Property Data

Akulon® F136-E1
PA6
Very High Viscosity, Lubricated, Nucleated, Film Extrusion

Print Date: 2017-03-28

Properties Typical Data Unit Test Method

Material specific properties

Viscosity number 245 cm³/g ISO 307, 1157, 1628

RSV formic acid, 1g/100ml 3.6 - DSM method

Melt Viscosity (260 °C) 2250 Pa s DSM method, 260 °C

Density 1130 kg/m³ ISO 1183

Thermal properties
Coeff. of linear therm. expansion (parallel) 0.9 E-4/°C ISO 11359-1/-2

Spec. heat capacity 1550 J/(kg K) -

Average spec. heat capacity 20-150 °C 2250 J/(kg K)

Mechanical properties (Film)

Modulus of elasticity 465 MPa DSM-Method, 50 mm/min

Stress at yield, parallel 34 MPa ISO 527-3

Maximum stress, parallel 94 MPa ISO 527-3

Maximum strain, parallel 350 % ISO 527-3

Trouser Tear resistance, parallel 32 - ISO 6383-1

Puncture resistance 1320 J/m DSM-Method

Static coefficient of friction 1.4 - ISO 8295

Dynamic coefficient of friction 0.8 - ISO 8295

Other Properties (Film)

Transparency/Clarity 85 % DSM method

Oxygen transmission rate at 23°C/0%r.h. 23 cm³/(m²*d*bar) DIS 15105-1/-2

Akulon®, Arnite®, Arnitel®, EcoPaXX®, ForTii®, Novamid®, Stanyl® and Xytron™ are trademarks of DSM. All information supplied by or on
behalf of DSM in relation to its products, whether in the nature of data, recommendations or otherwise, is supported by research and, in
good faith, believed reliable, but DSM assumes no liability and makes no warranties of any kind, express or implied, including, but not
limited to, those of title, merchantability, fitness for a particular purpose or non-infringement or any warranty arising from a course of
dealing, usage, or trade practice whatsoever in respect of application, processing or use made of the aforementioned information, or
product. The user assumes all responsibility for the use of all information provided and shall verify quality and other properties or any
consequences from the use of all such information. Typical values are indicative only and are not to be construed as being binding
specifications. This document replaces all previous versions relating to this subject. Copyright © DSM 2017. All rights reserved. No part of
the information may be reproduced, distributed, or transmitted in any form or by any means, including photocopying, recording, or other
electronic or mechanical methods, without the prior written permission of DSM.
Property Data

Akulon ® F136-E1
Print Date: 2017-03-28

Properties Typical Data Unit Test Method

Oxygen transmission rate at 23°C/85%r.h. 33 cm³/(m²*d*bar) DIS 15105-1/-2

Water Vapor Transmission Rate at 23°C/85%r.h. 35 g/(m²*d) DIS 15106-1/-3

Test specimen production (Film)

Type of extrusion cast - -

Thickness of specimen 0.05 mm -

Extruder temperature 270 °C

Die temperature 270 °C

Chill Roll Temperature 110 °C

Viscosity-shear rate
Viscosity-shear rate Akulon® F136-E1
1E4 240°C

260°C

280°C
Viscosity in Pa s

1E3

1E2

1E1
1E-2 1E-1 1E0 1E1 1E2 1E3 1E4

Shear rate in 1/s

Akulon®, Arnite®, Arnitel®, EcoPaXX®, ForTii®, Novamid®, Stanyl® and Xytron™ are trademarks of DSM. All information supplied by or on
behalf of DSM in relation to its products, whether in the nature of data, recommendations or otherwise, is supported by research and, in
good faith, believed reliable, but DSM assumes no liability and makes no warranties of any kind, express or implied, including, but not
limited to, those of title, merchantability, fitness for a particular purpose or non-infringement or any warranty arising from a course of
dealing, usage, or trade practice whatsoever in respect of application, processing or use made of the aforementioned information, or
product. The user assumes all responsibility for the use of all information provided and shall verify quality and other properties or any
consequences from the use of all such information. Typical values are indicative only and are not to be construed as being binding
specifications. This document replaces all previous versions relating to this subject. Copyright © DSM 2017. All rights reserved. No part of
the information may be reproduced, distributed, or transmitted in any form or by any means, including photocopying, recording, or other
electronic or mechanical methods, without the prior written permission of DSM.