Title:In-situ Synchrotron X-Ray Photoelectron Spectroscopy Study of Medium-Temperature Baking of Niobium for SRF Application
View PDF HTML (experimental)Abstract:In the present work the chemical composition of niobium surface upon 200-400 °C baking similar to "medium-temperature baking" and "furnace baking" of cavities is explored in-situ by synchrotron X-ray photoelectron spectroscopy (XPS). Our findings imply that below the critical thickness of $Nb_2O_5$ layer (about 1 nm) niobium starts to interact actively with surface impurities, such as carbon and phosphorus. By studying the kinetics of the native oxide reduction, the activation energy and the rate-constant relation have been determined and used for the calculation of the oxygen-concentration depth profiles. It has been established that the controlled diffusion of oxygen when the native-oxide layer represents an oxygen source is realized at temperatures 200-300 °C, while at 400 °C the pentoxide is completely reduced and the doping level is determined by an ambient oxygen partial pressure. Fluorine (F to Nb atomic ratio is about 0.2) after the buffered chemical polishing was found to be incorporated into the surface layer probed by XPS (about 4.6 nm), and its concentration increased during the low-temperature baking (F/Nb up to 0.35 at 230 °C) and depleted at higher temperatures (F/Nb=0.11 at 400 °C). Thus, the influence of fluorine on the performance of mid-T baked, mild-baked (120 °C/48 h) and nitrogen-doped cavities must be considered. The possible role of fluorine in the educed $Nb^{+5}$ to $Nb^{+4}$ reaction under the impact of an X-ray beam at room temperature and during the thermal treatment is also discussed. The range of temperature and duration parameters of the thermal treatment at which the niobium surface would not be contaminated with impurities is determined for industrial applications.
Submission history
From: Alena Prudnikava [view email][v1] Mon, 11 Dec 2023 17:05:58 UTC (4,088 KB)
[v2] Thu, 8 Feb 2024 14:07:35 UTC (3,598 KB)
Current browse context:
physics.acc-ph
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.