    1.2842 steel has high dimensional stability, cracking resistance, machinability, wear resistance, and toughness. It is suitable for measuring tools, machine knives, cold cutting shear blades, and thread cutting tools. 2. The steel has a carbon content of 0.9% and contains manganese, chromium, and vanadium. It exhibits a hardness of up to 229 HB after soft annealing and 63-65 HRC after hardening and quenching. 3. Heat treatment involves soft annealing at 690-720°C, hardening from 790-820°C followed by quenching in oil or salt baths at 180-220°C, and tempering from 100-

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    MERILO

    Uploaded by

    pedja
    28 views1 page
    1.2842 steel has high dimensional stability, cracking resistance, machinability, wear resistance, and toughness. It is suitable for measuring tools, machine knives, cold cutting shear blades, and thread cutting tools. 2. The steel has a carbon content of 0.9% and contains manganese, chromium, and vanadium. It exhibits a hardness of up to 229 HB after soft annealing and 63-65 HRC after hardening and quenching. 3. Heat treatment involves soft annealing at 690-720°C, hardening from 790-820°C followed by quenching in oil or salt baths at 180-220°C, and tempering from 100-

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    1.2842 steel has high dimensional stability, cracking resistance, machinability, wear resistance, and toughness. It is suitable for measuring tools, machine knives, cold cutting shear blades, and thread cutting tools. 2. The steel has a carbon content of 0.9% and contains manganese, chromium, and vanadium. It exhibits a hardness of up to 229 HB after soft annealing and 63-65 HRC after hardening and quenching. 3. Heat treatment involves soft annealing at 690-720°C, hardening from 790-820°C followed by quenching in oil or salt baths at 180-220°C, and tempering from 100-

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    28 views1 page

    MERILO

    Uploaded by

    pedja
    1.2842 steel has high dimensional stability, cracking resistance, machinability, wear resistance, and toughness. It is suitable for measuring tools, machine knives, cold cutting shear blades, and thread cutting tools. 2. The steel has a carbon content of 0.9% and contains manganese, chromium, and vanadium. It exhibits a hardness of up to 229 HB after soft annealing and 63-65 HRC after hardening and quenching. 3. Heat treatment involves soft annealing at 690-720°C, hardening from 790-820°C followed by quenching in oil or salt baths at 180-220°C, and tempering from 100-

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    SIHARD 2842

    MERILO
    DIN - Material - No. 1.2842
    Code 90MnCrV8
    Comparable standards AISI: O2, EU: 90MnV8
    Chemical composition C Si Mn Cr V
    (Typical analysis %) 0.90 0.25 2.00 0.35 0.10
    Steel properties High dimensional stability at heat treatment. Very high
    resistance to cracking. High machinability, wear resistant and
    toughness. Good cutting edge retention.

    Physical properties Thermal conductivity W/(m.K) 20oC


    30
    3
    Density g/cm 20oC
    7.85
    Coefficient of linear thermal expansion
    20-100 20-200 20-300 20-400 20-500 20-600 20-700oC
    10-6 oC-1 12.1 13.3 13.8 14.3 14.1 14.2 14.6

    Applications Measuring tools, machine knives for the wood, paper and metal
    industry, cold cutting shear blades, thread cutting tools.

    Stress Relieving Holding at approx 6500C for one hour.

    Heat treatment Soft annealingoC Cooling Hardness HB


    690 - 720 furnace max. 229
    Hardening fromoC in Hardness after quenching HRC
    790 - 820 oil, thermal bath 63 - 65
    180 - 220oC
    o
    Tempering C 100 200 300 400 500 600
    HRC 63 60 56 50 42 38

    Time - Temperature - Transformation - Diagram Tempering Diagram

    USBCO STEELS PVT LTD