . . . . . i
10 5
, , i i i i 1 ~ 1
10 6
r i , , , , ,
07
Number of cycles to failure N~, cycles
Figure 7-S-N curves.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
226 FRETTING FATIGUE: ADVANCES
phenomenon was caused as a result of an increase in the S [ 11-13]. Assuming that the S is
affected by the h*, the value of the S was calculated by using FEM analysis. The
analytical values in Fig. 9 are lower than the experimental values over the whole stress
amplitude range. One of the reasons for the results was suggested that because the L
shape arm bent by vibration during the fretting fatigue test, the experimental value of the
S was amplified and it was not possible to measure the exact value. The increase in the
analytic values of the S as decreasing of the h* was thought to be due to the deformation
of the bridge pad leg. The distribution of the S on the contact surface calculated by FEM
calculated by FEM is shown in Fig. 10. The stick area (S=O ~m) with the h* of 3.0 and
5.0 mm exists around the center of the contact surface. The range of stick area increased
as increasing of the h*. The results of FEM coincided with the observation results of the
fretted surface on specimen. It is thought that this is due to the effect of stiffness of
bridge pad leg.
3000 I I " I
P =200 MPa /
z~ h * = 0.5 mm
z o h*=l,0mm /~
<> h* = 3.0 mm
u. 2000 rn h* = 5.0 mm . /
,~ 1000
200 400
Stress amplitude a a , MPa
Figure 8-Relationship between frictional force F and stress amplitude ira.
30 , , ,
FEM Exp. /
A h* =0.5 mm
I
E ..... O h * = l . 0 mm
h* =3.0 mm .t=[
2O [ ] h*=5.0 mm
~10 ~ / 71
>,-
20( 400
Stress amplitude ~a ,MPa
Figure 9-Relationship between relative slip range S and stress amplitude ~a.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OCHI ET AL. ON CONTACT PAD GEOMETRY 227
15 , ,
P =200 MPa
E ~a=250 MPa
=. a h* =0.5 mm .~
~ ,.~
/u
O h* =1.0
<> h* =3.0
[] h* =5.0
mm
mm
mm
~
A A ~ "v''r
.,,.,~~
_~
"" .~~oooooOO~176176176176
, i
< ~
oooooOO~176
,,~176176176
_ . ~ " ~
1 2 3
Distance from inner edge if, mm
Figure 1O-Relationship between relative slip range S and distance from inner edge d
Figure 11 shows the results of the contact stress distribution in the position of 0.5
mm depth from the contact surface measured using 5-element strain gauge and calculated
using FEM analysis. In the present experiment, the contact stress on the contact surface
could not be measured because the distance of central position of the strain gauge from
the contact surface was about 0.5 mm as shown in Fig. 4. And the detailed measurements
could not be done, since a gauge pitch was 0.5 mm. In order to evaluate the contact stress,
the influence of the position of the strain gauge should be taken into account. Therefore,
we calculated the contact stress by using FEM analysis in order to compare it with
experimental results. Moreover, it must be considered that the value measured by strain
gauge used for this experiment contains the strain by the deformation of specimen by the
effect of the frictional force F and the stress amplitude ~ra. The contact stress which is
actually measured by the strain gauge was thought to be the value ~" that is calculated
using the following equation (1).
cr = cr + wr x (1)
Namely, the contact stress cr~ should be added the value multiplied the axial stress
Crxby the Poisson's ratio v. Therefore, in this sturdy, the analytic value to compare the
experimental value was defined as the ~ ' .
Fig. 11 (a) and (b) show the relationship between the ~" and distance from inner
edge d for cra=160 MPa, h*=l.0 mm and for ~a=160 MPa, h*=5.0 ram, respectively.
From both figures, at the maximum load of the stress amplitude (~ra ~,ox), the ~"
concentrated inside contact surface and decreased outside where the crack generation
side was found. This phenomenon is thought to be due to the deformation of the bridge
pad leg pushed out toward outside by tuning the elongation of specimen when stress
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
228 FRETTINGFATIGUE: ADVANCES
FEM Exp.
01-- ~ - - 9 az:aa=OMPa! , . I
~-2oo
2-300
~3 -4o0
_sooo , ~
Distance from inner edge d, mm
(b) P =200 MPa, era = 160 MPa, h* =5. 0 mm.
0
FEM Exp.
9 az: aa= 0 MPa I ,
...... O Oz " a a min
.... O O'z: (~amax
~. -100 ii iii
~'-200
.~.f... [] c~
r
-300
-400
-~oo , ~
Distance from inner edged, mm
(c) P =200 MPa, era =250MPa, h* =5. 0 ram.
Figure l l Distribution o f contact stress,
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OCHI ET AL. ON CONTACT PAD GEOMETRY 229
amplitude was loaded. The difference in the analytical results was little, but the
experimental value was higher than analytical value. Especially, at low h*, the effect was
more remarkable. This phenomenon is thought to be originated in the change of the
contact area by the abrasion. At the minimum load of stress amplitude (era re,n), the contact
pressure distribution was about the same as the result at (ra=0 MPa because the stress
ratio was 0.05.
Fig. 11 (c) shows the contact stress distribution for o-a=250 MPa, h*=5.0 ram. At
the cr~max in the higher (r~ level, the ~ ' increased in all the measurement area and the
average contact pressure P increased. Because the ~" contains the axial stress crx,the crz"
increased as increasing of the stress amplitude cr~ by the effect of the crx.At the cr~m~, in
the higher era level, the Crz"was considered to significant increasing as much as the inside
on the contact surface, since the deformation of bridge pad leg became larger as the tra
was higher.
Fig. 12 shows the fretted damage surface observed after the fretting fatigue test for
P=200 MP, cra=160 MPa at N = 6• 103 cycles. Although the Nf~t was low cycles, the wear
damage at both edges of contact surface was severe and these were shaved off owing to
the abrasion. It is thought that because of the change of the contact area by abrasion, the
peak of the actual ~" was generated inside from the peak point of the ~" by FEM.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
230 FRETTING FATIGUE: ADVANCES
10 4 10 s 10 6
Number of fretting cycles N~t ,cycles
Figure 13-Result of the two stage tests.
Conclusions
In order to investigate the effect of shapes of contact pad, the fretting fatigue tests
and two-stage tests by using the bridge pad with different leg height were carried out in
SNCM439 steel. Then, the contact stress distribution in the vicinity of the contact surface
was measured by using a 5-element strain gauge, and the FEM analysis was conducted to
compare with the experimental results.
1. Difference in the fretting fatigue strength between the conditions of leg height h* of
0.5 and 1.0 mm was a little, while in the range of the h* of 1.0 to 5.0 mm, the fretting
fatigue strength decreased as decreasing of the h*.
2. Difference in the frictional force F between the conditions of the h* of 0.5 and 1.0 mm
was a little, while in the range of the h* of 1.0 to 5.0 mm, the F increased as decreasing
of the h*.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OCHI ET AL. ON CONTACT PAD GEOMETRY 231
References
[1] Standard Method of Fretting Fatigue testing, The Japan Society of Mechanical
Engineers, 2002.
[2] Farris, T., Harish, (3., Tieche, C., Sakagami, I:, and Szolwinski, M., "Experimental
Tools for Characterizing Fretting Contacts," International Conference on
Advanced Technology in Experimental Mechanics, 1999, pp. 256-263.
[3] Dominguez, J., "Cyclic variations in friction forces and contact stresses during
fretting Fatigue," Wear, Vol.218, 1998, pp. 43-53.
[4] Zhou, Z., and Vincent, L., "Cracking Induced by Fretting of Aluminium Alloys,"
Transactions of the ASTM, American Society for Testing and Materials, 1997,
pp. 36-42.
[5] Nagata, K., and Fukakura, J., "Effect of Contact Materials on Fretting Fatigue
Strength of 3.5Ni-Cr-Mo-V Rotor Steel and Life-Prediction Method," Trans.
JSME Series A, The Japan Society of Mechanical Engineers,
58-553, 1992, pp. 1561-1568.
[6] Satoh, T., Mutoh, Y., Nishida, T., and Nagata, K., "Effect of Contact Pad Geometry
on Fretting Fatigue Behavior," Trans. JSME Series A, The Japan Society of
Mechanical Engineers, 61-587, 1995, pp. 1492-1499.
[7] Maruyama, N., and Sumita, M., "Fretting Fatigue Strength Analysis of Ti-6A1-4V
in Air," Tetsu-to-Hagane, The Iron and Steel Institute of Japan, Vol.76, 1990,
pp. 262-269.
[9] Tanaka, K., Matsuoka, S., Miyazawa, K., "Combined force characteristic of SNCM8
steel," Trans. JSME Series A, The Japan Society of Mechanical Engineers,
45-391, 1979, pp. 204-210.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
232 FRETTINGFATIGUE: ADVANCES
[10] Mutoh, Y., Nishida, T., and Sakamoto, I., "Effect of Relative Slip Amplitude and
Contact Pressure on Fretting Fatigue Strength," Journal of the Society of
Materials Science, Japan, The Society of Materials Science, Japan, 37-417,
1987, pp. 649-655.
[11] Husheng, G., Haicheng, G., and Huijiu, Z., "Effect of slip amplitude on fretting
fatigue," Wear, Vo1.148, 1991, pp. 15-23.
[12] Ochi, Y., Tateno, B., and Kuroki, T., "Fretting Fatigue Strength Properties of
Pearlitic Balnitic Steels with Medium Carbon Steel Contact Material," Journal
of the Society of Materials Science, Japan, The Society of Materials Science,
Japan, 47-10, 1998, pp. 1065-1070.
[13] Ochi, Y., Hayashi, H., Tateno, B., Ishii, A., and Urashima, C., "Fretting Fatigue
Properties in Rail Steel and Fish Plate Materials (Effects of Contact Pressure
and Relative Slip Amplitude)," Trans. JSME Series A, The Japan Society of
Mechaifical Engineers, 63-607, 1998, pp. 453-458.
[14] Wharton, M., Taylor, D., and Waterhouse, R., "Metallurgical Factors in the
Fretting-Fatigue Behavior of 70/30 Brass and 0.7% Carbon Steel," Wear,
Vol.23, 1973, pp. 251-260.
[15] Satoh, T., Mutoh, Y., and Yada, T., "Effect of Contact Pressure on High
Temperature Fretting Fatigue," Journal of the Society of Materials Science,
Japan, The Society of Materials Science, Japan, 42-472, 1993, pp. 78-84.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LOADING CONDITION AND ENVIRONMENT
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Jeremy Hooper: and Phil E. Irvingz
Reference: Hooper, J. and Irving, P. E., "Fretting Fatigue under Block Loading
Conditions," Fretting Fatigue: Advances in Basic Understanding and Applications, STP
1425, Y. Mutoh, S. E. Kinyon, and D. W. Hoeppner, Eds., ASTM International, West
Conshohocken, PA, 2003.
Abstract: The effect on fretting fatigue life of applying periodic overloads and two-level
block loading has been investigated, and the applicability of Miners damage
accumulation under fretting fatigue loading conditions has been tested. The application of
single 150% overloads at given intervals had a considerable effect on life, with life
extensions on the order of two being observed for overload application intervals of 10z to
104 cycles. Miner's law was unable to predict the life extensions found. Two-level block
loading spectra were applied in which the single overloads were made equivalent to a
high-level loading block consisting of a single cycle. The effect of increasing the number
of overloads in a high-level block was investigated. It was observed that as the proportion
of cycles in the high-level block was increased, the damage accumulation became
dominated by the high-level loading. The effect of lower-level constant amplitude
loading was to extend life and delay the damage process. A hypothesis based on the
contact stress analysis and tangential force hysteresis loops has been proposed and
successfully explains all of the variations in fretting fatigue life observed. Miner's law
cannot be confidently applied for the loading conditions tested.
Keywords: fretting fatigue, block loading, overloads, variable amplitude loading, Miner
Introduction
Almost all laboratory research in fretting fatigue has been carried out under conditions
of constant amplitude loading (CAL). However, real-life loading is invariably variable
amplitude by nature. Real-life complex loading spectra are frequently approximated by
block loading tests in the laboratory. In order to calculate life under block loading
conditions, a damage law such as Miner's rule, given in equation (1), is required.
However, as Miner's law is empirical and based on limited fatigue data, it may not be
accurate for all conditions. This fact was underlined by Troshchenko et al. [1] who found
during an extensive review of the literature, considerable scatter in damage summations.
l Professor, Damage Tolerance Group, School of Industrial and Manufacturing Scxence, Cranfield
Umverslty, Cranfield, MK43 0AL, United Kingdom.
2Professor,Damage Tolerance Group, School of Industrial and Manufacturing Smence, Cranfield
Umversity, Cranfield, MK43 0AL, Umted Kingdom.
235
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
236 FRETTINGFATIGUE: ADVANCES
With this in mind, equation (I) can be re-written as equation (2), where a is the actual
damage sum for the test. I f a is greater than unity then Miner's law gives a conservative
prediction for fretting fatigue life, and ifa is less than unity Miner's law gives a non-
conservative prediction of fretting fatigue life.
ni = 1
i~1 N, (1)
where n, is the number of fatigue cycles of stress amplitude ~ in the ith block and Ni is the
number of cycles at ~ required to induce failure under constant amplitude loading
conditions. s
.~n; = a (2)
_ N i
The first significant paper on variable amplitude loading was that of Gassner [2] in
1963, who found that the strength reduction caused by fretting was less marked under
VAL conditions than under CAL conditions. In a series of investigations into fretting
fatigue under Gaussian-type loading [3, 4, 5], Edwards investigated the effects on fretting
fatigue life of applying two types of VAL spectra; Gaussian random loading (GRL) and
programmed random loading (PRL). The PRL spectrum was similar to the Gaussian
spectrum but with higher peak stresses. It was found that GRL was less damaging than
CAL, and PRL was less damaging still. Thus agreeing with Gassner's findings. In
contradiction, Mutoh et al [6] found that GRL was actually more damaging than CAL,
Van Leeuwen et al [7] carried out one of the first studies into fretting fatigue under a
simplified aero-engine spectrum; namely a low-amplitude, high-frequency "ripple"
superimposed on a main high-amplitude low-frequency crenelated waveform. It was
concluded that the additional ripple accelerated fretting and crack initiation but did not
affect crack propagation. More recently Cortez et al (1999) [8] compared the effect on life
of applying similar spectra, where 500 low-amplitude cycles at 200 Hz were superimposed
onto a high-amplitude crenelated waveform at 1 Hz, with CAL tests at 200 Hz and at 1
Hz. It was found that the VAL fretting fatigue lives fell within the scatter bands of the 200
Hz CAL results and that Miner's rule provided reasonable, but slightly non-conservative,
predictions of VAL fretting fatigue lives. Similar results were found by Szolwinski et al
[9], and Iyer and Mall [10].
Mutoh et al [11] studied the effects of two-level block loading on fretting fatigue and
investigated the accuracy of Miners summations. It was found that when the number of
blocks to failure was high, the linear damage law (LDR) held for fretting fatigue.
However, for a low number of blocks to failure, the damage in the first block seemed to
significantly influence the cumulative damage value and failure. Troshchenko et al [1]
also studied two-level block loading spectra, consisting of greater than ten blocks until
failure for fretting fatigue. It was found that at failure, the damage accumulation on the
high step remained close to unity, irrespective of the loading regime. However, on the low
block step, the damage process was inconsistent with the linear damage rule.
Hooper and Irving [12] investigated the effects of applying single overloads to a CAL
spectrum at a range of cycle intervals. It was found that the fretting fatigue life was highly
dependent upon the overload application interval and overload amplitude, with life
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOOPER AND IRVING ON BLOCK LOADING CONDITIONS 237
increasing by a factor of 2-3 for the application of 150% overloads every 100-10 000
cycles. Linear damage summations under predicted life by up to a factor of 2. Analysis of
the tangential force hysteresis loops showed that a shift in the stick-slip boundaries at the
contact patch took place on overload, and that damage was therefore accumulating at more
than one location, with consequent increase in life. In the present work, these results have
been extended into the two-level block loading regime, and changes in life and accuracy
of Miners rule are further investigated.
Experimental
The experimental configuration is shown in Figure 1 and has been described in detail
previously [12]. The bulk axial load is applied using a 30 kN servo-hydraulic fatigue
machine equipped with digital control allowing variable amplitude spectra to be applied.
All tests were carried out at 5 Hz and at an R-ratio (minimum axial load/maximum axial
load) of 0.1. Overload tests consisted of constant amplitude loading (CAL) with single
150% overloads [12] applied at specified cycle intervals. The overload starts and finishes
at the minimum load of the CAL cycles. In the case of two-level block loading tests, all
blocks have R = 0.1, to allow application of Miner's law by direct comparison with
previous produced CAL stress-life (S-N) data. The normal load P is applied via calibrated
spring-loaded bolts. The value of P was chosen to give a peak Hertzian contact pressure of
160 MPa. The selected combination of contact stress, pad radius and sample alternating
stress resulted in the contact area being in the partial slip regime. Partial slip is the most
damaging slip regime with respect to the specimen life [13].
P
(1) ~ a
,
P
Figure 1 - Test Configuration and Loading Condttions
The specimens, (1) on Figure 1, were machined from A1 2618-T6 forgings and had a
rectangular gauge length, of cross section 12ram x 7mm. The specified ultimate tensile
strength and 0.2% proof strength of the alloy were 430 MPa and 340 MPa, respectively.
The steel fretting contact pads (2) were machined with a cylindrical surface, chosen to
give a contact stress distribution calculable using well-established expressions. Edge
effects and digging-in problems associated with flat and bridge type fretting pads were
thus avoided [14]. A radius of curvature rc = 220 mm was chosen for the fretting pad to
give a contact semi-width greater than the critical size found for similar materials in the
tests ofNowell & Hills [15]. Strain-gauged bridges, (3) on Figure 1, were used to hold the
fretting pads in place. The strain-gauge output was used to monitor the tangential force,
Qt, induced at the contact interface due to friction when stress was applied to the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
238 FRETTING FATIGUE: ADVANCES
specimen. Under sliding conditions, the tangential force equals the frictional force, i.e. the
product of the coefficient of friction and normal force. The tangential force was
monitored throughout each test.
The extent of slip during fatigue was derived by plotting tangential force against
applied bulk axial stress. As sample loading is elastic, load will be directly proportional to
displacement at the contact patch. Plots of tangential force against axial stress will be
equivalent to plotting tangential force against contact patch displacement. The resulting
hysteresis loop shape indicates the slip regime [16]. There are three possible slip regimes
in fretting; stick, partial slip and gross slip. The associated hysteresis loop shapes are
linear, elliptical and parallelepiped, respectively [16]. The width of the loop provides an
indication of partition between slip and stick regions in the partial regime.
A CAL cycle will be defined as an overload of 100% amplitude. In this series of tests,
single overloads of 150% amplitude were applied at intervals. An example overload event
is given in Figure 2. The CAL axial stress amplitude, crcnz,was 60 MPa for all overload
tests, i.e. the stress range is 120 MPa for the CAL cycles. Earlier tests by the authors gave
the fretting life for a CAL test with CrCAL= 60 MPa to be 4.4x105 cycles [12], shown as a
dashed line on Figure 3.
!50 "
'.00
OVAL=60MPa -1. . . . . . . . . . . . . . - ~ - - -
50
00-
50
0
time
Overloads of 150% amplitude were applied at intervals of Ixl05, 2x104, lxl04, 1000,
100, 50, 20, 10 or 5 constant amplitude loading cycles. Figure 3 compares the fretting
fatigue lives for each of these tests. It can be seen that fretting fatigue lives are highly
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOOPER AND IRVING ON BLOCK LOADING CONDITIONS 239
dependent on the frequency of overload application. A maximum life, which is over twice
that of the CAL test, exists when 150% overloads are applied every 1000 cycles. At
overload application intervals of greater than 2x 104 cycles, the fretting fatigue lives tend
towards that of CAL tests. The fretting fatigue lives are considerably lower than under
CAL for tests with overload application intervals of 20 cycles or less, A curve
representing Miner's law predictions is also shown in Figure 3.
1.2E+06
(~CAL = 60MPa
1.0E+06 Po = 160MPa
(~OL = 90MPa
,-,8.0E+05
.~.6.0E+05
__N_ _*_ .......................
9
~4.0E+05
2.0E+05 Y
0.0E+00 i i ~ i i
From Figure 3 it can be seen that Miner's law is only valid for small overload
application intervals (20-100 cycles) and for very large intervals (>105 cycles). For
intermediate intervals Miner's law under estimates life by a factor of approximately 2.
Figure 4 shows a typical elliptical tangential force hysteresis loop for a CAL test at
~cAz= 60 MPa. The form of the loop is characteristic of the partial slip regime. The
tangential force scale has been normalised to allow direct comparison between hysteresis
loops for CAL and overload tests, by setting the Qt,,,,, to zero. The effects on the hysteresis
loop shape of applying single 150% overloads is shown in Figure 5. The subscripts 1 and
2 correspond to the CAL cycles immediately before and after the overload application.
The important parameters are the tangential force range, AQt, and the deviation of CAL
hysteresis loop position from the pre-overload position. From Figure 5 it can be seen that a
shift in the mean tangential force, AQt:n.... value occurs with the application of an
overload. This implies a movement of the stick-slip boundaries in the partial slip contact.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
240 FRETTINGFATIGUE: ADVANCES
The CAL tangential force range, AQt, undergoes negligible change when an overload is
applied.
~CAL= 60MPa / t
P~ i AO~
m
i
,.-, 2
~1.81
1.4 j I / 2~CAL ~.,
U. 1.2 ~ ~'~'---~,. . . . . . . . . . --~ shiftin
| / (. ~ I
O'1 i I
=o.6~1Aq,I ~'.//~, I
m ! ~ "1 ///J" I ~ A O~
~.o. 4 t: I J///c~2 !I OCAL= 60MPa
E 0.2 ~ , ~ i ~ = 9oMP~
ot_~__:_...... j: ~o:~Oo~a
~-0.2 4-7 . . . . . . . . . -, . . . . . . . . . . .
0 50 100 150 200 250
B u l k A x i a l Stress [ M P a ]
Relaxation Tests
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOOPER AND IRVING ON BLOCK LOADING CONDITIONS 241
Tests were carried out applying a 150% overload and monitoring the tangential force
hysteresis loops over the next 2x104 CAL cycles. Figure 5 shows the results of the test for
the application of a 150% overload. The tangential force axis has been normalised to zero
for comparison purposes. The post-overload CAL hysteresis loop moves back towards the
pre-overload CAL hysteresis loop position within approximately 6500 cycles of the 150%
overload application (averaged over three tests) and remained in the original equilibrium
position throughout the remainder of the 2x104 cycles. However, the rate of relaxation is
not linear and the size of return shift over the first 1000 post-overload cycles increases
with increasing overload size.
~ 0.4
i 0.2
~ 0
~-0.2
,~-0.4 r ~ , r 7
0 50 100 150 200 250
Bulk Axial Stress [MPa]
Overloads o f r 0 MPa greater than the CAL range were applied to specimens subjected
to simple non-fretting fatigue. A life reduction of 80% was found for the test with
overloads every lxl03 cycles. This suggests that the increases in life due to applying
overloads at similar frequencies in fretting fatigue tests were due to a contact
phenomenon, and not a material characteristic.
The single overload tests reported in section 3 can be equated to two-level block
loading tests where the higher level block consists of a single cycle. An example of a two-
level block loading spectrum is given schematically in Figure 7. The spectrum consists of
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
242 FRETTINGFATIGUE: ADVANCES
two blocks, of different amplitude and different numbers of cycles, which are repeatedly
applied until failure occurs.
The aim of this series of tests was to observe the effect on fretting fatigue life of
increasing the number of cycles in the higher level block systematically, from 1 cycle to
1000 cycles. The number of cycles NA in the lower level block (era = 60 MPa) was kept
constant at 5000 cycles for all tests. The number of cycles NB in the higher level (orb = 90
MPa) blocks were 1, 10, 100, 250, 500, 750, or 1000 for the relevant test. All blocks had
an applied R-ratio of 0.1. Figure 8 shows the variation in total number of cycles to failure
Nvs. the number of cycles in each high level block N~.
Applied ~N~ ~
I I
stress
o"[MPa]
....... II I
>
time or cycles
9 Expermental results
1.4E+06
~ Miner's Predictions
1.2E+06 4,
,--,
I/} 1.0E+06
_e
0
8.0E+05
6.0E§
"J 4.0E+05
~ra= 60MPa
2.0E+05 Po = 160MPa
GOL= 90MPa
0.0E+00
10 100 10013
High-level Block size, N B [cycles]
It can be seen from Figure 8 that increasing the number of cycles in the high level
block Ne from 1 to 100 cycles does not seem to have an effect on the total number of
cycles to failure. However, there is a marked decrease in the total failure life as NB
increases from 100 to 1000 cycles. The predicted failure lives using CAL S-N data and
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOOPER AND IRVING ON BLOCK LOADING CONDITIONS 243
Miner's law is shown by the grey curve. There is an obvious difference between the
experimental and predicted lives for most of the tests. A comparison between the
experimental results and damage summations for each loading level, a(crA)and a(crB), and
total damage sum, aror, for each of the tests in this series is presented in Table 1.
From the single overload test results, it was observed that applying a single 150%
overload caused a shift in the mean tangential force of the CAL hysteresis loop. These
changes have been previously used by the authors [12] to explain the life increases shown
in Figure 3. The hypothesis proposed is included in the discussion. Therefore it is
important to see how effectively applying repeated overloads to make up the high-level
block affects the tangential force hysteresis loops.
Figure 9 gives a schematic representation of the two-level block loading spectrum, and
will be used to show the variation in tangential force hysteresis loops throughout a test.
Figure 10 (a - e) shows the variation in tangential force throughout the transition from the
low level block to high level block and back to the low level block for test F, where N8 =
500 cycles.
Figure 10a shows a CAL cycle of era = 60 MPa. The resulting hysteresis loop is of
elliptical form and therefore representative of partial slip. Good agreement with Figure 4
can be seen, although the loop in Figure 10(a) is less uniform. The authors believe that this
is likely to be due to the build-up of debris causing damage on the fretting pad surface, as
the measurements were taken after 3.95x105 cycles. Foundation for this view comes from
the fact that the CAL cycle of trA= 60 MPa after the application of the high-level cycles
shows similar non-uniformity.
Figure 10b shows the tangential force hysteresis loop for the transition cycle from the
low-level block to the high level block, i.e. point B to point C on Figure 9. This cycle is
similar to that of the single overload cycle in section 3, but the minimum load at point C is
greater than that at point B, hence the loading cycle and therefore the hysteresis loop are
incomplete.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
244 FRETTINGFATIGUE: ADVANCES
Figure 10c shows the first complete high level CAL cycle of crs= 90 MPa. The
resulting hystersis loop is also elliptical, although the degree of hysteresis is much larger.
This implies that partial slip still results over the contact interface, but the fraction of the
interface undergoing slip is greater, as would be expected.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOOPER AND IRVING ON BLOCK LOADING CONDITIONS 245
/ q.~/
:,
~ e ;>~
O
~<
i
i
~< -2
i i
I
I
L~
+ Lo
i
I
I
i [N~] ~0~ le!lue6uel
i
1
,-r
o~
o
o 2:
o
i
J Oh
I
i
I . . . . o o o
o
<
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
246 FRETTINGFATIGUE: ADVANCES
Figure 10d shows a hysteresis loop representative of any of the other CAL cycles in the
high level loading block. There is no further movement in hysteresis loop position, with
respect to Qt, until the transition back to the low-level block occurs.
The transitional loading cycle from the high-level block to the low-level block, i.e.
point G to point H on Figure 9, and the respective hysteresis loop are over-complete as the
minimum load at point H is lower than that at point G.
Figure 10e shows the first post-overload low-level CAL cycle. A shift in mean
tangential force, compared to the pre-overload cycle, similar to that found in the single
overload tests (Figure 5) is observed. Subsequent cycling at era = 60 MPa sees a general
"relaxation" of the hysteresis loop back to the pre-overload equilibrium position, similar to
Figure 6. A close relationship is therefore observed between the hysteresis loop behaviour
of block loading and single overloads.
Discussion
Fretting fatigue endurance is influenced by the stress distribution within the contact
region. The localised stresses within this region are well-established for the case of a
cylindrical fretting pad in contact with a flat specimen. Applying a normal force to the
cylinder will cause a parabolic pressure distribution at the contact interface, as proposed
by Hertz [17]. Mindlin [18] developed equations for the shear traction distributions arising
in a Hertzian contact. These shear traction distributions were later modified by Nowell and
Hills [15] for a typical fretting fatigue situation, considering the effect of applying a bulk
axial load to the specimen that is not directly applied to the fretting pads. The effect of this
additional load is to cause an eccentricity e of the central stick region, therefore producing
a large slip region at the trailing edge of contact and a small, almost negligible, slip region
at the leading edge of contact. The associated stress peaks at the stick-slip boundaries are
also modified, with a major peak occurring at the trailing edge boundary. Figure 11 shows
a simplified approximation of the shear traction distribution for a fretting fatigue test
operating under partial slip conditions.
Under conditions of CAL, crack initiation invariably occurs at the trailing edge stick-
slip boundary, i.e. at the position of peak contact stress. Therefore it can be assumed that
this localised stress peak is the driving force in the initiation and early propagation of
fretting fatigue cracks. The current authors have previously used this assumption, along
with the changes in tangential force hysteresis loop due to the application of an overload,
to explain the considerable variation in fretting fatigue life with overload application
interval, as shown in Figure 3 [12]. For completeness, the hypothesis will be reproduced
here with the aid of Figure 12, which schematically shows the variation in peak contact
stress position due to the application of an overload.
During the application of an overload of amplitude aB, the size of the stick region
decreases and the eccentricity of the stick region increases [15]. Therefore a smaller stick
region exists, centered closer to the leading edge of contact, as shown in Figure 12(a).
Referring back to the tangential force hysteresis loops for the application of an overload,
Figure 5, it is observed that the overload cycle does not fully complete before the CAL
cycling of era re-starts. As the overload cycle is not closed, it implies that the reverse slip
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOOPER AND IRVING ON BLOCK LOADING CONDITIONS 247
back to the original situation has not fully occurred. Hence, for the application of the post-
overload CAL cycling, the new stick region will be centered over a similar section of the
specimen as for the overload cycle. The eccentricity decreases due to the lower applied
axial stress, so that the CAL stress conditions result but over a different area of the
specimen surface to the pre-overload CAL cycle, as shown in Figure 12(b).
a)
contact configuration K,,...._ I~ P Fretting~ J Sp/p~cimen
> x
0 eCAL n
SLIP STICK ~
e) specimen surface
~
N H
= wear damage
= undamaged
i I
Figure 11 - Contact Region Stress Analysis and Suggested Stick-Slip Regions from [15]
q(x) q(x)
f'Po fPo
/s
it I
t
It t I I
I !
~" X
~-II ~ll P" X
! I
Figure 6 showed that the shift in the CAL hysteresis loop position, due to the
application of the overload, gradually returned to the original pre-overload equilibrium
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
248 FRETTINGFATIGUE: ADVANCES
position during subsequent cycling at erA.For the overload amplitude used in this study,
the number of CAL cycles required for complete return was approximately 6500 cycles.
This implies that the post-overload CAL peak in Figure 12(b) moves over a region of the
specimen surface until it reaches the equilibrium position shown in grey after 6500 cycles.
This movement of the peak stress means that damage will be accumulating at a number of
spatially separated points and the damage at each site will be less than if there were only a
single location. Therefore the number of cycles required for crack initiation and early
propagation of a fretting fatigue crack is increased. This hypothesis has previously been
used to explain all of the points in Figure 3 [12].
Considering the block-loading test results from section 5. From Figures 9 and 10, it can
be seen that the effect on tangential force hysteresis loops of applying a block of overloads
OrBis similar to that of applying a single overload, in that a similar shift in the pre-overload
and post-overload CAL (erA)hysteresis loop position occurs. This implies that the
hypothesis proposed can also be used to explain the effects on life of applying blocks of
various numbers of cycles of overloads. From Figures 10(e) and 10(d) it can be seen that
applying additional overloads in the high-leVel block does not cause any further
movement in the stick-slip boundaries. Instead the tangential force hysteresis loops are
identical for all overload cycles. Implying that the overload block can be assumed to be
under similar conditions to a CAL test of ~rB.Therefore if the number of cycles in the
high-level block are great enough, a crack nucleation process can occur that would
compete with the crack nucleation process of the CAL cycles of erA.Table 2 shows the
individual contributions to the Miner's damage sum from the low-level and high-level
blocks. In all cases, the damage due to the low-level blocks is very high (>unity).
However, this does not account for the movement of the peak stress condition. Therefore
the majority of the low-level cycles that make up the damage sum have a very minor
effect on the actual damage mechanism.
Figure 8 shows that the effect of high-level block size on life can be separated into two
regions. There is a negligible effect on life of increasing the number of cycles in each
individual high-level block from 1 (single overload) to 100. It can be seen from Table 2
that for this range of numbers of high-level cycles NB, the damage sum due to the high-
level loading is negligible, and therefore is not sufficient to create a competing crack
nucleation process. However, when the number of cycles in each high-level block is above
100 cycles, there is an obvious effect Of NB on fretting fatigue life. Increasing the number
of CrBcycles causes life to decrease. This corresponds to an increase in the damage sum
due to the high-level loading blocks, as shown in Table 1. Hence it is fair to assume that as
the proportion of high-level cycles to low-level cycles increases, the damage mechanism is
increasingly due to the high-level cycles because only a fraction of the low-level cycles
occur at any given point on the specimen surface. As the number of cycles in the high-
level block increases above 100, the damage accumulating at the peak stress location
under OrBbecomes increasingly dominant and the total life reduces.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOOPER AND IRVING ON BLOCK LOADING CONDITIONS 249
Conclusions
1. In single overload tests, where 150% overloads are applied at given intervals of CAL
cycles, the interval of overload application has a large effect on fretting fatigue life.
2. Applying 150% overloads every 1 x 102 - 1 x 10 4 cycles causes fretting fatigue life to
increase by a factor of two. Miner's law is unable to predict these life variations.
3. As the number of high-amplitude cycles in a two-level block loading test is increased,
the fretting fatigue life decreases.
4. The damage accumulated during the high-level loading has the largest influence on
fretting fatigue life.
5. A hypothesis has been proposed, based on the shear traction distributions and
tangential force hysteresis loops, that successfully explains the life variations found in
both single overload and block loading tests.
6. Miner's law cannot be confidently applied for the loading conditions tested.
Acknow~dgmen~
The authors would like to thank Dowty Aerospace Propellers and the EPSRC for
jointly funding this research.
References
[1] Troshchenko, V. T., Dragan, V. I., and Semenyuk, S. M., "Fatigue Damage
Accumulation in Aluminium and Titanium Alloys Subjected to Block Program
Loading under Conditions of Stress Concentration and Fretting," International
Journal of Fatigue, Vol. 21, 1999, pp. 271-279.
[2] Gassner, E., "On the Influence of Fretting Corrosion on the Fatigue Life of Notched
Specimens of an AI-Cu-Mg2 Alloy," Fatigue of Aircraft Structure, Pergamon,
1963.
[3] Edwards, P. R. and Ryman, R. J., "Studies in Fretting Fatigue under Variable
Amplitude Loading Conditions," RAE-TR 75132, 1975.
[4] Edwards, P. R. and Cook, R., "Frictional Force Measurements on Fretted Specimens
under Variable Amplitude Loading," RAE-TR 78059, 1978.
[5] Edwards, P. R. and Cook, R., "Fracture Mechanics Predictions of Fretting Fatigue
under Gaussian Random Loading," RAE-TR 78086, 1978.
[6] Mutoh, Y., Tanaka, K. and Kondoh, M., "Fretting Fatigue in SUP9 Spring Steel under
Random Loading," JSME. International Journal - Series I, Vol.32, No.2, 1989, pp.
274-281.
[7] Van Leeuwan, H. P., Nederveen, A., and Ruiter, H., "Fretting Fatigue under Complex
Fatigue Loads," NLR-TR 73015, 1973.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
250 FRETTINGFATIGUE: ADVANCES
[8] Cortez, R., Mall, S. and Calcaterra, J. R., "Investigation of Variable Amplitude
Loading on Fretting Fatigue Behaviour of Ti-6A1-4V," International Journal of
Fatigue, Vol.21, 1999, pp. 709-717.
[9] Szolwinski, M. P., Matlik, J., and Farris, T. N., "Effects of HCF Loading on Fretting
Fatigue Crack Nucleation," International Journal of Fatigue, Vol.21, 1999, pp.
671-677.
[10] Iyer, K. and Mall, S., "Effects of Cyclic Frequency and Contact Pressure on Fretting
Fatigue under Two-Level Block Loading," Fatigue and Fracture of Engineering
Materials and Structures, Vol.23, No.4, 2000, pp. 335-346.
[I1] Mutoh, Y., Tanaka, K., and Kondoh, M., "Fretting Fatigue in JIS $45C Steel under
Two-Step Block Loading, JSME International Journal," Vol. 30, No.261, 1987,
pp. 386-393.
[12] Hooper, J. and Irving, P. E., "Fretting Fatigue under Conditions of Constant and
Variable Amplitude Loading," Proceedings of the International Tribology
Conference- Volume I, Japanese Society of Tribology, Nagasaki, 2000, pp. 419-
424.
[13] Vincent, L., Berthier, Y., Dubourg, M. C., and Godet, M., "Mechanics and Materials
in Fretting, Wear, Vo1.153, 1992, pp. 135.
[15] Nowell, D. and Hills, D. A., "Crack Initiation Criteria in Fretting Fatigue," Wear,
Vo1.136, 1990, pp. 329-343.
[I 6] Zhou, Z. R., Fayeulle, S., and Vincent, L., "Cracking Behaviour of Various
Aluminium Alloys During Fretting Wear," Wear, Vol. 155, 1992, pp. 317-330.
[17] Miscellaneous Papers by H.Hertz, (Ed. Jones & Scott), 1896, McMillan, London.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
John F. Matlik I and Thomas N. Farris 2
251
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
252 FRETTINGFATIGUE:ADVANCES
high-frequency
aeroelastic drivers
and system vibrations.~/
contact ~ . v
surface ......,~l~'jII g~s~-
~(bulk inertial
,ilF ,,ill ,'~
X,~tress) ........
~ ~ blade ~ "\' "" .
rOO~ <: ""
J
Figure 1 - Representative two-dimensional geometry of dovetail notch at turbine
blade root.
Introduction
Fretting and fretting fatigue phenomena arise whenever there exist two
contacting surfaces subjected to a vibration or repeated load. Though fretting
fatigue plagues machinery of all kinds, aircraft components and materials that are
continually driven to the limit of their load capacities for light weight design are of
particular interest to the fretting research community. Specific components
susceptible to fretting fatigue in aircraft include control surface hinge point bearings,
spline connections, pin joints, clamps [1], riveted lap joints [2-~], and of particular
interest to this work, dovetail turbine blade/disk connections (Figure 1) [5]. Fretting
in such turbomachinery components has become a focus of current research [6-8].
Recent estimates hold that possibly one sixth of all damage events associated
with United States Air Force (USAF) engine hardware are in relation to high-cycle
fatigue damage via fretting and galling [9]. When considering the possible aftermath
resulting from high speed turbomachinery and subsequent aircraft engine failure, the
reality of such a threat becomes clear. The blade/disk contact surfaces see a
complex variable amplitude, variable frequency load history during the course of any
given mission. In particular, the interaction between HCF and LCF load spectra has
the potential for significant reduction of aircraft component fatigue lives. Except for
early work [10], research efforts in fretting fatigue have focused almost exclusively on
low frequency (5-20 Hz) with constant amplitude loading waveforms [11]. However,
high-frequency engine vibration and unsteady aerodynamic flow over the blade lead
to complex, multi-axial, cyclic stress fields and sharp stress gradients at the fretting
contact. To successfully characterize the effects of frequency and random load
histories on fretting contact, a well-characterized, robust experimental setup must be
developed.
Both frequency and variable amplitude (or random) loading are considered
mechanical variables involved with the fretting and fretting fatigue processes. This
fact suggests a mechanics based approach to modeling. Such a mechanics based
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIK AND FARRIS ON HIGH-FREQUENCY EXPERIMENTS 253
approach has been proposed and experimentally verified for prediction of fretting
fatigue crack nucleation for a specimen subjected to a constant amplitude, fully
reversed loading history [12, 13]. Limited work has been done for both high
frequency and variable amplitude loading schemes with regard to fretting fatigue,
however.
Published literature has shown that the majority of all fretting fatigue tests
have been carried out with constant amplitude stress cycling. Variable amplitude
investigations have been greatly discouraged due to lack of success from current
cumulative damage schemes particularly with regard multi-axial cumulative damage
laws. Though there has been some success in showing Miner's rule to demonstrate
qualitative agreement with random loading fretting fatigue experiments [1~{, 15],
little confidence has been put in the varying quantitative results.
Waterhouse performed an excellent survey of the fretting fatigue factor
effects [11] in which he observed that little has been done with the frequency factor
in fretting fatigue since the work of Endo and Goto [10, 16]. This work as well as
others [17, 18] showed that the fretting and fretting fatigue strength of the materials
increased as the frequency increased. It was also observed that the coefficient of
friction decreased with an increase in frequency of relative movement [16, 19]
leading to a decrease in fretting wear rate at higher frequencies [18]. These results
suggested that the frequency effect was related to the environment and
corresponding oxidation rate. It was concluded that as the frequency increased less
time was available for chemical oxidation to occur. By effecting oxidation, the
frequency factor influenced the coefficient of friction which in turn effected the
contact stresses, surface wear, and overall fretting fatigue life of the specimen.
Current research has shown a trend toward fretting fatigue investigation at
relative slip frequencies of 200 Hz [15] and 300 Hz [19], more than an order of
magnitude greater than previous research. This frequency shift was motivated by a
growing interest in devising design methodologies capable of avoiding or minimizing
HCF damage arising in gas turbine engine fan, compressor or turbine blade
components.
No formal definition of high cycle fatigue (HCF) has been given except through
its relation to its larger load amplitude, lower frequency counterpart - low cycle
fatigue (LCF). HCF is best defined with regard to turbomachinery because blades
see both LCF load histories resulting from engine spool-up and HCF load histories
due to engine vibrations and unsteady flow over the blades. Historically, only the
higher amplitude LCF loading component was considered without any inclusion of
HCF loading or HCF/LCF interaction effects. However, it has been shown that
HCF loading can in fact produce significant reductions in the LCF life of a
component [8], and the effect becomes more pronounced as the amplitude of the
HCF loading cycle increases.
With a growing need for aircraft safety while pushing both the performance
and service life envelope, the necessary development of a robust damage tolerant
design approach is evident. To achieve this goal, a clear experimental observation
and modeling of currently ambiguous frequency and loading effects on fretting
fatigue is required. It remains to design and implement a cost effective, well
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
254 FRETTING FATIGUE: ADVANCES
Designing the C o n t a c t
To produce the small amplitude, oscillatory, relative tangential motion
associated with fretting contact, any fretting experimental rig must be designed to
generate contact between two bodies via the application of a clamping or normal
load, P, followed by an oscillatory tangential load, Q. The tangential load is
associated with the development of global sliding if Q is greater than the average
coefficient of friction times the normal load (#P) or partial slip if Q < #P. For
meaningful analysis and determination of critical parameters associated with fretting
contact, it is mandatory that a clear understanding of contact tractions and stresses
be monitored continuously throughout the experiment. To allow for a rigorous
analysis of contact pressure, shear traction distribution, and interior stress fields, the
current design adopted a fretting contact geometry similar to that originally devised
by Bramhall and O'Connor [20, 21] and implemented by Hills and Nowell [22]. This
geometry was also chosen because of its successful use with mechanics based life
predictions models [13]. The current design was built around a standard uniaxial
test specimen which was subsequently clamped between two cylindrical pads to
produce the classical Hertzian contact (Figure 2). The pad and specimen geometry
choice allows for many variations in contact geometry to be investigated. Pad
geometry can be machined to cylindrical profiles [22], spherical profiles [23], or any
variation of a nominally fiat pad with rounded edges [23]. The chosen specimen
geometry conforms to currently accepted standards for constant amplitude uniaxial
fatigue test specimens (American Society for Testing Materials E 466-96).
Fretting Test F i x t u r e
A common fretting fixture scheme used in fretting fatigue experimental
investigations can be seen in Figure 3a [13]. Both Figures 3a and 3b illustrate two
contacting cylindrical pads of radius R subjected to a cyclic tangential load of small
enough magnitude (IQI < #P) to achieve a condition of partial slip. In Figure 3a
after applying a normal load to introduce a contact, the oscillatory tangential load
can be generated by applying a cyclic bulk load, AL, to the free end specimen. As
pad moves with the specimen, the spring force resulting from the stiffness of the
fretting chassis resists the motion of the pad and generates an in-phase tangential
force, Q. The disadvantage in implementing this design scheme for high frequency
applications arises from the large amplitude of cyclic bulk load required. One of the
complications associated with high frequency operation is the apparent inverse
relationship between load and frequency.
Previously successful low frequency (5-20 Hz) fretting fatigue test fixtures have
relied on custom fretting fixtures mounted on standard uniaxial servohydraulic
fatigue test frames [13, 22]. Higher frequencies put severe demands on the hydraulic
actuators in these test setups and lead to significantly reduced tangential and bulk
load histories. Significantly increased operational frequency can also compromise the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIK AND FARRIS ON HIGH-FREQUENCY EXPERIMENTS 255
lin
(25.4ram)
T,'n --
1'lo
ii (12.7mm) 19 (50.8mm) ~i
0.75in T
0.25in
3.5in (6.35mm).~ 6.5in (101.6mm) I
(88.9mm i .25in 41.- 165.1mm)
i (61.35mm)
I II
1'
0.25in
r (6.35mm)
i --
1BSiR 1 I in Fretting Pad
(38.1mm) ~25.4mm)
0.5in
(12.7mm)
Fretting Specimen
Figure 2 - Designed fretting fatigue specimen and pad geometry and dimenswns.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
256 FRETTINGFATIGUE: ADVANCES
integrity of the hydraulic seals in the system. These two observations suggest two
areas of design modification: (1) investigate the increased control and frequency
range inherent to electric systems in efforts to realize the order of magnitude
increase in testing frequency, and (2) devise a way to generate comparable tangential
force magnitudes but circumvent the necessary cycling of the large amplitude bulk
load. The second design modification follows necessarily from the first because
electric actuator technology requires significantly lower operational loads than those
characteristic of lower frequency servohydraulic systems.
Figure 3b proposes an alternate fretting fixture configuration which escapes the
necessary cycling of the bulk load for indirect application of Q in Figure 3a by
cyclically loading the fretting pads instead of the specimen. This represents the
inverse configuration of Figure 3a in that the tangential load is directly applied and
the bulk stress indirectly results from the cyclic tangential loading of the contact.
This loading scheme exchanges an increase in magnitude of the cyclic tangential
load with a reduction in magnitude of cyclic bulk load amplitude. By implementing
this fixture style and state-of-the-art piezoelectric technology, a high frequency
fretting fatigue load frame has been designed (Figure 4).
Superstructure
The designed high frequency fretting rig was constructed and mounted on a
custom built n~achine base. Standard vibration dampening feet were used to
minimize vibrational response of the rig during high frequency operation. The
machine base also served as a house for the high voltage amplifier used to power the
piezoelectric actuator, and as a place to mount the hydraulic hand pumps for the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIK AND FARRIS ON HIGH-FREQUENCY EXPERIMENTS 257
I 9~1 Bu..osd,.g
Cylinder
i
~ ad Crunch
i
Self-Alignmen
Fixture -~ I I ~ I I
I I /I! I\ -Spherica'
L o ~ r ~ L - - ~.~'--Washers
Grip " " ~ - ~ ] . . ~ . ~ I I Linear
o r.LI I "F Bearln
I I
Middlef
Base Plate
r ' i ~
r~
I~
I -I
Base Plate
_High Voltage
Piezoelectric
Translator V
Figure 4 - A schematic of the designed high-frequency fretting fatigue load frame and
self-alignment fixture used for axial alignment of the fretting specimen.
bulk stress hydraulic loading cylinder. The fretting test fixture and load train was
built between three 25 mm (1 inch) thick hot rolled steel base plates each separated
by four 25 mm diameter, solid, chrome plated, 440C Stainless Steel shafts (see
Figure 4). The overall height of the rig is approximately 1.83 m (6 feet) from the
ground to the top base plate. The 610x356x25 mm (24x14xl inch) base plate of the
rig was bolted to the 762x610x25 mm (30x24xl inch) Mattison ground stainless steel
top of the machine base. The middle base plate serves as an anchor for the bottom
grip and a support plate to maintain alignment of the linear bearings used in
tangential load transfer from the piezoelectric actuator to the contact surface. The
top base plate is threaded to anchor the bulk loading hydraulic cylinder and allow
for application of an initial tensile bulk stress to the fretting specimen.
Bulk Stress Application
Though the experimental rig generates an oscillating bulk stress via the
cyclically applied tangential load, an initial static bulk load allowed for fretting
fatigue tests at a variety of mean stress levels. The existence of a tensile bulk stress
provided favorable conditions for crack growth and subsequent fracture of the
specimen after crack initiation due to fretting contact. The static bulk stress was
also necessary to provide sufficient gripping force for symmetric
(R-ratio=Qm,JQm~=-l.O) operation. The high frequency rig employed a pair of
22.3 kN (5000 lbs.) capacity wedge grips for specimen placement and bulk loading
application. Due to the wedge-shaped grip faces, the gripping force was directly
proportional to the applied tensile loading and required that the specimen always be
loaded in tension before the tangential load could be applied.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
258 FRETTINGFATIGUE: ADVANCES
To avoid the cost and control issues of a powered hydraulic pump and
double-acting cylinder, the tensile static bulk stress was applied using a 107 kN (12
ton) capacity, single-acting, hollow plunger cylinder and 69 MPa (10,000 psi.)
capacity hydraulic hand pump. Though most single-acting hydraulic cylinders have
applications for only pushing applications, this cylinder was designed to allow the
loading rod to pass through the center of the cylinder making a pulling or tensile
application possible. Bulk load drift was arrested by incorporating a hydraulic check
valve.
As with any axial fatigue load frame, axial alignment of the specimen must be
maintained in order to avoid the development of unwanted stresses due to torsion or
bending. The current rig addresses alignment through the use of a self-aligning
fixture as seen in Figure 4. Recalling that the lower grip is fixed, the upper grip is
threaded into a bolt which passes through a set of spherical washers and out of the
alignment fixture via a tapered 10 degree exit hole. A light machine oil is applied to
the spherical washers of diameter 38 mm (1.5 in.) to allow the mating surfaces of
the washer and alignment fixture surface to slide and the bolt to rotate in all planes.
As a result, the grip is free to rotate + / - 10 degrees and translate + / - 3 mm from
the center of the alignment fixture's through hole. Axial translation of the grip
occurs only with the travel of the bulk loading cylinder. The alignment fixture
adjusts for non-axial load misalignments in the specimen by rotating or translating
the spherical washer surfaces to attain an vrientation which will minimize or
eliminate these non-resisted forces.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIKAND FARRISON HIGH-FREQUENCYEXPERIMENTS 259
~111111111111111111111111111111~
II ./- ~ I I / NormalLoad
Diaphra , ~ ~t I I K~ t-' ~ Washer Load Cell
I/~/ / L~ ': r
r.////////I///I//ll//l//I/I////4
Figure 5 - A schematic of the fretting fatigue fixture for normal and tangential load
application.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
260 FRETTING FATIGUE: ADVANCES
Top View
Normal Load
Pad C r u n c h ~ Through Rod
I . ~' I i --W - I
Piezoelectric IJ'L ] ~ Lower Load Transfer j ,r~7
Stack Actuator~ [ Base Plate :~ :
// ,--':
e,\\\\\\xx\\\\\\\\~ .\\~ .\\\\\\\\\\\\\\\~ '.- i - -_- -_- i - - " 2 _ - - : - i = i - - -_i - = - ;
half of the load train which is threaded into the bulk loading cylinder.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIK AND FARRIS ON HIGH-FREQUENCY EXPERIMENTS 261
operation. The rod alignment is achieved by passing each through a flange mounted
Simplicity bearing from Pacific Bearing. The Simplicity bearing is characterized by
a smooth Frelon surface lining on the inside of the linear bearing. The liner wears off
during operation to serve as its own lubricant and aids in dampening vibration
associated with high frequency operation. The bearings prevent rotation in all axes
of motion and translation in all axes except for the direction of tangential loading.
Loading Sequence
With the outlined specifics of bulk, normal, and tangential load applications
presented, it is now possible to outline the loading sequence of an actual fretting
fatigue test in the following sequence.
1. After the specimen is mounted in the top and bottom grip, the bulk loading
cylinder is used to introduce a static bulk or mean stress into the specimen. Note
that at this point the pads have not been brought into contact and the bulk load at
the top, LT, equals the bulk load at the bottom, LB.
2. The static normal load is applied by tightening the set of nuts on the normal load
through rod to generate the contact.
3. The high frequency tangential load waveform is directly applied as the
piezoelectric stack actuator displaces the pads tangentially along the contact surface.
It is important to note that the oscillatory tangential load leads to different
oscillatory, subsurface, bulk stresses in the specimen above and below the contact.
D a t a Acquisition S y s t e m
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
262 FRETTINGFATIGUE: ADVANCES
Control Issues
Control of the piezoelectric actuator is achieved by oscillating the input voltage
via a Wavetek 2 MHz sweep / function generator. The Wavetek allows for variable
frequency, variable R-ratio tangential loading of the contact. The magnitude of the
applied tangential load can vary from zero to the maximum tangential load
amplitude corresponding to full-scale piezo actuator displacement. However, the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIK AND FARRIS ON HIGH-FREQUENCY EXPERIMENTS 263
Fretting Rig
!
~ o~
=~
Amplifier Waveform Generator
P r e l i m i n a r y E x p e r i m e n t a l Investigations
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
264 FRETTINGFATIGUE: ADVANCES
5% of the load applied during operation at frequencies that did not cause resonances
in the structure. This observed coupling between the normal and tangential load
was assumed negligible in the subsequent analysis. Due to extended duration tests
inherent to high cycle fatigue investigations, load drift also becomes an area of
concern. For two day experiments operated at 100 Hz, a 10% load drift was observed
in the normal load and a 5% drift in the mean bulk load was observed. Any analysis
of the experimental results must address the effects of load drift in the setup.
Experimental Observations
Several preliminary tests were run as a break-in effort for the high-frequency
fretting rig. The remaining efforts of this work are focused on the fretting crack
nucleation observation and prediction in the similar contact of a common aircraft
grade aluminum alloy, 2024-T4. The machined pad and specimen geometries chosen
for this preliminary investigation are the same as those presented in Figure 2.
Before the experiment commences, the measurement of the as-received pad and
specimen contact surface is achieved using a Talysurf surface profilometer. Due to
the intimate relationship between contact geometry and resulting surface tractions
and subsurface stresses, an accurate characterization of the contacting geometry is
mandatory. This also allows for determination of average roughness values (Ra) and
provides a way to compare the fretted and unfretted surfaces through subsequent
surface profiling after the experiment has been performed. Average roughness values
as obtained along the length of the AL 2024-T4 specimen in the contact region
ranged from 0.16 to 0.5 #m.
In each of the preliminary tests presented, the similar material (A1 2024-T4)
contact was subjected to an initial mean stress, 6~ of 110 MPa (16 ksi), a constant
normal load (P), an oscillatory tangential load of constant mean, Qo, and amplitude,
AQ/2, and an oscillatory bulk stress resulting from the applied tangential load. Note
that a different bulk stress history is experienced by the specimen above and below
the contact. The specimen above the contact was subjected to a cyclic bulk stress,
aTo =t=ANTI2, out-of-phase with the applied tangential load, Q. The specimen below
the contact was subjected to a bulk stress, (rBo~: Aa/2, in-phase with the tangential
load. As a result, the bulk stress means and amplitudes reported in Table 1 were
determined from the maximum and minimum tangential loads and specimen cross
sectional area, A, as calculated from the following static equilibrium equations.
A A
Q~o~ = ~ ( o . ~ o ~ - oT~,~) Q~,n = ~ ( o . ~ , ~ - o~o~) (1)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIK AND FARRIS ON HIGH-FREQUENCY EXPERIMENTS 265
Experiments FH04, PH05, and PH19 were stopped prematurely due to amplifier
overheat.
1Specimen failed
2Nucleated cracks observed
duration tests at 100 Hz, the initial (P,) and final (Pf) normal load measurements
have been reported.
The high-frequency, small-scale, oscillatory partial slip experienced by the
contact interface during these tests resulted in the generation of wear scars on each
contacting surface of the AL-2024 specimens and pads used. A representative wear
scar as generated during a preliminary 350 Hz fretting test can be seen in Figure 8.
Of the five preliminary tests run, one resulted in failure of a specimen at 350 Hz
operation. The specimen in experiment PH00 initially failed at the upper edge of
contact after 2.6x106 cycles of loading. A second failure at the lower edge of contact
occurred after the initial fracture to produce the hourglass shaped specimen. A
photograph of the failed specimen can be seen in Figure 9. Note that the cracks
nucleated on all four edges of contact. A close up of the wear scar and twin crack
nucleation site can be seen in Figure 10. The right photograph of Figure 10 shows
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
266 FRETTINGFATIGUE: ADVANCES
the resulting failure with the production of a small hourglass shaped piece bounded
on each side by the fracture surface of each of the four nucleated fretting cracks.
F r e t t i n g Life A n a l y s i s
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIK AND FARRIS ON HIGH-FREQUENCY EXPERIMENTS 267
integral equations were used for solving the subsurface stresses in the following life
analysis.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
268 FRETTING FATIGUE: ADVANCES
computational time as compared with critical plane life methods. The stress
equivalent parameter, a~q, used in this life analysis is defined as:
Fsj [_ ai,3
~aaz~
In the equations above, ci is the equivalent alternating stress, o'max is the maximum
calculated a~, Fsl is the stressed areas for the smooth bar, Fs: is the stressed area
of the test specimen, and Aaeq,~ and Aaeq,1 are the equivalent stresses as obtained
for the actual experiment and the smooth bar, respectively. This allows for the
comparison of the equivalent stress obtained in the experiment to the equivalent
stress in a smooth bar specimen having the same life as that in the experiment.
Szolwinski and Farris have shown some success predicting fretting fatigue
nucleation life by relation to conventional strain-life fatigue data given that a clear
knowledge of the near-surface contact stress field can be maintained [13]. Similarly,
to investigate the ability of the stressed area approach to model fretting fatigue
nucleation life of aluminum, this A1 2024-T351 data was analyzed. Smooth bar A1
2024-T3 fatigue life data from literature (Military Handbook 5G 1994) was used to
select a Walker exponent, w = 0.56, and a smooth bar stressed area, F s l = 161
mm 2. Due to lack of sufficient fretting data for aluminum, the value of the shape
factor, ~, was chosen by iterating until a minimum root mean square error between
the smooth bar equivalent stresses for each experiment and the calculated equivalent
stresses was found. The corresponding ~ was found to be 19. A plot of the
estimated nucleation life against the calculated equivalent stresses for the A1
2024-T351 data can be seen in Figure 11. The predicted value of nucleation life is
plotted as a solid line representing the smooth bar A1 2024-T3 equivalent stress.
Previous work on titanium showed that the same value of the shape factor, ~,
could be used for a range of notches and fretting contacts [24]. Therefore, the shape
factor for the A1 2024-T4, high-frequency tests was chosen to be the same as used in
the previous A1 2024-T351 life analysis (~ = 19). The experimental loading
conditions, subsurface stresses as found from the singular integral equations, and
equivalent stress method were then used to predict the nucleation lives. The
predicted and experimental high-frequency test results are shown in Figure 11 as
squares. Calculated equivalent stress values can be seen explicitly in Table 1. Note
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIK AND FARRIS ON HIGH-FREQUENCY EXPERIMENTS 269
200 ~ , ~ o , e 9
150 t 9
t3 ~ 9 9
that the high-frequency data is for A1 2024-T4 while the conventional fretting
fatigue data is for A1 2024-T351.
Right arrows indicate tests where no cracks were visually observed upon
termination of the experiment as in experiments PH05 and PH19. Experiments
PH00, PH04, and PH07 were test runs in which cracks were observed after the
experiment ended. Here failure is defined as the visual observation of a crack at the
upper or lower edge of contact. Experiment PH00 fractured from a crack initiating
at the top edge of contact followed by a second fracture from a crack initiating at
bottom edge of contact. Note that all crack observations were performed at the
termination of each test. Therefore, there is no observation of when or if the cracks
arrested. The squares in Figure 11 are reflective of the total number of cycles.
The promise of the stress equivalent approach to capture fretting fatigue crack
nucleation behavior as illustrated by Figure 11 and the high frequency experiments
presented here build confidence in this approach as a method for fretting crack
nucleation predictions. Recent successful fretting fatigue life predictions for
titanium [24] and the computational benefits of the stress invariant life models
provide sufficient impetus for further investigation of this approach as a method for
fretting fatigue life modeling.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
270 FRETTING FATIGUE: ADVANCES
Acknowledgments
This research was supported in part by the National Science Foundation
Fellowship for J. F. Matlik.
References
[1] Waterhouse, R. B., Fretting Corrosion, Pergamon Press, Oxford, 1972.
[2] Petiot, C., Vincent, L., Dang Van, K., Maouche, N., Foulquier, J., and Journet, B.,
~'An Analysis of Fretting-Fatigue Failure Combined with Numerical
Calculations to Predict Crack Nucleation/' Wear, 181-183, 1995, pp. 101-111.
[3] Muller, R. P. G., "An Experimental and Analytical Investigation on the Fatigue
Behavior of Fuselage Riveted Lap Joints," 1995.
[4] Szolwinski, M. P., Harish, G., McVeigh, P. A., and Farris, T. N., "Experimental Study
of Fretting Crack Nucleation in Aerospace Alloys with Emphasis on Life
Prediction," In Fretting Fatigue: Current Technology and Practices, ASTM
STP 1367~ D. W. Hoeppner, V. Chandrasekaran, and C. B. Elliott, Eds.,
American Society for Testing and Materials, West Conshohocken, PA, 2000,
pp. 267-281.
[5] Kalb, B. J., "Friction Stresses Between Blade and Disk Dovetail Possible Case of
Numerous Dovetail Problems," In USAF Structural Integrity Conference, 1999.
[6] Ruiz, C., Boddington, P. H. B., and Chen, K. C., "An Investigation of Fatigue and
Fretting in a Dovetail Joint," Experimental Mechanics, 24, 1984, pp. 208-217.
[7] Ruiz, C., Wang, Z. P., and Webb, P. H., "Techniques for the Characterization of
Fretting Fatigue Damage," In Standardization of Fretting Fatigue: Test Methods
and Equipment, ASTM STP 1159, M. H. Attia and R. B. Waterhouse, Eds.,
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MATLIK AND FARRIS ON HIGH-FREQUENCY EXPERIMENTS 271
[8] Szolwinski, M. P., Matlik, J. F., and Farris, T. N., "Effects of HCF Loading on
Fretting Fatigue Crack Nucleation," International Journal of Fatigue, 21, 1999,
pp. 671-677.
[9] Thomson, D., "The National High Cycle Fatigue (HCF) Program," In 3rd National
Turbine Engine High Cycle Fatigue (HCF) Conference, CD-ROM proceedings,
San Antonio, TX, Universal Technology Corp., 1998.
[10]Endo, K. and Goto, H., "Initiation and Propagation of Fretting Fatigue Cracks,"
Wear, 38, 1976, pp. 311-324.
[ll]Waterhouse, It. B., ~Fretting Fatigue," International Materials Reviews, 37, 1992,
pp. 77-96.
[14]Mutoh, Y., Tanaka, K., and Kondoh, M., "Fretting Fatigue in SUP9 Spring Steel
under Random Loading," Japan Society of Mechanical Engineers International
Journal, 32(2), 1989, pp. 274-281.
[15]Cortez, R., Mall, S., and Calcaterra, J. R., ~Investigation of Variable Amplitude
Loading on Fretting Fatigue Behavior of Ti-6A1-4V," International Journal of
Fatigue, 21, 1999, pp. 709-717.
[16]Endo, K., Goto, H., and Nakamura, T., "Effects of Cycle Frequency on Fretting
Fatigue Life of Carbon Steel," Bulletin of the Japan Society of Mechanical
Engineers, 12(54), 1969, pp. 1300-1308.
[17]Iwabuchi, A., Kayaba, T., and Kato, K., "Effect of Atmospheric Pressure on Friction
and Wear of 0.45% C Steel in Fretting~" Wear, 91(3), 1983, pp. 289-305.
[18]Feng, I. M. and Uhlig, H. M., "Fretting Corrosion of Mild Steel in Air and in
Nitrogen," Journal of Applied Mechanics, 21(4), 1954, pp. 395-400.
[19]Hutson, A. L., Nicholas, T., and Goodman, R., "Fretting Fatigue of Ti-6A1-4V Under
Flat-on-Flat Contact," International Journal of Fatigue, 21, 1999, pp. 663-669.
[20]BramhaU, R., Studies in Fretting Fatigue. PhD thesis, Oxford University, 1973.
[21]O'Connor, J. J., "The Role of Elastic Stress Analysis in the Interpretation of Fretting
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
272 FRETTING FATIGUE: ADVANCES
[22]Hills, D. A. and Nowell, D., "The Development of a Fretting Fatigue Experiment with
Well-Defined Characteristics," In Standardization of Fretting Fatigue: Test
Methods and Equipment, ASTM STP 1159, M. H. Attia and P~. B. Waterhouse,
Eds., American Society for Testing and Materials, Philadelphia, PA, 1992,
pp. 69-84.
[23]Fouvry, S., Kapsa, P., and Vincent, L., "A Multiaxial Fatigue Analysis of Fretting
Contact Taking Into Account the Size Effect," In Fretting Fatigue: Current
Technology and Practices, ASTM STP 1367, D. W. Hoeppner,
V. Chandrasekaran, and C. B. Elliott, Eds., American Society for Testing and
Materials, West Conshohocken, PA, 2000, pp. 167-182.
[24]Murthy, H., Farris, T., and Slavik, D., "Fretting Fatigue of Ti-6A1-4V Subjected to
Blade/Disk Contact Loading," In Developments of Fracture Mechanics for the
New Century, 50 th Anniversary of Japanese Society of Material Science , 2001,
pp. 41-48.
[26]Murthy, H., Harish, G., and Farris, T. N., "Efficient Modeling of Fretting of
Blade/Disk Contacts Including Load History Effects," ASME Journal of
Tribology , In-Press.
[28]McVeigh, P. A., Harish, G., Farris, T. N., and Szolwinski, M. P., "Modeling Interracial
Conditions in Nominally Flat Contacts for Application to Fretting Fatigue of
~rbine Engine Components," Int. J. of Fatigue, 21, 1999, pp. 5157-5165.
[31]Hills, D. A. and Nowell, D., "Crack Initiation Criteria in Fretting Fatigue," Wear, 136,
1990, pp. 329-343.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
H. Murthy, 1 P. T. Rajeev, 1 Masaki Okane, 2 and Thomas N. Farris 3
REFERENCE: Murthy, H., Rajeev, P.T., Okane, M., and Farrls, T.M., "Development
of Test Methods for High Temperature Fretting of Turbine Materials Silbjected to
Engine-Type Loading," Fretting Fatigue." Advances in Basic Understanding and
Apphcations, ASTMSTP 1425, Y. Mutoh, S. E. Kinyon, arrd D. W. Hoeppner Eds.,
ASTM International, West Conshohocken, PA, 2003.
Abstract: Two bodies are said to be in fretting contact when they are clamped
together under the action of a normal force and see an oscillatory motion of small
amplitudes at the contact interface due to the effect of shear force and bulk stress.
The contact stresses that drive crack nucleation are very sensitive to the shape of
the contacting surfaces and the coefficient of friction. To have an understanding of
fretting at the contacts in turbine engine components, it is important to simulate
similar temperature, load, and contact conditions in the laboratory and develop
tools to analyze the contact conditions. Efforts made to simulate the temperature
and load conditions typical of engine hardware in a controlled laboratory setting,
similar to that developed previously at room temperature, are described. It is shown
that the temperature in the contact region can be held constant at nominally 600~
Preliminary results are given in terms of loads and measured total lives along with
thoughts on development of a total life model for single crystal materials.
Introduction
TY'V~ho(X )
for points in contact
ho (x) - ~, (x) + ~ (x) - Co - C~x = 0
l""
| x,u
(a) (b)
Figure 1 - Dovetail joint in aircraft engine hardware and the equivalent profile.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MURTHY ET AL. ON TURBINE MATERIALS 275
Inconel 718 disk) or one of them is anisotropic (blade made from single crystal
nickel). In such cases the contact problem is considerably more difficult to solve.
The two-dimensional contact of dissimilar isotropic materials has been analyzed
using a numerical (SIE) method, that solves the governing Singular Integral
Equations (SIE) [5, 6]. The SIE method provides rapid calculation of the large edge
of contact pressure and shear stress present in engine blade/disk type contact and is
significantly faster than FEM while retaining the essential mechanics of fretting
contacts. The fretting contact stress conditions relevant to blade/disk contacts
described above are highly localized. Using these highly localized stresses in life
prediction requires great care. Efforts aimed at developing such tools are described
elsewhere[7].
The temperature at which some of the stages in a gas turbine engine operate is
very high. This high temperature calls for the use of specialized materials like single
crystal nickel (SCN) alloy and IN100 that have special charateristics at high
temperature. Hence, an attempt has been made to characterize the fretting fatigue
behavior of materials experimentally at high operating temperatures (~ 600~ A
new experimental setup has been designed to simulate the high temperature at the
local region of contact that is subjected to fretting loads. A set of igniters are used
to increase the local temperature to 600~ The features of the experiment include a
combination of an efficent cooling mechanism using water and an insulation
mechanism using ceramic blocks and sheets. The charactersitics of the rig, like the
normal load transfer ratio, have been experimentally studied. The rig has been used
to conduct an initial set of experiments using SCN specimens and IN100 pads, and
was found to function well under the operating temperature and load conditions.
For motivation of the development of high temperature fretting fatigue
capability, the paper begins with a brief description of existing room temperature
capabilities. A brief description of life prediction is then given to support the
relevance of laboratory fretting fatigue experiments to gas turbine engine hardware.
A detailed description of the high temperature experiments is given next followed by
results for a preliminary set of high temperature fretting fatigue experiments. The
paper concludes with thoughts on extending existing life prediction capability to the
single crystal materials used in the high temperature experiments.
Experimental Details
Nominally flat fretting pads, with rounded edges, and flat dog-bone specimens
are used to duplicate the local geometry at the blade/disk attachments in engine
hardware. To simulate the loading conditions, the nominally flat pad and the flat
specimen are clamped together to generate a normal load and then subjected to an
oscillatory tangential load. Such a configuration was achieved in the laboratory
using a fretting chassis attached to a standard uniaxial servo-hydraulic testing
machine. In addition to the contact loading, the laboratory experiments apply a
bulk load to the specimen.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
276 FRETTINGFATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MURTHY ET AL. ON TURBINE MATERIALS 277
1
Leaving contact intact I ~1 / ~
run increasing amplitude I ~ ~ ....
waveform R(N) I .....
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
278 FRETTINGFATIGUE: ADVANCES
Cylindrical pads with a pad radius of 178 mm were used in the friction
experiments. When the pad and the specimen are made from similar isotropic
materials an approach outlined in Hills & Nowell [9] is used to determine the slip
zone coefficient of friction, #s, in terms of the average coefficient of friction, #, and
the initial coefficient of friction, ~0 [4]. This formulation [9] is only suitable when the
pressures distribution is given by the Hertzian pressure distribution. In the case of
contact of dissimilar isotropic materials the pressure is not only not Hertzian but
also the solutions for the contact pressure and the shear traction are coupled. Hence,
a closed form relation between #8, p, and #0 cannot be simply deduced.
A numerical method has been devised to obtain ~, in terms of p and #0.
Essentially, #8 is increased in an incremental manner, starting from #0, until the
solution of the sliding contact problem yields the experimentally measured average
coefficient of friction, #. As with the Hills & Nowell approach #8 is taken as constant
in the slip zones, and the coefficient of friction in the stick zones does not change.
Initially, the coefficient of friction is assumed to be constant (= #0) through-out the
contact zone. As the slip zone coefficient of friction increases so does the stick zone
size. In each increment the ends of the stick zone are determined by solving the
partial slip contact problem taking into account the remote tension applied on the
specimen and the material dissimilarity of the pad and the specimen. Keeping track
of the previous increments allows us to determine the distribution of the coefficient
of friction within the contact zone in the current increment, #~(x). Hence, the
sliding contact problem for a given increment can be written as,
o5 + cl = - o2 de (1)
1 t--X
where H(x) is the gap function, p(x) and q(x) are the pressure and the shear
traction respectively, al and a2 are the ends of the contact zone, and the constants
kl and k2 are obtained from the elastic material properties of the two contacting
bodies (described in the next section). Once the sliding contact problem is solved
the average coefficient of friction in a given increment is obtained as,
# = f~7 #~(x)p(x) dx
fa~~p(x) dx (2)
where al and a2 are the ends of the contact zone. The results of the friction
experiments and the numerically calculated #s values are presented in Figure 4(a).
The distribution of the coefficient of friction in the contact zone and the evolution of
the stick zone as the fretting progresses can be seen from Figure 4.
C o n t a c t Stress C a l c u l a t i o n
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MURTHY ET AL. ON TURBINE MATERIALS 279
0.8- 1.0-
- final stick zone
/
0.8 I_ _i
0.6 ~ * o r
,,o..-o
=l.
0.4
I
....
o Average g I
Average I~fit
0.4 ~
9 Slip zone I1 i initial stick
Sip zone I~fit 0.2 zone
0.2' i I
0.0 ! , I , I
0 50000 100000 -2.50 0.00 2.50
N x, mrn
(a) (b)
Figure 4 - (a)Evolution of the average coej~icient of fraction, #, and the slip zone
coej~cient of friction, #s. (b)Distribution of the eoej~cient of friction. As #s
increases from #o to its final value, the stick zone size increases.
H(x) + C l X = 2Uz - l u z Jr Ho (4)
where Ho is a constant and C1 is the rotation term.
It has to be noted that the in-plane shear traction is produced as a result of
friction between the contacting bodies. For a general anisotropic body in-plane
tractions might produce out of plane relative displacements resulting in an out of
plane shear traction in addition to the in-plane shear traction. This effect is
neglected in our analysis, i.e., the out of plane shear traction is assumed to be zero.
By knowing the relationship between the surface displacements and the surface
tractions for an elastic half-space one can express, as shown in Equation 5 the initial
gap and relative slip functions in terms of the unknown contact pressure and shear
traction. Stroh formalism is used to derive the Green's function for an anisotropic
half-space resulting in the following system of coupled singular integral equations.
0
--OxI H(x)S(X)} = - [ a ] { q(x)
%
I- { dt
For isotropic bodies a l l = a2~ = 812 = fl21 = O, oh2 = -a21 = kl, and
811 = f12: = - k 2 where
k. 2(1 - + 2(1 -
- ~ E~ (7)
When both the bodies are made from similar isotropic materials, the fretting
contact problem has been solved very efficiently by Murthy et al [4] using a Fast
Fourier Transform (FFT) based approach. For the case of dissimilar isotropic bodies
a different numerical approach, the details of which are given in Rajeev & Farris [5],
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
280 FRETTINGFATIGUE: ADVANCES
o(t) T
Q'~ A A A,t
.Q-IV V V
|
f,-( 9 a, 61
I~ 2 a, "~
!
t s
'
I
Figure 5 - Schematic of two elastic bodies in partial slip contact, al and a2 denote
the ends of the contact zone and bl and b2 denote the ends of the 8tick zone.
is used to obtain the contact tractions. The pressure and shear are decomposed into
a sigular part and a non-singular part. The orders of singularity of the singular part
are determined using an eigenvalue analysis of the system of Equations 5. Bounded
contact tractions are obtained by iterating for the limits of the contact zone and the
stick zone such that, the constant multipliers of the singular parts are zero', and the
equilibrium conditions are satisfied. In both cases an F F T based approach [4] is
used to obtain the sub-surface stress distributions.
Murthy et.al. [71 discuss the utilization of subsurface stresses obtained from
the above approach to predict the life of specimens used in a well characterized set
of experiments. A crack nucleation parameter, aeq, was used to predict the crack
nucleation life [71 and conventional fracture mechanics based calculations were used
to obtain the propagation lives [10]. The results are presented in the Figure 6. The
consistency of the predictions with the experimental results provides confidence in
the aforementioned approach as a tool for life predictions.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MURTHY ET AL. ON TURBINE MATERIALS 281
600 107
" R e m o t e R == 00.50
,Le m 9 Remote R
A a I = 0.001
m 400 ci = 0.005
g. , 9 &-..,,.
m
"o
t::~=~ 200 - - uniaxial Curve ~ 10s 19' A A
~,o"a ,
9 Ti64-Ti64 "o
9 Ti64-1nco718 "~
a.
410 . . . . . i. . . . . . ll| . . . . |
. . . . . . i'() 4 ' . . . . . "I'()' . . . . . . i'()' ' . . . . . .i'()7 1 4 105 106
i |r""
107
Total Life (N) Experiment (cycles)
(a) (b)
characterize the effect of fretting on the life of these components, experiments have
to be conducted at the operating temperatures of the materials in consideration and
the analysis has to include the effect of anisotropic behavior on the contact stresses.
The existing fretting rig at Purdue University had been designed to operate at
room temperature. The rig was useful in testing the materials like Ti-6A1-4V, Til7,
and Inco718 that are used in components that operate at lower temperatures as
described above. However, advanced alloys like Single Crystal Nickel (SCN), IN100,
etc. that are used in high temperature applications have characteristic properties at
elevated temperature. Therefore, to study the material fretting fatigue
characteristics, the experiments must be conducted at elevated temperatures to
which the material is exposed in the engine environment. To achieve an elevated
temperature of 610~ at the contact region, a new rig was designed as is described
next.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
282 FRETTINGFATIGUE: ADVANCES
webs and the platforms that hold the pads were machined from a single Ti-6A1-4V
block. Further, the pad holder block was not made of two different parts that would
be bolted together with pad in between them, as is done in the room temperature
rig. As the normal load is applied, the pad gets wedged into a tapered groove
(tapered at an angle of 5~) machined in the pad holder block.
The temperature of the local area of contact was increased using a pair of
igniters on either side of the specimen. The igniters draw a current of 4.25 A to
4.75 A at 132 V, and the maximum temperature achieved by the igniter surface is
1550~ The heat transfer from the igniter to the specimen and the pads is through
radiation and convection with air as the medium. The temperature of the specimen
was measured using a K type thermocouple. The voltage output of the
thermocouple was used to control the temperature at the contact using on/off
control. The controller was set up such that the igniter switches off if the
temperature goes up by I~ from the desired temperature and switches on if the
temperature drops by 0.5~ On/off control requires an igniter capable of reaching a
very high temperature in a short period of time to minimize the fluctuations in
temperature. Hence, an igniter which can achieve the maximum temperature from
room temperature in 17secs was chosen. However, there was a fluctuation of =t=5~
when the desired temperature was 610~ The fluctuation may be due to air
currents affecting the convective heat transfer, in addition to on/off type of control.
The influence of air currents were minimized by forming a shield around the zone of
elevated temperature, using ceramic blocks and sheets. Since the fluctuation was less
than 1% of the desired value, it will be neglected in the subsequent modeling efforts.
The surface of the webs and the pad holder block facing the zone of elevated
temperature was covered with ceramic sheets glued using high temperature adhesive,
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MURTHY ET AL. ON TURBINE MATERIALS 283
Figure 9 - Schematic of the experiment conducted to obtain the load transfer ratio.
P'/P was found to be > 92%.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
284 FRETTINGFATIGUE: ADVANCES
Figure 10 - A simple linear model of the rig. (a) Schematic of the rig with specimen
and pad (Figure 2). (b) A simple linear spring model of the setup. The part of the
specimen below contact acts as a spring of stiffness kl and the part above acts as
sp~'ing of stiffness k3. The diaphragms act as springs of stiffness k2.
normal load was applied (Figure 9). The load transfer ratio was found consistently
to be between 92% and 95%. The experiments conducted to obtain the load transfer
ratio also provided insight into techniques for minimizing the moment and rotation
at the contact.
From the above relations and from the equilibrium condition Fo = F + 2Q, the
following relations can be deduced,
Fo ~o
F - 1+2 , O - 2+ ~2. (9)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MURTHY ET AL. ON TURBINE MATERIALS 285
''
1100 I - -:-- - , Expt. 2, e, = 2.8 '~
I....... Expt. 3.e, = Lr I
9 t t* 9 t t
t 9 9 9 9 x
I I I "~ 900
I I I
I I I
I I I 800 I I |
I
I
I
I
I
I
o 9'o 180 270 360
e~, deg.
(a) Co)
Figure 11 - (a) Schematic showzng the material principal axes with respect to the
specimen. (b) Effect of the change in orientation of principal axes with respect to
contact surface on the subsurface stresses.
Equation 9 gives a relation between the applied load, Fo, and the recorded loads, F
and Q, in terms of the stiffnesses of the specimen and the diaphragms, which in turn
are affected by the geometry and the material properties. This provided a valuable
tool to modify the design as described in the subsequent section.
Experimental Procedure
A procedure for setting up the experiment was arrived at based on the
experience with the experiments conducted to estimate the load transfer ratio. This
procedure was arrived at to minimize the moment and the rotation at the contact.
First the pads are pushed into contact with the specimen by pushing the pad holder
and held in place using screw-jacks. The pad holder moves towards the specimen in
a groove in the stiff beam made of steel. The bolts holding the block on to the stiff
beam chassis are tightened and the screw-jacks are removed. The small load applied
at the bottom, using the screw-jacks, creates a moment about the contact. To
relieve this moment, once a small normal load is applied using actuators, the bolts
are loosened and tightened again. Finally, the normal load is applied using the
hydraulic actuators. This causes the pad to get wedged into the groove in the pad
holder. In the process of wedging, the pad moves into the groove. Hence, the webs
now have to bend more while applying the normal load. This leads to a drop in load
transfer ratio. To avoid the problem, once the total normal load is applied and the
pad gets wedged into the grove, the rig is unloaded. The entire process of setting up
the contact is ~epeated again.
Preliminary Experiments
Cylindrical rods (0.2m long, 25.4mm in diameter) cast from SCN were used to
machine the fretting fatigue specimens. The primary principal axis (x0) is possibly
tilted from the cylinder axis (Xl) by a small angle (< 10~ A rectangular cross
section (15mmx9.6mm) oriented at an arbitrary angle about the xt-axis was
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
286 FRETTINGFATIGUE: ADVANCES
machined. Tabs made from WASP alloy were inertia welded to the ends to produce
the specimens. The nominally flat fretting pads were made from IN100. A schematic
of the specimen orientation with respect to the material principal axes is shown in
Figure ll(a). Three preliminary experiments were conducted to understand the
working of the rig and to study the nature of contact between the materials used at
high temperatures. The details of the experiments are listed in Table 1. The first
experiment provided valuable insight into the mechanics of the rig and the
temperature variation at the contact. Based on the behavior of the rig in the first
experiment, changes were made in the alignment procedure. The next two
experiments served the purpose of verifying the working of the rig. Coefficient of
friction was found to be 0.17 - 0.23 for the given contacting materials, due to which
gross sliding (implying Q = #P) was observed during the course of experiments. It
is possible that the relatively large displacements associated with sliding wear
introduced non-linearity into the load transfer relationship. Thus, P could be
smaller than the measured value.
In order to achieve partial slip, representative of engine hardware, the
tangential load has to be decreased such that Q < #P. From Equation 9, Q can be
reduced either by increasing k3 or by reducing k2. Therefore, either the length of the
specimen between the contact and the top grips could be reduced or the area of
cross-section (i.e, the thickness) of the diaphragms could be reduced. The length of
the specimen was reduced due to the ease of modification. This was achieved by
raising the fretting chassis, relative to the specimen, using spacers. By this process,
partial slip conditions were achieved in the subsequent experiments. Q/P ratios of
up to 0.27 were achieved implying that the coefficient of friction could be higher
than what was anticipated from the first few sliding experiments.
The sliding contact between the two materials was analyzed using the SIE
approach [6]. The orientation of the primary axis of the material with respect to the
axis of the specimen was obtained from the manufacturer. However, since the
orientation of the secondary axis with respect to the contacting surface was not
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MURTHY ET AL, ON TURBINE MATERIALS 287
known, SIE analysis was performed for all possible orientations. As can be seen from
Figure ll(b) the effect of orientation of the material principal axes on sub-surface
stresses is significant. Lau~ x-ray diffraction method will be used to determine the
orientation of the material principal axes to facilitate an accurate stress analysis for
each experiment.
Conclusions
[1] Farris, T. N., Szolwinski, M. P., and Harish, G., "Fretting in Aerospace
Structures and Materials," In Fretting Fatigue: Current Technology and
Practices, ASTM STP 1367, D. W. Hoeppner, V. Chandrasekaran, and
C. B. Elliott, Eds., American Society for Testing and Materials, West
Conshohocken, PA, 2000, pp. 523-537.
[2] McVeigh, P. A., Harish, G., Farris, T. N., and Szolwinski, M. P., "Modeling
Interfacial Conditions in Nominally Flat Contacts for Application to
Fretting of Turbine Engine Components," International Journal of
Fatigue, 21, 1999, pp. 157-165.
[3] Murthy, H., Harish, G., and Farris, T. N., "Efficient Modeling of Fretting of
Blade/Disk Contacts Including Load History Effects," ASME Journal of
Tribology , In-Press.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
288 FRETTINGFATIGUE: ADVANCES
[4] Murthy, H., Harish, G., and Farris, T. N., "Influence of Contact Profile on
Fretting Crack Nucleation in a Titanium Alloy," In Collection of
Technical Papers - ~lst AIAA/ASME/ASCE/AHS/ASC Structures,
Structural Dynamics and Materials Conference, vol. 1, AIAA, 2000,
pp. 1326-1333.
[7] Murthy, H., Farris, T. N., and Slavik, D. C., "Fretting Fatigue of Ti-6A1-4V
Subjected to Blade/Disk Contact Loading," Developments in Fracture
Mechanics for the New Century, 50th Anniversary of Japan Society of
Materials Science, 2001, pp. 41-48.
Is] Harish, G., Szolwinski, M. P., Farris, T. N., and Sakagami, T., "Evaluation of
Fretting Stresses Through Full-Field Temperature Measurements," In
Fretting Fatigue: Current Technology and Practices, STP 1367, D. W.
Hoeppner, V. Chandrasekaran, and C. B. Elliott, Eds., American Society
for Testing and Materials, West Conshohocken, PA, 2000, pp. 423-435.
[9] Hills, D. A. and Nowell, D., Mechanics of Fretting Fatigue, Kluwer, 1994.
[10]Golden, P. J., High Cycle Fatigue of Fretting Induced Cracks. PhD thesis,
Purdue University, West Lafayette, 2001.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
TITANIUM ALLOYS
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
David W. Hoeppner, 1 Amy M. H. Taylor, 1and Venkatesan Chandrasekaran 1
1 The authors are, respectively, Professor, research engineer, and research assistant
professor, Department of Mechanical Engineering, University of Utah, 50 S. Central
Campus Dr., Room 2202, Salt Lake City, UT 84112-9208.
291
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM International www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
292 FRETTINGFATIGUE: ADVANCES
is an existence of normal pressure threshold. These aspects will be discussed in the latter
part of this paper. However, under conditions of contact and applied cyclic stresses cracks
form from fretting damages after certain a damage threshold is reached. After this,
elimination of fretting may not have any favorable influence as nucleated cracks
eventually propagate to fatigue failure by cyclic stress alone. As a result fretting shortens
the fatigue life of a structural component. Thus it is imperative to inspect structural
components for fretting damages to eliminate the possibility of these damages becoming
crack nucleation sites.
It is well known that the influence of fretting on the fatigue life of a metal alloy is
dependent on numerous parameters. This paper will discuss some important fretting
fatigue variables such as normal load, surface conditions, environment, and contact
conditions. With the support of experimental studies these effects will be discussed as
related to aerospace components with emphasis on titanium alloys. First, experimental
data with regard to effects of normal pressure on fretting fatigue life of titanium alloys are
given in the following section.
As mentioned before, the basic effect of fretting is to decrease the fatigue life of a
material. One of the parameters that significantly contributes to the reduction in fretting
fatigue life of any metal alloy is the magnitude of the normal pressure that one component
exerts on the other component. This section summarizes experimental studies conducted
to illustrate the effects of normal pressure on the fatigue life of Ti-6A1-4V [1-16]. All
experiments discussed in this section were performed in the laboratories of the principal
author of this paper during the past four decades. Both fatigue specimens and fretting
pads were made using Mill Annealed Ti-6A1-4V. The fretting fatigue experimental
methods are described elsewhere in references 3, 5, and 10. It is important to note that the
results in all fretting fatigue experiments are influenced by experimental conditions a
great deal.
Figure 1 [ 1,2] provides some unpublished Ti-6A1-4V fatigue and fretting fatigue
experimental results generated in the early 1970s by the principal author of this paper.
The reduction in fatigue life of Ti-6A1-4V specimens is evident from this study when they
were subjected to the normal pressure of 20.7 MPa (3 ksi) at different maximum fatigue
stresses. The results from another study also showed that fretting fatigue life was reduced
when tested under the normal pressure of 20.7 MPa (3 ksi) (see Figure 2) [4]. It also was
observed from this study that at higher fatigue stresses the difference between fretting
fatigue life and fatigue life of Ti-6A1-4V is small whereas the difference is large at lower
fatigue stresses. This undoubtedly is due to the relatively high applied cyclic stress at the
shorter lives thus causing the fretting to provide less effect in life reduction. It was stated
that this might be because at lower fatigue stresses the fretting acting in conjunction with
fatigue produces crack(s) in a significantly smaller number of cycles whereas "pure"
fatigue conditions need a larger number of cycles to produce cracks. In another study
[10], the effect of fretting on the fatigue life of Ti-6A1-4V under different normal
pressures was evaluated. As shown in Figure 3, the fatigue life of Ti-6A1-4V was reduced
when the normal pressure was increased and vice versa. The scatter in the data presented
in the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOEPPNER ET AL. ON BEHAVIOR OF TITANIUM ALLOYS 293
. t A,.~lld,mdsHmadl~ok~
r D I r.,,~,~o.o.~t~
I I P~ ~'~" 1
o
0 C ZX 0 ~dm~
1
O
I
|. ,, , ,
1 ~
r,,,, H ~ --
I
0
2
t~
Figure 1: Fatigue and fretting fatigue data for Ti-6AI-4V annealed R = +0.1 (1970-75)
[1, 21.
.Pure Fatigue
1100
965
r.t3 [] [] []
689 D []
Fretting Fatigue
552 Normal Pressure
[] [] [] PN = 20.7 MPa
..~ [] [] [] [] []
(3 Ksi)
414 D
[]
276
MATERIAL:
138 Mill Annealed TI-6A1-4V
R = +0.1, 30 Hz Symbol for specime:
Room Temperature that did not fail.
0 i
'4 5 6 7
1011 10 10 10 10
Cycles to failure, N
Figure 2: Maximum Stress vs. Cycles to Failure for Ti-6Al-4Vfor Baseline Fatigue
and Fretting Fatigue Conditions [4].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
294 FRETTINGFATIGUE: ADVANCES
g. 827 D
r 1 4 9 []m
[] [] 0<> •9
[]
~ 689
O~s~mbol for
552 specimen 9 9 9
.~ 414
a PN = 20.7 MPa (3 ksi) 9 []
48.3
41.4 [] []
R= +0.1
R o o m Temperature
r.~
34.5 30 Hz
27.6
@ Max. fatigue
stress 552 MPa (80 ksi)
20.7 I'V1
6.89
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOEPPNER ET AL. ON BEHAVIOR OF TITANIUM ALLOYS 295
48.3
R -- + 0 . 1
[] []
Room Temperature
41.4
30 Hz
r~ [] []
o 20.7
13.8
O
Z [] O0 0
6.89
0
ii i i i
3 4 '5 6
10 10 10 10
Total cycles to failure, N
Figure 5." Fretting Fatigue Test Results for Ti-6Al-4V (MA) Material at Various
Normal Pressures, [7].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
296 FRETTINGFATIGUE: ADVANCES
These studies show that the variable normal pressure is a major factor in reducing the
fatigue life of Ti-6A1-4V. However, there exists a damage threshold beyond which
eliminating the cause of fretting does not have any effect on the remaining fatigue life of
Ti-6A1-4V [3, 4, 10]. The concept of damage threshold as related to fretting fatigue
behavior of Ti-6A1-4V is discussed in the next section.
82.7
R = +0.1
f=30Hz
68.9 IT1 Room Temperature
[] 7075-T6 @ 138 MPa;
55.2 (20 ksi)
[] [] 7075-T6 @ 345 MPa
41.4 (50 ksi)
r~
9 9 9 9 [] 9
[] [] (110 ksi)
27.6
[]
O
Z []
9 9 9 D9 [2D
13.8
9 mmm 9
9 9149
0
4 5 6
10 I0 10
Total cycles to failure, N
Figure 6: Fretting Fatigue Normal Pressure Threshold for 7075-T6 Aluminum Alloy
and Ti-6AI-4V Titanium Alloy at Various Maximum Fatigue Stress. [101
As mentioned before, fretting produces various damage states on the contact surfaces.
Cracks nucleate from these damage states after only a smaller number of applied cycles.
Experimental studies indicated that at all loading conditions a minimum amount of
fretting damage is needed to cause any reduction in fatigue life whatsoever. Interrupted
fretting fatigue experiments were conducted on Ti-6A1-4V specimens at two different
fatigue stresses; viz., 862 MPa and 483 MPa (125 ksi and 70 ksi) at 20.7 MPa (3 ksi)
normal pressure to observe the existence of the damage threshold. The results from this
study are plotted in Figure 8. As shown, at 100% fretting fatigue life, that is with the
fretting pad in
contact until the test specimen fractures, the cycles to failure was approximately 1.5X10 4.
Fretting damage was assessed by observing the remaining (residual) life after the fretting
pad was removed. Thus, at 60% fretting fatigue cycles, that is when the fretting pad was
removed, the specimen fractured after only 4X104 cycles. This is in fact little more than
the 100% value. In addition, at 20% fretting fatigue cycles it was observed that there was
no reduction in the fatigue life of Ti-6A1-4V as the cycles to failure are the same. This
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOEPPNER ET AL. ON BEHAVIOR OF TITANIUM ALLOYS 297
means that the damage produced under fretting condition does not contribute any fatigue
life reduction. In other words these results suggested that no fretting damage was
produced to cause a reduction in fatigue life at 60 to 0% fretting pre-cycles. Therefore, the
existence of a damage threshold in Ti-6A1-4V helps to alleviate fretting related challenges
only if these damages are removed before they become potential crack nucleation sites.
Once the crack nucleation has occurred from the fretting further exposure to the fretting
has virtually no continual effect on the life.
R =+0.1, f = 6 H z
Laboratory Air
96.5
m
[] Fretting Fatigue
Load,
82.7 1.65/0.165 KN
m
~ Fretting Fatigue
69 Load,
3.30/0.330 KN
O I~
55.2 Symbol for specimen
that &d not fail
41.4 []O
O
Z 27.6 __
13.8
0 --
4 5 6 7
10 10 10 10
Cycles to fmlure, N
Figure 7: Fretting Fatigue Test Resultsfor Ti-6 Al-4V Simulating Hip Prosthesis
Loading Conditions, [13]
Effect of Dissimilar Materials in Contact under Fretting Fatigue Conditions
Titanium alloys are known for their susceptibility to fretting degradation mechanisms
whether they are in contact with themselves or with other metal alloys. To evaluate the
fretting fatigue behavior of Ti-6A1-4V when it is in contact with itself or with other
materials, studies were conducted. In this study fretting pads were made from 7075-T6,
At-1100, Copper, 0.40/0.50 C Steel, and Ti-6A1-4V as well. Ti-6AI-4V fatigue specimens
were fretted with pads of different materials as mentioned above. Figure 9 shows the
fretting fatigue test results resulted from this study [14]. All tests were conducted at room
temperature under 20.7 MPa (3 ksi) normal pressure at different fatigue stresses. As can
be seen from the plot, Ti-6A1-4V in contact with Ti-6A1-4V (4, 7) exhibited
comparatively more reduction in fretting fatigue life. Moreover, as shown in Figure 10, in
general, the harder the fretting pad the larger the reduction in fatigue life of Ti-6A1-4V
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
298 FRETTINGFATIGUE: ADVANCES
under these conditions. This behavior was observed to be same for two different fatigue
stresses as shown.
100 9 []
80
[]
[] Symbol for specimen
[] that did not fail.
60
MATERIAL:
Mill Annealed TI-6A1-4V
ex0 R = +0.1, 30 Hz
4O Room Temperature
[] PN = 20.7 MPa (3 ksi)
20-
[]
0
104 105 10~ 107
Cycles to failure, N
[] Max. 9 Max.
Fatigue Fatigue
Stress Stress
483 MPa 862 MPa
(70 Ksi) (125 Ksi)
Chemical environment is one of the most important parameters that affect the fretting
fatigue behavior of a metal alloy including Ti-6AI-4V. Yet very little work has been
performed to study this issue especially on Ti-6A1-4V. However, to provide some
additional insight to environmental effects on fretting on Ti-6A1-4V this section discusses
some experimental results of the primary author's unpublished work. This study was
performed in different environmental conditions such as laboratory air, distilled water,
3.5% NaC1 under different normal pressure and fatigue stress levels. At both lower and
higher fatigue stress levels fretting fatigue tests in 3.5% NaC1 environment resulted in
greater reduction in fatigue life when compared to other environments (see Figure 11).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOEPPNER ET AL. ON BEHAVIOR OF TITANIUM ALLOYS 299
It is now well known that in applications which involve wear and fretting conditions
titanium alloys cannot be used without any surface treatments as they are known to
exhibit more material transfer. This may be the result of the breakdown in the oxide
protective film and the relatively rapid nucleation of cracks from the fretting damage.
Therefore, some studies were conducted to evaluate surface treatment as a means to
alleviate the reductions of life from fretting induced damage of titanium alloys [11, 16].
In aircraft structural components, especially in the aircraft fuselage and wing structures,
fretting mechanisms are observed to be one of the potential causes which nucleate cracks
from rivet or other fastener holes. In recent years, the solution-treated and aged (STA),
and the beta processed Ti-6A1-4V are extensively used to manufacture critical aircraft
components. 111addition, Boeing Commercial Airplane Company is using extensive
amounts of beta-processed Ti-6AI-4V on the B777.
827 oI *
No
"% 9
Failure of
* ~ in group
""o. Io
%%~
D~
552 *%%
*%
E "'-.D. o "
Freeing pad material
[] 7075-T6
~ 276 0 Al-
l Coppe
<> 0.40/0.50 C Steel Ti-6A1-4V
pad
5 _ _ Jt I i i _ i
0 4 ' ' . . . . 6
10 10 10 I0
Number of c'ycles to failure, n
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
300 FRETTINGFATIGUE: ADVANCES
Fretting corrosion and fretting fatigue are potential problems in maintaining the
structural integrity of aircraft components made using Ti-6A1-4V with aforementioned
processing conditions. It also will be of serious consequence when the fretting fatigue
behavior of Ti-6A1-4V alloy systems under different environments and temperatures is
not characterized. This section discusses some experimental studies that were conducted
to determine the effect of airframe design parameters and coatings on fretting fatigue life
of titanium alloys [16].
100
[] 9 Lab Air, PN = 20.7 MPa, R = +0.1
F = 20 Hz, Room Temperature
40
= 20
,0-.
k~
0
. . . . . . . . i . . . . . . l'l . . . . . . . .
4 5 6 7
10 10 10 10
Number of cycles to failure, n
Figure 10: Harder the Fretting Pad The Larger the Reduction in Fatigue Life
of Ti-6AI-4V [141.
Simulating aircraft structural joint design parameters fretting fatigue tests were
conducted first on uncoated Ti-6A1-6V-2Sn fatigue specimen with fretting pad made of
same material. The fretting pad was fastened to the fatigue specimen using different types
of fasteners, viz. Ti-6A1-4V screw clearance fit, Ti-6A14V taperlok interference fit, and
Ti-6A1-4V Hilok clearance fit. The objective of this study is to evaluate parameters such
as material, fastener type, interference, installation torque, stress level, cyclic loading
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOEPPNER ET AL. ON BEHAVIOR OF TITANIUM ALLOYS 301
frequency, and coatings. Different types of fasteners were selected because they induced
varying amounts of normal pressures at the interface. All experiments were conducted at
laboratory air. Fretting fatigue test results at different fatigue stresses for uncoated Ti-
6A1-6V-2Sn with different fastener types are summarized in Figure 12. From this study it
was concluded that Ti-6A1-4V taper-lok fasteners exhibited better fretting fatigue life
than Ti-6A1-6V-2Sn specimens. Subsequently, titanium alloy specimens made of Ti-6A1-
6V-2Sn, Ti-6A1-2Sn-4Zr-6Mo, and Ti-6A1-4V were coated with Molykote 106 and were
fretting fatigue tested with Ti-6A1-4V taper-lok fasteners.
The work showed that coated Ti-6AI-4V specimens exhibited greater reduction in
fretting fatigue life when compared other titanium alloys. However, additional work
showed that a significant improvement in the fretting fatigue life of coated (with
Molykote 106) Ti-6AI-6V-2Sn occurred when compared to uncoated Ti-6A1-6V-2Sn.
Recent Studies
In recent years other studies have shown similar effects to those discussed [17-26].
The studies reported by Antoniou and Radke [17] are an excellent summary of the current
state of the understanding of fretting fatigue of Ti alloys and validate many of the ideas
discussed earlier in this paper.
~g
[] |
o 7
Specimens
,--t that did not fail.
4 5 6
10 10 10 10
Cycles to failure, n
Figure 11: Fretting Fatigue Results Of Ti-6AI-4V under Different Environment Tested
At Room Temperature, R = +0.1,f=3OHz. [15]
,., Distilled
water,
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
302 FRETTINGFATIGUE: ADVANCES
552 []
m # oll9
414
276
r~3 %ODD g(~ U #
Test conditions []
138 f=30Hz
R= -0.1
laboratory air
-I
3 4 5
10 10 10 10
Cycles to failure, N
FASTENER TYPE
Ti-6A1-4V TaperLok 9 Ti-6A1-4V HiLok, Clearance Fit [] Ti-6AI-4V Screw
Interference Fit Torque 6.78 J, (60 in-lb) Clearance Fit
Torque 13.6 J Torque 7.91 J (70 in-lb)
(120 in-lb)
Figure 12: Fretting Fatigue Test Data for Uncoated Ti-6Al-6V-2Sn Simulating
Aircraft Structural Joint Design Parameters. HiLok and TaperLok are two
Commercial Fastener Types used in Industry [16].
Conclusions
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOEPPNER ET AL. ON BEHAVIOR OF TITANIUM ALLOYS 303
Future Needs
Although some studies were conducted on fretting fatigue behavior of titanium alloys
during the past several years, much more work is to be done in order to understand more
about this complex mechanism. Following are some recommendations to be pursued to
enhance our understanding of fretting fatigue of titanium alloys.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
304 FRETTINGFATIGUE: ADVANCES
References
[1] ASM Handbook, Vol. 18, Friction, Lubrication, and Wear Technology, 1994, 778.
[2] Hoeppner, D.W. "Mechanisms of Fretting Fatigue", Fretting Fatigue, ESIS 18, R.B.
Waterhouse and T.C. Lindley, Eds., Mechanical Engineering Publications,
London, (1994) 3-19.
[3] Hoeppner, D.W. and Goss, G.L., "Research on the Mechanism of Fretting Fatigue,
Corrosion Fatigue: Chemistry, Mechanics, and Microstructure, NACE-2, pp.
617-626, 1971.
[4] Hoeppner, D.W. and Goss, G.L., "A Fretting Fatigue Damage Threshold Concept",
Wear, 27, pp. 61-70, 1974.
[5] Hoeppner, D.W. and Goss, G.L., A New Apparatus for Studying Fretting Fatigue, The
Review of Scientific Instruments, 42, pp. 817-821, 1971.
[7] Hoeppner, D.W. and Goss, G.L., "Normal Load Effects in Fretting Fatigue of
Titanium and Aluminum Alloys," Wear, 27, pp. 153-159, 1974.
[8] Hoeppner, D.W. and Goss, G.L., "Metallographic Analysis of Fretting Fatigue
Damage in Ti-6A1-4V MA and 7075-T6 aluminum, Wear, 27, pp. 175-187, 1974.
[9] Hoeppner, D.W. and Goss, G.L., "Characterization of Fretting Fatigue Damage by
SEM analysis", Wear, 24, pp. 77-95, 1973.
[10] Adibnazari, S., Hoeppner, D.W., "The Role of Normal pressure in Modeling Fretting
Fatigue," Fretting Fatigue, ESIS 18, R.B. Waterhouse and T.C. Lindley, Eds.,
Mechanical Engineering Publications, London, (1994) pp. 125-134.
[ 11] Betts, R.E., "Development and Evaluation of Coatings for Alleviating Fretting on
Fatigue Life of Titanium Alloys", General Electric Co., Contract AF33615-70-C-
1537, 1971.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HOEPPNER ET AL. ON BEHAVIOR OF TITANIUM ALLOYS 305
[13] Hoeppner, D.W. and Chandrasekaran, V., "Characterizing the Fretting Fatigue
Behavior of Ti-6A1-4V in Modular Joints," Medical Applications of Titanium and
Its Alloys: The Material and Biological Issues, ASTM STP 1272, S.A. Brown and
J.E. Lemons, Eds., pp. 252-265, 1996.
[16] Padberg, D.J., "Fretting Resistant Coatings for Titanium alloys", McDonnell Aircraft
Co.,AFML TR-71-184, 1971.
[17] Antoniou, R.A., Radke, T.C., "The Mechanisms of Fretting Fatigue of Titanium
Alloys", Materials Science and Engineering, A237 (1997)pp229-240.
[18] Kinyon, S.E., Hoeppner, D.W., "Spectrum Load Effects on the Fretting Behavior of
Ti-6A1-4V", Fretting Fatigue: Current Technology and Practices, ASTM STP
1367, Hoeppner, D.W., Chandrasekaran, V., Elliott, C.B., Editors, American
Socaety for Testing and Materials, West Conshohocken, PA, 2000, pp 100-115.
[19] Hutson, A.L., Nicholes, T., "Fretting Behavior of Ti-6A1-4V Against Ti-6A1-4V
Under Flat-on Flat Contact With Blending Radii, Fretting Fatigue: Current
Technology and Practices, ASTM STP 1367, Hoeppner, D.W., Chandrasekaran,
V., Elliott, C.B., Editors, American Society for Testing and Materials, West
Conshohocken, PA, 2000, pp 308-321.
[20] Anton, D.L., Lutian, M.J., Favrow, L.H., Logan, D., Annigeri, B., "The Effects of
Contact Stress and Slip Distance on Fretting Fatigue Damage in Ti-6A1-4V/17-
4PH Contacts", Fretting Fatigue: Current Technology and Practices, ASTM STP
1367, Hoeppner, D.W., Chandrasekaran, V., Elliott, C.B., Editors, American
Society for Testing and Materials, West Conshohocken, PA, 2000, pp119-140.
[21] Satoh, T., "The Influence of Microstructure on Fretting Fatigue Behavior of Near
Alpha Titanium", Fretting Fatigue: Current Technology and Practices, ASTM
STP 1367, Hoeppner, D.W., Chandrasekaran, V., Elliott, C.B., Editors, American
Society for Testing and Materials, West Conshohocken, PA, 2000, pp295-307.
[22] Hutson, A.L., Nicholes, T., "Fretting Behavior of Ti-6A1-4V Against Ti-6A1-4V
Under Flat-on Flat Contact With Blending Radii, Fretting Fatigue: Current
Technology and Practices, ASTM STP 1367, Hoeppner, D.W., Chandrasekaran,
V., Elliott, C.B., Editors, American Society for Testing and Materials, West
Conshohocken, PA, 2000, pp 308-321.
[23] Anton, D.L., Lutian, M.J., Favrow, L.H., Logan, D., Annigeri, B., "The Effects of
Contact Stress and Slip Distance on Fretting Fatigue Damage in Ti-6A1-4V/17-
4PH Contacts", Fretting Fatigue: Current Technology and Practices, ASTM STP
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
306 FRETTINGFATIGUE: ADVANCES
[24] Satoh, T., "The Influence of Microstructure on Fretting Fatigue Behavior of Near
Alpha Titanium", Fretting Fatigue: Current Technology and Practices, ASTM
STP 1367, Hoeppner, D.W., Chandrasekaran, V., Elliott, C.B., Editors, American
Society for Testing and Materials, West Conshohocken, PA, 2000, pp295-307.
[25] Cortez, R., Mall, S., Calcaterra, J., "Investigation of Variable Amplitude Loading on
Fretting Fatigue Behavior of Ti-6A1-4V", International Journal of Fatigue, 21
(1999) 709-717.
[26] Wallace, J., Neu, R., "Fretting Fatigue Crack Nucleation in Ti-6A1-4V", submitted to
Fatigue and Fracture of Engineering Materials and Structures, 2001.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Alisha L. Hutson, 1 Noel E. Ashbaugh,2 and Ted Nicholas 3
Reference: Hutson, A. L., Ashbangh, N. E., and Nicholas, Y., "An Investigation of
Fretting Fatigue Crack Nucleation Life of Ti-6AI-4V under Flat-on-Fiat Contact,"
Fretting Fatigue." Advances in Basic Understanding and Applications, STP I425, Y.
Mutoh, S. E. Kinyon, and D. W. Hoeppner, Eds., ASTM International, West
Conshohocken, PA, 2003.
Introduction
1Assistant Research Engineer, Umversity of Dayton Research Institt, te, 300 College
Park, Dayton, OH 45469-0128.
2Senior Research Engineer, University of Dayton Research Institute, 300 College Park,
Dayton, OH 45469-0128.
3Senior Scientist, Air Force Research Laboratory, Materials and Manufacturing
Directorate, Metals, Ceramics & NDE Division (AFRL/MLLMN), Wright-
Patterson AFB, OH 45433-7817.
3O7
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM International www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
308 FRETTING FATIGUE: ADVANCES
fretting fatigue occurs and subsequent accurate life prediction modeling has been elusive.
Many different test systems have been developed to aid in the study of the fretting
fatigue phenomenon. Most research has been conducted on Hertzian [3, 5], or square
cornered punch-on-flat [3, 5] geometries because of the availability of closed form
analytical solutions for the resulting stress distributions. However, the applicability of
these geometries to real components is limited. Some work has been done to directly test
real component geometries [1], but specimens are expensive, determination of the stress
distribution is tedious and costly, and the results are difficult to model. A geometry that
provides information at an intermediate level of complexity is required as the next step
toward the development of an accurate life prediction model that bridges the gap
between laboratory and service conditions.
The authors have published work on a novel test geometry that simulates the
essential features of a turbine engine blade root attachment while maintaining the
simplicity of a more generalized geometry. Previously published work established the
viability of the test apparatus in investigating fretting fatigue behavior and documented
preliminary results on the effect of several parameters critical to fretting fatigue [6, 7].
The purpose of the present investigation is to extend the scope of prior work and
answer questions regarding the mechanisms of fretting fatigue crack nucleation in the
current test geometry. Of interest to the current work are the location of crack nucleation
sites, the portion of life spent in fretting fatigue crack nucleation, and quantification of
the effects of fretting fatigue damage on residual fatigue properties. Identification of
crack nucleation sites using post-mortem fractography has produced less than conclusive
results [6, 7]. In this study, crack nucleation life and location will be investigated by
conducting fretting fatigue tests that are interrupted based on two independent criteria.
The resultant damage will be characterized using scanning electron microscopy,
metallographic analysis and semi-quantitative elemental analysis.
ExperimentalApproach
Fretting Fatigue Apparatus
The fretting experiments in this study were designed to simulate the primary
loading conditions under which fretting fatigue damage occurs in turbine engine blade
attachments. The/d0vetail geometry of a blade attachment is, in part, composed of flat
pressure faces that blend into the mating component via rather large radii. The pressure
faces are subjected to a bending moment produced by the dovetail flank angle, and to
cyclic normal and shear forces. Either all of the shear load is transferred across the
contact or the threshold of gross sliding is achieved and one component moves with
respect to the mating component.
The fretting fatigue test apparatus used in this and related studies incorporates a flat
specimen tested against a flat pad with blending radii at the edges of contact to simulate
the dovetail pressure face geometry. Static clamping loads are imposed using
instrumented bolts to measure the clamping load. A cyclic bulk load applied to the
specimen produces a negligible bending moment and a cyclic shear stress at the contact
that results in fretting fatigue, as indicated in the magnified view in Figure 1. The
contribution of the bending moment in the dovetail geometry is assumed to be negligible.
Valid tests performed in this apparatus always result in full transfer of the shear
load to the fixture, thus producing a mixed slip/stick condition that results in fretting
fatigue crack nucleation. The test assembly produces two nominally identical fretting
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HUTSON ET AL. ON FLAT-ON-FLAT CONTACT 309
fatigue tests for each specimen, when similar clamping conditions are imposed in both
grips (see Figure 2) [8]. Additional details on the fixture can be found in reference [6].
For this study, fretting fatigue cycles were applied at 300 Hz.
Figure 1 n Test fixture schematic indicating pad lengths, distance from center of
specimen to lower edge of pad, and blending radius at edge of contuct.
Figure 2 n Test load train schematic. Numbers indicate edge of contact locations.
For part of the tests conducted in this study, fretting fatigue conditions were
discontinued after a small portion of total fretting fatigue life, and the residual fatigue
lives were evaluated in uniaxial fatigue. A servo-hydraulic test system was used to
conduct the uniaxial fatigue tests. The system was equipped with a 5000 lbf (22.24 kN)
capacity load cell, an analog controller operated in the load control mode, and hydraulic
wedge grips with a 25 kN grip capacity and anti-fret inserts made of surfalloy. Tests
were conducted at 3 Hz. All tests were conducted under ambient laboratory conditions.
Fretting fatigue specimens and pads were machined from forged Ti-6A1-4V plates
with a t~+[~duplex microstructure. Since no cracks were expected in the pads,
orientation with respect to loading for the pads was not specified or identified. Axial
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
310 FRETTINGFATIGUE: ADVANCES
specimens were machined with the fatigue axis oriented in the longitudinal direction.
The material yield strength is 930 MPa; the tensile strength is 980 MPa, and the modulus
is 116 GPa. Microstructure details can be found in reference [9]. Specimens and pads
were low stress ground to an RMS 8 pJnch surface finish.
Three objectives were defined for the current investigation: identify the location of
fretting fatigue crack nucleation, identify the portion of life spent nucleating fretting
fatigue cracks, and quantify the reduction of fatigue properties caused by fretting fatigue
damage accumulated by 10% of fretting fatigue life. Attempts to identify primary crack
nucleation sites and crack nucleation lives in prior work [6, 7] have been inconclusive.
Three series of experiments were designed for this investigation, as a continuation
of the previous work. First, the fretting fatigue limit stresses for a 107 cycle fatigue life
were identified using a step loading technique, designated as 100%-of-life tests. Then,
shear wave ultrasonic crack detection was used in situ to try to identify fretting fatigue
cracks early in the propagation portion of life, designated as NDWrtests. Finally, some of
the fretting fatigue experiments were interrupted at 10%-of-life, and the effect of cycling
was quantified as residual fatigue life.
Geometry and loading conditions were the same as those used in prior work.
Fretting fatigue sample dimensions were 10 mm x 2 mm x 150 mm. Nominal fretting
pad lengths were 12.7 mm and 25.4 mm. A contact radius of 3.2 mm was used, resulting
in contact lengths of 6.35 mm and 19.05 ram. Clamping stresses, t~N, of 200 MPa to 620
MPa were selected to approximate the stress range identified for the blade attachment
region. All of the fretting fatigue experiments were conducted at R = 0.5.
For the 100%-of-life series of tests each specimen was cycled to failure using a step
loading procedure to obtain the fretting fatigue limit for a 107 cycle fatigue life. The
procedure invoNed cycling the specimen at a constant stress, which was below the
expected fatigue limit stress, for 107 cycles. Then the stress level was increased by a
small amount, usually five percent, and the cycling was continued for an additional 107
cycles. The stress increments were continued-u~fitil the specimen fractured. Then, the
fatigue limit was calculated from the final stress, number of cycles at the final stress, and
the stress from the prior block, using linear interpolation [10]. Six tests were conducted
at the nominal 620 MPa clamping stress condition and three were conducted at the 200
MPa clamping stress condition. The purposes of these tests were to establish an average
fatigue strength for a 107 cycle fatigue life including data on the repeatability of each
condition, and to provide fretted surfaces at 100 percent of life. Fretting scars were
characterized in the SEM (Scanning Electron Microscope) for comparison to partial life
damage characterization from later tests.
For the NDET series of tests, specimens were cycled at a far field bulk stress of 350
MPa for the lower clamping stress and 260 MPa for the higher clamping stress. These
stress levels are roughly equal to the fatigue limit stresses identified for a 107 cycle
fatigue life in the 100%-of-life tests. During each test, two transducer/coupling wedge
assemblies were attached to the specimen, using a fast curing epoxy, to monitor cracking
in each grip independently. When applied to uniaxial fatigue specimens, the technique is
capable of detecting surface cracks with depths of ~200 Ixm. In the configuration
employed in this study, the transducers both transmitted the 10 MHz ultrasonic wave and
received reflections from cracks present in the structure. Identification of cracks was
achieved by comparing successive signals acquired at 500,000 mechanical fatigue cycle
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HUTSON ET AL. ON FLAT-ON-FLAT CONTACT 311
intervals, and identifying changes in shape and amplitude of various peaks occurring in
the vicinity of the edge of contact. If a crack was detected, the specimen was removed
for inspection in the SEM, heat tinted at 420~ for four hours to mark the location of the
crack front at the time of inspection, and then reinstalled in the test frame for cycling to
fracture at the same conditions used to nucleate the crack. Three fretting fatigue
specimens for each condition were tested using this technique.
For the 10%-of-life series of tests each specimen was cycled for 1 million cycles at
a far field bulk stress of 350 MPa for the lower clamping stress and 260 MPa for the
higher clamping stress. Then the fretting condition was discontinued and residual fatigue
life tests were conducted. These experiments are referred to as 10%-of-life tests, since
the fretting fatigue damage is removed at 10% of the expected fretting fatigue life. The
10%-of-life damage level was selected, in part, to allow comparison to work in the
literature [3, 5, 11, 12}, where significant damage progression up to 10% of life has been
reported. Damage characterization was conducted through SEM (Scanning Electron
Microscope) imaging and uniaxial residual fatigue life testing.
In previous work interrupted test specimens were re-machined into dogbone
samples in the vicinity of the fretting damage. The residual fatigue life test results
obtained from those samples did not indicate a reduction in fatigue life compared to
undamaged samples, except in the case of features that could not be attributed to fretting
damage [7]. SEM inspection of these fretting scars prior to re-machining indicated that
the highest levels of wear damage occurred at the sample edge. Thus, the results of these
tests provided information only on the location of the highest level of damage, which
was outside of the region of the fretting scars after dogbone specimen machining.
In the current work, the region of highest wear damage was isolated by cutting
straight sided (SS) specimens from the fretted regions, as shown in Figure 3. The
resulting straight sided sample dimensions were 2 mm X 2.5 mm X 100 mm. To
minimize grip failures, the ends of the specimen were covered with 0.127 mm (5 rail)
thick copper tabs. Samples were tested at 950 MPa maximum stress at R = 0.5. Several
baseline tests were also conducted on unfretted specimens to compare against the fretted
specimen data.
Pad Contact Regions
~ / ~ Specimen Edge ~ . ~
1<~-25 mm--~
'~t: - - 100ram 150~-25
# mm-~
1 )r ~ a~ mCut > T
Characterization
Specimens were characterized in the SEM after the application of fretting damage
to provide qualitative information on the level of wear generated in each test. Uniaxial
fatigue fracture surfaces were also inspected in the SEM after fracture. Crack nucleation
sites and causes were documented for all samples that fractured in the gage section. For
specimens that failed in the gage, but away from the fretting damage, the distance
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
312 FRETTINGFATIGUE. ADVANCES
between the fracture surface and the fretting scar was measured.
The fretting fatigue damage was also characterized with a metallographic cross-
section of a step load sample and with representative spectral analysis of the fretting
debris. The section was taken from the unfailed end of a failed sample bearing non-
failure cracks. Similar sections taken from samples subjected to fretting fatigue under
Hertzian or punch-on-flat contact conditions have been reported in the literature [2, 4, 5],
Those authors reported the presence of numerous non-propagating cracks and primary
crack nucleation angles of approximately 45*. A similar cross-section from the current
test geometry was cut to acquire information on the crack front location at the point at
which the section was taken and to allow future comparison to other geometries. Spectral
analysis of the fretting debris was conducted using Energy Dispersive Spectrometry
(EDS) to identify elemental differences between fretting debris and the base material.
Experimental Results
The results of the step load tests are presented in Figure 4, which shows the
estimated fatigue limit for 107 cycles versus average applied clamping stress. Some data
are included from previous work conducted at R = 0.5 on specimens having the same
contact radius, 3.2 mm, as that used here [6]. At 200 MPa average clamping stress the
average fatigue strength was ~ 330 MPa; at 620 MPa the average fatigue strength was -
250 MPa. Error bars representing two standard deviations are included. A subtle
increase in fatigue limit was observed as a function of decreasing clamping stress in
these results, although relatively large amounts of scatter tend to obscure the trend.
Nozr Results
Three tests were conducted at the 200 MPa clamping stress, in which the intent was
to interrupt the tests based on crack detection using shear wave Non-Destructive
Evaluation (NDE) technique. None of the attempts to detect cracks on specimens
subjected to this clamping stress were successful. Table 1 lists cycles to failure as well
as the cycle count of the last shear wave data acquisition. One of the tests at the 200
MPa clamping stress (#99-B57) was stopped for inspection based on changes in the
waveform that were thought to be indications of crack nucleation at ~11 million cycles.
However, careful inspection in the SEM did not reveal any cracks. If the shear wave
NDE results for the other two tests are accurate - that no cracks were present at the last
cycle count for which shear wave data were acquired - it can be concluded that less than
4 percent of life was spent in crack propagation. This conclusion is a direct contradiction
of the findings from earlier researchers [3, 5, 13] that indicate the presence of cracks very
early in life.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HUTSON ET AL. ON FLAT-ON-FLAT CONTACT 313
Cracks were successfully detected in two of the three tests conducted at the 620
MPa clamping stress (#s 99-B60 and 99-B61). Results for these tests are given in Table
2. The detected cracks were fairly large, so that the time to propagate the detected cracks
to failure was very small compared to the total specimen life. It should be noted that
application of this inspection technique has not previously been documented for fretting
fatigue. The viability of detecting cracks under these conditions was unknown, so the
detection of any cracks was considered a success. Ultimately, the observation of new
peaks in the waveforms lead to the identification of cracks in 99-B60 and 99-B61. While
these results do not provide adequate information on the crack nucleation life for the 620
MPa clamping stress condition, they do support the feasibility of using the shear wave
technique in situ in the high frequency contact laboratory environment. Feasibility of
using the shear wave ultrasonic technique was demonstrated despite the significant
amount of acoustic and electro-magnetic noise generated by the high frequency
mechanical fatigue apparatus.
For the tests subjected to the lower clamping stress, total lives ranged from 3.1
million to 14.6 million cycles, thus bracketing the estimated 107 cycle fatigue life. At the
higher clamping stress, the total lives ranged from 4.1 million to 7.3 million. For both
conditions, the cycles-to-failure results recorded were within the expected level of scatter
for such tests. Thus, these results may be used to substantiate the validity of the step
loading technique for fretting fatigue conditions, a point not previously demonstrated for
such complex loading.
4oo
<> !o
'F
~ 0
g_ 2s~I ~ - - ).96 ....................................... i........................... ~..~ .....
[ A v e = 253 M P a
E ).94
~ 150 0 Step road tests; R = 0.5 [6]
100 9 ~N = 420 Mpa; R = 0"5 o Dogbone (no damage) J
).~ [] SS (no damage) [ ....................
~ = 140 MPa; R = 0 . 5
* SS (140 M P a normal stress)J c
50 Uniaxiat Fatigue Limit (R = 0.5) = 660 MPl a' o s?o,!l . . . . . .
0.9
-1400-1200-1000 -800 -600 -400 -200 1000 10000 100000
Cycles to Failure
a N (MPa)
Figure 4 - - Fatigue limit stress at R = 0.5 Figure 5 - - S-N results for residual fatigue
versus average clamping stress for a 107 life specimens with lO%-of-life damage.
cycle life.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
314 FRETTINGFATIGUE: ADVANCES
Results of the residual fatigue life tests on straight sided specimens are shown in
Table 3 and Figure 5. Table 3 lists cycles to failure and the clamping stress under which
each fretting specimen was tested. In addition, the "failure location" column indicates
failure in the grip, at the fretting damage, Or the distance from the fretting damage that
failure occurred. Figure 5 presents the residual fatigue life test results in S-N form along
with baseline data described below.
Of the six residual fatigue life specimens whose damage was generated with 200
MPa clamping stress and 350 MPa axial fatigue stress, only one failed in the gage
section when subjected to uniaxial fatigue. The resulting fracture occurred ~ 2.6 mm
away from the line of fretting damage and, so was not a fretting fatigue related fracture.
No appreciable reduction in fatigue life was observed (note " . " i n Figure 5). The
remaining samples failed in the grip, and thus indicate that the fretting damage on those
samples was less severe than the stress concentration produced by contact with the grip.
Table 3 - Residual axial fatigue life test results at 950 MPa, R = 0.5.
Of the six specimens subjected to fretting fatigue damage at 620 MPa clamping
stress and 260 MPa axial fatigue stress, all six failed in the gage section when subjected
to uniaxial fatigue. (note "<>"symbol in Figure 5). One failed at approximately 3000
cycles at a sizeable fretting fatigue nucleated crack. Two more specimens failed in less
than 25 000 cycles at fretting damage where no obvious cracks were present. The
remaining three specimens failed away from the fretting damage in the gage section, and
produced residual lives of 30 000 cycles or greater. The wear scars on specimens
subjected to this clamping stress condition appeared nominally identical from the SEM
imaging in the absence of fretting fatigue nucleated cracks.
Additional baseline data are provided in Figure 5 for comparison. These tests were
conducted on as-received dogbone samples machined to the same surface condition as
the fretting fatigue samples, and are represented by "O". One unfretted straight sided
specimen was tested and fractured in the gage section, represented by "D". Only
specimens that failed at the line of fretting damage showed a marked decrease in residual
fatigue life compared to the baseline tests.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HUTSON ET AL. ON FLAT-ON-FLAT CONTACT 315
Characterization Results
Characteristic fretting scars from each clamping stress condition for both 100% and
10%-of-life tests are shown in Figures 6 through 9. All of the images were created using
backscatter emission imaging in the SEM to enhance wear features. Wear was minimal
in the 200 MPa samples (Figures 6 and 8) compared to the levels of wear observed in
other test geometries [2, 3]. By comparison, almost no wear was observed in the 620
MPa samples (Figures 7 and 9), except where fretting fatigue nucleated cracks resulted in
increased wear due to interaction of the crack and the edge of contact (Figure 10).
Debris was spread over a larger area in the 200 MPa specimens than in the 620 MPa
specimens. However, cracks of 1 mm or more in length were observed on all 620 MPa
specimens at 106 cycles, indicating that cracks nucleate in less than 10% of life for this
clamping stress condition. The crack nucleation life of specimens subjected to the lower
clamping stress was indicated to be greater than 95% from the ND~r test results.
The presence of cracks at 10% of life in the specimens subjected to the higher
clamping stress condition provides an explanation for the residual fatigue life results
discussed above. If crack nucleation required most of the fretting fatigue life for the tests
Figure 6 - - Wear debris for lO0%-of-life Figure 7 - - Non-crack wear debris for
at 200 MPa clamping stress. (Nf = 144 tO0%-of-life at 620 MPa clamping stress.
000 000 cycles) (Nf = 22 600 O0 cycles)
Figure 8 - - Wear debris for l O%-of-life at Figure 9 - - Non-crack wear debris for
200 MPa clamping stress, lO%-of-life at 620 MPa clamping stress.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
316 FRETTINGFATIGUE: ADVANCES
Figure 10 w Secondary fretting crack nucleated at 420 MPa clamping stress. (Nf ~ 4.1
million cycles)
conducted at the lower clamping stress, then reduction in residual fatigue life after only
10% of the estimated fretting fatigue life would not be expected. However, if crack
nucleation occurred early in life, as with the specimens tested at the higher clamping
stress, the reduction in residual fatigue life is likely.
Results from characterization of the NDETspecimens, conducted prior to fracture,
support these observations. On a given specimen, as many as eight crack nucleation sites
are present (two for each pad/specimen contact region indicated by the numbers in
Figure 2), and so simultaneous nucleation of cracks at two or more of these sites may
occur. Many sizeable cracks were observed on the specimens subjected to the higher
clamping stress, ranging in length from 200 ~tm to 1.6 mm as noted in Table 1. All of
the cracks appeared to have nucleated near the specimen edges. By comparison, no
cracks larger than 20 ~m were observed on the specimens subjected to the lower
clamping stress, and those cracks were contained entirely within the fretting debris. This
observation is consistent with the results of the ultrasonic waveform data, which
indicated no crack presence during testing. Previous work [14] has shown that cracks
such as those observed on the specimens subjected to lower clamping stress were either
non-propagating, or propagated in a manner that led to spalling of the wear products.
Inspection of the specimens subjected to the lower clamping stress was performed after
fracture, when interruption of the test prior to fracture was not achieved.
Representative fracture surfaces from 100%-of-life tests for both clamping stresses
are shown in Figures 11 and 12. The micrographs show the nucleation regions of the
fracture surfaces for 200 MPa and 620 MPa clamping stresses, respectively, and include
the entire thickness of the specimen. Figures 13 and 14 give closer views of the
estimated nucleation sites, indicated by the boxes in Figures 11 and 12. All four images
were taken in backscatter mode, where darker regions represent different alloy phases,
different levels in the fracture topography, or cracking parallel to the fatigue axis.
Inspection of both fracture surfaces reveals that the cracks nucleated from roughly
the same region with respect to the edge of the specimen, and propagated into the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HUTSON ET AL. ON FLAT-ON-FLAT CONTACT 317
specimen in the direction of the arrows (see Figures 11 and 12). The 200 MPa specimen
fracture surface has a more planar appearance with no evidence that any cracks nucleated
other than the dominant one that fractured the specimen. The 620 MPa specimen shows
evidence of multi-plane cracking and chipping (note damage to the right of the box in
Figure 12) resulting from the propagation of multiple cracks. The nucleation sites in
Figures 11 and 12 are within 1 mm of the specimen edge.
Closer inspection of the primary nucleation site of the 200 MPa specimen also
reveals a very planar fracture with no cracks parallel to the fatigue loading axis, pointing
to the dominance of the bulk axial load on crack propagation for this contact
configuration and loading condition. The magnified view of the 620 MPa specimen
fracture surface shows evidence of a higher stress state and the multi-axial nature of that
stress state in the form of cracking parallel to the fatigue axis.
Figure 11 - - 99-B74 (200 MPa clamping Figure 12 ~ 99-B72 (620 MPa clamping
stress) - step load test fracture surface, stress) - step load test fracture surface.
After residual fatigue life tests were completed on the 10%-of-life specimens, the
resulting fracture surfaces were inspected in the SEM to determine if the fractures were
fretting fatigue related. A representative fracture surface of a non-fretting fatigue gage
section failure is shown in Figure 15. This image was taken with the sample tilted at a
45 ~ angle and includes both the fretting scar and the fracture surface. In each non-
fretting gage section failure an unintentional notch was identified as the cause of crack
nucleation. Fretting damage was a sufficient distance from the crack nucleation site, as
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
318 FRETTINGFATIGUE: ADVANCES
noted in Table 3, that fretting could not have played a role in the specimen fracture,
except in one case. One specimen fractured under the pad contact area so that a
conclusive cause of crack nucleation could not be determined. The fracture surface for
this specimen is shown at a 45 ~ angle in Figure 16. A notch was present at the crack
nucleation site, but it occurred under the contact region. Since the source of the damage
was unknown, the role of the contact in crack nucleation could not be determined,
although the fatigue life of this specimen was not reduced appreciably.
Figure 15 - - Residual fatigue life sample Figure 16 m Residual fatigue life sample
with fracture surface and fretting scar with fracture surface shown at 45 ~ the
shown simultaneously at 45 ~ the fatigue fatigue loading axis. (Nf = 30,343 cycles -
loading axis. (Nf = 36,097 cycles) indeterminate failure)
Two of the specimens failed at the fretting edge of contact without the presence of
identifiable fretting nucleated cracking. A representative photo of one of the fracture
surfaces is shown in Figure 17. In both cases crack nucleation occurred within the line
of fretting fatigue damage, and without the presence of unintentionaldamage sites from
Figure 17 m Residual fatigue life sample Figure 18 --Residual fatigue life sample
with fracture surface shown at 45 ~ the with fracture surface shown at 45 ~ the
fatigue loading axis. (Nf = 11,042 cycles - fatigue loading axis. (Nf = 3,055 cycles-
fretting nucleated failure) failure from fretting nucleated crack)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HUTSON ET AL. ON FLAT-ON-FLAT CONTACT 319
other sources. The fretting "damage" that resulted in these failures was not noticeably
different from the "damage" observed on specimens where fracture occurred away from
the fretting site.
The last specimen failed at the fretting damage in the presence of a crack 400 ~rn
long by 160 grn deep. The 45 ~ view of the fracture surface is shown in Figure 18. Since
the presence of the crack was known prior to uniaxial fatigue testing, the specimen was
heat tinted to mark the location of the crack front. The crack was nearly elliptical, and
nucleated within 100 p.m of the specimen edge. This fracture surface supports the
hypothesis of crack nucleation location near, but not at the edge of the specimen.
One unfretted specimen was also tested for comparison purposes. Crack nucleation
was caused by surface damage perpendicular to the fatigue loading axis. While the
fatigue lives of the straight samples did not differ in a statistically significant manner
from the baseline tests on dogbone samples, some sort of stress riser was required to
achieve a gage section failure. This point suggests that damage at 10% of fretting fatigue
life obtained under 200 MPa clamping stress is less severe than a small damage site, such
as might be incurred during machining or installation of the specimen into the test frame.
Fretting damage obtained at 620 MPa clamping stress may be more severe than the types
of incidental damage described here, but is not necessarily so.
The fretting debris from an un-cracked fretting scar was characterized for elemental
content. The 200 MPa clamping stress condition was selected, since a greater volume of
wear debris was available and the expected anomalous elements were small. Figure 19
shows a portion of a spectral analysis chart for the unfretted material. Only titanium,
aluminum, and vanadium are present in significant quantities. Carbon and oxygen are
marked on the graph, but the amount present with respect to the primary alloy
constituents is negligible. A representative scan of the fretting debris is shown in Figure
20. Titanium, aluminum and vanadium are still the primary constituents, but the oxygen
and carbon peaks are more pronounced, and can no longer be described as noise. Note
that the primary titanium peak that occurs at ~4.5 keV and the vanadium peak that occurs
at -4.9 keV are not shown in Figures 19 and 20, but were present in the original scans at
counts of-500 and 100, respectively.
180
t20
160
140 AI zoo
120 O A1
100.
80
Ti 0
60
40
C ~ 2o
20
O o
o.2 o.4 o.~ o~e i l ~ 2 L 4 L 6 l~s ~ ~.2 0,2 0.4 0,6 0.8 1 1.2 1.4 1.6 1.8 2 2.2
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
320 FRETTINGFATIGUE: ADVANCES
Oxidation of the original material elements has been linked to premature crack
nucleation in both fretting fatigue and fretting wear in other materials [13, 15]. So the
presence of significant levels of oxygen, as found here, presented a possible mechanism
for crack nucleation in the specimens tested at the 200 MPa clamping stress. Brittle
reaction products such as TiO2 or AlzO3 could present ideal crack nucleation sites that
would allow crack propagation into the bulk material, if the oxide were fixed firmly to
the substrate. For each of the 200 MPa samples inspected in the SEM, the oxide was
fixed firmly enough to the base material that it was left undisturbed by rigorous
ultrasonic cleaning. This nucleation mechanism is not applicable to the higher clamping
stress condition, based on the observed volume of wear debris in the absence of cracks.
A metallographic cross-section was cut in the region of a secondary crack on the
unfractured end of a fractured specimen tested under the 620 MPa clamping stress
condition. The crack extended ~ 1 mm from the specimen edge. Two nucleation sites
were identified by the presence of relatively large amounts of fretting debris, and the
crack appeared to propagate outward from both sites along a complex propagation path
(Figure 10). The crack was sectioned to approximately 600 Ixm from the specimen edge
near the second nucleation site (Figure 10 - note section line at right of photo).
The depth of the crack at the section location was ~ 500 ~tm. As shown in Figure
21, the dominant crack nucleated at ~ 45 ~ to the loading axis, as reported by other
researchers [4], and within 5-10 p.m, turned perpendicular to the loading axis. Both
propagating and non-propagating cracks are observed. In this case, very little material
was removed from this part of the specimen face during the crack nucleation process.
Also, the crack propagated across the ~+~ lath before turning perpendicular to the
fatigue loading axis, indicating that the early stages of crack propagation under this
contact condition are not heavily influence by environmental conditions such as
oxidation or corrosion, as has been reported [13, 15]. Since no secondary cracking was
observed on specimens subjected to 200 MPa clamping stress, the role of environment
on fretting fatigue nucleated cracks could not be verified.
Taken together, the results from the different aspects of this investigation provide
new insight into the fretting fatigue behavior for the current contact geometry. Using
two clamping stress conditions representing the approximate range of normal stresses to
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
HUTSON ET AL. ON FLAT-ON-FLAT CONTACT 321
which a turbine engine blade attachment region is subject, two types of crack nucleation
behavior were identified and determined to be dependent on the applied clamping stress.
The number of cracks present on a single specimen was found to be dependent on
the clamping stress. The higher clamping stress produced multiple cracks, of which one
would eventually dominate. This trend in behavior was also reflected in the time
required for nucleation of cracks for the two clamping stress conditions. The 200 MPa
condition spent over 95% of life nucleating cracks, while the 620 MPa condition
nucleated cracks within 10% of fretting fatigue life.
From this difference in crack nucleation behavior, the residual fatigue life results
may be explained. If damage in the form of cracks can occur within 10% of life, as in
the case of the high clamping stress condition, then a debit in fatigue life is expected for
samples subjected to 10% of fretting fatigue life. However, the fretting fatigue limit
stresses for the two clamping stress conditions were similar to produce a fatigue life of
107 cycles.
Some behavior was not dependent on the clamping stress. Cracks nucleated in the
region near specimen edges, between 100 ~tm and 1 mm of the edge, regardless of the
applied normal stress. This trend is likely a function of the contact geometry and the
manner of load application. While such a trend may appear to be a deficiency in the
apparatus design, it gives some indication of what mechanisms are responsible for the
observed behavior. A general observation from the experiments performed here and in
prior work is that all contact related behavior is dependent on pad, specimen and
fixturing geometry.
In addition to the observations made regarding the objectives of this study, the step
loading technique, which was developed to rapidly determine fatigue limit stresses for
individual specimens, was verified for fretting fatigue conditions.
References
[1] Ruiz, C., Boddington, P. H. B., and Chen, K. C., "An Investigation of Fatigue
and Fretting in a Dovetail Joint," Experimental Mechanics, Vol. 24, 1984, pp.
208-217.
[2] Bryggman, U. and Soderberg, S., "Contact Conditions and Surface Degradation
Mechanisms in Low Amplitude Fretting", Wear, Vol. 125, 1988, pp. 39-52.
[3] Fretting Fatigue, ESIS 18, R.B. Waterhouse and T.C. Lindley, Eds., Mechanical
Engineering Publications, London, 1994, pp. 219-238.
[4] Zhou, Z. R. and Vincent, L., "Mixed Fretting Regime," Wear, Vol. 181-183,
1995, pp. 551-536.
[5] Standardization of Fretting Fatigue Test Methods and Equipment, ASTM STP
1159, M. Helmi Atria, and R. B. Waterhouse, Eds., American Society for Testing
and Materials, Philadelphia, PA, 1992, pp. 153-169.
[6] Hutson, A., Nicholas, T., and Goodman, R., "Fretting Fatigue of Ti-6A1-4V
Under Flat-on-Flat Contact," International Journal of Fatigue, Vol. 21, No 7,
1999, pp. 663 - 670.
[7] Hutson, A. and Nicholas, T., "Fretting Fatigue Behavior of Ti-6A1-4V against Ti-
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
322 FRETTINGFATIGUE: ADVANCES
[8] Hutson, A.L., "Fretting Fatigue of Ti-6AI-4V Under Hat-on-Flat Contact with
Blending Radii," M.S. Thesis, School of Engineering, University of Dayton,
Dayton, OH, August, 2000.
[9] Haritos, G.K., Nicholas, T. and Lanning, D., "Notch Size Effects in HCF
Behavior of Ti-6A1-4V," International Journal of Fatigue, Vol. 21, No 7, 1999,
pp. 643 - 652.
[10] Maxwell, D.C. and Nicholas, T., "A Rapid Method for Generation of a Haigh
Diagram for High Cycle Fatigue," Fatigue and Fracture Mechanics: 29th
Volume, ASTM STP 1321, T. L. Panontin and S.D. Sheppard, Eds., American
Society for Testing and Materials, 1999, pp. 626-641.
[11] Endo, K. and Goto, H., "Initiation and Propagation of Fretting Fatigue Cracks,"
Wear, Vol. 38, 1976, pp. 311-324.
[12] Nix, K.J. and Lindley, T.C., "The Application of Fracture Mechanics to Fretting
Fatigue," Fatigue and Fracture of Engineering Materials Structures, Vol. 8, No.
2, 1985, pp. 143-160.
[I3]. Blanchard, P., Colombie, C., Pellerin, V., Fayeulle, S. and Vincent, L. "Material
Effects in Fretting Wear - Application to Iron, Titanium, and Aluminum Alloys,"
Metallurgical Transactions, Vol. 22A, 1991, pp. 1535-1544.
[14] Fayeulle, S., Blanchard, P., and Vincent, L., "Fretting Behavior of Titanium
Alloys," Tribology Transactions, Vol. 36, No. 2, 1993, pp. 267-275.
[15] Waterhouse, R.B., "Fretting Wear," Wear, Vol. 100, 1984, pp. 107-118.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Kazuhisa Miyoshi, l Bradley A. Lerch, I Susan L. Draper, l and Sai V. Raj t
Reference: M.iyoshi, K., Lerch, B. A., Draper, S. L., and Raj, S. V., "Evaluation of Ti-
48AI-2Cr-2Nb Under Fretting Conditions," Fretting Fatigue: Advances in Basic
Understanding and Applications, ASTM STP 1425, Y. Mutoh, S. E. Kinyon, and D. W.
Hoeppner Eds., ASTM International, West Conshohocken, PA, 2003.
INational Aeronautics and Space Administration, Glenn Research Center, Cleveland, Ohio
44135-3191.
2Composition, at.%: titanium, 47.9; aluminum, 48.0; niobium, 1.96; chromium, 1.94;
carbon, 0.013; nitrogen, 0.014; and oxygen, 0.167.
323
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
324 FRETTINGFATIGUE: ADVANCES
Introduction
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MIYOSHI ET AL. ON ALLOYS UNDER FRETTING CONDITIONS 325
Materials
The nickel-base superalloy was solutioned and aged according to Aerospace Material
Specification AMS 5596G, SAE, Warrendale, PA, 1987, yielding Rockwell C-scale
hardness HRc of 36. The tensile properties [16] are shown in Table 2. The ultimate tensile
strength of superalloy is greater than that of Ti-48A1-2Cr-2Nb by a factor of -3.5 at room
temperature and -2 at high temperature (~ 1000 K).
The reference Ti-6AI-4V specimens were of the following nominal composition (in
weight percent): titanium, balance; aluminum, 5.5-6.75; vanadium, 3.5-4.5; iron, <0.J0;
carbon, <0.08; nitrogen, <0.05; oxygen, <0.20; and hydrogen, <0.015 [17].
Experiments
Figure 1 presents the fretting wear apparatus used in this investigation. Fretting wear
experiments were conducted with 9.4-ram-diameter, hemispherical nickel-base superalloy
pins in contact with Ti-48Al-2Cr-2Nb flats or with 6-ram-diameter, hemispherical
Ti-48Al-2Cr-2Nb pins in contact with nickel-base superal!oy flats in air at temperatures
from 296 to 823 K. All the flat and pin specimens used were polished with 3-~tm-diameter
diamond powder. Both pin and flat surfaces were relatively smooth, having centerline-
average roughness R, in the range 18 to 83 nm (Table 3). The Vickers hardness, measured
at a load of 1 N, for the polished flat and pin specimens is also shown in Table 3.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
326 FRETTINGFATIGUE: ADVANCES
/~Load
Sensor
L
t~ Sensor
~~ , /~\t//,/~tI /~ ~ Test
specimen
J ~ L ~ ~ Oscillation
~De~ail
ThermOcOuple CD-01-81402
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MIYOSHI ET AL. ON ALLOYS UNDER FRETTING CONDITIONS 327
Observations
Surface and subsurface damage always occurred on the interacting surfaces of the Ti-
48A1-2Cr-2Nb fretted in air. The surface damage consisted of material transfer, pits, oxides
and debris, scratches, fretting craters and/or wear scars, plastic deformation, and cracks.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
328 FRETTING FATIGUE: ADVANCES
50X103 Ti Ni
40 -
Cr
30 -
l e
d 20 -
O
0
0
i!:
0 ! ' I 1' i I ii iilli ii I
0 2 4 6 8 10 12 14
Electron energy, keV
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MIYOSHI ET AL. ON ALLOYS UNDER FRETTING CONDITIONS 329
Figure 3--Wear sca~" (a) on E-48A1-2Cr-2Nb pin and (b) on superalloy flat. Fretting
conditions. load, ] N,'j?equency, 80 Hz; slip amplitude, 50pro," total number of cycles,
1 million," environment, air," and temperature, 823 K.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
330 FRETTINGFATIGUE: ADVANCES
Figure 4--Surface and subsurface damage in Ti-48Al-2Cr-2Nb flat in contact with super-
alloy pin. (a) Scratches. (b) Cracks in oxide layers. (e) Cracks in metal. (d) Fracture pits
and plastic deformation. Fretting conditions: load, 1 N,"frequency, 80 Hz; slip amplitude
and total number of cycles: (a) 50 tim and i million, (b) 60/tm and t 0 million, (c) 50 pm
and I million, (d) 70 ~tm and 20 million; environment, air," and temperature, 823 K.
part of the load, they cause concentrated pressure peaks on both surfaces. The pressure
peaks may well be the origin of crack nucleation in the oxide layers and the bulk alloys.
Two types of crack were observed on the wear surface of Ti-48A1-2Cr-2Nb: cracks in the
oxide layers, and cracks in the bulk Ti-48A1-2Cr-2Nb.
Oxide layers readily form on the Ti-48A1-2Cr-2Nb surface at 823 K and are often a
favorable solution to wear problems. However, if the bulk Ti-48A1-2Cr-2Nb is not hard
enough to carry the load, it will deform plastically or elastically under fretting contact. With
Ti-48A1-2Cr-2Nb, cracks occurred in the oxide layers both within and around the contact
areas (Fig. 4(b)).
Fractures in the protective oxide layers produced cracks in the bulk Ti-48A1-2Cr-2Nb
(Fig. 4(c)) and also produced wear debris; chemically active, fresh surfaces; plastic
deformation; and craters or fracture pits (Fig. 4(d)). The wear debris caused third-body
abrasive wear (Fig. 4(a)). Local, direct contacts between the fresh surfaces of Ti-48AI-2Cr-
2Nb and superalloy resulted in increased adhesion and local stresses, which may cause
plastic deformation, flake-like wear debris, and craters (e.g., the fracture pits in the
Ti-48A1-2Cr-2Nb shown in Fig. 4(d)).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MIYOSHI ET AL. ON ALLOYS UNDER FRETTING CONDITIONS 331
Figure 6 shows the wear volume loss measured by the optical interferometer as a
function of fretting frequency for Ti-48A1-2Cr-2Nb in contact with superalloy. Although
there were some exceptions, the wear volume loss generally decreased with increasing
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
332 FRETTING FATIGUE: A D V A N C E S
6.0xl 04
[] Temperature,
oK
O 296
[] 823
9
::L []
9
o 4.0 -
[]
E
_=
9
9
2.0 I ~_ I I
0 50 100 150 200
Frequency, Hz
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MIYOSHI ET AL. ON ALLOYS UNDER FRETTING CONDITIONS 333
6.0xl 04 Frequency,
Hz C}
o
% o 50 []
C) [] 80
o
A 120
o 4.0 - 9 160 O
oJ
E
9
2.0
200 400 600
Temperature, ~
l~ I ~ J
273 473 673 873
Temperature, K
107 --
Temperature,
K
0 296
106 [] 823
o
E [] o
2:~ 1o5
o
[] o
104 I ~ L I J
0 50 100 150 200
Amplitude, Ltm
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
334 FRETTINGFATIGUE: ADVANCES
more metallic wear debris, causing severe abrasive wear in the contacting metals. Figure 9
presents a three-dimensional, optical interferometry image of the Ti-48A1-2Cr-2Nb wear
scar at a slip amplitude of 200 I.tm and a temperature of 296 K. In the wear scar are large,
deep grooves where the wear debris particles have scratched the Ti-48A1-2Cr-2Nb surface
in the slip direction.
Figure 10 shows the measured wear volume loss as a function of load for Ti-48A1-
2Cr-2Nb in contact with superalloy at a temperature of 823 K, a fretting frequency of
80 Hz, and a slip amplitude of 50 Ixm for 1 million cycles. The fretting wear volume loss
generally increased as the load increased, generating more metallic wear debris in the
contact area, the primary cause of abrasive wear in both Ti-48A1-2Cr-2Nb and superalloy.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MIYOSHI ET AL. ON ALLOYS UNDER FRETTING CONDITIONS 335
8.0xl 0 4
9
6.0- 9
%
:::l.
4.0-
E
2.0--
9
0 ( I ~ _ _ l
0 1 2 3 4
Load, N
Figure l O----Wearvolume loss of Ti-48Al-2Cr-
2Nb flat in contact with superalloy pin as
function of load. Fretting conditions."fre-
quency, 80 Hz; slip amplitude, 50 pro; total
number of cycles, 1 million," environment,
air," and temperature, 823 K.
Concluding Remarks
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
336 FRETTINGFATIGUE: ADVANCES
Acknowledgment
The authors are grateful to Dr. Gary R. Halford and Dr. Michael V. Nathal for very
helpful discussions.
References
[2] Miyoshi, K., "Aerospace Mechanisms and Tribology Technology: Case Study,"
Tribology International, Vol. 32, 1999, pp. 673-685.
[3] Tallian, T. E., "Failure Atlas for Hertz Contact Machine Elements," Fretting Wear,
ASME Press, New York, 1992, pp. 141-154.
[5] Waterhouse, R. B., "Occurrence of Fretting in Practice and Its Simulation in the
Laboratory," Materials Evaluation Under Fretting Conditions, ASTM STP 780,
American Society for Testing and Materials, Philadelphia, PA, 1982, pp. 3-16.
[6] Kusner, D., Pooh, C., and Hoeppner, D. W., "A New Machine for Studying Surface
Damage due to Wear and Fretting," Materials Evaluation Under Fretting
Conditions, ASTM STP 780, American Society for Testing and Materials, West
Conshohocken, PA, 1982, pp. 17-29.
[8] Lutynski, C., Simansky, G., and McEvily, A. J., "Fretting Fatigue of Ti-6A1-4V
Alloy," Materials Evaluation Under Fretting Conditions, ASTM STP 780, American
Society for Testing and Materials, West Conshohocken, PA, 1982, pp. 150-164.
[9] Bill, R. C., "Review of Factors That Influence Fretting Wear," Materials Evaluation
Under Fretting Conditions, ASTM STP 780, American Society for Testing and
Materials, West Conshohocken, PA, 1982, pp. 165-182.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MIYOSHI ET AL. ON ALLOYS UNDER FRETTING CONDITIONS 337
[10] Hansson, T., et al., "High Temperature Fretting Fatigue Behavior in an XD y-Base
TiAI," Fretting Fatigue: Current Technology and Practices, ASTM STP 1367, D.W.
Hoeppner, V. Chandrasekaran, and C. B. Elliot III, Eds., American Society for
Testing and Materials, West Conshohocken, PA, 2000, pp. 65-79.
[11] VanStone, R. H., Lawless, B. H., and Hartle, M., "Fretting in Ti~6A1-4V at Room
Temperature," Proceedings of 5th National Turbine Engine High Cycle Fatigue
(HCF) Conference, 2000, Session 4. paper 1.
[12] Chakravarty, S., et al., "The Effect of Surface Modification on Fretting Fatigue in Ti
Alloy Turbine Components," JOM, Vol. 47, No. 4, 1995, pp. 31-35.
[13] Hoeppner, D., Adibnazan, S., and Moesser, M. W., "Literature Review and
Preliminary Studies of Fretting and Fretting Fatigue Including Special Applications to
Aircraft Joints," DOT/FAA/CT-93/2, Defense Technical Information Center, Ft.
Belvoir, VA, 1994.
[14] Hutson A. L. and Nicholas, T., "Fretting Fatigue Behavior of T1-6A1-4V Against Ti-
6AI-4V Under Flat-on-Flat Contact With Blending Radii," Fretting Fatigue: Current
Technology and Practices, ASTM STP 1367, D. W. Hoeppner, V. Chandrasekaran,
and C. B. Elliot III, Eds., American Society for Testing and Materials, West
Conshohocken, PA, 2000, pp. 308-321.
[ 15] Miyoshi, K., et al., "Sliding Wear and Fretting Wear of Diamondlike Carbon-Based,
Functionally Graded Nanocomposlte Coatings," Wear, Vol. 225-229, 1999,
pp. 65-73.
[17] Donachie, M. J. (Ed.), Titanium and Titanium Alloys, Source Book, American
Society for Metals, Metals Park, OH, 1982.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Shankar Mall]* Vinod K. Jain, 2 Shantanu A. Namjoshi, 3 Christopher D. Lykins 4
Reference: Mall S., Jain V. K., Namjoshi S. A., and Lykins C. D., "Fretting Fatigue
Crack Initiation Behavior of Ti-6AI-4V," Fretting Fatigue: Advances in Basic
Understanding and Applications, STP 1425, Y. Mutoh, S. E. Kinyon, and D. W.
Hoeppner, Eds., ASTM International, West Conshohocken, PA, 2003.
Abstract: Fretting fatigue crack initiation behavior of titanium alloy, Ti-6A1-4V was
investigated by using different geometries of the fretting pad. Specimens were examined
to determine the crack initiation location and the crack angle orientation along the contact
surface. Fretting fatigue experiments were analyzed with the finite element analysis.
Several critical plane based parameters were used to predict the number of cycles to
fretting fatigue crack initiation, crack initiation location and crack orientation angle along
the contact surface. These predictions were compared with the experimental counterparts
to study the role of normal and shear stresses on the critical plane in order to characterize
fretting fatigue crack initiation behavior. From these comparisons, the fretting fatigue
crack initiation mechanism in the tested titanium alloy appears to be governed by the
shear stress on the critical plane. However, the role of normal stress on the critical plane
at present appears to be unclear.
Keywords: fretting fatigue, titanium alloy, crack initiation, critical plane parameters
Introduction
Aircraft engine components are currently less prone to the failures associated with
i Air Force Research Laboratory, Materials and Manufacturing Directorate, Wright Patterson AFB, OH
45433-7817, *To whom correspondence be addressed at AFIT/ENY, Bldg. 640, 2950 P. St., Air Force
Institute of Technology, Wright-PattersonAFB, OH, 45433-7765, emad: Shankar.Mall@afit.edu.
2 Mechanical and Aerospace Engineenng Department,University of Dayton, Dayton, OH 45469-0210.
3Department of AeronauUcs and Astronautics, Atr Force Institute of Technology, Wright-PattersonAir
Force Base, OH 45433-7765.
4Formerly with Air Force Research Laboratory,Aero Propulsion and Rockets Directorate, Wright
Patterson AFB, OH 45433-7251.
338
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MALL ET AL. ON CRACK BEHAVIOR OF TI-6AL-4V 339
low cycle fatigue (LCF) as a great deal of attention has been paid to the LCF area over
the last two decades [1,2]. On the other hand, high cycle fatigue (HCF) has received
much less attention and has resulted recently in higher incidence of failures related to
HCF in many military aircraft engines. Under HCF conditions, engine components
experience high frequency, vibrational type loads, often superimposed on a high mean
stress. There is a lack of understanding of materials response and capability in the
presence of in-service damage under HCF loading conditions. In the LCF arena, the
"damage tolerant" approach has worked well where the remaining life is predicted from
the crack propagation of an inspectable flaw size to a critical size. The direct extension of
such an approach to HCP is a challenging task since a large fraction of life is spent during
the crack nucleation and growth to a detectable size, and a very small fraction of life is
spent in crack propagation from the detectable or inspectable flaw size to a critical size.
Fretting fatigue related failures in disk/blade attachments are one of the most insidious
problems related to HCF in gas turbine engines. It is further exacerbated by the difficulty
in detecting fretting fatigue crack initiation and propagation. Fretting is the process that
occurs from the relative surface displacements, on the micro-scale (i.e. of the order of
microns), at the interface between two mating components subjected to fatigue in the
presence of normal pressure. Fretting acts as a damage generator that leads to crack
nucleation, growth to a detectable size and propagation on the surface or subsurface level
between two mating components, generally at a fraction of fatigue lives under the plain
fatigue condition. In HCF failures, crack propagation does not constitute a large part of
life and hence its analysis using a damage tolerant approach may not be applicable. In
HCF failures a major part of the life is spent in 'crack initiation', which is the sum total
of crack nucleation and growth to a detectable size. Thus, the long-term goal of this study
is to develop an understanding of the high cycle fretting fatigue related failures in
dovetail joints.
There have been several phenomenological life prediction models proposed [3-8],
where fretting fatigue life predictions are made based on the life debit due to fretting
(correlated using one or more test variables) as compared to plain fatigue. The presence
of applied normal, tangential and axial loads during fretting causes a stress magnification
at the edge of contact. Researchers have proposed fracture mechanics methods, where
this stress intensity factor can be used to determine loading conditions that could lead to
crack growth and arrest behavior [9,10,11] or the onset of fretting fatigue crack
propagation [12]. However, in these methods, either an initial crack length and/or the
crack orientation are assumed or an estimate of threshold (or maximum allowable value)
of the flaw size that can be tolerated for infinite fretting fatigue life is provided.
Currently, these approaches do not provide/predict the remaining life or life consumed to
reach a certain initial crack length.
Two parameters, specifically developed for the fretting fatigue condition, are based on
the work done by the frictional force between contacting bodies [13]. The first
parameter, a measure of the frictional energy expenditure density, is defined as the
maximum value of the product of the shear stress ('c) and the slip amplitude (5) at the
contact surface between two bodies. The second parameter; a modification to the first
parameter recognizing the fact that crack nucleation in fretting fatigue can also depend on
the maximum tangential stress, r on the interface; is defined as the maximum value of
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
340 FRETTINGFATIGUE: ADVANCES
c~T'cS. There has been mixed success in predicting the location, orientation, and initiation
time for the fretting fatigue crack using this approach [14,15].
Researchers have also used characteristic descriptions of the local conditions (such as
extrusion of material a l o n g persistent slip bands, dislocation glides along the
crystallographic slip planes etc) to model crack nucleation mechanisms [16,17]. These
micro level approaches are desirable from a fundamental point of view but are not
sufficiently developed for use in industry. Crack initiation in fretting fatigue can be
modeled by correlating the number of cycles to develop a crack of a certain size with
continuum field variables or some parameters dependent on the state of cyclic stress or
strain, or any combination of these. This approach though empirical, has potential to
bring in the physics of crack formation into the analysis.
Many models/criteria/parameters have been proposed for fatigue crack initiation under
the multiaxial stress state, which is the case in fretting fatigue [18]. A majority of the
current multiaxial fatigue approaches can be grouped into two main categories: a)
equivalent (invariant) stress models (such as Goodman, Gerber, Soderberg relations, yon
Mises equivalent stress amplitude, Modified Manson-Mcknight etc.), and b) critical plane
models [19, 20]. The equivalent stress models require the determination of an equivalent
cyclic scalar parameter often in terms of mean stress to be used in conjunction with
uniaxial stress versus fatigue life data, while the critical plane models have been
developed based on observations that fatigue cracks often nucleate on a particular plane.
In the critical plane models, a combination of normal and shear stresses (strains) on the
critical plane can be used to model crack initiation. It is hypothesized that shear stresses
induce dislocation movement along slip lines, causing nucleation and growth of cracks
while normal stresses open the crack and reduce the friction between the crack surfaces.
The critical plane methods have the distinct advantage that they predict the orientation of
crack, and they have a potential for providing an estimate of the crack size. Thus, the
combination of critical plane methods and fracture mechanics approaches could
eventually provide the total (i.e. the sum of nucleation, initiation and propagation)
fretting fatigue crack behavior.
In the past, Szolwinski and Farris [21] proposed a critical plane approach for fretting
fatigue based on a plain fatigue approach developed by Smith et al [22] which was
formulated to account for the stress ratio (or the mean stress) effects. Their modified
parameter assumed that crack initiation occurs on the plane where the product of normal
strain amplitude, ca, and maximum normal stress, CYmax,is the maximum. Neu et al [23]
found that for PH-13-8 Mo steel, the normal stress dominated Smith-Watson-Topper
(SWT) [23] critical plane parameter predicted the crack location well but not the initial
crack orientation while the shear stress dominated Fatemi-Socie (FS) parameter [24]
predicted not. only the location but also the orientation of the primary fretting fatigue
crack. The present authors observed similar features with the SWT critical plane
parameter in titanium alloy, Ti-6AI-4V [25], hence proposed a shear stress based critical
plane parameter [26]. The fretting crack location as well as orientation was effectively
characterized by this parameter involving the maximum shear stress range along with the
local shear stress ratio effect on a critical plane. However, it has been observed that both
the shear and normal stresses may play a role in the crack initiation under multiaxial
fatigue conditions, e.g. Van and Maitournam have shown that fretting fatigue may be
characterized by the shear amplitude and hydrostatic pressure on a critical plane [27].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MALL ET AL. ON CRACK BEHAVIOR OF TI-6AL-4V 341
Experiments
Test Setup
The fretting setup used in this study incorporated a rigidly mounted fretting fixture on
a servo-hydraulic fatigue test machine, as shown in Figure 1. This test-set was capable to
apply cyclic axial stress, O'ax~aI and cyclic shear load, Q on the test specimen, while the
normal load, P was held constant. This setup is capable of testing up to a frequency of
200 Hz, and it has one load cells on each side of the specimen so that all of the applied
(or) and reacted (Q) forces can be recorded at any point of interest during the test. A
detailed explanation of the experimental setup is provided in a previous study [28].
I't ............. i l l
I,.....
~ i i i Lateral Springs L__J P
Pressure Transduc'e?...........................I~ - -
~ * ~axial
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
342 FRETTINGFATIGUE: ADVANCES
Three types of pads (two cylindrical and one Hat with edge radii) were used. Figure 2
shows a schematic of the dogbone specimen used in this work The cylindrical pads had
radii of 50.8 mm and 101.6 ram, while the flat pad had an edge radius of 5.08 mm with a
flat center section of 5.08 ram. The latter geometry of the pad was selected to simulate
contact geometry in the dovetail joint of gas turbine engines. The specimens and pads
were machined by the wire electrical discharge method from Ti-6A1-4V forged plates
which had been preheated and solution treated at 935~ for 105 minutes, cooled under
flowing air, vacuum annealed at 705~ for 2 hours, and then cooled under flowing argon.
This resulted in a duplex microstructure consisting of 60% (volume) of primary-c~ (hcp)
and 40% (volume) of transformed-13 (c~ platelets in a 13 matrix - bcc) phases with a grain
size of about 10 btm. The longitudinal tensile properties (along the loading axis) were
determined to be elastic modulus = 127 GPa and yield strength = 930 MPa. The fretting
fatigue specimen had thickness, 2b = 1.93 mm and width, w = 6.35 rnm.
0.64cm
1.27cm
5.59cm a..-km
l .70cm ,,
Test Details
Constant amplitude fretting fatigue tests were conducted at 200 Hz, over a wide range
of axial stress levels, ~axial,~x = 400 MPa to 700 MPa with stress ratios, R, ranging from a
nominal value of 0.0 to 0.7. The normal load for both the cylindrical pad with 50.8 mm
radius and the flat with edge radii pad was 1.33 kN which resulted in the peak normal
pressure of 304 MPa and 961 MPa respectively. The normal load for the cylindrical pad
with 101.6 mm radius was 2.22 kN which resulted in the peak normal pressure of 267
MPa. The coefficient of friction was determined to be 0.5 for this experimental
configuration by Iyer and Mall [29].
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MALL ET AL ON CRACK BEHAVIOR OF TI-6AL-4V 343
The finite element method was used to determine stress, strain and displacement fields
at the contact interface. The analysis used was similar to that in a previous study [30].
Four node, plane strain quadrilateral elements were used with the "master-slave"
interfacial algorithm developed for contact modeling in the finite element code,
ABAQUS [31]. The measured loads were applied to the model in three steps. The
normal load, P was applied in the first step. In the second step, the maximum tangential
load, Qmaxand the maximum axial stress, O'axlal,rnaxwere applied to match the experimental
maximum cyclic load condition. Finally in the third step, the mimmum tangential load,
QmH1and minimum axial stress, O'axlal,rmn were applied to match the experimental minimum
cyclic load condition.
Damage Mechanisms
The main or primary crack, which caused failure in all specimens, initiated at the
contact surface and near the trailing edge of contact. Other small secondary cracks were
also observed. However, these did not grow enough to cause any specimen failure.
Several specimens were sectioned to investigate the primary and secondary crack
orientations and locations. The experimentally observed primary crack orientations
angles were either -450 or 450 with a variation of -+ 15o from a perpendicular to the
loading direction [26]. Figure 3 shows a typical initiation orientation and propagation
path of the primary crack. The primary crack in this specimen was initially oriented at
the interface at an angle, 0 = -30 ~ initially and then at 0 = -43 ~ where negative angles are
measured in clockwise direction from the perpendicular to the direction of applied axial
Figures 3 and 4 - Primary (Fig 3) and Secondary (Fig. 4) Crack Growth Path in
Specimens Tested with 101.6 mm and 50.8 mm Cylindrical Pads respectively.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
344 FRETTING FATIGUE: ADVANCES
stress. The crack propagated in a tortuous manner until it reached a depth of about 91
~tm. At this location the crack orientated perpendicular to the axial stress, 0 = 0 ~ Figure
4 also shows a typical secondary crack, which orientated at the contact interface at an
angle, 0 = 29 ~ It should be noted that the cracks shown in Figures 3 and 4 have
initiated/propagated in both intergranular and transgranular manners. Similar features
were noted with other specimens. Thus, the grain boundaries were not the preferred
location/direction for crack initiation/propagation in the tested specimens. Further, this
behavior about crack initiation and orientation was independent of the fretting pad
geometry.
The fretting fatigue data, i.e. the applied stress versus fatigue life are compared to the
plain fatigue life data in Figure 5. Both sets of these data were generated at different
stress ratios. It is well documented in the fatigue literature that there is a mean stress or
stress ratio effect on the fatigue life or strength. There are several ways this effect can be
accounted for. In this study, a method suggested by Walker was used [32], which is as
follows:
where I~effectlve is the effective stress taking into account the stress ratio effect, Otnaxis the
maximum applied stress on the specimen, R is the stress ratio and m is a fitting
parameter, which was determined to be 0.45 in a previous study [26]. The resulting fit to
the plain fatigue life data is shown as a solid line in Figure 5. The plain fatigue data,
lOOO ~ ~ R =50.8 mm
9 R = 101.6 mm
800 O Flat Pad
- - Plain Fatigue
600'
2e0
,, . . . . . . . . L . . . . . . .
Figure 5 - Effective Stress versus Life Relationships for Fretting Fatigue from Three Pad
Geometries and Plain Fatigue
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MALL ET AL. ON CRACK BEHAVIOR OF TI-6AL-4V 345
obtained from R values ranging from -1.0 to 0.5, are not shown for the sake of clarity.
This relationship can be expressed as an exponential function containing two terms as:
where C1, C2, C3 and C4 are fitting parameters. The constants in equation (2) were
obtained by using the best fit to the plain fatigue data, which provided Cl = 4.51x105
MPa, C2 = -0.720, C3 = 246 MPa and C4 = 5.81x10 3. This comparison clearly shows that
there is a reduction in the fatigue life under the fretting condition as expected. However,
this type of comparison is of a simplistic nature, as it does not provide any mechanistic
basis for estimating life debit due to fretting. Further, this direct comparison based on the
stress applied to the specimen does not account for the two very important factors; a) the
stress magnification in the contact region under the fretting condition and b) the
multiaxial loading effects also under the fretting condition. Therefore, multiaxial fatigue
parameters are considered next.
O R = 50.8 mm
9 R=101.6mm
~4 9 Flat Pad
l~ ~ Plain Fatigue
lira . . . . 3x Lower Bound
O <> <~"; . . . . 3x Upper Bound
~2
[.,,
Szolwinskl and Farris [21] modified the Smith-Watson-Topper parameter for the
fretting fatigue crack initiation. This modified parameter assumed that crack initiation
occurs on the plane where the product of normal strain amplitude, ~, and maximum
normal stress, ~r~ax is the maximum. Using the computed stresses and strains from the
finite element analysis of the fretting fatigue experiments, this parameter was calculated
at all planes ranging from -90 ~ < 0 < 90 ~ in increments of 0.1 ~ which provided this
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
346 FRETTINGFATIGUE: ADVANCES
parameter's maximum value, location and critical plane orientation. The measured
fretting fatigue life data were then plotted as a function of SWT parameter along with the
counterpart from the plain fatigue condition (Figure 6). This clearly shows that the
majority of the fretting fatigue crack initiation life data lie within -+3Ni scatter bands of
the plain fatigue life data. In other words, the fretting fatigue crack initiation life can be
predicted from the SWT versus fatigue life relationship of the plain fatigue. In addition,
the predicted crack location was determined to be near the trailing edge of the contact
based on this approach, which was in good agreement with experimental observations.
Further, the predicted angle of crack orientation based on this approach at the contact
surface was within +5~ +8 ~ of the perpendicular to the applied loading direction, and
these were not in agreement with experimental crack orientations. This clearly shows that
this parameter has the limitation in this respect.
In this approach, the maximum and minimum shear stresses were computed on all
planes ranging from -90 ~ _< (9 _< 90 ~ in 0.1 ~ using the computed stresses and strains
obtained from the finite element analysis. From this, the critical plane and magnitude of
the maximum shear stress range, A ~ c n t = qTmax - "Crmnwas obtained. Then the shear stress
ratio effect on the critical plane was accounted for by incorporating a technique proposed
by Walker [32], which is expressed as:
where '[maxis the maximum shear stress on the critical plane, R~ is the shear stress ratio on
the critical plane, and m is a fitting parameter, which was determined to be 0.45 from the
plain fatigue data. The measured fretting fatigue life data are plotted as a function of the
parameter, Azc~,t,effec~ve(Figure 7). As can be seen, the majority of the fretting fatigue data
lie within +3N, scatter bands of the plain fatigue data. Hence, this parameter can be also
used to predict the fretting fatigue life from the plain fatigue data in conjunction with an
analysis.
It should be noted that the maximum shear stress range occurs on two planes, one in
the positive quadrant (i.e. from 0 ~ to 900 from the perpendicular to the loading direction,
Figure 3) and the other in the negative quadrant (i.e. from 0 ~ to -90o from the
perpendicular to the loading direction). For each state of stress, there are thus two critical
shear stress planes, which are at 90 ~ to each other and either of the two orientations is
equally possible, however local variation in microstmctural properties may cause one
orientation to be preferred. The orientation of primary cracks at the contact surface
predicted from this approach was either from +450 to +500 or from -450 to -500 which
correlated well with the experimental observations. Furthermore, the predicted crack
initiation location agreed with the experimental results and it was determined to be near
the trailing edge of the contact.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MALL ET AL. ON CRACK BEHAVIOR OF TI-6AL-4V 347
8OO
O R = 2 inch
700 9 R = 4inch
O Flat Pad
-- Plain Fatigue
6O0
.... 3x Lower Bound
.... 3x Upper Bound
5O0
400
8 II
300
O
2O0
100 i , J i , r , l t i , J i , r l , [ r i J , F , l , I
Figure 7 - Shear Stress Range Critical Plane Parameter versus Life Relationships for
Fretting Fatigue from Three Pad Geometries and Plain Fatigue
Findley Parameter
The crack initiation in the multiaxial fatigue loading should be influenced by both
normal and shear stresses (strains). The previous approach is primarily a shear stress
based approach. In order to investigate the effect of the normal stress on the critical
plane, a multiaxial fatigue approach on the critical plane, where normal stresses (strains)
is included explicitly, was also considered in this study. One of these is the Findley
parameter, (FP) [33]. In this approach, crack initiation is assumed to be governed by both
the maximum shear stress amplitude, za = (%ax - "c~n)12 and maximum stress normal to
orientation of the maximum shear ((Ymax)multiplied by an influence factor, k, as shown in
the following. The k was determined to be equal to 0.35 from the plain fatigue data [25].
FP = ~a + kCYmax (4)
The Findley parameter, FP was calculated at all planes ranging from -90 ~ _< 0 < 90 ~ in
0.1 ~ from the computed stresses and strains obtained from the finite element analysis.
These calculations provided the critical plane where this parameter was the maximum.
The measured fretting fatigue crack initiation life data were plotted as a function of this
parameter (Figure 8), along with the corresponding relationship for the plain fatigue data.
In this case, the FP versus fatigue life relationships for the plain fatigue and fretting
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
348 FRETTINGFATIGUE: ADVANCES
fatigue did not agree with each other showing that this parameter can not be used to
predict the fretting fatigue lives from the plain fatigue data. However, fretting fatigue
data from different geometries were in agreement with each other within a scatter band.
Further, the predicted angle of crack orientation based on this approach at the contact
surface was within +50 to +25 o of the perpendicular to the applied loading direction. The
predicted crack initiation location was near the trailing edge. This shows that this
parameter has these two limitations, i.e. it did not predict the fretting fatigue life from the
plain fatigue data well, and the predicted crack orientations were different from than
those observed experimentally.
700
<> R = 50.8 mm
600 9 R = 1 0 1 . 6 mm
9 Flat Pad
~ 500 - - Plain Fatigue
400
300 o O
O
200 o o % <>
Figure 8 - Findley Parameter versus Life Relationships for Fretting Fatigue from Three
Pad Geometries and Plain Fatigue
To overcome the above shortcoming of the Findley parameter, shear stress range
critical plane parameter was modified in the form similar to Findley parameter to account
the normal stress that generally aids in opening the crack surfaces. This modified version
of shear stress range critical plane parameter, MSSR is expressed as follows:
In this approach, the first term, A'ITcritis the same as in equation 3 and the second term
is the maximum normal stress on the critical plane. The constants, A, B, C and D were
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MALL ET AL. ON CRACK BEHAVIOR OF TI-6AL-4V 349
obtained by curve fitting. The measured fretting fatigue life data are plotted as a function
of the MSSR parameter (Figure 9). As can be seen, the majority of the fretting fatigue
data lie within +3N, scatter bands of the plain fatigue data. Hence, this parameter can be
also used to predict the fretting fatigue life from the plain fatigue data in conjunction with
an analysis. Furthermore, this modified parameter predicted angle of crack orientation
and crack location which were same as in the case of the shear stress range critical plane
parameter, and these were in agreement with their experimental counterparts as stated
earlier. Finally, this modified parameter explicitly included the effects of the shear stress
as well as normal stress as it is should be the case in multiaxial fatigue loading.
80
:x•._-
. %
".. (30 ~
%
"'.
".
"..
<> R = 2Inch
9 R = 4inch
O Flat Pad
Plain Fatigue
,., 6O
""._ c ~ " ~ ""., - " - "3x Lower Bound
"'"-. ----3x UpperBound
O
40
:~ 20
M S S R = AA~:~ + C~DNormal
(A=0.5, B=0.75, C=0.35, D=0.5)
0 I I I I I [ I I ] I I I I I I I I I I I [ I d I I I ] I I I I I I I I
Summary
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
350 FRETTINGFATIGUE: ADVANCES
counterparts. Further, the Findley parameter, a critical plane approach involving both
normal and shear stresses (or both tensile and shear cracking) predicted the cycles to
fretting fatigue crack initiation and crack orientation which were not in agreement with
their experimental counterparts. Hence, a critical plane parameter involving both normal
and shear stresses (or both tensile and shear cracking) is proposed that predicted the
cycles to fretting fatigue crack initiation, crack initiation location, and crack orientation
which were in agreement with their experimental counterparts. From these observations,
it appears that that fretting fatigue crack mechanism in the tested titanium alloy is
governed by the shear stress on the critical plane. However, the role of the normal stress
on the critical plane upon the fretting fatigue crack initiation behavior appears to be
unclear from this study, and hence more experiments involving various pad geometries
and loading conditions are needed to investigate this phenomenon.
AcknowLedgment
The authors would like to gratefully acknowledge the computer support for this study
provided by The Ohio Supercomputer Center (OSC).
References
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
MALL ET AL. ON CRACK BEHAVIOR OF TI-6AL-4V 351
[9] T. Lindley and K. Nix, "The Role of Fretting in the Initiation and Early Growth of
Fatigue Cracks in Turbo Generator Materials", Multiaxial Fatigue, ASTM, 1985,
pp. 340-360.
[10] K. Nix and T. Lindley, "The Application of Fracture Mechanics to Fretting
Fatigue", Fatigue and Fracture of Engineering Materials and Structures, Vol. 8,
No.2, 1985, pp. 143-160.
[11] A.E. Giannakopoulus, T. C. Lindley and S. Suresh, "Aspects of Equivalence
Between Contact Mechanics and Fracture Mechanics: Theoretical Connections
and a Life-Prediction Methodology for Fretting Fatigue", Acta Materialla, Vol.
46, 1998, pp. 2955-2966.
[12] S. Faanes and U. Fernando, "Life Prediction in Fretting Fatigue using Fracture
Mechanics", Fretting Fatigue, Mechanical Engineering Publications, London,
1994, pp. 149-159.
[13] C. Ruiz, P. H. B. Boddington and K. C. Chen, "An investigation of fatigue and
fretting in a dovetail joint", Experimental Mechanics, Vol. 24, 1984, pp. 208-217.
[14] D. Nowell and D. A. Hills, "Crack Initiation Criteria in Fretting Fatigue", Wear,
Vol. 136, 1990, pp. 329-343.
[15] C.D. Lykins, S. Mall and V. K. Jain, "An evaluation of parameters for predicting
fretting fatigue crack initiation", International Journal of Fatigue, 20, 2000, pp.
703-716.
[16] M. Kuno, R. B. Waterhouse, D. Nowell, and D. A. Hills, "Initiation and growth of
fretting fatigue cracks in the partial slip regime", Fatigue and Fracture of
Engineering Materials and Structures 12/5, 1989, pp. 387-398.
[17] C.H. Gob, R. W. Neu, and D. L. McDowell, "Shakedown, Ratchetting, and
Reversed Cycle Plasticity in Fretting Fatigue of Ti-6A1-4V Based on Polycrystal
Plasticity Simulation", presented at the 6th National Turbine Engine High Cycle
Fatigue Conference, Jacksonville, FL, 5-8 March 2001.
[18] A. Krgo, A. R. Kallmeyer, and P. Kurath, "Evaluation of HCF Multiaxial Fatigue
Life Prediction Metrologies for Ti-6A1-4V", Proceedings of the 5th National
Turbine Engine High Cycle Fatigue Conference, Arizona, 2000.
[19] J.E. Shigley and C. R. Mischke, "Mechanical Engineering Design", McGraw-
Hill, New York, 1989.
[20] J. Morrow, "Fatigue Design Handbook", SAEAE-6, J. A. Graham, Ed., Society of
Automotive Engineers, 1968, pp. 17-58.
[21J M. Szolwinski and T. Farris, "Mechanics of fretting fatigue crack formation",
Wear, Vol. 198, 1996, pp. 93-107.
[22] R.N. Smith, P. Watson, and T. H. Topper, "A Stress-Strain Function for the
Fatigue of Metals", Journal of Materials, JMLSA, Vol. 5, 1970, pp. 767-778.
[23] R. Neu, J. Pape, D. Swalla-Michaud, "and Methodologies for Linking Nucleation
and Propagation Approaches for Predicting Life Under Fretting Fatigue", Fretting
Fatigue: Current Technology and Practices, ASTM 1367, D. Hoeppner, V.
Chandrasekaran and C. Elliot, Eds. American Socaety for Testing and Materials,
1999.
[24] A. Fatemi and D. Socie, "A critical plane approach to multiaxial fatigue damage
including out of phase loading", Fatigue and Fracture of Engineering Materials
andStruetures, Vol. 11, 1988, pp. 149-165.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
352 FRETTINGFATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
S. Shirai, ~ K. Kumuthini, 1 Y. Mutoh, t and K. Nagata 2
REFERENCE: Shirai, S., Kumuthini, K., Mutoh, Y. and Nagata, K., "Fretting Fatigue
Characteristics of Titanium Alloy Ti-6AI-4V in Ultra High Cycle Regime," Fretting
Fatigue: Advances of Basic Understanding and Applications, ASTM STP 1425, Y. Mutoh,
S. E. Kinyon, and D. W. Hoeppner, Eds., ASTM Intei-national, West Conshohocken, PA,
2003.
ABSTRACT: In the present study, fretting fatigue behavior of a Ti-6AI-4V alloy under
high stress ratios in the ultra high cycle regime (up to 109 cycles) has been investigated.
The slope of S-N curve decreased with increasing stress ratio. The slope was steeper in
short fatigue life region and became flatter in longer life region. The test results under
various stress ratios followed the modified Goodman diagram for both the fatigue
strengths defined at 10 7 cycles and l0 s cycles. The so-called non-propagating cracks,
which were often observed in steels and ahtminum alloys, could not be found in the
run-out specimens tested up to 107 cycles. In the further loading cycles up to 109 cycles at
the same stress amplitude, no crack initlahon and propagation could be observed, which
indicated that the conventional fretting fatigue strength defined 10 7 cycles was still
effective at least up to 109 cycles. Different behavior between the titanium alloy used and
the other materials mainly results from the different crack initiation behavior.
KEYWORDS" fretting fatigue, mean stress, stress ratio, ultra high cycle, titanium alloy
Introduction
Titanium alloy has been increasingly applied to steam turbine components as well
as gas turbine components due to its excellent specific strength, corrosion resistance, etc.
In these applications, the components such as blades suffer a high centrifugal force with
vibrating loads, which produces a high cycle fatigue condition with high mean stress. It is
also known that endurance lives in service are 108-109cycles for car engines, 109cycles
for high-speed trains and 10 ~~ cycles for aircraft engines, which are further longer than
the endurance life of 107 cycles in conventional fatigue tests. Therefore, fatigue behavior
under high stress ratio as well as in the ultra high cycle regime should be understood for
estimating fatigue lives of these components in service.
353
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
354 FRETTINGFATIGUE: ADVANCES
Since 1970, many researches have been devoted in fretting fatigue of titanium
alloys [1-11]. Fretting fatigue behavior of titanium alloys has been discussed in detail
from both microstructural and mechanical points of view. However, detailed fretting
fatigue processes, such as how long the crack initiation stage is, have not yet been clear.
Effect of high mean stress on fretting fatigue behavior has also not yet been obvious.
Since no report on fretting fatigue test over 108 cycles has been available, fretting fatigue
behavior in the ultra high cycle regime has not yet been understood. There are several
topics to be solved in fretting fatigue in the ultra high cycle regime: existence of fatigue
limit, change of fatigue fracture mechanisms, non-propagating crack, etc.
In the present study, fretting fatigue tests at stress ratios o f - l , 0.5 and 0.7 up to 108
cycles and at a stress ratio o f - 1 up to 109 cycles were conducted. Fretted surfaces and
longitudinal cross-sections of tested specimens were observed in detail to discuss the
effect of high stress ratio and the fretting fatigue crack initiation and propagation
behaviors in the ultra high cycle regime.
Experimental Procedures
The material used for the specimen was a Ti-4AI-6V alloy, which was also used for
the contact pad. Chemical composition and mechanical properties of the material are
shown in Tables 1 and 2, respectively. Figure 1 shows a microstructure of the material.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SHIRAI ET AL. ON ULTRA HIGH CYCLE REGIME 355
Shapes and dimensions of the fretting fatigue specimen and the contact pad are
shown in Fig. 2. A pair of contact pads was clamped against the opposite flats of the
fretting fatigue specimen using a calibrated proving ring, as schematically illustrated in
Fig. 3. The contact pads were mounted in the clamping jig. The contact pressure of
I00MPa was applied to the contact pads. The clamping load was measured with strain
gages bonded to the proving ring. The relative slip amplitude between the contact pad
and the specimen was monitored by calibrated extension meters of the type shown in Fig.
3. The frictional force (tangential force) between the contact pad and the specimen was
also measured by strain gages bonded at the neck part of the clamping jig. The tests were
performed in air at frequencies of 20 Hz for ~10 7 cycles and 30-47 Hz for ~10 S cycles
using a conventional servo-hydraulic testing machine. The test up to 10 9 cycles was
conducted at a frequency of 340 Hz using a newly developed electro-dynamic fatigue
machine. The effect of frequency was checked by comparing three kinds of fretting
fatigue test results at the stress amplitude of 270 MPa under R=-I: the fretting fatigue life
at a frequency of 340 Hz was 9.2 • 104 cycles and that of frequency alternating test for
2O0
s e c t i o n A- AJ4:13
Proving ring
~/,/
l J,/
Specimen
~ ' - - - l r ~ Extenso- m e t e r
~ " (for measuring relative slip)
~ ~ Strain gauge
w (for measuring tangential f o r c e )
$
Fig.3-Schematic illustration of Frettingjig
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
356 FRETTING FATIGUE: ADVANCES
each 104 cycles between 30 Hz and 340 Hz was 7.9x104 cycles, which were in good
agreement with that at 30 Hz (1.2 x 10s cycles).The stress ratios were -1, 0.5 and 0.7 to
investigate the fretting fatigue strengths at high stress ratios. The cracks on the fretted
surface and the fretting fatigue crack path on the longitudinal cross-section of the
specimens tested were observed using a scanning electron microscope (SEM) in detail.
Results
S - N curve
The S-N curves for the Ti-6A1-4V alloy are shown in Fig. 4. From the figure, the
following characteristics can be pointed out:
(1) The slope of S-N curve was different between regions below and above 107 cycles:
The steeper slopes in the region below 107 cycles were observed, while the slopes in the
region above 107 cycles were almost flat.
(2) In the region below 107 cycles, the slope decreased with increasing the stress ratio.
(3) The fretting fatigue strengths defined at 107 cycles were 130MPa for R=-I, 100MPa
for R=0.5 and 80MPa for R=0.7. Those defined at 108 cycles were 130MPa for R=-I,
90MPa for R=0.5 and 70MPa for R=0.7. (The fatigue strength is defined as follows: if
the two data points at the same stress amplitude are available, the fatigue strength is the
stress where one is failure and the other run-out. If only one data point is available, the
fatigue strength is the stress for run-out.)
(4) The specimen tested at 130MPa, which was the fatigue strength defined at 107 cycles,
survived up to 109 cycles.
I I
OC o R=-I
9 R=0.5
R=0.7
0
_~oc 0 0 9
E
o g__;
}oc ~176176
o ,~ o--)
I I I I I
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SHIRAI ET AL. ON ULTRA HIGH CYCLE REGIME 357
The modified Goodman diagram obtained from the S-N curves is shown in Fig. 5. It
can be seen from the figure that the data points are well laid along a straight line of the
Goodman diagram for both the fatigue strengths defined at 107 cycles and at 108 cycles.
Both tangential force and relative slip amplitude were unstable up to initial few
hundreds cycles. However, after that, they are stable and almost constant during fretting
fatigue tests until failure or run-out. Relationship between tangential force and stress
amplitude is shown in Fig. 6, where stable values of tangential force are plotted. From the
figure, it seems that tangential force depends on stress amplitude regardless of stress
ratio.
9 5ol- \\ -
z~ 6O
9 o
-~ 40
%oo
I
E
20 mim 9 R=-I
o R=O.5
9 R=0.7
I I i l i
] O0 200 300
Slress amplitude C~a[MPa]
Fig.6 Tangential force vs. stress amplitude
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
358 FRETTING FATIGUE: ADVANCES
30
~g
A"
ed
2o O
E
r~
O o
~10
.=> 9 R~i
o)
o R=0.5
t~ 9 R=0.7
o I I i I I
100 200 300
Stress amplitudeOa[MPa]
Fig.7-- Relative slip amplitude vs. stress amplitude
Relationship between relative slip amplitude and stress amplitude is shown in Fig. 7,
where stable values of relative slip amplitude are also plotted. As can be seen from the
figure, relative slip amplitude depends on stress amplitude regardless of stress ratio.
These behaviors result from that mean stress is static and only stress amplitude induces
relative movement between the specimen and the contact pad.
Observations of Fretted Surface and Longitudinal Cross section of the Specimens Tested
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SHIRAI ET AL. ON ULTRA HIGH CYCLE REGIME 359
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
360 FRETTINGFATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SHIRAI ET AL. ON ULTRA HIGH CYCLE REGIME 361
The transition of crack initiation site from surface to subsurface in high strength
alloys has been often observed at 106-108 cycles under high cycle fatigue without fretting
[12-19]. This corresponds to the change of crack initiation mechanism from the
extrusion-intrusion to the internal defect, which induces high local stress concentration.
Selection of the two mechanisms is competitive depending on stress level, size and shape
of defect, cyclic deformation behavior, etc. The transition also introduces a knee followed
by a rather sharp drop in S-N curve [18]. Subsurface crack origins of titanium alloys are
often cleavage facets because of their high purity [14-19], while those of high strength
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
362 FRETTINGFATIGUE: ADVANCES
The slope of S-N curve in fretting fatigue of titanium alloy, which is steeper in
shorter life region, becomes more flat in longer life region, as can be seen from Fig. 4.
The similar change of slope in fretting fatigue has been found in aluminum alloys [22,23],
a rotor steel [20] and a carbon steel [29]. The deformation of contact edge between the
specimen and the contact pad can be categorized in three types: a) sticking, b) slipping
and c) gapping. Based on the detailed analysis [30], no singular behavior at the contact
edge can be found in case of gapping. Stror~ger stress singhlarity at the contact edge was
found in case of slipping compared to the case of sticking. The deformation type depends
on many parameters: rigidity of contact pad, contact pressure, stress amplitude, relative
slip amplitude, etc. When the stress amplitude decreases, the deformation type is
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SHIRAI ET AL. ON ULTRA HIGH CYCLE REGIME 363
changing from slipping to sticking, that is the stress singularity at contact edge becomes
weaker. This change of deformation type and then the change of stress singularity at
contact edge will be one of the reasons for changing the slope of S-N curve in fretting
fatigue.
Conclusions
Fretting fatigue behavior of a Ti-6A1-4V alloy under high stress ratios and in the very
high cycle regime was investigated. The main conclusions obtained are summarized as
follows.
1) Fretting fatigue strengths with various stress ratios defined both 10 7 cycles and 108
cycles were followed the modified Goodman diagram.
2) Surface cracks on the fretted surface of both the fractured and the run-out specimens
could rarely be found in Ti-6A1-4V alloy, suggesting that once a crack nucleates, it
grows rapidly to final failure.
3) No changes of crack initiation mechanism and initiation site were found for fretting
fatigue in the present range of fatigue cycle up to 10 9 cycles, contrary to the case of
fatigue without fretting. The high stress concentration at the contact edge in fretting
fatigue will be a possible reason for these phenomena.
4) In Ti-6A1-4V alloy, non-propagating crack could not be found in the survived
specimen at 10 7 cycles. In the further loading cycles up to 10 9 cycles at the same
stress amplitude, no crack initiation and propagation could be observed, which
indicated that the conventional fretting fatigue strength defined at 10 7 cycles was still
effective at least up to 109 cycles.
References
[1] Milestone, W. D., "A New Apparatus for Investigating Friction and Metal-to-Metal
Contact in Fretting Joints," Effects of Environment and Complex Load History on
Fatigue Life, ASTM STP 462, 1970, pp. 318-328.
[2] Salkind, M. J., Lucas, J. J., "Fretting Fatigue in Titanium Helicopter Components,"
NACE International Conference on Corrosion Fatigue" Chemistry, Mechanics and
Microstructure, 1971.
[3] Waterhouse R. B. and Dutta, M. K., "The Fretting Fatigue of Titanium and Some
Titanium Alloys in a Corrosive Environment," Wear, Vol. 25, 1973, pp. 171-175.
[4] Goss, G. L. and Hoeppner, D. W., "Normal Load Effects in Fretting Fatigue of
Titanium and Aluminum Alloys," Wear, Vol. 27, 1974, pp. 153-159.
[5] R. B. Waterhouse and M. H. Wharton, "The Behavior of Three High-Strength
Titanium Alloys in Fretting Fatigue in a Corrosive Environment," Lubrication
Engineering, Vol. 32, 1976, pp. 294-298.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
364 FRETTINGFATIGUE: ADVANCES
[6] Lutynski, C., Simansky, G., and McEvily, A. J., "Fretting Fatigue of Ti-6A1-4V
Alloy," Materials Evaluation Under Fretting Conditions, ASTM STP 780, 1982, pp.
150-164.
[7] R. Cortez, R. Mall and J. R. Caleaterra "Interaction of High-Cycle and Low-Cycle
Fatigue on Fretting Behavior of Ti-6-4," Fretting Fatigue: Current Technology and
Practices, ASTM STP 1367, 2000, pp. 183-198.
[8] Satoh, T., "Influence of Microstructure on Fretting Fatigue Behavior of Near-alpha
Titanium," Fretting Fatigue: Current Technology and Practices, ASTM STP 1367, 2000,
pp. 295-307.
[9] Huston A. L. and Nicholas, T., "Fretting Fatigue Behavior of Ti-6A1-4V Against
Ti-6A1-4V Under Flat-on-Flat Contact with Blending Radii," Fretting Fatigue: Current
Technology and Practices, ASTM STP 1367, 2000, pp. 308-321.
[10] S. E. Kinyon and D. W. Hoeppner, "Spectrum Load Effects on the Fretting Fatigue
Behavior of Ti-6A1-4V," Fretting Fatigue: Current Technology and Practices, ASTM STP
1367, 2000, pp. 100-115.
[11] Anton, D. L., Lutian, M. J, Favrow, L. H., Logan D., and Annigeri, B., "The Effects
of Contact Stress and Slip Distance on Fretting Fatigue Damage in Ti-6AI-4V/17-4PH
Contacts," Fretting Fatigue: Current Technology and Practices, ASTM STP 1367, 2000,
pp. 119-140.
[12] Masuda, C., Nishijima, S., Sumiyoshi, H., Tanaka Y., and Ishii, A., "Mode II Crack
Observed at the Origin offish Eye for SCr 420 Carburized Steel," J. Soc. Mater Sci. Jpn.
(Zairyo) Vol. 34, 1985, pp. 664-669.
[13] Abe T. and Kanazawa, K., "Fatigue strength and fatigue crack initiation and
propagation of high strength steels," J. Soc. Mater Sei., Jpn. (Zairyo), Vol. 40, 1991, pp.
1447-1452.
[14] Neal D. F. and Blenkinsop, E A., Acta Metall., Vol. 24, 1976, p. 59.
[15] Ruppen, J., Bhowal, P., Eylon, D., and McEvily, A. J., Fatigue Mehcanisms, ASTM
STP 675, 1979, p. 47.
[16] Eylon, D., J. Mater Sci., Vol. 14, 1979, p. 1914.
[17] Ruppen J. A., Eylon, D., and MeEvily, A. J., Metall. Trans., llA, 1980, p. 1072.
[18] Atrens, A. Hoffelner, W. Duerig, T. W. and Allison, J. E., Scr Metall. Vol. 17, 1983,
p. 601.
[19] Hagiwara M., Kaieda Y., Kawabe, Y., and Miura, S., Tetsu-to-Hagane, Vol. 76, 1990,
p. 2182 (in Japanese).
[20] King, R. N., Lindley, T. C. "Fretting Fatigue in a 3.5NiCrMoV Rotor Steel," Proc. of
Fifth Int. Conf. on Fracture, 1980, pp. 631-640.
[21] Spink, G. M., "Fretting Fatigue of A2.5%NiCrMoV Low Pressure Turbine Shaft -
The Effect of Different Contact Pad Materials and of Variable Slip Amplitude," Wear, Vol.
136, 1990, pp. 281-297.
[22] Rayaprolu, D. B., Cook, R., "A Critical Review of Fretting Fatigue Investigations at
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SHIRAI ET AL. ON ULTRA HIGH CYCLE REGIME 365
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
SURFACE TREATMENT
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Tomohisa Nishida, 1 Junnosuke Mizutani, 2 Yoshiharu Mutoh, 3 and Masatsugu Maejima 4
REFERENCE: Nishida T., Mizutani J., Mutoh Y., and Maejima M., "Effect of
Lubricating Anodic Film on Fretting Fatigue Strength of Aluminum Alloy,"
Fretting Fatigue: Advances in Basic Understanding and Applications, STP 1425, Y.
Mutoh, S. E. Kinyon, and D. W. Hoeppner, Eds., ASTM International, West
Conshohocken, PA, 2003.
ABSTRACT: Wear, scratch, plain fatigue and fretting fatigue tests were carried out
using aluminum alloy JIS 6063-T5 specimens with anodic film and lubricating anodic
film. Though the surface hardness of lubricating anodic film was lower than that of
anodic film, lubricating anodic film had excellent wear resistance and crack resistance
compared to anodic film, Plain fatigue strength of the specimen with anodic film was
lower than that of the specimen with lubricating anodic film, which almost coincided
with that of the specimen without film. The low fatigue strength of the specimen with
anodic film may result from the brittleness and tensile residual stress of the anodic film,
which attribute to the cracking at lower applied stress. Cracking of the lubricating anodic
film during fatigue tests hardly occurred due to its ductile nature and low residual stress
and consequently the fatigue strength was not degraded. Fretting fatigue strength of the
specimen with lubricating anodic film was higher than that of the specimen with anodic
film, which was higher than that of the specimen without film. The lubricating anodic
film had the lowest coefficient of friction and a higher cracking resistance, which
contributed to the retardation crack initiation and the low crack growth rates. The anodic
film also had low coefficient of friction compared to the specimen without film and
prevented meta-to-metal contact, which may result in higher fatigue strength compared
to the specimen without film. The lubricating anodic film is of significant benefit to
369
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
370 FRETTINGFATIGUE: ADVANCES
KEYWORDS: plain fatigue, fretting fatigue, lubricating anodic film, anodic film,
in-situ observation, tangential force coefficient
Introduction
Aluminum alloy, which has superior mechanical properties, low cost, light weight
and reliability, has been widely used for automobile parts, aircraft parts, air and oil
compressors and other components. However, aluminum alloy has problems of surface
damage due to its softness and corrosion. Therefore, improvement of surface properties
is required in practical applications. Anodic oxide treatment, which is so-called anodic
film treatment is widely used for this purpose. Anodized film impregnated with fluorine
resin or molybdenum sulfide has also been used for automobile parts and oil
compressors because of high wear resistance. Joining of components is common in such
machines and structures. Once one of the components or both the two components suffer
a load, fretting fatigue can be a potential failure mode. Therefore, not only plain fatigue
properties but also fretting fatigue properties are important for designing machines with
high reliability. Although some research works on fatigue of aluminum alloys with
anodic film have been reported [1-4], those on fretting fatigue have rarely, been done.
In the present study, plain fatigue and fretting fatigue tests were carried out to
investigate fretting fatigue properties of aluminum alloy JIS 6063-T5 specimens with
anodic film and lubricating anodic film. Furthermore, fretting fatigue cracks of the
specimen were observed in-situ using a fatigue testing machine with SEM (Scanning
Electron Microscope).
Experimental Procedure
Material
The material used for specimens was an aluminum alloy (JIS 6063-T5), of which
the chemical compositions and mechanical properties are shown in Tables 1 and 2,
respectively. The material used for the contact pad was a chromium-molybdenum steel
(JIS SCM420). Three types of the specimens were used: the specimen without film, the
specimen with anodic film (alumite), and the specimen with lubricating anodic film.
After degreasing an aluminum specimen surface with a neutral degreasing agent, it was
anodized for 35 min in a bath containing 20 wt% sulfuric acid solution with constant
current density of 2.5 A/dm2, to obtain an oxide film with 30 ttm thickness. This film
was re-anodized in aqueous solution of ammonium thiomolybdate with constant current
density of 0.1 A/dm2 for 6 rain and then molybdenum sulfide was impregnated into
oxide film pores.
Wear and scratch tests were carried out to investigate the fundamental properties of
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON EFFECT OF LUBRICATING ANODIC FILM 371
the anodic film prior to the fatigue tests. The wear test was carried out using a
ball-on-disk type wear tester (material of ball: a high carbon chromium bearing steel (JIS
SUJ2), diameter of ball: 5 ram, sliding distance per revolution: 3.14 cm ) under sliding
distance of 62 m, load of 1.5 kN and sliding speed of 5 crn/sec in air. The scratch test
was also carded out with a sapphire needle. Film surface was horizontally scratched by a
0.2 mm diameter sapphire needle at a normal load of 4.9 N and test speed of 50 mm/min.
The resultant cracks were observed using an optical microscope.
Since the anodic oxide film is amorphous, the measurement of residual, stress by
X-ray diffraction method is very difficult. The residual stress was estimated by the
following method.
After degreasing 99.8 % pure aluminum foil "(50 wnx25 ram• 100 ram) with a
neutral degreasing agent, it was perfectly annealed (400 ~ I hr). After one surface of
the foil was masked by an organic adhesive tape, 2,5,8,10,15,20 and 24 Izm thickness of
anodic oxide films were formed on the other non-masked surface in a bath containing 15
wt% sulfuric acid solution at 15 ~ bath temperature with constant current density of 2
A/din 2. In 0.I wt% aqueous solution of ammonium thiomolybdate ((NI-LI)2MoS4), the
stainless steel (JIS SUS304) plate was arranged as the cathode and the anodic oxide film
was arranged as anode. Electrolysis was processed at 20 ~ bath temperature with a
constant current density of 50 mA/dm 2 to 120 V. After anodizing, aluminum board was
well rinsed and masking tape on it was peeled carefully with organic solvent, dried in
hot air at 60 ~C and held at room temperature. The residual stress of anodic film was
calculated using equation of Barklie & Davies [5] with the measured radius of curvature.
[:44 1 . . . .
I 0.01
SCM420 I 0 C
.21 0S23
" I Mn0.70 I 0.016P [ 0.014
S i 0C13 t 0NiT [ 1C01
,, Mo
0.15
Table 2--Mechanicalproperties.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
372 FRETTINGFATIGUE: ADVANCES
The shapes and dimensions of the plain fatigue specimen, fretting fatigue specimen
and bridge-type contact pad are shown in Fig. 1 and Fig. 2. The gage parts of all the
fatigue specimens ~ d pad contact feet were polished using successively finer grade of
emery paper and the final polishing was conducted longitudinally with 1500 grade
emery paper. Fretting was induced by clamping a pair of bridge-type pads onto both
sides of the specimen (Fig. l(b)), using a proving ring [6]. The clamping pressure was
adjusted before and during the tests to give a constant value of 50 MPa. The tangential
force between the specimen and the pad during the tests was measured by strain gages
attached underneath the central part of the pad. The plain fatigue and fretting fatigue
tests were carried out using a servo-hydraulie fatigue test machine with a capacity of 98
kN under a stress ratio R o f - 1 at frequencies ranging from 10 to 20 Hz. Fracture
surfaces of the specimens tested were observed using a scanning electron microscope
and surface roughness of the fretted region was measured using a surface roughness
tester.
Fretting fatigue cracks were continuously observed using small fretting fatigue
specimens and a fatigue testing machine with SEM (Scanning Electron Microscope).
The shapes and dimensions of the fretting fatigue specimen and the bridge-type contact
pad are shown in Fig. 3. Fretting fatigue tests were carded out under a stress ratio R of
-1 and a clamping pressure of 50 MPa, which was applied by using a proving ring, as
shown in Fig. 4.
Figure 5 shows the relationship between frictional coefficient and sliding distance.
The anodic film shows stable value of friction coefficient, 0.4, after about 10 m running
(300 revolutions). On the other hand, the lubricating anodic film shows stable value of
friction coefficient, 0.2, after about 50 m running (1500 revolutions). The frictional
coefficient of the lubricating anodic film was approximately half of that of the anodic
film.
Figure 6 shows the observations of scratched surface of 24 lam thickness film. It was
found that number of cracks by scratched test in the lubricating anodic film was less than
that in the anodic film, which indicated that the lubricating anodie film had higher
resistance for cracking compared to the anodic film.
Figure 7 shows the relationship between hardness and distance from the surface of
film. The hardness test was carried out under a load of 0.5 N and hold time of 30
seconds. Surface hardness of the anodic film and lubricating anodic film was 0.55 GPa
and 0.37 GPa, respectively. The hardness of base material was about 0.1 GPa. This value,
HV=0.1 GPa is the same in comparison with aluminum alloy before anodizing.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL ON EFFECT OF LUBRICATING ANODIC FILM 373
---~---'+
140 :.1
•// A
IBO
62
I o 1 F:7--q~
Sectfon A-A
(a)Frettingfatigue specimen (b)Contactpad
Figure 3 - Frettingfatigue specimen and contactpadfor SEM Servo.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
374 FRETTING FATIGUE: ADVANCES
.~ 0,5 A n o d i c film
~o.4
0
~ 0.3
~0.2 Lu.-anodie film
O
",~ J "" I I I I I
~ 0 20 40 60 80 1O0
Sliding distance (In)
0.6
r~ 0.,
A Anodie film
[] Lu.-anodic film
~ 0.2
= [3
g
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON EFFECT OF LUBRICATINGANODIC FILM 375
Though the surface hardness of lubricating anodic film was lower than that of anodic
film, the former exceeds the latter in frictional property and crack resistance.
It is well known that the volume of anodic oxide film increases about 1.49 times of
that of aluminum bulk metal, if perfect alumina crystal structure is assumed as
explanation of Kabasbersky's volume ratio (oxide film/metal) [7]. Therefore,
compressive residual stress might be induced in anodic film. When the volume ratio is
less than 1.0, tensile residual stress may be caused [7], which is known to influence
mechanical properties and corrosion resistance in most materials.
In the anodic oxidizing process, dense layer with 5 % porosity, which is almost
equivalent to a volume ratio of 1.49 [8,9], is formed at the initial stage, while the volume
ratio decreases with increasing thickness of film. On the average, the through-thickness
porosity will be 20 %. Near surface layer of the film will have much higher porosity.
According to the simple calculation, the volume ratio at the initial stage (2-5 gin,
thickness) is 1.40 (1.49• When the porosity is assumed to be about 20 %,
the volume ratio of the film is estimated to be 1.18. Therefore, the compressive residual
stress in the film will be considerably reduced [10].
The residual stress in the film is influenced not only by porosity but also by other
factors, such as solution, intermetal compounds, etc. It is difficult to measure the
residual stress by X-ray method, because the anodic film is amorphous.
Figure 8 shows curvatures of the foil specimen with various thickness of anodic film,
which is produced on the one side of fully annealed aluminum foil. The curvature
increases with increasing film thickness. The same result was observed in the case of
lubricating anodic film. Figure 9 shows the difference in the curvature between anodic
film and lubricating anodic film. By impregnation of molybdenum sulfide in lubricating
anodic film, the compressive residual stress increased and the curvature was reduced.
Based on these observations, the residual stress of anodic film and lubricating anodic
film is estimated according to Borklie & Davies [5] equation:
o =h2E/6rd(1-d/h),
where, h: foil thickness in mm, E: Young's modulus of the aluminum foil in MPa, r:
radius of curvature in ram, d : anodic oxide film thickness in mm. Figure 10 shows the
relationship between residual stress and thickness of anodic oxide film. As can be seen
from the figure, the tensile residual stress of lubricating anodic film was reduced by
about 20 MPa compared to that ofanodic film.
The S-N curves for plain fatigue of anodic film and lubricating anodic film
aluminum alloys are shown in Fig. 11. The plain fatigue strengths at 107 cycles were
around 80 MPa for the specimen with anodic film and around 90 MPa for the specimen
with lubricating anodic film and also around 90 MPa for the specimen without film.
Shiozawa [1] has reported that the plain fatigue strength at 107cycles using bending
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
376 FRETTING FATIGUE: ADVANCES
6O
T
o
film
4~
2o
." " ][TI
b
' -20
"~,
~ -40
-60
0 10 20 30
Film thickness ( # m)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON EFFECT OF LUBRICATINGANODIC FILM 377
rotational fatigue tester for the aluminum alloy specimen (JIS A2014-T6 and JIS
A615 I-T6) with anodic film was lower 20~30 % than that without film. Hirata et al. [2]
have reported that though the plain fatigue life in high stress region for the aluminum
alloy specimen (JIS AI080) with anodic film was shorter than that without film, the life
in low stress region was longer than that without film. These results show that cracking
of anodic film during fatigue tests results in low fatigue strength.
Fig. 12 shows a SEM observation of plain fatigue crack initiation after the specimen
failed. Though the fatigue cracks of the specimen without film were initiated by
associating with slipping on the surface as shown in Fig. 12(a), it seemed that the fatigue
cracks of the specimen with anodic film were initiated from fracture region of the film as
shown in Fig.12(b). On the other hand, it seemed that the fatigue cracks of the specimen
with lubricating anodic film were initiated inside base material as shown in Fig. 12(c).
The S-N curves for fretting fatigue are shown in Fig.l 1. The fretting fatigue
strengths of 10 7 cycles were around 30 MPa for the specimen without film, around 40
MPa for the specimen with anodic film and around 50 MPa for the specimen with
lubricating anodic film.
The relationship between tangential force coefficient measured after getting stable
condition and relative slip amplitude is shown in Fig.13. The tangential force coefficient
is given as~ =Fa/P,where Fa is the amplitude of tangential force and P is the contact
pressure. The tangential force coefficient increased with increasing relative slip
amplitude for all materials and attained a constant value. Relative slip amplitude was the
calculated value as rigid to contact pad. The constant value of the frictional force
coefficient of the specimen without film, anodic film and lubricating anodic film were
0.85, 0.7 and 0.6 respectively. The small difference in frictional force coefficient
between two anodic films in fretting tests compared to the case of ball-on-disk test may
result from the severe test condition including contact piece geometry and contact load.
Surface Roughness
The maximum roughness of the fretted surface was also measured in order to
examine the fretting surface damage. The relationship between maximum surface
roughness and relative slip amplitude is shown in Fig.14. The maximum surface
roughness increased with increasing relative slip amplitude for all materials and was
saturated over 10~20 p,m of relative slip amplitude. The maximum surface roughness
values were around 45 pan for the specimen without film, around 20 ~tm for the
specimen with anodic film and around I0 ~tm for the specimen with lubricating anodic
film. The maximum surface roughness values for the specimen with lubricating anodic
film were significantly lower than those of other materials. From the results of tangential
force coefficient and surface roughness, though the difference was not so significantly
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
378 FRETTING FATIGUE: ADVANCES
b
O
\ " ~'~"--. ~..,A
.~. 1 0 0
(I~ []\ "" ~ ----
4 105 10 6 10 z 108
Number of cycles to failure N,
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON EFFECT OF LUBRICATING ANODIC FILM 379
1.0 '1 J I
/'
O
@
0.6
oo
~ 0.4 0 Uncoated
A Anodic~
[] Lu~-anod/rfilm
0.2
i l , i I , l i i I i i l l _
0 10 20 30
6O i
0 Uncoated
A A~lic film
[] Lu.-anodic O O
O
4C
O
2
0 0
A
20 A
n 0
[] 0
o []
0 10 20 30
Relative slip amplitude S(/1 m)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
380 FRETTINGFATIGUE: ADVANCES
large as the case of the frictional coefficient on the wear test, lubricating anodic film
excelled anodie film in the fretting wear characteristics.
in all materials, fretting fatigue cracks were initiated near the edge of the contact
region. A longitudinal cross section of the fretting fatigue specimen is shown in Fig.15.
Fig. 15(a) shows that the fretting crack on the specimen without film grows to 45 ~ to
fretting surface. This is almost the same with the case of other materials without film [11
-13]. The observation near the edge of the contact region is shown in Fig.15(b). The
damage of film was significantly severe and that there were lots of small fretting cracks.
The damage of lubricating anodic film was very small as shown in Fig.15(c). The
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON EFFECT OF LUBRICATING ANODIC FILM 381
lubricating anodic film had the lowest coefficient of friction and a higher cracking
resistance, which contributed to the late crack initiation and the low crack growth rates.
Fretting fatigue crack growth behavior in anodic film is shown in Fig.16. Fretting
fatigue cracks in anodic film were initiated in the early stage of fatigue life. In some
cases, the cracks were initiated just when contact pressure was applied. However, the
cracks in the anodic film generally initiated over 5 • 102 cycles and they grew into base
material over 3 x 103 cycles.
Figure 17 shows the fretting fatigue crack growth behavior in anodic film and
lubricating anodic film at the same stress level. In both materials, wear powder produced
during the test was observed in the late stage of life but was less in quantity compared to
the case of material without film. The surface hardness was improved due to the hard
film, which contributed to the wear resistance. The cracks in the anodic film initiated
over 5 • 102 cycles, and the cracks grew into the base material over 3 • 103 cycles. On the
other hand, the cracks in the lubricating anodic film initiated over 1.2• 103 cycles, and
the cracks grew into the base material over 6.4• 103 cycles. Lubricating anodic film
contributed to the retardation crack initiation and also to the low crack growth rate due
to the lower tangential force coefficient than that of the bulk material without film.
The effects ofanodic film on fatigue strength are summarized from results obtained
as follows.
Plain fatigue strength of the specimen with anodie film was lower than that of the
specimen with lubricating anodic film, which almost coincided with that of the specimen
without film. The low fatigue strength of the specimen with anodic film may result from
the brittleness and tensile residual stress of the anodic film, which are attributed to the
cracking at lower applied stress. On the other hand, cracking of the lubricating anod;c
film during fatigue tests hardly occurred due to its ductile nature and low residual stress
and consequently the fatigue strength was not degraded.
Fretting fatigue strength of the specimen with lubricating anodic film was higher
than that of the specimen with anodic film, which was higher than that of the specimen
without film. The lubricating anodic film had the lowest coefficient of friction and a
higher cracking resistance, which contributed to the retardation crack initiation and the
low crack growth rates. The anodie film also had low coefficient of friction as compared
with the specimen without film and so prevents meta-to-metal contact, which may result
in higher fatigue strength compared to the specimen without film.
The lubricating anodic film is of significant benefit for fretting fatigue strength
without degradation of plain fatigue strength.
Conclusions
Fundamental properties of aluminum alloy JIS 6063-T5 specimens with anodic film
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
382 FRETTINGFATIGUE: ADVANCES
Figure 16-- Observations offretting crack on the side surface of the specimen
Figure 17-- Observations of fretting crack on the side surface of the specimen with SEM
( a a=12OMPa,P=5OMPa).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
NISHIDA ET AL. ON EFFECT OF LUBRICATING ANODIC FILM 383
and lubricating anodic film were investigated. Plain fatigue and fretting fatigue tests
were also carried out to investigate fretting fatigue properties of the aluminum
alloyspecimens with anodic film and lubricating anodic film.
Furthermore, fretting fatigue cracks of the specimen were observed in-situ using
small fretting fatigue specimens and a fatigue testing machine with SEM (Scanning
Electron Microscope).
The main results obtained are summarized as follows:
(1) Though the surface hardness of lubricating anodic film was lower than that of
anodic film, the lubricating anodic film had excellent frictional property and crack
resistance compared to the anodic film.
(2) Plain fatigue strength of the specimen with anodic film was lower than that of the
specimen with lubricating anodic film, which almost coincided with that of the specimen
without film. The low fatigue strength of the specimen with anodic film may result from
the brittleness and tensile residual stress of the anodic film, which hre attributed to the
cracking at lower applied stress. Cracking of the lubricating anodic film during fatigue
tests hardly occurred due to its ductile nature and low residual stress and consequently
the fatigue strength was not degraded.
(3) Fretting fatigue strength of the specimen with lubricating anodic film was higher
than that of the specimen with anodic film, which was higher than that of the specimen
without film. The lubricating anodic film had the lowest coefficient of friction and a
higher cracking resistance, which contributed to the retardation crack initiation and the
low crack growth rates. The anodic film also had low coefficient of friction as compared
with the specimen without film and prevents meta-to-metal contact, which may result in
higher fatigue strength compared to the specimen without film.
The lubricating anodic film is of significant benefit for fretting fatigue strength
without degradation of plain fatigue strength.
References
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
384 FRETTINGFATIGUE: ADVANCES
[10] Maejima, M., Saruwatari, K., Isawa, K., and Takaya, M., "Curvatures of Anodized
Coatings of Aluminum" Surface technology, Vol.46-9, 1995, pp. 856-859.
[11] Tanaka, K., Mutoh, Y., and Sakoda, S., "Effect of ContactMaterials on Fretting
Fatigue in a Spring Steel" Japan Society of Mechanical Engineers, Vol.51-464,
1986, pp.1200-1207.
[12] Mutoh, Y., Nishida, T., and Sakamoto, I., "Effect of Relative Slip Amplitude and
Contact Pressure on Fretting Fatigue Strength" Japan of the Society of Material
Science, Vol.37-417, 1988, pp.649-655.
[13] Waterhouse, R. B., "Fretting Fatigue in Aqueous Electrolytes," Fretting Fatigue,
Applied Science Publication, 1981, pp.159-175.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Masaki Okane, l Kazuaki Shiozawa,2 Masaharu Hiki,3 and Kazntaka Suzuki4
REFERENCE: Okane, M., Shiozawa, K., Hiki, M., Suzuki, K., "Fretting Fatigue
Properties of WC-Co Thermal Sprayed NiCrMo Steel," Fretting Fatigue: Advances
in Basic Understanding and Applications, ASTM STP 1425, Y. Mutoh, S. E. Kinyon, and
D. W. Hoeppner Eds., ASTM International, West Conshohocken, PA, 2003.
ABSTRACT: Fretting fatigue tests of NiCrMo steel (JIS SNCM439) sprayed with
tungsten carbide with additive of 12% cobalt (WC-Co) by HVOF (High Velocity
Oxygen Fuel) were carried out to study the effect of WC-Co coating on fretting
fatigue behavior. Since the fatigue strength of the present alloy steel was reduced to
about 27% by the effect of fretting, fretting fatigue strength was improved by
approximately 30% by WC-Co spraying onto the specimen. The tangential force
coefficient, which is tangential force measured during the fretting fatigue tests
divided by contact load, behaviors of WC-Co sprayed specimen were different
form those of the non-sprayed specimen. Especially, the tangential force of WC-Co
specimen in an early stage of the test indicated significant low value compared with
that of non-sprayed specimen and this was caused from good wear resistance of
WC-Co layer. Therefore, the initiation of a fretting crack in case of WC-Co sprayed
specimen delayed, and crack propagation rate was lower than that of non-sprayed
specimen. These were main reasons for the improvement of fretting fatigue strength
by WC-Co spray.
KEYWORDS: fretting fatigue, NiCrMo steel, spray, WC-Co, HVOF, fretting wear
Introduction
385
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTMlntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
386 FRETTINGFATIGUE: ADVANCES
Experimental Procedure
In this study, Nickel-Chromium-Molybdenum steel JIS SNCM439 was used for the
substrate material and for the contact material. The chemical compositions of the material
used are shown in Table 1. The specimen w~asmachined from a bar with a diameter of
22mm after the heat treatments as follows, at 1123K (850~ for 1.7h O.Q. (Oil
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OKANE ET AL. ON FRETTING FATIGUE PROPERTIES 387
C Si Mn P S Cu Ni Cr Mo
0.37 0.28 0.75 0.021 0.017 0.05 0.74 0.81 0.15
Fig. 1 - Shapes and dimensions of the (a) fretting fatigue specimen, (b) plain
fatigue specimen and (e) eontactpad. (Un# : ram)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
388 FRETTINGFATIGUE: ADVANCES
Quenching) then at 893K (620~ for 2h W.C. (Water Cooling). The mechanical
properties of the material after heat treatment are shown in Table 2.
The shapes and dimensions of the specimens used are shown in Fig.h (a) shows
the fretting fatigue specimen, (b) the plain fatigue specimen and (c) the contact pad. The
gauge parts of both fatigue specimens (fretting fatigue specimen: 30mm long, plain
fatigue specimen: 10mm long) were polished with emery paper up to grade #1500
longitudinally and final polishing was conducted for the plain fatigue specimen by using
alumina slurry with grain size of 0.3 pm. The contact pad was cut from a bar with a
diameter of 60mm by wire-EDM (Wire Electric Discharge Machining) into designed
shape and two contact area of each contact pad (2mmx4mm face) were finalized by the
flat-surface grinding machine. Two kinds of contact pad, as shown in Fig. l(c) were used
for the fretting fatigue tests. One was, with lmm foot height, for the fretting fatigue test
of non-sprayed specimen and the other was, with 0.1ram foot height, for the test of
WC-Co sprayed specimen. Detail explanation will be given later in this paper.
Tungsten carbide with additive of 12wt.% cobalt (WC-12%Co, Grain size: 6-38pm)
was sprayed onto surface of the fretting fatigue specimen by HVOF (High Velocity
Oxygen Fuel) process. The DJ (Diamond Jet [22]) gun was used for HVOF process. The
chemical compositions and spraying conditions were summarized in Table 3 and Table 4,
respectively. Before HVOF process, blast treatment was applied onto the specimen
surface to enhance the bonding between substrate metal and WC-Co layer. The blast
Co TC Fe W
12.7 5.4 0.2 bal.
Oxygen 1.03
Gas pressure [MPa] C3H8 0.69
Air 0.52
Oxygen 4.77 x 10-3
Gas flow [m3/s] C3H8 1.31 x 10-3
Air 5.84 x 10-3
Powder delivery rate [N/s] 0.3626~0.3724
Spraying distance [m] 0.17
Pre-heating 333
Specimen Temperature [K]
After spraying 413~433
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OKANE ET AL. ON FRETTING FATIGUE PROPERTIES 389
conditions were shown in Table 5. Surface of the WC-Co layer was ground
perpendicularly by using diamond grind wheel, and after that final polish was conducted
longitudinally by using diamond emery paper up to grade of #1500. The thickness of
WC-Co layer was 100~tm and the micro vickers hardness of the layer HV was about 1152
(about 11.3 GPa).
A fatigue test machine with 49 kN capacities was used for fretting fatigue tests and
plain fatigue tests. All the tests were carried out under a load-controlled sinusoidal wave
form condition with a stress ratio R (O'min/~max)=-l, and frequency f=20Hz in air at room
temperature. For the fretting fatigue tests, two contact pads were pressed onto both sides
of the gauge section, and a contact pressure was controlled at constant value of 100 MPa
by using proving ring.
Tangential force between specimen and contact pad during the fretting fatigue test
was measured using a strain gauge attached on the bottom of the contact pad as shown in
Fig. 2(a). And relative slip amplitude between them was also measured by using small
extensometer as shown in Fig. 2(b).
After the tests, fretted surfaces were observed in detail by using a scanning electron
microscope (SEM). The cross section of the specimen around the fretted region was also
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
390 FRETTINGFATIGUE: ADVANCES
700
A I --~--Plain fatigue (No sprayed), -
600
,~ 200
I Stress ratio: R =-1 I "ID-----(~ ~ -
100 [Frequency: f=20 Hz J --
observed using SEM to discuss the initiation and growth of the fretting cracks.
S-N Curves (Relationship between fretting fatigue lives and applied stresses)
The relationship between applied stress amplitude and number of cycles to failure
(S-N curve) is shown in Fig. 3. In the figure, data points with arrow show that no failure
occurred up to the testing cycles of 5x106 cycles. It can be seen from the figure that the
S-N curve for plain fatigue of the substrate material (z~) was almost horizontal and the
fatigue strength at 5x106 cycles was around ~,=560 MPa. The fretting fatigue strength at
5x106 cycles of both no-sprayed ((2)) and WC-Co sprayed ( [ ] ) specimen were
significantly reduced compared with the plain fatigue strength. The fretting fatigue
strength of the no-sprayed specimen at 5 x 106 cycles was ~a--150 MPa which was about
27% comparing with the plain fatigue strength and that of the WC-Co sprayed specimen
was Cra=200 MPa. About 30% increase of fretting fatigue strength was observed in the
WC-Co sprayed specimen compared with the no-sprayed specimen.
As mentioned before, two kinds of contact pads as shown in Fig. 1(c) were used in
this study. The contact pad with I mm foot height was used for the fretting fatigue test of
no-sprayed specimen and 0.1 mm foot height contact pad was used for the experiment of
WC-Co sprayed specimen. This is because that when the higher foot contact pads were
used for the experiments of WC-Co sprayed specimen, the contact pads were broken at
their foot roots before the specimen failure occurred. Therefore, contact pads were used
for the tests of WC-Co sprayed specimen with foot height of 0.1 mm for reducing stress
concentrations at their roots. It is well known that the fretting fatigue life and strength are
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OKANE ET AL. ON FRETTING FATIGUE PROPERTIES 391
+ rv,,++o-++l ++
~~ ~ ~ I9 2OOMP. 9 3oo~P. I::1
u.Z ~ ~ I0 230MPa V 350MPaH
I~ 280UPa [ ] 450MPalZi
01-,,,,1 , I r,,illl i , Iiii+ii ~ ........ ~ ..... Ill
103 104 105 10+ 107
Number of fretbng cycles, N
(b) WC-Co sprayed
Fig. 4 - Variations of tangential force coefficients q)during the fretting fatigue tests.
significantly affected by the shape and dimension of the contact pad [23,24]. For
confirmation, several fretting fatigue tests of the no-sprayed specimens using 0.1 mm foot
height contact pads were conducted. Results of the tests were indicated in Fig. 3 by
half-solid circles. No significant differences were found in fretting fatigue lives and
strength between the test results with 1 mm and 0.1 mm foot height contact pads. And
also no significant difference was found in the results of tangential force coefficient and
relative slip amplitude between them as described later (Fig. 6). Therefore, the difference
in the shapes and dimensions of two kinds of contact pads used in this study seems to
have no influences on fretting fatigue behaviors of the present material. All experimental
results of WC-Co sprayed specimen shown in Fig. 3 were the results using 0.1 mm foot
height contact pads.
Variations of the tangential force coefficient ~ during the fretting fatigue tests are
shown in Fig. 4. The tangential force coefficient ~ was defined as a ratio of the tangential
force F to the contact load P, ~b=F/P. In case of no-sprayed specimen, tangential force
coefficients were almost constant during the fretting fatigue tests, which increased with
increasing stress amplitude. This tendency is similar to that of many metallic materials
observed by many investigators previously [1-4]. On the other hand, in case of WC-Co
sprayed specimen tangential force coefficients at early stage of the experiments, were
about 0.2 to 0.4 and have no dependence on the applied stress level. They were clearly
low compared to those of the no-sprayed specimens. Thereafter, the tangential force
coefficients increased gradually with the number of fretting cycles. In this study, a pair of
contact pads were used for each fretting fatigue test and the tangential force was
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
392 FRETTINGFATIGUE: ADVANCES
E
:~. 60 fill I I l nlnnnl L n i i i llll[ n n 1111111 l i 11111
30 7~ . . . . . . . .
~ 0.8
/0
/
/1
-- C'>
~ ~
rn wc-co sprayed(0.1 mm foot height c.p.) I
~ Meanvaluesat earlystages
I WC-Cosprayed(0.1 mmfootheightc.p)~
I
0.7
(..3
0.6
a=0MPa
0.5
%=230MPa
-~ 0.4 +~=350MPa --
'~ 0.3
~_ 0.2 /
%=230MPa
%=300MPa ~ra=280MPa
0.1
0 , , , I , , , , I , , , , I , , , , I .... l,
0 10 20 30 40 50
Rela~veslipamplitude ~,pm
Fig. 6-ReMtionsh~ between~ngentialforcecoeffic~nt~andre~tivesl~ amplitude~
measured at each contact pad respectively. In case of no-sprayed specimen, since the two
values of tangential forces were almost equal, the mean values of them were plotted in
Fig. 4(a). However, in case of WC-Co sprayed specimen, there were some cases that
significant difference was observed between two measured tangential forces especially in
latter stage of the experiment. In that case, the tangential force at the side where the main
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OKANE ET AL ON FRETTING FATIGUE PROPERTIES 393
Fretted specimen surfaces after the experiments were observed by SEM. The
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
394 FRETTING FATIGUE: ADVANCES
~ 0.8 z .....
c~a =300 MPa ~
WC-Co sprayed
" "
o
o 0.6 _ Nr=l.01XlO 6 cycles Side A _
o
~ o.4
~ I ~ SideB
0.2
results are shown in Fig. 7. Figure 7(a) shows a fretted surface around the contact edge of
no-sprayed specimen and a detailed observation of Fig. 7(a) is shown in Fig. 7(b). It is
clearly shown that there are some cracks near an edge of contact induced by fretting
action. All of no-sprayed specimens fractured from the cracks as shown in Fig. 7(a) and
7(b). Figure 7(c) shows a fretted surface around the contact edge of WC-Co sprayed
specimen. Damage on the WC-Co sprayed specimen was not so severe as the fretting
damage of no-sprayed specimen. Some cracks are observed near the contact edge where
the wear of WC-Co layer is severe as shown in Fig. 7(d), and all WC-Co sprayed
specimens fractured from these cracks. Wear and spalling of WC-Co layer occurred at
whole of contact region. However, since the full-thickness wear and attrition of the
WC-Co layer did not occur, the layer was remaining until the final fracture occurred.
Cross section of the WC-Co sprayed specimen tested, which was cut along
longitudinal direction, was observed by using SEM. The SEM micrographs are shown in
Fig. 8. Although cracks in the WC-Co layer are not so clear to find out as those in
substrate metal, it can be seen that a crack initiated at specimen surface by the fretting
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OKANE ET AL. ON FRETTING FATIGUE PROPERTIES 395
action propagates through the WC-Co layer with slight angle. The crack has further
propagation into the substrate metal after slight growth along the boundary between the
layer and the substrate.
From the experimental results, it was found that fretting fatigue lives of WC-Co
sprayed specimen increased 2-10 times compared to those of no-sprayed specimen. And
the fretting fatigue strength of WC-Co sprayed specimen significantly increased
comparing with that of no-sprayed specimen. Therefore, WC-Co spray by HVOF seems
to become an effective method for improving fretting fatigue strength. In this section,
fretting fatigue fracture process will be discussed.
As mentioned before, there were some cases in which significant difference in
tangential force variation of WC-Co sprayed specimen was observed. The most
significant case is shown in Fig. 9. For convenience, each fretted region is called "Side
A" and "Side B" respectively in this study. The tangential force coefficient at "Side A"
increased gradually with increasing number of fretting cycles after the middle stage of the
test. However, the tangential force coefficient at the opposite side did not increase, as
much as "Side A", it seems to be constant. The principal crack occurred at "Side A" in
this case. Figure 10 shows fretted surfaces and cross sections of "Side A" and "Side B"
observed by using SEM. It can be clearly found from Fig. 10(a) and 10(b) that the
damage on the surface of "Side A" is severer than that of "Side B". It can be also seen
from Fig. 10(c) and 10(d) that there is fretting crack at "Side A", but no crack was found
at "Side B". These results mean that in case of the present WC-Co sprayed specimen,
fretting crack is not induced under a condition that the tangential force coefficient is
lower than approximately 0.4, which is the final value of "Side B". The larger value of
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
396 FRETTING FATIGUE: ADVANCES
= I _ i l i j , j ~ j I l ~ l t I J ] I I ~ -
0.8 V V V VV
o~ V
o 0.6
o
~o 0.4
r~ i : 280 MPa [] : 450 MPa -
0.2 - ( vvu-uo sprayea I [ <~ : 300MPa "~
0 i t T I f I r I r I r I r ) i I ~ l
I--- 0 0.1 0.2 0.3 0.4 0,5 0.6 0.7 0.8 0.9
Ratio of number of cycles to the fretting fatigue life N/Nf
Fig. 11 - Variations of the tangential force coefficient as a function of the fatigue
life ratio N/Nf
tangential force coefficient than 0.4 seems to be essential to initiate the fretting cracks. In
the case shown in Fig. 9 and 10, fretting cracks seemed to initiate on "Side A" at a certain
stage when the tangential force coefficient became larger than approximately 0.4. The
initiation condition of fretting crack is thought to be depending on not only the tangential
force (tangential force coefficient) but also applied stress level. However, the tangential
force coefficients at early stage were almost equal irrespective of stress level, and the
tangential force, rather than the applied stress, affected local stress condition around the
crack initiation site significantly [25,26]. Therefore, the tangential force coefficient at the
point of fretting crack initiation does not seem to depend on the applied stress.
Relationship between the tangential force coefficient and the fatigue life ratio of
WC-Co sprayed specimen, i.e. the ratio of number of fretting cycles to fretting fatigue
life N/Nf, is shown in Fig. 11. If the fretting crack is assumed to initiate when the
tangential force coefficient becomes 0.45-0.5 (the range is indicated in Fig. 11 by a gray
colored band), based on the previous discussion, the fretting crack initiation life is
estimated about 10-30% of whole fatigue life as shown in Fig. 11. In many metallic
materials, the fretting fatigue crack initiates at very early stage, which is less than 25% of
the life, and almost the whole of fretting fatigue life is spent in propagating the fretting
crack [27]. Thus, no significant difference in crack initiation life is found between the
case of present WC-Co sprayed specimen and the cases of many metallic materials. Since
total fretting fatigue lives of WC-Co sprayed specimen are 2-10 times longer than those
of no-sprayed specimen, the crack initiation cycles of WC-Co sprayed specimen are
thought to be larger number than those of no-sprayed specimen. This is considered one of
the reasons that the fretting fatigue life was improved by WC-Co spraying.
Furthermore, the tangential force coefficient at crack initiation in WC-Co sprayed
specimen is smaller compared with that in no-sprayed specimen under the condition of
same stress level. Since fretting fatigue crack propagation rate strongly depends on the
magnitude of tangential force coefficient i.e. the tangential force, the propagation rate of
WC-Co specimen seemed to be lower than that of no-sprayed specimen. Thus, the
propagation lives of WC-Co sprayed specimen were thought to be longer than those of
no-sprayed specimen as a consequence. This is considered as the other reason why the
fretting fatigue life was improved by WC-Co spraying. Further experiment and
discussion will be needed for clarifying the mechanism.
The reason that the fretting fatigue life was improved by WC-Co spraying is
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OKANE ET AL. ON FRETTING FATIGUE PROPERTIES 397
summarized as follows. The tangential force coefficient of WC-Co sprayed specimen was
significantly lower than that of no-sprayed specimen, because of excellent fretting wear
resistance of WC-Co, especially in the early stage of the test. Therefore, initiation of the
fretting fatigue crack in WC-Co sprayed specimen was delayed compared with that of
no-sprayed specimen, and the crack propagation rate in WC-Co specimen was lower
compared with that of no-sprayed specimen. The cooperation of these two mechanisms
may give the improvement in fretting fatigue life and strength in WC-Co sprayed
specimen. In other word, the fretting fatigue properties of WC-Co sprayed specimen
strongly depend on fretting wear properties of WC-Co, which is affected significantly by
spraying process and quality of the powder. Another series of fretting fatigue test of
WC-Co sprayed specimen should be conducted with controlling the spraying process
systematically.
Conclusions
Fretting fatigue tests were carried out using NiCrMo steel (JIS-SNCM439) sprayed
with tungsten carbide with additive of 12wt.% cobalt (WC-12%Co) by High Velocity
Oxygen Fuel (HVOF) process. The main results obtained are summarized as follows:
1. The fatigue strength of the NiCrMo steel was reduced into 1/4 by fretting.
2. The fretting fatigue strength of the NiCrMo steel was improved about 30% by WC-Co
spraying.
3. The tangential force coefficients of no-sprayed specimens were almost eonstant during
the test, and those values depended on the applied stress amplitude.
4. The tangential force coefficients of WC-Co sprayed specimens were low at early stage
of the tests, which were about 0.3 irrespective of stress level, and after that, they
increased gradually with the number of fretting cycles.
5. The WC-Co sprayed specimen was fractured by the fretting crack which was initiated
at the surface of WC-Co layer and propagated into the substrate steel.
6. The improvement in fretting fatigue strength by WC-Co spraying was given by
interaction of retardation of fretting fatigue crack initiation and its lower propagation
rate.
Acknowledgments
References
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
398 FRETTINGFATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
OKANE ET AL. ON FRETTING FATIGUE PROPERTIES 399
[21] T.Nishida, Y.Mutoh and S.Niwa, in Proceeding of the 48t# Annual Meeting of Japan
Society of Materials Science, (1999), pp. 117-117 (in Japanese).
[22] Sulzer Meteco Ltd.
[23] Y.Mutoh, T.Nishida and I.Sakamoto, "Effect of Relative Slip Amplitude and Contact
pressure on Fretting Fatigue Strength", J. Soc. Mater. Sci. Jpn., 37-417, (1988),
pp.649-655 (in Japanese).
[24] K.Nakazawa, M.Sumita and N.Maruyama, "Effects of Fretting Pad Shape and
Clamping Condition on Fretting Fatigue in SNCM439 Steel", Proceeding of 1998
JSMEAnnual Meeting, 98-1, (1998), pp.161-162 (in Japanese).
[25] Y.Mutoh, "Mechanisms of Fretting Fatigue", JSME Inter. Journal, A, 38-4, (1995),
pp.405-415.
[26] R.B.Waterhouse, "Fretting Fatigue", International Materials Reviews, 37-2, (1992),
pp.77-97.
[27] K.Tanaka, Y.Mutoh and S.Sakoda, "Effect of Contact Materials on Fretting Fatigue
in a Spring Steel", Trans. Jpn. Soc. Mech. Eng. (A), 51-464, (1985), pp.1200-1207
(in Japanese).
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
CASE STUDIES AND APPLICATIONS
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Trevor C. Lindley
Abstract: Fretting wear and fatigue damage induced by wind vibration in overhead
power conductors has been investigated by metallographic and fractographic
examination. It has been concluded that wear, corrosion and fatigue can each play a role
in the degradation of cable, sometimes leading to complete failure.
Introduction
Wind induced vibrations can cause wear, sometimes leading to cracking and possibly
complete failure in overhead electricity supply lines [1,2]. For power lines situated near
the coast, the problem can be further exacerbated by corrosion, wind borne sea salt spray
being carried inland for many miles.
The present paper is concerned with fretting wear and fatigue damage in the clamp-
conductor region ofACSR (Aluminium Conductor Steel Reinforced) multi-layer cables.
The wind induced vibration modes which can subject a conductor to fatigue loading are
either sub-conductor oscillation or aeolian vibration. Aeolian is small amplitude vibration
which causes fretting between individual wires making up the cable. Sub-conductor
oscillation can cause much more severe bending forces and is induced by strong winds
403
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTMlntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
404 FRETTINGFATIGUE: ADVANCES
and gales which may even cause cable "galloping". Despite both types of vibration
modes being wind induced, sub-conductor oscillation promotes displacements which are
essentially restricted to a horizontal plane whereas aeolian vibration gives rise to a
vertical motion of the conductor. The two vibration modes also differ in frequency
response and often in magnitude of induced stress. Sub-conductor oscillation has a
vibration frequency of about 1Hz and is typically associated with stress amplitudes values
of +/-40 MPa. Aeolian vibration typically occur at frequencies up to 20Hz at stresses of
+/- 10 MPa. The present work is particularly concerned with the aeolian vibration which
induces fretting damage by promoting small oscillatory displacements between individual
strands making up the conductor cable. The conductors involved in the present study had
been in service for more than 20 years.
The paper describes a detailed metallurgical investigation including fractography of
cables damaged by fretting where wear, corrosion and fatigue can each play a role in the
degradation of the cable.
Experimental Method
Macroscopic and microscopic examination was carried out in order to satisfy the
following objectives:
1) to note the location of significant wear and to assess the extent of wear between
individual strands and relate this wear to the observation of cracking.
2) to record the occurrence and orientation of all cracks and to identify the sites of crack
initiation.
3) to determine the mechanism of cracking
4) if the cracking was due to fatigue, determine the operative vibration mode (sub-
conductor or aeolian).
5) to determine the extent to which corrosion was important in the failures.
Experimental Results
Cable Construction
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LINDLEY ON OVERHEAD ELECTRICAL CONDUCTOR CABLES 405
General Examination
In-service damage was located in regions close to the Andre spacers (figures 3 and 4)
where the cable exits a support bush. The four conductors can be conveniently identified
by their positions in the spacer as 'top inner' (TI), 'top outer' (TO), 'bottom inner' (BI)
and 'bottom outer' (BO). After dismantling, the position previously occupied by the
spacer clamp is easily defined by two dark witness marks (figure 3a), sometimes
showing evidence of pronounced corrosion in some regions (figure 3b). Limited
corrosion was noted on TO conductors but patches of corrosion was found on TI, BI and
BO conductors. The corrosion present on some strands was sufficient to give a significant
reduction in cross section (figure 4) but such corrosion was never associated with either
strand cracking or complete failure. In all cases, cracking occurred close to the dark
witness mark (near the edge of the clamp) and ran diagonally across each strand when
viewed from the outside of the conductor (see figure 5a and 5b). In each conductor, all
cracked or fractured strands were at the same end of the clamp. Cracking never occurred
at both ends of a clamp.
The outer layers of the conductor samples were examined optically and the locations
of all fractured, cracked or severely corroded strands recorded as shown in figure 6. The
cracked or fractured strands tended to be grouped together in any one conductor rather
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
406 FRETTINGFATIGUE: ADVANCES
than being randomly distributed around the circumference. There was apparently no
relationship between the occurrence of cracking in a strand and the presence of corrosion
(compare figures 7 and 8). It was noted that corrosion tended to occur in strands
positioned toward the bottom of the conductor whereas cracking tended to occur at all
points on the circumference of the conductor with the exception of the very bottom
strand, none of which showed cracks.
Figure 2 The Andre Spacer (ignore the weights in the foreground which were absent in
the present study)
A conductor was partly dismantled in order to investigate the wear between strands in
the outer and second layers. Some of the outer layer strands were removed, exposing lens
shaped wear scars on both the second layer strands and on the matching faces of the outer
layer strands as shown in figures 9. The lens markings are bright in appearance with
relatively little surface oxidation for positions near to a clamp. At distances greater than
about 100mm from a clamp, a few lens markings were found to be covered with patches
of a dark surface oxide (figure 10). Significant quantities of white oxide found between
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LINDLEY ON OVERHEAD ELECTRICAL CONDUCTOR CABLES 407
Figure 3 General Views of the Conductors in the Region of the Spacer Clamps
(a) the TO position showing two dark witness marks (arrowed)
(b) the Tl position showing heavily corroded region beneath the clamp
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
408 FRETTINGFATIGUE: ADVANCES
the strands was identified by X-ray analysis as a mixture of the Gibbsite and Bayerite
forms of aluminium hydroxide. Metallographic cross-sections taken through a strand at a
lens marking showed a relatively smooth surface with little sub-surface damage. The lens
type wear was quantified by measuring the length of individual lens scar markings
around the circumference of a conductor section. Lens scar length measurements were
made over a range of distances from the centre of the clamp (figure 11). The wear
between strands was a maximum close to the edges of a clamp and gradually reduced
with distance away from the clamp.
In addition to the lens shaped scars on the underside of the outer strands, flats were
apparent on the side faces of these strands (figure 12a) i.e. at the point of contact between
adjacent strands in the outer layer. This form of wear was completely absent at the centre
of the clamp, with flats developing from a point very close to the edge of the clamp
(figure 12b). Figure 13 shows the variation in the width of the flat with distance from the
centre of the clamp, plotted on both sides (labelled left and right) of the clamp.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LINDLEY ON OVERHEAD ELECTRICAL CONDUCTOR CABLES 409
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
410 FRETTINGFATIGUE: ADVANCES
Mechanisms of Wear
As already noted, the wear between adjacent strands resulted in the formation both of
lens type markings (on the underside of outer layer strands) and fiats (on the side faces of
the strands). Both forms of wear result from relative sliding between adjacent layers. The
factors controlling the amount of wear include the contact pressure between strands, the
amplitude of relative sliding and the number of sliding cycles. Both types of wear show a
maximum near to the edge of the clamp (figures 11 and 13), a consequence of both a high
contact pressure due to the proximity of the clamp together with significant relative
sliding. At the centre of the clamp, the lens type wear was somewhat reduced since
sliding between the outer and second layers was restrained by the clamp. Wear resulting
in fiats was completely absent at this point suggesting that relative sliding was not
possible as a consequence of the outer layer strands being locked together by the clamp.
Both forms of wear show a reduction in magnitude with distance from the clamp
although the lens type wear was present over the whole of the conductor sections
examined whereas no fiats were present at positions remote from the clamp. This would
indicate that the formation of flats was due to a wear mechanism more specific to the
clamp, unlike the formation of lens markings which are more of a long range process
increased in magnitude by the presence of the clamp.
In the region adjacent to the clamp, the appearance of the wear damage produced by
the two forms of wear is a manifestation of two extremes of repeated sliding wear
behaviour. The lens type wear associated with little sub-surface damage and large
quantities of white oxide deposits is typical of wear at a relatively low contact pressure
and high values of relative slip, promoting material removal by a grinding type action.
Conversely, the flats with their adherent oxide and evidence of sub-surface damage is
typical of fretting wear at a relatively high contact pressure (greater than 15MPa) and a
low range of relative slip (<30~tm). In this later case, surface material is removed by the
repeated shear and fracture of asperities.
The presence of an angled crack in a single strand from the outer conductor layer is
shown in a view of the side face in figure 14. Wear between adjacent strands in the outer
layer has caused the introduction of a fiat and subsequently the angled crack. In other
cases, two cracks were found which had initiated from both flats on either side of the
strand. Crack initiation at a flat was confirmed by scanning electron microscopy (SEM)
as shown in figure 15. Note that this crack did not grow to fracture and the final fatigue
crack tip position before breaking open is indicated. The fracture surface near to the crack
initiation site was heavily oxidised, consistent with the crack developing very slowly in
its early stages.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LINDLEY ON OVERHEAD ELECTRICAL CONDUCTOR CABLES 411
Figure 6 Schematic showing locations of cracked, failed and severely corroded strands.
In the present investigation, all cracked strands (figure 6) showed crack initiation at a
fiat at a position close to the outer edge of the clamp. Each crack then grows into the
strand at a shallow angle and in the direction beneath the clamp. Such a crack trajectory
is typical of a crack developing by fretting. Crack initiation by a fretting mechanism was
further supported by taking metallographic axial sections through the strands
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
412 FRETTING FATIGUE: ADVANCES
perpendicular to flats in regions adjacent to the major cracks. The section in figure 16
shows multiple initiation of angled cracks, typical of fretting fatigue.
Two outer layer strands which failed completely are shown in figure 17, one of which
failed from a single fatigue crack whilst the other failed from two cracks initiating on
either side of the strand. Fatigue cracks often grew to occupy about 80% of the strand
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LINDLEY ON OVERHEAD ELECTRICAL CONDUCTOR CABLES 413
Figure 9 Partially dismantled conductor showing wear between outer and second layer
strands responsiblefor lens shaped markings
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
414 FRETTING FATIGUE: ADVANCES
12
I
10
E
E 8 I C~, Bottom right
c f ", ~V "--- ....... .-o.-.
4 _ ~ %**%4
I Edge of '%.o.
I clamp .."%%
I
I
[ I , 1 ,I I ....I t .1 ....
0 20 40 60 80 100 120 140 160 180 200 220
Distance from clamp centrefine, mm
cross section prior to failure. The final failure occurs by a ductile failure giving a fracture
surface which is approximately perpendicular to the strand surface.
Note that in the present survey, cracks were not found at the lens shaped scars (arising
from contact between strands in adjacent layers). Here, it is possible that under the
prevailing contact conditions, the wear rate might be sufficiently high to remove any
incipient cracks.
Conclusions
1. The cracking observed in outer layer strands of the conductors initiated by fretting
fatigue at a position close to the edge of the spacer clamp,
2. Fretting fatigue occurred due to the contact between the side faces of adjacent strands
in the outer conductor layer. This fretting also resulted in the formation of wear flats
at a location specific to the neighbourhood of the clamp.
3. A second wear mechanism was apparent which took place between strands in the
outer and second layers. This wear was less specific to the clamp region, being
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LINDLEY ON OVERHEAD ELECTRICAL CONDUCTOR CABLES 415
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
416 FRETTING FATIGUE: ADVANCES
1,4
1.2
1.0
E cjl~t side
E
0.8
i.ooo, ", \.
I \X
0~6
(),4
0,2
! ".... \
:.., I ! t ......l , , I ,, ,L ,,"""-
20 40 60 80 100 120 140
Figure 13 Variation in width offlat with distance from centre line of clamp
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LINDLEY ON OVERHEAD ELECTRICAL CONDUCTOR CABLES 417
Figure 15 Low power SEM micrograph of cracked strand broken open to revealfracture
surface (final posttion offatigue crack tip arrowed)
apparent to a distance of at least 0.5m from the clamps. This wear resulted in the
formation of lens shaped markings on the underside of outer layer strands. The wear was
more severe than that between outer layer strands due to a greater amount of relative
sliding between strands, further exacerbated by the formation of a large amount of
fretting debris. There were no incidences of cracking with this type of wear.
4. Considerable amounts of corrosion were present on some strands. This corrosion was
concentrated in the region beneath the clamps to the underside of the conductor. This
corrosion sometimes caused large reductions in the cross section of the strands but no
cracking was associated with corrosion so that the fretting fatigue was not related to
the corrosion.
5. Microcracks formed by fretting subsequently developed by mechanical fatigue to
eventually occupy about 80% of the cross section, final strand failure then occurring
by ductile fracture. The inclined orientation of the cracks indicated that the loading
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
418 FRETTING FATIGUE: ADVANCES
Figure 16 Cross section through strand at a flat showing multiple initiation of angled
cracks typical offretting fatigue
developed in the strands was significantly influenced by local contact stress in the
proximity of the clamp.
6. There was no evidence to indicate that which mode of conductor loading
(subconductor oscillation or aeolian vibration) was responsible for the cracking.
Acknowledgements
The author is extremely grateful to Drs K J Nix and A Camyab who each made
significant contributions to the work reported.
References
[1] Cardou,A., Leblond, A., Goudreau, S. and Cloutier, L., "Electrical Conductor
Bending Fatigue at Suspension Clamps: a Fretting Fatigue Problem", Fretting Fatigue,
ESIS 18, R.B.Waterhouse and T.C.Lindley, Eds, European Structural Integrity Society,
Mechanical Engineering Publications, London, 1994, pp 257-266.
[2] Cardou, A., Cloutier, L., St-Louis, M. and Leblond, A., "ACSR Electrical Conductor
Fretting Fatigue at Spacer Clamps", Standardisation of Fretting Fatigue Test Methods
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LINDLEY ON OVERHEAD ELECTRICAL CONDUCTOR CABLES 419
Figure 17a SEM micrograph offractured outer layer strandfailing from two fatigue
cracks on either side of strand
and Equipment, ASTM 1159, M.H.Attia and R.B.Waterhouse, Eds., American Society
Testing and Materials, West Conshohocken, PA, 1992, pp 231-242.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
420 FRETTING FATIGUE: ADVANCES
Figure 17b SEM micrograph offractured outer layer strandfailing from a singlefatigue
crack
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
LINDLEY ON OVERHEAD ELECTRICAL CONDUCTOR CABLES 421
List of Figures
Figure 2. The Andr6 spacer (ignore the weights shown in the foreground which were
absent in the present study).
Figure 3. General views of the conductors in the region of the spacer clamps
(a) the TO position showing two dark witness marks (arrowed)
(b) the TI position showing heavily corroded region beneath the clamp.
Figure 5. General views of conductors in the region of the spacer clamp showing major
cracking(a) conductor BO (b) conductor BI.
Figure 6. Schematic showing locations of cracked, failed and severely corroded strands.
(orientation of conductors as during service).
Figure 9. Partially dismantled conductor showing wear between outer and second layer
strands responsible for lens shaped markings.
Figure 10. Lens marking approximately 200mm from edge of clamp showing patchy
surface oxide.
Figure 11. Length of lens shaped markings in terms of distance from clamp centreline.
Figure 12 Flats on side faces of outer layer strands formed by wear against adjacent outer
layer strand.
(a) fully developed flat about 20ram from edge of clamp.
(c) development of flat close to edge of clamp.
Figure 13. Variation in width of flat with distance from centre line of clamp.
Figure 14. Angled crack in fiat on side face of an outer layer single strand.
Figure 15 Low power SEM micrograph of cracked strand broken open to reveal fracture
surface (final position of fatigue crack tip arrowed).
Figure l 6. Cross section through strand at a flat showing multiple initiation of angled
cracks typical of fretting fatigue.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
422 FRETTING FATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Toshihiko Yoshimura, 1 Takashi Machida, 2 and Toshio Hattori3
REFERENCE: Yoshimura, T., Machida, T., and Hattori, T., "Evaluating Fatigue
Life of Compressor Dovetails by Using Stress Singularity Parameters at the
Contact Edge," Fretting Fatigue. Advances in Basic Understanding and
Applications, STP 1425, Y. Mutoh, S. E. Kinyon, and D. W. Hoeppner, Eds., ASTM
International, West Conshohocken, PA, 2003.
Abstract: Fretting fatigue life of compressor dovetail for gas turbine was investigated
using stress singularity theory. It is found that the crack initiation of fretting fatigue
between blade dovetail and wheel dovetail occtirs at the contact edge of blade dovetail.
The parameters of stress singularity obtained from maximum principal stress
distribution are capable to evaluate the fretting fatigue strength with the cyclic load
having a constant angle against the contact surface under a variable contact pressure.
The ratio of between the intensW range of stress singularity and the critical intensity
range of stress singularity, /X H 1/ A H c, is an effective parameter to predict the
fretting fatigue life of compressor dovetail.
Introduction
An increase in the length of gas-turbine compressor blades with an increase in
the compression ratio and the volume of gas passing through may cause fretting
fatigue problems because of an increase in the blade centrifugal force and contact
pressure between the blade and wheel dovetails. Constant contact stress at the edge
between the blade and wheel dovetails leads fretting fatigue. In order to estimate the
life-time of gas turbine compressor dovetail, a fatigue experiment was conducted and
the stress singularity theory was applied to estimate the fretting fatigue strength of a
compressor dovetail.
423
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTM lntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
424 FRETTING FATIGUE: ADVANCES
Experiment
Figure 1 shows the fatigue experiment conditions. 15-Cr steel for the blade
and NiCrMoV steel for the wheel were used. The blade dovetail was inserted into the
wheel dovetail. During the fatigue experiment, the maximum axial force, which
included the blade centrifugal force, was applied to both the dovetails. The cyclic
force corresponding to the gas-bending force of the compressor blade was then
superimposed on the axial force. The loading conditions for the fatigue experiment
are shown in Fig. 2. Stress ratio R ranged from 0--0.91. The number of crack initiation
cycles were detected based on the output variation from a pair of strain gauges, which
were installed on both sides of the blade dovetail. As shown in Fig. 3, to clarify the
effect of the contact angle between the blade and wheel dovetails (do,vetail shoulder
angle) on the fatigue life of the compressor blade, the kinds of dovetail shoulder
angles of 30, 35, and 40 degrees were chosen.
Blade dovetail
(15Cr steel)
,
i j
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
YOSHIMURA ET AL. ON LIFE OF COMPRESSOR DOVETAILS 425
Analysis
The stress around a contact edge is represented by the following equation [1].
cr ( r ) =H/r ~ (1)
Here, ty is the stress (MPa), r is the distance from the contact edge, H is the
intensity of stress singularity, and 3. is the order of stress singularity.
In this study, the crack initiation due to fretting fatigue was evaluated by using
parameters H and 3.. The order of stress singularity, 3. ,was obtained from the
stress distribution calculated by a field-element method, and 3. was obtained by
calculations using the contact angle of the both dovetails. The dovetail region around
the contact edge was divided into 100-/1 m-long meshes as shown in Fig. 4. The stress
distribution was analyzed by using the successive-finite-element method and the
intensity of stress singularity, H, and the order of stress singularity, 3. were
calculated. The circmnferential stress distribution and the maximum principal stress
distribution were obtained by defining the contact edge as the origin of the polar
coordinate.
Results
Figure 5 shows the dovetail contact region before fretting fatigue crack
initiation. As can be seen in the figure, many abrasion particles appeared around the
contact area. Crack initiation was observed at the contact edge between the blade and
wheel dovetails. These results suggest that the friction between the blade and wheel
dovetails, which was added to the contact pressure due to a high centrifugal force,
leads to fretting fatigue. The cracks due to fretting fatigue tend to grow along the
direction of the maximum shear stress.
Figure 6 shows the relationship between the number of crack initiation cycles,
Nf, and the ratio of the repetition load to the maximum load, AF/Fmax. The time of
crack initiation due to fretting fatigue depends on the dovetail shoulder angle, which
means that the life of a dovetail with a shoulder angle of 30 ~ will be longer than that
of a dovetail with a shoulder angle of 40.
The parameters of stress singularity obtained from the circumferential stress
distribution and the maximum principal stress distribution by the fimte-element
method are summarized in Table 1. The circumferential stress distribution was
obtained along the direction of crack propagation by defining the contact edge as the
origin of the polar coordinate. The order of stress singularity, 3. o, 3. 1, tended to
increase with an increase in the dovetail shoulder angle. While the intensity of stress
singularity, H o, from the circumferential stress distribution increased with an
increase in the dovetail shoulder angle, the mtensity of stress singularity, H 1, from
the maximum principal stress distribution did not show any significant increase. The
reason of such a discrepancy might be due to the stress distribution along the direction
of the maximum shear stress. In the case of the circumferential stress, the force
normal to contact surface, which directly affects the circumferential stress, decreases
with the dovetail shoulder angle. On the other hand, in the case of maximum principal
stress, the maximum principal stress may not depend on the dovetail shoulder angle, if
Mohr's circle for stress around the contact area is taken into consideration.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
426 FRETTING FATIGUE: ADVANCES
hd2scbenrd~gga/22 e
B lade
Contacl; edge bel~ een b ladedovetail
Bhdedovetail I l l / andwheeldovetad
[ Doveta il shouIderang,b
I (30~ ,35~ ,40~ )
I
I
b
(r) =H/r't
4~
03
Figure 4 - - F E M m e s h f o r dovetail.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
YOSHIMURA ET AL. ON LIFE OF COMPRESSOR DOVETAILS 427
I
A dovetatl angle 40~ with crack I
/
120 [] dovetail angle 35~ with crack
O dovetail angle 30~ with crack II
9 dovetatl angle 40~ crack
100 -*, ~ O
9 dovetail angle 35~ without crack
9 dovetail angle 30~ without crack
80
K'I 0
6O
A OH 0
40
II o
2O A
F p p r r
0
10E+03 I OE+04 1.0E+05 ! OE+06 1.0E+07 I OE+08 I OE+09
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
428 FRETTINGFATIGUE: ADVANCES
Discussion
The predictability of crack initiation due to fretting fatigue under arbitrary
contact conditions was investigated by comparing the intensity of stress singularity,
H, and the order of stress singularity, ~ , obtained by the finite element method, with
the critical intensity of stress singularity, H e.
Critical intensity of stress singularity H e is the intensity of stress singularity
that causes crack initiation when the stress of a specific distance from the contact edge
reaches its limit. The fatigue limit (smoothed test piece), Crwo, of the 15Cr steel used
for the blade was 780 MPa (R=0), and the threshold stress intensity factor range, A
Kth , w a s 3.1 MPa4-'m=98 M P a f ' m m (R=0). These values are plotted in this order in
Fig.7. Fatigue limit crwo does not depend on the distance from the contact edge and
is constant. In contrast, threshold stress intensity factor range A Kth depends on the
(depth)-I/2. The intersection point ofo-wo and A Kth is considered to define a
specific distance, which corresponds to the crack initiation distance [2]. This leads to
the following equation,
The relationship between the critical intensity of stress singularity, H c, and the order
of stress singularity, 3., is graphically shown in Fig. 8. The symbo! at )t =0
corresponds to the fatigue limit of a [smoothed test piece], while the symbol at )t
=0.5 corresponds to threshold stress intensity factor range A Kth. When ~. =0.5, the
following relationship is formed.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
YOSHIMURA ET AL. ON LIFE OF COMPRESSOR DOVETAILS 429
A Kth=98~Pa"4-m
crwo=780MPa
t~e~ "'~
............. ~ .............. ~'-" ~ 100 . . . . . . . .
u~ O. O025mm ""-
-10. . . . . . . .
Cwo=780MPa [
900
E
E 800
/ I Hc (X)=780 x 0'0025)x l - -
lC rack hitiation criterionJ
~ 700
.-.r-
.~ 6oo
.~ 500
400
A Kth=98M P a'm m o.__55
q-o
300
200
.~ 100
$_
0
0 0.1 0.2 0.3 0.4 0.5
0 rder o f stress shgularity
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
430 FRETTING FATIGUE: ADVANCES
E
E
o_
900
800
~ 780M Pa I
Ho (Z)=780 x 0 0025)x
700 ~ ~ C r a o k h~iatbn c r i t e r b n ~ _ _
~" 600
.g 500
4- 300
400
\
o
[] AI A Kth=98M Pa'm m~
~: 200
~-
100 o ~
..~I 9 IIA
L
o 0 P I 9 i
ADovetail a n g l e 40 ~ w i t h c r a c k
5. O0
ODovetail a n g l e 35 ~ w i t h c r a c k
ODovetail a n g l e 30 ~ w L t h c r a c k
4. O0 &Doveta=l a n g l e 40 ~ w = t h o u t c r a c k
iDovetall a n E l e 35 ~ w i t h o u t crack
0
9 Dovetail a n g l e 30* w } t h o u t c r a c k
3. O0
\
2. O0
1. O0 0[30 A
o ~; o .%,
l i i Q i
0 O0
1.0E§ I OE+04 I. OE+05 I. OE+06 1. OE+07 I OE+08 1.0E+09
Number of crack i n i t i a t i o n cycles Nf (Cycles)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
YOSHIMURA ET AL. ON LIFE OF COMPRESSOR DOVETAILS 431
As can be seen in the figure, the deviation is smaller than that in the relationship
between the number of crack initiation cycles, Nr, and the ratio of the cyclic load to
the maximum load, AF/Fm~x, as shown in Fig. 6. When AHo/AHc was more than
0.5, crack initiation occurred.
The relationship between the intensity of stress singularity and the order of
stress singularity obtained from the maximum principal stress distribution (H I and/l ~,
respectively) is plotted in Fig. 11. The solid circle, solid square, and solid triangle
correspond to dovetail shoulder angles of 30, 35, and 40, respectively. Here, the ratio
of H1/Hc was higher than that of Ho/Hc. The intensity ranges of stress singularity, A
H~, calculated by using the ratio of cyclic force, /XF, and the maximum axial force,
F , are shown in Fig. 12. As for the circumferential stress distribution, the open
symbols indicate the specimens with crack initiation, while the solid symbols indicate
the specimens without crack initiation. We found that the specimens with intensity of
stress singularity AHI lower than /XHc did not show crack initiation. Figure 13
shows the relationship between the ratio of intensity range of stress singularity to the
critical intensity range of stress singularity, AH1/AHc, and the number of crack
initiation cycles, Nf. The open symbols indicate the specimens with crack initiation,
while the solid symbols indicate the specimens without crack initiation. We found that
the devaation was smaller than the deviation in the relationship between Nf and the
ratio of A F/Fmax, as shown in Fig. 6 for AHo/AH~. Crack initiation occurred when
A H 1 / A H c was more than 1.0. These results suggest that the ratio of ZXHI//X H~
is effective in predicting fretting fatigue life. One of our specimens had crack
initiation at a ratio ofA H1//X Hc slightly greater than 1.0.
Earlier, T. Hattori and T. Watanabe [3] investigated fretting fatigue by using
stress singularity parameters and a cyclic load parallel to the contact surface under a
constant pressure on the contact surface. In this study, the cyclic load had a constant
angle against the contact surface under a variable pressure on the contact surface. The
results of this study indicate that under these conditions, fretting fatigue can be
evaluated using the stress singularity theory. Thus, while Hattori and Watanabe used
parameters of stress sir;gularity obtained from a circumferential stress distributmn to
evaluate the fretting fatigue of a cyclic load parallel to the contact surface under a
constant pressure, we used the maximum principal stress distribution to evaluate the
fretting fatigue of a cyclic load with a constant angle against the contact surface under
a variable contact pressure. When R=0.gl, which corresponds to a constant
gas-bending force of a compressor blade with a ratio of /XHI//XHc bellow 1.0, there
will be no fretting fatigue. Thus, to ensure reliability of gas turbines, the ratio of A
H 1/A H~ must be bellow 1.0 in the start-up, shutdown, and abnormal operation of gas
turbines.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
432 FRETTING FATIGUE: ADVANCES
-- 900 ,,~=780MPa [
E
9 800
13.
=o
700 I'Hc (3.)=780 X @.0025)x ~ ]
Crack h~htbn c r i t ~ r ~
.~ 600
-~ 500
400
\ 9
~o 300
.~ 100
0 '
0 0,1 0.2 03 0.4 0.5
0 rder of stress s hgu laribj
Figure l 1-Critical intenstty o f stress singularity H e f o r each
order stress singularity. ( 30 ~ 35 ~ :40~
f r o m maximum principal stress distribution)
8OO
[Crack hithtbn cr~rbn}
700
800
500
\
400 ~ ~AKth=98MPa'mm~
[] A \
300
200 k
i-1 A
A
\
.~ 100 -- ^
0
0 01 02 0.3 0.4 0.5
0 rder of stress shgularity Z
Figure 12--Intensity range o f stress singularity from maximum principal
stress distribution f o r critical intensity o f stress singularity.
(030 ~ , •35 ~ , A 4 0 o : with crack,
0 3 0 ~ , m 3 5 ~ , , 4 0 o . without crack)
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
YOSHIMURA ET AL. ON LIFE OF COMPRESSOR DOVETAILS 433
0. 00
1.0E+03 10E+04 1 0E+05 1.0E+06 1,0E+07 1.0E+08 1.0E+0g
Number o f c r a c k initiation cycles Nf (Cycles)
Conclusion
The relationship between the dovetail shoulder angle and the fretting fatigue
life of a compressor dovetail for a gas turbine by using the singularity theory was
investigated.
(1) Crack initiation due to fretting fatigue occurred at the contact edge of the blade
dovetail between the blade and wheel dovetails, and progressed to the side of the
blade dovetail.
(2) The parameters of stress singularity obtained from the maximum principal stress
distribution can be used to evaluate the fretting fatigue of a cyclic load with a constant
angle against the contact surface under a variable contact pressure.
(3) The ratio of the intensity range of stress singularity to the critical intensity range
of stress singularity, A HI/A He, is an effective parameter to predict the fretting fatigue
life.
References
[1] Bogy, D. B., Journal of Applied Mechanics, Vol. 38, (1971) p.377.
[2] Hattofi, T., Journal of the Marine Engineering Sooety in Japan, Vol. 33, No.3
(1998-3) pp.203-211.
[3] Hattori, T. and Watanabe, T., The Japan Society of Mechanical Engineers, Proe.
of M&M2000 (2000-10) pp.413-414.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
Masanobu Kubota, i Hidenori Odanaka, 2 Chu Sakae, 3 Yoshihiro Ohkomori,4 and
Yoshiyuki Kondo5
The Analysis of Fretting Fatigue Failure in Backup Roll and its Prevention
Reference: Kubota, M., Odanaka, H., Sakae, C., Ohkomori, Y., and Kondo, Y., "The
Analysis of Fretting Fatigue Failure in Backup Roll and its Prevention," Fretting
Fatigue: Advances in Basic Understanding and Applications, STP 1425, Y. Mutoh, S. E.
Kinyon, and D. W. Hoeppner, Eds., ASTM International, West Conshohocken, PA, 2003.
Abstract: In the present research, a fretting fatigue failure in a backup roll (BUR) was
examined. Fretting fatigue properties of the roll material were experimentally obtained
and the prevention of the fretting fatigue failure was proposed. BUR is one of the most
important components in a steel making rolling mill for the control of plate thickness and
flatness. The BUR was initially supported by oil film bearings. Recently, oil film bearings
have been rapidly replaced by roller bearings for the purpose of high-precision rolling.
After the replacements, fretting fatigue failures of BUR have begun to occur. Rotating
bending fatigue tests were performed with a 40 rnm diameter shrink-fit axle to evaluate the
fretting fatigue strength of the BUR material and to examine the improvement of the
fretting fatigue strength of the holding part of the BUR. The effects of roller machining
and overhanging of the contact edge on the fretting fatigue strength were investigated.
Based on the results of this study, roller machining was applied to the holding part of the
BUR. Furthermore, the diameter of the holding part of the BUR was increased. No failure
occurred due to fretting in the BUR for more than four years since these countermeasures
were applied.
Keywords: fretting fatigue, failure analysis, steel making rolling mill, backup roll,
shrink-fitted axle, surface rolling, overhanging of the contact edge
Introduction
The backup roll (BUR) is one of the most important components in the steel making
rolling mill with regard to the quality of rolled products. A steel making rolling mill is
shown in Fig. 1. The rolling mill consists of BURs, intermediate rolls and work rolls.
434
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed
Copyright9 by by ASTMlntcrnational www.astm.org
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KUBOTA ET AL. ON ANALYSIS OF FAILURE IN BACKUP ROLE 435
The BUR has an important role in controlling with high precision the thickness and
flatness of the steel plate under the rolling load of more than 10 MN [1]. In the middle of
1990s, a succession of BUR failure accidents occurred. The failure occurred at the axle
part of the BUR as shown in Fig. 1, where the inner race of the roller bearing is fitted.
The failure was due to fretting fatigue. Since the working conditions of BUR have
become severer in response to demands for improving productivity and precision of the
rolled products, the problem of fretting fatigue in the BUR has risen in recent years. The
present study shows a failure analysis of the BUR, results of the fretting fatigue tests and
changes made to the actual BUR based upon the fretting fatigue tests.
The need for improving work efficiency in rolling has tended toward extended campaign
cycles and higher rolling loads [2]. An oil film bearing has been used in the steel making
rolling mill. Recently, oil film bearing has been replaced by roller bearing for
high-precision rolling in recent years [i]. Thus, the problem of fretting fatigue has
occurred in the BUR. The BUR axle is assembled by a shrink fit with the inner race of
the roller bearing. Figure 2 shows the fitted part of the BUR.
2060
12 o -L_
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
436 FRETTINGFATIGUE: ADVANCES
Oil film bearings from 13 BURs were replaced by roller bearings. One of these
BURs with roller bearings failed within three years due to cracking at the BUR axle. Five
similar failures followed the first one within 6 months. Two of them were completely
broken. It was estimated that the number of cycles to failure was approximately 4 • 107.
The surface of the BUR, which suffers from wear and spalling, is ground at regular
interval to remove small cracks and irregularities. About 10 to 20 years of BUR service
life is usually determined by the decrease in the diameter by the grinding. The BUR axle
must endure more than 10s cycles of rolling load during service.
Figures 3 and 4 show a cracked BUR. Since unusual severe vibration occurred in
the operation, the BUR was removed from the rolling mill. When the inner races of the
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KUBOTA ET AL. ON ANALYSIS OF FAILURE IN BACKUP ROLE 437
roller bearing were separated from the BUR axle, several large cracks were found along
with rust. The rust did not cover the entire surface where the inner race was fitted
but covered only the contact edge. This appearance shows the same for typical fretting
fatigue failure found in fitted axles such as railway axles. The axial length of the rusted
area was about 100 mm. The fatal cracks were initiated within the rusted area which was
located 5 mm inside from the contact edge. The length of the largest crack was about
one-third the circumference. Figure 5 shows the fracture surface of the BUR. There are
distinct traces of fatigue crack growth. No material faults and manufacturing defects were
detected at the crack initiation site.
Figure 6 shows the rusted surface, which was observed by SEM after removal of
the rust. Many small cracks were observed with many small pits. Figure 7 is a photo of
these cracks in the axial section. The cracks propagated at an angle to the surface. The
characteristics of the cracks and the pits were consistent with these observed for typical
long-life fretting fatigue [3].
The maximum bending stress at the cracked part of the BUR axle was estimated to
be less than 130 MPa. Taking the failure life, the observations of the surface of the axle
and cracks and the stress condition into consideration, it was concluded that the cause of
the failure of the BUR axle was fretting fatigue.
A study on the fatigue strength of a fitted-axle assembly, which has its origin in the
studies of the wheelset for rolling stock carried out by Wh61er [4, 5], has been studied for
more than 140 years. Nowadays, many measures to improve fatigue strength of the fitted
axle are known. However, the fatigue strength of the BUR axle has not been clarified
[1]. Also the effective measures to prevent fretting fatigue failure depend on the
structures and materials of the machines [3]. Fretting fatigue tests were performed using
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
438 FRETTING FATIGUE: ADVANCES
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KUBOTA ET AL. ON ANALYSIS OF FAILURE IN BACKUP ROLE 439
shrink-fitted axle assemblies with a 40 mm diameter in order to examine the cause of the
failure and to establish the measures to prevent BUR axle fretting fatigue failure.
Experimental procedure
Rotating bending fatigue test machines, whose load capacity is 4.4 kN and rotating
speed is 1600 rpm, were used for the fretting fatigue tests. The test machines have a
mechanism to align automatically the axle center. Usually the test machines are used to
evaluate the fatigue strength of high-speed railway axles [6. 7].
Figure 8 shows a drawing of the shrink-fitted axle assembly used in the
experiments. The assembly consists of an axle and boss. Both ends of the axle are
supported by two bali bearings on the test machine. The boss is midway between the
bearings and is given the bending load by the servo-hydraulic loading equipment.
1000
105., 835 ,6~
4175 417,5 - ~,.-,-
"~Z 2.0/ ~!" ~_,c~ ~,, ~12:]~1
~ ~ M35
oo 1
k_ 15o
Figure 8 -- Drawing of Shrink-Fitted Axle Assembly Used in the Fretting Fatigue Tests
Three kinds of axles were used in the experiments. One was manufactured by the
same method as the actual BUR axle. The others were finished by surface rolling which
introduces a surface compressive residual stress to the fitted part. One of the rolled axles
had two grooves cut at the contact edges. The grooves were introduced to make the boss
edges overhang. The rolled and overhung axle is simply named "the overhung axle". The
condition of surface rolling and the shape of the groove are shown in Fig. 9. Compressive
residual stress prevents growth of fatigue cracks [3, 8]. Overhanging of the boss edge
decreases the relative slip amount [9, 10]. Therefore, it is expected that the fretting
fatigue strength of the BUR axle may be improved by the surface rolling and the
overhanging. Since the actual BUR has more than a 500 mm diameter at the axle part and
weighs over 11 tons, the methods for improving the fretting fatigue strength are very
limited.
The contact pressure between the BUR axle and inner race of the roller bearing is
approximately 12 MPa. Interference of the fit at such a low contact pressure is too small
for the 40 mm-diameter axle with regard to machining tolerance; therefore, the contact
pressure of the axle assembly used in the experiment was 24 MPa. The fretting fatigue
limit in the experiment was defined as the fretting fatigue strength at 2 • 10 7 cycles
considering that the fracture of the BUR axles occurred at more than 107 cycles.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
440 FRETTINGFATIGUE: ADVANCES
Pressing load 7 k N L
Feed ~)dSmm~rev[ [ ~ R~
18 rpm
~_64&
The axle was made with SKD 6 forged steel. The boss was made with SFNCM
alloy steel. Both materials are defined by Japanese Industrial Standards. The chemical
compositions are shown in Table 1. The axle material was taken from the actual BUR.
The boss material was the same as the actual inner race. Table 2 shows the mechanical
properties of the materials used. Carburizing and quenching were done to the boss in
order to make the hardness equal to that of the actual inner race. The boss is twice as hard
as the axle in Vickers hardness.
The distribution of the axial residual stress of the surface-rolled axle is shown in
Fig. 10. The maximum compressive stress was approximately 1000 MPa at the surface.
The extent of the compressive residual stress was from the surface to an approximately
1.5 mm deep.
The results of the fretting fatigue tests are shown in Fig. 11. The fretting fatigue
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KUBOTA ET AL. ON ANALYSIS OF FAILURE IN BACKUP ROLE 441
l ' f l l l l l , , j ~ l ,
-500
t.
<
0 0.5 1 1.5 2
Depth below surface (ram)
Figure 10--Distribution of the Residual Stress of the Rolled Axle
limit based on the stress to break specimen, a,,.p, of the normal axle was in the range from
155 MPa to 172 MPa. Since the fatigue limit of the BUR material obtained by the
rotating bending fatigue test with the 12 ram-diameter specimens was 550 MPa [2], the
fatigue limit decreased approximately one-third due to fretting. Since the fretting fatigue
strength of fitted axles is significantly influenced by the diameter of the axle [11. 12], the
fretting fatigue strength of the actual BUR axle is assumed to be lower than that obtained
by the experiment.
The a,,,~ values of the rolled axle and the overhung axle were more than 182 MPa.
The improvement in the a,,.p of both axles were considered to be attained by the restraint
of the fatigue crack growth due to the residual stress induced by surface rolling.
The fretting fatigue limit based on a stress to initiate cracks, a,,fl, of the overhung
axle was more than 97 MPa. The a,r of the normal and rolled axle were less than
97 MPa. The overhanging of the contact edge has a positive effect on the improvement of
fatigue strength of the crack initiation.
The relative slip amount of the normal axle was measured by the displacement
sensor attached near the contact edge. Since the contact edge of the overhung axle was
covered by the overhung boss edge, the relative slip amount of the overhung axle could
not be directly measured. Therefore, the relative slip amount of the overhung axle was
evaluated by a finite element analysis [1]. Figure 12 shows the relative slip range
obtained by the finite element analysis and the experiments. The par~imeter controlling
the friction between the axle and the boss in the analysis was determined so that the
analytical slip amount coincided with the experimental one. Since the axial stress near the
contact edge was decreased by the groove, the relative slip amount of the overhung axle
is small in comparison with that of the normal axle. A decrease in the relative slip amount
leads to a decrease in the tangential force coefficient [13]. Therefore, it can be considered
that the ~,,,fl value of the overhung axle was improved.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
442 FRETTING FATIGUE: ADVANCES
200 . . . . . . . . . , ........ /
-X. . . . . . . . . . . . . . . . . . . . . . . . . Crack iength~
150 ~ ~ 9 250 lam
HNorma! ] 9 170
100 ]-] 9 Cracked] 9 120 -~
~Lx ~
50 ........ I ........ 9
106 107 108
200 ........ ,
@
150
* 6001006lam"1
100 Rolled
9 Cracked
I ,~2,o . . . . .
,00f
5 0 ~
o t
s
10 10 10
Number of cycles
40 Experimental l
--O-- Normal axle
Analytical
~ 3O --•-- Normal axle .-
--C}-- Overhung axle --"
e~ 2O
= 10
00 100 200
Bendingstress, o-~(MPa)
Figure 12--Relative Slip Range of 40 mm Diameter Axle
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KUBOTA ET AL. ON ANALYSIS OF FAILURE IN BACKUP ROLE 443
Figure 13 shows the fretting fatigue cracks. The initiation site of the fretting fatigue
cracks was not at the contact edge but at the fretted area inside the fitted part. which
was from 0.5 mm to 2 mm from the contact edge. The observations of the fretting wear
and fretting fatigue cracks show the same characteristics as the failed BUR. Since severe
wear wore away minute surface cracks [13], the fretting fatigue cracks were observed at
the fretted surface where the wear depth gradually decreased toward the center of the
fitted part.
The crack lengths measured are shown in Fig. 11. Although the o-,r value of the
overhung axle was higher than that of the rolled axle, the overhung axle had large cracks
above 172 MPa in stress amplitude. When the overhung axle was manufactured, the
grooves were cut after the surface rolling in order to keep the groove edge sharp.
Therefore, the compressive residual stress near the groove was presumed to decrease.
This could be the reason why the large cracks existed in the overhung axle.
On the basis of this study, surface rolling was applied to the actual BUR.
Furthermore, the diameter of the BUR axle was increased in order to decrease the stress
at the fretted part. Four years have passed and no BUR has failed after these changes
were made. To increase the diameter of the BUR axle is a difficult task, since
reconstructing the steel making rolling mill should be done. Although the rolled axle
endured 2 • 10 7 cycles with the higher stress amplitude compared with the normal axle in
the experiment, many non-propagating cracks, which are as much as 1 mm or more,
existed in the rolled axle. It should be noted that the BUR should endure more than 1 •
10 8 cycles of repetition load during its service life and that there is a kind of size effect on
the fretting fatigue strength [11]. This is the reason why the increase in the BUR axle
diameter for decreasing stress was achieved in cooperation with the roll user. Since the
test result of the overhung axle indicated that the improvement of the fretting fatigue
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
444 FRETTING FATIGUE: ADVANCES
strength was less than expected, the overhanging of the contact edge was not adopted.
Conclusion
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
KUBOTA ET AL. ON ANALYSIS OF FAILURE IN BACKUP ROLE 445
References
[1] Ohkomori, Y., Odanaka, H., Kubota, M., and Sakae, C., "The Analysis and
Prevention of Failure in Steel Making Backup Roll," Preprint of Japan Society of
Mechanical Engineers Kyushu Branch Summer Meeting, The Japan Society qf
Mechanical Engineers, No. 008-2, 2000, pp. 5-6, Japanese.
[2] Ohkomori, Y., and Nagamatsu, T., "Fretting Fatigue Strength Properties of
Journal Portion of Steel Making Backup Roll," Preprint of Regular Meeting, The
Iron andSteel Institute of Japan, CAMP-ISIJ Vol. 12, 1999, pp. 1172, Japanese.
[3] Hirakawa, K., "Case Histories and Prevention of Fretting Fatigue Failure,"
Sumitomo Metals, Vol. 46, No. 4, 1994, pp. 4-16, Japanese.
[4] Wh61er, A., "Versuche fiber Biegung und Verdrehung von
Eisenbahnwagen-Achsen W~ihrend der Fahrt," Zeit. Bauwesen, Vol. 8, 1858, pp.
641-652.
[5] Wh61er, A., "Versuche fiber die Relative Festigkeit von Eisen," Stahl und Kupfer,
Vol. 16, 1866, pp. 67-84.
[61 Makino, T., Yamamoto, M., and Hirakawa, K., "Fracture Mechanics Approach to
the Fretting Fatigue Strength of Axle Assemblies," ASTM STP 1367, D. W.
Hoeppner, V. Chandrasekaran and C. B. Elliott III, Eds., American Society for
Testing and Materials, West Conshohocken, PA, 2000, pp. 509-522.
[7] Makino, T., Yamamoto, M., and Hirakawa, K., "The Fretting Fatigue Crack
Initiation Behavior at Press-Fitted Axle Assembly with Variable Stress Loading
(Effects of Stress Cycle Ratio, Number of Load Levels and Axle Size),"
Proceedings of l 2th International Wheelset Congress, 1998, pp. 147-152.
[8] Horger, O. J., and Maulbetsch, J. L., "Increasing the Fatigue Strength of
Press-Fitted Axle Assemblies by Surface Rolling," Journal oJ Applied
Mechanics, Vol. 3, 1936, pp. A-91-A-98.
[9] Hirakawa, K., Toyama, M., and Kubota, M., "The Analysis and Prevention of
Failure in Railway Axles," International Journal of Fatigue, Vol. 20, No. 2,
1998, pp.135-144.
[IO] Maxwell, W. W., Dudly, B. R., Cleary A. B., Richards, J., and Shaw, J.,
"Measures to Counter Fatigue Failure in Railway Axles," Journal o/" the
Institution of Locomotive Engineers, Vol. 58, No.2, 1968, pp. 136-171.
[11] Hirakawa, K., and Kubota, M., "On the Fatigue Design Method for High-Speed
Railway Axles," Proceedings of the Institution of Mechanical Engineers. Journal
ofRail and Rapid Transit,Vol. 215, Part F, 2001, pp.73-82.
[12] Kondo, Y., and Bodai, M., "Study on Fretting Fatigue Crack Initiation
Mechanism Based on Local Stress at Contact Edge," Transaction o! Japan
Society of Mechanical Engineers, Series A, Vol. 63, No. 608, 1997, pp.669-676.
[13] Nishioka, K., and Hirakawa, K., "Fundamental Investigation of Fretting Fatigue,
Part 5, Effect of Relative Slip Amplitude," Bulletin of Japan Society of
Mechanical Engineers, Vol. 12, No. 52, 1969, pp. 692-697.
[14] Nishioka, K., and Hirakawa, K., "Fundamental Investigation of Fretting Fatigue,
Part 3, Some Phenomena and Mechanisms of Surface Cracks," Bulletin o/Japan
Society of Mechanical Engineers, Vol. 12, No. 51, 1969, pp. 397-407.
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
STP1425-EB/Mar. 2003
Author Index
A Kimua, T., 76
Kondoh, Kazunori, 33, 61
Akiyama, Taisuke, 220 Kondo, Yoshiyuki,434
Araujo, J. Alex, 133 Kubota, Masanobu, 434
Ashbaugh, Noel E., 307 Kumuthini, K., 353
C L
O
Irving, Phil E., 235
Ochi, Y., 220
J Odanaka, Hidenori, 434
Ohkomori, Yoshihiro, 434
Jain, Vinod K., 338 Okane, Masaki, 273, 385
K R
S V
Vincent, L6o, 17
Sakae, Chu, 434
Sato, Kenkichi, 76 W
Shiozawa, Kazuaki, 385
Shirai, S., 353 Watanabe, Takashi, 159
Suzuki, Kazutaka, 385 Waterhouse, Robert B., 3
Swalla, D. R., 89
X
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by
(PDVSA Los Teques) pursuant to License Agreement. No further reproductions authorized.
STP 1425-E B/Ma r.2003
Subject Index
A
Copyright by ASTM Int'l (all rights reserved); Sat Dec 31 13:13:34 EST 2011
Downloaded/printed by