Material Product Data Sheet

High Carbon Iron-Molybdenum Composite Powder

Thermal Spray Powder Products: Quick Facts

Metco 350NS
Classification Composite, iron based

1 Introduction Chemistry Fe 16Mo 2C 0.25Mn

Metco™ 350NS is a high carbon iron-molybdenum compos- Manufacture Mechanically clad
ite powder developed as a thermal sprayed alternative to
Morphology Irregular
hard chrome plating.
Apparent Density 3.1 ± 0.3 g/cm3

The addition of carbon increases the hardness and wear Purpose Wear and scuff resistance
­resistance. The formation of surface films effects sliding Service Temperature ≤ 340 °C (650 °F)
­characteristics of this material. The molybdenum constituent Process Atmospheric plasma spray or
provides good scuff resistance due to its ability to form an combustion powder Thermospray™
­lubricious film. The film can be formed by a reaction with the
environment or by transferring material from one sliding
­surface to the other. Sliding then takes place between one of
the surfaces and the transferred film.

Molybdenum has very high melting points thus the

­interaction between substrate and coating particles (bond
strength) will be increased due to the higher temperatures
­involved and longer cooling cycles.

Application and processing temperatures may affect the

hardness and wear resistance of these coatings. Thus these
coatings are recommended for service temperature below
340 °C (650 °F). Higher temperatures may tend to ­oxidize
the molybdenum constituent which could reduce coating
­integrity.

1.1 Typical Uses and Applications

n Hard bearing surfaces for shifter forks, synchronizer rings,
gear cones and pump seals
n Rebuilding worn, damaged cylinder bore walls and other
parts with a hard, wear-resistant surface
n Salvage of mismachined parts
n Abrasion resistance on machine element surfaces
n Sliding wear resistance for piston rings

DSM-0375.0 – FeMoC Composite Powder

© 2022 Oerlikon Metco 1
2 Material Information

2.1 Chemical Composition and Phase Constituents

Product Chemical Composition (wt. %)

Fe Mo C Mn
Metco 350NS Balance 16 – 18 2–3 0.25

2.2 Particle Size Distribution and Other Characteristics

Product Nominal Particle Size Distribution Hall Flow

Metco 350NS -90 +11 µm 18 – 33 s/50 g

Upper particle size distribution determined by sieve; lower size distribution determined by Microtrac.
Hall flow in accordance with ASTM B213

2.3 Key Selection Criteria n Metco 64 is a molybdenum/molybdenum carbide

n The molybdenum constituent gives rise to coatings with ­powder. Coatings of Metco 64 have better scuff and
excellent scuff resistance and improves chemical corro- ­corrosion resistance than coatings of Metco 350NS,
sion resistance over 300 series stainless steel substrates. with similar or slightly lower abrasion resistance.
n The scuff resistance of Metco 350NS coatings are n Amdry 1371, a blend of self-fusing nickel-based alloy
­compatible with many mating surfaces, including cast and molybdenum, produces coatings with similar
iron, iron-based alloys, aluminum and aluminum alloys. abrasion and scuff resistance, yet slightly better corro-
n Metco 350NS has a unique chemical and synergistic sion resistance than coatings of Metco 350NS.Coat-
­r­­­eaction during spraying that produces coatings with ings of Amdry 1371 can be used at service tempera-
­excellent wear resistance, with low levels of oxides. tures up to 350 °C (660 °F).
n Metco 350NS can be applied using atmospheric plasma n Chromium oxide composites can be considered as alter-
spray or combustion powder Thermospray™, including native materials, particularly for use in various chemical
use of MPS as the combustion powder Thermospray fuel medias as these materials produce very inert coatings.
gas. The chromium oxide component contributes hardness,
wear-resistance and thermal stability when used in sliding
2.4 Related Products contact. Products include:
n Molybdenum-based coatings are generally used for n Amdry 6462 and Amdry 6460 are fused and crushed
­sliding wear applications. They have good thermal chromium oxide composites. Coatings of these mate-
­conductivity, low thermal expansion, good frictional rials are tough, corrosion and wear resistant with high
­properties and self-bond to steel. Products include: resistance to mechanical shock compared to other ce-
n Amdry 313X is a pure molybdenum, agglomerated ramics and has good friction characteristics.
and spheroidized powder that can be used instead of n Metco 6483 is a sintered and crushed chromium oxide
Metco 350NS when better scuff and corrosion composite powder that produces hard coatings with
­resistance is ­required. excellent abrasion, heat and corrosion resistance.

DSM-0375.0 – FeMoC Composite Powder

© 2022 Oerlikon Metco 2
3 Coating Information

3.1 Key Thermal Spray Coating Information

Specification Typical Data (depending on spray process and gun chosen)

Recommended Spray Process Atmospheric Plasma Spray or Combustion Powder Thermospray™
Preparation When coating aluminum and aluminum alloy substrates, prepare surfaces us-
ing steel grit. Metcolite grit is not recommended.
Surface Roughness Ra As-Sprayed 6 – 22 µm 300 – 900 µin
Ground 0.2 – 1.0 µm 7 – 45 µin
Macrohardness 45 – 50 HRC
Microhardness 600 – 700 HV0.3
Density 6.9 – 7.2 g/cm3
Porosity 1.0 – 2.5 vol. %
Oxide Content 5 – 25 vol. %
Thickness Limits Combustion Spray 2 mm 0.080 in
Plasma Spray 0.6 mm 0.025 in
Bond Strength a 20 – 41 MPa 3000 – 6000 psi
Maximum Service Temperature  340 °C 650 °F
a On grit-blasted substrates; varies depending on substrate composition.

3.3 Coating Parameters Recommended Spray Guns

Please contact your Oerlikon Metco Account Representative
Atmospheric Plasma Combustion Powder
for parameter availability. For specific coating application
Metco 3MB series Metco 6P-II series
­requirements, the services of Oerlikon Metco’s Coating
­Solution Centers are available. Metco 9MB series Metco 5P-II
Metco F4 series

4 Commercial Information

4.1 Ordering Information and Availability

Product Order No. Package Size Availability Distribution

Metco 350NS 1000589 25 lb (approx. 11.4 kg) Stock Global

4.2 Handling Recommendations 4.3 Safety Recommendations

n Store in the original container in a dry location. See SDS 50-159 (Safety Data Sheet) in the localized version
n Tumble contents gently prior to use to prevent s­ egregation. applicable to the country where the material will be used.
n Open containers should be stored in a drying oven to SDS are available from the Oerlikon web site at
prevent moisture pickup. www.oerlikon.com/metco (Resources – Safety Data Sheets).

Information is subject to change without prior notice.