Understanding the roles of electronic effect in CO on Pt-Sn alloy surface via band structure measurements
Authors:
Jongkeun Jung,
Sungwoo Kang Laurent Nicolai,
Jisook Hong,
Jan Minár,
Inkyung Song,
Wonshik Kyung,
Soohyun Cho,
Beomseo Kim,
Jonathan D. Denlinger,
Francisco J. C. S. Aires,
Eric Ehret,
Philip N. Ross,
Jihoon Shim,
Slavomir Nemšák,
Doyoung Noh,
Seungwu Han,
Changyoung Kim,
Bongjin S. Mun
Abstract:
Using angle-resolved photoemission spectroscopy, we show the direct evidence of charge transfer between adsorbed molecules and metal substrate, i.e. chemisorption of CO on Pt(111) and Pt-Sn/Pt(111) 2x2 surfaces. The observed band structure shows a unique signature of charge transfer as CO atoms are adsorbed,revealing the roles of specific orbital characters participating in the chemisorption proce…
▽ More
Using angle-resolved photoemission spectroscopy, we show the direct evidence of charge transfer between adsorbed molecules and metal substrate, i.e. chemisorption of CO on Pt(111) and Pt-Sn/Pt(111) 2x2 surfaces. The observed band structure shows a unique signature of charge transfer as CO atoms are adsorbed,revealing the roles of specific orbital characters participating in the chemisorption process. As the coverage of CO increases, the degree of charge transfer between CO and Pt shows clear difference to that of Pt-Sn. With comparison to DFT calculation results, the observed distinct features in the band structure are interpreted as backdonation bonding states of Pt molecular orbital to the 2π orbital of CO. Furthermore, the change in the surface charge concentration, measured from the Fermi surface area, shows Pt surface has a larger charge concentration change than Pt-Sn surface upon CO adsorption. The difference in the charge concentration change between Pt and Pt-Sn surfaces reflects the degree of electronic effects during CO adsorption on Pt-Sn.
△ Less
Submitted 9 August, 2021;
originally announced August 2021.
Failure mechanisms of single-crystal silicon electrodes in lithium-ion batteries
Authors:
Feifei Shi,
Zhichao Song,
Philip N. Ross,
Gabor A. Somorjai,
Robert O. Ritchie,
Kyriakos Komvopoulos
Abstract:
Long-term durability is a major obstacle limiting the widespread use of lithium ion batteries (LIBs) in heavy-duty applications and others demanding extended lifetime. As one of the root causes of degradation and failure of battery performance, the electrode failure mechanisms are still unknown. Here, we reveal the fundamental fracture mechanisms of single-crystal silicon electrodes over extended…
▽ More
Long-term durability is a major obstacle limiting the widespread use of lithium ion batteries (LIBs) in heavy-duty applications and others demanding extended lifetime. As one of the root causes of degradation and failure of battery performance, the electrode failure mechanisms are still unknown. Here, we reveal the fundamental fracture mechanisms of single-crystal silicon electrodes over extended lithiation/delithiation cycles, using electrochemical testing, microstructure characterization, fracture mechanics, and finite element analysis. Anisotropic lithium invasion causes crack initiation perpendicular to the electrode surface, followed by growth through the electrode thickness. The low fracture energy of the lithiated/unlithiated silicon interface provides a weak microstructural path for crack deflection, accounting for the crack patterns and delamination observed after repeated cycling. Based on this physical understanding, we demonstrate how electrolyte additives can heal electrode cracks and provide strategies to enhance the fracture resistance in future LIBs from surface chemical, electrochemical, and material science perspectives.
△ Less
Submitted 18 June, 2016;
originally announced June 2016.