Thermal characteristics of a class F fly ash

Article in Cement and Concrete Research · June 1998

DOI: 10.1016/S0008-8846(98)00054-4

CITATIONS READS
21 995

3 authors, including:

Prabir K. Kolay Devendra Narain Singh

Southern Illinois University Carbondale Indian Institute of Technology Bombay
108 PUBLICATIONS 1,369 CITATIONS 316 PUBLICATIONS 7,137 CITATIONS

SEE PROFILE SEE PROFILE

All content following this page was uploaded by Prabir K. Kolay on 08 October 2017.

The user has requested enhancement of the downloaded file.

 Cement and Concrete Research, Vol. 28, No. 6, pp. 841– 846, 1998
Copyright © 1998 Elsevier Science Ltd
Printed in the USA. All rights reserved
0008-8846/98 $19.00 1 .00
PII S0008-8846(98)00054-4

THERMAL CHARACTERISTICS OF A CLASS F FLY ASH

M.V.B.B. Gangadhara Rao, P.K. Kolay, and D.N. Singh1

Department of Civil Engineering, Indian Institute of Technology, Bombay, Powai,
Mumbai-400076, India

(Received November 3, 1997; in final form April 8, 1998)

ABSTRACT
It is necessary to evaluate thermal properties of geotechnical materials, viz.
soils and rocks, for power cables and oil pipe lines and disposal of nuclear
wastes. A situation may arise where the heat dissipation through the soils and
rocks may not be satisfactory, leading to adoption of a backfill. Fly ash can be
used in conjuction with aggregates to design a proper backfill material. The
thermal characteristics of this material, in terms of its resistivity, play an
important role in the design of a thermally stable backfill, i.e., Fluidized
Thermal Backfill (FTB). As such it is desired to establish thermal response of
the fly ash based on its physical and moisture- holding characteristics. In this
paper an effort has been made to evaluate the thermal resistivity of a Class F
fly ash using a laboratory thermal needle/probe. The effect of density of
compaction and the moisture content on the thermal response of the fly ash has
been also studied. © 1998 Elsevier Science Ltd

Introduction

Thermal properties of materials are important for various engineering projects, ranging from
those of man-made materials such as insulation, to those of natural materials such as soil,
which is significant in view of the modern trends of utilizing the subsurface for several
purposes such as burial of high voltage electric power cables (1), storage and containment of
radioactive spent fuel (2,3), burial of pipelines for the conveyance of high-temperature
liquids (oil pipes and steam pipes), and utilization of earth energy for space heating/cooling
via ground-coupled heat pumps (4,5). For these situations, thermal characteristics of the
material, such as the thermal resistivity and the thermal stability, must be known.
Soil as such is not a good conductor of heat when compared to the metals (normal
conductors). Soil thermal resistivity is a measure of the resistance offered by the soil to the
passage of heat. Thermal stability is normally related to the ability of moist soil to maintain
a relatively constant thermal resistivity when subjected to an imposed temperature difference.
Thermal instability occurs when a soil is unable to sustain a rate of heat transfer; to overcome
this, the native soil is replaced by materials (backfills) with better thermal properties. Fly ash,
mixed with sand and aggregates, can be used as a good backfill material, called Fluidized

1
To whom correspondence should be addressed.
841
842 M.V.B.B. Gangadhara Rao et al. Vol. 28, No. 6

Thermal Backfill (FTB) (2), to maintain thermally stable conditions. It is essential to access
the thermal behaviour of fly ash before it is utilized as an backfill material.
In this paper, the thermal characteristics of a class F fly ash have been evaluated using the
laboratory thermal probe.

Principle of Operation

For the sake of completeness, the principle of operation is presented in the following. A
thermal needle (or a Probe) approximates a line source of heat input of Q per unit length, of
constant strength, in an infinite homogeneous soil medium maintained at uniform tempera-
ture, initially. Temperature at any point in the soil medium depends on several variables, the
important ones being duration of heating (time) and the soil thermal conductivity. In the
mathematical form the same can be presented as (6):

]u
]t
5a S
] 2u 1 ]u
1
]r2 r ]r
D (1)

where u is the temperature of the soil mass, t indicates the time of heating, a is the thermal
diffusivity constant (5k/gzCp), k represents the thermal conductivity of the soil, Cp is the
specific heat of the soil, g represents the unit weight of the soil, and r is the radial distance
from the heat source.
Thus the temperature rise, Du, between the time interval t1 and t2 may be represented as:

Du 5 S D SD
Q
4pk
log e
t2
t1
(2)

As such, plot of temperature against log of time shows a straight portion of slope S D
Q
4pk
.
It will be noted that the average property of the body entering this expression is the thermal
coductivity, and that the other terms in Eq. 2 are quantities readily measurable with the
thermal probe designed by the authors.

Test Setup

Based on the above-mentioned principle, a needle that is stiff enough to withstand the
pressures generated either during the process of fly ash compaction in preparation of a
sample, or for inserting it into the fly ash after making a sample at a particular density, was
fabricated for thermal resistivity evaluation. Such an arrangement, as presented in Figure 1,
has been termed a “laboratory thermal probe,” which consists of insulated Nichrome heater
wire (with resistivity equal to 0.1923 V/cm) inserted in a copper tube (14 cm long, external
diameter of 2.5 mm). A thermocouple was attached on the surface of the tube as shown in
the figure. The calibration of this probe has been done using a standard liquid glycerol with
thermal resistivity equal to 349°C-cm/W. The thermal resistivity value of the glycerol as
measured by using this probe is observed to be 357.52°C-cm/W, with a small deviation of
only 2.4%.
A metal container (12.6 cm long, 10.1 cm diameter) was used to prepare fly ash samples
corresponding to a particular density. A 3-mm diameter hole was drilled in the sample so as
Vol. 28, No. 6 TEMPERATURE, FLY ASH, HUMIDITY, STABILITY 843

FIG. 1.
Details of the laboratory thermal probe.

to tightly fit the thermal probe into it. The probe was allowed to gain thermal equilibrium in
the fly ash for some time (5 min. approx.) followed by switching on the controlled electrical
power supply. The temperature of the probe was recorded as a function of time to compute
thermal resistivity of the fly ash as discussed earlier.

Properties of the Fly Ash

Fly ash from Koradi Thermal Power Plant in Nagpur (India) has been taken for the present
study. It is a light grey powder with specific gravity equal to 2.14. The particle size analysis
has been conducted using a laser particle analyzer. It is noticed that the fly ash sample
consists of about 90% silt (2–75 mm) with 10% clay (,2 mm).

Chemical Composition

The chemical composition (by percentage weight) is presented in Table 1.

844 M.V.B.B. Gangadhara Rao et al. Vol. 28, No. 6

TABLE 1
Chemical composition of the fly ash.
SiO2 59.89%
Al2O3 27.20%
Fe2O3 4.33%
CaO 1.01%
MgO 1.53%
SO3 0.03%
Na2O 0.06%
K2O 0.93%
MnO2 0.08%
TiO2 2.30%
P2O5 0.23%
Loss on Ignition 2.40%

Mineralogical Characterization

The fly ash sample has been evaluated for its mineral composition by scanning from 5– 60°
on a XRD spectrometer using Cu-Ka radiation. The minerals are identified by the Search
Match JCPDS. The minerals present in the same are: Quartz low (syn)-most predominant,
Mullite(syn)-predominant, Brookite, Sillimanite, and Ferroselite.

Compaction Characteristics

Standard Proctor compaction characteristics of the fly ash are presented in Figure 2.

FIG. 2.
Standard Proctor compaction curve for the fly ash.
Vol. 28, No. 6 TEMPERATURE, FLY ASH, HUMIDITY, STABILITY 845

FIG. 3.
Thermal resistivity curve for the fly ash.

Results and Discussions

Tests have been conducted to obtain thermal resistivity of the fly ash with varying moulding
moisture content for different density of compaction.
Figure 3 presents the thermal resistivity curves for the fly ash. From these curves it can be
noticed that for dry state of the fly ash, the thermal resistivity value varies from 900°C-cm/W
to 1150°C-cm/W with dry-density ranging from 1.0 to 1.1 gm/cc. With the addition of 5%
moisture to the oven-dry fly ash, the thermal resistivity values drop to 600 –750°C-cm/W.
The drop in resistivity values continues up to almost 20% moisture content. However, this
drop is much less as compared to the drop in the resistivity values for moisture content less
than 10%. It can be noticed that the variation of thermal resistivity values in the moisture
content range of 25 to 30% is almost negligible, and at 30% moisture content the fly ash
exhibits lowest resistivity value (the range being 250 to 300°C-cm/W), which remains
constant even with further addition of moisture. It is important to notice that minimum
resistivity values are achieved close to the optimum moisture content of the fly ash (the same
being 32%).
In general, from the resistivity-moisture content variations for fly ash (Fig. 3), it can be
 846 M.V.B.B. Gangadhara Rao et al. Vol. 28, No. 6

noticed that the resistivity of the fly ash decreases as its moisture content increases. The
reason is that when water is added to the ash, it forms a thin film around the fly ash particles
that eases the conduction of heat, i.e., incresasing its conductivity and reducing its resistivity.
This may also be attributed to the fact that the thermal resistivity of air (equal to 4000°C-
cm/W) is higher than that of the water (equal to 165°C-cm/W). The addition of water to the
fly ash results in a decrease in the air voids (and hence the density increases), and as such the
thermal resistivity of the fly ash in the near vicinity of its optimum moisture content (OMC)
attains almost a constant value that is the minimum value of thermal resistivity the fly ash can
exhibit. At this situation the resultant resistivity of the fly ash, known as “critical moisture
content,” is more dependent upon the resistivity of the pore water. There is a rapid increase
in the thermal resistivity of the soil, with a small reduction in moisture content at moisture
contents less than the critical moisture content. This critical moisture content depends on the
particle size distribution and the density of compaction.
From the resistivity-moisture content variations, another important observation is that as
compaction density increases, critical moisture content decreases. The range of critical
moisture content values for fly ash as obtained in the present investigation is 28 –32%.

Conclusions

Based on the results and discussions presented in the above, the following generalised
conclusions can be made:

1. Resitivity of the fly ash decreases as the dry density increases. However, this effect is
much more pronounced on the dry OMC as compared to the wet OMC.
2. The rate of decrease of resistivity is much more in the initial stage of moisture addition
as compared to the moisture content close to the OMC. Close to the OMC the resistivity
of the fly ash is minimal, and it remains almost constant, corresponding to the critical
moisture content for the fly ash.

References

1. S.Y. King and N.A. Halfter, Underground Power Cables, Longman Press, London, 1982.
2. F.J. Sanger, J. Soil Mech., Fdns. Div., Am. Soc. Civ. Engrs. 94, 131 (1968).
3. H.R. Thomas, Int. J. Numer. Analyt. Meth. Geomech. 9, 573 (1985).
4. D.L. Slegel and L.R. Davis, J. Heat Transfer 99, 541 (1977).
5. J. Ewen, Proc. Conf. Long Term Storage in Solar Systems, p. 56, 1984.
6. F.C. Hopper and F.R. Lepper, Trans. Am. Soc. Heat. Vent. Engrs. 56, 309 (1950).

View publication stats