    Paint Inspection Limited Surface Preparation Standards

    Uploaded by

    Andrew Patterson
    The document provides guidelines for steel surface preparation grades prior to painting. It establishes four grades of rust (A-D) and several preparation grades for both hand/power tool cleaning and blast cleaning. The higher the preparation grade, the more thoroughly mill scale, rust, and other matter are removed from the steel surface. Thorough preparation is important for an anti-corrosive paint to achieve its effective life. The standards aim to clearly specify the required preparation quality for different situations.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    Paint Inspection Limited Surface Preparation Standards

    Uploaded by

    Andrew Patterson
    426 views19 pages
    The document provides guidelines for steel surface preparation grades prior to painting. It establishes four grades of rust (A-D) and several preparation grades for both hand/power tool cleaning and blast cleaning. The higher the preparation grade, the more thoroughly mill scale, rust, and other matter are removed from the steel surface. Thorough preparation is important for an anti-corrosive paint to achieve its effective life. The standards aim to clearly specify the required preparation quality for different situations.

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    The document provides guidelines for steel surface preparation grades prior to painting. It establishes four grades of rust (A-D) and several preparation grades for both hand/power tool cleaning and blast cleaning. The higher the preparation grade, the more thoroughly mill scale, rust, and other matter are removed from the steel surface. Thorough preparation is important for an anti-corrosive paint to achieve its effective life. The standards aim to clearly specify the required preparation quality for different situations.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    426 views19 pages

    Paint Inspection Limited Surface Preparation Standards

    Uploaded by

    Andrew Patterson
    The document provides guidelines for steel surface preparation grades prior to painting. It establishes four grades of rust (A-D) and several preparation grades for both hand/power tool cleaning and blast cleaning. The higher the preparation grade, the more thoroughly mill scale, rust, and other matter are removed from the steel surface. Thorough preparation is important for an anti-corrosive paint to achieve its effective life. The standards aim to clearly specify the required preparation quality for different situations.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 19

    Paint Inspection Limited

    Engineers Field Guide


    www.paint-inspection.co.uk

    ==========================================================================================

    Contents
    Foreword Rust grades Preparation grades. Scraping and wire-brushing Preparation grades. Blast cleaning Illustrations of standards Steel Surface Preparation Product Application SSPC Preparation Descriptions

    2|P ag e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    The effective life of a coating of anti-corrosive paint applied to a steel surface is to a very large extent, dependent on how thoroughly the surface has been prepared prior to painting. It is also important to be able to specify clearly the quality of preparation required in each particular case. Accordingly a Standard has been approved, specifying four grades of rusting and a number of preparation grades, each establishing a quality grade or preparation prior to protective painting required on a steel surface in a standard rust grade. These grades are presented in this Standard as a series of prints, which provide a clearer and more rapidly appreciated definition than a verbal description. The standard has been prepared by the Swedish Corrosion Institute in cooperation with the American Society for Testing and Materials, ASTM, and Steel Structures Painting Council, SSPC, USA. In the specifications relating to preparation of surfaces prior to painting, the SSPC and SIS designations correspond as follows:

    SSPC-Vis 1
    SSPC SP5 SSPC SP10 SSPC SP 6 SSPC SP 7

    SIS 05 59 00
    A Sa 3, B Sa 3, C Sa 3 and D Sa 3 A Sa 2, B Sa 2, C Sa 2 and D Sa 2 B Sa2, C Sa 2 and D Sa 2 B Sa1, C Sa 1 and D Sa 1

    Description of the SSPC standards can be found later in this field guide.

    3|P ag e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust grades A B C D
    Steel surface covered completely with adherent mill scale and with little if any rust. Steel surface which has begun to rust and from which the mill scale has begun to flake. Steel surface on which the mill scale has rusted away or from which it can be scraped, but with little pitting visible to the naked eye Steel surface on which the mill scale has rusted away and on which considerable pitting is visible to the naked eye.

    Preparation grades. Hand & Power Tool Preparation Standards


    It is assumed that prior to treatment the steel surface has been cleaned of dirt and grease, and that the heavier layers of rust have been removed by chipping.
    St 2 Thorough scraping and wire-brushing - machine brushing - grinding - etc. The treatment shall remove loose mill scale, rust and foreign matter. Finally, the surface is cleaned with a vacuum cleaner, clean dry compressed air or a clean brush. It should have a faint metallic sheen. The appearance shall correspond to the prints designated St 2. Very thorough scraping and wire-brushing - machine brushing - grinding - etc. Surface preparation as for St 2, but much more thoroughly. After removal of dust, the surface shall have a pronounced metallic sheen and correspond to the prints designated St 3.

    St 3

    4|P ag e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Preparation grades. Blast cleaning


    It is assumed that prior to treatment the steel surface has been cleaned of dirt and grease, and that the heavier layers of rust have been removed by chipping.

    Sa 1

    Light blast cleaning. Loose mill scale, rust and foreign matter shall be removed. The appearance shall correspond to the prints designated Sa 1. Thorough blast cleaning. Almost all mill scale, rust and foreign matter shall be removed. Finally, the surface is cleaned with a vacuum cleaner, clean dry compressed air or a clean brush. It shall be greyish in colour and correspond in appearance to the prints designated Sa 2. Very thorough blast cleaning. Mill scale, rust and foreign matter shall be removed to the extent that the only traces remaining are slight stains in the forms of spots or stripes. Finally, the surface is cleaned with a vacuum cleaner, clean dry compressed air or a clean brush. It shall correspond in appearance to the prints designated Sa 2. Blast cleaning to pure metal. Mill scale, rust and foreign matter shall be removed completely. Finally, the surface is cleaned with a vacuum cleaner, clean dry compressed air or a clean brush. It shall then have a uniform metallic colour and correspond in appearance to the prints designated in Sa 3.

    Sa 2

    Sa 2

    Sa 3

    5|P ag e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade A

    Rust Grade B

    6|P ag e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade C

    Rust Grade D

    7|P ag e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Preparation Standards Hand & Power Tools

    Rust Grade B Preparation Standard St 2

    Rust Grade B Preparation Standard St3

    8|P ag e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade C Preparation Standard St2

    Rust Grade C Preparation Standard St3

    9|P ag e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade D Preparation Standard St2

    Rust Grade D Preparation Standard St3

    10 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Preparation Standards Blast Cleaning

    Rust Grade A Blast Cleaning Standard Sa2

    Rust Grade A Blast Cleaning Standard Sa3

    11 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade B Blast Preparation Standard Sa1

    Rust Grade B Blast Preparation Standard Sa2

    12 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade B Blast Preparation Standard Sa2

    Rust Grade B Blast Preparation Standard Sa3

    13 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade C Blast Preparation Standard Sa1

    Rust Grade C Blast Preparation Standard Sa2

    14 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade C Blast Preparation Grade Sa2

    Rust Grade C Blast Preparation Grade Sa3

    15 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade D Blast Preparation Grade Sa1

    Rust Grade D Blast Preparation Grade Sa2

    16 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Rust Grade D Blast Preparation Sa2

    Rust Grade Blast Preparation Sa3

    17 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    Steel Surface Preparation and Product Application Advantages Of Blast Cleaning


    It has been indicated by The British Iron & Steel Research Association that surface coating applied to blast cleaned substrates may be expected to last five times as long as the same surface that had been weathered, then manually wire brushed. The preparation of steelwork obviously has a bearing on the success or failure of any surface coating, and therefore the following information is relevant to steelwork prepared to Swedish Standard SIS 05 59 00 Sa 2.5. British Standard BS 7079: Part A1: 1989 (ISO 8501 1:1988) Surface Finish of Blast Cleaned Steel for Painting and Steel Structures Painting Council of America also set out standards for cleanliness.

    Amplitude Surface Profile


    Amplitude is a measurement (given in microns (m)), that shows the difference between the peaks and troughs in a metal surface produced by blast cleaning. There must be adequate amplitude on the surface of the substrate to ensure good adhesion commonly known as the key. However, if the amplitude on the surface is too rough, then there is a risk that the peaks of the blast cleaning process will protrude through the paint film, leading to significantly higher paint consumption or peak rashing or spot rusting. On average, a surface that has been grit blasted should have a profile that lies between 50 to 70 microns, and shot blasted steel under blast primers should be 30 to 50 microns. Profiles in excess of 100 microns should be avoided.

    Degreasing
    Any surface that is to be blast cleaned and subsequently painted must be thoroughly degreased and cleaned prior to application of any coating. Degreasers must be used in conjunction with an absorbent cloth which must be changed frequently to avoid re-depositing oil / grease onto the substrate. When degreasing, it is necessary to wear adequate personal protection equipment. Refer to manufacturers Material Safety Data Sheet for further information.

    18 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147

    SSPC Preparation Descriptions


    Standard SSPC SP5 Description NACE A White Metal Blast Cleaned surface, when viewed without NACE 1 magnification, shall be free of all visible oil, grease, dirt, dust, mill scale, rust, paint, oxides, corrosion products, and other foreign matter. Before blast cleaning, visible deposits of oil or grease shall be removed by any of the methods specified in SSPC-SP1 or other agreed upon methods A Near-White Blast Cleaned surface, when viewed without NACE 2 magnification, shall be free of all visible oil, grease, dirt, dust, mill scale, rust, paint, oxides, corrosion products, and other foreign matter, except for staining. Staining shall be limited to no more than five percent of each square-inch of surface area and may consist of light shadows, slight steaks, or minor discoloration caused by stains of rust, stains of mill scale, or stains of previously applied paint. Before blast cleaning, visible deposits of oil or grease shall be removed by any of the methods specified in SSPCSP1 or other agreed upon methods A Commercial Blast Cleaned surface, when viewed without NACE 3 magnification, shall be free of all visible oil, grease, dirt, dust, mill scale, rust, paint, oxides, corrosion products, and other foreign matter, except for staining. Staining shall be limited to no more than 33 percent of each square inch of surface area and may consist of light shadows , slight streaks, or minor discoloration caused by stains of rust, stains of mill scale, or stains of previously applied paint. Before blast cleaning, visible deposits of oil or grease shall be removed by any of the methods specified in SSPCSP1 or other agreed upon methods. A Brush Off Blast Cleaned surface, when viewed without NACE 4 magnification, shall be free of all oil, grease, dirt, dust, loose mill scale, loose rust, and loose paint. Tightly adherent mill scale, rust, and paint may remain on the surface. Mill scale, rust, and coating are considered adherent if they cannot be removed by lifting with a dull putty knife. Before blast cleaning, visible deposits of oil or grease shall be removed by any of the methods specified in SSPCSP1 or other agreed upon methods.

    SSPC SP10

    SSPC SP6

    SSPC SP7

    19 | P a g e

    Paint Inspection Ltd, Trafalgar Wharf Portchester PO6 4BX 023 93233147