Highly Active Nanoperovskite Catalysts for Oxygen Evolution Reaction: Insights into Activity and Stability of Ba0.5Sr0.5Co0.8Fe0.2O3 and PrBaCo2O6
Authors:
Bae Jung Kim,
Xi Cheng,
Daniel Abbott,
Emiliana Fabbri,
Francesco Bozza,
Thomas Graule,
Ivano Castelli,
Luke Wiles,
Nemanja Danilovic,
Katherine Ayers,
Nicola Marzari,
Thomas Schmidt
Abstract:
It is shown that producing PrBaCo2O5 and Ba0.5Sr0.5Co0.8Fe0.2O3 nanoparticle by a scalable synthesis method leads to high mass activities for the oxygen evolution reaction with outstanding improvements by 10 and 50 times, respectively, compared to those prepared via the state of the art synthesis method. Here, detailed comparisons at both laboratory and industrial scales show that Ba0.5Sr0.5Co0.8F…
▽ More
It is shown that producing PrBaCo2O5 and Ba0.5Sr0.5Co0.8Fe0.2O3 nanoparticle by a scalable synthesis method leads to high mass activities for the oxygen evolution reaction with outstanding improvements by 10 and 50 times, respectively, compared to those prepared via the state of the art synthesis method. Here, detailed comparisons at both laboratory and industrial scales show that Ba0.5Sr0.5Co0.8Fe0.2O3 appears to be the most active and stable perovskite catalyst under alkaline conditions, while PrBaCo2O6 reveals thermodynamic instability described by the density functional theory based Pourbaix diagrams highlighting cation dissolution under oxygen evolution conditions. Operando Xray absorption spectroscopy is used in parallel to monitor electronic and structural changes of the catalysts during oxygen evolution reaction. The exceptional BSCF functional stability can be correlated to its thermodynamic metastability under oxygen evolution conditions as highlighted by Pourbaix diagram analysis. BSCF is able to dynamically self reconstruct its surface, leading to formation of Co based oxyhydroxide layers while retaining its structural stability. Differently, PBCO demonstrates a high initial oxygen evolution reaction activity while it undergoes a degradation process considering its thermodynamic instability under oxygen evolution conditions as anticipated by its Pourbaix diagram. Overall, this work demonstrates a synergetic approach of using both experimental and theoretical studies to understand the behavior of perovskite catalysts.
△ Less
Submitted 9 December, 2020;
originally announced December 2020.
-
Effect of lattice volume and strain on the conductivity of BaCeY-oxide ceramic proton conductors
Authors:
Qianli Chen,
Artur Braun,
Songhak Yoon,
Nikolai Bagdassarov,
Thomas Graule
Abstract:
In-situ electrochemical impedance spectroscopy was used to study the effect of lattice volume and strain on the proton conductivity of the yttrium-doped barium cerate proton conductor by applying the hydrostatic pressure up to 1.25 GPa. An increase from 0.62 eV to 0.73 eV in the activation energy of the bulk conductivity was found with increasing pressure during a unit cell volume change of 0.7%,…
▽ More
In-situ electrochemical impedance spectroscopy was used to study the effect of lattice volume and strain on the proton conductivity of the yttrium-doped barium cerate proton conductor by applying the hydrostatic pressure up to 1.25 GPa. An increase from 0.62 eV to 0.73 eV in the activation energy of the bulk conductivity was found with increasing pressure during a unit cell volume change of 0.7%, confirming a previously suggested correlation between lattice volume and proton diffusivity in the crystal lattice. One strategy worth trying in the future development of the ceramic proton conductors could be to expand the lattice and potentially lower the activation energy under tensile strain.
△ Less
Submitted 27 June, 2012;
originally announced June 2012.
-
The effect of compressive strain on the Raman modes of the dry and hydrated BaCe0.8Y0.2O3 proton conductor
Authors:
Qianli Chen,
Tzu-Wen Huang,
Maria Baldini,
Anwar Hushur,
Vladimir Pomjakushin,
Simon Clark,
Wendy L. Mao,
Murli H. Manghnani,
Artur Braun,
Thomas Graule
Abstract:
The BaCe0.8Y0.2O3-δ proton conductor under hydration and under compressive strain has been analyzed with high pressure Raman spectroscopy and high pressure x-ray diffraction. The pressure dependent variation of the Ag and B2g bending modes from the O-Ce-O unit is suppressed when the proton conductor is hydrated, affecting directly the proton transfer by locally changing the electron density of the…
▽ More
The BaCe0.8Y0.2O3-δ proton conductor under hydration and under compressive strain has been analyzed with high pressure Raman spectroscopy and high pressure x-ray diffraction. The pressure dependent variation of the Ag and B2g bending modes from the O-Ce-O unit is suppressed when the proton conductor is hydrated, affecting directly the proton transfer by locally changing the electron density of the oxygen ions. Compressive strain causes a hardening of the Ce-O stretching bond. The activation barrier for proton conductivity is raised, in line with recent findings using high pressure and high temperature impedance spectroscopy. The increasing Raman frequency of the B1g and B3g modes thus implies that the phonons become hardened and increase the vibration energy in the a-c crystal plane upon compressive strain, whereas phonons are relaxed in the b-axis, and thus reveal softening of the Ag and B2g modes. Lattice toughening in the a-c crystal plane raises therefore a higher activation barrier for proton transfer and thus anisotropic conductivity. The experimental findings of the interaction of protons with the ceramic host lattice under external strain may provide a general guideline for yet to develop epitaxial strained proton conducting thin film systems with high proton mobility and low activation energy.
△ Less
Submitted 26 November, 2011;
originally announced November 2011.
-
High temperature oxygen NEXAFS valence band spectra and conductivity of LaFe3/4Ni1/4O3 from 300 K to 773 K
Authors:
Artur Braun,
Selma Erat,
Ahmad K. Ariffin,
Recardo Manzke,
Hiroki Wadati,
Thomas Graule,
Ludwig J. Gauckler
Abstract:
LaFe3/4Ni1/4O3 was subjected to oxygen near edge x-ray absorption fine structure (NEXAFS) spectroscopy for 300 K < T < 773 K. The spectra show in the pre-edge a small hole doped peak originating from Ni substitution. The relative spectral weight of this transition to the weight of the hybridized O(2p) - Fe(3d) transitions scales with T and has a maximum at around 600 K. The characteristic energies…
▽ More
LaFe3/4Ni1/4O3 was subjected to oxygen near edge x-ray absorption fine structure (NEXAFS) spectroscopy for 300 K < T < 773 K. The spectra show in the pre-edge a small hole doped peak originating from Ni substitution. The relative spectral weight of this transition to the weight of the hybridized O(2p) - Fe(3d) transitions scales with T and has a maximum at around 600 K. The characteristic energies of the thermal activated spectral intensity and conductivity suggest that the concentration of charge transferred electrons from O(2p) to Ni(3d) increases and that the pre-edges account in part for the polaron activated transport.
△ Less
Submitted 26 November, 2011;
originally announced November 2011.
-
Evolution of structural properties of iron oxide nano particles during temperature treatment from 250°C - 900°C: X-ray diffraction and Fe K-shell pre-edge X-ray absorption study
Authors:
Debajeet K. Bora,
Artur Braun,
Selma Erat,
Olga Safonova,
Thomas Graule,
Edwin C. Constable
Abstract:
Iron oxide nano particles with nominal Fe2O3 stoichiometry were synthesized by a wet, soft chemical method with the heat treatment temperatures from 250°C to 900°C in air. The variation in the structural properties of the nano particles with the heat treatment temperature was studied by X-ray diffraction and Fe K shell X-ray absorption study. X-ray diffractograms show that at lower annealing tempe…
▽ More
Iron oxide nano particles with nominal Fe2O3 stoichiometry were synthesized by a wet, soft chemical method with the heat treatment temperatures from 250°C to 900°C in air. The variation in the structural properties of the nano particles with the heat treatment temperature was studied by X-ray diffraction and Fe K shell X-ray absorption study. X-ray diffractograms show that at lower annealing temperatures nano particle comprises both maghemite and hematite phases. With increasing temperature, the remainder of the maghemite phase transformed completely to hematite. Profile analysis of the leading Bragg reflections reveals that the average crystallite size increases from 50 nm to 150 nm with increasing temperature. The mean primary particle size decreased from 105 nm to 90 nm with increasing heat treatment temperature. The X-ray diffraction results are paralleled by systematic changes in the pre-edge structure of the Fe K-edge X-ray absorption spectra, in particular by a gradual decrease of the t2g/eg peak height ratio of the two leading pre-edge resonances, confirming oxidation of the Fe from Fe2+ towards Fe3+. Transmission electron microscopy (TEM) on the samples treated at temperatures as high as 900°C showed particles with prismatic morphology along with the formation of stacking fault like defects. High resolution TEM with selected area electron diffraction (SAED) of samples heat treated above 350°C showed that the nano particles have well developed lattice fringes corresponding to that of (110) plane of hematite.
△ Less
Submitted 26 November, 2011;
originally announced November 2011.
-
Proton diffusivity in the BaZr0.9Y0.1O3-δ proton conductor
Authors:
Artur Braun,
Sophie Duval,
Peter Ried,
Jan Embs,
Fanni Juranyi,
Thierry Strässle,
Ulrich Stimming,
Rolf Hempelmann,
Peter Holtappels,
Thomas Graule
Abstract:
The thermally activated proton diffusion in BaZr0.9Y0.1O3-δ was studied with electrochemical impedance spectroscopy (IS) and quasi-elastic neutron scattering (QENS) in the temperature range from 300 K to 900 K. The diffusivities for the bulk material and the grain boundaries as obtained by IS obey an Arrhenius law with activation energies of 0.46 eV and 1.21 eV, respectively. The activation energi…
▽ More
The thermally activated proton diffusion in BaZr0.9Y0.1O3-δ was studied with electrochemical impedance spectroscopy (IS) and quasi-elastic neutron scattering (QENS) in the temperature range from 300 K to 900 K. The diffusivities for the bulk material and the grain boundaries as obtained by IS obey an Arrhenius law with activation energies of 0.46 eV and 1.21 eV, respectively. The activation energies obtained by IS for the bulk are 0.26 eV above 700 K and 0.46 eV, below 700 K. The total diffusivity as obtained by IS is by one order of magnitude lower than the microscopic diffusivity as obtained by QENS. The activation energies obtained by QENS are 0.13 eV above 700 K and 0.04 eV, below 700 K. At about 700 K, the diffusion constants for IS and QENS have a remarkable crossover, suggesting two processes with different activation energies.
△ Less
Submitted 9 June, 2011;
originally announced June 2011.
-
Protons in lattice confinement: Static pressure on the Y-substituted, hydrated BaZrO3 ceramic proton conductor decreases proton mobility
Authors:
Qianli Chen,
Artur Braun,
Alejandro Ovalle,
Cristian-Daniel Savaniu,
Thomas Graule,
Nikolai Bagdassarov
Abstract:
Yttrium substituted BaZrO3, with nominal composition BaZr0.9Y0.1O3, a ceramic proton conductor, was subject to impedance spectroscopy for temperatures 300 K < T < 715 K at mechanical pressures 1 GPa < p < 2 GPa. The activation energies Ea of bulk and grain boundary conductivity from two perovskites synthesized by solid-state reaction and sol-gel method were determined under high pressures. At high…
▽ More
Yttrium substituted BaZrO3, with nominal composition BaZr0.9Y0.1O3, a ceramic proton conductor, was subject to impedance spectroscopy for temperatures 300 K < T < 715 K at mechanical pressures 1 GPa < p < 2 GPa. The activation energies Ea of bulk and grain boundary conductivity from two perovskites synthesized by solid-state reaction and sol-gel method were determined under high pressures. At high temperature, the bulk activation energy increases with pressure by 5% for sol-gel derived sample and by 40% for solid-state derived sample. For the sample prepared by solid-state reaction, there is a large gap of 0.17 eV between the activation energy at 1.0 GPa and > 1.2 GPa. The grain boundary activation energy is around a factor two times as that of the bulk, and it reaches a maximum at 1.25 - 1.5 GPa, and then decrease as the pressure increases, indicating higher proton mobility in the grain boundaries at higher pressure. Since this effect is not reversible, it is suggested that the grain boundary resistance decreases as a result of pressure induced sintering. The steady increase of the bulk resistivity upon pressurizing suggests that the proton mobility depends on the space available in the lattice. In return, an expanded lattice with a/a0 > 1 should thus have a lower activation energy, suggesting that thin films expansive tensile strain could have a larger proton conductivity with desirable properties for applications.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Evolution of an oxygen NEXAFS transition in the upper Hubbard band in α-Fe2O3 upon electrochemical oxidation
Authors:
Debajeet K. Bora,
Artur Braun,
Selma Erat,
Romy Löhnert,
Kevin Sivula,
Jörg Töpfer,
Michael Grätzel,
Thomas Graule,
Edwin Constable
Abstract:
Electrochemical oxidation of hematite (α-Fe2O3) nano-particulate films at 600 mV vs. Ag+/AgCl reference in KOH electrolyte forms a species at the hematite surface which causes a new transition in the upper Hubbard band between the Fe(3d)-O(2p) state region and the Fe(4sp)-O(2p) region, as evidenced by oxygen near edge x-ray absorption fine structure (NEXAFS) spectra. The electrochemical origin of…
▽ More
Electrochemical oxidation of hematite (α-Fe2O3) nano-particulate films at 600 mV vs. Ag+/AgCl reference in KOH electrolyte forms a species at the hematite surface which causes a new transition in the upper Hubbard band between the Fe(3d)-O(2p) state region and the Fe(4sp)-O(2p) region, as evidenced by oxygen near edge x-ray absorption fine structure (NEXAFS) spectra. The electrochemical origin of this transition suggests that it is related with a surface state. This transition, not known for pristine α-Fe2O3 is at about the same x-ray energy, where pristine 1% Si doped Si:Fe2O3 has such transition. Occurrence of this state coincides with the onset of an oxidative dark current wave at around 535 mV - a potential range, where the tunneling exchange current has been previously reported to increase by three orders of magnitude with the valence band and the transfer coefficient by a factor of 10. Oxidation to only 200 mV does not form such extra NEXAFS feature, supporting that a critical electrochemical potential between 200 and 600 mV is necessary to change the electronic structure of the iron oxide at the surface. Decrease of the surface roughness, as suggested by visual inspection, profilometry and x-ray reflectivity, points to faceting as potential structural origin of the surface state.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Fe-resonant valence band photoemission and oxygen NEXAFS study on La1-xSrxFe0.75Ni0.25O3-δ
Authors:
Selma Erat,
Hiroki Wadati,
Funda Aksoy,
Zhi Liu,
Thomas Graule,
Ludwig J. Gauckler,
Artur Braun
Abstract:
Iron resonant valance band photoemission spectra of Sr substituted LaFe0.75Ni0.25 O3-δ have been recorded across the Fe 2p - 3d absorption threshold to obtain Fe specific spectral information on the 3d projected partial density of states. Comparison with La1-xSrxFeO3 resonant VB PES literature data suggests that substitution of Fe by Ni forms electron holes which are mainly O 2p character. Substit…
▽ More
Iron resonant valance band photoemission spectra of Sr substituted LaFe0.75Ni0.25 O3-δ have been recorded across the Fe 2p - 3d absorption threshold to obtain Fe specific spectral information on the 3d projected partial density of states. Comparison with La1-xSrxFeO3 resonant VB PES literature data suggests that substitution of Fe by Ni forms electron holes which are mainly O 2p character. Substitution of La by Sr increases the hole concentration to an extent that the eg structure vanishes. The variation of the eg and t2g structures is paralleled by the changes in the electrical conductivity.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Correlation of conductivity and angle integrated valence band photoemission characteristics in single crystal iron perovskites for 300 K < T < 800 K: Comparison of surface and bulk sensitive methods
Authors:
A. Braun,
B. S. Mun,
Y. Sun,
Z. Liu,
R. Mäder,
S. Erat,
X. Zhang,
S. S. Mao,
E. Pomjakushina,
K. Conder,
L. J. Gauckler,
T. Graule
Abstract:
A single crystal monolith of La0.9Sr0.1FeO3 and thin pulsed laser deposited film of La0.8Sr0.2Fe0.8Ni0.2O3 were subject to angle integrated valence band photoemission spectroscopy in ultra high vacuum and conductivity experiments in ambient air at temperatures from 300 K to 800 K. Except for several sputtering and annealing cycles, the specimen were not prepared in-situ.. Peculiar changes in the t…
▽ More
A single crystal monolith of La0.9Sr0.1FeO3 and thin pulsed laser deposited film of La0.8Sr0.2Fe0.8Ni0.2O3 were subject to angle integrated valence band photoemission spectroscopy in ultra high vacuum and conductivity experiments in ambient air at temperatures from 300 K to 800 K. Except for several sputtering and annealing cycles, the specimen were not prepared in-situ.. Peculiar changes in the temperature dependent, bulk representative conductivity profile as a result of reversible phase transitions, and irreversible chemical changes are semi-quantitatively reflected by the intensity variation in the more surface representative valence band spectra near the Fermi energy. X-ray photoelectron diffraction images reflect the symmetry as expected from bulk iron perovskites. The correlation of spectral details in the valence band photoemission spectra (VB PES) and details of the conductivity during temperature variation suggest that valuable information on electronic structure and transport properties of complex materials may be obtained without in-situ preparation.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Entanglement of charge transfer, hole doping, exchange interaction and octahedron tilting angle and their influence on the conductivity of La1-xSrxFe0.75Ni0.25O3-δ: A combination of x-ray spectroscopy and diffraction
Authors:
Selma Erat,
Artur Braun,
Cinthia Piamonteze,
Zhi Liu,
Alejandro Ovalle,
Hansjürgen Schindler,
Thomas Graule,
Ludwig J. Gauckler
Abstract:
Substitution of La by Sr in the 25% Ni doped charge transfer insulator LaFeO3 creates structural changes that inflect the electrical conductivity caused by small polaron hopping via exchange interactions and charge transfer. The substitution forms electron holes and a structural crossover from orthorhombic to rhombohedral symmetry, and then to cubic symmetry. The structural crossover is accompanie…
▽ More
Substitution of La by Sr in the 25% Ni doped charge transfer insulator LaFeO3 creates structural changes that inflect the electrical conductivity caused by small polaron hopping via exchange interactions and charge transfer. The substitution forms electron holes and a structural crossover from orthorhombic to rhombohedral symmetry, and then to cubic symmetry. The structural crossover is accompanied by a crossover from Fe3+-O2--Fe3+ superexchange interaction to Fe3+-O2--Fe4+ double exchange interaction, as evidenced by a considerable increase of conductivity. These interactions and charge transfer mechanism depend on superexchange angle, which approaches 180° upon increasing Sr concentration, leading an increased overlap between the O (2p) and Fe/Ni (3d) orbitals.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Nitrogen doping of TiO2 photocatalyst forms a second eg state in the Oxygen (1s) NEXAFS pre-edge
Authors:
Artur Braun,
Kranthi K. Akurati,
Giuseppino Fortunato,
Felix A. Reifler,
Axel Ritter,
Ashley S. Harvey,
Andri Vital,
Thomas Graule
Abstract:
Close inspection of the pre-edge in oxygen near-edge x-ray absorption fine structure spectra of single step, gas phase synthesized titanium oxynitride photocatalysts with 20 nm particle size reveals an additional eg resonance in the VB that went unnoticed in previous TiO2 anion doping studies. The relative spectral weight of this Ti(3d)-O(2p) hybridized state with respect to and located between th…
▽ More
Close inspection of the pre-edge in oxygen near-edge x-ray absorption fine structure spectra of single step, gas phase synthesized titanium oxynitride photocatalysts with 20 nm particle size reveals an additional eg resonance in the VB that went unnoticed in previous TiO2 anion doping studies. The relative spectral weight of this Ti(3d)-O(2p) hybridized state with respect to and located between the readily established t2g and eg resonances scales qualitatively with the photocatalytic decomposition power, suggesting that this extra resonance bears co-responsibility for the photocatalytic performance of titanium oxynitrides at visible light wavelengths.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Correlation of high temperature X-ray photoemission spectral features and conductivity of epitaxially strained (La0.8Sr0.2)0.95Ni0.2Fe0.8O3/SrTiO3(110)
Authors:
A. Braun,
X. Zhang,
Y. Sun,
U. Müller,
Z. Liu,
S. Erat,
M. Ari,
H. Grimmer,
S. S. Mao,
T. Graule
Abstract:
Reversible and irreversible discontinuities at around 573 K and 823 K in the electric conductivity of a strained 175 nm thin film of (La0.8Sr0.2)0.95Ni0.2Fe0.8O3-δ grown by pulsed laser deposition on SrTiO3 (110) are reflected by valence band changes as monitored in photoemission and oxygen K-edge x-ray absorption spectra. The irreversible jump at 823 K is attributed to depletion of doped electron…
▽ More
Reversible and irreversible discontinuities at around 573 K and 823 K in the electric conductivity of a strained 175 nm thin film of (La0.8Sr0.2)0.95Ni0.2Fe0.8O3-δ grown by pulsed laser deposition on SrTiO3 (110) are reflected by valence band changes as monitored in photoemission and oxygen K-edge x-ray absorption spectra. The irreversible jump at 823 K is attributed to depletion of doped electron holes and reduction of Fe4+ to Fe3+, as evidenced by oxygen and iron core level soft x-ray spectroscopy, and possibly of a chemical origin, whereas the reversible jump at 573 K possibly originates from structural changes.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
An electron hole doping and soft x-ray spectroscopy study on La1-xSrxFe0.75Ni0.25O3-δ
Authors:
Selma Erat,
Artur Braun,
Alejandro Ovalle,
Cinthia Piamonteze,
Zhi Liu,
Thomas Graule,
Ludwig J. Gauckler
Abstract:
The conductivity of the electron hole and polaron conductor La1-xSrxFe0.75Ni0.25O3-δ, a potential cathode material for intermediate temperature solid oxide fuel cells, was studied for 0 <x < 1 and for temperatures 300 K <T < 1250 K. In LaSrFe-oxide, an ABO3 type perovskite, A-site substitu-tion of the trivalent La3+ by the divalent Sr2+ causes oxidation of Fe3+ towards Fe4+, which forms conducting…
▽ More
The conductivity of the electron hole and polaron conductor La1-xSrxFe0.75Ni0.25O3-δ, a potential cathode material for intermediate temperature solid oxide fuel cells, was studied for 0 <x < 1 and for temperatures 300 K <T < 1250 K. In LaSrFe-oxide, an ABO3 type perovskite, A-site substitu-tion of the trivalent La3+ by the divalent Sr2+ causes oxidation of Fe3+ towards Fe4+, which forms conducting electron holes. Here we have in addition a B-site substitution by Ni. The compound for x = 0.5 is identified as the one with the highest conductivity (σ ~ 678 S/cm) and lowest activation energy for polaron conductivity (Ep = 39 meV). The evolution of the electronic structure was monitored by soft x-ray Fe and oxygen K-edge spectroscopy. Homogeneous trend for the oxida-tion state of the Fe was observed. The variation of the ambient temperature conductivity and activation energy with relative Sr content (x) shows a correlation with the ratio of (eg/eg+t2g) in Fe L3 edge up to x=0.5. The hole doping process is reflected by an almost linear trend by the variation of the pre-peaks of the oxygen K-edge soft x-ray absorption spectra.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Electron hole - phonon interaction and structural changes in La0.9Sr0.1FeO3 by temperature dependent conductivity and valence band photoemission spectros-copy
Authors:
A. Braun,
J. Richter,
A. S. Harvey,
A. Infortuna,
A. Frei,
E. Pomjakushina,
Bongjin S. Mun,
P. Holtappels,
U. Vogt,
K. Conder,
L. J. Gauckler,
T. Graule
Abstract:
Electric conductivity and structural details of the hole-doped polaron conductor La0.9Sr0.1FeO3 (LSF10) are reported. The conductivity of a single crystal shows an exponential increase with temperature with a maxi-mum of 100 S/cm at 700 K and with activation energy of about 375 meV, and a decrease for higher temperatures that follows a power law. The exponential increase of the electric conductivi…
▽ More
Electric conductivity and structural details of the hole-doped polaron conductor La0.9Sr0.1FeO3 (LSF10) are reported. The conductivity of a single crystal shows an exponential increase with temperature with a maxi-mum of 100 S/cm at 700 K and with activation energy of about 375 meV, and a decrease for higher temperatures that follows a power law. The exponential increase of the electric conductivity for 300 K {\leg} T {\leg} 700 is accompanied by a shift of spectral weight in the photoemission valence band towards the Fermi level, indicative of a strong electron-phonon interaction. The subsequent decrease of the conductivity for T > 700 K is accompanied by a reversible phase transformation from orthorhombic to rhombohedral symmetry. The decreasing conductivity for T > 700 K is likely due to the reduction of the iron due to oxygen loss causing a decreasing hole concentration, as evidenced by a substantial chemical shift in the Fe K-shell x-ray absorption spectra. Two additional fine structures in the conductivity data at 357 K, this is, a small temperature reversible jump in the conductivity, and at 573 K, a slight reversible increase of the polaron activation energy, are correlated with an exceptionally strong decrease in spectral valence band intensity near the Fermi level, and with the onset of a corresponding structural transition.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Direct evidence for electron hole depletion in La0.5Sr0.5FeO3-d upon B-site cation doping
Authors:
Artur Braun,
Defne Bayraktar,
Ashley S. Harvey,
Daniel Beckel,
John A. Purton,
Peter Holtappels,
Ludwig J. Gauckler,
Thomas Graule
Abstract:
Partial substitution of Fe by Ta in the hole-doped La0.5Sr0.5FeO3 decreases the electric conductivity by up to three orders of magnitude. This decrease is in immediate correlation with a decrease of the electron hole concentration and a shift of the spectral weight within the O(1s)-Fe(3d) mixed states from eg bands near the Fermi energy to t2g bands. Corresponding differences in the Fe(2p) and O(1…
▽ More
Partial substitution of Fe by Ta in the hole-doped La0.5Sr0.5FeO3 decreases the electric conductivity by up to three orders of magnitude. This decrease is in immediate correlation with a decrease of the electron hole concentration and a shift of the spectral weight within the O(1s)-Fe(3d) mixed states from eg bands near the Fermi energy to t2g bands. Corresponding differences in the Fe(2p) and O(1s) X-ray absorption spectra reveals formation of states with increased covalency in the initial state and states which contain O(2p) character, and that hole states are responsible for transport changes in the material. The intensity ratio of eg and t2g bands appears to be a spectral indicator for hole formation.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.