SN359 1 2009 07 e材料对照表 PDF
SN359 1 2009 07 e材料对照表 PDF
Materials
Comparison of German and Chinese SN 359-1
Selection
1 Field of application
The comparison of German and/or European and Chinese materials is based on the selected materials given in the Standards
Book, Part 1. It is intended for selecting comparable Chinese materials and their use instead of the materials specified on the
drawings.
Missing comparative materials will be supplemented in the new edition of the standard and can be determined until then by
inquiry at the standards office.
This copy will not be updated in case of changes!
2 Normative references
SMS Siemag Standards Book 2008, Part 1
identical = Both materials are identical with regard to their essential properties
similar = Both materials are identical with regard to their essential properties; existing deviations must be checked
with regard to the usability, if necessary.
do not use = The comparative material does not meet the properties of the drawing material and should not be used.
Matching/deviation can be immediately detected by means of the listed values and assessed.
Anhang/Appendix A1 (normativ):
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
Engineering steels
C content 0.28 to 0.38%,
E295 1. 0050 St 50-2 DIN EN 10025-2 - Q275 Z GB 700-88 only limited weldability, identical
Z = Fully killed steel only is permissible,
E335 1. 0060 St 60-2 DIN EN 10025-2 - Q 345 A GB T 1591-94 Fully killed steel is permissible identical
E360 1. 0070 St 70-2 DIN EN 10025-2 - Q 390 A GB T 1591-94 Fully killed steel is permissible identical
St 37-2
KV at room temperature,
S235JR 1. 0038 R St 37-2 DIN EN 10025-2 Q 235 B GB 700-88 Fully killed steel is permissible identical
unkilled not permitted
S235JRG2
R St 37-3 KV at 0°C, unkilled not Fully killed steel only permissible,
S235J0 1. 0114 DIN EN 10025-2 Q 235 C GB 700-88 similar
S235J0G2 permitted KV at 0°C ,
Fully killed or double-killed steel is
Q St 37-3N KV at -20°C, unkilled not
S235J2 1. 0117 DIN EN 10025-2 Q 235 D GB 700-88 permissible, similar
S235J2G3 permitted
KV at -20°C ,
St 44-2 C content must be limited to 0.22%,
KV at room temperature,
S275JR 1. 0044 S275JRG2 DIN EN 10025-2 Q 275 Z GB 700-88 otherwise only limited weldability, notch similar
unkilled not permitted
S275JRC impact energy not guaranteed.
C content must be limited to 0.22%, notch
Q 275 GB 700-88 do not use
KV at 0°C, unkilled not impact energy not guaranteed.
S275J0 1. 0143 St 44-3 DIN EN 10025-2
permitted Fully killed steel is permissible,
Q 345 C GB T 1591-94 similar
KV at 0°C,
St 44-3N C content must be limited to 0.22%, notch
Q 275 GB 700-88 do not use
S275J2G3 KV at -20°C, unkilled not impact energy not guaranteed.
S275J2 1. 0145 DIN EN 10025-2
S275J2G3C permitted Fully killed steel is permissible,
S275J2G4
Q 345 D GB T 1591-94 identical
KV at -20°C.,
KV at room temperature,
S355JR 1. 0045 - DIN EN 10025-2 Q 345 B GB T 1591-94 Fully killed steel is permissible, identical
unkilled not permitted
KV at 0°C, unkilled not Fully killed steel is permissible,
S355J0 1. 0553 S355J0G2 DIN EN 10025-2 Q 345 C GB T 1591-94 identical
permitted KV at room 0°C,
KV at -20°C, unkilled not Fully killed steel is permissible,
S355J2 1.0577 S355J2G3 DIN EN 10025-2 Q 345 D GB T 1591-94 identical
permitted KV at -20°C.,
S620Q 1.8914 StE 620V DIN EN 10025-6 quenched & tempered 18CrMnMoB Q/ZB 61-73 Fully killed steel is permissible, similar
S690Q 1. 8931 StE690V DIN EN 10025-6 quenched & tempered Q690E/Q690D GB/T 16270-96 Fully killed steel is permissible, similar
Seite/Page 2 von/of 40
SN359-1 : 2009-07
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
C45 +C or +SH 1. 0503 C 45 DIN EN 10277-2 45 GB 699-88 Z = killed only is permissible similar
Bright steel products,
+C = cold drawn
C15 +C or +SH 1. 0401 C15 DIN EN 10277-2 15 GB 699-88 Z = killed only is permissible similar
+SH = as rolled and
turned
E 295GC +C or +SH 1. 0533 St 50-2 KG DIN EN 10277-2 Q 275 GB 700-88 similar
Sheets
DC01 1. 0330 St 12 DIN EN 10130 08F GB 699-88 Sameness must be checked in every case similar
Pipes, tubes
20 GB 8163-87
20G GB 5310-95
20 GB 8163-87 similar
P235TR2 1. 0255 QSt 37.0 DIN EN 10216-1 normalised 20 GB 8162-87 KV is not guaranted similar
P355N 1.0562 StE 355 DIN EN 10216-3 normalised 16Mn GB 6479-86 similar
Seite/Page 3 von/of 40
SN359-1 : 2009-07
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
51CrV4+QT 18.159 - DIN EN 10083-1 quenched & tempered 50CrVA4 GB/T 1222 +QT similar
25CrMo4+QT 1.7218 25 CrMo 4 V DIN EN 10083-1 quenched & tempered 30CrMo GB 3077-88 Heat treatment strength to be agreed upon similar
42CrMo4+QT 1.7225 42 CrMo 4 V DIN EN 10083-1 quenched & tempered 42CrMo GB 3077-88 Heat treatment strength to be agreed upon similar
50CrMo4+QT 1.7228 50 CrMo 4 V DIN EN 10083-1 quenched & tempered 50CrMo EZB 1184-93 similar
34CrNiMo6+QT 1.6582 34 CrNiMo 6 V DIN EN 10083-1 quenched & tempered 34CrNi3Mo EZB 1184-93 similar
30CrNiMo8+QT 1.6580 30 CrNiMo 8 V DIN EN 10083-1 quenched & tempered 30Cr2Ni2Mo EZB 1184-93 similar
Seite/Page 4 von/of 40
SN359-1 : 2009-07
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
Nitriding steels
32Cr3MoVA
14CrMoV6-9 1.7735 - SEL 2003 ? +QT and nitiding Ä similar
38CrMoAlA
34CrAlMo5-10 1.8507 - DIN EN 10085 38CrMoAl GB/T 3077-99 similar
Heat-resisting steels
X20CrMoV11-1 1.4922 X 22 CrMoV 12 1 DIN EN 10222-2 1Cr11MoV GB 1221-92 similar
Tool steel
60WCrV 7 1.2550 60 WCrV7 DIN EN ISO 4957 6 Cr W 2 Si GB 1299-85 similar
Seite/Page 5 von/of 40
SN359-1 : 2009-07
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
32CrMo12 1.7361 - SEW 550 +QT 30Cr2Ni2Mo EZB 1184-93 +QT similar (~)
X4CrNi18-10 1.4301 X 5 CrNi 18 9 DIN EN 10250-4 solution annealing 0Cr18Ni9 GB/T 1220-92 similar
X6CrNiTi18-10 1.4541 X 10 CrNiTi 18 9 DIN EN 10250-4 solution annealing 0Cr18Ni10Ti GB/T 1220-92 similar
X6CrNiMoTi17-12-2 1.4571 X 10 CrNiMoTi 18 10 DIN EN 10250-4 solution annealing 0Cr18Ni12Mo2Ti GB/T 1220-92 similar
X5CrNiMo17-12-2 1.4401 X 5 CrNiMo17 12 2 DIN EN 10250-4 solution annealing 0Cr17Ni12Mo2 GB/T 1220 / 1221-92 similar
X4CrNiMo16-5-1 1.4418 - DIN EN 10250-4 solution annealing Not known Not known -
Seite/Page 6 von/of 40
SN359-1 : 2009-07
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
Stainless steels
X20Cr13 1.4021 X 20 Cr 13 DIN EN 10088-1 to 3 2Cr13 GB/T 1220-92 similar
X46Cr13 1.4034 X 46 Cr 13 DIN EN 10088-1 to 3 HRC min. 55 4Cr13 GB/T 1220-92 HRC min 50 similar
X5CrNiMo17-12-2 1.4401 X 5 CrNiMo17 12 2 DIN EN 10088-1 to 3 solution annealing 0Cr17Ni12Mo2 GB/T 1220-92 similar
X6CrNiTi18-10 1.4541 X 10 CrNiTi 18 9 DIN EN 10088-1 to 3 solution annealing 0Cr18Ni10Ti GB/T 1220-92 similar
0Cr18Ni10Ti GB 1221-92 similar
0Cr18Ni10Ti GB 3280-92 similar
X6CrNiMoTi17-12-2 1.4571 X 10 CrNiMoTi 18 10 DIN EN 10088-1 to 3 solution annealing 0Cr18Ni12Mo2Ti GB T 4237-92 similar
Seite/Page 7 von/of 40
SN359-1 : 2009-07
Anhang/Appendix A2 (normativ):
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
G20Mn5 +N or +QT 1 .6220 GS-20Mn5V DIN EN 10293 quenched & tempered ZG 20 Mn JB T 6402-92 similar
Important! C content 0.40 to 0.50 %, only
GS-52N 1.O552 GS-52N DIN 1681 normalised ZG 270 - 500 GB 11352-89 do not use
limited weldability.
No composition specification, only P and S
ZGD 290 - 510 GB T 14408-93 similar
max. 0.040 each
G28Mn6 +QT1 or QT2 1. 1165 GS-30Mn5V DIN EN 10293 quenched & tempered ZG 30 Mn JB T 6402-92 similar
For weldet parts the C-content must be <
G26 CrMo4 +QT1 or +QT2 1. 7221 GS-25 CrMo4V DIN EN 10293 quenched & tempered ZG 35 Cr1Mo JB T 6402-92 similar
0,30%
G42 CrMo4 +QT1 or QT2 1. 7231 GS-42 CrMo4V DIN EN 10293 quenched & tempered ZG 42Cr1Mo JB T 6402-92 similar similar
G35CrNiMo6-6 +N or +QT1 or
1. 6582 GS-34CrNiMo6V DIN EN 10293 quenched & tempered ZG 34 Cr2Ni2Mo JB T 6402-92 similar
QT2
GS-34 CrMo4V 1. 7220 GS-34 CrMo4V DIN 17205 quenched & tempered ZG 35Cr1Mo JB T 6402-92 similar
G42CrMo4 1. 7231 GS-42CrMo4 SEW 835 quenched & tempered ZG 42 Cr1Mo JB T 6402-92 similar
G50CrMo4 1. 7232 GS-50CrMo4 SEW 835 quenched & tempered ZG 50 Cr1Mo JB T 6402-92 similar
Seite/Page 8 von/of 40
SN359-1 : 2009-07
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
G20Mo5+QT 1. 5419 GS-22Mo4V DIN EN 10213-2 quenched & tempered ZG 20MnMo JB T 6402-92 +QT similar
C content higher, V alloyed, Rm and Re
G17CrMo5-5+QT 1. 7357 GS-17CrMo55V DIN EN 10213-2 quenched & tempered ZG 20CrMoV JB / T 7024-93 similar
identical
ZG 15Cr1Mo1V JB / T 7024-93 similar
G17CrMoV5-10+QT 1. 7706 GS-17CrMoV5 11V DIN EN 10213-2 quenched & tempered +QT (Ä)
ZG17Cr1Mo1VG GB/T 16253-1996 similar
GX23CrMoV12-1+QT 1. 4931 G-X22CrMoV12 1V DIN EN 10213-2 quenched & tempered ZG23Cr12Mo1NiVG GB/T16253-1996 +QT (Ä) similar
Seite/Page 9 von/of 40
SN359-1 : 2009-07
Anhang/Appendix A3 (normativ):
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
GJS-400-18U 1062 GGG-40 DIN EN 1563 U = test bar attached Not known Not known -
GJS-400-15U 1072 GGG-40 DIN EN 1563 U = test bar attached QT 400-15 GB 1348-88 identical
GJS-500-7U 1082 GGG-50 DIN EN 1563 U = test bar attached QT 500-7 GB 1348-88 identical
GJS-600-3U 1092 GGG-60 DIN EN 1563 U = test bar attached QT 600-3 GB 1348-88 identical
GJS-700-2U 1102 GGG-70 DIN EN 1563 U = test bar attached QT 700-2 GB 1348-88 identical
EN-GJMW-400-5 EN-JM 1030 GTW-40-05 DIN EN 1562 Not known Not known -
Seite/Page 10 von/of 40
SN359-1 : 2009-07
Anhang/Appendix A4 (normativ):
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
Seite/Page 11 von/of 40
SN359-1 : 2009-07
German Chinese
Material designation
Material No. Former design. Standard Remark Material design. Standard Remark Matching of properties:
Basis NH, Teil 1
White bronze
Produkt from Main-
Not according to standard, White bronze with special guaranteed Metall_Foundry
Main-Metall*
values.
Not known Not known -
(www.main-
metall.com)
Seite/Page 12 von/of 40
SN359-1 : 2009-07
Anhang/Appendix B1 (normativ):
Comparison of german and chinese material properties, steels
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
≤ 16 295
20
16 - 40 285
40 - 63 275 470-610 19
St 50-2 63 - 80 265
Unkilled not permitted
E 295 +N DIN EN 10025-2 1.0050 +N 18 - - - - - - 0,055 0,055 0,012
Notch impact energy not guaranteed.
80 - 100 255
Non-alloy structural steels
Fe 490-2
≤16 275 20
16 - 40 265 19
40 - 60 255 18
0,28 - 0,50 - Z = Fully killed steel is permissible
Q275 Z GB 700-88 +N 490-630 - - - 0,35 0,05 0,045
0,38 0,80 +N Normalised is permissible
60 - 100 245 17
>150 225 15
≤ 16 335
16
16 - 40 325
40 - 63 315 570-770 15
63 - 80 305
Non-alloy structural steels
St 60-2
Unkilled not permitted
E 335 +N DIN EN 10025-2 1.0060 +N 14 - - - - - - 0,045 0,045 - - - 0,012
Notch impact energy not guaranteed.
Fe 590-2 80 - 100 295
≤ 16 345
V 0,02-0,15
16 - 35 325 1,00
Nb0,015- Z = Fully killed steel is permissible
Q345A GB 1591-94 470-630 21 - - - 0,20 0,55 - 0,045 0,045
0,060 +N Normalised is permissible
35 - 50 295 1,60
Ti0,02-0,20
50 - 100 275
Seite/Page 13 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
≤16 360
11
16 - 40 355
40 - 63 345 670-900 10
63 - 80 335
Non-alloy structural steels
≤ 16 390
V 0,02-0,15
16 - 35 370 1,00
Nb0,015- Z = Fully killed steel is permissible
Q390A GB 1591-94 490-650 19 - - - 0,20 0,55 - 0,045 0,045 0,30 0,70
0,060 +N Normalised is permissible
35 - 50 350 1,60
Ti0,02-0,20
50 - 100 330
3 - 16 235 26
0,19
16 - 40 225 26
40 - 63 215 25
340-470 27 20
RSt 37-2 63 - 80 215 24
Non-alloy structural steels
S235JR +N DIN EN 10025-2 1.0038 +N - - 1,50 0,045 0,045 - - - 0,014 Cu max. 0,60 Unkilled not permitted
Fe 360 B-FN 80 - 100 215 24
0,23
S235JRG2 100 - 150 195 22
≤16 235 26
Seite/Page 14 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
3 - 16 235 26
16 - 40 225 26
Non-alloy structural steels
40 - 63 215 25
340-470
63 - 80 215 24
S235J0 +N DIN EN 10025-2 1.0114 +N - 27 0 0,19 - 1,50 0,04 0,04 - - - 0,014 Cu max. 0,60 Unkilled not permitted
80 - 100 215 24
100 - 150 195 22
150 - 200 185 21
320-470
200 - 250 175 21
≤16 235 26
16-40 225 25
0,30
40-60 215 24 0,12 - Z = Fully killed steel is permissible
Q235C GB 700-88 375-460 - 27 0 0,30 - 0,045 0,045
60-100 205 23 0,20 +N Normalised is permissible
0,70
100-150 195 22
>150 185 21
3 - 16 235 26
16 - 40 225 26
Non-alloy structural steels
40 - 63 215 25
340-470
63 - 80 215 24
S235J2 +N DIN EN 10025-2 1.0117 +N - 27 -20 0,19 - 1,50 0,035 0,035 - - - - Cu max. 0,60 Fully killed steel is permissible
80 - 100 215 24
100 - 150 195 22
150 - 200 185 21
320-470
200 - 250 175 21
≤16 235 26
16-40 225 25
0,30
40-60 215 24 0,12 - Z = Fully killed steel is permissible
Q235D GB 700-88 375-460 - 27 -20 0,30 - 0,045 0,045
60-100 205 23 0,20 +N Normalised is permissible
0,70
100-150 195 22
>150 185 21
3 - 16 275 21
0,24
16 - 40 265 21
40 - 63 255 410-560 20
27 20
St 44-2 63 - 80 245 19
S275JR +N DIN EN 10025-2 1.0044 +N - - 1,60 0,045 0,045 0,014 Cu max. 0,60 Unkilled not permitted
Fe 430 B 80 - 100 235 19
Non-alloy structural steels
0,25
S275JRG2 100 - 150 225 400-540 19
150 - 200 215 380-540 18
23 20
200 - 250 205 18
≤16 275 20 - C content must be limited to 0.22%, otherwise only
16-40 265 19 - limited weldability.
0,28 0,50 Notch impact energy not guaranteed.
40-60 255 18 -
Q275 Z GB 700-88 490-630 - - 0,35 - 0,05 0,045 Z = Fully killed steel is permissible
60-100 245 17 -
0,38 0,80 +N Normalised is permissible
100-150 235 16 -
>150 225 15 -
Q295B GB/T 1591-94 ≤16 295
16-35 275 0,80 - Z = Fully killed steel is permissible
390 - 570 23 34 20 0,16 0,55 0,04 0,04
35-50 255 1,50 +N Normalised is permissible
50-100 235
Seite/Page 15 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
3 - 16 275 21
16 - 40 265 21
40 - 63 255 410-560 20
Non-alloy structural steels
63 - 80 245 19
S275J0 +N DIN EN 10025-2 1.0143 +N - 27 0 0,21 - 1,60 0,04 0,04 0,012 Cu max. 0,60 Unkilled not permitted
80 - 100 235 19
100 - 150 225 400-540 19
150 - 200 215 380-540 18
200 - 250 205 18
≤16 275 20 C content must be limited to 0.22%, otherwise only
16-40 265 19 limited weldability.
0,28 0,50 Notch impact energy not guaranteed.
40-60 255 18
Q275Z GB 700-88 490-630 - - - - 0,35 - 0,05 0,045 Z = Fully killed steel is permissible
60-100 245 17 0,38 0,80 +N Normalised is permissible
100-150 235 16
>150 225 15
3 - 16 275 21
16 - 40 265 21
40 - 63 255 410-560 20
Non-alloy structural steels
St 44-2 63 - 80 245 19
S275J2 +N DIN EN 10025-2 1.0145 +N - 27 -20 0,21 - 1,60 0,035 0,035 - Cu max. 0,60 Fully killed steel is permissible
Fe 430 B 80 - 100 235 19
S275JRG2 100 - 150 225 400-540 19
150 - 200 215 18
380-540
200 - 250 205 18
≤16 275 20 C content must be limited to 0.22%, otherwise only
16-40 265 19 limited weldability.
0,28 0,50 Notch impact energy not guaranteed.
40-60 255 18
Q275Z GB 700-88 490-630 - - - - 0,35 - 0,05 0,045 Z = Fully killed steel is permissible
60-100 245 17 0,38 0,80 +N Normalised is permissible
100-150 235 16
>150 225 15
3 - 16 355
20
16 - 40 345
40 - 63 335 470-630 19
Non-alloy structural steels
63 - 80 325
S355JR +N DIN EN 10025-2 1.0045 - +N 18 - 27 20 0,27 0,60 1,70 0,045 0,045 0,014 Cu max. 0,60 Unkilled not permitted
80 - 100 315
100 - 150 295 18
150 - 200 285 450-600
17
200 - 250 275
≤16 345
16-35 325 V 0,02-0,15
470-630 22 - 34 20 1,00
35-50 315 Nb0,015- Z = Fully killed steel is permissible
Q345B GB 1591-94 Normalized 0,20 0,55 - 0,04 0,04
50-100 275 0,060 +N Normalised is permissible
1,60
Ti0,02-0,20
Seite/Page 16 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
3 - 16 355
20
16 - 40 345
40 - 63 335 470-630 19
Non-alloy structural steels
63 - 80 325
S355J0 +N DIN EN 10025-2 1.0553 - +N - 27 0 0,24 0,55 1,60 0,035 0,035 0,012 Cu max. 0,60 Unkilled not permitted
80 - 100 315 18
100 - 150 295
150 - 200 285 450-600
17
200 - 250 275
≤16 345
16-35 325 V 0,02-0,15
470-630 22 - 34 0 1,00 Nb0,015-
35-50 315 Z = Fully killed steel is permissible
Q345C GB 1591-94 Normalized 0,18 0,55 - 0,035 0,035 0,060
50-100 275 +N Normalised is permissible
1,60 Ti0,02-0,20
Al ≥0,015
3 - 16 355
20 0,23
16 - 40 345
40 - 63 335 470-630 19
63 - 80 325
S355J2 +N DIN EN 10025-2 1.0577 +N - 27 -20 0,60 1,70 0,035 0,035 Cu max. 0,60 Fully killed steel is permissible
Non-alloy structural steels
80 - 100 315 18
0,24
100 - 150 295
150 - 200 285 450 - 600
17
200 - 250 275
≤ 100 315 490 20 35 Al min. 0,020
S355J2 +N DIN EN 10250-2 1.0570 +N 100 - 250 275 18 30 -20 0,22 0,55 1,6 0,035 0,035 0,3 0,08 0,3 Cr+Mo+Ni Steel for forgings
450
250 - 500 265 18 27 max. 0,48
≤16 345
16-35 325 V 0,02-0,15
470-630 22 - 34 -20 1,00 Nb0,015-
35-50 295 Z = Fully killed steel is permissible
Q345D GB 1591-94 Normalized 0,18 0,55 - 0,03 0,03 0,060
50-100 275 +N Normalised is permissible
1,60 Ti0,02-0,20
AL≥0,015
3 - 16 355
20 0,23
16 - 40 345
470-630
Non-alloy structural steels
40 - 63 335 19
27 -30
63 - 80 325
S355K2 +N DIN EN 10025-2 1.0596 - +N - 0,60 1,70 0,035 0,035 Cu max. 0,60 Fully killed steel is permissible
80 - 100 315 18
0,24
100 - 150 295
150 - 200 285 450-600
17 33 -20
200 - 250 275
≤16 345
16-35 325 V 0,02-0,15
470-630 22 - 27 -40 1,00 Nb0,015-
35-50 295 Z = Fully killed steel is permissible
Q345E GB 1591-94 Normalized 0,18 0,55 - 0,025 0,025 0,060
50-100 275 +N Normalised is permissible
1,60 Ti0,02-0,20
Al ≥0,015
Seite/Page 17 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
≤ 16 355 270
Weldable fine grain structural
Seite/Page 18 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
≤ 16 420
16-40 400 19 63 20 AL>0,020%
Weldable fine grain structural steels
≤ 16 460
16-40 440 AL>0,020%
40-63 430 550-720 Cu<0,55%
Weldable fine grain structural steels
55 20
63-80 410 17 47 0 1,00 - Nb<0,05%
S 460 N +N DIN EN 10025-3 1.8901 St E 460 +N - 0,20 0,60 0,03 0,025 0,30 0,10 0,80 0,025 KV at -20°C
80-100 400 43 -10 1,70 V <0,20%
40 -20
100-150 380
150-200 370 530-700
200-250 - - Ti<0,05%
≤ 16 460
0,02-0,2 V
16-35 440 1,00 Fully killed steel is permissible
0,015-0,06 Nb
Q460D GB 1591-94 Normalized 550-720 17 - 34 -20 0,20 0,55 - 0,03 0,03 0,70 0,70 KV at -20°C
35-50 420 0,02-0,2 Ti
1,70 +N Normalised is permissible
Al>0,015
50-100 400
≤ 16 460
16-40 440 63 20 AL>0,020%
40-63 430 550-720 55 0 Cu<0,55%
Weldable fine grain structural steels
Seite/Page 19 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
3 - 50 620 Cu ≤0,60
700-890 max. Nb≤0,06
S 620 Q DIN EN 10025-6 1.8914 StE 620 V +QT 50 - 100 580 15 - 30 -20 0,20 0,80 0,025 0,015 1,50 0,70 2,00 0,025 KV at -20°C
1,70 Ti≤0,05
100 - 150 560 650-830 B≤0,005
max. 0,10 V
≤50 620 1,00 max. 0,06 Nb
Fully killed steel is permissible
Q 620 D GB 16270-96 +QT 720-890 15 - 40 -20 0,18 0,55 - 0,03 0,03 0,80 0,60 1,20 0,20 Ti
KV at -20°C!
50-100 600 1,60 0,003 B
3 - 50 620 Cu ≤0,60
700-890 max. Nb≤0,06
S 620 QL DIN EN 10025-6 1.8927 TStE 620 V +QT 50 - 100 580 15 - 30 -40 0,20 0,80 0,025 0,015 1,50 0,70 2,00 0,025 KV at -40°C
1,70 Ti≤0,05
100 - 150 560 650-830 B≤0,005
max. 0,10 V
≤50 620 1,00 max. 0,06 Nb
Fully killed steel is permissible
Q 620 E GB 16270-96 +QT 720-890 15 - 27 -40 0,18 0,55 - 0,025 0,025 0,80 0,60 1,20 0,20 Ti
0,003 B
KV at -40°C!
50-100 600 1,60
max. 0,10 V
≤50 690 1,00 max. 0,06 Nb
Fully killed steel is permissible
Q 690 E GB 16270-96 +QT 770-940 14 - 27 -40 0,18 0,55 - 0,025 0,025 0,80 0,60 1,20 0,20 Ti
KV at -40°C!
50-100 670 1,60 0,003 B
turned)
63-100 - 820 -
5-10 510 650-950 6
E295GC DIN EN 10277-2 1.0533 St50-2KG - - - 0,045 0,045 0,009 Unkilled not permitted
10--16 420 600-900 7
+C
16-40 320 550-850 8
purposes
(cold drawn)
40-63 300 520-770 9
63-100 255 470-740 9
≤16 275 20
16 - 40 265 19
40 - 60 255 18 0,28 - 0,50 -
Q275 GB 700-88 490-630 - - - 0,35 0,05 0,045 Fully killed steel is permissible
60 - 100 245 17 0,38 0,80
100 - 150 235 16
>150 225 15
Seite/Page 20 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
+SH
16-40 - -
(as rolled and 40-63 - 580 - 820 - - - - 172 - 242
turned)
63-100 - -
5-10 565 750 - 1050 7
0,42 - 0,50 -
C45 DIN EN 10277-2 1.0503 C45 0,40 0,045 0,045 0,40 0,10 0,40 Cr+Mo+Ni Unkilled not permitted
10--16 500 710 - 1030 8 0,50 0,80
+C max. 0,63
16-40 410 650 - 1000 9 - - -
(cold drawn)
40-63 360 630 - 900 11
Bright steel for general engineering purposes
+SH 16-40 - -
(as rolled and 40-63 - 330-600 - - - - 98-178
turned) 63-100 - -
5-10 380 500-800 7 0,12 - 0,30 -
C15 DIN EN 10277-2 1.0401 C15 0,40 0,045 0,045 Unkilled not permitted
10--16 340 480-780 8 0,18 0,80
+C
16-40 280 430-730 9 - - -
(cold drawn)
40-63 240 380-670 11
63-100 215 340-600 12
DC01 DIN EN 10130 1.0330 St 12 03 +LC ≤3 140 270 - 410 28 - - - - 0,12 - 0,60 0,045 0,045 - - - -
0,05 - 0,25 -
08F GB 699-88 25 175 295 35 60 - - 131 0,03 0,035 0,035 0,10 - 0,25 - Cu 0,25 Sameness must be checked in every case.
0,11 0,50
Seite/Page 21 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
≤16 235
100 -
P235TR1 DIN EN 10216-1 1.0254 St 37.0 Normalized 16-40 225 360 - 500 25 - - - 0,17 - - 0,04 0,04 - - - - Nb≤0,009
140
40-60 215
0,17 0,35
GB 8162-87 0,17 - GB8162-87 Seamless tubes used for construction
20 -≤ 15 245 390-530 20 - - - - 0,035 0,035 - - - -
GB 8163-87 0,24 GB8163-87 Seamless tubes used for liquid transmitting
0,37 0,65
≤16 235
100 -
P235GH DIN EN 10216-2 1.0345 St 35.8 Normalized 16-40 225 360 - 500 25 - - - 0,17 - - 0,04 0,04 - - - - Nb≤0,009
140
40-60 215
0,17 0,35
GB 8162-87 0,17 - GB8162-87 Seamless tubes used for construction
20 -≤ 15 245 390-530 20 - - - - 0,035 0,035 - - - -
GB 8163-87 0,24 GB8163-87 Seamless tubes used for liquid transmitting
Non-alloy steel for tubes
0,37 0,65
≤12
355 490 - 650
12-20 Alges.
20-40 345 min.0,020
145 - 0.90 - Cu max.0,30
P355N +N DIN EN 10216-3 1.0562 StE 355 +N 40-50 335 490 - 630 22 - 55 20 0,20 0,50 0,025 0,02 0,30 0,08 0,50 0,02
185 1,70 Nb max.0,05
50-65 325 Ti max.0,040
65-80 315 V max.0,10
450 - 590
80-100 305
E 235 +N DIN EN 10305-4 1.0308 +N 235 340 - 480 25 - - - - 0,17 0,35 1,20 0,025 0,015 - - - - -
0,17 0,35
0,17 -
20 GB 8162-87 ≤ 15 245 390-530 20 - - - - 0,035 0,035 - - - - GB8162-87 Seamless tubes used for construction
0,24
0,37 0,65
Seite/Page 22 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
500 -
250 490 22 - 40 20
1000
0,17 - 0,17 - 1,40 -
20Mn2 GB 3077-88 ≤ 15 590 785 10 40 47 20 max. 187 0,035 0,035 0,30 - 0,30 Cu max. 0,30 Z = Fully killed steel is permissible
0,24 0,37 1,80
≤ 600 265 470 15 30 39 20
0,16 - 0,60 - 1,00 -
20SiMn GB 3077-99 0,035 0,035
600 - 900 255 450 14 30 39 20 0,22 0,80 1,30
500 -
260 540 17 - 20 20
1000
≤ 16 240 430 24 - - -
C22 DIN EN 10083-2 1.0402 C22N +N max. 156 0,17 - 0,40 - Cr+Mo+Ni Unkilled not permitted
0,40 0,045 0,045 0,40 0,10 0,40 -
16 - 100 210 410 25 - - - 0,24 0,70 max. 0,63
C22 DIN EN 10250-2 1.0402 C22N +N ≤ 100 210 410 25 - - - max. 156 Steel for forgings
0,17 - 0,17 - 0,35 -
20 GB 699-88 Normalized ≤ 25 245 410 25 55 - - max. 156 0,035 0,035 0,25 0,25 Cu 0,25 Fully killed steel is permissible
0,24 0,37 0,65
Seite/Page 23 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
≤ 16 300 550 18
0,32 - 0,50 - Cr+Mo+Ni
C35 +N DIN EN 10083-2 1.0501 C35N +N - - - max. 156 0,40 0,045 0,045 0,40 0,10 0,40 - Unkilled not permitted
16 - 100 270 520 19 0,39 0,80 max. 0,63
100 - 250 245 500 19
≤ 16 430 630 - 780 17 40
0,32 - 0,50 - Cr+Mo+Ni
C35 +QT DIN EN 10083-2 1.0501 C35V +QT 16 - 40 380 600 - 750 19 45 35 20 0,40 0,035 0,035 0,40 0,10 0,40 - Unkilled not permitted
0,39 0,80 max. 0,63
40 - 100 320 550 - 700 20 50
≤ 16 430 630 - 780 17 40
0,32 - 0,50 - Cr+Mo+Ni
C35E +QT DIN EN 10083-1 1.1181 Ck35V +QT 16 - 40 380 600 - 750 19 45 35 20 0,40 0,035 0,035 0,40 0,10 0,40 - Unkilled not permitted
Steels unalloyd or alloyd, normalized or quenched and tempered / Steel forgings
≤ 70 320 550 20 35
+QT 70 - 160 290 490 22 31 20
160 - 330 270 470 21 25
Normalized or
0,32 - 0,17 - 0,50 -
35 GB 699-88 quenched and ≤ 25 315 530 20 45 55 20 max. 156 0,035 0,035 0,25 0,25 Cu 0,25 Fully killed steel is permissible
tempered
0,40 0,37 0,80
≤ 16 340 620 14
0,42 - 0,50 - Cr+Mo+Ni
C45 +N DIN EN 10083-2 1.0503 C45N +N 16 - 100 305 580 16 - - - max. 207 0,40 0,045 0,045 0,40 0,10 0,40 - Unkilled not permitted
0,50 0,80 max. 0,63
100 - 250 275 560 16
≤ 16 490 700 - 850 14 35
0,42 - 0,50 - Cr+Mo+Ni
C45 +QT DIN EN 10083-2 1.0503 C45V +QT 16 - 40 430 650 - 800 16 40 25 20 0,40 0,045 0,045 0,40 0,10 0,40 - Unkilled not permitted
0,50 0,80 max. 0,63
40 - 100 370 630 - 780 17 45
≤ 16 490 700 - 850 14 35
0,42 - 0,50 - Cr+Mo+Ni
C45E +QT DIN EN 10083-1 1.1191 Ck45V +QT 16 - 40 430 650 - 800 16 40 25 20 0,40 0,045 0,045 0,40 0,10 0,40 - Unkilled not permitted
0,50 0,80 max. 0,63
40 - 100 370 630 - 780 17 45
Seite/Page 24 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
55
tempered
0,60 0,37 0,80
≤ 16 340 620 14
0,57 - 0,60 - Cr+Mo+Ni
C60 +N DIN EN 10083-2 1.0601 C60N +N 16 - 100 305 580 16 - - - max. 207 0,40 0,045 0,045 0,40 0,10 0,40 - Unkilled not permitted
0,65 0,90 max. 0,63
100 - 250 275 560 16
≤ 100 340 670
100 - 250 310 650 16
+N 250 - 500 275 630 max. 207
DIN EN 10250-2 500 - 1000 260 620 10 0,57 - 0,60 - Cr+Mo+Ni
C60E 1.1221 CK45 - - - 0,40 0,035 0,035 0,40 0,10 0,40 - Steel for forgings
SEW 550 500 - 1000 345 680 - 830 12 0,65 0,90 max. 0,63
≤ 70 450 750 14
+QT 70 - 160 390 690 15
160 - 330 350 670 14
0,57 - 0,17 - 0,50 -
60 GB 699-88 Normalized ≤ 25 400 675 12 35 - - max. 255 0,035 0,035 0,25 0,25 Cu 0,25 Fully killed steel is permissible
0,65 0,37 0,80
≤ 16 700 900 - 1100 12 50 45 20
16 - 40 600 800 - 950 14 55 50 20
25CrMo4 DIN EN 10083-1 1.7218 25CrMo4V +QT
40 - 100 450 700 - 850 15 60 50 20
0,22 - 0,60 - 0,90 - 0,15 -
100 - 160 400 650 - 800 16 60 45 20 0,40 0,035 0,035 - -
0,29 0,90 1,20 0,30
≤ 70 450 700 15 50 20
25CrMo4 DIN EN 10250-3 1.7218 25CrMo4V +QT 70 - 160 400 650 17 - 45 20 Steel for forgings
160 - 330 380 600 18 38 20
0,26 - 0,17 - 0,40 - 0,80 - 0,15 -
30CrMo GB 3077-88 ≤ 25 785 930 12 50 63 20 229 0,34 0,37 0,70 0,035 0,035 1,10 0,25 Fully killed steel is permissible
≤ 70 550 800 14 45 20
34CrMo4 DIN EN 10250-3 1.7220 34CrMo4V +QT 70 - 160 450 700 15 - 40 20 Steel for forgings
160 - 330 410 650 16 33 20
0,32 - 0,17 - 0,40 - 0,80 - 0,15 -
35CrMo GB 3077-88 ≤ 25 835 980 12 45 63 20 229 0,40 0,37 0,70 0,035 0,035 1,10 0,25 Fully killed steel is permissible
Seite/Page 25 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
Seite/Page 26 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
≤ 70 980 1100 10 - 28 20
70 - 160 820 1000 12 - 48 20
DIN EN 10250-3 160 - 330 780 950 12 - 48 20 0,28 - 0,15 - 1,00 - 0,30 - 2,90 -
33NiCrMoV14-5 1.6956 33 NiCrMo14 5 +QT 0,40 0,035 0,035 - V 0,08 - 0,25 Steel for forgings
SEW 550 ≤ 1000 785 930 - 1130 12 - - 0,38 0,40 1,70 0,60 3,80
No conversion
No conversion
+A - - - - - - - max. 223
DIN EN ISO 0,95 - 0,15 - 0,25 - 1,35 -
102Cr6 1.2067 100 Cr 6 0,03 0,03 - - - -
4957 HRC min. 1,10 0,35 0,45 1,65
- - - - - - -
+H 60
Tools steels
+A max. 229
DIN EN ISO 0,55 - 0,70 - 0,15 - 0,90 - V 0,10 - 0,20
60WCrV8 1.2550 60 WCrV 7 0,03 0,03 - -
4957 HRC min. 0,65 1,00 0,45 1,20 W 1,70 - 2,20
+H 58
≤ 100 39 20
Heat-resisting steels
Seite/Page 27 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
+A 207
Stainless steels
OFH:
0,36 - 12,0 -
GB 1220-92 (+QT) Not known HRC min. 0,60 0,80 0,035 0,03 Material is only similar (Mechanical properties!)
4Cr13 0,45 14,0
50
No conversion
Seite/Page 28 von/of 40
SN359-1 : 2009-07
Notice
Material Mechanical properties Chemical composition
Elongation at
Notch impact
Thickness or
Reduction of
strength Rm
temperature
strength Re
energy KV
Hardness
after heat
treatment
diameter
fract. A5
Tensile
area Z
Test-
Yield
°C
Group Material designation Standard Mat.- Former Heat mm MPa MPa % % J °C HBW C Si Mn P S Cr Mo Ni N other
No. designation treatment
min. or range % max. or range
X4CrNi18-10 DIN EN 10088 1.4301 X5 CrNi 18 9 solution ≤ 250 190 500 - 700 35 - 100 20 17,00 - 8,00 -
0,07 1,00 2,00 0,045 0,015 - ≤ 0,11
annealing 19,50 10,50
X4CrNi18-10 DIN EN 10250-4 1.4301 X5 CrNi 18 9 ≤ 250 190 500 - 700 35 - 100 20 Steel for forgings
solution 17,00 - 8,00 - Material is only similar,
0Cr18Ni9 GB 1220-92 ≤ 180 205 520 40 60 - - max. 187 0,07 1,00 2,00 0,035 0,03 - -
anealing 19,00 11,00 Notch impact energy not guaranteed,
X6CrNiTi18-10 DIN EN 10088 1.4541 X10 CrNiTi 18 9 ≤ 250 190 500 - 700 30 - 100 20
DIN EN 10216-5
X6CrNiTi18-10 1.4541 ≤ 50 200 500 - 730 35 - 100 20 130 - 180 Pipes and tubes
DIN EN 10217-7
GB 1220-92
GB 1221-92
GB 3280-92
GB4237-92
GB4238-92 solution 17,00 - 8,00 - Ti = 5xC, max. Material is only similar,
0Cr18Ni10Ti ≤ 180 205 520 40 60 - - max. 187 0,08 1,00 2,00 0,035 0,03 - -
GB 4356-84 annealing 19,00 11,00 0,80 Notch impact energy not guaranteed,
GB 12771-91
Stainless steels
GB 13296-91
GB/T 14975-94
GB/T 14976-94
X5CrNiMo17-12-2 DIN EN 10088 1.4401 X5 CrNiMo 17 12 2 ≤ 250 200 500 - 700 30 - 100 20 max. 215
solution 16,50 - 2,00 - 10,00 -
0,07 1,00 2,00 0,045 0,015 ≤ 0,11
annealing 18,50 2,50 13,00
X5CrNiMo17-12-2 DIN EN 10250-4 1.4401 X5 CrNiMo 17 12 2 ≤ 250 200 500 - 700 30 - 100 20 Steel for forgings
X6CrNiMoTi17-12-2 DIN EN 10088 1.4571 X10 CrNiMoTi 18 10 ≤ 250 200 500 - 700 30 - 100 20 max. 215
16,50 - 2,00 - 10,00 -
0,07 1,00 2,00 0,045 0,015 ≤ 0,11
solution 18,50 2,50 13,00 Ti = 5xC, max.
annealing 0,70
X6CrNiMoTi17-12-2 DIN EN 10250-4 1.4571 X10 CrNiMoTi 18 10 ≤ 250 200 500 - 700 30 - 100 20 Steel for forgings
Seite/Page 29 von/of 40
SN359-1 : 2009-07
Anhang/Appendix B2 (normativ):
Comparison of german and chinese material properties, cast steels
Elongation at
Thickness or
Reduction of
temperature
proof stress
toughness
Yieldpoint,
Hardness
annealing
diameter
strength
strength
fracture
Fatigue
Tensile
(20°C)
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW C Si Mn P S Cr Mo Ni N other
designation treatment
min. or range max. or range %
Cu max.
GS 200 DIN EN 10293 1.0449 GS-38N normalised ≤ 100 200 380 - 530 25 - 35 20 - - 0,18 0,60 1,20 0,03 0,025 0,30 0,12 0,40
0,30
Cu max.
GS 240 DIN EN 10293 1.0445 GS-45N normalised ≤ 100 240 450 - 600 22 - 31 20 - - 0,23 0,60 1,20 0,03 0,025 0,30 0,12 0,40 -
0,30
V max.
ZG 270-500 GB 11352-89 ≤ 100 270 500 18 25 22 20 - - 0,40 0,50 0,90 0,04 0,04 0,35 0,20 0,30 - 0,05, Cu
max. 0,30
V max. C content must be limited, otherwise only limited
ZG 310-570 GB 11352-89 ≤ 100 310 570 15 21 15 20 - - 0,50 0,60 0,90 0,04 0,04 0,35 0,20 0,30 - 0,05, Cu weldability.
max. 0,30
ZG 290-510 GB/T 14408-93 ≤ 100 290 510 - - - - - - - - - 0,04 0,04 - - - - -
Seite/Page 30 von/of 40
SN359-1 : 2009-07
Elongation at
Thickness or
Reduction of
temperature
proof stress
toughness
Yieldpoint,
Hardness
annealing
diameter
strength
strength
fracture
Fatigue
Tensile
(20°C)
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW C Si Mn P S Cr Mo Ni N other
designation treatment
min. or range max. or range %
JB/T 6402-92 +N 392 588 12 20 191 0,30 - 0,30 - 0,50 - 0,80 - 0,20 - For welded parts C-content must be < 0,30%,
Quenched and tempered steel castings
+QT1 100 - 150 550 700 - 850 10 - 27 20 - - 0,38 - 0,60 - 0,80 - 0,15 - Cu max.
G42CrMo4 DIN 10293 1.7231 GS-42CrMo4V 0,60 0,025 0,02 0,4 -
150 - 250 350 650 - 800 10 - 16 20 - - 0,45 1,00 1,20 0,30 0,30
ZG 34Cr2Ni2Mo JB/T 6402-92 +QT 150 - 250 650 800 - 950 12 - - - - 220 - 270 0,30 - 0,30 - 0,60 - 0,035 0,035 1,40 - 0,15 - 1,40 - comparison for QT1 and QT2!
0,37 0,60 1,00 1,70 0,35 1,70
250 - 400 650 800 - 950 10 - - - - 220 - 270
≤100 700 850 - 1000 - 45 20 0,32 - 0,60 - 1,40 - 0,15 - 1,40 - Cu max.
G35CrNiMo6-6 DIN EN 10293 1.6579 GS-34CrNiMo6V 0,6 0,025 0,02 -
+QT1 100 - 150 650 800 - 950 12 35 20 0,38 1,00 1,70 0,35 1,70 0,30
Seite/Page 31 von/of 40
SN359-1 : 2009-07
Elongation at
Thickness or
Reduction of
temperature
proof stress
toughness
Yieldpoint,
Hardness
annealing
diameter
strength
strength
fracture
Fatigue
Tensile
(20°C)
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW C Si Mn P S Cr Mo Ni N other
designation treatment
min. or range max. or range %
JB/T 6402-92 +N 392 588 12 20 191 0,30 - 0,30 - 0,50 - 0,80 - 0,20 - +N is not comparison, +QT-steel is permisible for
ZG 35Cr1Mo 0,035 0,035 - - -
EZB 1162-92 0,37 0,50 0,80 1,20 0,30 comparison,
+QT 539 686 12 25 240
JB/T 6402-92 0,46 - 0,25 - 0,50 - 0,90 - 0,15 - EZB-Standards are work-standards from CHINA
ZG 50Cr1Mo +QT 520 740 - 880 11 - 34 20 - 200 - 260 0,035 0,035 - - - NATIONAL ERZHONG GROUP
EZB 1162-92 0,54 0,50 0,80 1,20 0,25
0,18 - 0,50 -
GP240GH DIN EN 10213 1.0619 GS-25V +QT ≤ 100 240 420 - 600 22 - 40 20 - - 0,60 0,03 0,02 - - - - -
0,23 1,20
Seite/Page 32 von/of 40
SN359-1 : 2009-07
Elongation at
Thickness or
Reduction of
temperature
proof stress
toughness
Yieldpoint,
Hardness
annealing
diameter
strength
strength
fracture
Fatigue
Tensile
(20°C)
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW C Si Mn P S Cr Mo Ni N other
designation treatment
min. or range max. or range %
Heat-resistant steel castings
V 0,20 -
0,15 - 0,50 - 1,20 - 0,90 - 0,30
G17CrMoV5-10 DIN EN 10213 1.7706 GS-17CrMoV5 11V +QT ≤ 150 440 590 - 780 15 - 27 20 - - 0,60 0,02 0,015 - -
0,20 0,90 1,50 1,10 Sn max.
0,025
V 0,25 -
0,20 - 0,50 - 11,30 - 1,00 - max. 0,35
GX23CrMoV12-1 DIN EN 10213 1.4931 GX-22CrMoV12 1 +QT ≤ 150 540 740 - 880 15 - 27 20 - - 0,40 0,03 0,02 -
0,26 0,80 12,20 1,20 1,00 W max.
0,50
Seite/Page 33 von/of 40
SN359-1 : 2009-07
Anhang/Appendix B3 (normativ):
Comparison of german and chinese material properties, cast irons
Elongation at
Thickness or
Reduction of
temperature
proof stress
toughness
Yieldpoint,
Hardness
annealing
diameter
strength
strength
fracture
Fatigue
Tensile
(20°C)
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW C Si Mn P S Cr Mo Ni N other
designation treatment
min. or range max. or range %
10 - 20 - 180 - - - - 90 250
GG-20
EN-GJL-200 DIN EN 1561 EN-GJL-200 - 20 - 40 - 155 - - - - - 235 Referenc composition, at supplier's discretion
GGL-20
40 - 80 - 130 - - - - - 235
Without heat
treatment or 3,0 - 1,6 - 0,5 - 0,20 - 0,60 -
GGL-320MoCr8 - - - 350 max. 280 0,20 0,12 - - - Elevated temperature resistant and wear resistant
stress 3,4 2,4 1,0 0,40 1,00
reliving
No conversion
Seite/Page 34 von/of 40
SN359-1 : 2009-07
Elongation at
Thickness or
Reduction of
temperature
proof stress
toughness
Yieldpoint,
Hardness
annealing
diameter
strength
strength
fracture
Fatigue
Tensile
(20°C)
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW C Si Mn P S Cr Mo Ni N other
designation treatment
min. or range max. or range %
QT400-18 GB 1348-88 - - 250 400 18 - - - - 130 - 180 Referenc composition, at supplier's discretion
EN-GJS-500-7U -
EN-GJMW-360-12 DIN EN 1562 EN-JM1020 GTW-38 -12 - 12 190 360 5 max. 200 Referenc composition, at supplier's discretion
No conversion
EN-GJMW-400-5 DIN EN 1562 EN-JM1030 GTW-40 -05 - 12 220 400 5 max. 220 Referenc composition, at supplier's discretion
No conversion
Seite/Page 35 von/of 40
SN359-1 : 2009-07
Anhang/Appendix B4 (normativ):
Comparison of German and Chinese material properties, Non-ferrous metals
Elongation at
Thickness or
Reduction of
temperature
proof stress
Yieldpoint,
toughness
annealing
Hardness
diameter
strength
strength
fracture
Fatigue
Tensile
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW10 Cu Sn Pb Ni Sb Al Zn Si Fe other
designation treatment
min. or range max. or range %
Copper-tin-
P+S
CC493K- 81,0 - 6,0 - 5,0 - 2,0 -
CuSn7Zn4Pb7-C-GS DIN EN 1982 G-CuSn7ZnPb - 8,80 120 230 15 - - - 110 60 2,00 0,3 0,01 0,01 0,2 je max.
GS 85,0* 8,0 8,0 5,0
0,10
remai 6,0 - 5,0 - 3,0 - EZB-Standards are work-standards from CHINA
ZCuSn7Zn4Pb6-S EZB 1179-93 120 240 15 - - - - 65 - - - - - -
nder 8,0 7,0 5,0 NATIONAL ERZHONG GROUP.
P+S
81,0 - 6,0 - 5,0 - 2,0 - YZB-Standards are work-standards from CHINA
CuSn7Zn4Pb7-C-GZ DIN EN 1982 CC493K-GZ GZ-CuSn7ZnPb - 8,80 120 260 12 - - - 110 70 2,00 0,3 0,01 0,01 0,2 je max.
85,0* 8,0 8,0 5,0 FIRST HEAVY INDUSTRIE
0,10
remai 6,0 - 5,0 - 3,0 -
ZCuSn7Zn4Pb6-Li EZB 1179-93 130 270 13 - - - - 75 - - - - - -
nder 8,0 7,0 5,0
Copper-tin-lead cast alloy
P+S
(cast tin-lead-bronze)
Seite/Page 36 von/of 40
SN359-1 : 2009-07
Elongation at
Thickness or
Reduction of
temperature
proof stress
Yieldpoint,
toughness
annealing
Hardness
diameter
strength
strength
fracture
Fatigue
Tensile
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW10 Cu Sn Pb Ni Sb Al Zn Si Fe other
designation treatment
min. or range max. or range %
P max.
CC480K- 85,0 - 11,0 -
CuSn10-C-GS DIN EN 1982 G-CuSn10 - 8,60 140 260 7 - - - - 80 0,7 2,00 0,15 0,01 - 0,01 0,20 0,60 * including Ni
GS 88,5 13,0
S max.
remai 11,0 - 1,0 -
ZCuSn10P1-S EZB 1179-93 140 260 10 - - - - 80 - - - - - - -
nder 13,0 2,0
P max.
CC480K- 85,0 - 11,0 -
CuSn10-C-GZ DIN EN 1982 GZ-CuSn10 - 8,60 150 280 5 - - - - 90 0,7 2,00 0,15 0,01 - 0,01 0,20 0,60
GZ 88,5 13,0
S max.
140 260 10 - - - - 80
remai 11,0 - 1,0 -
ZCuSn10P1-Li EZB 1179-93 - - - - - - -
nder 13,0 2,0
P max.
CC480K- 85,0 - 11,0 -
CuSn10-C-GC DIN EN 1982 GC-CuSn10 - 8,60 150 300 6 - - - - 90 0,7 2,00 0,15 0,01 - 0,01 0,20 0,60
GC 88,5 13,0
S max.
remai 11,0 - 1,5 -
ZCuSn10P1-La EZB 1179-93 170 300 10 - - - - 90 - - - - - - -
nder 13,0 2,5
Copper-tin cast alloy (in bronze)
P max.
CC483K- 85,0 - 11,0 -
CuSn12-C-GS DIN EN 1982 G-CuSn12 - 8,60 140 260 7 - - - - 80 0,7 2,00 0,15 0,01 - 0,01 0,20 0,60
GS 88,5 13,0
S max.
remai 11,0 - 1,0 -
ZCuSn12Pb1-S EZB 1179-93 140 260 10 - - - - 80 - - - - - - -
nder 13,0 2,0
Seite/Page 37 von/of 40
SN359-1 : 2009-07
Elongation at
Thickness or
Reduction of
temperature
proof stress
Yieldpoint,
toughness
annealing
Hardness
diameter
strength
strength
fracture
Fatigue
Tensile
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW10 Cu Sn Pb Ni Sb Al Zn Si Fe other
designation treatment
min. or range max. or range %
P 0,05 -
CC484K- 84,5 - 11,0 - 1,5 -
CuSn12Ni2-C-GC DIN EN 1982 GC-CuSn12Ni - 8,60 180 300 10 - - - - 95 0,3 0,05 0,01 0,4 0,01 0,20 0,40
GS 87,5 13,0 2,5
S max.
remai 11,0 - 1,5 -
ZCuSn12Ni2-La EZB 1179-93 170 300 10 - - - - 90 - - - - - - -
nder 13,0 2,5
P
CC482K- 83,5 - 10,5 - 0,7 -
CuSn11Pb2-C-GS DIN EN 1982 G-CuSn12Pb - 8,70 130 240 5 - - - - 80 2,00 0,2 0,01 2 0,01 0,20 max.0,40
GS 87,0 12,5 2,5
S max.
remai 11,0 - 1,0 -
ZCuSn12Pb1-S EZB 1179-93 140 260 10 - - - - 80 - - - - - - -
Copper-tin cast alloy (in bronze)
140 260 10 - - - - 80
84,0 - 11,0 - 1,0 - devagleit TM is the product from Federal Mogul
devagleit TM dg02 Basic-material is 2.1061.01 CuSn12Pb - 8,70
87,0 13,0 2,0
2,0 0,2 - -
(www.deva.de)
150 280 5 - - - - 90
140 280 7 - - - - 85
DF-5(1) 170 330 4 - - - - 88
DF-5(2) 200 540 15 - - - - 110
Seite/Page 38 von/of 40
SN359-1 : 2009-07
Elongation at
Thickness or
Reduction of
temperature
proof stress
Yieldpoint,
toughness
annealing
Hardness
diameter
strength
strength
fracture
Fatigue
Tensile
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW10 Cu Sn Pb Ni Sb Al Zn Si Fe other
designation treatment
min. or range max. or range %
10,0 - 3,0 -
ZCuAl10Fe4Ni2-Li YZB 267-2002 7,40 205 515 12 - - - - >83 2,5
11,5 5,0
remai 8,5 - 2,0 - Werte erreichen nicht die von APMCO 18-23, daher
ZCuAl10Fe3 (GS) EZB 1179-93 180 500 15 - - - - 115
nder 11,0 4,0 nur mit Einschränkung verwendbar.
Not according to standard, CuAl alloy with special 220 - 1,0 - 35 - rema Main-Metall is the product from Main-Metall
bronze
No conversion
Seite/Page 39 von/of 40
SN359-1 : 2009-07
Elongation at
Thickness or
Reduction of
temperature
proof stress
Yieldpoint,
toughness
annealing
Hardness
diameter
strength
strength
fracture
Fatigue
Tensile
Notch
Test-
after
area
Group Material designation Standard No. Former Heat- mm MPa MPa % % J °C Mpa HBW10 Cu Sn Pb Ni Sb Al Zn Si Fe other
designation treatment
min. or range max. or range %
ZCuZn35Al1Fe1Mn2-Li
65,0 2,0 2,0 inder 2,0 3,0
No conversion
Seite/Page 40 von/of 40