Crack-free caustic magnesia-bonded refractory castables
Authors:
V. C. Miguel,
D. S. Fini,
V. S. Pinto,
M. H. Moreira,
V. C. Pandolfelli,
A. P. Luz
Abstract:
A growing interest in designing high-alumina MgO-bonded refractory castables has been identified in recent years due to the magnesia ability to react: (i) with water at the initial processing stages of these materials (inducing the precipitation of brucite phase) or (ii) with alumina, giving rise to in situ MgAl2O4 generation at high temperatures. Nevertheless, despite the great potential of caust…
▽ More
A growing interest in designing high-alumina MgO-bonded refractory castables has been identified in recent years due to the magnesia ability to react: (i) with water at the initial processing stages of these materials (inducing the precipitation of brucite phase) or (ii) with alumina, giving rise to in situ MgAl2O4 generation at high temperatures. Nevertheless, despite the great potential of caustic magnesia to be used as a binder in such systems due to its high reactivity, it is still a challenge to control the hydration reaction rate of this oxide and the negative effects derived from the expansive feature of Mg(OH)2 formation. Thus, this work evaluated the incorporation of different contents of aluminum hydroxyl lactate (AHL) into caustic magnesia-bonded castables, aiming to control the brucite precipitation during the curing and drying steps of the prepared samples, resulting in crack-free refractories. The designed compositions were characterized via flowability, setting behavior, X-ray diffraction, cold flexural strength, porosity, permeability and thermogravimetric measurements. According to the results, instead of Mg(OH)2, hydrotalcite-like phases [Mg6Al2(OH)16(OH)2.4.5H2O and Mg6Al2(OH)16(CO3).4H2O] were the main hydrated phases identified in the AHL-containing compositions. The addition of 1.0 wt.% of aluminum hydroxyl lactate to the designed castable proved to be, so far, the best option for this magnesia source, resulting in the development of a crack-free refractory with enhanced properties and greater spalling resistance under heating.
△ Less
Submitted 9 March, 2021;
originally announced March 2021.
-
Aluminum lactate role in improving hydration and drying behavior of MgO-bonded refractory castables
Authors:
D. S. Fini,
V. C. Miguel,
V. S. Pinto,
V. C. Pandolfelli,
M. H. Moreira,
A. P. Luz
Abstract:
Developing MgO-bonded castables is still an important subject for refractory producers and end-users based on the expansive character of the in-situ Mg(OH)2 formation. Considering that magnesia undergoes hydration when exposed to water and the generated hydrated phase needs to be properly accommodated in the resulting microstructure to inhibit the generation of cracks, it is very important to find…
▽ More
Developing MgO-bonded castables is still an important subject for refractory producers and end-users based on the expansive character of the in-situ Mg(OH)2 formation. Considering that magnesia undergoes hydration when exposed to water and the generated hydrated phase needs to be properly accommodated in the resulting microstructure to inhibit the generation of cracks, it is very important to find out alternatives to control the MgO hydration reaction rate. This research investigated the use of aluminum lactate (AL) as a likely additive to change the hydration and drying behavior of vibratable castables bonded with different MgO sources (dead burnt, caustic or fumed one). Firstly, XRD, TG and DSC measurements of magnesia-based aqueous suspensions were evaluated to identify the AL effect on changing the hydration reaction products during the curing and drying steps. After that, Al2O3-MgO refractories were prepared and their flowability, curing behavior, cold flexural strength, apparent porosity, permeability and explosion resistance were evaluated. The results indicated that, instead of Mg(OH)2, Mg6Al2(OH)16(OH)2.4.5H2O/ Mg6Al2(OH)16(CO3).4H2O was the main hydrated phase identified in the AL-containing compositions. Due to this change in the hydration behavior of the refractories, the mixtures prepared with dead-burnt or magnesia fumes plus organic salt presented a longer setting time. Besides that, crack-free samples with improved permeability and green mechanical strength could be obtained when adding 0.5 wt.% or 1.0 wt.% of aluminum lactate to the tested castable compositions. Consequently, 1.0 wt.% of the selected additive favored the design of refractories with enhanced properties and greater spalling resistance, as no explosion could be observed even when subjecting the prepared samples to severe heating conditions (20C/min).
△ Less
Submitted 2 February, 2021;
originally announced February 2021.
-
Fast drying of high-alumina MgO-bonded refractory castables
Authors:
V. S. Pinto,
D. S. Fini,
V. C. Miguel,
V. C. Pandolfelli,
M. H. Moreira,
T. Venancio,
A. P. Luz
Abstract:
Refractory producers face many challenges in terms of producing MgO-containing castables due to the high likelihood of magnesia to hydrate in contact with water, resulting in Mg(OH)2 generation. The expansive feature of this transformation affects the performance of such refractories, as (i) if this hydrated phase is not accommodated in the formed microstructure, ceramic linings with cracks and lo…
▽ More
Refractory producers face many challenges in terms of producing MgO-containing castables due to the high likelihood of magnesia to hydrate in contact with water, resulting in Mg(OH)2 generation. The expansive feature of this transformation affects the performance of such refractories, as (i) if this hydrated phase is not accommodated in the formed microstructure, ceramic linings with cracks and low green mechanical strength will be obtained; and (ii) if crack-free pieces are prepared, they should present low porosity and reduced permeability, which require special attention when heating these materials. This work investigated the ability of various additives in the optimization of the drying behavior of Al2O3-MgO castables. Vibratable compositions were tested after incorporating polymeric fibers (PF), an organic salt (OAS), SiO2-based additive (SM) or permeability enhancing active compound (MP) into the dry-mixtures. Various experimental measurements were performed to infer the role of the drying agents to prevent the samples explosion and whether they would also influence other properties of the castables. As observed, OAS and MP helped to inhibit the MgO-bonded samples explosion even under severe heating conditions (2-20C/min) and increased their green mechanical strength and slag infiltration resistance when compared to the additive-free composition. On the other hand, the addition of polymeric fibers (PF) or silica-based compound (SM) to the formulations was not able to prevent the castables explosion when using a high heating rate and other side effects could also be observed when testing these materials. Thus, the selection of suitable drying agents is a key issue, as they may allow the development of MgO-bonded castables with enhanced properties and lower spalling risk during their first thermal treatment.
△ Less
Submitted 30 January, 2021;
originally announced February 2021.