High temperature internal friction in a Ti-46Al-1Mo-0.2Si intermetallic, comparison with creep behaviour
Authors:
M. Castillo-Rodríguez,
M. L. No,
J. A. Jimenez,
O. A. Ruano,
J. San Juan
Abstract:
Advanced g-TiAl based intermetallics Mo-bearing have been developed to obtain the fine-grained microstructure required for superplastic deformation to be used during further processing. In the present work we have studied an alloy of Ti-46Al-1Mo-0.2Si (at%) with two different microstructures, as-cast material with a coarse grain size above 300 mm, and the hot extruded material exhibiting a grain s…
▽ More
Advanced g-TiAl based intermetallics Mo-bearing have been developed to obtain the fine-grained microstructure required for superplastic deformation to be used during further processing. In the present work we have studied an alloy of Ti-46Al-1Mo-0.2Si (at%) with two different microstructures, as-cast material with a coarse grain size above 300 mm, and the hot extruded material exhibiting a grain size smaller than 20 mm. We have used a mechanical spectrometer especially developed for high temperature internal friction measurements to study the defect mobility processes taking place at high temperature. The internal friction spectra at different frequencies has been studied and analyzed up to 1360 K in order to characterize the relaxation processes appearing in this temperature range. A relaxation peak, with a maximum in between 900 K and 1080 K, depending on the oscillating frequency, has been attributed to Ti-atoms diffusion by the stress-induced reorientation of Al-VTi-Al elastic dipoles. The high temperature background in both microstructural states, as-cast and extruded, has been analyzed, measuring the apparent activation parameters, in particular the apparent energies of Ecast(IF) 4.4 +- 0.05 eV and Eext(IF) 4.75 +- 0.05 eV respectively. These results have been compared to those obtained on the same materials by creep deformation. We may conclude that the activation parameters obtained by internal friction analysis, are consistent with the ones measured by creep. Furthermore, the analysis of the high temperature background allows establish the difference on creep resistance for both microstructural states
△ Less
Submitted 4 February, 2024;
originally announced February 2024.
-
Advanced monitoring of rail breakage in double-track railway lines by means of PCA techniques
Authors:
F. Espinosa,
J. J. García,
A. Hernández,
M. Mazo,
J. Ureña,
J. A. Jiménez,
I. Fernández,
C. Pérez,
J. C. García
Abstract:
This work describes a classifier designed to identify rail breakages in double-track railway lines, completing the electronic equipment carried out by authors. The main objective of this proposal is to guarantee the integrity of tracks before the railway traffic starts working. In addition, it facilitates maintenance tasks providing information about possible breakages. The detection of breakages…
▽ More
This work describes a classifier designed to identify rail breakages in double-track railway lines, completing the electronic equipment carried out by authors. The main objective of this proposal is to guarantee the integrity of tracks before the railway traffic starts working. In addition, it facilitates maintenance tasks providing information about possible breakages. The detection of breakages is based on the analysis of eight currents provided by the electronic equipment, one per rail, at the ends of the section (emitting and receiving nodes). The imbalance that occurs among the value of these currents implies that there is at least a breakage in the track section under analysis. This analysis is conducted according to three phases. The first one identifies whether there is a breakage, and, in that case, the damaged track is identified. The second phase provides information about which rail is broken (internal, external or both of them) in the previously identified track. Finally, if there is only one breakage, the third phase estimates its most likely zone along the track section. This situation is considered as a classification problem, and solved by means of the Principal Component Analysis technique. This means that a significant number of measurements is required for every breakage pattern (types of breakages) to be considered. Due to the difficulty of having real data, the proposal has been validated using an 8km-long double-track hardware simulator specially designed by the authors, with specific localizations for breakages.
△ Less
Submitted 4 February, 2024;
originally announced February 2024.
-
Coupled VO2 oscillators circuit as analog first layer filter in convolutional neural networks
Authors:
Elisabetta Corti,
Joaquin Antonio Cornejo Jimenez,
Kham M. Niang,
John Robertson,
Kirsten E. Moselund,
Bernd Gotsmann,
Adrian M. Ionescu,
Siegfried Karg
Abstract:
In this work we present an in-memory computing platform based on coupled VO2 oscillators fabricated in a crossbar configuration on silicon. Compared to existing platforms, the crossbar configuration promises significant improvements in terms of area density and oscillation frequency. Further, the crossbar devices exhibit low variability and extended reliability, hence, enabling experiments on 4-co…
▽ More
In this work we present an in-memory computing platform based on coupled VO2 oscillators fabricated in a crossbar configuration on silicon. Compared to existing platforms, the crossbar configuration promises significant improvements in terms of area density and oscillation frequency. Further, the crossbar devices exhibit low variability and extended reliability, hence, enabling experiments on 4-coupled oscillator. We demonstrate the neuromorphic computing capabilities using the phase relation of the oscillators. As a application, we propose to replace digital filtering operation in a convolutional neural network with oscillating circuits. The concept is tested with a VGG13 architecture on the MNIST dataset, achieving performances of 95% in the recognition task.
△ Less
Submitted 18 November, 2020;
originally announced November 2020.
-
Confirmation of the Luminous Blue Variable status of MWC 930
Authors:
A. S. Miroshnichenko,
N. Manset,
S. V. Zharikov,
J. Zsargo,
J. A. Juarez Jimenez,
J. H. Groh,
H. Levato,
M. Grosso,
R. J. Rudy,
E. A. Laag,
K. B. Crawford,
R. C. Puetter,
D. E. Reichart,
K. M. Ivarsen,
J. B. Haislip,
M. C. Nysewander,
A. P. LaCluyze
Abstract:
We present spectroscopic and photometric observations of the emission-line star MWC 930 (V446 Sct) during its long-term optical brightening in 2006--2013. Based on our earlier data we suggested that the object has features found in Luminous Blue Variables (LBV), such as a high luminosity (~3 10^5 Lsun, a low wind terminal velocity (~ 140 km/s), and a tendency to show strong brightness variations (…
▽ More
We present spectroscopic and photometric observations of the emission-line star MWC 930 (V446 Sct) during its long-term optical brightening in 2006--2013. Based on our earlier data we suggested that the object has features found in Luminous Blue Variables (LBV), such as a high luminosity (~3 10^5 Lsun, a low wind terminal velocity (~ 140 km/s), and a tendency to show strong brightness variations (~1 mag over 20 years). For the last ~7 years it has been exhibiting a continuous optical and near-IR brightening along with a change of the emission-line spectrum appearance and cooling of the star's photosphere. We present the object's $V$--band light curve, analyze the spectral variations, and compare the observed properties with those of other recognized Galactic LBVs, such as AG Car and HR Car. Overall we conclude the MWC 930 is a bona fide Galactic LBV that is currently in the middle of an S Dor cycle.
△ Less
Submitted 3 April, 2014;
originally announced April 2014.
-
Nanoscale austenite reversion through partitioning, segregation, and kinetic freezing: Example of a ductile 2 GPa Fe-Cr-C steel
Authors:
L. Yuan,
D. Ponge,
J. Wittig,
P. Choi,
J. A. Jiménez,
D. Raabe
Abstract:
Austenite reversion during tempering of a Fe-13.6Cr-0.44C (wt.%) martensite results in an ultrahigh strength ferritic stainless steel with excellent ductility. The austenite reversion mechanism is coupled to the kinetic freezing of carbon during low-temperature partitioning at the interfaces between martensite and retained austenite and to carbon segregation at martensite-martensite grain boundari…
▽ More
Austenite reversion during tempering of a Fe-13.6Cr-0.44C (wt.%) martensite results in an ultrahigh strength ferritic stainless steel with excellent ductility. The austenite reversion mechanism is coupled to the kinetic freezing of carbon during low-temperature partitioning at the interfaces between martensite and retained austenite and to carbon segregation at martensite-martensite grain boundaries. An advantage of austenite reversion is its scalability, i.e., changing tempering time and temperature tailors the desired strength-ductility profiles (e.g. tempering at 400°C for 1 min. produces a 2 GPa ultimate tensile strength (UTS) and 14% elongation while 30 min. at 400°C results in a UTS of ~ 1.75 GPa with an elongation of 23%). The austenite reversion process, carbide precipitation, and carbon segregation have been characterized by XRD, EBSD, TEM, and atom probe tomography (APT) in order to develop the structure-property relationships that control the material's strength and ductility.
△ Less
Submitted 19 February, 2012;
originally announced February 2012.
-
Calculation of the bootstrap current profile for the TJ-II stellarator
Authors:
J. L. Velasco,
K. Allmaier,
A. Lopez-Fraguas,
C. D. Beidler,
H. Maassberg,
W. Kernbichler,
F. Castejon,
J. A. Jimenez
Abstract:
Calculations of the bootstrap current for the TJ-II stellarator are presented. DKES and NEO-MC codes are employed; the latter has allowed, for the first time, the precise computation of the bootstrap transport coefficient in the long mean free path regime of this device. The low error bars allow a precise convolution of the monoenergetic coefficients, which is confirmed by error analysis. The radi…
▽ More
Calculations of the bootstrap current for the TJ-II stellarator are presented. DKES and NEO-MC codes are employed; the latter has allowed, for the first time, the precise computation of the bootstrap transport coefficient in the long mean free path regime of this device. The low error bars allow a precise convolution of the monoenergetic coefficients, which is confirmed by error analysis. The radial profile of the bootstrap current is presented for the first time for the 100_44_64 configuration of TJ-II for three different collisionality regimes. The bootstrap coefficient is then compared to that of other configurations of TJ-II regularly operated. The results show qualitative agreement with toroidal current measurements; precise comparison with real discharges is ongoing.
△ Less
Submitted 7 October, 2011; v1 submitted 18 August, 2011;
originally announced August 2011.