Abstract
The strong light emission and absorption exhibited by single atomic layer transitional metal dichalcogenides in the visible to near-infrared wavelength range make them attractive for optoelectronic applications. In this work, using two-pulse photovoltage correlation technique, we show that monolayer molybdenum disulfide photodetector can have intrinsic response times as short as 3âps implying photodetection bandwidths as wide as 300âGHz. The fast photodetector response is a result of the short electronâhole and exciton lifetimes in this material. Recombination of photoexcited carriers in most two-dimensional metal dichalcogenides is dominated by nonradiative processes, most notable among which is Auger scattering. The fast response time, and the ease of fabrication of these devices, make them interesting for low-cost ultrafast optical communication links.
Similar content being viewed by others
Introduction
Two-dimensional (2D) transition metal dichalcogenides (TMDs) have emerged as interesting materials for low-cost optoelectronic devices, including photodetectors, light-emitting diodes, and, more recently, lasers1,2,3,4,5,6,7,8,9,10,11. In the case of photodetectors, the response time and the quantum efficiency are two important figures of merit. The intrinsic response time of TMD photodetectors and the ultimate limits on the speed of operation are unknown. The reported quantum efficiencies of TMD materials and devices are typically in the 0.0001â0.01 range5,6,7,8,9,12,13,14,15, indicating that most of the electrically injected or optically generated electrons and holes recombine nonradiatively. Understanding the nonradiative carrier recombination mechanisms, as well as the associated timescales, is therefore important. Previously, ultrafast optical/THz pumpâprobe as well as ultrafast photoluminescence techniques have been used, by the authors and others, to study the ultrafast carrier dynamics in metal dichalcogenides and in molybdenum disulfide (MoS2) in particular12,16,17,18,19,20,21,22. In these measurements, free-carrier recombination dynamics, exciton formation and recombination dynamics, refractive index changes, optical/THz intraband and interband conductivity changes, as well as the dynamics associated with carriers trapped in optically active midgap defects are all expected to play a role to varying degrees and, consequently, the results have been difficult to interpret and reconcile.
In this letter, we present experimental results on ultrafast two-pulse photovoltage correlation (TPPC) measurements on monolayer MoS2 metal-semiconductor photodetectors. In TPPC measurements, a photodetector is excited with two identical optical pulses separated by a time delay and the integrated detector photoresponse (either photovoltage or photocurrent response) is recorded as a function of the time delay. TPPC thus uses the photodetector to perform an optical correlation measurement. The nonlinearity of the photoresponse with respect to the optical pulse energy enables one to determine ultrafast intrinsic temporal response of the detector with sub-picosecond resolution23,24,25,26,27. Our measurements show that the photovoltage is suppressed when the two optical pulses arrive together indicating a saturation of the photoresponse. As the time delay between the two pulses is increased from zero, the photovoltage recovers, and the recovery, as a function of the time delay, exhibits two distinct timescales: (i) a fast timescale of the order of 3â5âps and (ii) a slow timescale of â¼80â110âps. These two timescales are found to be largely independent of the temperature, exhibits only a mild dependence on the pump fluence, and varies a little from sample to sample. Between 50 and 75% of the photovoltage correlation response recovers on the fast timescale implying that ultrafast TMD photodetectors with (8âdB) current modulation bandwidths in the 200â300âGHz range are possible. The fast response speed is a result of the short lifetime of the photoexcited carriers. Since TPPC measures the photovoltage (or photocurrent), this technique is sensitive only to the total photoexcited carrier population, including both bound (excitons) and free carriers, that contributes to the photoresponse. TPPC therefore also offers important and unique insights into the carrier recombination dynamics. The temperature and pump fluence dependence of our TPPC results are consistent with defect-assisted recombination as being the dominant mechanism, in which the the photoexcited electrons and holes, both free and bound (excitons), are captured by defects via Auger scattering28. Strong Coulomb interactions in 2D TMDs, including the correlations in the positions of free and bound electrons and holes arising from the attractive interactions, result in large carrier capture rates by defects via Auger scattering28. Our results underscore the trade-off between speed and quantum efficiency in TMD photodetectors.
Results
Two-pulse photovoltage correlation technique
Microscope image of a monolayer metal-MoS2 photodetector is shown in Fig. 1a, and the schematic in Fig. 1b depicts the setup for a TPPC experiment. A â¼80-fs, 905-nm (1.37âeV) centre wavelength, optical pulse from a â¼83-MHz repetition rate TiâSapphire laser is frequency doubled to 452ânm (2.74âeV, â¼150âfs) by a beta-BaB2O4 crystal, then mechanically chopped at 1.73âKHz and then split into two pulses by a 50/50 beam splitter. The time delay Ît between these two pulses is controlled by a linear translation stage. The resulting voltage across the photodetector is measured as a function of the time delay between the pulses using a lock-in amplifier with a 10âMΩ input resistance. In experiments, the maximum photoresponse was obtained when the light was focused on the sample near one of the metal contacts of the device, and the photoresponse decayed rapidly as the centre of the focus spot was moved more than half a micron away from the metal contact. The direction of the d.c. photocurrent, and the resulting sign of the measured d.c. photovoltage are shown in Fig. 1b, and were determined without using the lock-in. Photovoltage was always positive at the contact near which the light was focused. Figure 1c shows a low-frequency circuit model of the device and the measurement. The circuit model shown can be derived from a high-frequency circuit model (Supplementary Fig. 2 and Supplementary Note 3). If the time-dependent short circuit current response of the illuminated junction to a single optical pulse is I1(t), and to two optical pulses separated by time Ît is I2(t, Ît), and the external resistance Rext is much larger than the total device resistance, then the measured d.c. voltage Vc(Ît) is approximately equal to (Rj/TR)â«I2(t, Ît)dt, where TR is the pulse repetition period, Rj is the resistance of the metal-MoS2 junction, and the time integral is over one complete period. As the time delay Ît becomes much longer than the duration of I1(t), one expects Vc(Ît) to approach (2Rj/TR)â«I1(t)dt.
Experimental results
Figure 2a shows the measured two-pulse photovoltage correlation signal Vc(Ît) plotted as a function of the time delay Ît between the pulses. The substrate temperature is 5âK, the gate bias is 0âV, and the pump fluence is 8âμJâcmâ2. Vc(Ît) is minimum when the two pulses completely overlap in time (that is, when Ît=0). This implies, not surprisingly, that the photovoltage response of the detector to an optical pulse is a sublinear function of the optical pulse energy. As Ît increases from zero, Vc(Ît) also increases from its minimum value at Ît=0. As Ît becomes much longer than the duration of the response transient of the detector to an optical pulse, Vc(Ît) approaches a constant value. The timescales over which Vc(Ît) goes to the constant value are related to the timescales associated with the response transient of the detector to an optical pulse. These timescales are better observed in the measured data if the magnitude of ÎVc(Ît), defined as Vc(Ît)âVc(â), is plotted on a log scale, as shown in Fig. 2b. The plot in Fig. 2b shows two distinct timescales: (i) a fast timescale of â¼4.3âps and (ii) a slow timescale of â¼105âps. In different devices, the fast timescales were found to be in the 3â5âps range, and the slow timescales were in the 90â110âps range. The fast timescales imply (8âdB) current modulation bandwidths wider than 300âGHz.
Measurements were performed at different temperatures and using different pump pulse fluences to understand the mechanisms behind the photoresponse and the associated dynamics. Figure 2b shows |ÎVc(Ît)| plotted for two different extreme temperatures: T=5âK and T=300âK. Gate bias is 0âV. The pump fluence is 8âμJâcmâ2. Two distinct timescales are observed at both temperatures and these timescales are largely independent of the temperature. Measurements performed at intermediate temperatures provided the same results. |ÎVc(Ît)| was found to be larger at smaller temperatures. We attribute this to the increase in the metal-semiconductor junction resistance Rj at lower temperatures. Figure 2c shows |ÎVc(Ît)| plotted for different values of the pump pulse fluence. The pump pulse fluence was varied from 1 to 16âμJâcmâ2. Higher values of the pump fluence were not used to avoid optical damage to the sample12. T=300âK and gate bias is 0âV. Figure 2c shows that the same two timescales are observed for all values of the pump fluence and these timescales are not very sensitive to the pump fluence. The observed timescales also did not change in any significant way under a positive or a negative gate bias (Supplementary Figs 3 and 4 and Supplementary Note 4). The internal and external detector quantum efficiencies were estimated from the measured values of Vc(â) and the junction resistance Rj to be in the 0.008â0.016 and 0.001â0.002 ranges, respectively.
The two different timescales observed in our two-pulse photovoltage correlation experiments match well with the two different timescales observed previously in ultrafast optical/THz pumpâprobe studies of carrier dynamics as well as in ultrafast photoluminescence studies of MoS2 monolayers12,22. It is therefore intriguing if the model for defect-assisted carrier recombination reported previously by the authors12,28 for explaining the ultrafast carrier dynamics in MoS2 monolayers can be used to obtain photovoltage correlations that are in good agreement with the experimental results reported in this letter. We show below that this is indeed the case.
Ultrafast photoresponse of the metal-MoS2 junction
Understanding the ultrafast photoresponse of the detector, and in particular the short circuit current response I2(t, Ît), is important for interpreting the experimental results. Figure 3a depicts the band diagram of the metal-MoS2 junction (plotted in the plane of the MoS2 layer) after photoexcitation with an optical pulse. Given the Schottky barrier height of 100â300âmeV (ref. 8), the width of the MoS2 region near the metal with a non-zero lateral electric field is estimated to be to â¼100â300ânm (ref. 29). As a result of light diffraction from the edge of the metal contact, light scattering from the substrate, and plasmonic guidance, a portion of the MoS2 layer of length equal to a few hundred nanometres is photoexcited even underneath the metal (Supplementary Fig. 1 and Supplementary Note 1). The photoresponse of graphene photodetectors has been explained in terms of contributions from photovoltaic and photothermoelectric contributions23,24,25,26,27,30. In our MoS2 samples, the carrier mobilities and diffusivities are 2â3 orders of magnitude smaller than in graphene and the time period in which most of the photoexcited carriers recombine and/or are captured by defects is in the few picoseconds range12,20,21,22,28. Assuming similar mobilities and diffusivities of electrons and holes in MoS2, the photoexcited carriers, both free and bound (excitons), move, either by drift in the junction lateral electric field or by diffusion, less than â¼10ânm in 5âps before they recombine and/or are captured by defects. The photoexcited carrier distributions therefore do not change significantly in space during their lifetime. Separation of electrons and holes either by the junction lateral electric field or at the metal-MoS2 interface will contribute to the integral â«I2(t, Ît)dt(âVc(Ît)) (the measured dependence of the photoresponse on the junction electric field and the gate voltage is discussed in the Supplementary Figs 3 and 4 and Supplementary Note 4. We assume that the integral â«I2(t, Ît)dt is approximately proportional to the integral â«[pâ²(t, Ît) + nâ²(t, Ît)]dt (Supplementary Note 2). Here, pâ²(t, Ît) and nâ²(t, Ît) are the time-dependent photoexcited electron and hole densities in the junction, including carriers both free and bound (excitons). This assumption, although simple, allows one to relate the measured photoresponse to the carrier dynamics and, as shown below, the results thus obtained are in excellent agreement with the experiments. We expect that on much longer timescales, when the photoexcited carriers have recombined or been captured, the photoresponse is entirely thermoelectric in nature, as is the case in metalâgraphene photodetectors23,25,26,27,30. But in this letter we focus on the dynamics occurring on only short timescales.
Carrier capture and recombination model
It is known that most of the photoexcited carriers in monolayer MoS2 recombine nonradiatively12,15,28. The temperature independence as well as the sample dependence of the recombination rates in previously reported works suggested that free and bound (excitons) carriers recombine via capture by defects through Auger scattering12,28. Monolayer MoS2 can have several different kinds of defects, including grain boundaries, line defects, interstitials, dislocations and vacancies31,32,33,34,35,36,37. The strong electron and hole Coulomb interaction in monolayer TMDs makes defect capture via Auger scattering very effective28. The time constants observed in this work in the photovoltage correlations are also temperature independent (Fig. 2b) and also match well with the time constants observed previously in optical/THz pumpâprobe and photoluminescence measurements12,22. We therefore use the model for carrier capture by defects via Auger scattering in MoS2 presented by Wang et al.12,28 to model our TPPC experimental results (Supplementary Fig. 5 and Supplementary Note 5). The model assumes carrier capture by two different defect levels, one fast and one slow12. The essential dynamics captured by the model, and their relationships to the experimental observations, are as follows12. After photoexcitation, electrons and holes thermalize and lose most of their energy on a timescale much shorter than our experimental resolution (â¼0.5â1.0âps) and, therefore, thermalization is assumed to happen instantly in our model38. Most of the photoexcited holes (both free and bound), followed by most of the electrons, are captured by the fast defects within the first few picoseconds after photoexcitation. During the same period, a small fraction of the holes is also captured by the slow defects. This rapid capture of the photoexcited electrons and holes is responsible for the fast time constant observed in our photovoltage correlation experiments. The remaining photoexcited electrons are captured by the slow defects on a timescale of 65â80âps and this slow capture of electrons is responsible for the slow time constant observed in our photovoltage correlation experiments. We should point out here that the two time constants observed in the photovoltage correlation signal ÎVc(Ît) are always slightly longer than the corresponding two time constants exhibited by the carrier densities in direct optical pumpâprobe and measurements12, as is to be expected in the case of correlation measurements. Finally, the superlinear dependence of the carrier capture rates on the photoexcited carrier densities in the model, and therefore on the optical pulse energy, results in the experimentally observed negative value of the photovoltage correlation signal ÎVc(Ît=0) at zero time delay. The values of the fitting parameters used in the theoretical model to fit the experimental data are given in the Supplementary Table 1 and are almost identical to the values extracted previously from direct optical pumpâprobe measurements of the carrier dynamics in monolayer MoS2 (ref. 12).
The comparison between the data and the model are shown in Fig. 3b which plots the measured and computed photovoltage correlation |ÎVc(Ît)| as a function of the time delay Ît for different pump fluence values: 4, 8 and 16âμJâcmâ2. All curves are normalized to a maximum value of unity (since the model gives the photovoltage correlation signal up to a multiplicative constant). The model not only reproduces the very different timescales observed in |ÎVc(Ît)| measurements, it achieves a very good agreement with the data over the entire range of the pump fluence values used in our experiments for the same values of the parameters (Supplementary Table 1). Figure 3c shows the scaling of the measured and computed values of |ÎVc(Ît=0)| with the pump pulse fluence. Again, a very good agreement is observed between the model and the data.
Discussion
Our results reveal the fast response time and the wide bandwidth of metal-MoS2 photodetectors and show that these detectors can be used for ultrafast applications. Our results also shed light on the carrier recombination mechanisms and the associated timescales. Although we focused mainly on the carrier dynamics in this paper, the device intrinsic resistances and capacitances are not expected to fundamentally limit the device speed because of the rather small capacitances associated with the lateral metal-semiconductor junctions (Supplementary Note 3). An obstacle to using TMDs in practical light emission and detection applications is the small values of the reported quantum efficiencies in these materials5,6,7,8,9,12,13,14,15. In photodetectors, the response speed and the quantum efficiency are often inversely related39. In most semiconductor photovoltaic detectors with large carrier mobilities and long recombination times (for example, group IIIâV semiconductor photodetectors39), the transit time of the photogenerated carriers through the junction depletion region determines the detector bandwidth39. Given the relatively small carrier mobilities and diffusivities in MoS2, the fast carrier recombination times determine the speed in our metal-MoS2 detectors. The price paid for the the fast response time is the small internal quantum efficiency: most of the photogenerated carriers recombine before they make it out into the circuit. The best reported carrier mobilities in monolayer MoS2 are an order of magnitude larger than in our devices and, therefore, metal-MoS2 photodetectors with internal quantum efficiencies around 0.1 (approximately an order of magnitude larger than of our devices) are possible without sacrificing the wide bandwidth. Density of defects, which contribute to carrier trapping and recombination, is also a parameter that can be potentially controlled in 2D TMD optoelectronic devices to meet the requirements for ultrafast or high quantum efficiency applications. In addition, vertical heterostructures of 2D TMD materials can also be used to circumvent the transport bottleneck in high speed applications 40.
Methods
Device fabrication and characterization
Monolayer MoS2 samples were mechanically exfoliated from bulk MoS2 crystal (obtained from 2D Semiconductors) and transferred onto highly n-doped Si substrates with 90ânm thermal oxide. Monolayer sample thickness was confirmed by Raman and reflection spectroscopies41. Au metal contacts (with a very thin Cr adhesion layer) were patterned and deposited onto the samples using electron-beam lithography. The doped Si substrate acted as the back gate. Microscope image of a 10 à 10âμm2 area device is shown in Fig. 1a. Carrier densities and mobilities in the devices were determined using electrical transport measurements on devices of different dimensions. The devices were found to be n-doped with electron densities around 1 à 1012â2 à 1012 cmâ2 (under zero gate bias). The intrinsic doping was attributed to impurities and defect levels8. The electron mobility in the devices was found to be in the 15â20âcm2âVâ1âsâ1 range at 5âK. The zero gate bias device resistance was typically <1âMΩ at all temperatures for a 10 à 10âμm2 area device. While the device resistance decreased under a positive gate bias, no signature of hole conduction was observed even when a large negative gate bias was applied indicating that the Fermi level in the MoS2 layer was likely pinned at defect levels within the bandgap under a negative gate bias. The devices were mounted in a helium-flow cryostat and the temperature was varied between 5 and 300âK during measurements. The zero gate bias device resistance was found to be a function of the temperature and decreased almost linearly with the temperature from â¼1âMΩ at 5âK to values 5â7 times smaller at 300âK. The total device resistance was dominated by the metal Schottky contacts to the device. For example, at 5âK the resistance contributed by the 10 à 10âμm2 area MoS2 strip is estimated to be in the 0.10â0.20âMΩ range (from the measured mobility values), which is approximately only one-tenth to one-fifth of the total device resistance. The reported Schottky barrier heights between similarly n-doped monolayer MoS2 and Au/Cr contacts are in the 100â300âmeV range8. Depending on how strongly the Fermi level gets pinned at the defect levels in the bandgap, the lateral potential drop in the MoS2 layer at the metal-MoS2 interface (depicted in Fig. 3a) could be equal to or smaller than the Schottky barrier height.
TPPC experiment setup
In the TPPC measurements, the two 452ânm optical pulses were cross-polarized to minimize interference and focused onto the device using a 20 à or a 100 à microscope objective resulting in a minimum focus spot size of around 0.75âμm. Optical absorption in monolayer MoS2 layers was characterized using a confocal microscope-based relection/transmission setup12 and yielded â¼11â12% absorption (single-pass) in monolayer MoS2 on oxide at 452ânm (pump pulse wavelength). Measurement of the photovoltage using a high input impedance voltage amplifier (Lock-in in our case) was found to give a much better signal-to-noise ratio than the measurement of the photocurrent directly using a low input impedance transimpedance amplifier.
Additional information
How to cite this article: Wang, H. et al. Ultrafast response of monolayer molybdenum disulfide photodetectors. Nat. Commun. 6:8831 doi: 10.1038/ncomms9831 (2015).
References
Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805 (2010) .
Splendiani, A. et al. Emerging photoluminescence in monolayer MoS2 . Nano Lett. 10, 1271â1275 (2010) .
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699â712 (2012) .
Mak, K. F. et al. Tightly bound trions in monolayer MoS2 . Nat. Mater. 7, 207â211 (2013) .
Lopez-Sanchez, O., Lembke, D., Kayci, M., Radenovic, A. & Kis, A. Ultrasensitive photodetectors based on monolayer MoS2 . Nat. Nanotechnol. 8, 497â501 (2013) .
Ross, J. S. et al. Electrically tunable excitonic light-emitting diodes based on monolayer WSe2 pn junctions. Nat. Nanotechnol. 9, 268â272 (2014) .
Yin, Z. et al. Single-layer MoS2 phototransistors. ACS Nano 6, 74â80 (2012) .
Sundaram, R. S. et al. Electroluminescence in single layer MoS2 . Nano Lett. 13, 1416â1421 (2013) .
Baugher, B. W. H., Churchill, H. O. H., Yang, Y. & Jarillo-Herrero, P. Optoelectronic devices based on electrically tunable pân diodes in a monolayer dichalcogenide. Nat. Nanotechnol. 9, 262â267 (2014) .
Zhang, C., Wang, H., Chan, W., Manolatou, C. & Rana, F. Absorption of light by excitons and trions in monolayers of metal dichalcogenide MoS2: experiments and theory. Phys. Rev. B 89, 205436 (2014) .
Wu, S. et al. Monolayer semiconductor nanocavity lasers with ultralow thresholds. Nature 520, 69â72 (2015) .
Wang, H., Zhang, C. & Rana, F. Ultrafast dynamics of defect-assisted electron-hole recombination in monolayer MoS2 . Nano Lett. 15, 339â345 (2015) .
Bernardi, M., Palummo, M. & Grossman, J. C. Extraordinary sunlight absorption and one nanometer thick photovoltaics using two-dimensional monolayer materials. Nano Lett. 13, 3664â3670 (2013) .
Furchi, M. M., Pospischil, A., Libisch, F., Burgdrfer, J. & Mueller, T. Photovoltaic effect in an electrically tunable van der Waals heterojunction. Nano Lett. 14, 4785â4791 (2014) .
Furchi, M. M., Polyushkin, D. K., Pospischil, A. & Mueller, T. Mechanisms of photoconductivity in atomically thin MoS2 . Nano Lett. 14, 6165â6170 (2014) .
Shi, H. et al. Exciton dynamics in suspended monolayer and few-layer MoS2 2D crystals. ACS Nano 7, 1072â1080 (2013) .
Wang, R. et al. Ultrafast and spatially resolved studies of charge carriers in atomically thin molybdenum disulfide. Phys. Rev. B 86, 045406 (2012) .
Sim, S. et al. Exciton dynamics in atomically thin MoS2: interexcitonic interaction and broadening kinetics. Phys. Rev. B 88, 075434 (2013) .
Sun, D. et al. Observation of rapid excitonâexciton annihilation in monolayer molybdenum disulfide. Nano Lett. 14, 5625â5629 (2014) .
Lagarde, D. et al. Carrier and polarization dynamics in monolayer MoS2 . Phys. Rev. Lett. 112, 047401 (2014) .
Korn, T., Heydrich, S., Hirmer, M., Schmutzler, J. & Schller, C. Low-temperature photocarrier dynamics in monolayer MoS2 . Appl. Phys. Lett. 99, 102109 (2011) .
Docherty, C. J. et al. Ultrafast transient terahertz conductivity of monolayer MoS2 and WSe2 grown by chemical vapor deposition. ACS Nano 8, 11147â11153 (2014) .
Urich, A., Unterrainer, K. & Mueller, T. Intrinsic response time of graphene photodetectors. Nano Lett. 11, 2804â2808 (2011) .
Prechtel, L. et al. Time-resolved picosecond photocurrents in contacted carbon nanotubes. Nano Lett. 11, 269â272 (2011) .
Prechtel, L. et al. Time-resolved ultrafast photocurrents and terahertz generation in freely suspended graphene. Nat. Commun. 3, 646 (2012) .
Graham, M. W., Shi, S.-F., Ralph, D. C., Park, J. & McEuen, P. L. Photocurrent measurements of supercollision cooling in graphene. Nat. Phys. 9, 103â108 (2013) .
Sun, D. et al. Ultrafast hot-carrier-dominated photocurrent in graphene. Nat. Nanotechnol. 7, 114â118 (2012) .
Wang, H. et al. Fast exciton annihilation by capture of electrons or holes by defects via Auger scattering in monolayer metal dichalcogenides. Phys. Rev. B 91, 165411 (2015) .
Petrosyan, S. G. & Shik, A.Ya. Contact phenomena in low-dimensional electron systems. Zh. Eksp.Teor. Fiz. 69, 1261 (1989) .
Tielrooji, K. et al. Generation of photovoltage in graphene on a femtosecond timescale through efficient carrier heating. Nat. Nanotechnol. 10, 437â443 (2015) .
Fuhr, J. D., Saúl, A. & Sofo, J. O. Scanning tunneling microscopy chemical signature of point defects on the MoS2(0001) surface. Phys. Rev. Lett. 92, 026802 (2004) .
Komsa, H.-P. et al. Two-dimensional transition metal dichalcogenides under electron irradiation: defect production and doping. Phys. Rev. Lett. 109, 035503 (2012) .
Enyashin, A. N., Bar-Sadan, M., Houben, L. & Seifert, G. Line defects in molybdenum disulfide layers. J. Phys. Chem. C 117, 10842â10848 (2013) .
Zhou, W. et al. Intrinsic structural defects in monolayer molybdenum disulfide. Nano Lett. 13, 2615â2622 (2013) .
Noh, J.-Y., Kim, H. & Kim, Y.-S. Stability and electronic structures of native defects in single-layer MoS2 . Phys. Rev. B 89, 205417 (2014) .
Yuan, S., Roldán, R., Katsnelson, M. I. & Guinea, F. Effect of point defects on the optical and transport properties of MoS2 and WS2 . Phys. Rev. B 90, 041402 (2014) .
Liu, D., Guo, Y., Fang, L. & Robertson, J. Sulfur vacancies in monolayer MoS2 and its electrical contacts. Appl. Phys. Lett. 103, 183113 (2013) .
Kaasbjerg, K., Bhargavi, K. S. & Kubakaddi, S. S. Hot-electron cooling by acoustic and optical phonons in monolayers of MoS2 and other transition-metal dichalcogenides. Phys. Rev. B 90, 165436 (2014) .
Donati, S. Photodetectors: Devices, Circuits and Applications 1st ed. Prentice Hall (1999) .
Massicotte, M. et al. Picosecond photodetection in van der Waals heterostructures. Preprint at http://arxiv.org/abs/1507.06251 (2015) .
Lee, C. et al. Anomalous lattice vibrations of single- and few-layer MoS2 . ACS Nano 4, 2695â2700 (2010) .
Acknowledgements
The authors acknowledge helpful discussions with Jared H. Strait, Michael G. Spencer and Paul L. McEuen, and support from CCMR under NSF grant number DMR-1120296, AFOSR-MURI under grant number FA9550-09-1-0705, ONR under grant number N00014-12-1-0072, and the Cornell Centre for Nanoscale Systems funded by NSF.
Author information
Authors and Affiliations
Contributions
H.W. performed the experiments, modelling, and simulation. C.Z and W.C fabricated the devices. S.T. and F.R initiated and supervised the work.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-5, Supplementary Table 1, Supplementary Notes 1-5 and Supplementary References (PDF 576 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the articleâs Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wang, H., Zhang, C., Chan, W. et al. Ultrafast response of monolayer molybdenum disulfide photodetectors. Nat Commun 6, 8831 (2015). https://doi.org/10.1038/ncomms9831
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms9831