    ISO 898 Grade 10.9

    Uploaded by

    Mihaela Nastase
    This document provides information on steel grade 10.9, including its chemical composition, mechanical properties, and transformation temperatures. The steel grade is suitable for quenching and tempering and requires 90% martensite content. It has a carbon content between 0.4-0.45%, silicon 0.15-0.35%, and manganese 0.75-0.9%. Mechanical properties include a minimum yield strength of 940 MPa and tensile strength over 1040 MPa. Transformation temperatures are MS at 400°C, AC1 at 723°C, and AC3 at 827°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    ISO 898 Grade 10.9

    Uploaded by

    Mihaela Nastase
    325 views2 pages
    This document provides information on steel grade 10.9, including its chemical composition, mechanical properties, and transformation temperatures. The steel grade is suitable for quenching and tempering and requires 90% martensite content. It has a carbon content between 0.4-0.45%, silicon 0.15-0.35%, and manganese 0.75-0.9%. Mechanical properties include a minimum yield strength of 940 MPa and tensile strength over 1040 MPa. Transformation temperatures are MS at 400°C, AC1 at 723°C, and AC3 at 827°C.

    Original Description:

    ISO 898 grade 10.9

    Original Title

    ISO 898 grade 10.9

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on steel grade 10.9, including its chemical composition, mechanical properties, and transformation temperatures. The steel grade is suitable for quenching and tempering and requires 90% martensite content. It has a carbon content between 0.4-0.45%, silicon 0.15-0.35%, and manganese 0.75-0.9%. Mechanical properties include a minimum yield strength of 940 MPa and tensile strength over 1040 MPa. Transformation temperatures are MS at 400°C, AC1 at 723°C, and AC3 at 827°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    325 views2 pages

    ISO 898 Grade 10.9

    Uploaded by

    Mihaela Nastase
    This document provides information on steel grade 10.9, including its chemical composition, mechanical properties, and transformation temperatures. The steel grade is suitable for quenching and tempering and requires 90% martensite content. It has a carbon content between 0.4-0.45%, silicon 0.15-0.35%, and manganese 0.75-0.9%. Mechanical properties include a minimum yield strength of 940 MPa and tensile strength over 1040 MPa. Transformation temperatures are MS at 400°C, AC1 at 723°C, and AC3 at 827°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    Material data sheet Last revised: Tue, 19 Mar 2019 09:05:39 GMT

    Steel grade

    ISO 898 grade 10.9 All

    General Information
    The steel grade variants are suitable for quenching and tempering to 8.8 or 10.9 properties. Required 90% martensite in the centre of the material
    is achieved up to diameter of each variant by oil quenching. The limiting factor for maximum size is the amount of the martensite in the core of the
    material. Therefore the same maximum diameters apply for 8.8 fasteners.

    For additional Heat Treatment Data, please visit the Heat Treatment Guide.

    Chemical composition
    Variant Cast Di C% Si % Mn % P% S% Cr % Mo %
    Min 0.40 0.15 0.75 0.000 0.000 0.90 0.15
    42CrMnMo4-4,SAE 4140 (6115) CC 6.8
    Max 0.45 0.35 0.90 0.020 0.025 1.10 0.25

    Mechanical Properties
    Dimension Yield strength min Tensile strength Elongation Reduction of area Impact (ISO-V)
    Variant Condition Format Hardness
    [mm] [MPa] [MPa] A5 [%] Zmin [%] strengthmin
    42CrMnMo4-4,SAE Round
    +QT 25 < 60 940 > 1040 9 48 316-375 HB -20 °C 27 J (long)
    4140 (6115) bar
    Rp0.2 * Reh, ** Rel

    Transformation temperatures
    Temperature °C
    MS 400
    AC1 723
    AC3 827

    Other properties (typical values)


    Youngs module (GPa) Poisson´s ratio (-) Shear module (GPa) Density (kg/m3)
    210 0.3 80 7800
    Average CTE 20-300°C Specific heat capacity 50/100°C Thermal conductivity Ambient Electrical resistivityAmbient temperature
    (µm/m°K) (J/kg°K) temperature (W/m°K) (µΩm)
    12 460 - 480 40 - 45 0.20 - 0.25

    Contact us
    Would you like to know more about our offers? Don´t hesitate to contact us:
    Via e-mail: info@ovako.com
    Via telephone: +46 8 622 1300
    For more detailed information please visit http://www.ovako.com/en/Contact-Ovako/

    Disclaimer
    The information in this document is for illustrative purposes only. The data and examples are only general recommendations and not a warranty or a guarantee.
    The suitability of a product for a specific application can be confirmed only by Ovako once given the actual conditions.The purchaser of an Ovako product has
    the responsibility to ascertain and control the applicability of the products before using them. Continuous development may necessitate changes in technical
    data without notice. This document is only valid for Ovako material. Other material, covering the same international specifications, does not necessarily comply
    with the properties presented in this document.