C93200 Spec4

Download as pdf or txt
Download as pdf or txt
You are on page 1of 1

C932000

Product Description: High-Leaded Tin Bronze


Soilds: 1/2" to 13" OD
Tubes 1" to 16" OD
Rectangles: Up to 20"
Standard Lengths: 144"
Shape/Form semi-finished, mill stock or near-net shapes, anode, bar stock, billet/bloom, squares, hex, plate, profile or
structural shape, flats/rectangular bar

TYPICAL USES
Automotive automotive fittings
Fasteners washers
Industrial thrust washers, pumps, bushings, machine parts, main spindle bearings, machine tool bearings, bearings for
cranes, trunion bearings, roll neck bearings, rolling mill bearings, linkage bushings for presses, fuel pump
bushings, water pump bushings, diesel engine wrist pin bushings, forging press toggle lever bearings, hydraulic
press stuffing box, hydraulic press main lining, pump impellers, general purpose bushings, fittings, pump
fixtures, insert bearings, bearings
SIMILAR OR EQUIVALENT SPECIFICATION
CDA ASTM ASARCON SAE AMS FEDERAL MILTIARY OTHER
QQ-C-390B MIL-B- BEARING
C93200 B505 77 660
TYPE III 11553, BRONZE
J461
J462
CHEMICAL COMPOSITION
P Al
Alloy Cu% Sn% Pb% Zn% Fe% Ni% Sb% S% Si%
% %
C93200 81.00-85.00 6.30-7.50 6.00-8.00 2.00-4.00 0.2 1 0.35 0 0 0 0

Chemical Composition according to ASTM B505/B505M-14

MACHINABILITY
Alloy Machinability Rating Density (lb/cu in.)
C93200 70 0.322

MECHANICAL PROPERTIES
Tensile Strength, min Yield Strength, at .5% Elongation in 2 in. or
Brinell Hardness Remarks
extension under load min 50 mm min

ksi Mpa ksi Mpa % typical BHN


35 241 20 138 10

Mechanical Properties according to ASTM B505/B505M-14

PHYSICAL PROPERTIES
US Customary Metric
Melting Point – Liquidus 1790˚ F 977˚ C
Melting Point – Solidus 1570˚ F 854˚ C
Density 0.322 lb/in3 at 68˚ F 8.91 gm/cm3 at 20˚ C
Specific Gravity 8.91 8.91
Electrical Resistivity 85.90 ohms-cmil/ft at 68˚ F 14.29 microhm-cm at 20˚ C
0.07
Electrical Conductivity 12% IACS at 68˚ F MegaSiemens/cm at
20˚ C
Thermal Conductivity 33.60 Btu · ft/(hr · ft2 · ˚F) at 68˚ F 58.2 W/m at 20˚ C
18.0 · 10-6 per ˚C (20˚-
Coefficient of Thermal Expansion 100 · 10-6 per ˚F (68˚-572˚ F)
300˚ C)
Specific Heat Capacity 0.090 Btu/lb/˚F at 68˚ F 377.1 J/kg at 293˚ C
Modulas of Elasticity in Tension 14500 ksi 100000 MPa
Magnetic Permeability 10 1

PHYSICAL PROPERTIES PROVIDED BY CDA

Fabrication Practices
Joining Technique Suitability
Soldering Excellent
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Coated Metal Arc Welding Not Recommended

Fabrication Properties provided by CDA

Thermal Properties
TREATMENT Temp./Time - US Temp./Time - SI
Stress Temperature 500 260
Solution Minimum
Solution Maximum
Solution Time 0.0 0
Solution Medium
Precipitation Value
Precipitation Time
Precipitation Medium
Annealing Minimum
Annealing Maximum
Annealing Time
Hot Works Minimum
Hot Works Maximum
Thermal Properties provided by CDA