COLD GALVANISING Spray

Technical Data
COLD GALVANISING Spray

Optimum Galvanic Protection
Product Overview Directions for Storage and Use

ROCOL® COLD GALVANISING Spray offers ultra • Apply to a clean, degreased, dry surface for best
long term corrosion protection for metal components results.
requiring a permanent zinc-rich mid-grey coating. • Remove any residual rust and scale with a wire
Ideal for components that cannot be galvanised using brush or other abrasive method.
a hot dip process. It can also be used to repair the
• Rust removers based on phosphoric acid which
surface of galvanised components that have been
leave an electrically insulating film should not be
damaged or repaired prior to welding or other used as this will interfere with the galvanic
mechanical operations. protection action.
Typical Applications • Clean the area to be treated with a non-residue
solvent cleaner such as ROCOL INDUSTRIAL
Ports and docks, marine and offshore, farm and other CLEANER Rapid Dry Spray, p/c 34131, and
industrial equipment: ensure the solvent has evaporated completely
before continuing.
Steel door and window frames, fences, gates, garage
doors, trailer and caravan chassis, couplings, internal • Invert can and shake vigorously for 2 minutes
car body panels, structural steel and guard rails, after the agitator ball starts to rattle. Shake
welded seams, drains and boilers, storage tanks, frequently during use.
piping and fittings etc. • Hold upright and spray from a distance of
approximately 15-30 cm.
Features and Benefits
• Apply in light, even layers:
• Ultra long term protection for ferrous metals – o For best results apply 2 light films at 15-
3500 hours salt spray test. 20 minute intervals rather than 1 heavy
• 92% zinc-rich dry film coating – provides sacrificial film.
cathodic protection to ferrous metals. o Additional layers can be applied at 15-20
• Self-healing mechanism – scratches are re-sealed minute intervals.
by the formation of zinc oxide and carbonates. • Clear nozzle after use - invert can and spray for 3-
• Meets the requirements of ISO 3549 and ISO 5 seconds until only propellant is expelled.
1461 section 6.3. • Touch dry in 15 minutes at 20°C – Fully cured in
• Unique combination of flexibility and hardness – approximately 24 hours at 20°C.
highly resistant to peeling, flaking and abrasion. • If contact is unavoidable, test compatibility with
• Exceptional water resistance – tough polymeric painted or coated surfaces, plastics and rubbers
zinc-rich film. prior to application.
• Outstanding temperature resistance: -30°C to • Storage temperature should be kept below 50°C.
+450°C. Storage area should be out of direct sunlight.
• High performance coating or primer – contains • Shelf life 4 years from date of manufacture.
pure zinc, synthetic resin and additives. Pack Sizes
• Non-toxic formulation – lead and chromate free.
Pack Size Part Code
• Excellent repair for galvanised surfaces – adheres
400ml 69515
well to metal surfaces.
Technical Data
COLD GALVANISING Spray

Optimum Galvanic Protection
Typical Properties
Property Result
Appearance Medium grey dry film coating
Curing Time (20°C):
Touch Dry 15 mins
Full Cure Approximately 24 hrs
Applied Film Resin bonded micronised zinc
Resin Type Epoxy ester
Solids (applied film) 92% w/w zinc
Solvent Hydrocarbon
Propellant DME (Dimethyl ether)
Wet film - 0.1mm typical

Applied Film Thickness (1 coat)
Dry film – 0.05mm typical
Salt Spray Test (ASTM B-117):

3,500 hours at 35°C (2 coats) 0% corrosion
Temperature Range -30°C to +450°C
Coverage per Aerosol (0.1mm, dry) 1.5m2
Values quoted above are typical and do not constitute a specification.
Safety Data Sheets

Safety data sheets are available for download from our website www.rocol.com or may be obtained from your usual
ROCOL contact.
The information in this publication is based on our experience and reports from customers. There are many factors outside our control or
knowledge which affect the use and performance of our products, for which reason it is given without responsibility.
Issue: 3 Date: 01-20

COLD GALVANISING Spray - GB

Uploaded by

Copyright:

Available Formats

COLD GALVANISING Spray - GB

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

COLD GALVANISING Spray - GB

Uploaded by

Copyright:

Available Formats

Technical Data

Product Overview Directions for Storage and Use

COLD GALVANISING Spray

Wet film - 0.1mm typical

Salt Spray Test (ASTM B-117):

Values quoted above are typical and do not constitute a specification.