Location via proxy:   [ UP ]  
[Report a bug]   [Manage cookies]                
Scribd Logo
Upload

Welcome to Scribd!

  • 897 views

    8810

    Uploaded by

    Sikander Aleem
    Product code: Xylan (r) 8810 Organic solvent based, food contact acceptable, non-stick, interior coating. Final product quality and performance depends on careful SUBSTRATE PREPARATION. Each item to be coated must be free of all contaminants, e.g. Oil, grease, detergent, rust and blast media. An Ra (mean roughness) of 4 +1 microns, measured using surface roughness measuring equipment is recommended.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    8810

    Uploaded by

    Sikander Aleem
    897 views2 pages
    Product code: Xylan (r) 8810 Organic solvent based, food contact acceptable, non-stick, interior coating. Final product quality and performance depends on careful SUBSTRATE PREPARATION. Each item to be coated must be free of all contaminants, e.g. Oil, grease, detergent, rust and blast media. An Ra (mean roughness) of 4 +1 microns, measured using surface roughness measuring equipment is recommended.

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Product code: Xylan (r) 8810 Organic solvent based, food contact acceptable, non-stick, interior coating. Final product quality and performance depends on careful SUBSTRATE PREPARATION. Each item to be coated must be free of all contaminants, e.g. Oil, grease, detergent, rust and blast media. An Ra (mean roughness) of 4 +1 microns, measured using surface roughness measuring equipment is recommended.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    897 views2 pages

    8810

    Uploaded by

    Sikander Aleem
    Product code: Xylan (r) 8810 Organic solvent based, food contact acceptable, non-stick, interior coating. Final product quality and performance depends on careful SUBSTRATE PREPARATION. Each item to be coated must be free of all contaminants, e.g. Oil, grease, detergent, rust and blast media. An Ra (mean roughness) of 4 +1 microns, measured using surface roughness measuring equipment is recommended.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    PRODUCT DATA SHEET

    1. GENERAL INFORMATION.
    Product name: Product code: Recommended use: Typical applications:

    PAGE: PRINT DATE

    1 of 2 04/03/2003

    Xylan 8810
    Organic solvent based, food contact acceptable, non-stick, interior coating. Thermostatically controlled appliances, Industrial Use, waffle iron, |Storage Tank. Broad Chemical Resistant.

    2. PRODUCT SPECIFICATIONS.
    Theoretical solids: Relative density: Theoretical coverage @ 25 microns: Theoretical coverage at the recommended dry film thickness: Viscosity, as shipped ( 23C) 24.3 - 40.1 % by weight 14.9 - 22.7 % by volume ( 23C) >= 1.08 g / cm 5.33 - 7.61 m 5.3 - 9.5 m 70 85 Flash point: Operating temperature: 69 C -40C to 330C - Continuous. -40C to 360C - Intermittent.
    2 2 3

    <= 1.30 g / cm
    2/ 2/

    / kg 5.95 - 9.06 m / kg 5.9 - 11.3 m

    litre(s): litre(s):

    75 seconds in a DIN 4 Viscosity cup 90 seconds in a FORD 4 Viscosity cup

    105 - 115 seconds in a BS 4 Viscosity cup

    3. SUBSTRATE PREPARATION.
    Final product quality and performance depends on careful substrate preparation. Contaminated substrates may cause poor adhesion of the coatings or defects in the final dry film. Each item to be coated must be free of all contaminants, e.g. oil, grease, detergent, rust and blast media. Substrate preparation should be based on the design requirements of the part. If you are unsure which process is best suited to your needs please contact our technical service department. The following are the recommended substrates and substrate preparation used with this coating. Substrates: Substrate preparation: Aluminium / Mild steel / Stainless Steel. Degrease and gritblast. An Ra (mean roughness) of 4 1 microns, measured using surface roughness measuring equipment is recommended. This can typically be obtained using 40 - 60 mesh (250 - 375 micron) iron free, aluminium 2 ). However since the Ra value achieved depends oxide grit at 80 psi (5.5 kgf/cm on the actual substrate, initial trials are recommended to establish the optimum grit size and air pressure for each substrate type. Not required but Xylan 4080 / Xylan 4090 can be used to improve overall performance.

    Primer:

    4. PRODUCT PREPARATION FOR APPLICATION.


    Mixing prior to use: Recommended application viscosity: Viscosity adjustment / thinning: It is imperative that the material is adequately mixed before use. The material should be high speed / shear mixed before use to eliminate any settling. This material is generally suitable for application as supplied. Optimum results are obtained when the material is at "room temperature" nominally 15 - 30C. If absolutely necessary adjust viscosity with Whitford solvent 88. Add thinner in 2% increments until the desired application characteristics are obtained. Take care not to add too much solvent as low viscosity may produce rapid settling, runs and sags or low film thicknesses.

    The information presented in this publication is based upon the research and experience of Whitford. No representation or warranty NON-WARRANTY. is made, however, concerning the accuracy or completeness of the information presented in this publication. Whitford makes no warranty or representation of any kind, express or implied, including without limitation any warranty of merchantability or fitness for any particular purpose, and no warranty or representation shall be implied by law or otherwise. Any products sold by Whitford are not warranted as suitable for any particular purpose to the buyer. The suitability of any products for any purpose particular to the buyer is for the buyer to determine. Whitford assumes no responsibility for the selection of products suitable to the particular purposes of any particular buyer. Whitford shall in no event be liable for any special, incidental, or consequential damages.

    Product name:
    Filtering:

    Xylan

    8810

    PAGE: PRINT DATE

    2 of 2 04/03/2003

    This material is sieved before dispatch from our factory but as an added precaution we recommend that you filter it through a 75 mesh (200 micron) sieve prior to use.

    5. RECOMMENDED APPLICATION TECHNIQUE.


    Application equipment / technique: This material is designed primarily for spray application. Contact our technical service department if other types of application are being considered. This coating is applied in our laboratories using a Binks Bullows 630 spray gun equipped with a 071 (1.8 mm) material nozzle, a 66SD1 air cap and a stainless steel needle. The air supply should be equipped with air and moisture traps which are drained / serviced regularly. The proper amount of coating should be achieved with two or three passes of the spray gun across the work piece. Apply the coating to a uniform, full wet appearance. 22.5 2.5 microns (typical wet film thickness 120 15 microns). < 45C (110F). Typically 1. Will recoat, flash off between coats if applying multiple coats. Whitford solvent 91.

    Recommended dry film thickness / coat: Substrate temperature: Number of coats recommended: Clean-up solvent:

    6. FLASH OFF AND CURE SCHEDULE.


    Please note that oven temperatures can be very different to substrate temperatures and the following temperatures apply to PEAK SUBSTRATE TEMPERATURE . Flash-off conditions: Optimum cure schedule: Minimum cure temperature: Maximum cure temperature: 10 minutes at 100 - 150C [212F]. 5 minutes at 400C [752F]. 15 minutes at 375C [707F]. 5 minutes at 420C [788F].

    7. WHITFORD QUALITY CONTROL TEST METHODS.


    Evaluate the cured coating according to the following specifications: Test. Test method number. Specification. Dry film thickness 114 A 22.5 2.5 microns. Adhesion, boil, bump, crosshatch and sellotape 132 K No loss of adhesion. Non-stick test (egg) 199 L Test food removed intact, coating wiped clean. Non-stick test (pancake) 199 M Test food removed intact, coating wiped clean. 0-T Bend 133 C No loss of adhesion.

    8. SHELF LIFE, STORAGE AND HANDLING.


    Handling: When using do not smoke. Avoid contact with the skin and the eyes. Keep away from tobacco products. Do not breathe vapours or spray mist. Use only in area provided with appropriate exhaust ventilation. Wash hands before breaks and at the end of workday. Keep containers tightly closed in a cool, well-ventilated place. Store in original container. Keep at temperatures between 5 and 30C. 12 months. High speed/shear mix the material(s) every month to maintain quality. H. C. Wilson J. Gascoyne M. J. Day 20 13/02/2003 30/07/2002

    Storage: Shelf life: Prepared by: Checked by: Approved by: Revision number: Revision date: Date of last revision: