Title:Emergence of high-temperature superconducting phase in the pressurized La3Ni2O7 crystals
View PDFAbstract:The recent report of pressure-induced structure transition and signature of superconductivity with Tc = 80 K above 14 GPa in the La3Ni2O7 crystals has garnered considerable attention. To further elaborate this discovery, we carried out comprehensive resistance measurements on the La3Ni2O7 crystals grown with the optical-image floating zone furnace under oxygen pressure (15 bar) by using the diamond anvil cell (DAC) and cubic anvil cell (CAC), which employs the solid and liquid pressure transmitting medium, respectively. For the sample #1 measured in DAC, it exhibits a semiconducting-like behavior with large resistance at low pressures and becomes metallic gradually upon compression. At the pressures P >= 13.7 GPa, we observed the appearance of resistance drop as large as ~50% around 70 K, which evolves into a kink-like anomaly at pressures above 40 GPa and shifts to lower temperatures gradually with increasing magnetic field. These observations are consistent with the recent report mentioned above. On the other hand, the sample #2 measured in CAC retains the metallic behavior in the investigated pressure range up to 15 GPa. The hump-like anomaly in resistance around ~130 K at ambient pressure disappears at P >= 2 GPa. In the pressure range from 11 to 15 GPa, we observed the gradual development of a shoulder-like anomaly in resistance at low temperatures, which evolves into a pronounced drop of resistance by 98% below 62 K at 15 GPa, reaching a temperature-independent resistance of 20 uOhm below 20 K. Similarly, this resistance anomaly can be shifted to lower temperatures progressively by applying external magnetic fields, resembling a typical superconducting transition.
Current browse context:
cond-mat.supr-con
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.