Title:Electrical Properties and Subband Occupancy at the (La,Sr)(Al,Ta)O$_3$/SrTiO$_3$ Interface
View PDFAbstract:The quasi two-dimensional electron gas (q-2DEG) at oxide interfaces provides a platform for investigating quantum phenomena in strongly correlated electronic systems. Here, we study the transport properties at the high-mobility (La$_{0.3}$Sr$_{0.7}$)(Al$_{0.65}$Ta$_{0.35}$)O$_{0.3}$/SrTiO$_{0.3}$ (LSAT/STO) interface. Before oxygen annealing, the as-grown interface exhibits a high electron density and electron occupancy of two subbands: higher-mobility electrons ($\mu_1\approx{10^4}$ cm$^2$V$^{-1}$s$^{-1}$ at 2 K) occupy the lower-energy $3d_{xy}$ subband, while lower-mobility electrons ($\mu_1\approx{10^3}$ cm$^{2}$V$^{-1}$s$^{-1}$ at 2 K) propagate in the higher-energy $3d_{xz/yz}$-dominated subband. After removing oxygen vacancies by annealing in oxygen, only a single type of 3dxy electrons remain at the annealed interface, showing tunable Shubnikov-de Haas (SdH) oscillations below 9 T at 2 K and an effective mass of $0.7m_e$. By contrast, no oscillation is observed at the as-grown interface even when electron mobility is increased to $50,000$ cm$^{2}$V$^{-1}$s$^{-1}$ by gating voltage. Our results reveal the important roles of both carrier mobility and subband occupancy in tuning the quantum transport at oxide interfaces.
Current browse context:
cond-mat.str-el
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.