ESPECIFICACIÓN DE PROCEDIMIENTO DE SOLDADURA DE CAÑERÍA (MAPA DE SOLDADURA DE CAÑERÍA) 13213-FI-SIG-001

Nº REVISIÓN 0 CLIENTE Celulosa Arauco y Constitución DOC. REFERENCIA PROYECTO MONTAJE ELECTROMECÁNICO NUEVAS PRENSAS DE BLANQUEO
ELABORADO JUAN OLAVE B. OBRA Nº 13213
APROVADO UBICACIÓN Nueva Aldea CONTRATO GIC 4007
FECHA 8/8/2013 NORMA ASMEB31.3

PRECALENTAMIENTO
TIPO DE SOLDADURA MATERIAL DE

ESPECIFICACIÓN DEL

ESPERSOR (mmm)
ENSAYO NO DESTRUCTIVOS
RANURA FILETE RELLENO
CLASES DE

Ø CAÑERIA
MATERIAL

MATERIAL

MATERIAL

LONGITUDINAL
UNION A TOPE

REFORZADAS

MIN ºc
DERIVACION
ARRANQUE

ACCESORY
ITEM

WPS
FLANGERS
LINEA DE SERVICIO

RELLENO
SOCKET

REMATE
UNION
O SISTEMA

RAÍZ

RX

PT

VT
X <2 TODOS P8-505 ER-316L ER-316L 30 10% 100%
X 2 a 4 TODOS P8-505 ER-316L ER-316L 30 10% 100%
X >4 TODOS P8-505 ER-316L ER-316L 30 10% 100%
ACERO INOXIDABLE

X TODOS TODOS P8-505 ER-316L ER-316L 30 10% 100%

X >4 TODOS P8-505 ER-316L ER-316L 30 10% 100%
B55, B58, V58, W10, X <4 TODOS P8-505 ER-316L ER-316L 30 10% 100%
1 150H1A W30, W34, W35
316L
X >4 TODOS P8-505 ER-316L ER-316L 30 10% 100%
X <4 TODOS P8-505 ER-316L ER-316L 30 10% 100%
X TODOS TODOS P8-505 ER-316L ER-316L 30 10% 100%
X TODOS TODOS P8-505 ER-316L ER-316L 30 10% 100%
X TODOS TODOS P8-505 ER-316L ER-316L 30 10% 100%
X <2 TODOS P8-03 ER-308 ER-308 30 10% 100%
X 2 a 4 TODOS P8-03 ER-308 ER-308 30 10% 100%
X >4 TODOS P8-03 ER-308 ER-308 30 10% 100%
ACERO INOXIDABLE

X TODOS TODOS P8-03 ER-308 ER-308 30 10% 100%

X >4 TODOS P8-03 ER-308 ER-308 30 10% 100%
2 150H1A 304L X <4 TODOS P8-03 ER-308 ER-308 30 10% 100%
X >4 TODOS P8-03 ER-308 ER-308 30 10% 100%
X <4 TODOS P8-03 ER-308 ER-308 30 10% 100%
X TODOS TODOS P8-03 ER-308 ER-308 30 10% 100%
X TODOS TODOS P8-03 ER-308 ER-308 30 10% 100%
X TODOS TODOS P8-03 ER-308 ER-308 30 10% 100%
X <2 TODOS SAF-2205 ER-209L E-209L 30 10% 100%
ACERO INOXIDABLE DUPLEX

X 2 a 4 TODOS SAF-2205 ER-209L E-209L 30 10% 100%

X >4 TODOS SAF-2205 ER-209L E-209L 30 10% 100%
X TODOS TODOS SAF-2205 ER-209L E-209L 30 10% 100%
X >4 TODOS SAF-2205 ER-209L E-209L 30 10% 100%
3 150H1A 2205 X <4 TODOS SAF-2205 ER-209L E-209L 30 10% 100%
X >4 TODOS SAF-2205 ER-209L E-209L 30 10% 100%
X <4 TODOS SAF-2205 ER-209L E-209L 30 10% 100%
X TODOS TODOS SAF-2205 ER-209L E-209L 30 10% 100%
X TODOS TODOS SAF-2205 ER-209L E-209L 30 10% 100%
X TODOS TODOS SAF-2205 ER-209L E-209L 30 10% 100%
X <2 TODOS P1-01 E-6010 E-7018 30 10% 100%
X 2 a 4 TODOS P1-01 E-6010 E-7018 30 10% 100%
X >4 TODOS P1-01 E-6010 E-7018 30 10% 100%
ACERO CARBONO

X TODOS TODOS P1-01 E-6010 E-7018 30 10% 100%

X >4 TODOS P1-01 E-6010 E-7018 30 10% 100%
A-53 / A-516 /
4
A-106
 ACERO CARBONO
A-53 / A-516 / X <4 TODOS P1-01 E-6010 E-7018 30 10% 100%
4
A-106
X >4 TODOS P1-01 E-6010 E-7018 30 10% 100%
X <4 TODOS P1-01 E-6010 E-7018 30 10% 100%
X TODOS TODOS P1-01 E-6010 E-7018 30 10% 100%
X TODOS TODOS P1-01 E-6010 E-7018 30 10% 100%
X TODOS TODOS P1-01 E-6010 E-7018 30 10% 100%
X <2 TODOS 100%
X 2 a4 TODOS 100%
X >4 TODOS 100%
X TODOS TODOS 100%
X >4 TODOS 100%
FRP

5 B55, P55, V55 X <4 TODOS 100%

X >4 TODOS 100%
X <4 TODOS 100%
X TODOS TODOS 100%
X TODOS TODOS 100%
X TODOS TODOS 100%
NOTAS FLUIDO:
1.- El Proceso de soldadura GTAW, SMAW, GMAW, o FCAW, se puede aplicar usando un WPS Calificacdo de acuerdo B55 Agua blanca, etapa de dioxido de cloro
a ASME sección IX. B58 Agua Blanca
2.-Antes del Proceso de soldadura, en la clase P55 Pulpa, etapa de dioxido de carbono
de material GSl,el Galvanizado se debe retirar con un proceso de esmerilado. W10 Agua Potable
W30 Agua caliente
W34 Agua
W35 Agua
Caliente