Modulating thermoelectric properties in oxygen-passivated Sb2Te3 thin film through grain boundary engineering
Authors:
Abhishek Ghosh,
Chandan Kumar Vishwakarma,
Prashant Bisht,
Narinder Kaur,
Mujeeb Ahmad,
Bodh Raj Mehta
Abstract:
The present study demonstrates the effectiveness of incorporating oxygen atoms into the Sb2Te3 thin film, leading to an improved power factor and reduction in thermal conductivity. Based on the experimental evidence, it can be inferred that oxygen-related impurities preferentially wet the grain boundary (GB) and introduce a double Schottky barrier at the GB interface, promoting energy-dependent ca…
▽ More
The present study demonstrates the effectiveness of incorporating oxygen atoms into the Sb2Te3 thin film, leading to an improved power factor and reduction in thermal conductivity. Based on the experimental evidence, it can be inferred that oxygen-related impurities preferentially wet the grain boundary (GB) and introduce a double Schottky barrier at the GB interface, promoting energy-dependent carrier scattering, ultimately leading to a rise in the Seebeck coefficient. Additionally, the introduction of chemisorbed oxygen creates a high mobility state within the valence band of Sb2Te3, as corroborated by theoretical calculations, resulting in a significantly increased electrical mobility. These factors collectively contribute to improved thermoelectric performance. A set of Scanning probe (SPM) techniques is used to experimentally confirm the alteration in charge transport resulting from the oxygen-passivated grain boundary. Additionally, Scanning Thermal Microscopy (SThM) is employed to observe the spatial variations of thermal conductivity at the nanoscale regime. This study presents a comprehensive microscopic investigation of the impact of oxygen on the phonon and charge carrier transport characteristics of Sb2Te3 thermoelectric materials and indicates that incorporating oxygen may represent a feasible approach to improve the thermoelectric efficiency of these materials.
△ Less
Submitted 15 August, 2023;
originally announced August 2023.
-
Tuning thermoelectric properties of Sb$_2$Te$_3$-AgSbTe$_2$ nanocomposite thin film -- synergy of band engineering and heat transport modulation
Authors:
Abhishek Ghosh,
Khushboo Agarwal,
Sergio Gonzalez Munoz,
Prashant Bisht,
Chandan K Vishwakarma,
Narinder Kaur,
Mujeeb Ahmad,
Per Erik Vullum,
Branson D. Belle,
Rajendra Singh,
O. V. Kolosov,
Bodh Raj Mehta
Abstract:
The present study demonstrates a large enhancement in the Seebeck coefficient and ultralow thermal conductivity (TE) in Sb$_2$Te$_3$-AgSbTe$_2$ nanocomposite thin film. The addition of Ag leads to the in-situ formation of AgSbTe$_2$ secondary phase nanoaggregates in the Sb$_2$Te$_3$ matrix during the growth resulting in a large Seebeck coefficient and reduction of the thermal conductivity. A serie…
▽ More
The present study demonstrates a large enhancement in the Seebeck coefficient and ultralow thermal conductivity (TE) in Sb$_2$Te$_3$-AgSbTe$_2$ nanocomposite thin film. The addition of Ag leads to the in-situ formation of AgSbTe$_2$ secondary phase nanoaggregates in the Sb$_2$Te$_3$ matrix during the growth resulting in a large Seebeck coefficient and reduction of the thermal conductivity. A series of samples with different amounts of minor AgSbTe$_2$ phases are prepared to optimize the TE performance of Sb$_2$Te$_3$ thin films. Based on the experimental and theoretical evidence, it is concluded that a small concentration of Ag promotes the band flattening and induces a sharp resonate-like state deep inside the valence band of Sb$_2$Te$_3$, concurrently modifying the density of states (DOS) of the composite sample. In addition, the electrical potential barrier introduced by the band offset between the host TE matrix and the secondary phases promotes strong energy-dependent carrier scattering in the composite sample, which is also responsible for enhanced TE performance. A contemporary approach based on scanning thermal microscopy is performed to experimentally obtain thermal conductivity values of both the in-plane and cross-plane directions, showing a reduced in-plane thermal conductivity value by ~ 58% upon incorporating the AgSbTe$_2$ phase in the Sb$_2$Te$_3$ matrix. Benefitting from the synergistic manipulation of electrical and thermal transport, a large ZT value of 2.2 is achieved at 375 K. The present study indicates the importance of a combined effect of band structure modification and energy-dependent charge carrier scattering along with reduced thermal conductivity for enhancing TE properties.
△ Less
Submitted 30 May, 2023;
originally announced May 2023.
-
Effect of induced shape anisotropy on magnetic properties of ferromagnetic cobalt nanocubes
Authors:
D. Srikala,
V. N. Singh,
A. Banerjee,
B. R. Mehta
Abstract:
We report on the synthesis of ferromagnetic cobalt nanocubes of various sizes using thermal pyrolysis method and the effect of shape anisotropy on the static and dynamic magnetic properties were studied. Shape anisotropy of approximately 10 % was introduced in nanocubes by making nanodiscs using a linear chain amine surfactant during synthesis process. It has been observ…
▽ More
We report on the synthesis of ferromagnetic cobalt nanocubes of various sizes using thermal pyrolysis method and the effect of shape anisotropy on the static and dynamic magnetic properties were studied. Shape anisotropy of approximately 10 % was introduced in nanocubes by making nanodiscs using a linear chain amine surfactant during synthesis process. It has been observed that, ferromagnetism persisted above room temperature and a sharp drop in magnetic moment at low temperatures in zero-field cooled magnetization may be associated with the spin disorder due to the effective anisotropy present in the system. Dynamic magnetic properties were studied using RF transverse susceptibility measurements at different temperatures and the singularities due to anisotropy fields were probed at low temperatures. Symmetrically located broad peaks are observed in the frozen state at the effective anisotropy fields and the peak structure is strongly affected by shape anisotropy and temperature. Irrespective of size the shape anisotropy gave rise to higher coercive fields and larger transverse susceptibility ratio at all temperatures. The role of shape anisotropy and the size of the particles on the observed magnetic behaviour were discussed.
△ Less
Submitted 9 March, 2010;
originally announced March 2010.
-
Control of magnetism in cobalt nanoparticles by oxygen passivation
Authors:
D. Srikala,
V. N. Singh,
A. Banerjee,
B. R. Mehta,
S. Patnaik
Abstract:
We report on the preparation of ferromagnetic cobalt nanospheres with antiferromagnetic oxide capping layer and its implication for the variation in magnetic property. The hcp cobalt nanospheres were prepared by thermal decomposition of cobalt carbonyl in the presence of organic surfactants. The spherical nanoparticles thus prepared were oxidized to grow antiferromagnetic layers of varying compo…
▽ More
We report on the preparation of ferromagnetic cobalt nanospheres with antiferromagnetic oxide capping layer and its implication for the variation in magnetic property. The hcp cobalt nanospheres were prepared by thermal decomposition of cobalt carbonyl in the presence of organic surfactants. The spherical nanoparticles thus prepared were oxidized to grow antiferromagnetic layers of varying composition and thickness on top of cobalt spheres. High resolution transmission electron microscopy confirmed growth of Co3O4 in one case and CoO in another case. Strong exchange anisotropy and enhanced coercive field was observed due to the core-shell structure in Co-CoO system. On the other hand only a marginal improvement was seen in Co-Co3O4 system. A low temperature paramagnetic behavior was also observed that is interpreted in the framework of crystal defects in the oxide shell.
△ Less
Submitted 5 August, 2009;
originally announced August 2009.
-
Synthesis and characterization of ferromagnetic cobalt nanospheres, nanodiscs and nanocubes
Authors:
D. Srikala,
V. N. Singh,
A. Banerjee,
B. R. Mehta,
S. Patnaik
Abstract:
We report the synthesis of cobalt nanoparticles with different shapes and sizes by rapid pyrolysis of cobalt carbonyl in the presence of various surfactants. The size and shape of the nanoparticles were influenced by reaction conditions, such as type of the surfactant, molar ratio of surfactant to precursor, reflux temperature and reaction time. The shapes that we have achieved include spherical…
▽ More
We report the synthesis of cobalt nanoparticles with different shapes and sizes by rapid pyrolysis of cobalt carbonyl in the presence of various surfactants. The size and shape of the nanoparticles were influenced by reaction conditions, such as type of the surfactant, molar ratio of surfactant to precursor, reflux temperature and reaction time. The shapes that we have achieved include spherical, nearly spherical, disc and cube. The presence of linear amine yielded nanodiscs and they spontaneously self-assembled into long ribbons. The effect of shape anisotropy on magnetic nanoparticles has been investigated. Spherical nanoparticles of diameter 14.5 nm show strong ferromagnetic behavior at low temperature and superparamagnetism at room temperature. On the other hand the cubic nanoparticles of 45 nm sides showed negligible coercive field at T = 10 K and ferromagnetism that persisted above T = 300 K. The cobalt nanospheres were oxidized to grow cobalt oxide shell of varying thickness to study exchange bias effect. A pronounced exchange bias and a strong temperature dependant magnetization were observed in oxidized cobalt nanospheres.
△ Less
Submitted 5 August, 2009;
originally announced August 2009.