Flexural Performance of RC Beams Strengthened by Carbon Fiber Reinforced Polymer (CFRP) Laminates

Published by : http://www.ijert.org International Journal of Engineering Research & Technology (IJERT) ISSN: 2278-0181 Vol. 9 Issue 04, April-2020 Flexural Performance of RC Beams Strengthened by Carbon Fiber Reinforced Polymer (CFRP) Laminates Steve Efe1, Jacob Oluwoye2 1 Department of Civil Engineering, Morgan State University, Baltimore Maryland, U.S. 2 Alabama A and M university, Huntsville, Alabama, U.S Abstract:- The use of composite materials and strengthening systems have gained attention for structural reinforcement and strengthening solutions in concrete, masonry and timber structures in need of repair or upgrade. While many studies have addressed external strengthening of undamaged concrete members with various spacing of the wrappings, design considerations such as member cross-section, stirrup and reinforcement ratio, and level of strengthening, little or no information exist on repair of previously damaged members. This paper seeks to consider the performance of prior-damaged reinforced concrete (RC) beams strengthened by externally bonded carbon fiber reinforcement polymer (CFRP) laminates to enhance the beam’s load carrying capacity and failure mode. The five (5) beam specimens (1 plain concrete beam, 1 control RC beam-B1, 1 pre-loaded CFRP-B2 wrapped RC beam-B3, and 2 CFRP wrapped RC beams-B4 and B5) of dimensions of 100 mm × 200 mm × 1520 mm were reinforced with two 12.7 mm diameter bars as main reinforcements, two 9.5 mm diameter two-legged stirrups spaced at 150 mm with a clear cover of 25 mm. CFRP strips of width of 25 mm and a length of 400 mm were epoxy bonded to the underside of the CFRP wrapped beams with a centreto-centre spacing of 120 mm. Ultimate loads, load-deflection relation and failure pattern were recorded for each beam as the beam failure progression and damage states were observed. The results of the study indicate that, 1) there is a marginal increase in first crack and ultimate loads. The first crack load increase was 15-40%, while that in the ultimate load was between 5-18%; 2) the CFRP wrapped beams experienced a flexural mode and found to be due to debonding of the FRP wraps. Keywords: Concrete; fabrics; FRP; repair; shear 1. INTRODUCTION The degradation of infrastructure in and around the world requires urgent attention in the form of replacement, rehabilitation or repair. Concrete structures deterioration or damage during its lifetime can be due to physical (abrasion, wear, earthquake, overloading, impact, erosion, thermal expansion, settlement freeze-thaw cycles, etc.), chemical factors (sulphate attack and corrosion of rebars), and construction and design deficiencies. On many occasions, corrosion of rebars may trigger off cracking and spalling of concrete, coupled with deterioration in the strength of RC structural members. The response and service life of such structures is greatly altered as a result and such situations IJERTV9IS040207 call for repairs of affected zones and sometimes replacement of the entire structure (Esfahani et al. 2007). Various techniques are available for concrete structures repair and rehabilitation to close-up defect and mitigate failure. Steel plate bonding, steel jacketing and FRP sheets are methods of choice in strengthening of structural members. FRP laminates are widely used as external reinforcement compared to steel plate due to high tensile strength, high strength–weight ratio and corrosion resistance, however bond degradation and installation difficulty are still some challenges to overcome. Externally bonded FRP laminates and fabrics can be used to increase the capacity of corroded beams as well as its shear and flexural strength (Ashour et al. 2004). These FRP laminates which are manufactured as sheets or strips by pultrusion are typically made of unidirectional or bidirectional carbon or glass fiber epoxy bonded to concrete structures. Sing-ping Chiew et al (2007) conducted an experimental study on the flexural performance of retrofitted beams wrapped with FRP laminates which were bonded to the tension face of the flexural RC beams. The study found out that the strengthening ratio increases linearly with the increase of the axial rigidity of the external CFRP laminates. Jumaat et al. (2010) evaluated the effectiveness of external strengthening on RC beams cracking moment, maximum moment, deflection, and crack patterns. An increase (up to 110%) in the cracking moment of the CFRP repaired beams was noticed. The deflection decreased inversely with the number of CFRP layers on each beam. This, alternatively, caused the stiffness to increase while the crack patterns are different between the control and the CFRP repaired beams. The control had wider cracks while the repaired beams showed smaller cracks at failure. Also ACI 440 documents the effectiveness (up to 160 %) of FRP laminate external bonding to improve the capacity of RC members. While many studies have addressed external strengthening of undamaged concrete members with having various spacing of the wrappings, design considerations such as member cross-section, stirrup and reinforcement ratio, and level of strengthening , little or no information exist on repair of previously damaged members. With nearly one-third of the highway bridges in the United States currently in need of repair or replacements, innovative bridge concepts and www.ijert.org (This work is licensed under a Creative Commons Attribution 4.0 International License.) 231 Published by : http://www.ijert.org International Journal of Engineering Research & Technology (IJERT) ISSN: 2278-0181 Vol. 9 Issue 04, April-2020 legged stirrups with a clear cover of 35 mm [1.5 inches] and spaced at 120 mm [4.8 inches]. The geometry, reinforcement and symmetric loading set up of the beams are shown in Figure 1. The concrete mix was designed according to ACI 211.4R-08, and the mix proportion was obtained as 1: 2.2: 3.0 with a water-cement ratio of 0.46. For each casting (consisting of the plain, control beam and the beam to be wrapped), three 6 inches diameter and 12 inches height concrete cylinder were cast as companion specimens. The 2. METHODOLOGY concrete mix proportions of the concrete constituent A. RC Specimen materials are shown in Table 1. All the five beams used for this experiment were designed A waterproof, multipurpose adhesive based on solvent- free according to ACI 318-16 and ACI 440.2R.08 to fail in flexure. The RC beams dimensions were 100 mm x 200 mm x epoxy resin with a cure time of 10 hours at 20˚ C. was used 1520. Two No. 4 diameter bars were embedded at the bottom and for the bonding of the fiber fabric to the repaired top of the beam. No. 3 diameter bars were considered as two specimens. Table 1: Concrete Mix Design Proportions construction methods to maintain the structural integrity and cost saving and cost-effective maintenance are vital (Thompson et al. 2007). In many cases, damages to highway infrastructure and bridges due to over-height collisions can be significant problem. This paper thus seeks to evaluate the flexural performance of damaged RC beams retrofitted with CFRP wraps. Weight, kN/m3 3.23 1.48 7.06 3.74 7.55 Material Ordinary Portland Cement Water Natural Sand Coarse Aggregate 3/8 inches Coarse Aggregate ½ inches Table 2: Compressive strength of companion specimen and beams Average diameter, m Height, m Density, kN/m3 Maximum load at failure, kN Cylinder compressive strength, kN/m2 Average cylinder comp. Strength, kN/m2 The formwork for the RC specimen was constructed to be rigid and water-proof and the beam steel cage consisting of the longitudinal bars and stirrup were placed in formwork. The concrete was mixed using a mixer, poured and compacted in the formwork. The concrete was left to cure for 30 hours using wet burlap at the Concrete Materials laboratory at Morgan State University before being tested. Two loading regimes were implemented: 1) Three point loading beam testing procedure was adopted and incremental loads of 10 kN were applied in flexure to the beam until the ultimate load was reached. Data acquisition of deflection at the left, midspan and right of the RC beams was carried out using the linear variable displacement transducers (LVDT) which records at each loading interval as shown in Figure 1. Omega Pre-wired strain gauges of a length of 3 mm and resistance of 120 Ω were attached to the stirrups in the shear span to measure strain as shown in IJERTV9IS040207 Specimen 1 0.15 0.3 23044.6 123.2 34646.2 Specimen 2 0.15 0.3 24018.5 139.7 35148.9 34698.8 Specimen 3 0.15 0.3 23295.9 113.9 34497.7 Figure 3. 2) The five beams were then unloaded, removed from the supports and three of the beams were repaired using CFRP fabrics. The Carbon Fibre Reinforced Polymer (CFRP) wraps of a width of 4 inches and a length of 100 inches were then glued to the bottom of three beams as shown in Figure 2. The CFRP wraps used had a Young’s modulus of 120 MPa and a tensile strength of 1516 MPa. The CFRP beams were divided into two groups. The first group consist of beams B-3 and B-4 were repaired using one layer of CFRP wraps applied to the beam, while the second group consisted of beam B4 were repaired using two layers of CFRP. These were loaded until failure or when flexural capacity was observed to be reached. The beam details and method of repair is given in Table 3, and Table 4 shows the properties of the reinforcing bars obtained based on the experimental investigations. www.ijert.org (This work is licensed under a Creative Commons Attribution 4.0 International License.) 232 Published by : http://www.ijert.org International Journal of Engineering Research & Technology (IJERT) ISSN: 2278-0181 Vol. 9 Issue 04, April-2020 Table 3: RC Beam Details Specimen id Bottom Steel Top Steel Stirrups Repair Material Number of FRP Layers B1 None None None None None B2 2#4 2#4 2#3 None None B3 2#4 2#4 2#3 CFRP 1 B4 2#4 2#4 2#3 CFRP 1 B5 2#4 2#4 2#3 CFRP 2 Table 4: Reinforcement bar details. Reinforcing bar Elastic Modulus (MPa) Diameter (mm) Yield Strength (MPa) Ultimate Strength (MPa) Longitudinal 200 12.7 470 620 Stirrup 210 10 380 550 The stirrup spacing, beam aspect ratio (a/d) and provision of wraps around beam would affect the overall performance of the beams. All the beams have aspect (a/d) ratio of 2.6 and a stirrup spacing of 4 inches which is less than the maximum allowable spacing in ACI 440 (d/2 or 24 inches for ∅𝑣𝑐 ≥ ∅𝑣 𝑣𝑢 > 𝑐 ). This was carried out to initiate possible flexural 2 failure in the beam. Flexural failure with enhanced ductility and a marginal increase in the first crack strength are expected in wrapped beams B3, B4, and B5 beams. DATA ACQUISITION Deflections in the beams were measured using LVDT installed at three different locations as shown in Fig. 2. Strain gages were installed on stirrups of all the beams to measure strains as shown in Fig. 3. Beams were tested in a four-point bending test. The loading was realized as deformation controlled using hydraulic jacks with calibrated gauges. The first stage of the research was focused on recognizing the process of the crack’s initiation in the plain concrete beam B1 and strengthened reinforced concrete beams B3, B4 and B5. Figure 1: Experimental Setup of Control Beam Figure 1: Longitudinal and cross-sections of the beam IJERTV9IS040207 www.ijert.org (This work is licensed under a Creative Commons Attribution 4.0 International License.) 233 Published by : http://www.ijert.org International Journal of Engineering Research & Technology (IJERT) ISSN: 2278-0181 Vol. 9 Issue 04, April-2020 Figure 2: Strengthening scheme using CFRP wrapping Figure 3: Location of embedded strain gauges (2 mm gauge length) on stirrup strengthened with one or two layers of CFRP sheets, appearing of cracks was delayed, also the width of those cracks and the inter-space between cracks were reduced. There were two main failure modes for the beams strengthened, i.e. snapping and debonding of CFRP sheets, and shear cracks propagated toward the loading point accompanied by debonding of the CFRP sheets from the concrete. The failure mode of the beams, B3, B4, B5 and B6, was characterized by the snapping of one layer or two layers of CFRP sheets that were bonded on the tensile face of the beams. However, the beams of B5 and B6 failed by the debonding of CFRP sheets from mid span or loading point. RESULTS AND DISCUSSIONS A. Failure Mode and Loads Table 4 summarizes the outcomes of the flexural tests: the first crack load, the ultimate load, the measured deflection corresponding to the ultimate load and the failure mode. A brittle, sudden failure behavior was observed after the appearance of the first flexural crack in beam B1 during the experiment. The failure mode of the reference beam B2 is a typical bending failure pattern, i.e. the failure basically consists of flexural cracks in the constant moment section characterized by yielding of the longitudinal steel bars and the concrete crush in the compressive zone. For the beams Table 5. Test results of the beams tested Beam Crack Load, kN B1 B2 B3 B4 B5 12.54 21.56 31.95 33.72 21.68 Ultimate Load, kN 17.36 43.33 48.15 60.62 69.82 The first crack loads of the beams B3, B4 and B5, which were strengthened with one and two layers of CFRP sheets respectively, are 32.5, 36.0% and 49.0% higher than that of the reference beam B2, due to the restraining effect of CFRP sheets respectively. However, the first crack loads are not proportional to the number of layers of CFRP sheets applied. The beam B3 gives a higher crack load than that of beams B1 and B2 but lower than that of the beam B4 and B5 since IJERTV9IS040207 Deflection, mm Failure modes 4.22 9.46 13.1 10.20 10.30 Brittle Failure Flexural Failure CFRP Snapping and Flexural Failure CFRP debonding and flexural failure CFRP debonding and flexural failure the beams was preloaded and the cracks were developed before the final failure tests. As shown in Table II, the ultimate loads of the control beams B2 is 59.87% higher than that of the plain beam B1. The table also shows that there is no an apparent gain on the strength when the reinforcement is increased from one layer to two layers. The beam B5 gives the ultimate load of 69.82 kN, which is 30.4% and 13.2% higher than that of the beams B3 and B4, respectively. www.ijert.org (This work is licensed under a Creative Commons Attribution 4.0 International License.) 234 Published by : http://www.ijert.org International Journal of Engineering Research & Technology (IJERT) ISSN: 2278-0181 Vol. 9 Issue 04, April-2020 Results given in Table II also show that the beams strengthened perform better than the control beam with respect to load carrying capacity and ductility. However, preloading on the beams may likely results in a decrease in flexural strength and ultimate ductility. B. Load-deflection Behaviour Fig. 2 shows that the initial stiffness of beams strengthened increases significantly in comparison to the control beam due to the contribution from the CFRP reinforcement. Beam B3 gives a smaller deflection at the given load than that of beam B4 from zero loads to the load of 52 kN, since the cracks developed during the preloading degraded the beam stiffness [1]. The control beam B2 with longitudinal reinforcement has a higher stiffness than that of the plain beam (WR4) which had premature brittle failure. Overall, the beam B5 gives a higher stiffness and ultimate strength than all the tested beams, due to contribution of longitudinal reinforcement and two layers of the CFRP stip. Beam B2: The beam failed due to concrete crushing at midspan after yielding of the tension steel. No shear cracks are observed as expected as the beams has a shear span of 12 inches and stirrup spacing of 4 inches. After failure, flexural cracks are observed in the beams throughout the span length. Significant strain readings were recorded from strain gauges sg1 and sg2 in the shear span and these strain readings are higher compared to other strain gauges sg3, sg4, sg5 and sg6 (Figs. 4a and 4b). All strain readings are nearly same at peak load, however, sg5 showed some variation before the tension steel yielded. Wider cracks are noticed near sg3 at failure of the beam. Beams B3: The preloaded concrete beams B3 strengthened with one layer of CFRP fabric, failed due to yielding of steel followed by rupture of fabric and crushing of concrete at mid-span. After failure, flexural cracks are observed in the beams. Shear cracks are not observed. The sg1 and sg6 strain gauges were located in the shear span. As shown in Figure 4c, It was noted that the strains in the sg1 and sg2 exhibited a steep increase after a load of 42 kN. The strain gauge sg5 recorded a steep increase in strain around the experimental peak load, which suggests that the failure occurred around the location of this strain gauge. Beams B4: The concrete beams B4 strengthened with one layer of CFRP fabric, failed due to yielding of steel followed by rupture of fabric and crushing of concrete at mid-span. After failure, flexural cracks are observed in the beams. Shear cracks are not observed. Figure 4d shows that sg1 and IJERTV9IS040207 sg6 strain gauges showed higher strain values compared to the other electrical strain gauges, similar to what was observed for the B2 control beam. It can also be seen that sg5 was mostly in compression, while the sg2 was always under tension. Beam B5: The concrete beam B5 strengthened with two layers of CFRP fabric, failed due to yielding of steel followed by debonding of fabric at mid-span followed by crushing of concrete. The term debonding implies that, at failure, the carbon sheet/fabric separated from the resin without any concrete or resin attached to it. After failure, flexural cracks are observed in the beam and while shear cracks are not observed. After failure, the CFRP fabric is easily peeled off from the beam, and no concrete chunks stuck to the fabric. The strain gauges sg1 and sg6 showed higher strain values compared to other strain gauges The sg2 gauge near the peak load carried a higher degree of tension, which indicates a possible de-bonding and thus putting a demand on the stirrup to take the tension. In fact, the final de-bonding failure occurred near the sg2 gauge. e of the scientific research was focused on recognizing the process of the crack’s initiation in plain concrete and slightly reinforced concrete beams. The experimental investigation was performed on 3 plain concrete beams and 3 slightly reinforced concrete beams (reinforcement ratio 0.12%). Beams were tested in a four-point bending test. The beams were loaded with two concentrated forces which were applied from bottom to top in one third of the span. The application of the upturned way of loading and the loading procedure by forcing displacement allowed to slow down the failure process and to observe crack developing precisely. The loading was realized as deformation controlled using hydraulic jacks with calibrated gauges. The beams were made of normal strength concrete. The first stage of the scientific research was focused on recognizing the process of the crack’s initiation in plain concrete and slightly reinforced concrete beams. The experimental investigation was performed on 3 plain concrete beams and 3 slightly reinforced concrete beams (reinforcement ratio 0.12%). Beams were tested in a fourpoint bending test. The beams were loaded with two concentrated forces which were applied from bottom to top in one third of the span. The application of the upturned way of loading and the loading procedure by forcing displacement allowed to slow down the failure process and to observe crack developing precisely. The loading was realized as deformation controlled using hydraulic jacks with calibrated gauges. The beams were made of normal strength concrete. www.ijert.org (This work is licensed under a Creative Commons Attribution 4.0 International License.) 235 Published by : http://www.ijert.org International Journal of Engineering Research & Technology (IJERT) ISSN: 2278-0181 Vol. 9 Issue 04, April-2020 80 50 Two layers CFRP 40 30 Load (kN) Load (kN) 60 B1 B2 20 Plain Beam 10 Control Beam B3 B4 B5 One layer CFRP 40 One layer CFRP - Preloaded 20 0 0 0 2 4 6 8 10 12 0 14 2 4 6 8 10 12 14 Midspan Deflection (mm) Midspan Deflection (mm) (b) (a) Figure 3. Load vs. deflection result of (a) Steel reinforced beam (b) CFRP strengthened beam 160 100 140 80 120 Load (in kN) Load (in kN) B1 60 sg1 sg2 sg3 sg4 sg5 sg6 40 B2 100 sg1 sg2 sg3 sg4 sg5 sg6 80 60 40 20 20 0 0 -400 -200 0 200 Strain (a) 400 600 800 -500 0 500 1000 1500 2000 2500 Strain (b) Fig. 4. Load-strain (in µε) curves for (a) plain beam B1 (b) control beam B2 (c) Wrapped CFRP beam B3 (d) Wrapped GFRP beam B4 (e) WGFRP CFRP beam B5 IJERTV9IS040207 www.ijert.org (This work is licensed under a Creative Commons Attribution 4.0 International License.) 236 Published by : http://www.ijert.org International Journal of Engineering Research & Technology (IJERT) ISSN: 2278-0181 Vol. 9 Issue 04, April-2020 180 120 160 100 140 B3 B4 120 Load (in kN) Load (in kN) 80 60 sg1 sg2 sg3 sg4 sg5 sg6 40 20 100 sg1 sg2 sg3 sg4 sg5 sg6 80 60 40 20 0 0 -600 -400 -200 0 200 400 600 800 1000 0 -200 1200 200 400 600 800 1000 Strain Strain (c) (d) 180 160 B5 140 Load (in kN) 120 100 80 sg1 sg2 sg3 sg4 sg5 sg6 60 40 20 0 -100 -50 0 50 100 150 200 250 300 Strain (e) Fig. 8 Load-deflection curves for the three control beams Fig. 4. Load-strain (in µε) curves for (a) plain beam B1 (b) control beam B2 (c) Wrapped CFRP beam B3 (d) Wrapped CFRP beam B4 (e) CFRP CFRP beam B5 C. Comparison with ACI 440.2R theoretical formulation In general, the proposed theoretical approach used for the flexural strength is based on the sectional analysis and strain compatibility. Figure 5 shows the internal strain and stress distribution for a retrofitted rectangular section under flexure at the ultimate limit state. According to ACI 440.2R-17, the ultimate strength of the beam should satisfy strain compatibility and force equilibrium, and should consider the governing mode of failure. The flexural strength of the beams is given by 𝑀𝑢 = 𝑀𝑐 + 𝑀𝑠 + 𝑀𝑓 (1) where, 𝑀𝑐 𝑎𝑛𝑑 𝑀𝑠 are the contribution of the concrete and internal reinforcing steel bars IJERTV9IS040207 www.ijert.org (This work is licensed under a Creative Commons Attribution 4.0 International License.) 237 Published by : http://www.ijert.org International Journal of Engineering Research & Technology (IJERT) ISSN: 2278-0181 Vol. 9 Issue 04, April-2020 Reinforced Concrete Sections Force Equilibrium Force Equilibrium Strain Distribution (Non-linear Concrete (Equivalent Concrete Stress Distribution Stress Distribution Figure 5. Internal strain and stress distribution for a rectangular section under flexure at ultimate limit state The nominal flexural strength of the section with FRP external reinforcement is computed from 𝑀𝑛 = 𝐴𝑠 𝑓𝑠 (𝑑. 𝛽1 .𝑐 2 + Ψ𝑓 𝐴𝑓 𝑓𝑓 ℎ 𝛽1 .𝑐 2 ) (2) where ψf, is an additional reduction factor applied to the flexural-strength contribution of the FRP reinforcement. As is the area of steel bars, fs is the stress in the steel (MPa), d is the effective depth of the section, 𝐴𝑓 𝑎𝑛𝑑 𝑓𝑓 are the area and stress level in FRP reinforcement respectively, and 𝑐 is the distance from extreme compression fiber to the neutral axis. The terms 𝛽1 is a parameters defining a rectangular stress block in the concrete equivalent to the nonlinear distribution of stress. The values of the beam carrying capacity, Peqn, estimated from equation 2 was compared to the test result, Pexp, of the CFRP wrapped beams B3, B4 and B5 and a ratio of Pana / Pexp was evaluated in Table 6. It can be concluded that the estimated values were quite lower than those of experimental ones. One possible reason for the difference between both the theoretical approaches and the experimental values can be found in the value of the maximum compressive concrete strain considered, because in all the theoretical approaches this value was the same as 0.003. Table 6: Comparison of Test Results and Theoretical Equation Beam B3 B4 B5 Ultimate Load, Pexp (kN) 48.76 60.42 74.68 ACI 440.2R-17, Peqn (Eqn. 2) 52.25 67.68 79.82 REFERENCES CONCLUSIONS [1] The results indicated that the flexural carrying capacity of the RC beams strengthened using externally bonded CFRP sheets on bottom faces could significantly enhance the flexural capacity of the beams tested. The increase on the overall flexural capacity of the CFRP strengthened beams varies between 41% and 125% over the control beam. The strength and ductility for the beams strengthened could be enhanced significantly by providing effective bond, increasing the number of CFRP layers the longitudinal reinforcement ratio, but the preloading before the failure test might result in a little decrease in flexural strength, stiffness and ductility. It is noted that the final failure of the wrapped beams occurred due to the de-bonding of the wrap in the compression zone and failure was sudden. IJERTV9IS040207 Peqn/ Pexp 0.93 0.89 0.93 [2] [3] [4] [5] [6] Ashour, A. F., El-Refaie, S. A., & Garrity, S. W. (2004). Flexural strengthening of RC continuous beams using CFRP laminates. Cement and concrete composites, 26(7), 765-775. Chiew, S. P., Sun, Q., & Yu, Y. (2007). Flexural strength of RC beams with GFRP laminates. Journal of composites for Construction, 11(5), 497-506. Esfahani, M. R., Kianoush, M. R., & Tajari, A. R. (2007). Flexural behaviour of reinforced concrete beams strengthened by CFRP sheets. Engineering structures, 29(10), 2428-2444. Jumaat, M. Z., Rahman, M. M., & Alam, M. A. (2010). Flexural strengthening of RC continuous T beam using CFRP laminate: A review. International Journal of the Physical Sciences, 5(6), 619-625. Thompson, N. G., Yunovich, M., & Dunmire, D. (2007). Cost of corrosion and corrosion maintenance strategies. Corrosion Reviews, 25(3-4), 247-262. American Concrete Institute - ACI 440.2R – A Guide for the Design and Construction of Externally Bonded FRP Systems for Strengthening Concrete Structures. www.ijert.org (This work is licensed under a Creative Commons Attribution 4.0 International License.) 238