Location via proxy:   [ UP ]  
[Report a bug]   [Manage cookies]                
Scribd Logo
Upload

Welcome to Scribd!

  • 75 views

    Basell 2427h

    Uploaded by

    chaitanya

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Basell 2427h

    Uploaded by

    chaitanya
    75 views2 pages

    Original Title

    basell 2427h

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    75 views2 pages

    Basell 2427h

    Uploaded by

    chaitanya

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    Lupolen 2427 H

    Polyethylene, Low Density

    Product Description
    Lupolen 2427 H is an additivated, low density polyethylene. It contains an antioxidant, slip and
    anti-blocking agent. It is delivered in pellet form.

    Foodlaw compliance information about this product can be found in separate product
    documentation.

    This product is not intended for use in medical and pharmaceutical applications.

    Product Characteristics

    Status Commercial: Active

    Test Method used ISO

    Availability Europe, Asia-Pacific, Africa-Middle East

    Processing Methods Blown Film, Cast Film

    Features Unspecified Antiblocking , Low Friction, Opticals, Good


    Processability, Unspecified Slip

    Typical Customer Bags & Pouches, Blown Film, Cast Film, Film, Food Packaging Film,
    Applications Shrink Film

    Typical Properties Method Value Unit


    Physical
    Density ISO 1183 0.924 g/cm³
    Melt flow rate (MFR) (190°C/2.16kg) ISO 1133 1.9 g/10 min
    Mechanical
    Dart drop impact (50µm, Blown Film) ASTM D 1709 110 g
    Tensile Modulus ISO 527-1, -2 260 MPa
    Tensile Stress at Yield ISO 527-1, -2 11.0 MPa
    Tensile Strength ISO 527-1, -3
    25.0 MPa
    Note: MD
    21.0 MPa
    Note: TD
    Tensile Strain at Break ISO 527-1, -3
    250 %
    Note: MD
    600 %
    Note: TD
    Thermal
    Vicat softening temperature (A50 (50°C/h 10N)) ISO 306 94.0 °C
    Melting Temperature ISO 3146 111 °C
    Optical
    Haze (50µm) ASTM D 1003 <9 %
    Gloss ASTM D 2457
    (20°, 50µm) >50
    (60°, 50µm) >100
    Film
    Melt Temperature 160 to 200 °C

    Additional Properties
    Film properties tested using 50 µm thickness blown film extruded at a melt temperature of 180°C
    and a blow-up ratio of 1:2.5.
    Natural Silica, ISO 3451-1: 0.1%
    Erucamide, DIN 51454: 0.05%
    Failure Energy, DIN 53373, 50 µm: 4 J/mm
    Coefficient of Friction, ISO 8295: <20%
    Recommended Film Thickness: 20 to 60 µm

    Notes
    Typical properties; not to be construed as specifications.