Technical Data Sheet

Approved 1505;1506 1,2 1505 phenolic/novolac ^(ValidationDate) 1

epoxy

Epoxy HR

Product description
This is a two component polyamine cured phenolic/novolac epoxy coating. It is heat resistant up to 205 °C (401
°F) and can be applied on hot substrates up to 150 °C (302 °F). The standard aluminium version may be used
as primer, mid coat or finish coat. Suitable for properly prepared carbon steel, galvanised steel, stainless steel
and aluminium substrates.

Typical use
Protective:
Designed as corrosion protection for surfaces operating at elevated temperatures where long corrosion
protection is desired. Suitable for insulated and non insulated surfaces.
Other

Colours
aluminium, light grey, red, white, bright aluminium (RAL 9006)

Bright aluminium is a specialty bright aluminium finish similar to RAL 9006. Can only be used as a finish coat.

Product data
Property Test/Standard Description

Solids by volume ISO 3233 63 ± 2 %

Gloss level (GU 60 °) ISO 2813 matt (0-35)
Flash point ISO 3679 Method 1 28 °C
Density calculated 1.6 kg/l
VOC-US/Hong Kong US EPA method 24 (tested) 330 g/l
(CARB(SCM)2007, SCAQMD rule 1113, Hong Kong)
VOC-EU IED (2010/75/EU) (theoretical) 365 g/l
VOC-China GB/T 23985-2009 (tested) 330 g/l
VOC-Korea Korea Clean Air Conservation Act (tested) 383 g/l

The provided data is typical for factory produced products, subject to slight variation depending on colour.
All data is valid for mixed paint.
Gloss description: According to Jotun Performance Coatings' definition.

Film thickness per coat

Typical recommended specification range

Dry film thickness 100 - 200 μm

Wet film thickness 160 - 320 μm
Theoretical spreading rate 6.3 - 3.2 m²/l

Date of issue: 7 March 2019 Page: 1/5

This Technical Data Sheet supersedes those previously issued.

The Technical Data Sheet (TDS) is recommended to be read in conjunction with the Safety Data Sheet (SDS) and the
Application Guide (AG) for this product. For your nearest local Jotun office, please visit our website at www.jotun.com
Technical Data Sheet
Epoxy HR

Surface preparation
To secure lasting adhesion to the subsequent product all surfaces shall be clean, dry and free from any
contamination.

Surface preparation summary table

Surface preparation

Substrate Minimum Recommended

Carbon steel St 2 (ISO 8501-1) Sa 2½ (ISO 8501-1)

Stainless steel The surface shall be hand or machine Abrasive blast cleaning to achieve a
abraded with non-metallic abrasives surface profile using non-metallic
or bonded fibre machine or hand abrasive media which is suitable to
abrasive pads to impart a scratch achieve a sharp and angular surface
pattern to the surface. profile.
Aluminium The surface shall be hand or machine Abrasive blast cleaning to achieve a
abraded with non-metallic abrasives surface profile using non-metallic
or bonded fibre machine or hand abrasive media which is suitable to
abrasive pads to impart a scratch achieve a sharp and angular surface
pattern to the surface. profile.
Galvanised steel The surface shall be clean, dry and Sweep blast-cleaning using non-
appear with a rough and dull profile. metallic abrasive leaving a clean,
rough and even pattern.
Shop primed steel Dry, clean and approved inorganic Sa 2½ (ISO 8501-1)
zinc shopprimer.
Coated surfaces Clean, dry and undamaged compatible Clean, dry and undamaged compatible
coating coating

Optimum performance, including adhesion, corrosion protection, heat resistance and chemical resistance is
achieved with recommended surface preparation.

Application
Application methods
The product can be applied by

Spray: Use airless spray.

Brush: Recommended for stripe coating and small areas. Care must be taken to achieve the
specified dry film thickness.

Product mixing ratio (by volume)

Epoxy HR Comp A 6.5 part(s)

Epoxy HR Comp B 1 part(s)

Date of issue: 7 March 2019 Page: 2/5

This Technical Data Sheet supersedes those previously issued.

The Technical Data Sheet (TDS) is recommended to be read in conjunction with the Safety Data Sheet (SDS) and the
Application Guide (AG) for this product. For your nearest local Jotun office, please visit our website at www.jotun.com
Technical Data Sheet
Epoxy HR

Thinner/Cleaning solvent
Thinner: Jotun Thinner No. 23

Guiding data for airless spray

Nozzle tip (inch/1000): 17-21
Pressure at nozzle (minimum): 150 bar/2100 psi

Drying and Curing time

Substrate temperature 10 °C 15 °C 23 °C 40 °C 100 °C

Surface (touch) dry 16 h 12 h 4h 2 h 30 min

Walk-on-dry 26 h 20 h 10 h 4 h 1h
Dry to over coat, minimum 26 h 20 h 10 h 4 h 1h
Dried/cured for service 21 d 14 d 7d 3 d 1d

For maximum overcoating intervals, refer to the Application Guide (AG) for this product.

Drying and curing times are determined under controlled temperatures and relative humidity below 85 %, and
at average of the DFT range for the product.

Surface (touch) dry: The state of drying when slight pressure with a finger does not leave an imprint or reveal
tackiness.

Walk-on-dry: Minimum time before the coating can tolerate normal foot traffic without permanent marks,
imprints or other physical damage.

Dry to over coat, minimum: The recommended shortest time before the next coat can be applied.

Dried/cured for service: Minimum time before the coating can be permanently exposed to the intended
environment/medium.

Induction time and Pot life

Paint temperature 23 °C

Induction time 20 min

Pot life 4h

Reduced at higher temperatures.

Date of issue: 7 March 2019 Page: 3/5

This Technical Data Sheet supersedes those previously issued.

The Technical Data Sheet (TDS) is recommended to be read in conjunction with the Safety Data Sheet (SDS) and the
Application Guide (AG) for this product. For your nearest local Jotun office, please visit our website at www.jotun.com
Technical Data Sheet
Epoxy HR

Heat resistance
Temperature
Continuous Peak

Dry, atmospheric 205 °C -

The temperatures listed relate to retention of protective properties. Aesthetic properties may suffer at these
temperatures.

Product compatibility
Depending on the actual exposure of the coating system, various primers and topcoats can be used in
combination with this product. Some examples are shown below. Contact Jotun for specific system
recommendation.

Previous coat: inorganic zinc shop primer

Subsequent coat: phenolic/novolac epoxy, silicone acrylic

Packaging (typical)
Volume Size of containers
(litres) (litres)

Epoxy HR Comp A 16.3 20

Epoxy HR Comp B 2.5 3

The volume stated is for factory made colours. Note that local variants in pack size and filled volumes can vary
due to local regulations.

Storage
The product must be stored in accordance with national regulations. Keep the containers in a dry, cool, well
ventilated space and away from sources of heat and ignition. Containers must be kept tightly closed. Handle
with care.

Shelf life at 23 °C
Epoxy HR Comp A 24 month(s)
Epoxy HR Comp B 24 month(s)

In some markets commercial shelf life can be dictated shorter by local legislation. The above is minimum shelf
life, thereafter the paint quality is subject to re-inspection.

Date of issue: 7 March 2019 Page: 4/5

This Technical Data Sheet supersedes those previously issued.

The Technical Data Sheet (TDS) is recommended to be read in conjunction with the Safety Data Sheet (SDS) and the
Application Guide (AG) for this product. For your nearest local Jotun office, please visit our website at www.jotun.com
Technical Data Sheet
Epoxy HR

Caution
This product is for professional use only. The applicators and operators shall be trained, experienced and have
the capability and equipment to mix/stir and apply the coatings correctly and according to Jotun's technical
documentation. Applicators and operators shall use appropriate personal protection equipment when using this
product. This guideline is given based on the current knowledge of the product. Any suggested deviation to suit
the site conditions shall be forwarded to the responsible Jotun representative for approval before commencing
the work.

Health and safety

Please observe the precautionary notices displayed on the container. Use under well ventilated conditions. Do
not inhale spray mist. Avoid skin contact. Spillage on the skin should immediately be removed with suitable
cleanser, soap and water. Eyes should be well flushed with water and medical attention sought immediately.

Colour variation
When applicable, products primarily meant for use as primers or antifoulings may have slight colour variations
from batch to batch. Such products may fade and chalk when exposed to sunlight and weathering.

Disclaimer
The information in this document is given to the best of Jotun's knowledge, based on laboratory testing and
practical experience. Jotun's products are considered as semi-finished goods and as such, products are often
used under conditions beyond Jotun's control. Jotun cannot guarantee anything but the quality of the product
itself. Minor product variations may be implemented in order to comply with local requirements. Jotun reserves
the right to change the given data without further notice.

Users should always consult Jotun for specific guidance on the general suitability of this product for their needs
and specific application practices.

If there is any inconsistency between different language issues of this document, the English (United Kingdom)
version will prevail.

Date of issue: 7 March 2019 Page: 5/5

This Technical Data Sheet supersedes those previously issued.

The Technical Data Sheet (TDS) is recommended to be read in conjunction with the Safety Data Sheet (SDS) and the
Application Guide (AG) for this product. For your nearest local Jotun office, please visit our website at www.jotun.com