Draft Copy Only

SEMINAR ON ENERGY CONSERVATION IN IRON CASTING INDUSTRY

Sponsored by United Nations Industrial Development Organization (UNIDO) and Ministry of International Trade and Industry (MITI), Japan Hosted by Ministry of Industry Socialist Republic of Viet Nam Organized by The Energy conservation Center, Japan (ECC)

1998 Hanoi

PREFACE
The conservation of energy is an essential step we can all take toward overcoming the mounting problems of the worldwide energy crisis and environmental degradation. Although developing countries and countries with

economies in transition are very much interested in addressing the issues related to the inefficient power generation and energy usage in their countries, only a minimum amount of information on the rational use of energy is available to them. Therefore, distributing the available information on modern energy saving techniques and technologies to government and industrial managers, and to engineers and operators at the plant level in these countries is essential. In December 1983, UNIDO organized a regionalmeeting on energy consumption and an expert groupmeeting on energy conservation in small- andmedium-scale industries for Asian countries. The outcome of these promotional activities prompted UNIDO to initiate a new regional programme designed to increase the awareness and knowledge of government officials and industrial users on appropriate energy saving processes and technologies. In 1991, the first project, Programme for Rational use of Energy Saving Technologies in Iron and Steel and Textile Industries in Indonesia and Malaysia (US/RAS/90/075), was approved and financed by the Government of Japan. The successful completion of this project prompted UNIDO to request the financial support of the Government of Japan to carry out similar projects under this programme in other Asian countries. Since 1992, under continuous support of the Government of Japan, three other projects have successfully been completed: Rational Use of Energy Saving Technologies in Pulp and Paper and Glass Industries in the Philippines and Thailand (US/RAS/92/035); in Ceramic and Cement Industries in Bangladesh and Sri Lanka (US/RAS/93/039); and in Plastic Forming and Food Industries in India and Pakistan (US/RAS/ 94/044). This year UNIDO is carrying out the programme in China and Vietnam, targeting two energy intensive industrial sub-sectors: iron casting andrubber industries. Iron casting industry consumes a substantial amount of energy. Excessive

use of energy is usually associated with many industrial plants worldwide, and iron casting plants are no exception. Enormous potential exists for

cost-effective improvements in the existing energy-using equipment.

Also,

application of good housekeeping measures could result in appreciable savings in energy. Therefore, it is imperative to introduce anddistribute information on modern energy-saving techniques and technologies among the parties

concerned in government and especially, at plant level, in industries. To achieve the objectives of this programme, UNIDO has adopted the following strategy:

Conduct plant surveys to characterize energy use and to identify measures to improve energy conservation at the plants. Prepare handy manuals on energy management and on applicable energy conservation techniques and technologies. Organize seminars to discuss the content of the handy manuals and the findings of the plant surveys with government officials, representatives of industries, plant managers and engineers. Distribute the handy manuals to other developing countries and countries with economies in transition for their proper use by the targeted industrial sectors. UNIDO prepared this handy manual for the iron casting industry, with the cooperation of experts from the Energy Conservation Center, Japan (ECCJ), on energy saving technologies in the framework of this UNIDO programme. It is designed to provide an overview of the main processes involved in iron casting, and to present a concise outline of the applicable energy saving measures. Appreciationis expressed to the following institutions for their valuable contribution to the successful preparation and publication of this manual:

The State Economic and Trade Commission of the People's Republic of China; The Ministry of Industry of the Socialist Republic of Viet Nam; The Ministry of International Trade and Industry of Japan; and The Energy Conservation Center, Japan.

Contents

1.

Manufacturing of castings and energy . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1

2.

Production of cast iron and energy consumption ..................... 2 2.1 Cast iron .............................................................. 2 2.2 The production of cast iron and energy consumption rate ....... 3 2.3 The yield of products and the energy consumption rate .......... 4 2.4 Cast iron melting and energy conservation ........................ 6

3. Cupola melting ............................................................ 9 3.1 Functions of cupola .................................................. 3.2 Structure of cupola .................................................. 3.3 Melting operation of cupola ........................................ 9 9 16

3.4 Foundry coke .......................................................... 19

4.

Energy conservation of cupola ......................................... 4.1 Heat efficiency of cupola .......................................... 4.2 Calculation of heat input .......................................... 4.3 Calculation of heat output .........................................

22 22 23 25

4.4 Heat balance diagrams and heat efficiency of a cupola ......... 25

5.

Improving the heat efficiency of a cupola .......................... 27 5.1 Hot blast cupola ..................................................... 27 5.2 Oxygen enriching cupola ............................................. 5.3 Humidity control cupola ............................................. 5.4 Multi-stage air blasting cupola ................................... 29 31 33

5.5 Water cool cupola .................................................... 36

5.6 Improvement of heat efficiency by synergetic effect of air blast conditions . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 39 5.7 Examples of improvement in properties of molten metal by measurement control of a cupola . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 41

6.

Natural gas cupola ......................................................

46

6.1 The structure of a natural gas cupola ............................ 46 6.2 Comparison of melting energy ....................................... 49

6.3 Comparison of exhaust gas in melting ............................. 50 6.4 Advantages of a natural gas cupola ................................ 51

7.

Induction melting furnace ..............................................

53

7.1 Features of induction melting furnace ............................ 53 7.2 Heat balance of induction furnace ................................. 53 7.3 Energy saving measures for induction furnaces
l

................ 56

8.

Arc furnace melting . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 68 8.1 Melting energy . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 68 8.2 Energy saving measures for arc melting furnace
l

............... 69

Energy Conservation in Cast Iron Foundry

1.

Manufacturing of castings and energy

The foundry sector is well recognized as one of the supporting industries for the machinery and assembling industry. With a recent remarkable economic

development in Asia, the production of castings, as apart of process materials in every engineering industry, has been increased; that of the Asian area is the highest in the world. However, the production of castings per capita is

only 8.2 kg, which is lower than world average of 13.6 kg. This fact shows that the production of castings will be sure to increase along with an economic growth not only in the Asian area, but also in developing countries. From another point of view on the economic development, an increase in the amount of energy consumption has become as a great problem for mankind. Energy problems such as limited fossil fuels, global warming caused by carbon dioxide generated by combustion, air pollution caused by other oxides,

destruction of plants and world heritage buildings caused by acid rain generated by sulphur oxides, radioactive wastes from nuclear power plants, etc. to be continued on the 21st century, are important problems inevitable for the survival of mankind. Since a large amount of energy is consumed in melting metals at high temperatures, the foundry sector has to be a source of various kinds of

pollution; on the other hand, it plays a role in recycling a large amount of metal scraps occurring in a modern society. Thus, the production of castings

has a lot of global environmental problems to be solved in the future. The development of an earth-friendly casting production process is the highest on the list in the foundry industry.

- l -

2.

Production of cast iron and energy consumption 2.1 Cast iron

The term "Cast iron" is a general term for "gray iron castings" and "spheroidal graphite cast iron castings". Since cast iron is easy to

manufacture and its manufacturing cost is low, and, besides, it has various physical and chemical properties, it is used in the largest amount among metal products in almost all area of industries including the automobile in the beginning. The annual production of cast iron castings in the world

is over 50 million tons. Gray iron castings are distinguished by good castability, abrasion resistance, damping capacity, corrosionresistance, machinability, etc.; they have been used for a long time and are produced in the largest amount among all sorts of castings. iron. Spheroidal graphite cast iron is superior to gray cast iron in mechanical properties, especially in ductility. Though only a half century has passed It forms about 75% of the total production of cast

since the invention of spheroidal graphite cast iron, its production has been increasing year by year since its utilization technology was established; it reaches 13 million tons, which is 25% of whole cast iron The 21st century

and the further increase will be expected also in the future.

may be called as the age of spheroidal graphite cast iron. Thoughmalleable iron castings are a parity of cast iron, statistically it is usually excluded from cast iron. Since malleable cast iron has to be

heattreated in the process of its manufacturing for long hours at high temperature in order to improve its mechanical properties, a large amount of energy has to be consumed; the rate of energy consumption per ton of malleable cast iron is four or more times of cast iron. Therefore malleable

cast iron is replaced with spheroidal graphite cast iron and its production has remarkably decreased.

- 2 -

2.2 The production of cast iron and energy consumption rate

The process of manufacturing iron castings is mainly divided into the melting process where metal is melted at high temperature over 1400C and the molding process where a mold is prepared into which molten iron is poured. It is obvious that of these two processes the melting process consumes most of cast iron manufacturing energy. Though iron castings are mainly used as Some of them may be The amount of energy

cast for final products having necessary properties. subjected to heat treatment to get necessary properties.

consumed varies depending on the materials and it is said that 50 to 90% of whole energy for the production of iron castings is consumed in melting process. To ensure energy conservation in cast iron foundry, it is necessary to grasp the amount of energy consumed in them and to recordthe kinds andamounts of energy used in the foundry every month and every year. Since the amount

of energy used is expressedusing different energy consumption rate for each kind of energy, the total consumption of heat is obtainedby summing up every kind of energy consumed (kcal) after calculating the amount of energy consumed using the respective heat consumption rate. Naturally, this total amount of heat varies depending on the change in the production volume, and it is impossible to evaluate the state of energy conservation only by the total amount of heat. The value obtained by dividing

this total amount of heat by the weight of production (in tons) is called the unit requirement for converting the amount of heat of energy (kcal/ton) and is used as an evaluation standard.

- 3 -

2.3 The yield of products and the energy consumption rate

The energy consumption rate is a value obtained by dividing the total consumption of energy by the production volume by ton, and the yield of products, that is, the ratio of the weight of final products to that of raw materials used has a great influence on the energy consumption rate. It is

indispensable for reducing the unit requirement to improve the yield of products, which results from the foundry technology accumulated in each process of manufacturing of castings.

(a) The yield of melting

The yield of melting is defined as the percentage of the weight of molten metal cast in the mold against that of raw materials charged in the melting furnace. The yield of melting becomes worse because of metal loss

due to oxidation in the melting process, metal adhesion to the furnacewall, ladle, etc., molten metal disposal due to improper chemical compositions and temperature, failure by poor pouring into the mold, residual molten metal due to rough estimation of weight, etc.

(b) The yield of casting

The cast shape against its final shape is planned prior to patternmaking, some surpluses are needed for sound castings such as, machining allowances, pattern draft. Padding for better directional solidification, wall Based on

thickness allowances covering dimensional fluctuation, and etc.

the above shape, risers and gating system are designed, that is, proper risers to compensate the shrinkage of molten metal through solidification and gating system to prevent any damage on castings by controlling speed of molten flow and to avoid any slag inclusions into castings. The yield of casting is defined as the percentage of the weight of deliver castings against cast weight including whole surpluses of the avobe.

- 4 -

The yield of casting is reduced by the deformation of the mold during molding caused by pattern such as loosening, low accuracy, insufficient strength, obsolescence, insufficient draft angle, etc., by unnecessary

large risers and gating system, by expansion of the mold due to weakness of molding sand, by lifting of the cope and leaking of molten metal due to clamping of the mold and an insufficient weight, etc. Adversely, the

yield can be improved by using a cylindrical sleeve ensuring heat insulation of the riser, a heat generating sleeve actively heating the riser by exothermic reaction, or a chiller for thick parts to reduce the size of the feeding head, etc.

(c) The percent defective of castings

Some castings are judged to be rejected according to the inspecting standard in the finishing and inspection process before shipment.

Defective castings show their defects in various forms andcauses of defects are not simply connectedwith defective phenomena. Practical information

on all the processes of manufacturing of castings and a lot of experience ensuring correct evaluation are necessary for taking measures against defects. Taking measures against defects in casting correctly found may

sometimes lead to lowering of the yield, but it is sure to be increased on the whole by the reduction in the percent defective. Also in melting, the quality of cast iron obtained can vary subtlely depending on the raw materials and melting conditions. Shrinkage cavities and chills can be

caused frequently in castings even with the same chemical compositions of molten metal. This is explained by oxidation and melting of the cupola.

It is the accepted view that high temperature melting over 1550C is necessary to prevent the above phenomenon. Raising tapping temperature

will lead to consumption of excessive energy, but energy conservation can be realized by lowering the percent defective of castings.

- 5 -

2.4

Cast

iron

melting

and

energy furnace

conservation

2.4.1

Cast

iron

melting

Fig.1 shows the kinds of cast iron melting furnace.

Today the

percentage of cupolas and induction furnaces used for cast iron melting is obscure due to lack of proper statistics. Systems with a cupola used

for primary melting formedabout 85 % in 1970s, but it was remarkably reduced to 63% around 1980, and after that cupolas may be used at a percentage of
50 to 60%.

Fig.1

Classification

of

cast

iron

melting

furnaces

The cupola is a shaft furnace for continuous melting of cast iron with new pig iron, return scrap iron, and steel scrap used as raw materials and coke used as a fuel. A cupola has not only an economic advantage of low

equipment cost, but also refining and self-purifying capability, which makes it possible to get excellent molten metal even from inferior-quality raw materials and has been widely used. However, the exhaust gas from cupola, containing not only carbon

- 6 -

dioxide from coke combustion, but also smoke and dust generated coak ash, NO, and SO,, causes pollution in air and working environment. The use of a solid fuel makes it difficult to manage and control operation, making it difficult to cope with mechanization, personnel saving, especially lack of skilled workers. The induction furnace is of electric heating type, whichmakes it easy to handle and to control temperature and to adjust chemical compositions has an advantage over cupola in capability to improve the quality of material and ensure the reliability of quality. In addition, since air is not used

for heating, oxidation loss of metal is low, the amount of carbon dioxide and smoke and dust generated is less, which can improve working environment; and is useful for the protection of global environment. However, high

equipment cost, comparatively high power rates, etc. make the induction furnace have to share the major part of cast iron melting with the cupola. The arc furnace has developed mainly as a steel melting furnace. In Japan some people say that there are technical problems inmelting of gray cast iron, and only 3 to 5% of whole melting process are seemed to be arc furnace including the use as a dual melting furnace with a cupola.

2.4.2 Energy conservation in melting

Independently of the kind of melting furnace,

the following

considerations are necessary for energy conservation in the melting process: (1) improvement of melting operation; (2) reduction of heat input; (3) reduction of heat loss. Items characteristic of each sort of melting furnace will be described in details later; the following are common ones:

- 7 -

(1) Improvement of melting operation a) Removal of rust, sand and oil stain on charged scrap

They form slag which need more heat input; they shall be removed by shot blast before charging. In addition, attention shall be paid

to the scrap storage to prevent rusting.

To reduce melting time, analysis time shall be reduced as far as possible. To realize this, it is necessary to put the melting furnace

and analysis test place as near as possible and attention shall be paid for rapid and exact communication of the analysis result.
c) Reduction waste time for molding and crane to furnace

Attention shall be paid not to hold molten metal uselessly by mismanaging the tapping timing with mold preparations or by waiting a crane, etc.
d) Reduction in residual molten metal

The weight of metal cast shall be estimated properly to reduce the amount of residual molten metal.

(2) Reduction of heat input a) Lowering of temperature of molten metal

To avoid raising of tapping temperature in consideration of temperature loss during pouring and keeping a proper pouring temperature, attention shall be paid to perform preheating of the ladle, to prevent heat radiation using the lid of the ladle, to locate themelting furnace and pouring place as near as possible, and to reduce moving time, etc.

(3) Reduction of heat loss

Details will be described in each sort of furnace.

- 8 -

3. Cupola melting 3.1 Functions of cupola

A cupola is intended to economically obtain molten metal ensuring castings with few defects, that is, (1) to produce hot and clean molten metal; (2) to produce molten metal with high fluidity; (3) to produce molten metal with proper chemical compositions (4) to ensure economical and constant operation and easiness of repair. To fulfil these functions, the following are necessary: (1) to design the cupola with proper structure; (2) to select and use proper charge materials; (3) to establish and manage proper operating conditions; (4) to control the inter-process quality properly.

3.2 Structure of cupola

Fig.3 shows the basic structure of a cupola and Table 1 - the standard dimensions of principal parts of conventional cupola. The function of a

cupola depends on the part lower than the charging door, which is divided into the preheating zone, the melting zone, the superheating zone, and the well from a functional point of view. Metal charged through the charging door is first heated in the preheating zone by combustion gas heat of coke, and then melted in the melting zone followed by being subjected to superheating and tapped from the tapping hole through the trough. In favorable operation, as shown in Fig.2, the furnace

temperature is said to be 500 to 1000C in the preheating zone, 1200 to 1500C in the melting zone, and 1600 to 1800C in the superheating zone; it is desirable that the tapping temperature be 1500 to 155OC. The melting zone and the superheating zone are classified into the deoxidation zone and the oxidation zone from the viewpoint of combustion reaction. In cupola melting,

- 9 -

the positions of these deoxidation zone and oxidation are important; they have a great influence on the properties of molten metal. When the oxidation

zone is expanded to the top of furnace or solid metal is put in a strong oxidizing atmosphere because of lowering of the metal melt-down position, oxidation of molten metal is accelerated, the melting loss of Si is increased, which may cause the abnormal of graphite form and defect such as shrinkage cavity, etc.

(1) Effective height

The height from the tuyere (lower tuyere in case of a multistage tuyere) to the lower end of the charging door is called "effective height", which is the most important part from a functional point of view. This

part, which is a preheating zone where metal and coke are preheated by heat of combustion gas blown up form below and moisture of coke is evaporated, needs enough height, while excessive height may increase blast resistance and cause crushing of coke at the time of charging; it is desirable that it be 3.5 to 6.0 times as large as the inside diameter of the cupola.

(2) Tuyeres

They are blastingports for combustion air; this is an important part affecting the combustion of coke. Uneven pressure or quantity of air

supplied from each tuyere will lead to uneven combustion and heat generation of coke at the tuyere, causing oxidation melting in lowtemperature parts, thus generally lowering the temperature of molten metal. There are many researches and patents related to equi-blast such The ratio of the

as the form of the tuyere, windbox, buffer plate, etc.

total cross section of tuyeres to the cross section of the furnace (tuyere ratio) is 5 to 9 for a small furnace and 10 to 15 for a large furnace.

- 1 0 -

This is because in the case of a large furnace it is necessary to increase wind speed so that wind will reach the inner part of the furnace. The

number of tuyeres shall be increased so that there are no dead points where combustion is insufficient; it shall be 6 in the case of a small furnace and be increasedwith an increase of the size of furnace; tuyeres shall be arranged horizontally on a plane at equal intervals, surrounding the furnace.

(3) Windbox

The windbox is intended to convert the kinetic pressure of air to static pressure to make equi-blasting from each tuyere into the furnace . The windbox shall be designed so that the velocity head of air passing through the air blast tube will be as small as possible to supply an equal quantity of air to each tuyere.

Molten iron

Fig.2 Combustion reaction and gas distribution in cupola

- 1 1 -

Fig.3 Structure of cupola and functional zones

- 1 2 -

Table 1 Standard dimensions of principal parts of cupola

section of wind box

(4) Blast volume and pressure

The blast volume and pressure are important to ensure proper operation of a cupola. In Table 2 are given some examples of relationship between The blast volume shall

capacity of a cupola, blast volume and pressure.

be large enough to supply sufficient oxygen to hold proper combustion andensure complete combustion of carbon content in coke except that picked up to iron. But too large blast volume will lower the furnace temperature, The

leading to oxidation melting, to which attention shall be paid. theoretical air quantity is 7.75 Nm /min per 1 kg of coke.
3

Shown in Fig.4 is the mesh diagram of the relationship between blast volume, carbon ratio, tapping temperature and melting speed. Most

effective blast volume is shown by the dotted curve plottedby connecting the highest points of tapping temperature for each carbon ratio. Fig.5

shows the relationshipbetween blast volume and oxidation loss of molten metal. As seen from the figure, oxidation proceeds rapidly when blast

volume exceeds certain value and oxidation loss increases more sharply according as coke ratio is lowered. Blast pressure shows resistance by charges in the furnace; pressure shall be changed by the height of the coke bed and particle size of coke, and operation trouble such as hanging and clogging of a tuyere with shall be watched slag by means of wind pressure.

- 1 4 -

Table 2 Example of cupola blower

melting speed (t/h) 2 3 5

Specifications of Blower Blast volume Motor output (kW) 22 30 45 (HP) 29.5 40.2 60.3

Wind pressure 3 3 2 (m /min) (m /min.m ) (mm H20) 40 141 1200 60 156 1400 80 126 1550

Fig.4

Relationship among blast volume, carbon ratio, melting speed, and tapping temperature

- 1 5 -

Inside diameter of cupola : 500mm Acid, water-cooled operation Particle size of coke
: 80 to

100mm

Fig.5 Oxidation loss, blast volume and coke ratio

3.3 Melting operation of cupola (1) Ignition

After repaired and dried cupola, firewood for igniting coke is put on the bottom and ignited. After ignition, bed coke is charged to a

specified height followed by burning it sufficiently by natural draft.

(2) Fore blowing

As soon as flames reach above the bed coke, the tuyere peep holes are closed and conduct fore blowing for 3 to 5 minutes is allowed, then the height of the bed coke shall be adjusted using a chain, a steel bar, etc. from the charging port. The proper height of the bed coke is 1.5

to 1.8 times as large as the furnace diameter for small furnace up to 700 mm in diameter, and 1200 to 1300 mm for larger furnace.

- 1 6 -

(3) Charging of materials

Metallic materials such as pig iron, scrap iron, steel scrap, ferro-alloys are mixed in accordance with the pre-determined table and charged into furnace. It is desirable that a batch of metal charge is Then a fixed

about l/10 of the quantity of molten metal tapped per hour.

amount of coke (charging coke) to compensate the loss of bed coke and lime stone of 3 to 4% of metal to increase the fluidity of slag generated during melting. Charging shall be done in order of coke, limestone then Too

metallic materials and shall be up to just below the charging port.

large chargedmaterials increase the speed of passage of combustion gas, lowering preheating effect. They may cause hanging sometime. On the

other hand, too small materials prevent ventilation in the furnace, causing incomplete combustion or lowering melting speed. It is

recommended that materials charged have the following dimensions. Coke l/5 to l/8 of the inside diameter of furnace Metal l/3 or less of the inside diameter of furnace and l/6 or less of the cross section of furnace Pig iron, scrap iron Steel scrap 15 kg or less/pc. Thickness 25 mm or less

(4) Start of blasting

After charged materials, hold them for 15 to 20 minutes to preheat them followed by starting air blast through the blast tube, windbox, and tuyeres with the use of the air blower to start melting. Materials on the bed coke are preheated by combustion gas, then melting starts. In 3 to 5 minutes molten metal can be seen through tuyere dropping in the bed coke. If it takes less than 2 minutes the bed coke is too low, and

- 1 7 -

if it takes more than 6 minutes the bed coke is too high. In 15 to 20 min after starting air blast the tapping hole shall be open. Molten metal is heated in the superheating zone and accumulated

in the well followed by being tapped through the tapping hole and trough. The temperature of the first molten metal is generally low and is apt to fluctuate in chemical compositions; it is recommended that initial tap shall not be used for qualitatively important products. To get the

high temperature molten metal form the beginning, it is necessary to increase slightly the height of the bed coke and to blast excessive air at initial stage, to add 2% of calciumcarbide to the first charging coke, or to perform air blasting with oxygen enriched.

(5) Tapping Since materials charged in the furnace begin to fall after air blasting is started, coke, metal, etc. shall be supplied continuously at constant intervals so that the furnace will always be filled with raw materials up to just under the charging door. The change in this height

will lead to a change in blast pressure, affecting the furnace condition, to which attention shall be paid. Even when operation is conducted with

a proper blast volume and proper coke ratio, the bed coke inevitably lowers due to errosion of the furnace wall in the melting zone after longtime operation. To compensate this, it is necessary to add about one charge

of coke every 1 to 1.5 hours after operation is started. When the cupola is working satisfactorily, 1) the color of a flame of combustiongas in the charging door is light purple or light pink. A yellowish-red flame shows an oxidizing atmosphere; 2) each tuyere is uniformly bright; 3) slag is of good fluidity, glossy, andglassy, light green or whitish,

-18-

and light; at the time of oxidaizing melting, the Fe0 content is increased in slag and its color becomes blackish, its specific gravity becomes higher, and it loses gloss;, 4) molten metal is hot (1530C or higher) and the break surface figure of molten metal does not appear for awhile after poured into ladle.

3.4 Foundry coke Foundry coke has two roles an energy source for melting and carbon pick up agent to iron. Attention shall be paid to the following items when

selecting foundry coke:

(1) Particle size

The size of coke is recommended to be 1/5 to 1/8 of the inside diameter of the cupola. The coke particle size has a great influence on ventilation

resistance and combustion in the furnace. When the particle size is small, the surface area becomes larger and the oxidation zone just above tuyeres becomes shorter and hotter, accelerating deoxidation reaction, lowering furnace temperature. thus

In addition, the position of the metal

melting zone is also lowered, causing lowering of melting temperature. On the other hand, when the particle size is large, the oxidation zone is expanded, making CO2 deoxidation reaction insufficient, thus

generating an atmosphere with a lot of CO2 in the upper part and causing oxidizing melting.

- 1 9 -

(a) Small-size

(b) Medium-size

Large-size

Fig.6 Effects of coke size to combustion in cupola

(2) Coke strength (Shatter index)

When coke strength is insufficient, coke can be damaged at the time of charging in the cupola or during transportation, leading to a lot of loss and uneven particle size, causing unstable melting. In Japan, JIS

standards specify that the shatter index should be 85 or more (85% or more of coke dropped from a height of 2 m four times remain after sifting with the use of a 50 mm sieve), and practically coke with a shatter index of 93% or more is supplied.

(3) Porosity

The volume of void spaces in coke is an important factor related to its combustibility and reactivity. High-porosity (low apparent specific

gravity) coke can increase melting speed, but lowers tapping temperature. Coke on the Japanese market has an apparent specific gravity of 1.15 to 1.30.

(4) Ash content

When the ash content of coke increases, the amount of fixed carbon decreases. Under the same operating conditions, low ash content coke

- 2 0 -

increases carbon pickup to molten metal, raising tapping temperature. Therefore, in case of small cold blast cupola operation, low ash content coke is often used, while a hot blast cupola, high ash content coke is used from an economical point of view, because blast temperature is high and influence of ash is reduced.

(5) Sulfur content

Sulfur in coke, when molten metal comes in contact with red-hot coke, the sulfur pickup to molten iron should occur and badly effect. content of foundry coke should be as low as possible. Sulfur

(6) Moisture

Moisture in coke is heated and evaporated in the preheating zone of cupola, so it is said to have little influence on molten metal. However,

the change of moisture content affects the weighing accuracy of charged coke, making proper melting difficult. Therefore, when storing coke,

attention shall be paid so that a roof will be provided to prevent penetration of rain, the floor will be inclined slightly to prevent formation of puddles, and good ventilation will be ensured for natural drying.

-21-

4.

Energy conservation of cupola 4.1 Heat efficiency of cupola

The energy conservation of cupola is evaluated by its heat efficiency. That is, Heat efficiency = (Heat content of molten metal/Total heat input) x 100. The heat efficiency is calculated by using the above formula after calculating heat balance by using heat input and heat output obtained for each item per ton of molten metal. and heat output. Table 3 shows main items of heat input

Heat balance is intended for examining heat output in detail

to take measures for reducing heat loss, but it is difficult to realize it only by the foundry from the viewpoint of measuring equipment and technology. The heat efficiency alone can be calculated from the four factors of heat input and sensible heat carried away by molten metal.

Table 3 Factors of heat balance of cupola

- 2 2 -

4.2 Calculation of heat input (1) Combustion heat of coke

To obtain correct combustion heat of coke is difficult, because inter-reaction of fixed carbon, volatile materials, sulfur, moisture, etc. in coke is complex, and a lower heating value, heat of condensation of water vapor reduced from higher heating value, is used as combustion heat of coke. Lower heating value (H1) = Hh - 6 x (9 x h + w) (kcal/kg), Higher heating value (Hh) = 81x C + 340 x (h-O/8) + 25 x S (kcal/kg), where h: Actual hydrogen content in coke (%) w: Actual whole moisture at usage in coke (%) C: Fixed carbon of coke (%) 0: Oxygen of coke (%) S: Sulfur of coke (%). Since in a cupola, coke is consumed not only for combustion, but also carbon pickup, the amount of coke practically burned is obtained by subtracting the amount of coke consumed for picking up from the total amount of coke used. The amount (W) of coke burned per lt of molten metal is: W = (W1 - W2)/T, where W1: Total amount of coke used (kg) W2: Amount of coke consumed for carbon pickup (kg) T : Total amount of molten metal (t) The heating value (Q1) of coke per lt of molten metal is:

- 2 3 -

(2) Sensible heat in air blast

The sensible heat (Q2) in air blast per ton of molten metal is:

where Lo:
G air :

Quantity of air blasted per ton of molten metal (Nm ) Mean specific heat of air (kcal/Nm C) ... Usually 0.321 kcal/Nm C
3 3

Tair: T r:

Air blasting temperature (C) Ordinary temperature (C)

(3) Oxidation heat of metal

In cupola melting, the oxidation heating values of Fe, Si, and Mn are calculated. Fe + (1/2)02 = Fe0 + 898 kcal/kg Si + O2 = Si02 + 7406 kcal/kg Mn + (1/2)02 = MnO + 1760 kcal/kg The heating value (kcal/t) by oxidation of these elements is

molten metal as follows:

(4) Combustion heat value of auxiliary fuel

Heavy oil, gas, carbide, etc. are as used sometimes as auxiliary fuel of cupola. The combustion heat of auxiliary fuel (Qsup) per ton molten metal is calculated from the weight (Wsup) kg of auxiliary fuel used per It molten metal, the amount of gas (Lsup) Nm , the heating value of each of them (Hsup) kcal/kg or kcal/Nm as follows:
3 3

- 2 4 -

4.3 Calculation of heat output (1) Heat content carried away by molten metal

The heat content of moltenmetal is calculatedbased on the material and temperature. The heat capacity of each element in Table 4 is

calculated from the temperature followed by integrating them according to their percentage in the material.

Table 4 Heat capacity per ton of each element

Heat capacity (kcal/t x 10 ) Metal 1500C per 100C element 1400C C 533.2 580.5 47.3 Si Mn Ni S Fe 725.8 313.0 258.0 222.7 298.4 751.6 332.0 274.3 239.9 315.6 25.8 19.0 16.3 17.2 17.2

(Example) Gray cast iron C 3.3% 1.9% Si Mn 0.6% S 0.07% 94.2% Fe The heat capacity (Q) of molten metal per ton with a temperature of 1550C can be calculated in the following way: Q = (580.5 + 47.3 x 50 / 100) x 0.033 + (751.6 + 25.8 x 50 / 100) x 0.019 + (332.0 + 19.0 x 50 / 100) x 0.006 + (239.9 + 17.2 x 50 / 100) x 0.0007 + (315.6 + 17.2 x 50 / 100) x 0.942 = 342.1 (kcal/t x 10)

From the description above, expressed as follows:

the heat efficiency of a cupola is

Heat efficiency = (Heat content carried away by molten metal/Total heat input) x 100

4.4 Heat balance diagrams and heat efficiency of a cupola

Fig.7 shows examples of heat balance of cold blast operation and 300C and 600C hot blast operation of a cupola with an inside diameter of 650 mm. The heat efficiencies are 32.4%, 51.8%, and 60.0%, respectively.

- 2 5 -

Heat used for melting

32.4%:

Heating furnace

Fig.7 Heat balance diagrams of cold and hot blast operations of cupola

- 2 6 -

5.

Improving the heat efficiency of a cupola 5.1 Hot blast cupola 5.1.1 The purpose of hot blasting

The temperature of exhaust gas of a cupola is as high as 800C, making it possible to preheat blast air up to as high as 400C by heat exchange. Inaddition, both the sensible and latent heat of exhaust gas can be recycled for preheating blast air by combustion of CO gas included in exhaust gas. When blast air is preheated to 300C or higher, the sensible heat of blast air is added to heat input, activating combustion of coke, leading to the rise in combustion temperature (Fig.8}, thus improving heat

efficiency and economy owing to the reduction in the coke ratio andincrease in melting speed. Moreover, in the upper part of the combustion zone, CO2

gas due to coke is deoxidized by high temperature, realizing a highly reductive atmosphere, thus decreasing the oxidation loss of metal. In cold blast operation, combustion is hindered around tuyeres by cold air, while in hot blast operation, the maximum temperature zone comes down just above tuyeres (Fig.9).

Hot air temperature ["Cl Gas temperature ["Cl

Fig.8 Hot air temperature and coke flame temperature

Fig.9

Furnace temperature distribution in cold blast and hot blast operation

- 2 7 -

Hot blast i) reduces the coke ratio, improving the heat efficiency (See Fig.7); ii) raises tapping temperature, improving the quality of molten metal; iii) iv) increases melting speed, increasing melting capacity; increases the percentage of steel scrap in chargemetals due to the increase in carbon pickup and CE value, improving quality of the material and reducing the material cost; v) ensures little loss of Si and Mn in molten metal in a reductive atmosphere, saving ferro-alloys' cost. vi) reduces sulfur pick up to iron, improving the quality of material; vii) lowers the temperature of exhaust gas, reducing the

equipment and power cost due to miniaturization of a dust collector.

5.1.2 Hot blast equipment

(1) Furnace wall heat recovery type: Blast air is preheated by the sensible heat of exhaust gas by double wall of the furnace or using a sleeve. This is often used in a small cupola even today. (2) Stack gas heat exchange type: Preheating blast air is performed by using the sensible heat of exhaust gas of the stack. (3) Utilization of the latent and sensible heat of exhaust gas: Exhaust gas is sucked just below the material charging port to utilize both the latent and sensible heat of exhaust gas. Exhaust gas is taken

out of several suction ports, led into the combustion chamber followed by mixing with air and ignited. Then the burnt gas is controlled to Stable hot

a set temperature of about 1000C, led to heat exchanger.

- 2 8 -

air with a temperature of 400 to 600C can be obtained with 10% or more of CO gas content in stack gas.

5.2 Oxygen enriching cupola 5.2.1 The purpose of oxygen enrichment

Oxygen necessary for combustion of coke is no more than 21% of air; nitrogen occupying 79% of air absorbs heat in the furnace and carries away a lot of heat as stack gas. Oxygen enrichment is intended to increase the concentration of oxygen during air blasting to raise tapping temperature easily at the beginning of operation or at any melting condition and to increase melting speed. Table 5 shows some example of oxygen enrichment. The following are advantages of oxygen enrichment: i) ii) Raise tapping temperature, improving the quality. Increase melting speed and melting capacity.

iii) Decrease blast volume and save power. iv) Reduce coke ratio and improve heat efficiency. v) Increase steel scrap in charge and improve the quality of material and reduce the material cost. vi) Improve the yield of Si and Mn, and reduce fello-alloys. vii) Reduce S pickup to iron, andensure easy treatment of molten metal such as inoculation.
02 during air blasting (%)

Fig.10 Amount of oxygen and tapping temperature

-29-

Table 5 Effects of oxygen enrichment

Inside diameter of cupola inch (mm) 40 36 46 48 32 (1,014) ( 912)

Oxygen enrichment Melting speed (t/h) method (amount of added, %) Enrichment Enrichment Enrichment Injection Enrichment oxygen Before (2.5%) (3.0%) (4.0%) (3.0%) (2.0%) 6 4 10 7 2.5 After 8 5 12 7 2.5

Coke ratio (%) Before 14 15 12.5 12.5 17 After 12 10 9.4 9.4 14

( 811)

5.2.2 Oxygen enriching equipment

Though a method using an oxygen enrichment membrane has also been developed recently, generally pure oxygen produced by evaporating liquid oxygen is added through inserting duct in the air blast tube. Oxygen is

diluted with blast air and enriched uniformly to 22 to 25% blasted through tuyeres. The lattermethod is common and easy adjustable, it is used both In addition, there is also injection

continuously or intermittently.

procedure blowing oxygen into the furnace through ducts installed in tuyeres.

5.2.3 High-efficiency cupola with high-rate oxygen enrichment

The amount of oxygen enrichment is generally up to 4%, and it is said that enrichment exceeding this value can cause oxidation of molten metal. However, high rate oxygen enrichment can increase the heat efficiency of a cupola up to 35 to 40%, which has beendifficult for a small cupola, making it possible to produce a cupola ensuring high-quality molten metal by high-temperature tapping and capable of varying the melting speed in the range 60 to 200% of a rated value. This cupola ensuring both energy

conservation and flexible operation was commended as excellent energy saving equipment by Japan Machinery Federation. This cupola can be

- 3 0 -

produced both newly and by modifying an existing one.

5.3 Humidity control cupola 5.3.1 The purpose of humidity control of blast air

High moisture content of the blast air in cupola melting comes in contact with coke, causing the following reaction. H20 + C = CO + H2 - 123 kJ/mol 2H20 + C = CO2 + 2H2 - 81.1 kJ/mol The upper reactionprogresses at a temperature of 1000C or higher and the lower reaction - at a temperature below 1000C. Both of them are The The

endothermic, and the temperature adjacent to the tuyere fall down. condition of combustion and heating in the furnace becomes worse.

experiment has shown that tapping temperature sharply lowers at an absolute

reduces. Furthermore, moisture in blast air increases oxidizing metal in the furnace, causing adverse influence such as lowering of carbon pickup, and yield of silicon, etc. To cope with cupola operation in a high humidity

period, the height of the bed coke is generally increased or the coke ratio is increased in amounts of 1.5 to 2.0%. the viewpoint of energy conservation. By controlling humidity: i) reduction in conservation; ii) easy quality control for molten metal by keeping stable air low humidity in blast all the year round, reducing defective ratio of castings; iii) reduction in the material cost due to increase in the percentage of steel scrap in charge; the amount of coke used, ensuring energy But this is not desirable from

-31-

iv)

rise in the temperature of the first tap molten metal and increase in tapping temperature, etc.

But in Japan with a remarkable fluctuation of humidity in a year, the absolute humidity in the dry season is 4 to 6 g/m , while in the wet season
3 it is 18 to 24 g/m , that is, the difference between them is no less than 3 3 3

20 g/m .

In a cupola (about 3t/h) operation with blast volume of 60m /min, Though

water in blast air changes at a rate of as high as 1.2 litre/min.

the improvement of the heat efficiency is an effective achievement, stable quality is the greatest energy conservation effect of humidity control operation.

5.3.2

Dehumidification

equipments

i)

Dehumidification with equipment hygroscopic materials This type equipment is using as moisture adsorbents silica gel, activated alumina, calcium chloride or lithium chloride. Equipment is necessary for drying by heating and reclaiming absorbent materials when lost their power in longtime use.

ii)

Refrigeration This type equipment removes excess moisture by cooling air under a

dew point to condense. to the cupola.

Cooled air is heated by a reheater and supplied

The refrigerator type has become popular today by the refrigerator and measuring and

improvement of the capacity of a

controlling technology to keep humidity constant.

5.3.3 Effects of humidity control

Inhumidity control operation of cupola, tapping temperature rises and the coke ratio is reduced. Fig.11 shows a refrigerator type dehumidifier

capable of keeping the absolute humidity at about 6.5g/m all the year round. Fig.12 shows how the coke ratio was reduced by this operation.

-32-

Calendar months

Fig.12 Reduction of coke ratio by humidity control dehumidification

5.4 Multi-stage air blasting cupola 5.4.1 Purposes of multi-stage air blasting cupola

There are two points of view as shown below: Secondary air blast is provided above the main tuyere to burn CO gas coming up in the deoxidation zone and to use the combustion heat for; (1) metal preheating in the preheating zone is enhanced; or (2) themelting zone is expanded, the melting position is raised a little, the falling distance of molten drops is increased, and furnace temperature is raised to increase melting and superheating effect. Nowadays upper tuyeres are often provided in the coke bed for the latter purpose.

- 3 3 -

5.4.2 Multi-stage air blasting type

In a multi-stage blasting cupola the position of the upper tuyere and ratio of blast volume of the upper and lower tuyeres are to be determined according to the purposes. (1) When preheating solid metal, upper tuyeres shall be provided in places at a distance of 2 to 3 times the furnace diameter from lower ones, and the blast volume of them may be 15% of the total volume, when the amount of CO gas in flowing gas in the preheating zone is estimated to be 13 to 15%. (2) When expanding the melting zone and ensure sufficient superheating of molten drops, upper tuyeres shall also be provided in the coke bed; they shall be at a height of l.0 to 1.2 times the furnace diameter from level of lower tuyeres. The blast volume through upper tuyeres

is considered adequate to be equal as lower ones.

5.4.3 Effects of multi-stage blasting

Fig.13 shows heat balances for a large hot blast water cooled no lining cupola with the inside diameter 2300 mm where the upper tuyeres are provided whose total area is half of the main tuyere and at a height of 750 mm above the lower tuyeres. It is reported that the percentage of steel scrap in

charge and the yield of C, Si are increased, while the heat efficiency is improved only by 1.4% though. Fig.14 is a diagram illustrating the effect of multi-stage blasting cupola by British castings association. The reduction in the coke ratio

and the increase in melting speed to obtain the same tapping temperature are compared for ordinary operation and dual stage blasting. This figure

shows remarkable energy conservation and improvement of productivity.

-34-

Ordinary blasting Fig.13

Dual blasting

Comparison of heat balance for ordinary and dual blasting

Inside diameter of cupola:760mm Total amount of air blasted:43m3/min Blast volume ratio of dual tuyeres: 1:l Fig.14 Change in coke consumption and melting speed for dual blasting operation

-35-

5.5 Water cool cupola

As increasing in the size of cupola, the number of no-lining hot blast water cool cupolas having only a outer casing made of steel plate without lining in the melting and superheating zones and water shower cooling and preheating hot blast combined has been increasing, which ensures longtime continuous operation. i) Longtime continuous operation reduces the percentage of heat loss necessary for one operation in fixed amounts, improving the heat efficiency. ii) There is no change in the furnace inside diameter due to erosion of refractories in the melting zone, stabilizing the condition of the furnace. iii) There are no restrictions on kind of refractories, ensuring normal operation for a longtime. iv) Refining of molten metal is possible by arbitrary change fromacidic to basic operation. v) It is possible to reduce the refractory cost, improve productivity, and realize energy saving.

In the case of a small cupola, since too great a cooling effect adversely affects the condition of furnace and properties of molten metal, it is impossible The same effect as a large cupola can be expected by using highquality refractory (SiC family) inmelting zone with jacket or water shower cooling, by water cooled tuyeres projected into furnace which enable the combustion proceed at the center of furnace, and by banking operation for intermittent melting operation.

-36-

5.5.2

Examples of improvement of heat efficiency due to longtime continuous operation (Energy conservation case report, 1991 edition)

(1) Reasons for taking measures

At this plant melting was performed in a low-frequency induction furnace, but the galvanized zinc steel plates for automobiles is increased in steel scraps, which cause worse working environment and Zn content exceeds the allowable limit of 0.06% in molten metal 0.06% for induction furnace, increasing the amount of expensive pig iron and the cost of charge. To cope with this situation, a cupola was introduced to improve the heat efficiency. Fig.15 shows the state of energy use before taking measures.

(2) Measures taken (a) Tapping hole (patent pending)

The life of refractories of a cupola depends on the abrasion of the tapping hole. A method of replacing this from outside the furnace achieving longtime continuous

in hot condition was established,

operation for 20 weeks; until then bottom drop down had been performed after 4 day operation for repair. improved by 1.5%. The energy efficiency has been

- 3 7 -

Conventional cupola Melting energy Cokes

Low frequency induction furnace Electric power

Heat balance

Heat efficiency Consumption rate in crude Remarks Oil-equivalent CO2 generating quantity
Fig.15

33% 0.09 kl/t 106c kg/t

66% 0.15 kl/t 103c kg/t

Comparison between conventional cupola and low-frequency induction furnace

(b) Improvement of heat exchanger, others

The hot blast temperature is raised from 450C to 600C by improving the material and construction of the exhaust gas heat exchanger. The

heat efficiency has been improved by 3%. Air blast dehumidification was also performed and warm water was utilized for heating.

(3) Effects of measures Table 6 Summarized results of measures taken

Low-frequency furnace Melting efficiency (%) CO2 discharge (Ckg/t) 66 103

( ): heat efficiency Cupola after Conventional taking measures cupola 38 (33) 106 46 (39) 85

- 3 8 -

Fig.16 Heat balance of cupola after taking measures

5.6 Improvement of heat efficiency by synergetic effect of air blast conditions 5.6.1 Background of experiment

Cupola operating techniques have been developed one after another and it is difficult to correctly judge the synergetic effect of combinations of these techniques. In this operation experiment the effect of

combinations of a cupola with air blast conditions was checked. In particular, there is few operation experiments for a small cupola. These

will be a guideline of energy conservation and improve properties of molten metal of cupola for medium and small foundry.

5.6.2 The contents of experiments

Experiments were performedby using a 2T/H cupola under the following five conditions: (1) (2) (3) Cold blast + Non-dehumidification Cold blast + Dehumidification Hot blast + Dehumidification

(4) Oxygen enrichment + Dehumidification (5) Hot blast + Oxygen enrichment + Dehumidification

- 3 9 -

Air blasting conditions are: Humidity conditions Hot air temperature Oxygen enrichment
: 350C : +4% (25%)

5.6.3 Experiment results

It was possible for a small cupola to remarkably improve the heat efficiency by reducing the coke ratio and improving the melting speed through humidity control, oxygen enrichment and hot blast or combinations of them. In addition, advantages of increasing carbon pickup in molten

metal were also confirmed such as reduction in the percentage of pig iron in charge, improvement in the yield of material melted, rise in tapping temperature, etc.

- 4 0 -

Fig.17 Results of operation of high-efficiency small cupola

5.7 Examples of improvement in properties of molten metal by measurement control of a cupola 5.7.1 Background of taking measures

Molten metal of malleable cast iron is made by means of dual melting a 15 T/H hot blast cupola and a low-frequency induction furnace. A cupola

has an advantage of low melting cost, but has a lot of factors affecting themelting condition, and its operationrequires great skill. Themelting

- 4 1 -

condition was measured to ensure stable properties of molten metal and energy conservation.

5.7.2 Measures taken (1) Leveling of the height of charging material

Uneven height of charging material causes uneven blast air resistance, that is, it prevents equi-blasting, adversely affecting properties of molten metal. Attention was paid to the correlation between the ambient

temperature of the preheating zone of a cupola and the difference in height of charging material. Temperature was measured in 6 places around the

preheating zone as shown in Fig.18 to minimize the difference in height of charging material. At the time of starting of measurement, the difference in ambient temperature was no less than 250C and the difference in height of charging material was 400 mm. To cope with this situation, charging equipment

and were improved as shown in Fig.19.

- 4 2 -

Fig.18

Temperature

measurement

Fig.19 Effects of improvement

of

position and method

material charging apparatus

(2) Estimation and management of bed coke height

In cupola melting,

the positions of the oxidation zone and the The height of bed coke is a factor to

deoxidation zone are important. manage them.

However, it is difficult to directly measure the height

ofbedcoke and the following two indirect factors are used for estimation of the height. i) Estimation by continuous measurement of Si loss As a result of high-temperature melting, deoxidation of Si 2O progresses, improving the yield of Si. The height of bed coke is

estimated by calculating and displaying Si loss from charge Si and analysis of Si in molten iron, after correcting time lag. ii) Estimation based on vertical temperature measurement in the preheating zone Temperatures measured in 6 places arranged vertically in the preheating zone changed in good accordance with the change of the furnace

- 4 3 -

condition, which was effective in estimating the height of bed coke. It is possible to grasp the change of the furnace condition earlier than the melting operator judges it by tapping temperature, ensuring stable operation.

Fig.20 Time series change of vertical temperature in the preheating zone

5.7.3 Effects of measures taken

(1) The fluctuation of tapping temperature has become smaller and tapping temperature increased by 5C on average, remarkably reducing the power consumption rate of a low-frequency induction furnace. (2) The fluctuation of molten metal chemical compositions has become smaller and the amount of residual oxides such as Si20, MnO, etc. in molten metal has become smaller, reducing casting defects as shown in Fig.21.

- 4 4 -

Fig.21 Reduction of casting defects by improvement of properties of molten metal

- 4 5 -

6.

Natural gas cupola 6.1 The structure of a natural gas cupola

An example of a cokeless cupola which uses natural gas as an alternative fuel of coke is introduced. This is a shaft furnace having a cylindrical

steel plate lined with refractory same as a coke cupola. It has no tuyeres, but instead has a grate of water cooled pipes in the middle stage and natural gas burners under it. using natural gas. Fig.22 shows a schematic structure of a shaft furnace

(1) Melting capacity: 6t/hr;

Furnace inside diameter: 1000 mm

(2) Preheating zone

The furnace has an effective height ratio of 4.8; which has enough capacity for store and preheat charging material sufficient for about one hour melting, considering effective use of heat.

(3) Heat regenerative material bed and water cooled grate

The bed consists of ceramic balls with a diameter of about 150 mm laid in 2 to 3 layers. Theseballs are made of refractorymaterials having high-temperature strength capable of standing the melting loss against slag at high temperatures and the impact and weight of falling of charging material. A water cooled grate of steel pipe welded construction is used to support the weight of this bed and melting material and the impact load of falling of charged material.

(4) Combustion zone

Three natural gas burners with each capacity of 1.5 million kcal are installed at intervals of 120 to achieve a melting efficiency of 55%.

- 4 6 -

To ensure a balanced amount and pressure of combustion air supplied to each burner, a windbox having a sufficient sectional area is provided. Oxygen enrichment is also possible. Furnace temperature in the

combustion zone reaches 1600 to 1650C; combustion gas heats ceramic balls, melting and superheating raw materials. Water cooling is performed by Fig.23 shows an

shower to cool refractories of the furnace wall. operation scheme.

(5) Well

The well located under the combustion chamber has a tapping hole diameter of as large as 150 to 150 mm to prevent the tapping hole from being clogged with ceramic balls worn and dropped through the grate.

(6) Low-frequency induction furnace

With operation cost taken into account, molten metal tapped at low temperature of 1350C is subject to adjust carbon and other element content and to superheat in a low-frequency induction furnaces. There are two

low-frequency induction furnaces provided, each of which has a capacity of 3000 kg and an input of 600 kW-1000V. Their temperature raising

capacity from 1350C to 1500C is 8.5 t/h (71 kWh/t).

- 4 7 -

Water

cooled

grate

Gas

burner

Fig.22 Structure of natural gas cupola

- 4 8 -

Raw

material

Fig.23 Operation scheme of natural gas cupola

6.2 Comparison of melting energy

Table 7 shows a heat balance of a natural gas cupola in a steady state. In the case of this furnace, preheating is performed before melting in a steady state; the longer the continuous melting time in relation to the preheatingtime, the higher the heat efficiency. When preheating and melting

are performed for 72 minutes and 9 hours, respectively, the heat efficiency will be 51 to 52%.

Table 7 Heat balance table of natural gas cupola (%)

Potential heat Potential heat Potential heat Potential Gas combustion of molten metal of exhaust gas of cooling water heat of slag 56.3 15.0 14.8 4.9 100

Others 9.0

Tables 8 and 9 show heat balances including electric power of lowfrequency induction furnace for superheating and adjustment and electric power used for motive power of cupola. Standard examples of a coke cupola

- 4 9 -

and a low-frequency electric induction furnace are shown for reference.

From

the viewpoint of energy consumption, the natural gas cupola is the most earth-friendly of these three melting methods.

Table 8 Energy used in each melting furnace and their heat efficiency (Electric power: directly input)
Gas cupola Coke cupola Electric induction furnace Energy consumption /ton 0 0 650 6 Energy (kcal/ton) 0 0 559,000 5,160 564,160 68

Kind of energy

Unit

Heating value (kcal) 9,950 7,200 860 860 860

Energy Energy Energy Energy consumption (kcal/ton) consumption (kcal/ton) /ton /ton 60 0 80 5 6 597,000 0 68,800 4,300 5,160 675,260 I 57 0 155 0 10 20 0 1,116,OOO 0 8,600 17,200 1,141,800 33

Natural gas Coke Electric power Blower Dust collector

Nm3 kg kWh kWh kWh Total

Heat efficiency %

Table 9 Energy used in each melting furnace and their heat efficiency (Electric power: indirectly input)

6.3 Comparison of exhaust gas in melting

Exhaust gas of a conventional coke cupola and a natural gas cupola can be calculated from their fuel compositions and consumption.

- 5 0 -

From table 8, the consumption of natural gas in a natural gas cupola is 60m N/ton, and the consumption of coke per 1 ton of molten metal in a coke cupola is about 150 kg/ton, and the amount of carbon dioxide generated are 1.17 x 60 = 70.2m N/ton for a natural gas cupola and 1.61 x 150 = 241.5m N/ton for a coke cupola; the amount of carbon dioxide generated in a natural gas cupola is no more than 29% of that generated in a coke cupola.
6.4 Advantages of a natural gas cupola (1) Energy conservation
3 3 3

The heat efficiency of a natural gas cupola is higher than that of a coke cupola. It is somewhat lower than that of an electric induction

furnace with electric power charged directly, but it is higher than that of other melting furnaces with energy charged indirectly.

(2) Improvement of environment

The amount of carbon dioxide in discharge gas of a natural gas cupola is l/3 or less that of a coke cupola, greatly contributing to prevention of global warming. Sulphur oxides are not found in exhaust gas, ensuring

cleanness, which is incomparable with several tens of ppm of a coke cupola.

-51-

(3) Recycling automobile scraps Though in melting in an induction furnace, there are problems of worsening of working environment duringmelting, lowering of the quality of castings, shortening of life of refractories, etc. due to Zn galvanized steel plates of automobile scraps which are expected to increase in the future, the refining effect of a cupola makes it possible to recycle them. Harmful elements such as Pb, Sn, Al, etc. can be collected as oxides with a dust collector in the cupola.

-52-

7.

Induction melting furnace 7.1 Features of induction melting furnace

In metallic material placed in magnetic field generated by the current in induction coil of the furnace, electromotive force is induced by the action of electromagnetic induction, and induced current flows to heat up the material by its Joule's heat. Compared to other types of melting furnace,

induction furnace has the following features: (1) Its heat efficiency is high because the material is directly heated by electromagnetic induction. (2) No carbon dioxide is produced and little smoke and soot are emitted because cokes are not used as fuel. (3) Metal loss by oxidation is little, thus little contamination of in metal because of heating without air. (4) Temperature control is simple, uniform composition of metal product is attained by agitation effect and alloyed cast iron is easily produced. (5) Induction melting is suitable for high temperature melting because of its energy concentration, and installing space is reduced as compared with other types of melting furnace.

Induction furnace is classified into the following types according to its structure and frequency applied:

7.2 Heat balance of induction furnace 7.2.1 Total efficiency of induction furnace

Efficiency of induction furnace is expressed as a total, deducting

- 5 3 -

electrical and heat transfer losses.

Heat balance diagram of crucible type

induction furnace is shown in Fig.24. Electrical losses consist in transformer, condenser, wiring, cable, coil, etc. frequency converter,

Loss in coil is essential factor,

on which the furnace capacity depends.

Heat losses in induction furnace consist of conduction loss of heat escaping from furnace wall to coil side, radiation loss of heat released from melt surface, absorption loss in ring hood, slag melting loss, etc. Shown in Table 11 is an example of heat balance table of low-frequency and high-frequency induction furnaces. Heat efficiency of high-frequency furnace (60- 78%) is slightly larger Low-frequency furnace is

than that of low-frequency furnace (58 - 71%).

larger in heat loss, while high-frequency furnace is larger in electrical loss.

This is explicable from the fact that low-frequency furnace has lower power density at melting and larger heat loss due to long melting time, while high-frequency furnace has higher power density, heat loss is small due to short melting time and primary electrical loss is large due to

-54-

frequency conversion.

Table 12 Heat balance of induction furnaces at continuous operation Type of furnace Low-frequency furnace Channel type Rating Current density Heat efficiency Heat loss Electrical loss Wiring loss Secondary power loss Primary power loss Melting power rate Heating power rate High-frequency furnace Crucible type 300 1 50 0.3 58.1 7.5 28.2 3.3 1.3 1.6 655 41 1600 8 50 0.2 71.0 5.7 18.0 2.0 1.0 1.5 534 34 300 0.5 500 0.6 60.4 4.5 25.2 3.2 2.2 4.5 628 40 1600 2 500 0.8 73.2 2.1 15.4 2.7 2.1 4.5 520 33 300 0.1 3000 3.0 61.0 2.2 21.1 2.8 2.8 7.1 622 38 1600 0.5 3000 3.2 66.4 1.3 18.5 2.6 2.9 8.3 572 36

[kWl [tl [Hz1 [kW/kgl [%] [%] [%] [%]

300 5 50 0.06 67.2 23.6 3.0 3.3 1.3 1.6 36

1600 30 50 0.05 79.0 13.0 2.8 2.8 0.9 1.5 30

[%]
[kWh/t] [kWh/t]

Remark: Melting power rate is given up to 1500C and heating power rate is shown by 100C.

about 1 to 3 tons exceeds 700 kWh/t.

Dotted line with "X" marks in the figure

shows the power consumption rate at standard rating of the furnace with remaining 1/2 melt in the furnace, which is calculated about kWh/t lower than actual consumption. This rated value doesn't include the electric

energy required for holding molten metal, slag removing, tapping and other related operations. This difference in theoretical and practical values

indicate possibility for decreasing the power consumption rate.

7.3 Energy saving measures for induction furnaces 7.3.1 Improved heat efficiency by improvement of furnace

Energy efficiency at power source side, such as frequency convertion efficiency, power-factor improving capacitor, etc., includingproper coil design, can not be adjusted by user's side. On introducing the induction

furnace, specific features of the furnace must be understood fully to make proper decision about kind of material, size and shape of charging materials to be melted, melting amount, connection with pouring line and layout of the melting shop.

(1) Equipment layout

Induction furnace equipment should be melted with minimum distance between each equipment to reduce wiring losses. To reduce the wiring losses remarkably, it is essential to shorten the distance between furnace body and power-factor improving capacitor as very large current flows between them.

(2)

Frequency

(a) Skin effect: Induction current flows concentratedly in the surface of material to be melted. This concentration of current becomes more

remarkable as the frequency becomes higher, resulting in better heating efficiency.

- 5 6 -

Diameter or thickness of material to be melted in the furnace may be decreased according as the frequency becomes higher. When cast iron is melted in high-frequency induction furnace, there is

practically no limitation in its size, but in low-frequency furnace when starting with cold metal, melting has to be started only by the use of starting block. residual molten metal. (b) Effect of agitation: As molten metal is excited by current opposite to current flowing in induction coil, molten metal is agitated to raise its surface in the center. Surface of molten metal is risen Continuous melting is to be performed with

higher as frequency becomes lower, i.e. agitation of molten metal occurs stronger in low-frequency furnace than in high-frequency furnace. This effect of agitation makes it possible to ensure uniform

temperature of molten metal and its uniform quality as well as to promote entrapment of material charged and fusion of chemical composition adjusting agents, specially carbon addition. On the

other hand, excessive agitationmay cause such troubles as oxidative wearing of molten metal and fusing out of refractories or danger of spattering of molten metal. In this respect, as compared with

low-frequency furnace, high-frequency furnace can be charged with larger electric power at the same agitation degree, which will speed up the melting and improve the furnace heat efficiency because high-frequency furnace can be operated with power density about three
times larger than that of low-frequency furnace.

7.3.2 Improvement of heat efficiency in operation (1) Improvement of heat a) efficiency

Tapping temperature should be as low as possible.

Heat capacity of molten metal increases with increasing the tapping

- 5 7 -

temperature, and furnace heat loss is fully proportional to melting temperature. Heat capacity of gray iron increases about 20 kWh/t as Heat conduction loss (Qc) andradiation

its temperature rises per 100C.

loss (QR) are calculated as follows:

Qc : Conduction loss (kW) t: Cooling water temperature (K) T: Molten metal temperature (K) R: Heat resistance of furnace wall (kW/K)

QR : Radiation loss (kW) Emissivity A: Surface area of molten metal (m )

From the abovementioned equations it follows that conduction loss and radiation loss of high-frequency furnace with lt, 500 Hz and 900 kW at tapping temperature of 1500C come to 50 kW and 35 kW respectively, and these losses can be reduced approximately by 10 kW each at tapping temperature of 1400C. To keep the tapping temperature lower, it is necessary to take carefully thought out measures in practice, for example inoculation, laddle traveling distance, preheating and covering of laddle, etc.
b) Furnace cover should be closed as far as possible.

As calculated by the abovementioned equation (2), heat radiation loss from molten metal surface is proportioned to the forth power of temperature. This heat loss at temperature about 1500C comes to 60

-58-

- 70 kW/m, which is maximum loss in melting.

In practice of furnace

operation, especially in case of small-sized furnace, furnace cover sometimes remains open carelessly. It is important to train personnel

and make necessary preparation so as to charge materials and adjusting agents regulator as quick as possible. As the effect of furnace cover against radiation loss reduced by half, if even a small opening exists in covering, any erosion of

refractory by expansion or dropping at the top of crucible and/or furnace cover have to be repaired deligently.
c) Molten metal should be held at low temperature and in short time.

Molten metal should be held, when required, at low temperature, or turn off power supply. again. Rated power should be turned on to heat up

Chemical analysis of molten, preliminary furnace test and Preparatory

temperature measurement should be performed quickly.

operations should certainly be performed so that there is no unmatching with mold assembly or waiting for crane.
d) Dust collecting hood

Dust collecting degree and time should be controlled according to furnace running conditions.
e) Cleaning of sand, rust and other dirts

react with furnace refractory to form slags.

If slags are formed about

1% in melting of 3 tons iron, power loss at 1500C is about 10 kWh/t.

(2) Maximum power supply

It is proper to increase power input for improvement of heat efficiency of the furnace. Maximum capacity of the furnace can be

attained and power consumption rate can be reduced when operating the furnace with constant rated power.

-59-

a)

Raw material at the start of melting

Raw material should be charged as dense as possible.

It is better

to charge return scrap having low melting point for quick melting to improve power load factor.
b) Additional material charging

Additional cold material should be successively charged into the furnace when the first charge starts melting. Each charge should be about 10% of crucible volume so as to close the furnace cover.
c) Machining chips

Machining chips or other fine materials having a small bulk specific gravity cannot be heated effectively. They must be charged into molten

metal built up previously in the furnace, making use of agitation effect of molten metal. As machining chips may be stuck on furnace wall by

electromagnetic force, power supply should be turned off at intervals for falling down of the chips.
d) Melting with residual molten metal

In case of low-frequency furnace, melting with residual molten metal is indispensable to improve the power load factor of low-frequency furnace. Fig.26 shows the relationship between the percent molten As maybe seen from the

metal volume and furnace load characteristics.

figure, rated power is loaded for not less than 50% of residual molten metal. Residual molten metal isn't specially required for high-

frequency furnace, but residual molten metal about 5 - 10% may improve the power load factor and increase the melting capacity as against the case when melting from completely cold material.

-60-

Fig.26 Load characteristics of lowfrequency furnace.

Fig.27 Furnace characteristics versus refractory thickness.

e)

Keeping up the furnace inner diameter

Rated power is supplied to the furnace only when thickness of furnace refractory remains normal. Fig.27 shows the furnace characteristics Furnace power may be lowered when its

versus refractory thickness.

inner diameter changes due to erosion of furnace wall or slag attached to the wall. Furnace wall damaged by erosion should be repaired to

maintain the standard diameter in respect to thermal efficiency of the furnace. Before charging the material it is necessary to remove sand,

rust and other foreign matters causing slag formation.

7.3.3 Preheating of material

Quantity of heat required for cast iron melting process up to its melting point (about 1150C) accounts for 65% of the total heat consumed for heating cold material of room temperature (20C) to tapping temperature (1500C). Induction furnace consumes 87% of the total power consumption required for melt down. Remarkable power saving may be realized if raw material is

preheated up to 500 - 600C by any method more effective than induction

-61-

heating. Preheating of material has the following advantages other than the abovementioned: i) avoidance of steam exprosion caused by condensation of moisture on the surface of cold charge material; ii) possibility of energy cost saving;

iii) improvement of melting capacity by reducing the melting time in induction furnace.

(1) Preheating furnace type

There are many types of preheating furnace; charging bucket of induction furnace is used as preheater, at the top or bottom of which combustion chamber is provided and generated hot air is passed through the charged material; material in preheating chamber is heated up by circulating hot air fed out of combustion chamber, then material heated is charged into induction furnace by means of shooter; or material is heated directly and continuously by burner on vibrating conveyor or in kiln, etc.

(2) Example of preheating furnace

This is an example of research and development work performed for high-speed induction melting furnace system with effective use of preheating equipment. This melting furnace is of high-frequency induction type with capacity of 600 kW-lt. Specifications of its preheating furnace is given

hereafter and its configuration is shown in Fig.26. Materials to be preheated: Cast iron (20%), return iron scrap (40%), steel scrap (40%) Weight of preheated material: It/charge (at bulk specific gravity 2.0)

-62-

Fig.28 Details of preheating furnace (Preheating by hot air circulation and material charging by chute)

Heat balance table of this preheating furnace is given in Table 13. Absorption heat of material at first charge is low due to heat accumulation in cold furnace body, but absorption heat from 2nd and following charges becomes to 60%, assuring high heat efficiency.

- 6 3 -

Table 13 Heat calculation of preheating

furnace.
2nd charge 3rd charge Qty of heat 92,700 57,300 10,300 3,500 21,600 %

Qty of heat 97,600 56,500 11,900 2,200 27,000

&

100 47.2 8.2 0.3 44.1

100 57.9 12.2 2.3 27.6

100 61.8 11.1 3.8 23.3

Fig.29 and 30 show the temperature rising characteristics of charged material. Temperature of hot air at first charge rises slowly due to

heat accumulation in furnace body, but temperature of both hot air and material at 2nd, 3rd and following charges rises quickly.

Fig.29 Temperature rising characteristics at first charge.

Fig.30 Temperature rising characteristics at 2nd & following charges.

- 6 4 -

(3) Effects of preheating In Table 14 are given the melting characteristics of preheated material compared to non-preheated one. follows: i) Power consumption rate is reduced by 25.4%, from 626 kWh/t to 467 kWh/t. ii) Total unit consumption of energy including gas consumption is saved by 6.3%, from 538.4 x l0 kcal/t to 504.6 x l0 kcal/t. iii) Melting capacity is improved by 27%, from 0.81 t/h to l.03 t/h, namely dairy output of melt is increased from 7 tons to 9 tons.
3 3

Effects of preheating are as

Preheating may cause such demerits as increase of metal loss by to oxidation in preheating process, quality, etc. detrimental effect on the product

As may be seen from Fig.31, oxidation of carbon steel

material is very little under the temperature of 600C and proceeds rapidly over this temperature. This preheating equipment is constructed of hot

air circulating type with separating the combustion chamber from preheating chamber so that hot air over 600C doesn't directly contact with material to be preheated to eliminate the possibility of oxidation during its preheating.

-65-

Fig.31 Oxidation of material in hot air

- 6 7 -

8.

Arc furnace melting

Arc furnace essentially has been designed and has been developed as a steel melting furnace and its recent technological innovation is remarkable. But

in Japan there is a trend to indicate technological problems of melting of cast iron by are furnace, so arc furnace accounts for only 3 - 5% of cast iron melting furnaces, including the use as dual melting combined with cupola and the likes.

8.1 Melting energy

In case of arc furnace the melting heat efficiency in the process from ordinary temperature up to melt-down is high as compared with other melting furnaces, but the heat efficiency in superheating process after melt-down is lower than half of low frequency induction furnace. (Fig. 32)

The total energy for iron melting is consumed for preheating (20C 1200C), melting (1200C), and superheating (1200C - 1550C), which makes up 57%, 19% and 24% respectively, and this shows that energy consumption until melt-down amounts to 76% of the total energy. (Fig.33) In consideration of above-mentioned, cast iron mass production foundry have increasingly adopted dual melting process designed to combine effective furnaces specialized separately for metal melting and for holding and adjusting chemicals.

-68-

8.2 Energy saving measures for arc melting furnace (1) Decreasing of heat input (a) Substitution of heat input

In arc melting furnace, in order to shorten the melting time to improve productivity and power consumption rate, sometimes oxygen is blown in during melting and sometimes fuel oil, kerosene or the likes with oxygen to be burnt directly in the furnace.
(b) Preheating of charged material

Another effective method is preheating charged material by sensible heat of exhaust gas or other kinds of fuels, which enables to reduce heat input by sensible heat of materials and decrease the power consumption rate. Material in closed charging basket may be preheated

from its upper and lower sides by means of burner, or preheated in the preheating reservior with bypass provided directly in the duct between dust collector and arc furnace by using exhaust gas. Utilization of

-69-

exhaust heat allows electric power saving of 20 - 50 kWh/t.

By preheating the ladles sufficiently, by covering the ladles to prevent temperature drop by radiation, by shorten urg the processing time, including spheroidizing, inoculation, etc., and by decreasing the delivery distance, the tapping temperature shall be as low as possible.

(2) Reduction of heat loss (a) Improvement of furnace performance

The larger the furnace capacity is, consumption rate is.

the smaller the power

Fig. 34 shows the relationship between capacity

and power consumption rate of steel making arc furnace.

Fig.34 Capacity and power consumption rate of steel making arc furnace.

- 7 0 -

There are a lot of new designs for improvement of arc furnace performance, so adoption or improvement of arc furnace requires adequate study about them. i) For example,

Ultra high power (UHP) operation for rapid melting Low voltage and large current can make stable and thick short arc, which allows rapid melting with less erosion of refactories. Theoretically, efficiency in such operationmaybe 2.3 times as large as conventional regular power(RP) operation.

ii) Automatic electrode control This system enables to make fluctuation of arc current as small as possible to keep power constant. iii) Transformer secondary cable The water-cooled cable is used as a flexible connecting cable between transformer and electrode in order to reduce resistance. iv) Decreasing furnace openings Prevention from heat radiation requires decreasing the furnace openings as far as possible. In general, melt is discharged through

spouts, but in some cases tapping holes are located at the center of the hearth to shorten the tapping time and reduce the heat loss. Besides, there is an economizer, consisting of water-cooled ring located on electrode hole in furnace cover, which permits to reduce flameblowout from electrode holes and decrease oxidation loss of electrode by cooling effect. v) Water cooling of furnace wall In many cases water-cooled box is arranged on high temperature spots of furnace wall to shorten the repairing time and decrease the power consumption rate.

- 7 1 -

(2) Improvement of operating methods

(a) Quick charging of raw material In order to reduce the heat radiation from furnace, materials shall be charged one time in whole amount, but in practice materials are charged additionally 1 - 2 times. After starting when melting becomes available, additional amount of materials must be charged immediately in time. To protect the hearth and make melting easy, light-, heavy-, mediumand light-weight materials are charged in order from the bottom. Attention must be given to charging position so as not to destroy electrodes by falling down of heavy-weight material.
(b) Appropriate power input

Since power and time consumed during melting period will account for the greater part of, those required during the whole process, rapid melting needs additional energy supply, such as electric power and others. Above-mentioned UHP operation, auxiliary burning by means of

side burner and the likes are well-known methods. Just after started to apply electric current, the current fluctuates violently due to contact betweenmaterials and electrode, thus reactance in the circuit designed, but when metal starts melting the current is stabilized, then the reactance is eliminated and the power can be supplied efficiently.
(c) Cut down of the idling time

Time management,

including

reduction of

the analyse time,

elimination of the waiting time for crane, etc., must be made positively. Decreasing the furnace repairing time is one of important energy saving measures.
(d) Improvement of dust collecting efficiency

In many electric furnace shops the buildings are providedwith dust collecting system for environmental protection inside and outside of

-72-

foundry,

new concept is realized to collect dust directly from arc

furnace or by enclosing furnace entirely with panels so as to improve dust collecting efficiency. Utilization of exhaust gas in material preheating process allows to recover exhaust heat and make exhaust gas temperature lower, equipment. which serves to simplify the dust collecting

(3) Improvement of product yield

As mentioned before, improvement of product yield has an important relation to the energy consumption rate of product rather than the power consumption rate for melting. Moreover, it is important to reduce the

weight of metal to be melted by lessening defective casting ratio and decreasing the amount of remaining melt in ladle and furnace.

-73-