Coexistence of ferromagnetism and superconductivity at KTaO3 heterointerfaces
Abstract
ABSTRACT: The coexistence of superconductivity and ferromagnetism is a long-standing issue in superconductivity due to the antagonistic nature of these two ordered states. Experimentally identifying and characterizing novel heterointerface superconductors that coexist with magnetism presents significant challenges. Here, we report the experimental observation of two-dimensional long-range ferromagnetic order in the KTaO3 heterointerface superconductor, showing the coexistence of superconductivity and ferromagnetism. Remarkably, our direct current superconducting quantum interference device measurements reveal an in-plane magnetization hysteresis loop persisting above room temperature. Moreover, the first-principles calculations and X-ray magnetic circular dichroism measurements provide decisive insights into the origin of the observed robust ferromagnetism, attributing it to oxygen vacancies that localize electrons in nearby Ta 5 states. Our findings not only suggest KTaO3 heterointerfaces as time-reversal symmetry breaking superconductors, but also inject fresh momentum into the exploration of the intricate interplay between superconductivity and magnetism, enhanced by the strong spin-orbit coupling inherent to the heavy Ta in 5 orbitals of KTaO3 heterointerfaces.
INTRODUCTION
Two-dimensional oxide heterointerfaces exhibit a wide range of emergent quantum phenomena inaccessible in their bulk individuals due to the strong interplay between electrons with Coulomb interaction and the interfacial electron-phonon coupling at the interfaces ref1 ; ref2 ; ref3 . Among them, a landmark oxide interface is LaAlO3/SrTiO3 ref4 , which displays a plethora of appealing physical properties, encompassing two-dimensional electron gases with high electron mobility ref5 , strong Rashba-like spin-orbit coupling ref7 ; ref8 ; Soumyanarayanan , interfacial superconductivity ref6 ; Caviglia , and ferromagnetism ref9 ; ref10 . In particular, the coexistence of superconductivity and ferromagnetism has also been unveiled by high-resolution magnetic torque magnetometry ref11 , scanning superconducting quantum interference device (SQUID) ref12 , and magnetoresistance ref13 . This suggests the presence of a nontrivial superconducting phase in the ground state, such as an intriguing Fulde-Ferrell-Larkin-Ovchinikov-type condensate of Cooper pairs with finite momentum ref18 and a mixed-parity superconducting phase with an admixture of spin-singlet and spin-triplet pairing components LFu2015 ; Nagaosa2012 that is a candidate platform for realizing Majorana modes Potter2011 . However, the experimental challenges posed by the extremely low superconducting critical temperature (below 250 mK) of SrTiO3 heterointerfaces have hindered a comprehensive exploration of the underlying properties ref6 , leaving the origin of these quantum phases still elusive Fitzsimmons ; ref22 and motivating the search for a more favorable heterointerface superconductor that hosts the intricate interplay between ferromagnetism and superconductivity.
Very recently, an unforeseen crystalline-orientation-dependent superconductivity has been observed at KTaO3 heterointerfaces with as high as 2 K ref27 ; ref23 ; ref25 ; ref26 . This is nearly one order of magnitude higher in than that of SrTiO3 ref6 . The experimental findings also demonstrate that electronic states near the Fermi energy derived from Ta 5 orbitals with strong spin-orbit coupling play a decisive role in electronic conduction at the KTaO3 heterointerfaces Bruno2019 ; Mallik ; Hua2022 ; Arnault ; Ahadi2023 . Moreover, the existence of intrinsic anomalous Hall effect observed by electrical transport measurements at non-superconducting KTaO3 heterointerfaces Tawhid2022 ; Krantz2022 suggests an emergent ferromagnetism with time-reversal symmetry breaking. Additionally, at superconducting KTaO3 heterointerfaces, the in-plane azimuthal angle-dependent magnetoresistance and the superconducting critical field exhibit striking twofold symmetric oscillations deep inside the superconducting phase, whereas the anisotropy vanishes in the normal phase, as highlighted in our recent notable study ref26 . This observation indicates the intrinsic nature of the mixed-parity superconducting ground state with an admixture of -wave and -wave pairing components inherent to the inversion symmetry breaking at the KTaO3 heterointerfaces ref26 . Although the component of -wave pairing could be theoretically stabilized by the long-range ferromagnetic order ref32 ; Zou2020 , the existence of ferromagnetism at superconducting KTaO3 heterointerfaces, akin to the observation at superconducting SrTiO3 heterointerfaces ref11 ; ref12 ; ref13 , is highly desired to examine by using direct experimental accesses.
In this work, utilizing the measurements of direct current SQUID, we observe a distinct signal of an in-plane ferromagnetic hysteresis loop in the KTaO3 heterointerface superconductor, attributing it to intrinsic ferromagnetism that persists above room temperature. Moreover, the first-principles calculations and X-ray magnetic circular dichroism (XMCD) measurements provide decisive evidences in support of the robust ferromagnetism of superconducting KTaO3 heterointerfaces, which derives from the local moments of the Ta4+: ions brought about by the oxygen vacancies that host the two-dimensional electron gases formed at the KTaO3 heterointerfaces, which are responsible for the emergence of interfacial superconductivity. Remarkably, these findings indicate the coexistence of ferromagnetism and superconductivity at the KTaO3 heterointerfaces, offering novel insights into the intricate superconducting properties at these interfaces.
RESULTS AND DISCUSSION
Both the LaAlO3 and YAlO3 thin films are grown by pulsed laser deposition on top of the single-crystalline KTaO3(111) substrates (see Methods in Supporting Information). Atomic force microscopy (AFM) characterization reveals that the surface of KTaO3 substrates and thin films are atomically flat (see Figure S1, YAlO3 shown in Ref. ref26, ), suggesting a high-quality growth of the thin films on KTaO3. On the other hand, X-ray diffraction (XRD) exposes the absence of epitaxial Bragg reflection peaks in both the LaAlO3 and YAlO3 thin films (see Figure S2, YAlO3 presented in Ref. ref26, ), confirming the deposition of an amorphous phase for both the LaAlO3 and YAlO3 thin films on the KTaO3(111) substrates. These results align well with previous investigations ref23 ; ref25 ; ref26 . Subsequently, we conduct electrical transport measurements on the devices of the as-grown thin films arranged in Hall bar configurations (see Figure 1a) ref26 ; XueH2022 .
The longitudinal electrical resistances in Figure 1b exhibit metallic behavior from room temperature to 2.5 K for both LaAlO3/KTaO3(111) and YAlO3/KTaO3(111), indicating the formation of two-dimensional electron gases at their heterointerfaces, given that their bulk constituents are nonmagnetic insulators. In addition, the charge carriers in both cases are electrons with an estimated charge carrier density of cm-2 and cm-2, respectively, by the Hall measurements at 5 K (see Figure 1c). Remarkably, the superconducting transitions start at 2.32 K and 2.39 K, and resistances drop to zero at 1.66 K and 1.7 K, respectively, for LaAlO3/KTaO3 and YAlO3/KTaO3. In the LaAlO3/KTaO3(111), the field-dependent shown in Figure S3 yields the upper critical fields 5 T for fields parallel to the sample plane surface and 0.45 T for fields parallel to the crystallographic -axis. Here, is defined as the magnetic field at the midpoint of the electrical resistance transition. The extracted temperature dependence of is shown in Figure S3c, where a large ratio is perceived, suggesting strong anisotropic superconductivity of LaAlO3/KTaO3(111). Quantitatively, the out-of-plane polar angular -dependent at 1.6 K is used to verify this intriguing behavior, as shown in Figure 1d. Using the two-dimensional Tinkham and the three-dimensional anisotropic Ginzburg-Landau models to fit the , given by and , respectively Tinkham1963 ; ref38 , a cusp-like peak is clearly observed at around (see Figure 1d, inset), which is well described by the two-dimensional Tinkham model, as frequently observed in heterointerface superconductivity ref38 ; ref26 ; Zhang2022 and layered transition metal dichalcogenides LuJM ; ref32 . Qualitatively similar results have also been observed in YAlO3/KTaO3 ref26 , unambiguously demonstrating the intrinsic two-dimensional superconductivity at the KTaO3 heterointerfaces.
To further examine the intrinsic interfacial superconductivity at the KTaO3 heterointerfaces, we conduct measurements of the current-voltage (-) characteristics at various temperatures near (see Figure 1e). These characteristics, depicted on a log-log scale in Figure 1f, reveal a distinct critical current of 79.1 A at 1.4 K, below . The gradually decreases with increasing , eventually vanishing, indicating a transition from superconducting to normal phases. In the normal phase, we have according to Ohm’s law. However, a steeper power law emerges as drops. Following the Berezinskii-Kosterlitz-Thouless (BKT) definition Kosterlitz ; Beasley , the transition temperature corresponds to the dissociation of vortex-antivortex pairs. This obeys the universal scaling relation , since the superconducting phase consists of bound vortex-antivortex pairs in two-dimensional superconductors. We determine 1.793 K from where 3 interpolates. Furthermore, can be alternatively evaluated from the formula exp, where and are material parameters Halperin . Applying such a theoretical fit to the measured yields 1.878 K (see Figure S4). As expected, the obtained from these two independent approaches is close to , providing additional evidence for the two-dimensional superconducting nature of the KTaO3 heterointerfaces.
Next, we delve into the magnetic properties of KTaO3 heterointerfaces. Theoretically, the two-dimensional conducting electron gases at the interfaces of KTaO3 heterostructures primarily originate from the partially filled 5 orbitals of the Ta atoms induced by oxygen vacancies ref25 ; ref26 , these vacancies themselves have the potential to induce ferromagnetism. Experimentally, the zero-field-cooling (ZFC) and field-cooling (FC) curves of the as-grown thin films of LaAlO3 and YAlO3, measured at a temperature between 1.8 and 300 K with an applied in-plane field () of 50 Oe, are summarized in Figure S5. The figures exhibit the pronounced separation between the ZFC and FC curves up to 300 K, showing a signature of in-plane ferromagnetism at the superconducting KTaO3 heterointerfaces that persists at room temperature. In Figure 2, the well-defined magnetization-magnetic field () hysteresis loops observed at different temperatures for the LaAlO3/KTaO3 and YAlO3/KTaO3 provide clear evidence of the temperature dependence of long-range ferromagnetic order. Control experiments on an as-received KTaO3 substrate without LaAlO3 or YAlO3 overlayers only show a diamagnetic background (see Figures S6 and S7). Additionally, we conduct X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM)-energy dispersive X-ray spectroscopy (EDS) measurements to actively eliminate concerns related to extrinsic magnetic contamination during sample preparation. As anticipated, the samples exhibit no evidence of magnetic elements, such as Fe, Co, Mn, Ni or Cr, as shown in Figures S8 and S9. As a consequence, we attribute the universally and consistently observed distinct ferromagnetic signal depicted in Figure 2 to the intrinsic nature of the KTaO3 heterointerfaces. Specifically, we attribute the emergence of two-dimensional ferromagnetism to the Ta electrons induced by the high concentration of oxygen vacancies at the KTaO3 heterointerfaces ref25 . This observation is noteworthy because their bulk counterparts are typical nonmagnetic insulators. It is also important to note that the distinction contrasts with a previous report, in which the ferromagnetic response originates from an extrinsic magnetic thin film of EuO ref42 ; NPChen2024 .
Furthermore, we actively compare the in-plane and out-of-plane loop SQUID measurements of the LaAlO3/KTaO3 and YAlO3/KTaO3 (see Figures S10-S13). These measurements indicate that the temperature dependence of the long-range ferromagnetic order aligns with the in-plane orientation of the KTaO3 heterointerfaces, a consistency observed with the results from the first-principles calculations (see also the first-principles calculations below for a comprehensive analysis) and the anomalous Hall effect and the in-plane field-dependent magnetoresistance with butterfly-like hysteresis (see Figure S14). In addition, we quantify the in-plane magnetization of the itinerant electron gases formed at the KTaO3 heterointerfaces, revealing a magnitude of approximately 0.2 per interface unit cell (if we attribute all the magnetization to the interface). It is interesting to indicate that the KTaO3 heterointerfaces display a non-monotonic behavior in temperature-dependent magnetization (see Figure 2 and Figure S15). This non-monotonic pattern, also observed in previously explored LaAlO3/SrTiO3 ref10 and VSe2 monolayers on van der Waals substrates Bonilla , is attributed to the structural phase and charge-density-wave transitions, respectively. Since KTaO3 shares a number of properties in common with SrTiO3 ref26 , the observed non-monotonic temperature-dependent magnetization at KTaO3 heterointerfaces may be also attributed to the structural phase transitions located at the heterointerfaces. This non-monotonicity underscores the critical role of the KTaO3 surface and its phase transition in the origin of these emergent magnetic properties, and LaAlO3 or YAlO3 overlayers significantly amplify these effects by forming two-dimensional electron gases at the KTaO3 heterointerfaces ref10 . Further experimental efforts would be needed to confirm this underlying nature of the observed non-monotonicity in temperature-dependent magnetization. Moreover, at the lowest temperature of this measurement limited = 1.8 K, which is also lower than [2.32 K for LaAlO3/KTaO3(111) and 2.39 K for YAlO3/KTaO3(111)], the conspicuous signal of in-plane ferromagnetic hysteresis loops is reproducibly observed in the superconducting transition regime (see Figure 2), and the magnetization does not seem to be expelled entirely below . These universal and striking results are strongly reminiscent of the superconducting KTaO3 heterointerfaces spatially coexisting ferromagnetic order Pfleiderer (see also Figure S14). Therefore, we experimentally suggest the coexistence of ferromagnetism and superconductivity at the KTaO3 heterointerfaces, which has also long been a topic of interest sought in nanoscience and nanotechnology communities Ghosh .
To deepen our understanding of the intrinsic ferromagnetism emerging at the KTaO3 heterointerfaces, we delve into the electronic and magnetic properties using the first-principles calculations (see Methods in Supporting Information). For simplicity, we establish a theoretical model with the superlattice (KTaO3)6/(LaAlO3)6(111) comprising a supercell of six layers each for LaAlO3 and KTaO3, despite the amorphous phase of LaAlO3 thin films grown on KTaO3(111) substrates (see Figure S2), as schematically illustrated in Figure S16a. Interestingly, in the stoichiometric heterostructure (KTaO3)6/(LaAlO3)6(111), devoid of oxygen vacancy, the calculated layer-dependent projected density-of-states (PDOS) reveal that the system is a nonmagnetic band insulator with an energy band gap of 3.0 eV (see Figure S16), consistent with previous studies Fujii1976 . This result indicates that the emergent two-dimensional electron gases at the KTaO3 heterointerfaces are unlikely to stem from the diverging Coulomb field due to the polarity of individual layers of LaAlO3 and KTaO3, but rather from the presence of oxygen vacancies.
Principally, each oxygen vacancy donates two electrons into the LaAlO3/KTaO3(111) interface. In turn, the induced interface charges are typically spread over adjacent layers, giving rise to a Ta4+O2-Ta5+-like electronic configuration, which corresponds to several partially filled Ta 5 sub-bands that can lead to interfacial ferromagnetism. As expected, density functional theory calculations show that in the presence of oxygen vacancies (OV, denoted by red dotted circle shown in Figure 3a), the system behaves as a ferromagnetic metal with the conducting electrons mainly derived from the Ta 5 orbitals partially hybridized with the oxygen 2 orbitals (see Figure S17), which are responsible for the emergence of two-dimensional superconductivity ref23 ; Bruno2019 . Furthermore, Figure 3b,c show the spin-resolved PDOS for Ta atoms associated with the value of the magnetic moments of each Ta layer. The calculated magnetic moment of Ta, brought about by the nearby oxygen vacancy, is about 0.124 (see Figure 3c). These calculated results align qualitatively and quantitatively with the magnetization measurements presented in Figure 2, affirming the intrinsic nature of the long-range ferromagnetic order at the KTaO3 heterointerface. Additionally, it is noteworthy that we have adjusted the electron correlation effect of Ta 5 orbitals through the simplified on-site repulsion strength on Ta 5 orbitals Pentcheva . This adjustment yields a magnetic moment that closely corresponds to the experimental findings (see Figure 3c and Figure S18).
Experimentally, we independently conduct synchrotron XMCD measurements (see Methods in Supporting Information) to further investigate whether the interfacial ferromagnetism stems from the intrinsic spin polarization of Ta 5 electrons at the KTaO3 heterointerfaces, utilizing the element-specific technique and high sensitivity of XMCD. In Figure 4, we present the XMCD spectra near the Ta N3 absorption edge for a representative LaAlO3/KTaO3(111) sample at a temperature 15 K under an in-plane magnetic field. Remarkably, the reproducible dichroism features appeared only near the absorption peaks (see Figure 4b) are discernable that resemble XMCD signals were observed at LaAlO3/SrTiO3 heterointerfaces JSLeeNM , strongly indicating that these XMCD signals are indeed originating from the intrinsic spin polarization of the Ta electrons. It is worth emphasizing that the magnetic behavior observed via Ta XMCD aligns with the SQUID measurements presented in Figure 2.
To further control our experiments, we also re-prepare and post-anneal the LaAlO3/KTaO3(111) under various oxygen partial pressures (PO2) to effectively modulate the oxygen vacancies, thereby strengthening the theoretical scenario of emergent ferromagnetism induced by these vacancies, as illustrated in Figure 5. As expected from our intuitions, the increase in PO2 gradually fills oxygen vacancies at the KTaO3 heterointerfaces. This results in the enhancement of Rs (see Figure 5a) in the two-dimensional electron gases, accompanied by a substantial reduction in both charge carrier density (see Figure 5b) and ferromagnetization (see Figure 5c,d). Notably, the magnetic response for the LaAlO3/KTaO3 post-annealed at a PO2 of 1 mbar is significantly diminished, exhibiting an almost vanishing magnetic hysteresis loop (see Figure 5d). This underscores the pivotal role of oxygen vacancies in the emergence of interfacial ferromagnetism. Consequently, these independent and complementary electrical transport and magnetization measurements provide a robust and compelling evidence for that the ferromagnetic Ta at the superconducting KTaO3 heterointerfaces is distinctly linked to the partially filled 5 electrons brought about by the oxygen vacancies.
Physically, since the conducting bands at the Fermi energy at the KTaO3 heterointerfaces are predominantly Ta 5 orbitals, and the distinct ferromagnetism and superconductivity derive from the same Ta 5 electrons both theoretically and experimentally (see Figures 3 and 4), it is suggested that the superconductivity at the KTaO3 heterointerfaces could spatially coexist with the ferromagnetism at low temperatures. In addition, a notable observation in Figure 2 is the two-dimensional superconductivity developed inside a ferromagnetic phase at the KTaO3 heterointerfaces, implying that the ferromagnetism likely plays a crucial role in mediating the superconducting Cooper pairs Ghosh . Significantly, the KTaO3 heterointerfaces reveal mixed-parity superconductivity with an admixture of -wave and -wave pairings ref26 , compatible with the coexisting ferromagnetism. Moreover, it is intriguing that the KTaO3 heterointerfaces exhibit the highest of superconductivity among ferromagnetic EuO overlayer ref23 ; Hua2022 , suggesting that ferromagnetism may reinforce superconductivity. As a consequence, these complementary findings support the coexistence of ferromagnetism and superconductivity at the KTaO3 heterointerfaces (see also Figure S14). The superconductivity observed at the KTaO3 heterointerfaces is thus likely to be of nontrivial nature with broken time-reversal symmetry Stewart , making it promising for potential applications in topological quantum computing Nayak ; Alicea ; Beenakker ; Elliott .
CONCLUSION
In summary, we have experimentally developed two-dimensional superconducting heterointerfaces of KTaO3 and uncovered remarkable in-plane ferromagnetic hysteresis loops that persists above room temperature. Additionally, we conduct the first-principles calculations and XMCD measurements to elucidate further the intrinsic ferromagnetism emerging at the heterointerfaces of KTaO3. These intriguing findings highlight KTaO3 heterointerfaces as time-reversal symmetry breaking superconductors. Our results therefore pave the way to further experimental and theoretical studies aimed at unraveling the intricate interplay among strong spin-orbit coupling, ferromagnetism, and superconductivity at the newly discovered KTaO3 heterointerfaces.
Supporting Information
The Supporting Information is available free of charge at online.
Methods; Large-area AFM images of thin films and KTaO3 substrates; XRD images of thin films and KTaO3 substrates; Anisotropic superconductivity of LaAlO3/KTaO3(111); Extrapolated BKT superconducting transition temperature; Temperature-dependent magnetization of KTaO3 heterointerfaces; In-plane magnetization of KTaO3 substrates; Out-of-plane magnetization of KTaO3 substrates; XPS of KTaO3 heterointerface and KTaO3 substrate; SEM of KTaO3 heterointerfaces; In-plane magnetization of LaAlO3/KTaO3(111); In-plane magnetization of YAlO3/KTaO3(111); Out-of-plane magnetization of LaAlO3/KTaO3(111); Out-of-plane magnetization of YAlO3/KTaO3(111); Field-dependent electrical characteristics of magnetization; High temperature-dependent in-plane magnetization for LaAlO3/KTaO3(111); Electronic and magnetic properties of KTaO3 heterointerfaces; Calculated PDOS of (LaAlO3)6/(KTaO3)6(111) with an oxygen vacancy; Effective dependence of magnetic moments.
AUTHOR INFORMATION
∗Corresponding Author
Shan Qiao, Email: qiaoshan@mail.sim.ac.cn
Gang Mu, Email: mugang@mail.sim.ac.cn
Yan Chen, Email: yanchen99@fudan.edu.cn
Wei Li, Email: wli@fudan.edu.cn
Author Contributions
Z.N., J.Q., and Y.L. contributed equally to this work. W.L. and Y.C. conceived the project and designed the experiments. Z.N. and G.Z. grew the samples. Z.N., Y.L., F.C., G.Z., and G.M. performed the electrical transport measurements. Z.N. and Y.L. performed the magnetization measurements. M.Z., L.D., and S.Q. performed the XMCD measurement. X.Y. and Q.G. performed the XPS measurement. X.Y., Q.G., and H.J. performed the SEM measurement. W.P. and Y.C. assisted the magnetization, electrical transport and SEM experiments. J.Q. performed the first-principles calculations. W.L. wrote the paper with input from Z.N. and J.Q.. All authors discussed the results and gave approval to the final version of the manuscript.
Notes
The authors declare no competing financial interest.
Acknowledgements
This work is supported by the National Natural Science Foundation of China (Grant Nos. 11927807 and U2032207) and Shanghai Science and Technology Committee (Grant Nos. 23ZR1404600 and 20DZ1100604). The authors also thank beamline BL07U of the Shanghai Synchrotron Radiation Facility (SSRF).
References
- (1) Mannhart, J.; Schlom, D. G. Oxide interfaces–An opportunity for electronics. Science 2010, 327, 1607-1611.
- (2) Zubko, P.; Gariglio, S.; Gabay, M.; Ghosez, P.; Triscone, J.-M. Interface physics in complex oxide heterostructures. Annu. Rev. Condens. Matter Phys. 2011, 2, 141-165.
- (3) Hwang, H. Y.; Iwasa, Y.; Kawasaki, M.; Keimer, B.; Nagaosa, N.; Tokura, Y. Emergent phenomena at oxide interfaces. Nat. Mater. 2012, 11, 103-113.
- (4) Huijben, M.; Brinkman, A.; Koster, G.; Rijnders, G.; Hilgenkamp, H.; Blank, D. H. A. Structure-property relation of SrTiO3/LaAlO3 interfaces. Adv. Mater. 2009, 21, 1665-1677.
- (5) Ohtomo, A.; Hwang, H. Y. A high-mobility electron gas at the LaAlO3/SrTiO3 heterointerface. Nature 2004, 427, 423-426.
- (6) Shalom, M. B.; Sachs, M.; Rakhmilevitch, D.; Palevski, A.; Dagan, Y. Tuning spin-orbit coupling and superconductivity at the SrTiO3/LaAlO3 interface: A magnetotransport study. Phys. Rev. Lett. 2010, 104, 126802.
- (7) Caviglia, A. D.; Gabay, M.; Gariglio, S.; Reyren, N.; Cancellieri, C.; Triscone, J.-M. Tunable Rashba spin-orbit interaction at oxide interfaces. Phys. Rev. Lett. 2010, 104, 126803.
- (8) Soumyanarayanan, A.; Reyren, N.; Fert, A.; Panagopoulos, C. Emergent phenomena induced by spin-orbit coupling at surfaces and interfaces. Nature 2016, 539, 509-517.
- (9) Reyren, N.; Thiel, S.; Caviglia, A. D.; Kourkoutis, L. F.; Hammerl, G.; Richter, C.; Schneider, C. W.; Kopp, T.; Rüetschi, A.-S.; Jaccard, D.; Gabay, M.; Muller, D. A.; Triscone, J.-M.; Mannhart, J. Superconducting interfaces between insulating oxides. Science 2007, 317, 1196-1199.
- (10) Caviglia, A. D.; Gariglio, S.; Reyren, N.; Jaccard, D.; Schneider, T.; Gabay, M.; Thiel, S.; Hammerl, G.; Mannhart, J.; Triscone, J.-M. Electric field control of the LaAlO3/SrTiO3 interface ground state. Nature 2008, 456, 624-627.
- (11) Brinkman, A.; Huijben, M.; Zalk, M. van; Huijben, J.; Zeitler, U.; Maan, J. C.; Wiel, W. G. van der; Rijnders, G.; Blank, D. H. A.; Hilgenkamp, H. Magnetic effects at the interface between non-magnetic oxides. Nat. Mater. 2007, 6, 493-496.
- (12) Ariando; Wang, X.; Baskaran, G.; Liu, Z. Q.; Huijben, J.; Yi, J. B.; Annadi, A.; Barman, A. R.; Rusydi, A.; Dhar, S.; Feng, Y. P.; Ding, J.; Hilgenkamp, H.; Venkatesan, T. Electronic phase separation at the LaAlO3/SrTiO3 interface. Nat. Commun. 2011, 2, 188.
- (13) Li, L.; Richter, C.; Mannhart, J.; Ashoori, R. C. Coexistence of magnetic order and two-dimensional superconductivity at LaAlO3/SrTiO3 interfaces. Nat. Phys. 2011, 7, 762-766.
- (14) Bert, J. A.; Kalisky, B.; Bell, C.; Kim, M.; Hikita, Y.; Hwang, H. Y.; Moler, K. A. Direct imaging of the coexistence of ferromagnetism and superconductivity at the LaAlO3/SrTiO3 interface. Nat. Phys. 2011, 7, 767-771.
- (15) Dikin, D. A.; Mehta, M.; Bark, C. W.; Folkman, C. M.; Eom, C. B.; Chandrasekhar, V. Coexistence of superconductivity and ferromagnetism in two dimensions. Phys. Rev. Lett. 2011, 107, 056802.
- (16) Michaeli, K.; Potter, A. C.; Lee, P. A. Superconducting and ferromagnetic phases in SrTiO3/LaAlO3 oxide interface structures: Possibility of finite momentum pairing. Phys. Rev. Lett. 2012, 108, 117003.
- (17) Kozii, V.; Fu, L. Odd-parity superconductivity in the vicinity of inversion symmetry breaking in spin-orbit-coupled systems. Phys. Rev. Lett. 2015, 115, 207002.
- (18) Nakosai, S.; Tanaka, Y.; Nagaosa, N. Topological superconductivity in bilayer Rashba system. Phys. Rev. Lett. 2012, 108, 147003.
- (19) Potter, A. C.; Lee, P. A. Engineering a superconductor: Comparison of topological insulator and Rashba spin-orbit-coupled materials. Phys. Rev. B 2011, 83, 184520.
- (20) Fitzsimmons, M. R.; Hengartner, N. W.; Singh, S.; Zhernenkov, M.; Bruno, F. Y.; Santamaria, J.; Brinkman, A.; Huijben, M.; Molegraaf, H. J. A.; Venta, J. de la; Schuller, I. K. Upper limit to magnetism in LaAlO3/SrTiO3 heterostructures. Phys. Rev. Lett. 2011, 107, 217201.
- (21) Salman, Z.; Ofer, O.; Radovic, M.; Hao, H.; Shalom, M. B.; Chow, K. H.; Dagan, Y.; Hossain, M. D.; Levy, C. D. P.; MacFarlane, W. A.; Morris, G. M.; Patthey, L.; Pearson, M. R.; Saadaoui, H.; Schmitt, T.; Wang, D.; Kiefl, R. F. Nature of weak magnetism in SrTiO3/LaAlO3 multilayers. Phys. Rev. Lett. 2012, 109, 257207.
- (22) Liu, C.; Yan, X.; Jin, D.; Ma, Y.; Hsiao, H.-W.; Lin, Y.; Bretz-Sullivan, T. M.; Zhou, X.; Pearson, J.; Fisher, B.; Jiang, J. S.; Han, W.; Zuo, J.-M.; Wen, J.; Fong, D. D.; Sun, J.; Zhou, H.; Bhattacharya, A. Two-dimensional superconductivity and anisotropic transport at KTaO3 (111) interfaces. Science 2021, 371, 716-721.
- (23) Chen, Z.; Liu, Z.; Sun, Y.; Chen, X.; Liu, Y.; Zhang, H.; Li, H.; Zhang, M.; Hong, S.; Ren, T.; Zhang, C.; Tian, H.; Zhou, Y.; Sun, J.; Xie, Y. Two-dimensional superconductivity at the LaAlO3/KTaO3(110) heterointerface. Phys. Rev. Lett. 2021, 126, 026802.
- (24) Zhang, G.; Wang, L.; Wang, J.; Li, G.; Huang, G.; Yang, G.; Xue, H.; Ning, Z.; Wu, Y.; Xu, J.-P.; Song, Y.; An, Z.; Zheng, C.; Shen, J.; Li, J.; Chen, Y.; Li, W. Spontaneous rotational symmetry breaking in KTaO3 interface superconductor. Nat. Commun. 2023, 14, 3046.
- (25) Ueno, K.; Nakamura, S.; Shimotani, H.; Yuan, H. T.; Kimura, N.; Nojima, T.; Aoki, H.; Iwasa, Y.; Kawasaki, M. Discovery of superconductivity in KTaO3 by electrostatic carrier doping. Nat. Nanotechnol. 2011, 6, 408-412.
- (26) Bruno, F. Y.; Walker, S. M.; Riccò, S.; Torre, A. de la; Wang, Z.; Tamai, A.; Kim, T. K.; Hoesch, M.; Bahramy, M. S.; Baumberger, F. Band structure and spin-orbital texture of the (111)-KTaO3 2D electron gas. Adv. Electron. Mater. 2019, 5, 1800860.
- (27) Mallik, S.; Ménard, G. C.; Saïz, G.; Witt, H.; Lesueur, J.; Gloter, A.; Benfatto, L.; Bibes, M.; Bergeal, N. Superfluid stiffness of a KTaO3-based two-dimensional electron gas. Nat. Commun. 2022, 13, 4625.
- (28) Hua, X.; Meng, F.; Huang, Z.; Li, Z.; Wang, S.; Ge, B.; Xiang, Z.; Chen, X. Tunable two-dimensional superconductivity and spin-orbit coupling at the EuO/KTaO3(110) interface. npj Quantum Mater. 2022, 7, 97.
- (29) Arnault, E. G.; Al-Tawhid, A. H.; Salmani-Rezaie, S.; Muller, D. A.; Kumah, D. P.; Bahramy, M. S.; Finkelstein, G.; Ahadi, K. Anisotropic superconductivity at KTaO3(111) interfaces. Sci. Adv. 2023, 9, eadf1414.
- (30) Al-Tawhid, A. H.; Poage, S. J.; Salmani-Rezaie, S.; Gonzalez, A.; Chikara, S.; Muller, D. A.; Kumah, D. P.; Gastiasoro, M. N.; Lorenzana, J.; Ahadi, K. Enhanced critical field of superconductivity at an oxide interface. Nano Lett. 2023, 23, 6944-6950.
- (31) Al-Tawhid, A. H.; Kanter, J.; Hatefipour, M.; Irving, D. L.; Kumah, D. P.; Shabani, J.; Ahadi, K. Oxygen vacancy-induced anomalous Hall effect in a nominally non-magnetic oxide. J. Electron. Mater. 2022, 51, 7073-7077.
- (32) Krantz, P. W.; Tyner, A.; Goswami, P.; Chandrasekhar, V. Intrinsic magnetism in KTaO3 heterostructures. Appl. Phys. Lett. 2024, 124, 093102.
- (33) Jiang, D.; Yuan, T.; Wu, Y.; Wei, X.; Mu, G.; An, Z.; Li, W. Strong in-plane magnetic field induced reemergent superconductivity in the van der Waals heterointerface of NbSe2 and CrCl3. ACS Appl. Mater. Interfaces 2020, 12, 49252-49257.
- (34) Zou, M.; Chu, J.; Zhang, H.; Yuan, T.; Cheng, P.; Jin, W.; Jiang, D.; Xu, X.; Yu, W.; An, Z.; Wei, X.; Mu, G.; Li, W. Evidence for ferromagnetic order in the CoSb layer of LaCoSb2. Phys. Rev. B 2020, 101, 155138.
- (35) Xue, H.; Wang, L.; Wang, Z.; Zhang, G.; Peng, W.; Wu, S.; Gao, C.-L.; An, Z.; Chen, Y.; Li, W. Fourfold symmetric superconductivity in spinel oxide LiTi2O4(001) thin films. ACS Nano 2022, 16, 19464-19471.
- (36) Tinkham, M. Effect of fluxoid quantization on transitions of superconducting films. Phys. Rev. 1963, 129, 2413-2422.
- (37) Wang, L.; He, W.; Huang, G.; Xue, H.; Zhang, G.; Mu, G.; Wu, S.; An, Z.; Zheng, C.; Chen, Y.; Li, W. Two-dimensional superconductivity at the titanium sesquioxide heterointerface. ACS Nano 2022, 16, 16150-16157.
- (38) Zhang, G.; Liu, Y.; Li, G.; Wang, J.; Wu, Y.; Wang, L.; Xue, H.; Ning, Z.; Gao, C.; An, Z.; Li, J.; Shen, J.; Mu, G.; Chen, Y.; Li, W. Quantum metallic state in the titanium sesquioxide heterointerface superconductor. arXiv:2211.04035 (2022).
- (39) Lu, J. M.; Zheliuk, O.; Leermakers, I.; Yuan, N. F. Q.; Zeitler, U.; Law, K. T.; Ye, J. T. Evidence for two-dimensional Ising superconductivity in gated MoS2. Science 2015, 350, 1353-1357.
- (40) Kosterlitz, J. M.; Thouless, D. J. Long range order and metastability in two dimensional solids and superfluids. J. Phys.: Condens. Matter 1972, 5, L124-L126.
- (41) Beasley, M. R.; Mooij, J. E.; Orlando, T. P. Possibility of vortex-antivortex pair dissociation in two-dimensional superconductors. Phys. Rev. Lett. 1979, 42, 1165-1168.
- (42) Halperin, B. I.; Nelson, D. R. Resistive transition in superconducting films. J. Low Temp. Phys. 1979, 36, 599-616.
- (43) Zhang, H.; Yun, Y.; Zhang, X.; Zhang, H.; Ma, Y.; Yan, X.; Wang, F.; Li, G.; Li, R.; Khan, T.; Chen, Y.; Liu, W.; Hu, F.; Liu, B.; Shen, B.; Han, W.; Sun, J. High-mobility spin-polarized two-dimensional electron gases at EuO/KTaO3 interfaces. Phys. Rev. Lett. 2018, 121, 116803.
- (44) Hua, X.; Zeng, Z.; Meng, F.; Yao, H.; Huang, Z.; Long, X.; Li, Z.; Wang, Y.; Wang, Z.; Wu, T.; Weng, Z.; Wang, Y.; Liu, Z.; Xiang, Z.; Chen, X. Superconducting stripes induced by ferromagnetic proximity in an oxide heterostructure. Nat. Phys. 2024.
- (45) Bonilla, M.; Kolekar, S.; Ma, Y.; Diaz, H. C.; Kalappattil, V.; Das, R.; Eggers, T.; Gutierrez, H. R.; Phan, M.-H.; Batzill, M. Strong room-temperature ferromagnetism in VSe2 monolayers on van der Waals substrates. Nat. Nanotechnol. 2018, 13, 289-293.
- (46) Pfleiderer, C. Superconducting phases of -electron compounds. Rev. Mod. Phys. 2009, 81, 1551-1624.
- (47) Ghosh, S. K.; Smidman, M.; Shang, T.; Annett, J. F.; Hillier, A. D.; Quintanilla, J.; Yuan, H. Recent progress on superconductors with time-reversal symmetry breaking. J. Phys.: Condens. Matter 2021, 33, 033001.
- (48) Fujii, Y.; Sakudo, T. Dielectric and optical properties of KTaO3. J. Phys. Soc. Jpn. 1976, 41, 888-893.
- (49) Pentcheva, R.; Pickett, W. E. Correlation-driven charge order at the interface between a Mott and a band insulator. Phys. Rev. Lett. 2007, 99, 016802.
- (50) Lee, J.-S.; Xie, Y. W.; Sato, H. K.; Bell, C.; Hikita, Y.; Hwang, H. Y.; Kao, C.-C. Titanium ferromagnetism at the LaAlO3/SrTiO3 interface. Nat. Mater. 2013, 12, 703-706.
- (51) Stewart, G. R. Unconventional superconductivity. Adv. Phys. 2017, 66, 75-196.
- (52) Nayak, C.; Simon, S. H.; Stern, A.; Freedman, M.; Sarma, S. D. Non-Abelian anyons and topological quantum computation. Rev. Mod. Phys. 2008, 80, 1083-1159.
- (53) Alicea, J. New directions in the pursuit of Majorana fermions in solid state systems. Rep. Prog. Phys. 2012, 75, 076501.
- (54) Beenakker, C. W. J. Search for Majorana fermions in superconductors. Annu. Rev. Condens. Matter Phys. 2013, 4, 113-136.
- (55) Elliott, S. R.; Franz, M. Majorana fermions in nuclear, particle, and solid-state physics. Rev. Mod. Phys. 2015, 87, 137-163.