Abstract
Perovskite solar cells have shown unprecedent performance increase up to 22% efficiency. However, their photovoltaic performance has shown fast deterioration under light illumination in the presence of humid air even with encapulation. The stability of perovskite materials has been unsolved and its mechanism has been elusive. Here we uncover a mechanism for irreversible degradation of perovskite materials in which trapped charges, regardless of the polarity, play a decisive role. An experimental setup using different polarity ions revealed that the moisture-induced irreversible dissociation of perovskite materials is triggered by charges trapped along grain boundaries. We also identified the synergetic effect of oxygen on the process of moisture-induced degradation. The deprotonation of organic cations by trapped charge-induced local electric field would be attributed to the initiation of irreversible decomposition.
Similar content being viewed by others
Introduction
Metal halide perovskite solar cells1,2,3 have shown unprecedent performance increase up to 22% efficiency4 and are now considered not only as a low-cost alternative to commercialized solar cells5,6 but also as a functional cell with flexible applications7,8. However, their long-term stability has not been solved yet and this issue is the most pressing problem for commercialization9. It is well known that perovskite materials are vulnerable to the exposure of humidity and light10,11,12. Although many efforts to encapsulate the devices for preventing direct contact to humidity have been attempted, it was not successful to obtain long-term stability comparable to commercial photovoltaic devices13. Various factors that can affect the stability have been investigated from the viewpoints of chemical structure14, electrical stress15, hydrated states10,11,16 and heat17. However, the degradation mechanism is still unclear how a fully fabricated device deteriorates rapidly, even though its perovskite layer is tightly covered by the hole transport material (HTM) and the back electrode. It is also elusive why light soaking causes irreversible degradation of perovskite materials in the presence of moisture, whereas the moisture in the dark condition only induces reversible hydration of perovskite materials11,16.
The device structure and the choice of charge extraction materials also influence the stability18. The use of inorganic charge extraction layers was reported to enhance stability13,19. Other studies have focused on eliminating the pathway of water vapour infiltration into the perovskite film by coating carbon-based materials, polymers and hydrophobic materials on the top surface of the perovskite film12,20. These approaches provide the device lifespan longer than the case without these materials, but not long enough to ensure long-term stability. Such approaches also occasionally sacrifice the photovoltaic performance. Especially, the devices employing titanium dioxide (TiO2) as electron transport layer (ETL) are rapidly degraded under light soaking21, even though they are highly efficient in energy conversion and exhibit the worldâs best efficiency.
In the present study, we demonstrate that the charges trapped at the interface between perovskite and charge extraction materials are responsible for the irreversible degradation due to moisture. The elusive experimental puzzles both on the occurrence of degradation beginning from different side depending on different charge extraction material and the role of light soaking for irreversible degradation will be clearly explained from the present concept of the trapped charges later. To dig into this charge-driven degradation mechanism, we investigated controlled stability experiments both for commonly used CH3NH3PbI3 (MAPbI3), which is known to form structurally distorted tetragonal crystals, and a mixed perovskite material having more enhanced structural stability. The crystal structure of perovskite can become more stable by increasing the tolerance factor close to unity by incorporating other organic cation and halide anion with different ion sizes22,23 (see Supplementary Fig. 1). Addition of formamidinium (FA) cation and bromide (Br) anion could not only structurally stabilize the perovskite materials by increasing tolerance factor towards one for inducing cubic crystals but also enhance their photovoltaic performance by broadening absorption spectrum5,6. Although several studies on mixed cation and/or halide anion system of MAxFA1âxPbIyBr3ây have been suggested5,6,24, they focused on the performance aspect, not the stability aspect. Therefore, an effort is required to develop new composition perovskite, ensuring both stability and high performance. In this work, we developed a mixed MA0.6FA0.4PbI2.9Br0.1 perovskite, ensuring both high performance and stability via Lewis base adduct method25 (see Methods section, Supplementary Figs 1â4 and Supplementary Note 1). Later, it will be shown that this mixed perovskite still degrades, although its degradation speed is slower than the case of conventional MAPbI3 and the irreversible degradation of both perovskites is triggered by trapped charges.
Results
Performance and stability comparison depending on ETLs
First, we examined how solar cell degradation behaviour becomes different depending on different charge extraction layers, for example, C60 and compact TiO2 (see the detailed process for solar cell fabrication in the Methods section). Figure 1a,b show JâV curves for MA0.6FA0.4PbI2.9Br0.1 perovskite on the C60 ETL (Fig. 1a) and compact TiO2 layer (Fig. 1b), respectively. Figure 1a shows JâV curve for our mixed perovskite on 35ânm-thick, dense C60 layer deposited by thermal evaporation, which demonstrates hysteresis-less performance of the best power conversion efficiency (PCE) of 20.2%. The best PCE value was averaged from the JâV curves of forward and reverse scan, which is in agreement with 20.2% of steady-state efficiency shown in Supplementary Fig. 4b. The integrated Jsc estimated from external quantum efficiency (EQE) was also well-matched with the measured Jsc as shown in Supplementary Fig. 4c. Histograms of the short-circuit current (Jsc), the open-circuit voltage (Voc), the fill factor and the efficiency of 47 cells are shown in Supplementary Fig. 4dâg. The photovoltaic characteristics of these cells were highly reproducible with a small s.d. and the average values are Jsc=24.34âmAâcmâ2, Voc=1.058âV, fill factor=0.743 and PCE=19.12%, respectively. This would be the best performance of low-temperature processed perovskite solar cells without using mesoporous TiO2. On the other hand, the case coated on 40ânm-thick compact TiO2 showed a large hysteresis with PCE of 16.9% on the reverse scan and 9.0% on the forward scan, which is consistent with previous studies that also showed a large hysteresis for compact TiO2-based devices26.
As shown in Fig. 1c,d, non-encapsulated C60-based cell shows much more stable performance under one sun illumination but still degrades, whereas compact TiO2-based non-encapsulated cell completely died only after 6âh. To examine the detailed evolution of degradation, we investigated how the cross-sectional morphology of the C60- and TiO2-based devices would evolve under illumination via the focused ion beam-assisted scanning electron microscope (SEM) images shown in Fig. 2. Consistent with the PCE measurement results, the SEM images clearly confirm that the C60-based devices are much slowly degraded compared with the TiO2-based cells. Strikingly, they showed different degradation patterns, namely different side of degradation beginning where the degradation is initiated depending on different ETLs. Such degradation pattern is the same for conventional MAPbI3 perovskite (see Supplementary Fig. 5). As the reactants that can decompose perovskite materials could infiltrate from the thin metal electrode rather than from the thick indium tin oxide-coated (ITO) glass, it would be expected that the degradation should be initiated at the interface closer to the thin Au metal electrode. However, the perovskite films of TiO2-based devices began to be decomposed at the interface adjacent to the compact TiO2 layer near fluorine doped tin oxide (FTO) glass (as shown in Fig. 2b). Although these observations were attributed to ultraviolet light-induced photocatalytic effect of TiO2 layer according to the previous report27, we confirmed that the same degradation pattern happened in the TiO2- and C60-based devices aged even under ultraviolet-filtered light illumination (see Supplementary Fig. 6). For those of C60-based devices, the decomposition began from the interface adjacent to HTL near Au metal electrode opposite to the case of TiO2-based devices. As the two types of devices have identical structure, except for the ETL, C60 or TiO2/Perovskite/Spiro-MeOTAD/Au, these different degradation characteristics indicate that charge extraction may play an important role where moisture-driven decomposition of perovskite material begins. Second, the TiO2-based devices suffer from severe hysteresis, whereas the C60-based devices do not. Considering that the origin of hysteresis is known as capacitive current26, trapped charge28 and unbalanced charge injection29, many electrons may be accumulated near the ETL in the TiO2-based devices, whereas the C60-based devices hardly do. From the observation on the degradation of the TiO2-based devices that begins from the interface contacting TiO2 layer where many charges could be trapped, it is reasonable to suspect that trapped charges at the interface between perovskite and charge extraction layer would be responsible for initiating the moisture-related decomposition. Fast extraction of electrons through C60 would hardly accumulate negative charges at the interface between perovskite and C60, but hole extraction through Spiro-MeOTAD could be slower than the rate of electron extraction in the C60-based cell30,31. This could result in positive charge trapping at the interface between perovskite and hole extraction layer, which could be the cause why the degradation begins from the interface between perovskite and Spiro-MeOTAD for C60-based cells (see Fig. 2a). These results demonstrating the degradation beginning from opposite side for different charge extraction layers gave us a clue about the trapped charge-driven degradation regardless of polarity.
Hydration and light-induced degradation of perovskite materials
Another intriguing experimental observation is the light soaking in the presence of moisture, which consistently showed irreversible degradation of perovskite in previous works9,11,12, whereas in the dark condition moisture introduction only formed reversible hydrates of perovskites, for example, CH3NH3PbI3·H2O or (CH3NH3)4PbI6·2H2O (refs 11, 16). The reason has not been elucidated yet, although Christians et al.11 suggested that organic cation could become less tightly bound to PbI64â octahedra after light soaking. In the present study, along with the scenario of the above mentioned trapped charges that could trigger irreversible degradation, the charge generation under light soaking and subsequent trapping on the surface of perovskite is suspected to initiate the moisture-induced irreversible degradation under light illumination. To confirm the irreversible degradation under light soaking, we also investigated the experiments under light soaking or not in the presence of moisture. Figure 3aâf showed the degradation behaviour of MAPbI3 and our mixed MA0.6FA0.4PbI2.9Br0.1, respectively, for 2 days in the dark condition with relative humidity (RH) 90%. Absorption spectra measurements show that the original MAPbI3 (black curve) became hydrated (red curve) after 2 days and then dehydrated reversibly via N2 drying, which is consistent with previous studies11,16. On the other hand, the absorption spectra of our mixed MA0.6FA0.4PbI2.9Br0.1 perovskite were hardly changed with the same condition (see Fig. 3d) and X-ray diffraction (XRD) patterns were the same after 2 days (see Supplementary Fig. 7). This indicates our mixed composition perovskite would be more resistible to become hydrated than distorted tetragonal perovskite MAPbI3. It is likely to be that water molecules could penetrate more easily into the distorted tetragonal MAPbI3 than into the more compact cubic crystal structure of MA0.6FA0.4PbI2.9Br0.1 (ref. 23). A slight change of the absorption spectra shown in Fig. 3d indicates a slow hydration could still happen to our mixed perovskite under 90% RH. However, both perovskites showed irreversible degradation rapidly under light soaking even at low RH 20% (see Fig. 3gâl), which is also consistent with previous report11,12,21. It is interesting to note that under light soaking, our mixed perovskite degrades more slowly than the conventional MAPbI3. As mentioned earlier, perovskite-absorbing light can generate and store charges due to its capacitive property32 that may be trapped on the grain boundaries (we will show trapped charges along grain boundaries after light soaking later). It could be hypothesized that these trapped charges generated under light soaking would be responsible for irreversible degradation, which is in line with the aforementioned hypothesis of trapped charge-driven degradation explaining the initiation of degradation on different side, depending on different charge extraction layers.
Trapped charge-driven degradation
To prove this compelling hypothesis of trapped charge-driven degradation, we have configured an experimental setup employing an ion generator by corona discharge and a stainless chamber that blocks all incident light from outside as shown in Fig. 4a. Detailed descriptions of the ion generation via corona discharge method and ion deposition can be found in the refs 33, 34, 35. The air inside the chamber is isolated from the outside and controlled by two gas inlets that are connected to the independent gas sources (Gas 1 and Gas 2; see the Supplementary Note 2). Gas 1 is ionized by applying a high voltage to the pin of the corona chamber, delivered to the deposition chamber by gas flow and deposited on the perovskite film placed at the bottom of the deposition chamber. Gas 2 passes through a water bubbler to regulate the humidity level in the deposition chamber. We measured the time evolution of the absorption spectra as the perovskite films were gradually degraded in the deposition chamber. Gas 1 was chosen as nitrogen or hydrogen for generating positive or negative ions, for being used as different polarity charges trapped on the surface of perovskite, respectively, whereas Gas 2 was nitrogen (see the Supplementary Note 2). First, we needed to check that N2-positive ions and H2-negative ions themselves do not affect the degradation without moisture (see Supplementary Fig. 8). Next, we examined the degradation behaviour in the presence of moisture when charged ions deposited on the surface of perovskite. When the positively charged N2 ions were deposited and the RH in the chamber was held at 40%, the perovskite film rapidly decays as shown in Fig. 4b. The deposition of negatively charged H2 ions also showed the similar irreversible degradation behaviour under the same moisture level in Fig. 4c. Although Fig. 4c for negative charges appears to cause slower degradation than the case shown in Fig. 4b for positive charges, this could not tell which polarity charges affect more adversely on the degradation, as ion generation for different polarity in our experiment is different (see the Supplementary Note 2). It is noteworthy that, on the other hand, without depositing charges, the absorption spectra and XRD patterns of the perovskite film were hardly changed for 2 days even under 90% humidity as was shown in Fig. 3d and Supplementary Fig. 7. Similarly, at the presence of only charges without moisture, the degradation did not occur at all as shown in Supplementary Fig. 8. This suggests that the irreversible degradation of perovskite materials only take place when both moisture and charges exist simultaneously. Moreover, the structurally distorted (conventional) MAPbI3 film was degraded more quickly than the mixed stable MA0.6FA0.4PbI2.9Br0.1 under the same moisture and ion deposition level (Supplementary Fig. 9). Based on these observations, the degradation mechanism could be thought of a two-step process: the formation of hydrated perovskite by humidity and the irreversible decomposition by trapped charges. The first step of the formation of hydrated perovskite was already reported by several groups10,11,16. Here we suggest that local electric field caused by trapped charge could distort electrostatically the structure of hydrated perovskite in which octahedral PbX64â interacts with both organic cation and H2O, and trigger the initiation of irreversible decomposition of perovskite (will discuss more complete scenario in the Discussion section). Leijtens et al.9,15 found the irreversible degradation near the gold electrodes coated on perovskite film by applying a weak external field of 600âVâcmâ1 in the presence of moisture and attributed it to the ion movement through electric field. As an electric field was applied between two electrodes touching perovskite film, electric current could flow and there was a possibility of charge trapping underneath the electrode, which might have played a role for degradation. To isolate the effect of pure external electric field, we examined the degradation of perovskite materials by applying non-contact electric field, which was given by two floating electrodes; one electrode is in air above perovskite film coated on ITO glass and the other electrode exists beneath the glass. We found no degradation up to 12âkVâcmâ1 under 90% RH (see Supplementary Fig. 10). It is noteworthy that this field will be dropped across the air gap and, therefore, the real field inside perovskite film should be different from the given field and the perovskite film might be uniformly polarized by one-directional strong E-field, because perovskite materials have a high dielectric constant36,37. Therefore, further study should be needed to completely understand the effect of pure external electric field. It is noted that the differences between the fields due to the trapped charges and the external field lie in the point-like character of the trapped charges, which produce locally huge and irregular fields. The huge and irregular fields formed by charges trapped along grain boundaries could help the process of deprotonation27,38 (will discuss in the Discussion section).
Next we investigated how trapped charge could decompose perovskite material in time by examining morphology evolution via SEM analysis. As shown in Fig. 5eâl (tilted top-view and cross-sectional images) and Supplementary Fig. 11 (top-view images), the degradation is initiated from the grain boundaries. As the reaction continues, the colour of the film turns into yellow (Fig. 5aâd), indicating that the perovskite is irreversibly decomposed to PbI2 (see XRD patterns after degradation in Supplementary Fig. 12). It is interesting to dig into why degradation occurs from grain boundaries in line with our trapped charge mechanism. To check the distribution of trapped charges on the surface of perovskite after uniform ion deposition, we measured Kelvin probe force microscopy (KPFM) of untreated perovskite and ion-treated perovskite films (see the Supplementary Note 3). Figure 5m,n shows topology and surface potential distribution of the perovskite surface on which positive N2 ions were uniformly showered. Striking coincidence between two images is the evidence that charges are preferentially trapped along grain boundaries. Overlapped image of topology and potential distribution shown in Supplementary Fig. 13 clearly demonstrates charges are trapped along grain boundaries even though ions are showered uniformly. For untreated sample, there is no correlation between topology and potential distribution (see Supplementary Fig. 13). With this charge trapping along grain boundaries, experimentally observed degradation pattern following grain boundaries and the fact that the irreversible degradation occurs only when moisture and charges exist together are the evidences that trapped charges would be responsible for the initiation of irreversible degradation of perovskite materials. It is now apparent that grain boundaries are the most vulnerable sites for degradation, because they provide charge accumulation sites as well as infiltration pathway of water vapour9. Successful enhancement of stability using high-mobility inorganic charge extraction layers supports the present idea13,19.
To further investigate the possibility that the above mentioned intriguing experimental observation of irreversible degradation under light soaking might be related to the mechanism of trapped charges of the present study, we measured KPFM images on the surface of perovskite after light illumination without ion deposition. As shown in Supplementary Fig. 13, charges are clearly trapped along grain boundaries for the ITO/C60/perovskite sample soaked by light, which is in agreement with the previous report39. These results confirmed that light soaking alone induces charge trapping along the grain boundaries of perovskite material similar to what was done by introduction of ion charges in the dark condition. From our concept, these trapped charges can now trigger the irreversible degradation due to moisture, as the same happened when ion charges are deposited in the dark. Therefore, the fundamental cause for irreversible degradation would be the same, that is, the trapped charges that could trigger the irreversible degradation under humid air. Such irreversible degradation under light soaking was reported in previous several reports11,21; however, the reason has not been clearly elucidated so far, although Christians et al.11 suggested the lessened hydrogen bonding after photoexcitation as a possible cause. Here we argue that trapped charges under moisture would be responsible for the initiation of irreversible degradation under light or in the dark, as light illumination always generates charges and traps the charges along grain boundaries as shown earlier. This can explain well why moisture itself without illumination or intentional ion deposition only hydrated perovskite reversibly. Light illumination under nitrogen gas without moisture for 2 days was shown to hardly degrade the perovskite as shown in Supplementary Fig. 14, which is strongly in contrast with the case of light illumination under moisture (see Fig. 3j).
Discussion
We suggest a possible scenario how trapped charge could trigger the irreversible decomposition of perovskite materials. First, in the presence of water molecules, perovskite materials are known to form hydrates. Within the hydrated perovskite, octahedral PbX64â interacts with both organic cations (CH3NH3+, HC(NH2)2+) and H2O (ref. 11). Next, the charges trapped at the defect site regardless of polarity could help to deprotonate organic cations by induced local electric field similar to the way that was well known from the soft matter physics on electric-field-induced de-protonation of organic molecules40,41. Such de-protonation process27,38 in the presence of water could yield volatile molecules such as CH3NH2 and HC(=NH)NH2 that can evaporate at room temperature. The following deprotonation from organic cations could take place due to trapped charge-induced local electric field:
where TC means trapped charge. Evaporation of resulted volatile neutral molecules could shift the following equilibrium reaction that prevail during the formation of hydrates towards the right-hand side, which causes the beginning of irreversible degradation of perovskite:
where X denotes halide. In addition, trapped charges could help the hydration process by distorting the structure of perovskite electrostatically, which leads water molecule to penetrate easily into the perovskite structure.
Next, we investigated the effect of oxygen on the moisture-induced degradation of perovskite materials. Previous studies on device encapsulation have mostly focused on blocking moisture and overlooked the effect of oxygen. However, we found an interesting result that is the synergetic effect of oxygen on the process of moisture-induced degradation of perovskites. To test this, we switched the Gas 2 from N2 to dry air (N2+O2:8:2) for bubbling water (see Fig. 4a) with the Gas 1 remaining as N2 for ion generation. As shown in Fig. 6b, the addition of oxygen under the same condition of trapped charge and moisture of RH=40% clearly showed more rapid degradation compared with the case without oxygen (Fig. 6a). We also verified that degradation did not happen if a dry air gas was employed as Gas 2 without moisture (Supplementary Fig. 15). This implies that oxygen alone would not harm the perovskite even under the existence of trapped charges; however, the oxygen could worsen the degradation process in the presence of water and trapped charges. Previously, Niu et al.42 suggested reaction equations of oxygen-involved degradation in humid air condition, which represent the formation of H2O as a reaction product. Similarly, we explain the fast degradation in the presence of oxygen more clearly based on the scavenging effect of oxygen on H3O+ proton generated from irreversible de-protonation process (equation (1)). The process of scavenging H3O+ by oxygen could be expressed as follows.
The overall chemical reaction of the oxygen involved degradation can be expressed as:
We also confirmed that solid I2 is produced from the perovskite degraded in ambient air, which is evidenced by XRD results (see Supplementary Fig. 16). Interestingly, the overall reaction produces water, which is in agreement with the previous work42, and then this water could cause a chain reaction of water-induced degradation. Therefore, oxygen, which comprises about 20% of the atmosphere, should be considered as an additional target that must be avoided together with moisture.
In conclusion, we found that trapped charges would be responsible for triggering the irreversible degradation in the moisture-induced degradation of perovskite materials regardless of charge polarity. To verify this, we designed a novel experimental setup enabling the deposition of different polarity charges on the surface of perovskites for controlled moisture degradation experiments. From this setup, we demonstrated that the perovskite materials degraded irreversibly along grain boundaries only when both moisture and trapped charge exist simultaneously. During the course of study, we developed and used a mixed perovskite material that ensured both high performance and structural stability. Our study explains both why the degradation begins to occur from the different side of interface between perovskite and charge extraction layer for different charge extraction layers and how light soaking always degrades irreversibly in the presence of moisture. KPFM study reveals that charges are trapped preferentially along grain boundaries of perovskites even under uniform deposition of ion charges or uniform illumination of light, which supports our idea of trapped charge-driven degradation. We also found the synergetic effect of oxygen in the process of moisture-induced degradation. The present study suggests that the prevention of accumulation of charges at the interface is very important in addition to proper encapsulation for developing commercially viable perovskite solar cells.
Methods
Solar cell fabrication
ITO glass substrates (AMG, 9.5Ωâcmâ2, 25 à 25âmm2) were sequentially sonicated in acetone, isopropanol and deionized water. The cleaned substrate was sufficiently dried in an oven, to eliminate all residual solvents. A 35ânm-thick C60 layer43 was densely coated on the ITO glass substrates by using a vacuum thermal evaporator at the constant rate of 0.1âà âsâ1. The 50 wt% mixed perovskite solutions (MAI+FAI+MABrâ:âPbI2â:âdimethyl sulfoxide=1:1:1 in dimethylformamide (DMF) solvent) were coated on the ITO/C60 substrate by Lewis base adduct method25. To prepare our best compositional solution, 461âmg of PbI2, 79.5âmg of MAI, 68.8âmg of FAI, 11.2âmg of MABr and 78âmg of dimethyl sulfoxide were mixed in 0.55âml of dimethylformamide (DMF) at room temperature with stirring for 30âmin. After spin coating at 4,000âr.p.m. for 20âs with ether dripping treatment, the transparent adduct films were annealed at 130â°C for 20âmin, to form black perovskite films. To prepare the HTM, 72.3âmg of Spiro-MeOTAD (Merk) dissolved in 1âml Chlorobenzen (Sigma-Aldrich) with 28.8âμl of 4-tert-butyl pyridine and 17.5âμl of lithium bis (trifluoromethanesulfonyl) imide solution (520âmg lithium bis (trifluoromethanesulfonyl) imide in 1âml acetonitrile (Sigma-Aldrich, 99.8%)). The HTM solutions were spin coated onto the perovskite layer at 2,000âr.p.m. for 30âs. After all process, 50ânm gold (Au) as a counter electrode was deposited on the HTM at the rate of 0.3 à âsâ1 by using a vacuum thermal evaporator. All spin coating processes in our experiments were carried out in a dry room (RH <15%, room temperature).
In the case of TiO2-based devices, a TiO2 blocking layer was fabricated on FTO-coated glass substrates by spin coating 0.15âM titanium di-isopropoxide dis(acetylacetonate) (Sigma-Aldrich, 75 wt% in isopropanol) in 1-butanol (Sigma-Aldrich, 99.8%) at sequentially increasing spin rate of 700âr.p.m. for 8âs, 1,000âr.p.m. for 10âs and 2,000âr.p.m. for 40âs. After spin coating, the TiO2 blocking layer was heated at 125â°C for 5âmin and this process was repeated once again. The substrate was annealed at 550â°C for 1âh. The rest of the processes are identical to the fabrication of C60-based devices.
Characterization
The cross-sectional and surface images of the perovskite films and the fabricated perovskite solar cells were obtained from a high-resolution SEM with a focused ion beam system (Carl Zeiss, AURIGA). The optical absorption spectra of the perovskite films coated on the ITO substrate were measured by ultraviolet-visible spectrophotometer (Agilent Technologies, Cary 5000) in the 400-850ânm wavelength range. The XRD patterns of the perovskite films on the ITO glass were collected by using New D8 Advanced (Bruker) in the 2θ range of 5°â80°. Photocurrent densityâvoltage curves were measured by a solar simulator (Oriel Sol3A) with Keithley 2400 Source Meter under AM1.5G, which is calibrated to give 100âmWâcmâ2 using a standard Si photovoltaic cell (Rc-1000-TC-KG5-N, VLSI Standards). The JâV curves were measured by covering devices with a metal mask having an aperture. (6.76âmm2) EQE was measured by a specially designed EQE system (PV measurement Inc.) with 75âW Xenon lamp (USHIO, Japan) as a source of monochromatic light. High-performance long-pass filter (<425ânm, Edmund Optics) was used for aging the devices under ultraviolet-filtered light illumination.
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
Additional information
How to cite this article: Ahn, N. et al. Trapped charge-driven degradation of perovskite solar cells. Nat. Commun. 7, 13422 doi: 10.1038/ncomms13422 (2016).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Kojima, A., Teshima, K., Shirai, Y. & Miyasaka, T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050â6051 (2009).
Kim, H.-S. et al. Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%. Sci. Rep. 2, 591 (2012).
Lee, M. M., Teuscher, J., Miyasaka, T., Murakami, T. N. & Snaith, H. J. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643â647 (2012).
NREL efficiency chart. http://www.nrel.gov/ncpv/images/efficiency_chart.jpg. (2016).
Bi, D. et al. Efficient luminescent solar cells based on tailored mixed-cation perovskites. Sci. Adv. 2, e1501170 (2016).
Yang, W. S. et al. High-performance photovoltaic perovskite layers fabricated through intramolecular exchange. Science 348, 1234â1237 (2015).
Kim, B. J. et al. Highly efficient and bending durable perovskite solar cells: toward a wearable power source. Energy Environ. Sci. 8, 916â921 (2015).
Sung, H. et al. Transparent conductive oxide-free graphene-based perovskite solar cells with over 17% efficiency. Adv. Energy Mater. 6, 1501873 (2016).
Leijtens, T. et al. Stability of metal halide perovskite solar cells. Adv. Energy Mater. 5, 1500963 (2015).
Yang, J., Siempelkamp, B. D., Liu, D. & Kelly, T. L. Investigation of CH3NH3PbI3 degradation rates and mechanisms in controlled humidity environments using in situ techniques. ACS Nano 9, 1955â1963 (2015).
Christians, J. A., Miranda Herrera, P. A. & Kamat, P. V. Transformation of the excited state and photovoltaic efficiency of CH3NH3PbI3 perovskite upon controlled exposure to humidified air. J. Am. Chem. Soc. 137, 1530â1538 (2015).
Habisreutinger, S. N. et al. Carbon nanotube/polymer composites as a highly stable hole collection layer in perovskite solar cells. Nano Lett. 14, 5561â5568 (2014).
Chen, W. et al. Efficient and stable large-area perovskite solar cells with inorganic charge extraction layers. Science 350, 944â948 (2015).
Tong, C.-J. et al. Uncovering the veil of the degradation in perovskite CH3NH3PbI3 upon humidity exposure: a first-principles study. J. Phys. Chem. Lett. 6, 3289â3295 (2015).
Leijtens, T. et al. Mapping electric field-induced switchable poling and structural degradation in hybrid lead halide perovskite thin films. Adv. Energy Mater. 5, 1500962 (2015).
Leguy, A. M. A. et al. Reversible hydration of CH3NH3PbI3 in films, single crystals, and solar cells. Chem. Mater. 27, 3397â3407 (2015).
Divitini, G. et al. In situ observation of heat-induced degradation of perovskite solar cells. Nat. Energy 1, 15012 (2016).
Wojciechowski, K. et al. C60 as an efficient n-type compact layer in perovskite solar cells. J. Phys. Chem. Lett. 6, 2399â2405 (2015).
You, J. et al. Improved air stability of perovskite solar cells via solution-processed metal oxide transport layers. Nat. Nanotechnol. 11, 75â81 (2016).
Mei, A. et al. A hole-conductorâfree, fully printable mesoscopic perovskite solar cell with high stability. Science 345, 295â298 (2014).
Lee, J.-W. et al. Formamidinium and cesium hybridization for photo- and moisture-stable perovskite solar cell. Adv. Energy Mater. 5, 1501310 (2015).
Li, Z. et al. Stabilizing perovskite structures by tuning tolerance factor: formation of formamidinium and cesium lead iodide solid-state alloys. Chem. Mater. 28, 284â292 (2016).
Noh, J. H., Im, S. H., Heo, J. H., Mandal, T. N. & Seok, S. I. Chemical management for colorful, efficient, and stable inorganicâorganic hybrid nanostructured solar cells. Nano Lett. 13, 1764â1769 (2013).
Jeon, N. J. et al. Compositional engineering of perovskite materials for high-performance solar cells. Nature 517, 476â480 (2015).
Ahn, N. et al. Highly reproducible perovskite solar cells with average efficiency of 18.3% and best efficiency of 19.7% fabricated via Lewis base adduct of lead (II) iodide. J. Am. Chem. Soc. 137, 8696â8699 (2015).
Kim, H.-S. et al. Control of IâV hysteresis in CH3NH3PbI3 perovskite solar cell. J. Phys. Chem. Lett. 6, 4633â4639 (2015).
Ito, S., Tanaka, S., Manabe, K. & Nishino, H. Effects of surface blocking layer of sb2s3 on nanocrystalline TiO2 for CH3NH3PbI3 perovskite solar cells. J. Phys. Chem. C 118, 16995â17000 (2014).
Chen, B., Yang, M., Priya, S. & Zhu, K. Origin of JV hysteresis in perovskite solar cells. J. Phys. Chem. Lett. 7, 905â917 (2016).
Tress, W. et al. Understanding the rate-dependent J-V hysteresis, slow time component, and aging in CH3NH3PbI3 perovskite solar cells: the role of a compensated electric field. Energy Environ. Sci. 8, 995â1004 (2015).
Schmidt-Mende, L. & Grätzel, M. TiO2 pore-filling and its effect on the efficiency of solid-state dye-sensitized solar cells. Thin Solid Films 500, 296â301 (2006).
Liang, P.-W., Chueh, C.-C., Williams, S. T. & Jen, A. K. Y. Roles of fullerene-based interlayers in enhancing the performance of organometal perovskite thin-film solar cells. Adv. Energy Mater. 5, 140321 (2015).
Kim, H.-S. et al. Mechanism of carrier accumulation in perovskite thin-absorber solar cells. Nat. Commun. 4, 2242 (2013).
Kim, H. et al. Parallel patterning of nanoparticles via electrodynamic focusing of charged aerosols. Nat. Nanotechnol. 1, 117â121 (2006).
Lee, H. et al. Three-dimensional assembly of nanoparticles from charged aerosols. Nano Lett. 11, 119â124 (2011).
Hinds, C. W. Aerosol Technology : Properties, Behavior, and Measurement of Airborne Particles A Wiley-Interscience Publication2, (1999).
Lin, Q., Armin, A., Nagiri, R. C. R., Burn, P. L. & Meredith, P. Electro-optics of perovskite solar cells. Nat. Photonics 9, 106â112 (2015).
Juarez-Perez, E. J. et al. Photoinduced giant dielectric constant in lead halide perovskite solar cells. J. Phys. Chem. Lett. 5, 2390â2394 (2014).
Frost, J. M. et al. Atomistic origins of high-performance in hybrid halide perovskite solar cells. Nano Lett. 14, 2584â2590 (2014).
Yun, J. S. et al. Benefit of grain boundaries in organicâinorganic halide planar perovskite solar cells. J. Phys. Chem. Lett. 6, 875â880 (2015).
White, H. S., Peterson, J. D., Cui, Q. & Stevenson, K. J. Voltammetric measurement of interfacial acid/base reactions. J. Phys. Chem. B 102, 2930â2934 (1998).
Zhao, X., Ong, S., Wang, H. & Eisenthal, K. B. New method for determination of surface pKa using second harmonic generation. Chem. Phys. Lett. 214, 203â207 (1993).
Niu, G. et al. Study on the stability of CH3NH3PbI3 films and the effect of post-modification by aluminum oxide in all-solid-state hybrid solar cells. J. Mater. Chem. A 2, 705â710 (2014).
Yoon, H., Kang, S. M., Lee, J.-K. & Choi, M. Hysteresis-free low-temperature-processed planar perovskite solar cells with 19.1% efficiency. Energy Environ. Sci. 9, 2262â2266 (2016).
Acknowledgements
This work was supported by the Global Frontier R&D Program of the Center for Multiscale Energy Systems funded by the National Research Foundation under the Ministry of Education, Science and Technology, Korea (2011-0031561 and 2011-0031577). B.Y.L. acknowledges the support from the National Research Foundation of Korea (NRF) grant funded by the Ministry of Science, ICT and Future Planning (NRF-2016M3A7B4909581). We thank H. Sung and S.R. Noh for discussions and comments on this work.
Author information
Authors and Affiliations
Contributions
N.A., K.K. and M.C. conceived and designed the experiments, and analysed the data results. N.A., K.K., H.Y. and J.B. performed the device fabrication and photovoltaic performance measurements. N.A., K.K. and J.B. carried out the controlled stability test. B.Y.L. and J.-K.L. measured KPFM. P.V.P., N.A., K.K. and M.C. discussed the mechanism. M.C. led the project. N.A., K.K., M.S.J., P.V.P. and M.C. wrote the paper. All authors discussed the results.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-16, Supplementary Table 1, Supplementary Notes 1-3 and Supplementary References. (PDF 2301 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the articleâs Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Ahn, N., Kwak, K., Jang, M. et al. Trapped charge-driven degradation of perovskite solar cells. Nat Commun 7, 13422 (2016). https://doi.org/10.1038/ncomms13422