Abstract
In search of novel, improved materials for magnetic data storage and spintronic devices, compounds that allow a tailoring of magnetic domain shapes and sizes are essential. Good candidates are materials with intrinsic anisotropies or competing interactions, as they are prone to host various domain phases that can be easily and precisely selected by external tuning parameters such as temperature and magnetic field. Here, we utilize vector magnetic fields to visualize directly the magnetic anisotropy in the uniaxial ferromagnet CeRu2Ga2B. We demonstrate a feasible control both globally and locally of domain shapes and sizes by the external field as well as a smooth transition from single stripe to bubble domains, which opens the door to future applications based on magnetic domain tailoring.
Similar content being viewed by others
Introduction
The discovery of a skyrmion lattice phase in MnSi1 has been a prime example for self-organized, tunable microscopic magnetic structures with a great prospect in future applications. Subsequent research efforts focused on the non-centrosymmetric, ferromagnetic intermetallics2,3,4 and multiferroics5. On the other hand, the observation of skyrmions in a bilayer manganite compound with an inversion center6 has shifted the spotlight to the uniaxial ferromagnets, as they allow a tuning of the magnetic behavior based on their shape anisotropy rather than on intrinsic parameters such as the Dzyaloshinskii-Moriya anisotropy.
The recently reported series of Ce-based intermetallics CeRu2X2M (Xâ=âAl, Ga; Mâ=âB, C) offers an enticing playground to explore various magnetic phases and their respective transitions dictated by the balance between Kondo and Ruderman-Kittel-Kasuya-Yosida (RKKY) interactions7,8. The title compound CeRu2Ga2B (CRGB) exhibits ferromagnetic order below the Curie temperature of TCâ=â15.4âK as a result of RKKY interaction magnetic moments of Ceriumâs localized 4f electrons7. A strong, Ising-like uniaxial anisotropy has been revealed9, with the magnetic easy-axis coinciding with the crystallographic c axis, due to the crystalline electric field splitting, which results in the population of the ground state doublet10. While the bulk magnetic properties have been characterized, to some extent, the local domain structure still remains elusive. The influence of vector magnetic fields on the microscopic domain structure as well as the possibility to uncover unusual metastable magnetic phases are interesting, yet open issues for strongly uniaxial ferromagnets.
In this Article, we present the local magnetic state of a 4f-uniaxial-ferromagnet CRGB by using a novel magnetic force microscope (MFM) with vector magnetic fields. A periodic modulation of the out-of-plane magnetic moment together with the bubble domain size is directly visualized as the field rotates from the easy axis to the hard axis. This result evidences for the first time an Ising-like domain shape response to the vector field. Our study furthermore demonstrates a tuning of the magnetic domain structure globally via external magnetic field and temperature control, as well as locally via the MFM tip, allowing us to estimate the manipulation force for individual domains. Our experimental observations are supported by theoretical modeling based on time-dependent Ginzburg-Landau dynamics. The highly sensitive, metastable domains observed pave a venue for magnetic memory and spin-torque device applications via magnetic domain engineering.
Magnetic Anisotropy
A basic magnetic characterization of CRGB is given in Fig. 1. The initial bubble state at 10.9âK shown in Fig. 1a is obtained after field-cooling the sample through TC with Hzâ=â200 Oe. As the temperature approaches TC, the local magnetic moments decrease and the MFM contrast vanishes (see Fig. 1aâf). The comparison between the maximum frequency shift measured in MFM and the magnetization data (open blue squares vs. solid lines in Fig. 1g) reveals a reasonable agreement, considering the fundamental difference between the surface- and bulk sensitive experimental techniques. The averaged bubble size, obtained from a fast Fourier transform (FFT) analysis of the images, starts to increase considerably close to TC, succeeded by a slight decrease approximately 1âK below TC (see inset in Fig. 1f). The initial increase in bubble diameter d follows a thermally activated behavior of the domain volume, observed in rare earth-transition metal alloys, , where δ corresponds to the domain wall thickness11. A fit, shown as a thick red solid line in the inset of Fig. 1f, describes our data very well, and yields δâââ170ânm. Note that the magnitude of a domain wall thickness δ may be slightly different from the actual value due to both the tip effect and the imaging condition. In the lower half of Fig. 1e we show the MFM image obtained at 15.4âK rescaled to its full intensity, to emphasize a crossover from round to elongated/distorted bubble domains close to TC. This temperature-driven crossover leads to the decrease of the average domain size. It is related to a reduction of the effective magnetic anisotropy, which becomes comparable to the dipolar interactions close to TC12,13. The strong uniaxial anisotropy of CRGB due to the Ising-like spin character (sketched in the inset of Fig. 1g) is evident in the magnetization curves of Fig. 1h. While the saturation magnetization Ms at Tâ=â8âK is reached around Hâ=â1.5âkOe for H//c (along the easy axis), it requires slightly higher fields of Hâ=â2.5âkOe for Îâ=â45° (see arrows in Fig. 1h) and up to Hâ¼20âkOe for in-plane fields (not shown). The magnetocrystalline anisotropy energy as a function of field angle is schematically sketched in Fig. 1i. From the M-H curve along the hard axis we estimate the first and second order magnetocrystalline anisotropy constants at Tâ=â8âK as K1â=â1.37·105 erg/cm3 and K2â=â2.10·105erg/cm3â14. The total anisotropy energy for a uniaxial system is given by and both K1 and K2 are positive. Therefore, the anisotropy energy will be minimized for out-of-plane magnetic fields (Îâ=â0° and 180°)15.
To understand the impact of this huge intrinsic anisotropy microscopically, we perform MFM experiments in vector magnetic fields. Figure 2aâf show MFM images of the field-cooled state with Hâ=â200âOe for various field angles Î, indicated in each image and in Fig. 2g, at 8âK. Field-cooling in the out-of-plane orientation (Fig. 2a) leads to bubble domains with an average diameter of about 1âμm and a strong signal intensity. Tilting the field by 45° towards the plane has no apparent effect on the average bubble size and periodicity, as evidenced by FFT shown in Fig. 2i (brown vs. green curve), where line profiles through the 2-dimensional FFT image are shown (see the red dashed line in Fig. 2h). On the other hand, a pronounced change is observed in the MFM intensity: Bubble domains are of considerably diminished contrast, as seen in Fig. 2b and in the histogram (brown line in Fig. 2j), where the frequency span is rather narrow and the signal centers heavily around Îfâ=â0. As an external field of 200âOe is much smaller than the coercive field of the MFM tip at low temperatures (â¼1500âOe at 4âK), we rule out a modification of the tip magnetization. We therefore conclude that the out-of-plane component of the magnetic moment decreases due to canted spins, following the direction of the external magnetic field at Îâ=â45°. A closer look at the angular dependence of the MFM contrast reveals that the out-of-plane moment varies in a four-fold fashion â its full intensity is restored at Îâ=â90°, 180°, (270°, not shown) and 360° (), while it is minimized at 45° and 135° (as well as 225° and 315°, not shown). Comparing this behavior with the M-H curves in Fig. 1h, we find that aligning spins at 45° within the ac plane is relatively easy, while there is an immense energy barrier for rotating spins in-plane (see also cartoon in Fig. 1i). Hence, field-cooling CRGB in a weak in-plane magnetic field (Îâ=â90°) of 200âOe leaves the spins mostly aligned along their easy, out-of-plane axis (Fig. 2c). It also causes a zero-net magnetic moment, as neither the âupâ- nor the âdownâ-direction is preferred. Note that both average bubble domain size and periodicity are substantially decreased at Îâ=â90°. We can understand this phenomenon by considering the dipolar energy: For magnetic fields along the easy axis (H||c) the magnetostatic energy can be partially compensated, resulting in larger domains. Consequently, magnetic fields along the hard axis have no compensating effect and the average domain size will be reduced to minimize the magnetostatic energy15. As the external magnetic field continues to rotate back out-of-plane, the domain pattern for Îâ=â180° in Fig. 2e is essentially an inverted version of Fig. 2a, indicated by the MFM contrast as well as the histograms (cf. 0° with a negative net magnetization and 180° with a positive net magnetization in Fig. 2j). Field-cooling the sample in a magnetic field with Îâ=â360° (Fig. 2f) reproduces qualitatively the original MFM image of Fig. 2a. We note, however, that the local distribution of bubble domains has changed, suggesting that the bubble formation is not dominated by a nucleation process around local impurities.
Entering the bubble domain phase requires the presence of a threshold magnetic field (see also Fig. 3). We investigated the critical field strength for entering the bubble domain phase as function of Î in Fig. 2k. As we rotate the field from out-of-plane to Îâ=â75°, the threshold field increases. In contrast to fully out-of-plane fields, tilted fields will partially compensate the uniaxial anisotropy. At the same time, the z-component of the field decreases with increasing Î, thus accounting for the larger threshold-fields. Remarkably, above Îâ=â75°, this trend is reversed, together with the MFM contrast (cf. Fig. 2a and c). This behavior suggests that the magnetocrystalline anisotropy energy increases rapidly for , and becomes too large to be overcome by external magnetic fields of medium strength (i.e., far below saturation). This assumption is supported by the angle dependent magnetization curves in Fig. 1h, where a gradual change in initial slope for is followed by a more drastic change for . Therefore, large Î values can effectively reduce the out-of-plane anisotropy, while inducing a weak in-plane anisotropy. Ultimately, this leads to merging of bright bubbles into maze-like structures, enclosing dark, bubble-like areas, i.e., the observed reversal of the MFM contrast in Fig. 2b,c.
Domain Manipulation
If we decrease H below the threshold field during the field-cool process, we obtain dendritic domains instead (Fig. 3a). Such a domain structure is characteristic for uniaxial magnets and results from a competition of tendencies to minimize the dipolar energy (by partitioning into smaller domains) and to minimize the domain wall energy (by decreasing the overall length of domain walls and hence forming larger domains)16,17,18. After field-cooling in small out-of-plane fields (Fig. 3b and c), the additional Zeeman energy results in an imbalance between âupâ- and âdownâ-domains, and bubble domains emerge again once a critical area fraction has been reached (see below). Between 600âOe and 800âOe the domain pattern changes from bubbles to larger stripes (Fig. 3eâg). The increase in the domain size with increasing magnetic field is counter-intuitive, as one would expect a decrease and subsequent annihilation of minority domains as the Zeeman energy term increases. Instead, we observe a pronounced decrease in the domain wall density. This signals that the energy gain from reducing the number of canted and in-plane spins within the domain walls has to outweigh the energy cost of increasing the area of minority domains. At higher fields the stripes straighten and align at roughly 45° from the a and the b axes, i.e., along the [110] and [10] direction (Fig. 3j). This orientational preference is not clearly understood yet, although it is known that single crystalline samples of CRGB suffer from a certain degree of Ga-B intersite mixing7. A recent density functional theory study19 found that such a replacement can promote ferromagnetic superexchange. Considering the resulting exchange paths of Ce-Ga-Ce are along [110] and [10] would explain the observed preferred stripe direction. Around 1500âOe a nearly homogeneous image is obtained, indicating that H is close to saturation (Fig. 3l). A theoretical investigation reveals that a critical area fraction exists (with Amin being the area of the minority domains and Atotal the total area of the MFM frame), that separates the stripe domain phase from the bubble domain phase20. In Fig. 3m we plot the area fraction f as a function of magnetic field Hz (see blue dots). We find that for CRGB the area fraction f in the bubble phase is slightly below 0.2, while it rises above 0.2 in the stripe phase. Therefore, a critical area fraction of acts as the dividing line, indicated by the dashed blue line. This value is lower than the theoretically predicted fcâ=â0.2820. On the other hand, perturbations to the theory, such as in-plane anisotropies (e.g., due to intersite mixing), can lead to a reduction of fc20. At large fields the area fraction continues to decrease and eventually approaches fc, suggesting the possibility of inducing a bubble domain phase close to saturation (as we shall see in the next section, this is in fact observed). Based on our results we can now construct a H-T phase diagram for the different magnetic domains, see Fig. 3n. Bubble domains emerging at small, finite fields transition to elongated bubbles and stripes with increasing Hz. The saturation fields obtained from MFM experiments (blue spheres) complement the magnetization data (open white boxes) very well.
In contrast to CRGB, the antiferromagnetically coupled [(Co/Pt)8/Co/Ru]18 multilayers21,22, and the bilayer manganite La2â2xSr1+2xMn2O718 with a weak out-of-plane anisotropy both host bubble domain phases only in the vicinity of the magnetic saturation. In the case of CRGB the pre-existing uniaxial anisotropy is already very large. Therefore, (i) the threshold field for entering the bubble phase is relatively smaller, and (ii) the annihilation of minority domains occurs only at high fields. This clearly separates the threshold field for the bubble phase from the magnetic saturation.
As we have seen so far, the magnetic phases in CRGB decisively depend on the sampleâs field and temperature history. This behavior can be exploited to tailor magnetic domain structures. Starting from a homogeneous bubble domain phase by field-cooling to 8âK in Hzâ=â200âOe (Fig. 4a), we increase the magnetic field up to 1650âOe, which is close to the saturation field (Fig. 4b). Reducing the field down to 1540âOe leads to the re-occurrence of a single, round shaped magnetic domain in the upper right corner (Fig. 4c). With a further reduction of the magnetic field the domain expands to form a stripe running diagonally across the surface (Fig. 4d), as observed in field-cooled experiments (Fig. 3) and supported by theoretical modeling (see below). In order to check the reversibility, we increase the magnetic field up to 1630âOe (Fig. 4eâg). Interestingly, the stripe breaks into robust bubbles that only decrease in size as the field approaches saturation. Hence there must exist strong, intrinsic pinning centers that exert little influence on the nucleation of domains while field-cooling. Decreasing the field again from 1630âOe, the bubble domains gain in size (and hence, in MFM intensity) but they do not merge back into a stripe. Instead, the domain walls remain as barriers, resulting in a broken-up stripe as the magnetic field decreases further (Fig. 4hâj). Meanwhile, the stripe segments widen and start to branch out, while keeping the separating domain wall intact (Fig. 4kâl). The final domain configuration at zero fields resembles the zero-field cooled image in Fig. 3a shape-wise, but the scale is different, with much larger structures after field-cycling. The net magnetization estimated from MFM images is close to zero in both cases, and the M-H curves show no significant hysteretic behavior, highlighting that the initial and final states are identical from the bulk point of view. A MFM study of the uniaxial ferromagnet Nd-Fe-B comparing domain structures after thermally demagnetizing and demagnetizing by field reversal found a similar domain size difference17. This common observation suggests that systems with a strong uniaxial anisotropy reach their local, microscopic magnetic equilibrium state only after zero-field-cooling, while a demagnetization process via field-cycling leads to a metastable domain state.
While the domain manipulation via vector magnetic fields affects the system globally, we can also manipulate individual bubbles by using the magnetic moment of the tip with a reduced tip-sample distance dts. In Fig. 5a we create a diluted bubble domain pattern through field-cooling in Hzâ=â700 Oe down to 9âK. The image was obtained with dtsâ=â300ânm. In order to manipulate the domain pattern, we approach two bubbles consecutively (marked by yellow circles) by the magnetic tip with dtsâ=â20ânm. Imaging the surface after this procedure with a restored dts of 300ânm (Fig. 5b), we notice a successful manipulation, as the bubbles were erased, highlighting opposite directions of magnetization for the bubbles and the tip. In the next step, we position our tip towards the bubble marked by a blue circle (dtsâ=â50ânm) and move the tip laterally by â700ânm, dragging the bubble domain along (Fig. 5c). As a final step, we attempt to delete the dragged bubble via controlled tip-approach (Fig. 5d). Since we know the magnetic moment mtip of the MFM tip (see Supplementary Material for details), we can estimate the force necessary to manipulate individual bubbles. We extract the force between the tip and an individual bubble by applying a simple monopole-monopole approximation23, , where corresponds to the magnetic flux through an individual bubble. We use the signal of a magnetic flux quantum measured on a superconducting Nb film in a comparative experiment to approximate (see Supplementary material for details). With these values we find that a deleting process takes place through nN, while the movement of a bubble requires a force of ânN, corresponding to an energy cost of 2·10â15âJ for a movement over a distance of 1âμm. The possibility of dragging and deleting single bubble domains in a bulk ferromagnet by the local magnetic tip without a restoring force that would result in a wiggling motion23 suggests that these domains can be identified as point-like, 0-dimensional objects, rather than 1-dimensional domain strings that penetrate the whole bulk. This assumption is further solidified by the vector magnet experiments (Fig. 2), which did not unveil an elongation of bubbles or a transition into a stripe phase (i.e., the rotation of a cylindrical domain from out-of-plane to in-plane). Instead, bubbles emerge within the ab plane even for fields perpendicular to the c axis. As we will show in the following, theoretical modeling of magnetic domains can well reproduce our experimental observations.
Domain Modeling
We now turn to a theoretical model of the magnetic system in CRGB to describe the transition among bubbles and stripes. We begin with an effective energy obtained by expanding in powers of the local crystal magnetization ,
We work in dimensionless units with |S|â=â1 and E0â=â1. An external field H points in the direction, K controls the easy-axis anisotropy in Sz, and Î denotes the interaction operator. To capture the long-wavelength physics, we expand Î in even powers of â2, and truncate to obtain , or in Fourier space , with a the lattice constant and q0 the preferred spatial frequency. To capture the short-wavelength physics of domain walls, we also apply an ultraviolet cut-off. A large modulation length scale emerges if is positive and small. In a 3-dimensional crystal with low carrier density, electron mediated RKKY interactions typically favor ferromagnetic (kâ=â0) ordering. If competing interactions (e.g., nearest-neighbor antiferromagnetic superexchange acting on Ce moments) of the form exist, then the total interaction may favor a spatially modulated (kâ>â0) phase. The preferred spatial frequency is small if c2 is slightly larger than c1. Empirically, this is what we observe: the bubble domains have a diameter âμm much larger than the lattice constant aâ=â4.187âà , such that q0âââ0.005. Further modeling details are provided in the Supplementary Information.
To explore the magnetic domains predicted by our model, we use time-dependent Ginzburg-Landau (TDGL) dynamics, , where η(x, t) is Gaussian white noise. TDGL dynamics is the overdamped limit of physical Landau-Lifshitz-Gilbert dynamics. To construct a dense configuration of bubble domains, we choose dimensionless parameters Kâ=â0.25, , and field cool from kBTâ=ââ to 0.01 at a fixed dimensionless field H. In Fig. 6a,b we plot a bulk cross section at Hâ=â0.16 and Hâ=â0.22, respectively, colored by the local value of Sz, and find good qualitative agreement with the corresponding CRGB experiments (Figs 3c,d and 4a,b). We note that a finite K is important in stabilizing compact bubbles. At Hâââ0.22, bubble annihilation occurs analogous to our experimental observation (Fig. 3d,e). Subsequent decrease of the field from Hâ=â0.22 to Hâââ0.12 causes a single bubble to elongate into an extended domain string (Fig. 6c,d), again phenomenologically consistent with our experimental data (Fig. 4c,d).
Our comprehensive MFM study highlights the variety of magnetic metastable phases in CeRu2Ga2B and their manipulation as a function of temperature, magnetic field strength and direction. We find the emergence of bubble domains over an extended temperature range as we field-cool the sample in weak out-of-plane magnetic fields. A vector magnet study details the influence of the magnetic field direction on the domain formation in strongly anisotropic ferromagnets. Our field-cycling experiments demonstrate a feasible control over the global domain shape and size, while a magnetic tip achieves a local, selective manipulation of individual bubble domains, opening the door for in-situ domain engineering in uniaxial ferromagnets.
Methods
Single crystals of CeRu2Ga2B were grown via tri-arc melting synthesis as previously reported7. Magnetization measurements were performed in a superconducting quantum interference device (Quantum Design). The dimensions of the sample under investigation are 2.0âmmâÃâ0.9âmmâÃâ0.5âmm, resulting in the demagnetization factors Daâ=â0.138 and Dcâ=â054724. The single crystal was oriented via polarized Raman scattering (WITec alpha 300âR), comparing the intensities of Galliumâs A1g and Eg phonon modes as a function of crystal orientation25.
MFM measurements were performed in a low temperature MFM system with a home-built MFM probe inside a vector magnet with a field and temperature range of 2-2-9âT (in x-y-z direction) and 0.3â300âK, respectively26. All experiments were carried out with commercially available MFM tips (PPP-MFMR, Nanosensors). The magnetic force between the tip and the sample results in a frequency shift Îf of the tipâs resonance frequency f0, which can be related to the force gradient via , where k is the spring constant of the tip.
Additional Information
How to cite this article: Wulferding, D. et al. Domain engineering of the metastable domains in the 4f-uniaxial-ferromagnet CeRu2Ga2B. Sci. Rep. 7, 46296; doi: 10.1038/srep46296 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Mühlbauer, S. et al. Skyrmion Lattice in a Chiral Magnet. Science 323, 915 (2009).
Yu, X. Z. et al. Real-space observation of a two-dimensional skyrmion crystal. Nature 465, 901 (2010).
Münzer, W. et al. Skyrmion lattice in the doped semiconductor Fe1âx Co x Si. Phys. Rev. B 81, 041203(R) (2010).
Yu, X. Z. et al. Near room-temperature formation of a skyrmion crystal in thin-films of the helimagnet FeGe. Nature Mater. 10, 106 (2011).
Seki, S., Yu, X. Z., Ishiwata, S. & Tokura, Y. Observation of Skyrmions in a Multiferroic Material. Science 336, 198 (2012).
Yu, X. Z. et al. Biskyrmion states and their current-driven motion in a layered manganite. Nat. Commun. 5, 3198 (2014).
Baumbach, R. E. et al. Local moment ferromagnetism in CeRu2Ga2B. J. Phys.: Condens. Matter 24, 185702 (2012).
Baumbach, R. E. et al. CeRu2Al2B: A local-moment 4f magnet with a complex T-H phase diagram. Phys. Rev. B 85, 094422 (2012).
Sakai, H. et al. NMR study for 4f-localized ferromagnet CeRu2Ga2B. Phys. Rev. B 86, 094402 (2012).
Matsuno, H. et al. Ising-Type Ferromagnetic Ground State Driven by Anisotropic câf Hybridization in CeRu2Al2B. J. Phys. Soc. Jpn. 81, 073705 (2012).
Labrune, M., Rio, F. & Bernstein, P. Temperature dependence of the critical radius of domains in rare earth-transition metal alloys for magnetic media. Thin Solid Films 175, 305 (1989).
Choi, J. et al. Magnetic Bubble Domain Phase at the Spin Reorientation Transition of Ultrathin Fe/Ni/Cu(001) Film. Phys. Rev. Lett. 98, 207205 (2007).
Won, C. et al. Magnetic stripe melting at the spin reorientation transition in Fe/Ni/Cu(001). Phys. Rev. B 71, 224429 (2005).
Durst, K.-D. & Kronmüller, H. Determination of intrinsic magnetic material parameters of Nd2Fe14B from magnetic measurements of sintered Nd15Fe77B8 magnets. J. Magn. Magn. Mater. 59, 86 (1986).
Cullity, B. D. & Graham, C. D. Introduction to Magnetic Materials. John Wiley & Sons, Inc., Second Edition, Publication, New Jersey, (2009).
Goodenough, J. B. Interpretation of Domain Patterns Recently Found in BiMn and SiFe Alloys. Phys. Rev. 102, 356 (1956).
Thielsch, J. et al. In situ magnetic force microscope studies of magnetization reversal of interaction domains in hot deformed Nd-Fe-B magnets. J. Appl. Phys. 111, 103901 (2012).
Jeong, J. et al. Magnetic domain tuning and the emergence of bubble domains in the bilayer manganite La2â2x Sr1+2x Mn2O7 (xâ=â0.32). Phys. Rev. B 92, 054426 (2015).
Hua, L. & Tang, Y. First-principle study of the electronic structure and magnetic properties of CeRu2Al2B. Solid State Communications 152, 2105 (2012).
Ng, K.-O. & Vanderbilt, D. Stability of periodic domain structures in a two-dimensional dipolar model. Phys. Rev. B 52, 2177 (1995).
Bran, C. et al. Evolution of stripe and bubble domains in antiferromagnetically coupled [(Co/Pt)8/Co/Ru]18 multilayers. Phys. Rev. B 79, 024430 (2009).
Kiselev, N. S. et al. Metamagnetic domains in antiferromagnetically coupled multilayers with perpendicular anisotropy. Phys. Rev. B 81, 054409 (2010).
Auslaender, O. M. et al. Mechanics of individual isolated vortices in a cuprate superconductor. Nature Phys. 5, 35 (2009).
Aharoni, A. Demagnetizing factors for rectangular ferromagnetic prisms. J. Appl. Phys. 83, 3432 (1998).
Drachuck, G. et al. New Perspectives for Cuprate Research: (Ca x La1âx )(Ba1.75âx La0.25+x )Cu3O y Single Crystals. J. Supercond. Novel Magn. 25, 2331 (2012).
Yang, J. et al. Construction of a 3He magnetic force microscope with a vector magnet. Rev. Sci. Instrum. 87, 023704 (2016).
Acknowledgements
This work was supported by the Institute for Basic Science (IBS), Grant No. IBS-R014-D1. Work at Los Alamos was conducted under the auspices of the U.S. Department of Energy, Office of Basic Energy Sciences, Division of Materials Sciences and Engineering.
Author information
Authors and Affiliations
Contributions
J.K. conceived the original idea and supervised the project. D.W., H.K., I.Y., O.A., J.J., R.M., and J.K. performed the MFM experiments. R.B., E.B., F.R. made single crystals and measured transport properties. M.L., D.W., H.C., O.A., L.C., J.T. measured the polarized Raman spectrum of CRGB single crystal, and analyzed its orientation and global magnetization. K.B., Y.K., and I.M. performed the analytical and numerical work. D.W. and J.K. analyzed the data, and wrote the manuscript. All authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the articleâs Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wulferding, D., Kim, H., Yang, I. et al. Domain engineering of the metastable domains in the 4f-uniaxial-ferromagnet CeRu2Ga2B. Sci Rep 7, 46296 (2017). https://doi.org/10.1038/srep46296
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep46296