Title:Clustered vacancies in ZnO: Chemical aspects and consequences on physical properties
View PDFAbstract:Chemical nature of point defects, their segregation, cluster or complex formation in ZnO is an important area of investigation. In this report, 1.2 MeV Ar ion beam is used to incorporate defects in granular ZnO. Evolution of defective state with irradiation fluence 1 x 10^14 and 1 x 10^16 ions/cm2 has been monitored using XPS, PL and Raman spectroscopic study. XPS study shows presence of oxygen vacancies (VO) in the Ar ion irradiated ZnO. Zn(LMM) Auger spectra clearly identifies transition involving metallic zinc in the irradiated samples. Intense PL emission from IZn related shallow donor bound excitons (DBX) is visible in the 10 K spectra for all samples. Although overall PL is largely reduced with irradiation disorder, DBX intensity is increased for the highest fluence irradiated sample. Raman study indicates damage in both zinc and oxygen sub-lattice by energetic ion beam. Representative Raman modes from defect complexes involving VO, IZn and IO are visible after irradiation with intermediate fluence. Further increase of fluence shows, to some extent, a homogenization of disorder. Huge reduction of resistance is also noted for this sample. Certainly, high irradiation fluence induces a qualitative modification of the conventional (and highly resistive) grain boundary (GB) structure of granular ZnO. Low resistive path, involving IZn related shallow donors, across the GB can be presumed to explain resistance reduction. Open volumes (VZn and VO) agglomerate more and more with increasing irradiation fluence and finally get transformed to voids. Results as a whole have been elucidated with a model which emphasizes possible evolution of new defect microstructure that is distinctively different from the GB related disorder. Based on the model, qualitative explanations of commonly observed radiation hardness, colouration and ferromagnetism in disordered ZnO have been put forward.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.