Traps and transport resistance: the next frontier for stable state-of-the-art non-fullerene acceptor solar cells
Authors:
Christopher Wöpke,
Clemens Göhler,
Maria Saladina,
Xiaoyan Du,
Li Nian,
Christopher Greve,
Chenhui Zhu,
Kaila M. Yallum,
Yvonne J. Hofstetter,
David Becker-Koch,
Ning Li,
Thomas Heumüller,
Ilya Milekhin,
Dietrich R. T. Zahn,
Christoph J. Brabec,
Natalie Banerji,
Yana Vaynzof,
Eva M. Herzig,
Roderick C. I. MacKenzie,
Carsten Deibel
Abstract:
Stability is one of the most important challenges facing organic solar cells (OSC) on their path to commercialization. In the high-performance material system PM6:Y6 studied here, investigate degradation mechanisms of inverted photovoltaic devices. We have identified two distinct degradation pathways: one requires presence of both illumination and oxygen and features a short-circuit current reduct…
▽ More
Stability is one of the most important challenges facing organic solar cells (OSC) on their path to commercialization. In the high-performance material system PM6:Y6 studied here, investigate degradation mechanisms of inverted photovoltaic devices. We have identified two distinct degradation pathways: one requires presence of both illumination and oxygen and features a short-circuit current reduction, the other one is induced thermally and marked by severe losses of open-circuit voltage and fill factor. We focus our investigation on the thermally accelerated degradation. Our findings show that bulk material properties and interfaces remain remarkably stable, however, aging-induced defect state formation in the active layer remains the primary cause of thermal degradation. The increased trap density leads to higher non-radiative recombination, which limits open-circuit voltage and lowers charge carrier mobility in the photoactive layer. Furthermore, we find the trap-induced transport resistance to be the major reason for the drop in fill factor. Our results suggest that device lifetimes could be significantly increased by marginally suppressing trap formation, leading to a bright future for OSC.
△ Less
Submitted 22 March, 2022;
originally announced March 2022.
-
Ligand Dependent Oxidation Dictates the Performance Evolution of High Efficiency PbS Quantum Dot Solar Cells
Authors:
David Becker-Koch,
Miguel Albaladejo Siguan,
Vincent Lami,
Fabian Paulus,
Hengyang Xiang,
Zhuoying Chen,
Yana Vaynzof
Abstract:
Lead sulfide (PbS) quantum dot (QD) photovoltaics have reached impressive efficiencies of 12%, making them particularly promising for future applications. Like many other types of emerging photovoltaic devices, their environmental instability remains the Achilles heel of this technology. In this work, we demonstrate that the degradation processes in PbS QDs which are exposed to oxygenated environm…
▽ More
Lead sulfide (PbS) quantum dot (QD) photovoltaics have reached impressive efficiencies of 12%, making them particularly promising for future applications. Like many other types of emerging photovoltaic devices, their environmental instability remains the Achilles heel of this technology. In this work, we demonstrate that the degradation processes in PbS QDs which are exposed to oxygenated environments are tightly related to the choice of ligands, rather than their intrinsic properties. In particular, we demonstrate that while 1,2-ethanedithiol (EDT) ligands result in significant oxidation of PbS, lead iodide/lead bromide (PbX2) coated PbS QDs show no signs of oxidation or degradation. Consequently, since the former is ubiquitously used as a hole extraction layer in QD solar cells, it is predominantly responsible for the device performance evolution. The oxidation of EDT-PbS QDs results in a significantly reduced effective QD size, which triggers two competing processes: improved energetic alignment that enhances electron blocking, but reduced charge transport through the layer. At early times, the former process dominates, resulting in the commonly reported, but so far not fully explained initial increase in performance, while the latter governs the onset of degradation and deterioration of the photovoltaic performance. Our work highlights that the stability of PbS quantum dot solar cells can be significantly enhanced by an appropriate choice of ligands for all device components.
△ Less
Submitted 29 July, 2020;
originally announced July 2020.
-
Efficient and Stable PbS Quantum Dot Solar Cells by Triple-Cation Perovskite Passivation
Authors:
Miguel Albaladejo-Siguan,
David Becker-Koch,
Alexander D. Taylor,
Qing Sun,
Vincent Lami,
Pola Goldberg Oppenheimer,
Fabian Paulus,
Yana Vaynzof
Abstract:
Solution-processed quantum dots (QDs) have a high potential for fabricating low cost, flexible and large-scale solar energy harvesting devices. It has recently been demonstrated that hybrid devices employing a single monovalent cation perovskite solution for PbS QD surface passivation exhibit enhanced photovoltaic performance when compared to standard ligand passivation. Herein we demonstrate that…
▽ More
Solution-processed quantum dots (QDs) have a high potential for fabricating low cost, flexible and large-scale solar energy harvesting devices. It has recently been demonstrated that hybrid devices employing a single monovalent cation perovskite solution for PbS QD surface passivation exhibit enhanced photovoltaic performance when compared to standard ligand passivation. Herein we demonstrate that the use of a triple cation Cs0.05(MA0.17FA0.83)0.95Pb(I0.9Br0.1)3 perovskite composition for surface passivation of the quantum dots results in highly efficient solar cells, which maintain 96 % of their initial performance after 1200h shelf storage. We confirm perovskite shell formation around the PbS nanocrystals by a range of spectroscopic techniques as well as high-resolution transmission electron microscopy. We find that the triple cation shell results in a favorable energetic alignment to the core of the dot, resulting in reduced recombination due to charge confinement without limiting transport in the active layer. Consequently, photovoltaic devices fabricated via a single-step film deposition reached a maximum AM1.5G power conversion efficiency of 11.3 % surpassing most previous reports of PbS solar cells employing perovskite passivation.
△ Less
Submitted 29 July, 2020;
originally announced July 2020.