    Tpu WHT 6420 Tds

    Uploaded by

    Jose Miguel Navarrete Roa
    WHT-6420 is a polyester-based TPU hot-melt adhesive supplied as white or yellow pellets. It has high viscosity, fast crystallization, and good adhesion to materials like PVC, PU, fabric and leather. It can be used as a solution adhesive for footwear and fabrics or as a hot-melt adhesive film and tape. When used as a solution, it has a viscosity between 1500-2200 mPa.s at 15% solids in MEK at 23°C. Its suggested activation temperature is 60-100°C and it has a very fast crystallization rate.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Tpu WHT 6420 Tds

    Uploaded by

    Jose Miguel Navarrete Roa
    332 views1 page
    WHT-6420 is a polyester-based TPU hot-melt adhesive supplied as white or yellow pellets. It has high viscosity, fast crystallization, and good adhesion to materials like PVC, PU, fabric and leather. It can be used as a solution adhesive for footwear and fabrics or as a hot-melt adhesive film and tape. When used as a solution, it has a viscosity between 1500-2200 mPa.s at 15% solids in MEK at 23°C. Its suggested activation temperature is 60-100°C and it has a very fast crystallization rate.

    Original Description:

    Manual pp

    Original Title

    Tpu Wht 6420 Tds

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    WHT-6420 is a polyester-based TPU hot-melt adhesive supplied as white or yellow pellets. It has high viscosity, fast crystallization, and good adhesion to materials like PVC, PU, fabric and leather. It can be used as a solution adhesive for footwear and fabrics or as a hot-melt adhesive film and tape. When used as a solution, it has a viscosity between 1500-2200 mPa.s at 15% solids in MEK at 23°C. Its suggested activation temperature is 60-100°C and it has a very fast crystallization rate.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    332 views1 page

    Tpu WHT 6420 Tds

    Uploaded by

    Jose Miguel Navarrete Roa
    WHT-6420 is a polyester-based TPU hot-melt adhesive supplied as white or yellow pellets. It has high viscosity, fast crystallization, and good adhesion to materials like PVC, PU, fabric and leather. It can be used as a solution adhesive for footwear and fabrics or as a hot-melt adhesive film and tape. When used as a solution, it has a viscosity between 1500-2200 mPa.s at 15% solids in MEK at 23°C. Its suggested activation temperature is 60-100°C and it has a very fast crystallization rate.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    Product Datasheet

    WHT-6420

    Description WHT-6420 is polyester-based TPU hot-melt


    adhesive, supplied in form of white or slightly Property
    yellowish pellets with the characteristic of
    high viscosity, fast crystallization rate, and
    good adhesion strength to PVC, PU, fabric PRO PERT Y Method Units 6420
    and genuine leather.
    Application Solution adhesive for footwear, fabric
    Density ASTM D 792 g/cm3 1.2
    coatings, hot-melt adhesive film and tape.

    Working WHT-6420 is generally used as solutions in Tensile


    ASTM D 412 MPa 44
    MEK, EAc, TOL, THF, or Acetone, with strength
    ins tructions 15~20% solid content.
    While WHT-6420 is used as hot-melt, the Ultimate
    ASTM D 412 % 700
    characteristics of the extruder are the elongation
    followings:
    Solution
     L/D ratio between 25:1 and 30:1 for
    extrusion. viscosity (15%
    ISO 3219 mPa.s 1500~2200
     The extruder screw must have 3 zones in MEK,
    and a compression ratio between 2:1 23ºC)
    and 3:1.Screws with a compression
    ratio greater than 4:1 should be Crystallization
    Very Fast
    avoided. Rate
     The extruder screw should have a
    continuous regulation devic e and a Suggested
    working power higher than for Activation °C 60~100
    processing other plastics. temperature
    For optimum results, previous drying of the product during 3-6
    These products can only be ordered in typical quantities.
    hours at 40~50℃ is advisable, in a hot air circulatory, vacuum or
    desiccant-air dryer. The suggested processing-temperature profiles Please contact your sales representative for details.
    for injection are depicted in the table below.

    T - die Extrusion Guideline for WHT-6420

    Pr oduc t Die (℃) Metering ( ℃) Compression(℃) F eed ( ℃) Dr ying temperatur e( ℃) Dr ying time ( h)
    6420 180 175 165 150 30-45 3-6
    No te: The actual processing temperature should be adjusted properly while auxiliary materials were used.

    Re grind usage
    Where end-use requirements permit, up to 20% resin regrind may be used with virgin material, provided that the material is kept free of
    contamination and is properly dried (see section on Drying). Any regrind used must be generated from properly molded/extruded parts,
    sprues, runners, trimmings, and/or films. All regrind used must be clean, uncontaminated, and thoroughly blended with virgin resin pri or
    to drying and processing. Under no circumstances should degraded, discolored, or contaminated material be used for regrind. M aterials
    of this type should be discarded. Improperly mixed and/or dried regrind may diminish the desired properties. It is critical that you test
    finished parts produced with any amount of regrind to ensure that your end-use performance requirements are fully met.

    Di sclaimer
    The information provided here is for reference only. The specification will be provided in the quality certificate or in the contract. It is the
    user’s responsibility to test the material and its suitability for a process. We have no control over what another party does with the
    material and we cannot take any responsibility for another party’s action. Nor will we be responsible for any indirect damage s while using
    our products. The user is welcome to contact our customer and technical se rvice center with questions on our products

    Y a ntai Wanhua Polyurethanes Co., Ltd


    Add: No.7 South Xingfu Road, Yantai, Shandong 264002, P. R. China
    Tel: +86-535-338-8825 Fax: +86-535-685-7160 E d ition 2011
    Website:www.wanthane.comE-mail:tpuservice@ytpu.com Page 1 / 1

    You might also like